US20090054567A1 - Phosphite stabilizers for ionomeric polyester compounds - Google Patents

Phosphite stabilizers for ionomeric polyester compounds Download PDF

Info

Publication number
US20090054567A1
US20090054567A1 US12/196,499 US19649908A US2009054567A1 US 20090054567 A1 US20090054567 A1 US 20090054567A1 US 19649908 A US19649908 A US 19649908A US 2009054567 A1 US2009054567 A1 US 2009054567A1
Authority
US
United States
Prior art keywords
composition
acid
polymer
phosphorus compound
polyester
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US12/196,499
Other languages
English (en)
Inventor
Paul Lewis HEATER
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
M&G Polimeri Italia SpA.
APG Polytech LLC
Original Assignee
M&G Polimeri Italia SpA.
M&G USA Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by M&G Polimeri Italia SpA., M&G USA Corp filed Critical M&G Polimeri Italia SpA.
Priority to US12/196,499 priority Critical patent/US20090054567A1/en
Publication of US20090054567A1 publication Critical patent/US20090054567A1/en
Assigned to M & G USA CORPORATION, M & G POLIMERI ITALIA S.P.A. reassignment M & G USA CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: HEATER, PAUL L
Priority to US12/944,065 priority patent/US8063124B2/en
Assigned to TRIMONT REAL ESTATE ADVISORS, LLC reassignment TRIMONT REAL ESTATE ADVISORS, LLC SECURITY INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: M&G USA CORPORATION
Assigned to M&G USA CORPORATION reassignment M&G USA CORPORATION RELEASE BY SECURED PARTY (SEE DOCUMENT FOR DETAILS). Assignors: UNITED STATES BANKRUPTCY COURT FOR DISTRICT OF DELAWARE
Assigned to FE POLYTECH, LLC reassignment FE POLYTECH, LLC ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: M&G USA CORPORATION
Assigned to APG Polytech, LLC reassignment APG Polytech, LLC CHANGE OF NAME (SEE DOCUMENT FOR DETAILS). Assignors: FE POLYTECH, LLC
Assigned to M&G USA CORPORATION reassignment M&G USA CORPORATION RELEASE BY SECURED PARTY (SEE DOCUMENT FOR DETAILS). Assignors: TRIMONT REAL ESTATE ADVISORS, LLC
Assigned to M&G USA CORPORATION reassignment M&G USA CORPORATION RELEASE BY SECURED PARTY (SEE DOCUMENT FOR DETAILS). Assignors: TRIMONT REAL ESTATE ADVISORS, LLC
Abandoned legal-status Critical Current

Links

Classifications

    • CCHEMISTRY; METALLURGY
    • C08ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08KUse of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K5/00Use of organic ingredients
    • C08K5/49Phosphorus-containing compounds
    • C08K5/51Phosphorus bound to oxygen
    • C08K5/52Phosphorus bound to oxygen only
    • C08K5/524Esters of phosphorous acids, e.g. of H3PO3
    • CCHEMISTRY; METALLURGY
    • C08ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08LCOMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L67/00Compositions of polyesters obtained by reactions forming a carboxylic ester link in the main chain; Compositions of derivatives of such polymers
    • C08L67/02Polyesters derived from dicarboxylic acids and dihydroxy compounds
    • CCHEMISTRY; METALLURGY
    • C08ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08LCOMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L69/00Compositions of polycarbonates; Compositions of derivatives of polycarbonates
    • CCHEMISTRY; METALLURGY
    • C08ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08LCOMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L69/00Compositions of polycarbonates; Compositions of derivatives of polycarbonates
    • C08L69/005Polyester-carbonates

Definitions

  • compositions comprising an oxidizable phosphorus compound and an ionomeric polyester derived from at least one ionomeric monomer wherein at least 90% of the acid units of the ionomeric polyester are derived from the group consisting of terephthalic acid, isophthalic acid, orthophthalic acid, 2,6 dimethylnaphthalic acid, and their respective dimethyl esters and the composition has a total amount of polyester which is the amount of ionomeric polyester polymer plus the amount of non-ionomeric polyester polymer, if present.
  • the ionomeric monomer of the composition may be selected from the group consisting of the metal salt of a sulfonate of terephthalic acid, isophthalic acid, orthophthalic acid, 2,6 dimethylnaphthalic acid, and their respective dimethyl esters.
  • the oxidizable phosphorus compound can be selected from the group consisting of triphenylphosphite, trimethylphosphite, triethylphosphite, (2,4,6-tri-t-butylphenol)2-butyl 2 ethyl 1,3-propanediol phosphite, bis(2,4-di-tert-butylphenyl) Pentaerythritol diphosphite and tetrakis(2,4-di-tert-butylphenyl)4,4-biphenyldiphosphonite.
  • the oxidizable phosphorus compound is present in the ranges of 15 to 150 parts phosphorus to million parts total polyester polymer, 15 to 120 parts phosphorus to million parts total polyester polymer, or 30 to 100 parts phosphorus to million parts total polyester polymer.
  • composition be essentially void of a polyamide polymer. It is also disclosed that the may further comprises a polyamide polymer in the range of 0.2 percent by weight of the composition to 10 percent by weight of the composition.
  • the composition can also be essentially void of an elemental metal which was a metal ion reduced by the oxidizable phosphorus compound.
  • Essentially void means that there is virtually no ( ⁇ 0.5 ppm) precipitated metal which has been precipitated by the addition of the phosphite. There could be metal present which has been precipitated by another compound. The comparison would be made between the composition with and without the phosphorus compound.
  • the composition with the oxidizable phosphorus compound would contain ⁇ 0.5 ppm, and more preferably ⁇ 0.25 ppm, of the elemental or precipitated metal as compared to a composition without the oxidizable phosphorus compound.
  • composition may have some elemental metal but less than 1 ppm of an elemental metal, or 2 ppm of an elemental metal, or 5 ppm elemental metal, or even less than 10 ppm of an elemental metal.
  • This process also discloses a process for thermally treating the preceding compositions comprising the step of heating any one of the compositions to a temperature above 70° C. for more than 2 minutes in the presence of oxygen.
  • Non-oxidizable phosphorus (p +5 ) compounds are often used to stabilize polyester polymers.
  • Phosphoric acid (H 3 PO 4 ) is a commonly used stablizer.
  • Oxidizable phosphorus compounds (p +3 ), such triethylphosphite (TEP) are virtually never used to stabilize polyesters because of the oxidation-reduction reaction of the oxidizable phosphorus compound with the reducible (oxidized) metal ion catalyst usually present in the polymer.
  • TEP triethylphosphite
  • the metal is reduced, often creating an elemental metal particle that plugs filters, builds up on the reactor walls, and creates a dark color in the finished article.
  • the oxidizable phosphorus stabilizer is effective at reducing the color shift caused by subjecting the combination of the ionomeric polymer and a polyamide to a heat history such as drying or melting and extruding.
  • this invention is directed primarily to a composition comprising an ionomeric polyester polymer and an oxidizable phosphorus stabilizer and the composition does not contain a polyamide.
  • does not contain a polyamide it means that the composition could be void of a polyamide polymer, essentially void of a polyamide polymer, or contains essentially no polyamide.
  • compositions which would include a polyamide
  • the invention is also directed to a composition comprising an ionomeric polyester polymer and an oxidizable phosphorus stabilizer and the composition further comprises a polyamide polymer.
  • the invention is also to a process for heating a composition comprising an ionomeric polymer and a polyamide, where the process comprises the step or steps of creating a composition comprising an ionomeric polyester polymer, a polyamide polymer and an oxidizable phosphorus compound, subjecting the composition to a thermal treatment of at least 70° C. for at least 2 minutes in the presence of oxygen, such as drying in air.
  • This thermal treatment includes but is not limited to drying, extruding, and/or solid phase polymerizing the composition.
  • the ionomeric polymers suitable for this invention include those polyesters which are made using the polar co-monomers.
  • crystallizable sulfonated polyester polymers are the crystallizable sulfonated polyester polymers.
  • crystallizable means that the thermoplastic polymer can be become semi-crystalline, either through orientation or heat induced crystallinity. It is well known that no plastic is completely crystalline and that the crystalline forms are more accurately described as semi-crystalline.
  • semi-crystalline is well known in the prior art and is meant to describe a polymer that exhibits X-ray patterns that have sharp features of crystalline regions and diffuse features characteristic of amorphous regions. It is also well known in the art that semi-crystalline should be distinguished from the pure crystalline and amorphous states.
  • a crystallizable polymer will form crystals when the polymer is gradually cooled from the molten state. These crystals will generate diffraction observable by X-ray.
  • the thermoplastic polymers used in the present invention comprise a sulfonated polyester polymer which means a sulfonated homopolymer of polyethylene terephthalate or sulfonated crystallizable copolymer of polyethylene terephthalate.
  • crystallizable polyethylene terephthalate and group consisting of crystallizable polyethylene terephthalates refers to polymers which are crystallizable and comprised of at least 85% polyethylene terephthalate repeating segments. The remaining 15% may be any other combination of acid-glycol repeating units, provided that the resulting polymer is capable of achieving a degree of crystallinity of at least 5%, more preferably 10%.
  • crystallizable polyester refers to polymer which is crystallizable and at least 85% of its acid moieties are selected from the group consisting of terephthalic acid, 2,6-naphthalene dicarboxylic acid or their respective di-methyl esters.
  • the useful polyester polymers are the phthalate and naphthalate polymers which means that acid moieties are derived from terephthalic acid, orthophthalic acid, isophthalic acid, 2,6-naphthalate dicarboxylic acid, or their respective dimethyl esters.
  • At least some of the polyester polymer in the polyester phase is to be sulfonated.
  • PET is the group of polyesters consisting of polyethylene terephthalate and copolymers of polyethylene terephthalate including copolymers of polyethylene terephthalate modified with metal salt of sulfoisophthalate derived from the di-ester or di-carboxylic acid of sulfoisophthalate (SIPA) in the approximately 1:1 stoichiometric reaction of the acids, or their di-esters, with ethylene glycol.
  • SIPA sulfoisophthalate
  • Specific copolymers of interest are the crystallizable polyethylene terephthalates which have at least one sulfoisophthalate as an acid moiety and at least one other acid moiety derived from the comonomers selected from the group consisting of isophthalic acid or its diester, 2,6-naphthalene dicarboxylic acid or its diester, and cyclohexane dimethanol.
  • the preferred sulfoisophthalate is lithium sulfoisophthalate with the levels of lithium sulfoisophthalate within the range of 0.01 and 2.0 mole percent based upon the acid moieties of the polyesters in the article.
  • polytrimethylene terephthalate PTT
  • PTT polytrimethylene terephthalate
  • Preferred diacids and alkyl esters include terephthalic acid (TPA) or dimethyl terephthalate (DMT).
  • TPA terephthalic acid
  • DMT dimethyl terephthalate
  • the PTT preferably comprises at least about 80 mole percent of either TPA or DMT.
  • Other diols which may be copolymerized in such a polyester include, for example, ethylene glycol, diethylene glycol, 1,4-cyclohexane dimethanol, and 1,4-butanediol.
  • metal sulfonate such as the metal salt of sulfoisophthalic acid
  • other aromatic and aliphatic acids which may be used simultaneously to make a copolymer include, for example, isophthalic acid and sebacic acid.
  • polyethylene naphthalate also known as PEN. It is made by the reaction of 2,6-naphthalene dicarboxylic acid or its diester (2,6-dimethyl naphthalate) with ethylene glycol.
  • crystallizable polyester of the present invention may comprise recycled polyester or materials derived from post consumer or post industrial recycled polyester, such as polyester monomers, catalysts, and oligomers.
  • the polyester polymer could also be a mixture of unsulfonated polyester molecules and sulfonated polyester molecules.
  • the polyester polymer molecules in the polyester polymer phase usually contain at least one metal sulfonate. While the sulfonated polyester polymer affects the interfacial tension between the polyamide polymer when the two are mixed, the presence of the polyamide is not essential for the operation of the oxidizable phosphorus compound to stabilize the polyester without reducing the metal.
  • the preferred polymer composition is therefore an ionomeric polyester polymer where the ionomeric polyester polymer is a sulfonated polyester, preferably lithium sulfoisophthalic acid in the range of 0.01 mole % to 5 mole %, and triethylphosphite (TEP) in the amount of 5 to 200 ppm as elemental phosphorus in the TEP to sulfonated polyester.
  • TEP triethylphosphite
  • the sulfonated polyester polymer will usually comprise metal sulfonate derived from a functionalized metal sulfonate.
  • the term functionalized metal sulfonate to describe a compound of the form R—SO 3 M, where M is the metal ion and R is an aliphatic, aromatic, or cyclic compound with at least one functional group that allows the functionalized metal salt to react with the polyester or its respective monomers or oligomers where M designates the metal ion.
  • Functionalized metal sulfonates included in this invention are the lithium and sodium salts of sulfonated comonomers, including aliphatic and aromatic alcohols, carboxylic acids, diols, dicarboxylic acids, and multifunctional alcohols, carboxylic acids, amines and diamines.
  • non-functional metal sulfonates are those of the R—SO 3 M, and R does not have functional group.
  • the phrase metal sulfonate therefore refers to both functional and non-functional metal sulfonates.
  • An example of this sulfonated polystyrene or polyolefins which are known to act as metal sulfonates in the polyester-polyamide systems.
  • the metal sulfonate exists in functionalized form of the form X—R, where X is an alcohol, carboxylic acid or epoxy, most preferably a dicarboxylic acid or diol and R is R is —SO 3 M, —COOM, —OM, —PO 3 (M) 2 , with M being a metal in a +1 or +2 valence state which can be selected from the group consisting of Li, Na, Zn, Sn, K and Ca and X—R is copolymerized into the polyester polymer to modify the interfacial tension.
  • the amount of X—R needed will exceed 0.01 mole percent with respect to the total number of respective dicarboxylic acid or diol moles in the polymer composition. It is possible for X—R to include both a diol or dicarboxylic acid. In that case, the mole percent is based upon the total number of moles of respective diols, dicarboxylic acids, or polymer repeating units.
  • the functionalized metal sulfonate may contain 2 or more R groups.
  • R is combined directly to the aromatic ring of X, which could be a diol, a dicarboxylic acid, or a side chain such as a methylene group.
  • X which could be a diol, a dicarboxylic acid, or a side chain such as a methylene group.
  • R is —SO 3 M, —COOM, —OM, —PO 3 (M) 2 with M designating a metal in a +1 or +2 valence state which can be selected from the group consisting of Li, Na, Zn, Sn, Ca and K.
  • M designating a metal in a +1 or +2 valence state which can be selected from the group consisting of Li, Na, Zn, Sn, Ca and K.
  • R is —SO 3 M
  • the compound is known as sulfonate, an organic sulfonate, or more specifically, sulfoisophthalic acid. If this entity is the metal sulfonate, then the polyester would contain acid units derived from a metal salt of sulfoisophthalic acid, wherein the metal can be selected from the group consisting of lithium, sodium, zinc, tin, calcium and potassium.
  • the dicarboxylic acids represented by X may be each ortha, meta, or para. They comprise for instance aromatic dicarboxylic acids such as terephthalic acid, isophthalic acid, orthophthalic acid, naphthalene dicarboxylic acid, diphenylether dicarboxylic acid, diphenyl-4,4-dicarboxylic acid etc.
  • X may also be aliphatic.
  • aliphatic dicarboxylic acids such as oxalic acid, malonic acid succinic acid, glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, etc. are suitable.
  • Cycloaliphatic dicarboxylic acids such as cyclohexanedicarboxylic acid and one or more species of these can be used.
  • isethionic acid is also included. Specifically contemplated are mixtures of the dicarboxylic acids as well.
  • X can also represent an alcohol, preferably a diol of the structure:
  • R is —SO 3 M, —COOM, —OM, —PO 3 (M) 2 where M is a metal in a +1 or +2 valence state which can be selected from the group consisting of Li, Na, Zn, Sn, K, and Ca.
  • the diols represented by X may also be aliphatic glycols such as ethylene glycol, 1,3 propanediol, 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, 1,9-nonanediol, diethylene glycol, trimethylene glycol and cycloaliphatic diols such as cyclohexane diol, cyclohexanedimethanol and one or more species in combination can be used.
  • ethylene glycol, diethylene glycol and cyclohexanediol are preferred.
  • hydroxyl terminated polyethers such as polyethylene glycol (Carbowax) and cyclic amides such as ethoxylated dimethyl hydantoin.
  • polyesters can be reacted with epoxy terminated compounds, including epoxy terminated polyethers, to produce a polyether side chain attached to the polymer.
  • LiSIPA Lithium sulfoisophthalic acid
  • LiSIPA Lithium sulfoisophthalic acid
  • the di-carboxylic acid, di-ester, or pre-reacted low molecular weight oligomers such as the bis-hydroxyethyl ester of lithium sulfoisophthalate are preferred. It is also possible that the metal sulfonate, in this case the lithium sulfonate, occur in the diol form as well. Possible alternatives are ethylene glycol with the sulfonate group at the end of the pendant chain. It has even been proposed to place the sulfonate at the end of the polyester molecule. This can be accomplished by reacting or copolymerizing the polyester with the sulfonated salt of benzoic acid or other monofunctional species such as isethionic acid, either in the melt reactor or in an extruder.
  • the metal sulfonate In order to be reacted into, also known as copolymerized with, either polymer, the metal sulfonate must have at least one functional group.
  • these functional groups are carboxylic acid (—COOH), alcohol (—OH), the ester of the carboxylic acid, epoxy termination, the diamine, or amine end groups.
  • the non-functionalized metal sulfonates are those compounds which contain the polar group, for example, the lithium salt, but do not have any functional end groups which allow the metal sulfonate to react with the polyester or polyamide.
  • the lithium salt of sulfonated polystyrene is an example.
  • the mole percent of the metal sulfonate is the mole percent based upon all the acid groups of the polyester.
  • the polyester polymer is modified with the metal sulfonate. This modification is done by copolymerizing the metal sulfonate into the polymer chain.
  • the composition can comprise the elements in a two component form.
  • other compounds may, of course, be present in the composition.
  • a metal sulfonate is copolymerized with the polyester polymer to make the polyester a sulfonated polyester copolymer.
  • the elements of the composition can also be present as more than two components. Again, in addition to the critical components, other compounds may, of course, be present in the composition.
  • one embodiment is a polyester without a metal sulfonate copolymerized with the polymer, a polyester with a metal sulfonate copolymerized with the polymer, and the polyamide without a metal sulfonate copolymerized with the polyamide and an oxidizable phosphorus compound.
  • Another embodiment is a polyester without a metal sulfonate copolymerized with the polymer, a polyester with a metal sulfonate copolymerized with the polymer, and an oxidizable phosphorus compound.
  • Another embodiment is a polyester without a metal sulfonate copolymerized with the polymer, a polyester with a metal sulfonate copolymerized with the polymer, a polyamide with a metal sulfonate copolymerized with the polyamide and a polyamide without a metal sulfonate copolymerized with the polyamide and an oxidizable phosphorus compound.
  • a typical homopolymer polyester has 100 mole percent terephthalate derived from terephthalic acid and almost 100 mole percent ethylene derived from ethylene glycol, with the remaining glycol being diethylene derived from diethylene glycol which is derived in situ during the manufacturing process.
  • 100 moles of polymer with 5 mole percent of the ionic dicarboxylic acid co-monomer, such as lithium sulfoisophthalic acid would contain 95 moles of terephthalate derived from terephthalic acid, 5 moles of lithium sulfoisophthalate and approximately 100 moles of ethylene derived ethylene glycol.
  • another comonomer such as isophthalic acid.
  • the moles of acid are the moles of acid in the sulfonated polyester polymer plus the moles of acid in the compatible unmodified polyester polymer.
  • the mole percent of the sulfoisophthalate would be the moles of sulfoisophthalate divided by the moles of acid moieties of the two polyesters added together.
  • di-ethylene glycol is formed in-situ in the manufacture of polyester and about 1-3 percent of the total moles of glycol derived repeat unit will be diethylene derived from diethylene glycol. Therefore, the polyester compositions are often about 97 mole percent ethylene and about 3 mole percent di-ethylene.
  • Typical levels for a metal sulfoisophthalate derived from the metal sulfoisophthalic acid or its di-methyl ester are in the range of about 0.01 to about 15 mole percent, with the range of about 0.05 to about 10 mole percent being more preferred, with the range of about 0.1 to 5 mole percent also preferred, with the range of about 0.2 to about 4 mole percent and about 0.3 to about 2 mole percent also being good operational ranges.
  • the amount of metal sulfonate is determined by measuring the amount of sulphur in the polymer or the metal in the polymer.
  • the sulfonates belonging to the class of isophthalates they can be described as being a metal sulfoisophthalate derived from the metal sulfoisophthalic acid or glycol, wherein the metal is selected from the group consisting of lithium, sodium, potassium, calcium, zinc, and manganese.
  • Polyesters modified with the metal sulfonate employed in the present invention can be prepared by most polymerization procedures.
  • the traditional techniques can be divided into the ester, acid, and modified processes.
  • the ester process the dimethyl ester of the carboxylic acid or acids is reacted with the glycol or glycols in the presence of heat and the methanol removed yielding the bis-hydroxyethyl ester of the acids.
  • the bis-hydroxyethyl ester is then polymerized in its liquid form by subjecting the material to vacuum and heat to remove the glycols and increase the molecular weight.
  • a typical process for the object polymer with a metal sulfonate would start with these ratios: 98 moles of dimethyl terephthalate, 2 moles of dimethyl sodium salt of sulfoisophthalate and 220 moles of glycol, typically ethylene glycol. Of the 220 moles of glycol, 120 are excess which are removed during processing. It should be noted that it is possible to obtain the sulfonated co-monomer in either its bis-(hydroxyethyl) or dimethyl ester form.
  • the phrase copolymerized with at least X percent of a specific acid means that the compound is considered as part of the acid group of the polymer, such as terephthalic or isophthalic acid. It provides the reference to determine how many moles of the compound to use. The phrase does not mean that the compound must be added to the process as an acid.
  • lithium sulfoisophthalic acid could be copolymerized into polyethylene terephthalate as the acid with two carboxylic end groups, as the dimethyl ester of the carboxylic acid, as the bis-hydroxyethyl ester of the dimethyl ester, as very low molecular weight oligomers of a glycol acid polymer where the acid moieties are at least in part, the sulfoisophthalate salt, or as the di-alcohol.
  • copolymerized salt of the acid should not limit the claim to only using the acid form, but should be read to mean that the compound is one of the acid derived groups in the polymer.
  • copolymerized with means that the compound has been chemically reacted with the polymer, such as in the polymer chain or as a pendant group.
  • a polyester copolymerized with lithium sulfoisophthalate, or modified by copolymerizing at least 0.01 mole percent sulfoisophthalate into the polyester means that sulfoisophthalate is bonded to the polymer, including bound into the polymer chain, with at least one chemical bond.
  • the phrases are indifferent to how the material is incorporated into the polymer.
  • a polyester copolymerized with lithium sulfoisophthalate, or modified by copolymerizing at least 0.01 mole percent lithium sulfoisophthalate into polyester refers to a polyester containing the lithium sulfoisophthalate whether that lithium sulfoisophthalate was incorporated using but not to limited to lithium sulfoisophthalic acid, lithium sulfobenzoic acid, the dimethyl ester of lithium sulfoisophthalic acid, the methyl ester of lithium sulfobenzoic acid, the lithium sulfohydroxy benzene, the lithium salt of hydroxy benzene sulfonic acid, or oligomers or polymers containing the lithium sulfoisophthalate.
  • lithium sulfoisophthalate “and its derivatives” refers collectively and is not limited to lithium sulfoisophthalic acid, the dimethyl ester of lithium sulfoisophthalic acid, the bis-hydroxyethyl ester of lithium sulfoisophthalic acid, low molecular weight oligomers, and high I.V. polymers containing lithium sulfoisophthalate in the polymer chain.
  • the starting materials are the di-carboxylic acids, with water being the primary by-product.
  • the charge ratio in a typical acid process is 99.5 moles terephthalic acid, 0.5 moles of a metal salt of sulfoisophthalic acid (e.g. lithium sulfoisophthalic acid-LiSIPA), and 120 moles of glycols, typically ethylene glycol.
  • the initial charge also includes the oxidizable phosphorus compound and catalyst.
  • the material is subjected to the same polymerization process conditions as the ester process. In practice, many of the salts degrade and are therefore added in as a pre-reacted bis-hydroxy ester form.
  • the modified processes are variations of either process; combining the intermediary product at certain steps.
  • the acid process may be used with just terephthalic acid to produce its low molecular weight intermediate and the ester process used to produce the bis-hydroxyethyl ester of the homopolymer sulfonated polyester. These two intermediates are then combined and polymerized to a more random copolymer.
  • Another variation is to add the finished modified polymer to the melt reactor and let the melt process depolymerise the modified polymer and then form a random copolymer.
  • terpolymer containing the unmodified isophthalic acid derivative If one wanted to make a terpolymer containing the unmodified isophthalic acid derivative, one would use 98 moles of terephthalic acid, 0.5 moles of lithium sulfoisophthalic acid, and 1.5 moles of unsulfonated isophthalic acid.
  • modified polymer Another technique for manufacturing the modified polymer is to completely trans-esterify a modified polyester with a large amount of metal sulfonate moieties into a unmodified polyester to create a blockier copolymer. This can be done using other techniques such as a long residence time and/or high temperature extrusion.
  • Sandostab® P-EPQ (CAS 119345-01-6) also known as tetrakis(2,4-di-tert-butylphenyl)4,4-biphenyldiphosphonite available from Clariant GmbH, Germany.
  • Triethylphosphite (CAS 122-52-1) C 6 H 15 O 3 P, available from Sigma-Aldrich, St. Louis, Mo. 63103 USA.
  • Trimethylphosphite (CAS 121-45-9) C 6 H 15 O 3 P, available from Sigma-Aldrich, St. Louis, Mo. 63103 USA.
  • Triphenylphosphite (CAS 101-02-0) C 6 H 15 O 3 P, available from Sigma-Aldrich, St. Louis, Mo. 63103 USA.
  • Ultranox 626® (CAS 26741-53-7) known as bis(2,4-di-tert-butylphenyl) Pentaerythritol diphosphite available from Crompton Corporation, now Chemtura Corporation, Middlebury Conn., USA.
  • the stabilizer should be present in amount sufficient so that phosphorus is present in the range of 15 parts phosphorus per million parts of the total amount of polyester polymer in the composition to 150 parts phosphorus per million parts of the total amount of polyester polymer in the composition.
  • the total amount of polyester polymer in the composition is the amount of ionomeric polyester polymers present plus the amount of non-ionomeric polyester polymers, if present. While the 15 to 150 ppm on the basis of elemental phosphorus is desirable, 15 to 120 ppm on the basis of elemental phosphorus is more desirable with 20 to 100 ppm on the basis of elemental phosphorus being the most desired.
  • Addition of the oxdizable phosphorus compound is preferably done by melt mixing the oxidizable phosphorus compound with the ionomeric polyester polymer at the beginning of the reaction.
  • the stabilizer can also be added via subsequent melt mixing when the ionomeric polyester polymer melted and optionally extruded into a part or blended with a non-ionomeric polyester polymer, or optionally the polyamide.
  • the composition may be void of a polyamide polymer, essentially void of a polyamide polymer, consist of the ionomeric polymer and the oxidizable phosphorus compound, or consist essentially of the ionomeric polymer and the oxidizable phosphorus compound.
  • the composition may further comprise a polyamide polymer.
  • the polyamides which could be modified or unmodified that are suitable for this invention can be described as those selected from the group consisting of the repeating unit of amino caproic acid or A-D, wherein A is the residue of a dicarboxylic acid comprising adipic acid, isophthalic acid, terephthalic acid, 1,4-cyclohexanedicarboxylic acid, resorcinol dicarboxylic acid, or naphthalenedicarboxylic acid, or a mixture thereof, and D is a residue of a diamine comprising m-xylylene diamine, p-xylylene diamine, hexamethylene diamine, ethylene diamine, or 1,4 cyclohexanedimethylamine, or a mixture thereof.
  • polyamides can range in number average molecular weight from 2000 to 60,000 as measured by end-group titration. These polyamides can also be described as the reaction product of amino caproic acid with itself and/or the reaction product of a residue of dicarboxylic acid comprising adipic acid, isophthalic acid, terephthalic acid, 1,4-cyclohexanedicarboxylic acid, resorcinol dicarboxylic acid, or naphthalenedicarboxylic acid, or a mixture thereof with a residue of a diamine comprising m-xylylene diamine, p-xylylene diamine, hexamethylene diamine, ethylene diamine, or 1,4 cyclohexanedimethylamine, or a mixture thereof.
  • the reaction product of the residue of sebacic acid with hexamethylene diamine is nylon 6, 10 and the reaction product of the residue of adipic acid and hexamethylene diamine is nylon 6, 6.
  • Nylon 6, 12 is another nylon which benefits from the invention.
  • Nylon 6 is a special type of polyamide which is made by the opening of caprolactam and then polymerizing the resulting amino caproic acid which has a formula of H 2 N—(CH 2 ) 5 —COOH.
  • One useful polyamide is the reaction product of the residues of adipic acid and m-xylylene diamine, known as poly-m-xylylene adipamide. This product is commercially known as MXD6 or nylon MXD6 and can be purchased from Mitsubishi Gas Chemical Company, Japan.
  • the preferred amount of polyamide is between 1 and 15 parts per 100 parts of the composition of the article, preferably between 3 and 8 parts per 100 parts of the composition of the article, with the most utility occurring between 4 and 7 parts of polyamide per 100 parts of the composition of the article.
  • the amount of total polyester polymers should be at least 80% of the total weight of the article, with the weight percent of all components of the composition adding to 100%.
  • Crystallizable polyesters containing amounts lithium sulfonate in the form of lithium sulfo-isophthalate derived from lithium sulfoisophthalic acid were manufactured by placing 7692 gms of terephthalic acid, 194 gms of isophthalic acid, and 2924 gms of ethylene glycol into a vessel of pre-reacted oligomers from the previous batch. The pre-reacted oligomers are called a heel. The weight of heel to batch, amount charged to reactor, is approximately 1:1. The contents were held under 3.38 bar pressure at 262° C.
  • the vessel contents were transferred to a second vessel.
  • the heel remaining in the first vessel was approximately the same amount as was in the vessel when the raw materials were first charged.
  • 223 of 1% antimony by weight 191 gms of a 5% bis-hydroxyethyl ester of lithium sulfoisophthalic acid—95% ethylene glycol solution and 1412 gms of ethylene glycol were added to the material transferred from the first vessel to the second vessel.
  • the contents of the second vessel were agitated at atmospheric pressure and 244° C. After 30 minutes of mixing, the pressure was reduced to 100 torr, and after another 26 minutes, the pressure reduced to 1.0 torr. 40 minutes later the pressure was 0.2 torr and maintained at that pressure for 20 minutes before discharging the ingredients and pelletizing the material in its amorphous form.
  • This amorphous pelletized material was combined with several other similarly produced batches and then solid phase polymerized in a batch rotating vacuum vessel at 0.1 mmHg and 230° C. until a 0.802 I.V. (dl/gm) was reached.
  • the amount of lithium sulfoisophthalate was varied for the resulting mole percentages.
  • the amount of lithium sulfoisophthalate reported in the tables is based upon measuring the amount sulfur in the polymer using X-RAY and not upon the amount charged.
  • Crystallizable polyester resin was produced essentially as described in Example 1 except without the addition of LiSIPA and with adjustments to the toner levels to yield about the same polymer color as made in Example 1.
  • Resin was batch SSP as described in Example 1 and color data was measured. Hunter L* color was measured on the resin using a HunterLab ColorQuest XE. Results are reported in Table 1.
  • Controls were also produced following the procedures of Examples 1 and 2 without the addition of TEP, designated as 1a and 2a in Table 1 below.
  • the small change in L* color when Li(SIPA) is added indicates no precipitated antimony.
  • Crystallizable polyester resin was produced as described in Example 1.
  • the resin was batch solid state polymerized as described in Example 1.
  • Preforms were then produced and ground and air dried at 1 77° C. for 6 hours in SSP batch scale reactors to simulate a recycle process.
  • the Hunter b* color was measured on the ground performs.
  • Preform colors were measured using a HunterLab ColorQuest XE. The results are reported in Table 2.
  • Crystallizable polyester resin was produced as described in Example 3, however no TEP was added as a stabilizer. Preforms were produced and ground as described in Example 3. The Hunter b* color was measured on the ground performs. Preform colors were measured using a HunterLab ColorQuest XE. The results are reported in Table 2.
  • the HunterLab ColorQuest XE Spectrocolorimeter Test Method was used to measure L*, a* and b* colors on the resin. Following the instruction manual, and using the appropriate specimen holder each sample is tested in four different places. Upon completion of the test, the software is capable of displaying, saving, and printing an average and standard deviation for the requested customer defined scales and parameters.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Polyesters Or Polycarbonates (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
US12/196,499 2007-08-23 2008-08-22 Phosphite stabilizers for ionomeric polyester compounds Abandoned US20090054567A1 (en)

Priority Applications (2)

Application Number Priority Date Filing Date Title
US12/196,499 US20090054567A1 (en) 2007-08-23 2008-08-22 Phosphite stabilizers for ionomeric polyester compounds
US12/944,065 US8063124B2 (en) 2007-08-23 2010-11-11 Phosphite stabilizers for ionomeric polyester compounds

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US95770507P 2007-08-23 2007-08-23
US9086408P 2008-08-21 2008-08-21
US9074408P 2008-08-21 2008-08-21
US12/196,499 US20090054567A1 (en) 2007-08-23 2008-08-22 Phosphite stabilizers for ionomeric polyester compounds

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US12/944,065 Division US8063124B2 (en) 2007-08-23 2010-11-11 Phosphite stabilizers for ionomeric polyester compounds

Publications (1)

Publication Number Publication Date
US20090054567A1 true US20090054567A1 (en) 2009-02-26

Family

ID=39986444

Family Applications (3)

Application Number Title Priority Date Filing Date
US12/196,441 Active 2030-09-06 US8436080B2 (en) 2007-08-23 2008-08-22 Composition for maintaining good color when thermally treating polyester-polyamide blends
US12/196,499 Abandoned US20090054567A1 (en) 2007-08-23 2008-08-22 Phosphite stabilizers for ionomeric polyester compounds
US12/944,065 Expired - Fee Related US8063124B2 (en) 2007-08-23 2010-11-11 Phosphite stabilizers for ionomeric polyester compounds

Family Applications Before (1)

Application Number Title Priority Date Filing Date
US12/196,441 Active 2030-09-06 US8436080B2 (en) 2007-08-23 2008-08-22 Composition for maintaining good color when thermally treating polyester-polyamide blends

Family Applications After (1)

Application Number Title Priority Date Filing Date
US12/944,065 Expired - Fee Related US8063124B2 (en) 2007-08-23 2010-11-11 Phosphite stabilizers for ionomeric polyester compounds

Country Status (12)

Country Link
US (3) US8436080B2 (pt)
EP (1) EP2181152B1 (pt)
JP (1) JP5264909B2 (pt)
KR (1) KR101524118B1 (pt)
CN (1) CN101784598A (pt)
AU (1) AU2008288788B2 (pt)
BR (1) BRPI0815299B1 (pt)
CA (1) CA2695466C (pt)
MX (1) MX2010002103A (pt)
RU (1) RU2480493C2 (pt)
WO (1) WO2009026555A1 (pt)
ZA (1) ZA201000481B (pt)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20100233405A1 (en) * 2009-03-13 2010-09-16 Ciba Corporation Stabilized Blends of Polyester and Polyamide
WO2010103030A2 (en) 2009-03-13 2010-09-16 Basf Se Stabilized blends of polyester and polyamide
US20110057349A1 (en) * 2007-08-23 2011-03-10 Heater Paul Lewis Phosphite stabilizers for ionomeric polyester compounds
WO2013025784A3 (en) * 2011-08-16 2013-04-11 Oster Timothy Salts of 5-sulfoisophthalic acid and method of making same
US9193677B2 (en) 2011-03-02 2015-11-24 Futurefuel Chemical Company Metal salts of a dialkyl ester of 5-sulfoisophthalic acid and method of preparing same
US9212133B2 (en) 2011-08-29 2015-12-15 Futurefuel Chemical Company 5-sulfoisophthalic acid salts and process for the preparation thereof
US9359292B2 (en) 2009-10-20 2016-06-07 Futurefuel Chemical Company Use of an acetic acid/water solvent mixture for the preparation of low-sulfate 5-sulfoisophthalic acid, mono-lithium salt from 5-sulfoisophthalic acid

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB2549428B (en) 2015-01-06 2021-12-08 Lawter Inc Polyamide resins for coating of sand or ceramic proppants used in hydraulic fracturing

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6001910A (en) * 1999-04-09 1999-12-14 National Starch And Chemical Investment Holding Corporation Use of anionic or cationic plasticizers with sulfonated polyesters in hot melt formulations
US6066694A (en) * 1998-03-04 2000-05-23 General Electric Company Polyester molding composition
US20010009944A1 (en) * 1998-06-30 2001-07-26 General Electric Company Polyester molding composition
US20020173591A1 (en) * 2001-04-06 2002-11-21 Chisholm Bert Ja Polyester polyamide molding composition
US6500895B1 (en) * 2000-10-13 2002-12-31 General Electric Company Thermoplastic blend comprising poly(arylene ether) and polyamide
US20040013833A1 (en) * 2002-03-21 2004-01-22 Lee Robert A. Compatibilized polyester/polyamide blends
US20070135586A1 (en) * 2005-12-09 2007-06-14 Shreyas Chakravarti Polyamide blend compositions formed article and process thereof
US20080076841A1 (en) * 2006-09-11 2008-03-27 Graham Packaging Company, Lp Phosphorous containing reprocessed polymer materials, articles formed thereof, and methods of forming such articles
US20090054601A1 (en) * 2007-08-23 2009-02-26 Guliz Arf Elliott Composition for maintaining good color when thermally treating polyester-polyamide blends

Family Cites Families (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS50105755A (pt) * 1974-01-28 1975-08-20
US4680371A (en) * 1986-02-25 1987-07-14 Celanese Corporation Preparation of aromatic polyester with improved stability by addition of phosphite during preparation
AU628651B2 (en) * 1989-10-13 1992-09-17 Idemitsu Kosan Co. Ltd Styrene polymer composition
US5138024A (en) * 1991-01-25 1992-08-11 Eastman Kodak Company Modified polyester useful as photographic roll film support
US5296550A (en) * 1991-11-01 1994-03-22 Enichem S.P.A. Impact modified polyester blends with improved polymer compatibility
TW297822B (pt) * 1994-04-13 1997-02-11 Ciba Geigy Ag
US6437054B1 (en) * 1999-02-17 2002-08-20 General Electric Company Composition of polyester sulfonate salt ionomer, polyamide and polyepoxide
JP2002294056A (ja) * 2001-01-25 2002-10-09 Mitsubishi Chemicals Corp ポリエステル樹脂組成物及びそれからなる射出ブローボトル
US6908650B2 (en) * 2001-03-02 2005-06-21 Ciba Specialty Chemicals Corporation Polyester and polyamide compositions of low residual aldehyde content
US6479619B1 (en) * 2001-03-15 2002-11-12 E. I. Du Pont De Nemours And Company Sulfoisophthalic acid solution process therewith
JP4256754B2 (ja) * 2002-09-27 2009-04-22 富士フイルム株式会社 ポリエステル樹脂組成物
JP4677726B2 (ja) * 2004-03-01 2011-04-27 東レ株式会社 ポリエステル組成物及びそれからなる繊維
DK2159028T3 (da) * 2004-05-18 2013-03-18 M & G Polimeri Italia Spa Ruminddelte resinpellets og fremgangsmåde til termisk at behandle nævnte pellets
US8465818B2 (en) * 2005-10-07 2013-06-18 M & G Usa Corporation Polyamides and polyesters blended with a lithium salt interfacial tension reducing agent
KR101323835B1 (ko) * 2005-10-25 2013-10-31 엠 앤드 지 폴리메리 이탈리아 에스.피.에이. 폴리에스테르 및 폴리아미드의 동시 고체상 중합을 위한안정한 폴리아미드

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6066694A (en) * 1998-03-04 2000-05-23 General Electric Company Polyester molding composition
US20010009944A1 (en) * 1998-06-30 2001-07-26 General Electric Company Polyester molding composition
US6001910A (en) * 1999-04-09 1999-12-14 National Starch And Chemical Investment Holding Corporation Use of anionic or cationic plasticizers with sulfonated polyesters in hot melt formulations
US6500895B1 (en) * 2000-10-13 2002-12-31 General Electric Company Thermoplastic blend comprising poly(arylene ether) and polyamide
US20020173591A1 (en) * 2001-04-06 2002-11-21 Chisholm Bert Ja Polyester polyamide molding composition
US20040013833A1 (en) * 2002-03-21 2004-01-22 Lee Robert A. Compatibilized polyester/polyamide blends
US20070135586A1 (en) * 2005-12-09 2007-06-14 Shreyas Chakravarti Polyamide blend compositions formed article and process thereof
US20080076841A1 (en) * 2006-09-11 2008-03-27 Graham Packaging Company, Lp Phosphorous containing reprocessed polymer materials, articles formed thereof, and methods of forming such articles
US20090054601A1 (en) * 2007-08-23 2009-02-26 Guliz Arf Elliott Composition for maintaining good color when thermally treating polyester-polyamide blends

Cited By (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20110057349A1 (en) * 2007-08-23 2011-03-10 Heater Paul Lewis Phosphite stabilizers for ionomeric polyester compounds
US8063124B2 (en) * 2007-08-23 2011-11-22 M&G Usa Corporation Phosphite stabilizers for ionomeric polyester compounds
WO2010103023A1 (en) 2009-03-13 2010-09-16 Basf Se Stabilized blends of polyester and polyamide
WO2010103030A2 (en) 2009-03-13 2010-09-16 Basf Se Stabilized blends of polyester and polyamide
US20100233406A1 (en) * 2009-03-13 2010-09-16 Ciba Corporation Stabilized Blends of Polyester and Polyamide
US20100233405A1 (en) * 2009-03-13 2010-09-16 Ciba Corporation Stabilized Blends of Polyester and Polyamide
US8440281B2 (en) 2009-03-13 2013-05-14 Basf Se Stabilized blends of polyester and polyamide
US9359292B2 (en) 2009-10-20 2016-06-07 Futurefuel Chemical Company Use of an acetic acid/water solvent mixture for the preparation of low-sulfate 5-sulfoisophthalic acid, mono-lithium salt from 5-sulfoisophthalic acid
US9193677B2 (en) 2011-03-02 2015-11-24 Futurefuel Chemical Company Metal salts of a dialkyl ester of 5-sulfoisophthalic acid and method of preparing same
WO2013025784A3 (en) * 2011-08-16 2013-04-11 Oster Timothy Salts of 5-sulfoisophthalic acid and method of making same
US8772522B2 (en) * 2011-08-16 2014-07-08 Futurefuel Chemical Company Salts of 5-sulfoisophthalic acid and method of making same
US20130211116A1 (en) * 2011-08-16 2013-08-15 Timothy A. Oster Salts of 5-sulfoisophthalic acid and method of making same
US9212133B2 (en) 2011-08-29 2015-12-15 Futurefuel Chemical Company 5-sulfoisophthalic acid salts and process for the preparation thereof

Also Published As

Publication number Publication date
BRPI0815299B1 (pt) 2019-07-09
BRPI0815299A2 (pt) 2017-08-01
MX2010002103A (es) 2010-03-26
US8063124B2 (en) 2011-11-22
RU2010110807A (ru) 2011-09-27
CA2695466A1 (en) 2009-02-26
BRPI0815299A8 (pt) 2017-10-10
AU2008288788B2 (en) 2013-07-04
EP2181152A1 (en) 2010-05-05
US20090054601A1 (en) 2009-02-26
US20110057349A1 (en) 2011-03-10
EP2181152B1 (en) 2013-10-30
ZA201000481B (en) 2011-03-30
KR20100080898A (ko) 2010-07-13
CA2695466C (en) 2016-06-07
AU2008288788A1 (en) 2009-02-26
KR101524118B1 (ko) 2015-05-29
JP2010537007A (ja) 2010-12-02
CN101784598A (zh) 2010-07-21
RU2480493C2 (ru) 2013-04-27
WO2009026555A1 (en) 2009-02-26
US8436080B2 (en) 2013-05-07
JP5264909B2 (ja) 2013-08-14

Similar Documents

Publication Publication Date Title
US8063124B2 (en) Phosphite stabilizers for ionomeric polyester compounds
JP2010537007A5 (pt)
EP2271710B1 (en) Copper containing polyester-polyamide compositions
EP2181158B1 (en) Polyester-polyamide blends maintaining good color under thermal treatment
US9540507B2 (en) Composition for maintaining good color when thermally treating polyester-polyamide blends
US11141886B2 (en) Color control of polyester-cobalt compounds and polyester-cobalt compositions
US20130072603A1 (en) Color control of polyester-cobalt compounds and polyester-cobalt compositions

Legal Events

Date Code Title Description
AS Assignment

Owner name: M & G USA CORPORATION,WEST VIRGINIA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:HEATER, PAUL L;REEL/FRAME:024197/0175

Effective date: 20080822

Owner name: M & G POLIMERI ITALIA S.P.A.,ITALY

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:HEATER, PAUL L;REEL/FRAME:024197/0175

Effective date: 20080822

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION

AS Assignment

Owner name: TRIMONT REAL ESTATE ADVISORS, LLC, GEORGIA

Free format text: SECURITY INTEREST;ASSIGNOR:M&G USA CORPORATION;REEL/FRAME:044930/0245

Effective date: 20171220

AS Assignment

Owner name: FE POLYTECH, LLC, DELAWARE

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:M&G USA CORPORATION;REEL/FRAME:045567/0652

Effective date: 20180301

Owner name: M&G USA CORPORATION, WEST VIRGINIA

Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:UNITED STATES BANKRUPTCY COURT FOR DISTRICT OF DELAWARE;REEL/FRAME:045567/0597

Effective date: 20180201

AS Assignment

Owner name: APG POLYTECH, LLC, DELAWARE

Free format text: CHANGE OF NAME;ASSIGNOR:FE POLYTECH, LLC;REEL/FRAME:045819/0235

Effective date: 20180323

AS Assignment

Owner name: M&G USA CORPORATION, DELAWARE

Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:TRIMONT REAL ESTATE ADVISORS, LLC;REEL/FRAME:046067/0127

Effective date: 20180301

AS Assignment

Owner name: M&G USA CORPORATION, WEST VIRGINIA

Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:TRIMONT REAL ESTATE ADVISORS, LLC;REEL/FRAME:048000/0890

Effective date: 20181228