US20070163737A1 - Porous filler or coating pigment of paper and cardboard and a method of manufacturing it - Google Patents

Porous filler or coating pigment of paper and cardboard and a method of manufacturing it Download PDF

Info

Publication number
US20070163737A1
US20070163737A1 US10/573,028 US57302804A US2007163737A1 US 20070163737 A1 US20070163737 A1 US 20070163737A1 US 57302804 A US57302804 A US 57302804A US 2007163737 A1 US2007163737 A1 US 2007163737A1
Authority
US
United States
Prior art keywords
starch
carbon dioxide
pressure
ester
foam
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US10/573,028
Other languages
English (en)
Inventor
Allan Johansson
Pia Qvintus-Leino
Petri Varjos
Soili Peltonen
Hannu Mikkonen
Mauno Miettinen
Saija Luukkanen
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Valtion Teknillinen Tutkimuskeskus
Original Assignee
Valtion Teknillinen Tutkimuskeskus
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from FI20035172A external-priority patent/FI20035172A0/fi
Application filed by Valtion Teknillinen Tutkimuskeskus filed Critical Valtion Teknillinen Tutkimuskeskus
Assigned to VALTION TEKNILLINEN TUTKIMUSKESKUS reassignment VALTION TEKNILLINEN TUTKIMUSKESKUS ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: JOHANSSON, ALLAN, QVINTUS-LEINO, PIA, LUUKKANEN, SAIJA, MIETTINEN, MAUNO, PELTONEN, SOILI, VARJOS, PETRI, MIKKONEN, HANNU
Publication of US20070163737A1 publication Critical patent/US20070163737A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
    • C08J9/30—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof by mixing gases into liquid compositions or plastisols, e.g. frothing with air
    • D—TEXTILES; PAPER
    • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
    • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
    • D21H17/00—Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution
    • D21H17/20—Macromolecular organic compounds
    • D21H17/21—Macromolecular organic compounds of natural origin; Derivatives thereof
    • D21H17/24—Polysaccharides
    • D21H17/28—Starch
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2201/00—Foams characterised by the foaming process
    • C08J2201/02—Foams characterised by the foaming process characterised by mechanical pre- or post-treatments
    • C08J2201/032—Impregnation of a formed object with a gas
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2303/00—Characterised by the use of starch, amylose or amylopectin or of their derivatives or degradation products
    • D—TEXTILES; PAPER
    • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
    • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
    • D21H19/00—Coated paper; Coating material
    • D21H19/36—Coatings with pigments
    • D21H19/38—Coatings with pigments characterised by the pigments
    • D21H19/42—Coatings with pigments characterised by the pigments at least partly organic
    • D—TEXTILES; PAPER
    • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
    • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
    • D21H21/00—Non-fibrous material added to the pulp, characterised by its function, form or properties; Paper-impregnating or coating material, characterised by its function, form or properties
    • D21H21/50—Non-fibrous material added to the pulp, characterised by its function, form or properties; Paper-impregnating or coating material, characterised by its function, form or properties characterised by form
    • D21H21/56—Foam

Definitions

  • the present invention relates to a starch-based pigment, according to the preamble of claim 1 .
  • the present invention also relates to a method according to the preamble of claim 2 , and to use according to claim 12 .
  • the printing paper qualities and coated cardboards used today comprise considerable amounts of inorganic minerals, either as fillers or as coating pigments. These cause problems in recycling of fibre, in paper burning and in composting.
  • the minerals also increase the weight of the paper product considerably, which is very significant in the production of for example printable packing materials.
  • Synthetic organic pigments are known, too. Usually they have good optical properties, which are based on their ability to scatter visible light. However, a disadvantage associated with known synthetic plastic pigments is that alone they are not suitable as coating or filler pigments for paper, instead they are usually used as doped in mineral pigments.
  • U.S. Pat. No. 6,582,509 presents a method in which an organic pigment is prepared by swelling starch granules to increase their volume (2-4 times the original) and plasticity, yet such that the granular structure is preserved.
  • the swelling takes place in water, below the gelatinizing temperature.
  • the volume and the shape stability of the granules are increased by cross-linking.
  • Their surface can be made hydrophobic, too.
  • Gas bubbles or cavities which have a light scattering property are formed inside the granules.
  • the bubbles are generated by evaporating water or a solvent, or by releasing absorbed gas, or by using solvents to displace absorbed water.
  • the dimensions of the cavities in the swelled and stabilized granules are 0.1-5 ⁇ m.
  • the published EP Application No. 1254939 describes a method of producing biopolymer-based nanoparticles by extruding a plasticized biopolymer, such as starch, in the presence of a crosslinking chemical.
  • the glue is prepared by reactive extrusion from starch, glycerol and glyoxal in the presence of water, and the result is a dispersion in water.
  • the sizes of the nanoparticles are ⁇ 1000 nm (50-250), and preferably the amylopectin percentage of the starch is high.
  • the latex is used as a glue in the production of corrugated cardboard.
  • the published International Application No. WO 00/69916 presents nanoparticles of biopolymers.
  • the average particle size of these nanoparticles is ⁇ 400 nm.
  • the biopolymer is either a starch, a starch derivative or a polymer blend containing at least 50% starch.
  • the cross-linking is achieved by using dialdehydes or polyaldehydes, such as glyoxal.
  • a plasticator such as glycerol
  • the dispersion was prepared from granulate according to the examples, by grinding it and screening out particles bigger than 150 ⁇ m, and mixing the powder into water. A homogeneous, transparent light brown dispersion was formed following a viscose gel phase.
  • a disadvantage associated with the known technology is that the dispersion forms a transparent film when drying. Consequently, known nanoparticles are not suitable as coating pigments or fillers for paper or cardboard, and their use in this way is not mentioned in the reference publication, either.
  • U.S. Pat. No. 6,562,459 presents the preparation of round microparticles which consist totally or partly of at least one polysaccharide, insoluble in water.
  • the polysaccharide is dissolved in an organic solvent and precipitated, possibly cooled, and the microparticles are separated. These microparticles are used as fillers in polymers, in the separation of materials and in diagnostic tests.
  • Amylose-enriched starch or linear poly(1,4-alpha-D-glucan) is used in the preparation. Among others, glycogen and amylopectin are blended into straight-chain polyglucan.
  • the water insolubility of amylose/amylose-rich starch is utilized and, consequently, it was restricted to the use of straight-chain starch.
  • the solvent used, dimethylsulphoxide, is a toxic chemical and being a material which boils at a high temperature, it is difficult to remove from the product, which limits the usability of the product.
  • FI Patent Specification No. 98943 presents a method of improving the properties of paper or cardboard, and in particular it relates to a method in which the surface of paper or cardboard is treated with a compound which comprises a binding agent and a pigment component. Part of the pigment is formed of an aqueous phase-polymerization product of polymerized monomers and modified starch.
  • vinyl monomers are polymerized in the presence of starch.
  • monomeric compounds are grafted into the starch and the product is used to partly replace mineral pigments in the coating paste.
  • the grafting process is complicated and the pigment obtained is a mixture of natural substance and synthetic polymer. This limits the recycling and the biodegradation of the pigment.
  • the purpose of the present invention is to eliminate the disadvantages associated with the known technology and to generate a completely new pigment or filler product, one which is based on starch.
  • the present invention is based on the idea that the required light scattering ability of pigment and, correspondingly, of filler can, in starch-based initial materials, be generated using a solution which is completely different from the known technology in which solid and rigid pigment particles are produced.
  • the initial material is treated in order to build a stiff foam, which comprises pores (micro capsules) of a suitable size.
  • a stable foam such as this can be generated for example by dispersing air into aqueous solutions of starch derivatives, or by the foaming of starch derivatives in supercritical gas.
  • the foaming of polymer materials is well known per se. Air or some other gas can be used in the foaming. In patent literature, methods of foaming polymers using supercritical carbon dioxide are known, too.
  • U.S. Pat. No. 5,158,986 presents a way of preparing closed-cell, microporous material from thermoplastic polymers by treating them with pressurized carbon dioxide in supercritical condition, and letting the pressure drop rapidly after that.
  • PVC polyethylene-terephtalate or polyethylene
  • the foaming time varies from 20 seconds to 2 minutes, and the average pore sizes are in the range of 0.1-2.0 micrometres.
  • foamed LDPE insulant for example for insulating electrically conductive materials, can be prepared from thermoplastic polymer powders or polymer particles using supercritical carbon dioxide treatment (80 bar, 40° C., and 30 minutes) and then extruding it.
  • U.S. Pat. No. 6,558,607 describes the foaming of polyolefin using a solution in supercritical condition, leading to a material having an open pore structure, and which is suitable for several different purposes, among others, in the field of separation techniques, medicine and the textile industry.
  • thermoplastic materials have been foamed.
  • FI Patent Specification No. 100803 describes the use of supercritical carbon dioxide for the foaming of cellulose derivatives, which are insoluble in water, in which case the cellulose derivative, in the form of film, fibre or corresponding piece of solid material is contacted with high-pressure carbon dioxide. The method generates cellulose derivative fibres which are hollow or very porous inside.
  • the foamed products to be produced for example as pigments or filler materials for paper or cardboard.
  • the present invention demonstrates that the starch foams/micro capsules are very useful as paper pigments and especially as fillers, which means that a paper or cardboard that is completely free of mineral particles and has good optical properties can be produced. Used as a filler, the material also gives paper or cardboard good mechanical properties, because starch and starch derivatives are easily fastened to fibres.
  • the product according to the present invention is characterized by what is stated in the characterizing part of claim 1 .
  • the method according to the present invention is, in turn, characterized by what is stated in the characterizing part of claim 2 .
  • Considerable advantages can be achieved with the present invention.
  • organic natural materials for example starch
  • microporous foam which can be stabilized in the form of micro capsules.
  • the light scattering ability of the material is maximized, which means that the structure has good opacity properties (generally over 80%, especially over 85%).
  • Characteristic of the micro capsule structure is also that the strength properties are good considering its mass.
  • the material has a microporous structure it has good absorption properties, which are essential for the application.
  • the material produced can be used as a filler for paper or a coating for paper instead of mineral filler and coating pigments in applications where the grammage of the paper is desired to be low, or for paper that is desired to be totally recyclable (i.e. burnable without any significant formation of ash).
  • the invention can be used to substitute mineral filler or coating materials of paper with renewable materials of organic origin without the properties which are important for the end use of the paper being weakened.
  • By replacing the mineral filler or coating pigments a paper of a lower grammage can be produced and, consequently, the costs of logistics are reduced and a larger printing surface is obtained with the same mass.
  • the filler or coating materials of organic origin also remove the problems encountered during the final treatment of the ash generated in the burning and/or treatment of the de-inking slurry.
  • starch derivatives By combining starch derivatives or by using multifunctional products, it is possible to vary the properties of starch gels/starch foams. Among others, a formulation comprising hydroxyalkyl starch and starch alkenyl succinate has proved to be a good combination.
  • FIG. 1 shows an SEM image of micro bubbles prepared with a dispergator (initial material LN 100).
  • a porous starch material comprising micro bubbles/micro capsules is prepared in the present invention.
  • the micro bubbles are mainly gas-filled, small, unstable spheres in a solution.
  • the micro bubble is held together by a thin liquid wall, a film.
  • the micro capsules are stabilized micro bubbles. They are particles the average diameter of which is approximately 0.1-10 ⁇ m, and which comprise a core and a capsule wall which is usually solid.
  • the core is gas-filled (hollow).
  • the total porosity of the materials is 10-85% by volume, preferably approximately 30-80% by volume, in particular 40-75% by volume.
  • the products are stable. It is known that the stability of foams, particle dispersions and emulsions often depends on several factors, but an important factor is the stability of the films between the phases (life span).
  • the stabilization of these films requires that the liquid comprises some organic or inorganic material. Clean liquids as such do not among others build up a foam.
  • the life span of the films of the micro bubbles i.e. the gas-liquid-interface, is shortened mainly by the surface tension forces, which increase the pressure inside the bubble. As the pressure rises, it reaches a point where the structure of the bubble breaks down.
  • the bubbles can be stabilized by different methods of which can be mentioned crosslinking using linkable surface-active agents, which results in decreasing surface tension.
  • anionic, cationic or non-ionic amphiphilic chemicals are used as surface-active agents.
  • collecting agents for instance amines, xanthates, sulphates
  • surface-active agents for instance amines, xanthates, sulphates
  • “stable” foam means that the foam and its bubble do not break down significantly during storage (for example over a period of 1-10 weeks), nor in the end product, rather the structure essentially maintains its porosity in the paper or the cardboard.
  • the concentration of the surface-active agent must be clearly higher than the critical micelle formation concentration (c.m.c.).
  • the present invention comprises alternative methods of producing micro bubbles.
  • Air or some other gas is dissolved in a starch hydrogel at a low temperature, possibly at overpressure. By increasing the temperature, the gas and the liquid phases are separated, i.e. bubbles are formed. After crosslinking, a stable foam product is generated.
  • Air is mixed in the starch gel and the foamed gel is cooled very rapidly.
  • the foam is stabilized.
  • the bubble size no longer grows, instead small bubbles and a narrow bubble size distribution are obtained.
  • a micro-bubble emulsion is formed using aqueous solutions of starch and organic solvents while briskly mixing.
  • the method requires the use of surface-active agents and crosslinking reagents.
  • a capsule size of less than 2 microns and a very stable structure is achieved by using the method.
  • the pressure and the temperature of the carbon dioxide, and the period during which the starch derivatives are exposed to the carbon dioxide are selected according to the composition of the starch derivative, the measure proportions and the desired end result in such a manner that the high-pressure carbon dioxide penetrates into the solid starch derivative, which is swelled because of the carbon dioxide.
  • enhancing agents such as small molecular alcohols, organic acids or esters, can be added to the carbon dioxide.
  • the pressure on the starch derivative, which was swelled in the high-pressure carbon dioxide is lowered rapidly thereby producing a porous material following decompression.
  • the decompression can be effected for instance by releasing the carbon dioxide contacting the swelled starch derivative.
  • the decompression rate and the end pressure of the carbon dioxide are chosen in order to produce the desired microporous starch material.
  • soluble starch derivatives It is possible to prepare suitable products containing micro-bubbles by using soluble starch derivatives.
  • the starch is dissolved into water to form a solution of approximately 1-30% by weight, preferably approximately 5-20% by weight, most suitably approximately 10-15% by weight, and a solvent mixture is added into the solution.
  • surface-active agents are still added.
  • small quantities (0.01-10% by weight, typically approximately 0.1-5% by weight) of crosslinking agents, such as glyoxal can be added to the starch-bearing solution, too.
  • the solution is mixed using a high-speed mixer for a period of 1-60 minutes, preferably approximately 2-30 minutes. Stable foams are generated, the average bubble sizes of which are, at most, approximately 10 micrometres, typically 0.1-5 micrometres, preferably approximately 0.5-3 micrometres.
  • a starch derivative such as starch ester or starch ether is brought into contact with a material comprising mainly carbon dioxide and, after that, the pressure is allowed to fall rapidly, so that after the decompression microporous starch ester or starch ether is generated with an average pore diameter of less than 50 micrometres.
  • a substantial part of the bubbles at least 20% are, at most, 10 micrometres.
  • the average bubble size is less than 10 micrometres, typically approximately 0.1-5 micrometres.
  • the pressure is usually 100-310 bar and the temperature 50-100° C. Small molecular alcohol or ester, the quantity of which is approximately 1-15% by weight, is added to the carbon dioxide contacting the starch derivative. The pressure is reduced to an essentially lower pressure within 0.08-7 seconds.
  • the DS of the starch derivative is most suitably at least 0.5, preferably at least 1.0.
  • native starches used in the present invention can be modified in many different ways; the molar mass of the starch can be decreased chemically or enzymatically, resulting in a higher dry matter percentage without a high viscosity. In this case, cooking is not necessarily needed for preparing starch gel. However, if it is necessary to generate a high viscosity but not a high dry matter percentage, it is possible to prepare water soluble hydroxy propyl derivatives which have a high molecular weight and different degrees of substitution, and which are crosslinked in the same way as starch.
  • Anionic derivatives (carboxy-methyl starch, starch succinate) or cationic derivatives (for instance cationic starch esters which are self-dispersing) or crosslinking derivatives (UV-hardened double-bonded derivatives, acrylates) can be made from starch.
  • starch gels/starch foams can be varied.
  • a formulation comprising hydroxyalkyl starch and starch alkenyl succinate has proven to be a good combination.
  • the starch derivative is thus a starch ester, starch ether, mixed starch ester/ether or grafted starch prepared from native starch, hydrolyzed starch, oxidized starch, crosslinked starch or gelatinized starch.
  • the starch used can be based on any natural starch, the amylose percentage of which is 0-100% and the amylopectin percentage is 100-0%. Consequently, the starch can be sourced from barley, potato, wheat, oats, pea, corn, tapioca, sago, rice or similar tuber vegetables or cereal crops.
  • the starch derivative used in the present invention is based on products prepared by oxidizing, hydrolyzing, crosslinking, cationizing, grafting, etherifying or esterifying from the natural starches mentioned above.
  • the starch component is hydroxyalkylated starch or an ester of it.
  • more preferable are hydroxypropyl starches, the molar degree of substitution of which is at most 1.4, preferably at most 2 and especially at most 1, and hydroxypropyl starch esters, the molar degree of substitution of which is at most 1.4, preferably at most 1 and more preferably 0.1-0.8, and the degree of substitution is at least 2, preferably 2.5-3.
  • starch alkenyl succinate is used, one which has a linear or branched alkenyl group, comprising typically 3-24 carbon atoms (for instance an octenyl group).
  • a starch-based component is used, one which is derived from an ester formed both of starch and one or several aliphatic C 2-24 -carboxylic acids.
  • the carboxyl acid component of such an ester can be derived from a lower alcanoic acid, such as acetic acid, propionic acid or butyric acid, or a mixture of them.
  • the carboxyl acid component can also come from saturated or unsaturated fatty acids found in nature. Palmitinic acid, stearic acid, oleic acid, linolic acid and mixtures of them are typical examples.
  • an ester can consist of both long chain and short chain carboxyl-acid components. A mixed ester of acetate and stearate is a typical example. According to a known method, not only acids but also corresponding acid anhydrides and acid chlorides, and other corresponding reactive acid derivatives, can be used to form an ester, too.
  • fatty acid esters of starch is carried out, for example, as described in the professional publications: Wolff, I. A., Olds, D. W. and Hilbert, G. E., The acylation of Corn Starch, Amylose and Amylopectin, J. Amer. Chem. Soc. 73 (1952) 346-349 or Gros, A. T. and Feuge, R. O., Properties of Fatty Acid Esters of Amylose, J. Amer. Oil Chemists' Soc 39 (1962) 19-24.
  • a method described in FI Patent No. 107386 in which the esterifying is performed under pressure conditions is one example of a suitable production process.
  • the starch component is an esterified starch, most preferably starch acetate, the molar degree of substitution of which is 0.5-3, preferably 1.5-3 and most suitably 2-3.
  • transglycosylation products can be prepared from the starch derivatives mentioned above by bringing the derivative to react in acidic conditions with an alcanol which comprises 1-5 hydroxyl groups, and by recovering the reaction product or by subjecting it to further processing, for instance in a new reaction step or in a mixing step.
  • This method makes possible the preparation of a microporous starch derivative material, for instance a filler for paper, etc., not only at affordable cost but also by means of a simple process.
  • the foaming conditions i.e. the pressure, the temperature and quantity and quality of the enhancing agent, as well as the degree of substitution of the foamed substance, it is possible to affect the total porosity of the material, the pore size and the pore quality (open/closed).
  • the pore size of the foamed material is generally approximately 0.1-10 micrometres ( ⁇ m), preferably less than 1 ⁇ m, even 100-200 nm, and the total porosity is 75%, when the diameter of the individual particle is less than 5 ⁇ m, or in the case of the smallest pore size, less than 1 ⁇ m.
  • the areas of application of the present products are papers and cardboards, paints, plastics, rubbers, cosmetics, hygiene products, and detergents and other chemical products.
  • a starch which is as soluble as possible was dissolved in water to either a 10% or a 15% solution.
  • the starches used are LN 100, LM 100, C*em Cap Cerestar, dispersion (9 DIP-2103), TL-starch, Hylon-7 corn starch and different blends of them.
  • the collecting agents used were mainly cationic amines: dodecyl amine hydrochloride, octadecyl amine hydrochloride, di(C12-C18)alkyl-dimethyl-ammonium chloride (trade name A18).
  • Methyl isobutyl carbinol (abbreviation used MIBC) and polypropylene glycol methyl ether (trade name Dow Froth) were used as foaming agents.
  • MIBC Methyl isobutyl carbinol
  • Dow Froth polypropylene glycol methyl ether
  • the mixture has been stirred with a dispergator for 5-15 minutes (generally approximately 1-60 minutes) depending on the case, using a speed of rotation of 11 000-22 000 rpm (generally approximately 5 000-30 000 rpm).
  • the mixture was generally greyish, but generally it started to turn to a white or light stiffish foam immediately after the mixing started.
  • the foams generated have usually been analyzed with a conventional light microscope, a laser-particle size analyser and also with a SEM-microscope. At its best, the average diameter of the generated micro bubbles have so far been 1.2 micrometres, in which case 95% of the bubbles were 1.7 micrometres.
  • the bubbles were hereby prepared using a mixture composition of LN 100, A18, glyoxal, MIBC, mineral spirit and ethanol (in proportion 1:4).
  • the method can be used without solvents, too, in which case the preparation takes place in the water phase. Accordingly, the initial material used was a mixture of LN 100 and a dispersion (9 DIP-2103) with a high percentage of solids, mixed in water.
  • the collector used was A18 and, in addition, MIBC and glyoxal were used. As a result, a stable foam with micro bubbles was generated.
  • the electric flotation method too, has been tested for the production of starch-based micro bubbles. Tests were carried out with a flotation cell at a laboratory scale (400 ml) designed by the Geological Survey of Finland. Sodium chloride and sodium sulphate were used as electrolytes in the tests. The starches tested were potato starch (Merck), Hylon-7 corn starch and hydroxy propylated potato starch LN 100. Surface-active collector chemicals (sodium lauryl sulphate and amine collector agent Raiflot) as well as a foaming agent (MIBC: methyl isobutyl carbinol) were used as surface tension reducers and stabilizers.
  • MIBC methyl isobutyl carbinol
  • the starch was dissolved in water and slightly heated (generally 30-35° C.) to intensify the dissolution.
  • the insoluble part was generally filtered out.
  • the other reagents were added into the solution.
  • An electric voltage ( ⁇ 10 V, current 1-2 A) was passed through the flotation cell and the foaming was started. Gas-filled micro bubbles rose to form a foam at the top part of the cell, from which it could be continuously skimmed off into a separate vessel. Generally, white foam was generated for a period of 5-20 minutes.
  • Hylon-7 corn starch (10 g) was mixed in 370 ml of Millipore-water and the mixture was heated at 30° C. for 5 minutes. When heated, the starch was gelled to the extent that the filtration could not succeed.
  • a mixture comprising small amounts of solid matter was put in the electric flotation cell, and 8 ml of an electrolyte (NaCl, 200 g/l), 0.8 g of sodium lauryl sulphate used as a collector chemical together with 4 ml of MIBC foaming agent were added into the cell.
  • An electric voltage ( ⁇ 10 V) was passed through the cell and the foaming was started. Light foam was generated and rose up to the surface of the cell, from where it flowed along the side pipe of the cell to another vessel.
  • the test was stopped because the voltage started to decrease and hardly any foam was generated anymore. Big foam bubbles as well as small bubbles could be seen in the foam.
  • the sample was dried at room temperature.
  • Starch acetate powder (5.5 g), with a degree of acetylation of 2.8 was loaded into the cylinder, both ends of which were plugged with steel lattices. The sample was loaded so that it was isolated from both lattices by a wadding layer.
  • the cylinder was placed in a heatable high pressure reactor with a volume of 50 ml. This reactor was equipped with a ball valve. The pressure inside the reactor was then raised using carbon dioxide to 230 bar and the temperature was raised to 90° C. The temperature was measured at the lid inside the reactor vessel. At the end of the experiment, the device was discharged, resulting in the bulk of the carbon dioxide being released in approximately 100 milliseconds. The treatment time was 150 minutes.
  • the inner temperature of the reactor was approximately 90° C.
  • the outer temperature of the vessel was kept at approximately +90 . . . 95° C.
  • the ethanol (10% by weight) in the carbon dioxide was dosed by impregnating a calculated amount of it into a wad in a second, heated cartridge, through which CO 2 was conducted into the reactor. After the dosage, the wad was totally dry.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Manufacture Of Porous Articles, And Recovery And Treatment Of Waste Products (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
  • Paper (AREA)
US10/573,028 2003-10-02 2004-10-01 Porous filler or coating pigment of paper and cardboard and a method of manufacturing it Abandoned US20070163737A1 (en)

Applications Claiming Priority (5)

Application Number Priority Date Filing Date Title
FI20035172A FI20035172A0 (fi) 2003-10-02 2003-10-02 Huokoinen paperin ja kartongin täyteaine ja sen valmistusmenetelmä
FI20035172 2003-10-02
FI20040743 2004-05-31
FI20040743A FI122073B (fi) 2003-10-02 2004-05-31 Huokoinen paperin ja kartongin täyteaine tai päällystyspigmentti ja sen valmistus
PCT/FI2004/000576 WO2005030847A1 (en) 2003-10-02 2004-10-01 Porous filler or coating pigment of paper and cardboard and a method of manufacturing it

Publications (1)

Publication Number Publication Date
US20070163737A1 true US20070163737A1 (en) 2007-07-19

Family

ID=32395508

Family Applications (1)

Application Number Title Priority Date Filing Date
US10/573,028 Abandoned US20070163737A1 (en) 2003-10-02 2004-10-01 Porous filler or coating pigment of paper and cardboard and a method of manufacturing it

Country Status (5)

Country Link
US (1) US20070163737A1 (fi)
EP (1) EP1682610B1 (fi)
JP (1) JP5281242B2 (fi)
FI (1) FI122073B (fi)
WO (1) WO2005030847A1 (fi)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2012112118A1 (en) * 2011-02-20 2012-08-23 Franciscus Hubertus Jacobus Maurer Expanded polymeric membranes
WO2012127105A2 (en) 2011-03-24 2012-09-27 Upm-Kymmene Corporation Method for preparation of microcapsules from hemicellulose
US9045861B2 (en) 2012-05-28 2015-06-02 Nordkalk Oy Ab Manufacture and use of a composite structure containing precipitated carbonate
US10400105B2 (en) 2015-06-19 2019-09-03 The Research Foundation For The State University Of New York Extruded starch-lignin foams

Families Citing this family (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FI123642B (fi) * 2008-05-30 2013-08-30 Upm Kymmene Oyj Menetelmä pigmenttituotteen muodostamiseksi selluloosajohdannaisesta, pigmenttituote ja sen käyttö
FI20115784A0 (fi) * 2011-08-05 2011-08-05 Teknologian Tutkimuskeskus Vtt Oy Päällyste ja menetelmä sen valmistamiseksi
CN104381819A (zh) * 2014-11-11 2015-03-04 中南林业科技大学 一种营养微球制备的方法
SE1550649A1 (en) * 2015-05-21 2016-11-22 Stora Enso Oyj Aerosol and foam formation using nanosized gas bubbles
CN107501600B (zh) * 2017-08-31 2020-09-22 华南理工大学 一种利用脉冲电场制备改性多孔淀粉的方法

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3585149A (en) * 1968-12-23 1971-06-15 Us Plywood Champ Papers Inc Microcapsular opacifier system
US5158986A (en) * 1991-04-05 1992-10-27 Massachusetts Institute Of Technology Microcellular thermoplastic foamed with supercritical fluid
US5851461A (en) * 1992-06-19 1998-12-22 Albany International Research Co. Method of producing polysaccharide foams
US6369215B1 (en) * 1996-12-31 2002-04-09 Valtion Teknillinen Tutkimuskeskus Hydroxyalkylated starch ester and preparation and use thereof
US6558607B1 (en) * 1999-09-30 2003-05-06 University Of Massachusetts Crystallization of constrained polymers
US6562459B1 (en) * 1998-08-28 2003-05-13 Celanese Ventures Gmbh Method for the production of spherical microparticles consisting totally or partly of at least one water insoluble polyglucan containing branches and microparticles produced according to said method
US6582509B2 (en) * 1999-11-02 2003-06-24 Aveno Oy Organic pigment and a method for its preparation
US6605715B1 (en) * 1996-12-31 2003-08-12 Valtion Teknillinen Tutkimuskeskus Process for the preparation of a starch ester

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2547071B2 (ja) * 1988-05-27 1996-10-23 日本酸素株式会社 穀粒の改質方法
JPH0768403B2 (ja) * 1988-12-15 1995-07-26 東洋エンジニアリング株式会社 発泡体の製造方法
JP2000127610A (ja) * 1998-10-26 2000-05-09 Mitsubishi Paper Mills Ltd インクジェット記録シート

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3585149A (en) * 1968-12-23 1971-06-15 Us Plywood Champ Papers Inc Microcapsular opacifier system
US5158986A (en) * 1991-04-05 1992-10-27 Massachusetts Institute Of Technology Microcellular thermoplastic foamed with supercritical fluid
US5851461A (en) * 1992-06-19 1998-12-22 Albany International Research Co. Method of producing polysaccharide foams
US6369215B1 (en) * 1996-12-31 2002-04-09 Valtion Teknillinen Tutkimuskeskus Hydroxyalkylated starch ester and preparation and use thereof
US6605715B1 (en) * 1996-12-31 2003-08-12 Valtion Teknillinen Tutkimuskeskus Process for the preparation of a starch ester
US6562459B1 (en) * 1998-08-28 2003-05-13 Celanese Ventures Gmbh Method for the production of spherical microparticles consisting totally or partly of at least one water insoluble polyglucan containing branches and microparticles produced according to said method
US6558607B1 (en) * 1999-09-30 2003-05-06 University Of Massachusetts Crystallization of constrained polymers
US6582509B2 (en) * 1999-11-02 2003-06-24 Aveno Oy Organic pigment and a method for its preparation

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2012112118A1 (en) * 2011-02-20 2012-08-23 Franciscus Hubertus Jacobus Maurer Expanded polymeric membranes
WO2012127105A2 (en) 2011-03-24 2012-09-27 Upm-Kymmene Corporation Method for preparation of microcapsules from hemicellulose
US9045861B2 (en) 2012-05-28 2015-06-02 Nordkalk Oy Ab Manufacture and use of a composite structure containing precipitated carbonate
US10400105B2 (en) 2015-06-19 2019-09-03 The Research Foundation For The State University Of New York Extruded starch-lignin foams

Also Published As

Publication number Publication date
JP5281242B2 (ja) 2013-09-04
EP1682610B1 (en) 2013-02-20
FI20040743A0 (fi) 2004-05-31
WO2005030847A1 (en) 2005-04-07
FI20040743A (fi) 2005-04-03
JP2007524734A (ja) 2007-08-30
EP1682610A1 (en) 2006-07-26
FI122073B (fi) 2011-08-15

Similar Documents

Publication Publication Date Title
Hubbe et al. Nanocellulose in thin films, coatings, and plies for packaging applications: A review
Barbosa et al. Isolation and acetylation of cellulose nanostructures with a homogeneous system
EP1682610B1 (en) Porous filler or coating pigment of paper and cardboard and a method of manufacturing it
Abou-Zeid et al. Surfactant-assisted poly (lactic acid)/cellulose nanocrystal bionanocomposite for potential application in paper coating
Bloembergen et al. Biolatex binders for paper and paperboard applications
WO2020230035A1 (en) Method for applying starch to a paper or paperboard web
US8597422B2 (en) Pigment and filler and a method of manufacturing it
CA2938747C (en) A stabilized sizing formulation
McNamee et al. Rice starch particle interactions at air/aqueous interfaces—Effect of particle hydrophobicity and solution ionic strength
de Lima Moreira et al. Effect of adding micronized eggshell waste particles on the properties of biodegradable pectin/starch films
JP2023539608A (ja) ナノセルロースの調製のための効率的なグリーンプロセス、新規な変性ナノセルロース及びその用途
Wawro et al. Forming conditions and mechanical properties of potato starch films
CN1860160B (zh) 纸张和纸板的多孔填料或涂覆颜料及其制备方法
Salmon et al. Shear‐precipitated chitosan powders, fibrids, and fibrid papers: Observations on their formation and characterization
WO2012127105A2 (en) Method for preparation of microcapsules from hemicellulose
CN115584657B (zh) 一种疏水浆料及其制备方法和应用
Gopakumar et al. Extraction and Characterization of Nanomaterials from Agrowaste
EP2291407B1 (en) Process for producing a pigment product based on a cellulose ester
Lyytikäinen et al. Film formation and foamability of cellulose derivatives: Influence of co-binders and substrate properties on coating holdout
EP1915416A1 (en) Starch-based filler and coating pigment composition for fibre webs and method for the manufacture thereof
Bessa et al. Modifications and characterization of nanocellulose
KUDISRI et al. Influence of Chitosan nanoparticles on cellulose acetate film from Durian rind
WO2021124088A1 (en) Foam granulation method
CN118496637A (zh) 一种热塑性淀粉/pbat生物降解复合材料及其制备方法
Patel The Effect of Processing Conditions and Composition on Starch Microcellular Foam Properties.

Legal Events

Date Code Title Description
AS Assignment

Owner name: VALTION TEKNILLINEN TUTKIMUSKESKUS, FINLAND

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:JOHANSSON, ALLAN;QVINTUS-LEINO, PIA;VARJOS, PETRI;AND OTHERS;REEL/FRAME:018473/0404;SIGNING DATES FROM 20060314 TO 20060424

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO PAY ISSUE FEE