US20070251603A1 - Novel surface aesthetics employing magnetic particles - Google Patents

Novel surface aesthetics employing magnetic particles Download PDF

Info

Publication number
US20070251603A1
US20070251603A1 US11/412,178 US41217806A US2007251603A1 US 20070251603 A1 US20070251603 A1 US 20070251603A1 US 41217806 A US41217806 A US 41217806A US 2007251603 A1 US2007251603 A1 US 2007251603A1
Authority
US
United States
Prior art keywords
solid surface
magnetic
particles
surface material
anisotropic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US11/412,178
Other languages
English (en)
Inventor
Barry Olson
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
EIDP Inc
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to US11/412,178 priority Critical patent/US20070251603A1/en
Assigned to E. I. DU PONT DE NEMOURS AND COMPANY reassignment E. I. DU PONT DE NEMOURS AND COMPANY ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: OLSON, BARRY D.
Priority to MX2008013509A priority patent/MX2008013509A/es
Priority to EP07776219A priority patent/EP2010371B1/en
Priority to PCT/US2007/010079 priority patent/WO2007127275A2/en
Priority to NZ570737A priority patent/NZ570737A/en
Priority to CNA200780014770XA priority patent/CN101432125A/zh
Priority to KR1020087028757A priority patent/KR20080110935A/ko
Priority to JP2009507790A priority patent/JP5183624B2/ja
Priority to CA002646148A priority patent/CA2646148A1/en
Priority to AU2007243373A priority patent/AU2007243373A1/en
Publication of US20070251603A1 publication Critical patent/US20070251603A1/en
Priority to AU2012203256A priority patent/AU2012203256A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C70/00—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts
    • B29C70/58—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts comprising fillers only, e.g. particles, powder, beads, flakes, spheres
    • B29C70/64—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts comprising fillers only, e.g. particles, powder, beads, flakes, spheres the filler influencing the surface characteristics of the material, e.g. by concentrating near the surface or by incorporating in the surface by force
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C70/00—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts
    • B29C70/04—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts comprising reinforcements only, e.g. self-reinforcing plastics
    • B29C70/06—Fibrous reinforcements only
    • B29C70/10—Fibrous reinforcements only characterised by the structure of fibrous reinforcements, e.g. hollow fibres
    • B29C70/12—Fibrous reinforcements only characterised by the structure of fibrous reinforcements, e.g. hollow fibres using fibres of short length, e.g. in the form of a mat
    • B29C70/14—Fibrous reinforcements only characterised by the structure of fibrous reinforcements, e.g. hollow fibres using fibres of short length, e.g. in the form of a mat oriented
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2995/00—Properties of moulding materials, reinforcements, fillers, preformed parts or moulds
    • B29K2995/0003—Properties of moulding materials, reinforcements, fillers, preformed parts or moulds having particular electrical or magnetic properties, e.g. piezoelectric
    • B29K2995/0008—Magnetic or paramagnetic

Definitions

  • This invention relates to a process for producing a decorative surfacing material by selective orientation of decorative fillers by magnetic means.
  • a solid surface material is understood in its normal meaning and represents a uniform, non-gel coated, non-porous, three dimensional solid material containing polymer resin and particulate filler, such material being particularly useful in the building trades for kitchen countertops, sinks, wall coverings, and furniture surfacing wherein both functionality and an attractive appearance are necessary.
  • a well-known example of a solid surface material is Corian® produced by E. I. DuPont de Nemours and Company.
  • a number of design aesthetics are heretofore known in solid surface materials, such as granite and marble, but they have a mostly two-dimensional appearance.
  • thermoset processes such as sheet casting, cell casting, injection molding, or bulk molding.
  • the decorative qualities of such products are greatly enhanced by incorporating pigments and colored particles such that the composite resembles natural stone.
  • the range of patterns commercially available are constrained by the intermediates and processes currently used in the manufacturing of such materials.
  • Solid surface materials in their various applications serve both functional and decorative purposes.
  • the incorporation of various attractive and/or unique decorative patterns into solid surface materials enhances its utility.
  • Such patterns constitute intrinsically useful properties, which differentiate one product from another.
  • the same principle applies to naturally occurring materials such as wood, marble, and granite whose utility, for example in furniture construction, is enhanced by certain naturally occurring patterns, e.g., grain, color variations, veins, strata, inclusions, and others.
  • Commercially manufactured solid surface materials often incorporate decorative patterns intended to imitate or resemble naturally occurring patterns in granite or marble.
  • certain decorative patterns and/or categories of decorative patterns have not previously been incorporated in solid surface materials.
  • Decorative patterns that have been previously achieved in traditional solid surface manufacturing typically employ one of three methods:
  • the invention is a process for forming a decorative pattern in a surface of a solid surface material containing magnetic anisotropic particles comprising the steps of orienting at least a majority of the magnetic anisotropic particle in a flowable solid surface material, inducing a magnetic field in a portion of surface areas of the flowable solid surface material to change the orientation of magnetic particles in the magnetic field, and solidifying the flowable solid surface material.
  • FIG. 1 is cross-section of a sheet of material with oriented anisotropic particulate filler.
  • FIG. 2 is a cross-section of a sheet of material with regions of reoriented anisotropic particulate filler.
  • FIG. 3 is an illustration of the pattern created when traversing a composition containing anisotropic particulate filler that is magnetic in character with a magnetic field.
  • the present invention is a process for forming a decorative pattern in solid surface materials with magnetic anisotropic particles by orienting the anisotropic particulate filler.
  • the magnetic anisotropic particulate filler in an uncured solid surface composition may be oriented by various means wherein at least some of the orientable particles are in a common orientation and subsequently reorienting, by various means, at least some of the oriented magnetic anisotropic particles (i.e., flakes) in specific regions to form a decorative pattern in solid surface materials.
  • Another embodiment of the invention comprises a generally unoriented filler in the uncured solid surface composition and subsequently orienting, by various means, at least some of the unoriented magnetic anisotropic particles (i.e., flakes) in specific regions to form a decorative pattern.
  • the pattern is created by differences in anisotropic particle orientation between adjacent regions within the solid surface material. The process will create an aesthetic three-dimensional appearance in the solid surface material by the way ambient light differentially interacts with the adjacent regions due to particle orientation.
  • Solid surface compositions useful in the present invention are not specifically limited as long as they are flowable under process conditions and can be formed into a solid surface material.
  • the polymerizable composition may be a casting syrup as disclosed in U.S. Pat. No. 3,474,081 to Bosworth, and cast on a moving belt as disclosed in U.S. Pat. No. 3,528,131 to Duggins.
  • the polymerizable compositions may be made by a process in which compression molding thermosettable formulations are made and processed as described in Weberg et al, in U.S. Pat. No. 6,203,911 and the compression molding compound is put through an extrusion process step.
  • Solid surface formulations could also include various thermoplastic resins capable of compression molding.
  • the polymerizable composition may be made and extruded according to the disclosure of Beauchemin et al in U.S. Pat. No. 6,476,111.
  • orientable magnetic anisotropic aesthetic-enhancement particles are included in the polymerizable compositions, as described hereinafter.
  • Anisotropic pigments, reflective particles, fibers, films, and finely divided solids (or dyes) may be used as the aesthetic-enhancement particles to highlight orientation effects.
  • the translucency of the resulting solid surface material can be manipulated to give a desired aesthetic. Different colors, reflectivity, and translucency can be achieved by combining different amounts of enhancement particles, fillers, and colorants, and the degree to which the anisotropic filler particles are reoriented.
  • Magnetic anisotropic particulate fillers useful in the present invention are not specifically limited as long as they are magnetic in character, and have an aspect ratio that is sufficiently high to promote particle orientation during material processing and have an appearance that changes relative to the orientation to the material and the observer.
  • Preferred magnetic anisotropic particulate fillers include materials that have an aspect ratio that is sufficiently high to promote particle orientation during material processing and have an appearance that changes relative to the orientation to the material and the observer.
  • the aspect ratios of suitable enhancement particles cover a broad range, e.g. metallic flakes (20-100), mica (10-70), metallized glass fiber (3-25), metallized aramid fiber (100-500). These visual effects may be due to angle dependent reflectivity, angle dependent color absorption/reflection, or visible shape.
  • These magnetic particles may be plate-like, fibers, or ribbons.
  • the aspect ratio is the ratio of the greatest length of a particle to its thickness. Generally the aspect ratio will be at least 3, and more generally at least 20.
  • Plate-like materials have two dimensions significantly larger than the third dimension. Examples of plate-like materials include, but are not limited to: mica, synthetic mica, metal flakes, alumina, synthetic materials such as ultra-thin, multi-layer interference flakes (e.g., Chromaflair® from Flex Products).
  • the surfaces of the plate-like substrate are coated with various metal oxides or pigments to control color and light interference effects, and add magnetic properties. Some materials appear to be different colors at different angles. Metal flakes with magnetic properties are found to be especially useful. Exemplary metal flakes for magnetic reorientation include steel, stainless steel, nickel, and combinations thereof.
  • Metal-coated fibers have one dimension that is significantly larger than the other two dimensions.
  • fibers include, metal, polymer, carbon, glass, and ceramic.
  • Ribbons have one dimension that is significantly larger than the other two, but the second dimension is noticeably larger than the third. Examples of ribbons would include metals and polymer films.
  • the polymeric compositions may include particulate or fibrous fillers that are not isotropic, nor magnetic, nor aesthetic.
  • fillers increase the hardness, stiffness, or strength of the final article relative to the pure polymer or combination of pure polymers.
  • the filler can provide other attributes to the final article. For example, it can provide other functional properties, such as flame retardation, or it may serve a decorative purpose and modify the aesthetic.
  • Some representative fillers include alumina, alumina trihydrate (ATH), alumina monohydrate, aluminum hydroxide, aluminum oxide, aluminum sulfate, aluminum phosphate, aluminum silicate, Bayer hydrate, borosilicates, calcium sulfate, calcium silicate, calcium phosphate, calcium carbonate, calcium hydroxide, calcium oxide, apatite, glass bubbles, glass microspheres, glass fibers, glass beads, glass flakes, glass powder, glass spheres, barium carbonate, barium hydroxide, barium oxide, barium sulfate, barium phosphate, barium silicate, magnesium sulfate, magnesium silicate, magnesium phosphate, magnesium hydroxide, magnesium oxide, kaolin, montmorillonite, bentonite, pyrophyllite, mica, gypsum, silica (including sand), ceramic microspheres, ceramic particles, ceramic whiskers, powder talc, titanium dioxide, diatomaceous earth, wood flour, borax, or combinations thereof.
  • the fillers can be optionally coated with sizing agents, for example, silane (meth)acrylate which is commercially available from OSI Specialties (Friendly, W. Va.) as Silane 8 Methacrylate A-174.
  • sizing agents for example, silane (meth)acrylate which is commercially available from OSI Specialties (Friendly, W. Va.) as Silane 8 Methacrylate A-174.
  • the filler is present in the form of small particles, with an average particle size in the range of from about 5-500 microns, and can be present in amounts of up to 65% by weight of the polymerizable composition.
  • the nature of the filler particles has a pronounced effect on the aesthetics of the final article.
  • the refractive index of the filler is closely matched to that of the polymerizable component, the resulting final article has a translucent appearance.
  • the refractive index deviates from that of the polymerizable component, the resulting appearance is more opaque.
  • ATH is often a preferred filler for poly(methylmethacrylate) (PMMA) systems because the index of refraction of ATH is close to that of PMMA.
  • PMMA poly(methylmethacrylate)
  • Alumina Al 2 O 3
  • Fibers improve mechanical properties.
  • Some functional fillers are antioxidants (such as ternary or aromatic amines, Irganox® (Octadecyl 3,5-Di-(tert)-butyl-4-hydroxyhydrocinnamate) supplied by Ciba Specialty Chemicals Corp., and sodium hypophosphites, flame retardants (such as halogenated hydrocarbons, mineral carbonates, hydrated minerals, and antimony oxide), UV stabilizers (such as Tinuvin® supplied by Ciba Geigy), stain-resistant agents such as Teflon®, stearic acid, and zinc stearate, or combinations thereof.
  • antioxidants such as ternary or aromatic amines, Irganox® (Octadecyl 3,5-Di-(tert)-butyl-4-hydroxyhydrocinnamate) supplied by Ciba Specialty Chemicals Corp., and sodium hypophosphites, flame retardants (such as halogenated hydrocarbons, mineral carbon
  • the orientation of the anisotropic particulate fillers may be done by taking advantage of the tendency of the particles to align themselves during laminar flow of the polymerizable matrix, as shown schematically in FIG. 1 wherein the oriented anisotropic particles ( 200 ) are shown generally parallel to the surface of a sheet ( 100 ).
  • the laminar flow may be created by a number of process methods, depending on the rheological nature of the polymerizable composition.
  • Flowable compositions may have the anisotropic particulate fillers oriented by casting on a moving belt, with optional employment of a doctor blade.
  • Extrudable uncured solid surface molding compositions may employ extrusion through a die plate, with no limitations on the die geometry.
  • Calender rolls may be used as the primary means of anisotropic particulate filler orientation, or added as an additional.
  • the additional calendering step may be for the purpose of orienting the anisotropic particulate filler or may be for any other purpose, such as gauging the thickness of the material or adding a texture to the surface. In general at least 70% of the anisotropic particles, and more generally, at least 90% have the same orientation.
  • An aesthetic is created in the uncured solid surface composition by selective reorientation of the anisotropic particles.
  • the reoriented particles do not have the same orientation as the bulk of the material after selective reorientation, which results in the region of the reorientation ( 400 ) appearing visually different as shown in FIG. 2 .
  • the actual method of selected reorientation can vary depending on the nature of the uncured solid surface composition and the desired aesthetic.
  • the magnetic anisotropic particles have magnetic properties and are reoriented by traversing the uncured solid surface composition with magnetic fields.
  • the strength of the magnetic field is not critical provided the strength is sufficient to disrupt or change filler orientation in a localized volume of the surface.
  • a magnetic field of 35 gauss or less is suitable when applied over an extended time during the casting cure.
  • a magnetic field of 250 gauss or more is typically used for short exposure times, including exposures of less than one second. Pattern orientation through the full thickness of a 1 ⁇ 2-inch thick casting using approximate one-second exposure is produced with larger magnetic fields with mid thickness field strengths of approximately 250 gauss.
  • the uncured solid surface composition may optionally be textured after the reorientation of the anisotropic particles.
  • the uncured solid surface composition may be flattened to give a smooth texture, or have an aesthetic or functional texture added.
  • a preferred means of texturing is by calender roll.
  • the uncured composition is solidified.
  • Solidifying of the polymerizable composition after the reorientation of the anisotropic particles is done according to what polymer system is used. Most solid surface materials manufactured by thermoset processes, such as sheet casting, cell casting, injection molding, or bulk molding will use cure agents that when thermally activated will generate free radicals which then initiate the desired polymerization reactions. Either a chemically-activated thermal initiation or a purely temperature-driven thermal initiation to cure the acrylic polymerizable fraction may be employed herein. Both cure systems are well known in the art. Solidifying of thermoplastic embodiments of the invention, such as extruded thermoplastics, is accomplished by allowing the composition to cool below the glass transition temperature.
  • the mixture was then evacuated under vacuum (24-25 in Hg) using a pump and a suitable condensing vapor trap. After mixing and evacuating for approximately 3 minutes, 2.58 grams of calcium hydroxide slurry (34% in syrup) and 1.33 grams of ethylene glycol dimercaptoacetate were added using syringes. After 45 seconds of additional mixing and evacuation, the mixture was poured into a container of square design to form a layer of approximately 0.5-inch thickness. The container had a 0.040-inch thick metal bottom made of AISI 301 stainless steel that had been demagnetized prior to the pour. It took approximately 20 seconds to transfer the mixed material from the mixer and pour it into the container.
  • the casting was then traversed with a magnetic field, creating a linear pattern.
  • the magnetic field was created with two electromagnets with 0.5-inch diameter by 1.27-inch length inner cores made of 1215 steel.
  • the electromagnet coils consisted of 4,000 turns, a coil winding density of approximately 3200 turns/inch, and a coil resistance of 150 ohms.
  • the coil outer diameter was approximately 1 and 5/16-inches.
  • the centerlines of the cylindrical electromagnets were aligned and the ends of the cores were spaced 0.060-inches from the bottom of the casting container and from the top of the poured casting.
  • the electromagnet coils were wired with opposite polarity and powered with 0.5 amperes of direct current.
  • the electromagnets were positioned around the casting, the power was turned on, and the electromagnets were traversed across the casting at a speed of approximately 4.6 inches per second.
  • the power was turned on approximately 120 seconds after the calcium hydroxide slurry and ethylene glycol dimercaptoacetate were injected.
  • the electromagnet motion was stopped and the current was turned off at the end of the linear traverse.
  • the electromagnets were then moved away from the container, insulation was placed on top of the casting and underneath the casting container, and the casting was allowed to cure.
  • the electromagnet traverse created a linear pattern of darkened bands relative to the lighter background of the casting.
  • the pattern consists of an approximate 0.4-inch wide darkened line aligned with the centerline of the electromagnet traverse.
  • Two background colored lines approximately 0.15-inches wide parallel the 0.4-inch darkened centerline.
  • Two more darkened colored lines approximately 0.2-inches wide parallel the 0.15-inches lines.
  • the patterns around both end points of the electromagnet traverse are semicircular.
  • the semicircular patterns have darkened centers with perimeter semicircular rings around the end centers; background colored inner rings of 0.15-inch radial width and darkened outer rings of 0.2-inch radial width.
  • Example 1 The metal-bottomed container described in Example 1 was demagnetized and subsequently magnetized by using the electromagnet system and motion-traverse sequence described in Example 1. A casting mixture was weighed out, mixed, and evacuated in the same manner and sequence as done in Example 1. The mixture was poured into this magnetized container approximately 20 seconds after mixing was stopped, analogous to Example 1. Insulation was placed on top of the casting and underneath the casting container and the casting was allowed to cure.
  • the magnetic field imparted to the container was sufficient to produce the same linear particle reorientation pattern in the casting as described in Example 1.

Landscapes

  • Engineering & Computer Science (AREA)
  • Chemical & Material Sciences (AREA)
  • Composite Materials (AREA)
  • Mechanical Engineering (AREA)
  • Textile Engineering (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
  • Casting Or Compression Moulding Of Plastics Or The Like (AREA)
  • Hard Magnetic Materials (AREA)
  • Polymerisation Methods In General (AREA)
US11/412,178 2006-04-26 2006-04-26 Novel surface aesthetics employing magnetic particles Abandoned US20070251603A1 (en)

Priority Applications (11)

Application Number Priority Date Filing Date Title
US11/412,178 US20070251603A1 (en) 2006-04-26 2006-04-26 Novel surface aesthetics employing magnetic particles
AU2007243373A AU2007243373A1 (en) 2006-04-26 2007-04-24 Process for forming decorative patterns by orienting magnetic particles
NZ570737A NZ570737A (en) 2006-04-26 2007-04-24 Process for forming decorative patterns by orienting magnetic particles in flowable material, typically resin, and allowing material to solidify
EP07776219A EP2010371B1 (en) 2006-04-26 2007-04-24 Novel surface aesthetics employing magnetic particles
PCT/US2007/010079 WO2007127275A2 (en) 2006-04-26 2007-04-24 Process for forming decorative patterns by orienting magnetic particles
MX2008013509A MX2008013509A (es) 2006-04-26 2007-04-24 Proceso para formar configuraciones decorativas por la orientacion de particulas magneticas.
CNA200780014770XA CN101432125A (zh) 2006-04-26 2007-04-24 使用磁颗粒的新型表面艺术
KR1020087028757A KR20080110935A (ko) 2006-04-26 2007-04-24 자성 입자를 배향시킴으로써 장식 패턴을 형성하는 방법
JP2009507790A JP5183624B2 (ja) 2006-04-26 2007-04-24 磁性粒子を配向させることにより加飾パターンを形成する方法
CA002646148A CA2646148A1 (en) 2006-04-26 2007-04-24 Process for forming decorative patterns by orienting magnetic particles
AU2012203256A AU2012203256A1 (en) 2006-04-26 2012-06-01 Process for forming decorative patterns by orienting magnetic particles

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US11/412,178 US20070251603A1 (en) 2006-04-26 2006-04-26 Novel surface aesthetics employing magnetic particles

Publications (1)

Publication Number Publication Date
US20070251603A1 true US20070251603A1 (en) 2007-11-01

Family

ID=38606481

Family Applications (1)

Application Number Title Priority Date Filing Date
US11/412,178 Abandoned US20070251603A1 (en) 2006-04-26 2006-04-26 Novel surface aesthetics employing magnetic particles

Country Status (10)

Country Link
US (1) US20070251603A1 (https=)
EP (1) EP2010371B1 (https=)
JP (1) JP5183624B2 (https=)
KR (1) KR20080110935A (https=)
CN (1) CN101432125A (https=)
AU (2) AU2007243373A1 (https=)
CA (1) CA2646148A1 (https=)
MX (1) MX2008013509A (https=)
NZ (1) NZ570737A (https=)
WO (1) WO2007127275A2 (https=)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20090072185A1 (en) * 2001-07-31 2009-03-19 Jds Uniphase Corporation Anisotropic Magnetic Flakes
WO2009135506A1 (en) * 2008-05-07 2009-11-12 Actega Rhenania Gmbh Magnetic pigment coatings, laminates and method of production thereof
US8523236B2 (en) 2011-02-07 2013-09-03 Jenny Leary Magnetic field surface image method, kit and product
US20140199354A1 (en) * 2009-12-23 2014-07-17 Colgate-Palmolive Company Visually Patterned and Oriented Compositions
CN108451097A (zh) * 2018-03-23 2018-08-28 泉州冠拓鞋材有限公司 磁粉保健鞋面及其制作方法
CN116619772A (zh) * 2022-02-18 2023-08-22 科勒公司 包括铁质材料的模制固体表面
CN119824571A (zh) * 2025-03-17 2025-04-15 江苏金太阳纺织科技股份有限公司 一种玉石凉感纤维及其制备方法

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101283853B1 (ko) * 2009-02-27 2013-07-08 (주)엘지하우시스 자성반응물질을 포함하는 인조대리석 및 이의 제조방법
FR2985422B1 (fr) * 2012-01-10 2014-08-08 Oreal Composition cosmetique solide a effets magnetiques

Citations (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3474081A (en) * 1966-03-14 1969-10-21 Du Pont Methyl methacrylate polymer and process for making same
US3528131A (en) * 1968-12-19 1970-09-15 Du Pont Cast simulated marble building product and its manufacture
US6103361A (en) * 1997-09-08 2000-08-15 E. I. Du Pont De Nemours And Company Patterned release finish
US6203911B1 (en) * 1998-06-17 2001-03-20 E. I. Du Pont De Nemours And Company Thermoset volatile monomer molding compositions
US20020160194A1 (en) * 2001-04-27 2002-10-31 Flex Products, Inc. Multi-layered magnetic pigments and foils
US6476111B1 (en) * 2001-08-01 2002-11-05 E. I Du Pont De Nemours And Company Extrudable highly filled thermoplastic sheet composition
US6702967B2 (en) * 2001-07-27 2004-03-09 E. I. Du Pont De Nemours And Company Process for preparing decorative surface materials having a decorative pattern
US20040052976A1 (en) * 2000-01-24 2004-03-18 General Electric Company Article including particles oriented generally along an article surface and method for making
US20060150854A1 (en) * 2003-07-03 2006-07-13 Spica Holding S.A. Method and means for producing a magnetically induced design in a coating containing magnetic particles
US20060251754A1 (en) * 2003-07-25 2006-11-09 Peter Herring Methods and apparatus for forming a moulding comprising magnetic particles
US7588817B2 (en) * 2005-03-11 2009-09-15 Jds Uniphase Corporation Engraved optically variable image device

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH01259916A (ja) * 1988-04-11 1989-10-17 Toshiba Corp 成形用着色材料
JPH05192964A (ja) * 1992-01-22 1993-08-03 Kyushu Hitachi Maxell Ltd プラスチック成形品のパターン表出方法
DE10013617A1 (de) * 2000-03-18 2001-09-20 Hans Aussem Verfahren zur Herstellung eines Kunststoffteils mit mindestens einer marmorierten und/oder farbigen Sichtfläche
JP2005306992A (ja) * 2004-04-21 2005-11-04 Dainippon Ink & Chem Inc 機能性硬化膜

Patent Citations (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3474081A (en) * 1966-03-14 1969-10-21 Du Pont Methyl methacrylate polymer and process for making same
US3528131A (en) * 1968-12-19 1970-09-15 Du Pont Cast simulated marble building product and its manufacture
US6103361A (en) * 1997-09-08 2000-08-15 E. I. Du Pont De Nemours And Company Patterned release finish
US6203911B1 (en) * 1998-06-17 2001-03-20 E. I. Du Pont De Nemours And Company Thermoset volatile monomer molding compositions
US20040052976A1 (en) * 2000-01-24 2004-03-18 General Electric Company Article including particles oriented generally along an article surface and method for making
US20020160194A1 (en) * 2001-04-27 2002-10-31 Flex Products, Inc. Multi-layered magnetic pigments and foils
US6702967B2 (en) * 2001-07-27 2004-03-09 E. I. Du Pont De Nemours And Company Process for preparing decorative surface materials having a decorative pattern
US6476111B1 (en) * 2001-08-01 2002-11-05 E. I Du Pont De Nemours And Company Extrudable highly filled thermoplastic sheet composition
US20060150854A1 (en) * 2003-07-03 2006-07-13 Spica Holding S.A. Method and means for producing a magnetically induced design in a coating containing magnetic particles
US20060251754A1 (en) * 2003-07-25 2006-11-09 Peter Herring Methods and apparatus for forming a moulding comprising magnetic particles
US7588817B2 (en) * 2005-03-11 2009-09-15 Jds Uniphase Corporation Engraved optically variable image device

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
Definition of "pattern" accessed 12/17/2012 *

Cited By (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20090072185A1 (en) * 2001-07-31 2009-03-19 Jds Uniphase Corporation Anisotropic Magnetic Flakes
US9662925B2 (en) 2001-07-31 2017-05-30 Viavi Solutions Inc. Anisotropic magnetic flakes
US10242788B2 (en) 2007-03-21 2019-03-26 Viavi Solutions Inc. Anisotropic magnetic flakes
WO2009135506A1 (en) * 2008-05-07 2009-11-12 Actega Rhenania Gmbh Magnetic pigment coatings, laminates and method of production thereof
US20110117334A1 (en) * 2008-05-07 2011-05-19 ACTEGA RHENANANIA GmbH Magnetic Pigment Coatings, Laminates and Method of Production Thereof
US20140199354A1 (en) * 2009-12-23 2014-07-17 Colgate-Palmolive Company Visually Patterned and Oriented Compositions
US9408784B2 (en) * 2009-12-23 2016-08-09 Colgate-Palmolive Company Visually patterned and oriented compositions
US8523236B2 (en) 2011-02-07 2013-09-03 Jenny Leary Magnetic field surface image method, kit and product
CN108451097A (zh) * 2018-03-23 2018-08-28 泉州冠拓鞋材有限公司 磁粉保健鞋面及其制作方法
CN116619772A (zh) * 2022-02-18 2023-08-22 科勒公司 包括铁质材料的模制固体表面
EP4230378A1 (en) * 2022-02-18 2023-08-23 Kohler Co. Molded solid surfaces including ferrous material
US12472665B2 (en) 2022-02-18 2025-11-18 Kohler Co. Molded solid surfaces including ferrous material
CN119824571A (zh) * 2025-03-17 2025-04-15 江苏金太阳纺织科技股份有限公司 一种玉石凉感纤维及其制备方法

Also Published As

Publication number Publication date
JP2009535451A (ja) 2009-10-01
CN101432125A (zh) 2009-05-13
KR20080110935A (ko) 2008-12-19
NZ570737A (en) 2011-04-29
AU2012203256A1 (en) 2012-06-21
EP2010371A2 (en) 2009-01-07
WO2007127275A3 (en) 2007-12-21
WO2007127275A2 (en) 2007-11-08
EP2010371B1 (en) 2012-07-11
JP5183624B2 (ja) 2013-04-17
CA2646148A1 (en) 2007-11-08
MX2008013509A (es) 2008-10-28
AU2007243373A1 (en) 2007-11-08

Similar Documents

Publication Publication Date Title
EP2010371B1 (en) Novel surface aesthetics employing magnetic particles
EP1412166B1 (en) Decorative surface materials having a decorative pattern and process for preparing the same
AU2002322760A1 (en) Decorative surface materials having a decorative pattern and process for preparing the same
US7638189B2 (en) Artificial marble containing transparent chip using co-extrusion and process for preparing the same
KR100786003B1 (ko) 공압출 공법을 활용한 투명칩을 포함하는 인조대리석 및 이의 제조방법
KR20090018064A (ko) 고체 표면재의 표면에 장식 패턴을 형성하는 방법
WO2007127280A2 (en) Aesthetics in surfaces employing deformation and magnetic means
EP1414652B1 (en) Decorative materials having geometric patterns and process for preparing the same
KR100805636B1 (ko) 깊이감과 반짝이는 효과를 연출하는 고비중화 광반사칩,이의 제조방법 및 이를 포함하는 인조대리석

Legal Events

Date Code Title Description
AS Assignment

Owner name: E. I. DU PONT DE NEMOURS AND COMPANY, DELAWARE

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:OLSON, BARRY D.;REEL/FRAME:017928/0933

Effective date: 20060606

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION