US20070059506A1 - Glass fiber bundles for mat applications and methods of making the same - Google Patents

Glass fiber bundles for mat applications and methods of making the same Download PDF

Info

Publication number
US20070059506A1
US20070059506A1 US11/224,246 US22424605A US2007059506A1 US 20070059506 A1 US20070059506 A1 US 20070059506A1 US 22424605 A US22424605 A US 22424605A US 2007059506 A1 US2007059506 A1 US 2007059506A1
Authority
US
United States
Prior art keywords
glass fiber
chopped
fiber bundles
glass fibers
fibers
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US11/224,246
Other languages
English (en)
Inventor
William Hager
Leonard Adzima
Douglas Walden
David Shipp
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Owens Corning Intellectual Capital LLC
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to US11/224,246 priority Critical patent/US20070059506A1/en
Priority to US11/319,896 priority patent/US20070057404A1/en
Assigned to OWENS-CORNING FIBERGLAS TECHNOLOGY, INC. reassignment OWENS-CORNING FIBERGLAS TECHNOLOGY, INC. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: WALDEN, DOUGLAS H., ADZIMA, LEONARD, HAGER, WILLIAM G., SHIPP, DAVID L.
Priority to TW095130641A priority patent/TW200718537A/zh
Priority to ARP060103789 priority patent/AR055405A1/es
Priority to AU2006291220A priority patent/AU2006291220A1/en
Priority to CA 2621606 priority patent/CA2621606A1/en
Priority to KR1020087006008A priority patent/KR20080067327A/ko
Priority to JP2008531187A priority patent/JP2009508018A/ja
Priority to EP20060814264 priority patent/EP1924534A1/en
Priority to CNA2006800334862A priority patent/CN101263091A/zh
Priority to BRPI0615750-5A priority patent/BRPI0615750A2/pt
Priority to RU2008109060/03A priority patent/RU2008109060A/ru
Priority to PCT/US2006/034795 priority patent/WO2007032988A1/en
Publication of US20070059506A1 publication Critical patent/US20070059506A1/en
Assigned to OCV INTELLECTUAL CAPITAL, LLC reassignment OCV INTELLECTUAL CAPITAL, LLC ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: OWENS-CORNING FIBERGLAS TECHNOLOGY, INC.
Assigned to OCV INTELLECTUAL CAPITAL, LLC reassignment OCV INTELLECTUAL CAPITAL, LLC CORRECTIVE ASSIGNMENT TO CORRECT THE CORRECTIVE ASSIGNMENT TO REMOVED APPLICATION NUMBER 10/633,402 FROM THE PREVIOUSLY RECORDED REEL 022804 FRAME 0879. PREVIOUSLY RECORDED ON REEL 022804 FRAME 0879. ASSIGNOR(S) HEREBY CONFIRMS THE OWENS-CORNING FIBERGLAS TECHNOLOGY, INC. EXECUTION DATE: 11/21/2008. Assignors: OWENS-CORNING FIBERGLAS TECHNOLOGY, INC.
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C25/00—Surface treatment of fibres or filaments made from glass, minerals or slags
    • C03C25/10—Coating
    • C03C25/24—Coatings containing organic materials
    • C03C25/26—Macromolecular compounds or prepolymers
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C25/00—Surface treatment of fibres or filaments made from glass, minerals or slags
    • C03C25/10—Coating
    • C03C25/12—General methods of coating; Devices therefor
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C25/00—Surface treatment of fibres or filaments made from glass, minerals or slags
    • C03C25/10—Coating
    • C03C25/24—Coatings containing organic materials
    • C03C25/26—Macromolecular compounds or prepolymers
    • C03C25/32—Macromolecular compounds or prepolymers obtained otherwise than by reactions involving only carbon-to-carbon unsaturated bonds
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C25/00—Surface treatment of fibres or filaments made from glass, minerals or slags
    • C03C25/10—Coating
    • C03C25/24—Coatings containing organic materials
    • C03C25/26—Macromolecular compounds or prepolymers
    • C03C25/32—Macromolecular compounds or prepolymers obtained otherwise than by reactions involving only carbon-to-carbon unsaturated bonds
    • C03C25/323—Polyesters, e.g. alkyd resins
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C25/00—Surface treatment of fibres or filaments made from glass, minerals or slags
    • C03C25/10—Coating
    • C03C25/24—Coatings containing organic materials
    • C03C25/26—Macromolecular compounds or prepolymers
    • C03C25/32—Macromolecular compounds or prepolymers obtained otherwise than by reactions involving only carbon-to-carbon unsaturated bonds
    • C03C25/326—Polyureas; Polyurethanes
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C25/00—Surface treatment of fibres or filaments made from glass, minerals or slags
    • C03C25/10—Coating
    • C03C25/24—Coatings containing organic materials
    • C03C25/26—Macromolecular compounds or prepolymers
    • C03C25/32—Macromolecular compounds or prepolymers obtained otherwise than by reactions involving only carbon-to-carbon unsaturated bonds
    • C03C25/36—Epoxy resins
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F26—DRYING
    • F26B—DRYING SOLID MATERIALS OR OBJECTS BY REMOVING LIQUID THEREFROM
    • F26B13/00—Machines and apparatus for drying fabrics, fibres, yarns, or other materials in long lengths, with progressive movement
    • F26B13/001—Drying and oxidising yarns, ribbons or the like
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F26—DRYING
    • F26B—DRYING SOLID MATERIALS OR OBJECTS BY REMOVING LIQUID THEREFROM
    • F26B17/00—Machines or apparatus for drying materials in loose, plastic, or fluidised form, e.g. granules, staple fibres, with progressive movement
    • F26B17/02—Machines or apparatus for drying materials in loose, plastic, or fluidised form, e.g. granules, staple fibres, with progressive movement with movement performed by belts carrying the materials; with movement performed by belts or elements attached to endless belts or chains propelling the materials over stationary surfaces
    • F26B17/04—Machines or apparatus for drying materials in loose, plastic, or fluidised form, e.g. granules, staple fibres, with progressive movement with movement performed by belts carrying the materials; with movement performed by belts or elements attached to endless belts or chains propelling the materials over stationary surfaces the belts being all horizontal or slightly inclined
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F26—DRYING
    • F26B—DRYING SOLID MATERIALS OR OBJECTS BY REMOVING LIQUID THEREFROM
    • F26B3/00—Drying solid materials or objects by processes involving the application of heat
    • F26B3/32—Drying solid materials or objects by processes involving the application of heat by development of heat within the materials or objects to be dried, e.g. by fermentation or other microbiological action
    • F26B3/34—Drying solid materials or objects by processes involving the application of heat by development of heat within the materials or objects to be dried, e.g. by fermentation or other microbiological action by using electrical effects
    • F26B3/347—Electromagnetic heating, e.g. induction heating or heating using microwave energy
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/249921—Web or sheet containing structurally defined element or component
    • Y10T428/249924—Noninterengaged fiber-containing paper-free web or sheet which is not of specified porosity

Definitions

  • the present invention relates generally to non-woven fibrous mats, and more particularly, to dried bundles of chopped glass fibers that may be used as a replacement for glass forms conventionally utilized in mat forming applications, and even more particularly, to wet-laid mat forming applications. Methods of forming the dried bundles of chopped glass fibers are also provided.
  • glass fibers are formed by drawing molten glass into filaments through a bushing or orifice plate and applying an aqueous sizing composition containing lubricants, coupling agents, and film-forming binder resins to the filaments.
  • the sizing composition provides protection to the fibers from interfilament abrasion and promotes compatibility between the glass fibers and the matrix in which the glass fibers are to be used.
  • the wet fibers may be gathered into one or more strands, chopped, and collected.
  • the chopped strands may contain hundreds or thousands of individual glass fibers.
  • the collected chopped glass strands may then be packaged in their wet condition as wet chopped fiber strands (WUCS) or dried to form dry chopped fiber strands (DUCS).
  • WUCS wet chopped fiber strands
  • DUCS dry chopped fiber strands
  • wet chopped fibers are conventionally used in wet-laid processes in which the wet chopped fibers are dispersed in a water slurry that contains surfactants, viscosity modifiers, defoaming agents, and/or other chemical agents.
  • the slurry containing the slurry containing the fibers is deposited onto a moving screen where a substantial portion of the water is removed to form a web.
  • a binder is then applied, and the resulting mat is dried to remove any remaining water and cure the binder.
  • the formed non-woven mat is an assembly of dispersed, individual glass filaments.
  • Dried chopped strands are commonly used in dry-laid processes in which the dried strands are air blown onto a conveyor or screen and consolidated to form a mat.
  • dry chopped strands are suspended in air, collected as a loose web on a screen or perforated conveyor, and then consolidated to form a mat of randomly oriented bundles.
  • Fibrous mats formed by wet-laid and dry-laid processes are extremely suitable as reinforcements for many types of applications. In order for the final laminate to achieve acceptable mechanical performance, it must include a sufficient amount by weight of glass reinforcements. Although the bundles of fibers present in the dry-laid mats provide for a high glass content, manufacturing dry chopped strands is expensive because such strands are generally dried and packaged in separate steps before being chopped. Thus, it would be desirable to utilize a less expensive glass formation platform that would achieve the increased glass content in composites that require a high impact strength.
  • Bundles of dried chopped fibers have previously been manufactured. Some examples of the processes of forming these bundles of dried chopped fibers are described below.
  • U.S. Pat. No. 4,024,647 to Schaefer discloses a method and apparatus for drying and conveying chopped glass strands.
  • Glass filaments are attenuated through orifices in a bushing and coated with a lubricant binder and/or size.
  • the filaments are gathered into one or more strands and chopped.
  • the wet, chopped fibers then falls onto a first vibratory conveyor.
  • the vibrations of the first vibratory conveyor maintains the chopped strands in fiber bundles by keeping the bundles from adhering to each other.
  • the chopped strands are then passed to a second vibratory conveyor and through a heating zone where the chopped strands are heated to reduce the moisture content to less than 0.1 percent by weight.
  • Chopped strands of a desired length then pass through a foraminous portion of the second vibratory conveyor and into a collection package.
  • U.S. Pat. No. 5,055,119 to Flautt et al. describe an energy efficient process and apparatus for forming glass fiber bundles or strands.
  • Glass fibers are formed from molten glass discharged from a heated bushing. The fibers are moved downwardly and a sizing is applied to the glass fibers by an applicator. To dry the glass fibers, air from around the bushing is passed beneath the bushing where it is heated by the heat of the bushing. The heated air is drawn into a chamber through which the glass fibers pass. The heat transfer contact causes the water or solvent in the sizing composition to be evaporated. The dried fibers are then gathered into a bundle. The bundles may subsequently be chopped.
  • U.S. Pat. No. 6,148,641 to Blough et al. describe a method and an apparatus for producing dried, chopped strands from a supply of continuous fiber strands.
  • chopped fiber strands are produced from one or more continuous strands by chopping the fiber strands in a chopping assembly, ejecting the chopped strands from an exit assembly into a transition chute directly into a drying chamber, collecting the chopped strands in the drying chamber, and at least partially drying the strands in the drying chamber.
  • chopped strand glass mats have been formed that contain glass bundles, such as is found in dry-laid processes, and individual fibers such as are found in wet-laid processes, by utilizing wet-laid processes.
  • U.S. Pat. Nos. 4,112,174 and 4,129,674 to Hannes et al. disclose glass mats that are formed of a web of monofilament fibers and elongated glass fiber bundles interspersed throughout the web in a randomly oriented pattern.
  • the glass fiber bundles preferably contain from about 20-300 monofilaments.
  • the fibrous mats are formed by wet-laid processes. To keep the glass fiber bundles in a bundle form in the slurry during the mat forming process, the bundles are coated with a water or other such liquid insoluble binder.
  • U.S. Pat. Nos. 4,200,487 and 4,242,404 to Bodoc et al. describe glass mats that include individual glass filaments and extended glass fiber elements.
  • the extended glass fiber elements are formed from bundles of glass fibers that slide apart and become connected longitudinally when the slurry is agitated. It is asserted that the glass fiber elements contribute to high strength properties of the mat and that the individual filaments provide a uniform denseness necessary for the impregnation of asphalt in the manufacturing of roofing shingles.
  • the mats are formed by a wet-laid process.
  • U.S. Pat. No. 6,767,851 and U.S. patent application Publication No. 2002/0092634 to Rokman et al. disclose non-woven mats in which at least 20% of the fibers are present as fiber bundles having about 5-450 fibers per bundle. In preferred embodiments, at least 85% of the fibers in the mats are in the form of bundles.
  • the fibers are held in the bundles by a substantially non-water soluble sizing such as an epoxy resin or PVOH.
  • the bundles may comprise at least 10% reinforcing fibers such as glass fibers.
  • the mat may be made by a foam or water process.
  • the chopped glass fiber bundles are formed of a plurality of individual glass fibers positioned in a substantially parallel orientation to each other.
  • the glass fibers used to form the chopped fiber bundles may be any type of glass fiber.
  • reinforcing fibers such as natural fibers, mineral fibers, carbon fibers, ceramic fibers, and/or synthetic fibers may be present in the chopped glass fiber bundles, it is preferred that all of the fibers in the chopped glass fiber bundles are glass fibers.
  • the fibers are at least partially coated with a size composition that includes one or more film forming agents (such as a polyurethane film former, a polyester film former, and/or an epoxy resin film former), at least one lubricant, and at least one silane coupling agent (such as an aminosilane or methacryloxy silane coupling agent).
  • film forming agents such as a polyurethane film former, a polyester film former, and/or an epoxy resin film former
  • silane coupling agent such as an aminosilane or methacryloxy silane coupling agent
  • a size composition including one or more film forming agents (such as a polyurethane film former, a polyester film former, and/or an epoxy resin film former), at least one lubricant, and at least one silane coupling agent (such as an aminosilane or methacryloxy silane coupling agent) is applied to attenuated glass fibers in a conventional manner.
  • the sized glass fibers may be split into glass fiber strands containing a predetermined number of individual glass fibers. It is desirable that the glass fiber bundles have a bundle tex of 20-200 g/km.
  • the glass fiber strands may then be chopped into wet chopped glass fiber bundles and dried to consolidate or solidify the sizing composition.
  • the wet bundles of fibers are dried in an oven such as a conventional dielectric (RF) oven, a fluidized bed oven such as a Cratec® oven (available from Owens Corning), or a rotary tray thermal oven to form the chopped glass fiber bundles.
  • RF dielectric
  • Cratec® oven available from Owens Corning
  • rotary tray thermal oven to form the chopped glass fiber bundles.
  • a size composition including one or more film forming agents (such as a polyurethane film former, a polyester film former, and/or an epoxy resin film former), at least one lubricant, and at least one silane coupling agent (such as an aminosilane or methacryloxy silane coupling agent) is applied to glass fibers attenuated by a bushing.
  • the sized glass fibers may then be passed through a heat transfer chamber where air heated by the bushing is drawn into said heat transfer chamber to substantially dry the sizing on the glass fibers.
  • the dried glass fibers exiting the heat transfer chamber may be split into glass fiber strands that contain a preselected number of individual glass fibers. It is desirable that the glass fiber bundles have a bundle tex of 20-200 g/km.
  • the glass strands may be gathered together into a single tow prior to chopping the glass strands into chopped glass fiber bundles.
  • the chopped fiber bundles are further dried in a conventional dielectric (RF) oven, a fluidized bed oven such as a Cratec® oven (available from Owens Corning), or a rotary tray thermal oven.
  • RF dielectric
  • Cratec® oven available from Owens Corning
  • the chopped glass fiber bundles may be formed at a faster rate of speed than conventional air-laid processes. Increasing the rate of speed that the chopped glass fiber bundles can be produced permits for a higher throughput and additional product that can be sold to the customers.
  • the chopped glass fiber bundles can be formed with low manufacturing costs since the wet glass fibers do not have to be dried and chopped in separate steps.
  • FIG. 1 is a schematic illustration of a chopped strand bundle according to an exemplary embodiment of the present invention
  • FIG. 2 is a flow diagram illustrating steps of an exemplary process for forming glass fiber bundles according to at least one embodiment of the present invention
  • FIG. 3 is a schematic illustration of a processing ling for forming dried chopped strand bundles according to one exemplary embodiment of the present invention
  • FIG. 4 is a schematic illustration of a processing line for forming dried chopped strand bundles according to at least one other exemplary embodiment of the invention.
  • FIG. 5 is a schematic illustration of a processing line for forming a chopped strand mat utilizing chopped strand bundles according to the present invention
  • FIG. 6 is a graphical illustration of the laminate tensile strengths in the machine direction and the cross direction for conventional chopped strand mats and chopped strand mats utilizing dried chopped glass fiber bundles according to the instant invention
  • FIG. 7 is a graphical illustration of the laminate tensile moduli in the machine direction and the cross direction for conventional chopped strand mats and chopped strand mats utilizing dried chopped glass fiber bundles according to the instant invention
  • FIG. 8 is a graphical illustration of the laminate flexural strengths in the machine direction and the cross direction for conventional chopped strand mats and chopped strand mats utilizing dried chopped glass fiber bundles according to the instant invention
  • FIG. 9 is a graphical illustration of the laminate flexural moduli in the machine direction and the cross direction for conventional chopped strand mats and chopped strand mats utilizing dried chopped glass fiber bundles according to the instant invention.
  • FIG. 10 is a graphical illustration of the tensile strength in the machine direction for laminates formed utilizing dried chopped glass fiber bundles according to the present invention.
  • FIG. 11 is a graphical illustration of the tensile strength in the cross-machine direction for laminates formed utilizing dried chopped glass fiber bundles according to the present invention.
  • FIG. 12 is a graphical illustration of IZOD notched impact strength of bulk molding compounds made with glass fibers sized with sizing compositions according to the present invention versus control at 0 degrees;
  • FIG. 13 is a graphical illustration of IZOD notched impact strength of bulk molding compounds made with glass fibers sized with sizing compositions according to the present invention versus control at 90 degrees.
  • the present invention relates to chopped glass fiber bundles that may be used as a replacement for conventional glass forms utilized in mat forming applications and to a process for forming such chopped glass fiber bundles.
  • An example of a chopped glass fiber bundle according to the present invention is depicted generally in FIG. 1 .
  • the chopped glass fiber bundle 10 is formed of a plurality of individual glass fiber 12 having a diameter 16 and a length 14 .
  • the individual glass fibers 12 are positioned in a substantially parallel orientation to each other in a tight knit or “bundled” formation.
  • substantially parallel is meant to denote that the individual glass fibers 12 are parallel or nearly parallel to each other.
  • the chopped glass fiber bundles according to the present invention may be used in the formation of chopped strand mats (CSM), in forming sheet molding compounds (SMC), in bulk molding compounds (BMC), in hand lay-up applications, and in spray-up applications.
  • CSM chopped strand mats
  • SMC sheet molding compounds
  • BMC bulk molding compounds
  • RTM resin transfer molding
  • SRIM structural reaction injection molding
  • the dried chopped glass fiber bundles 10 are blown onto a screen to take the shape of the desired part, such as a truck bed or automobile door inner.
  • the glass fibers used to form the chopped fiber bundles may be any type of glass fiber, such as A-type glass fibers, C-type glass fibers, E-type glass fibers, S-type glass fibers, ECR-type glass fibers (e.g., Advantex® glass fibers commercially available from Owens Corning), wool glass fibers, or combinations thereof.
  • the glass fibers are wet use chopped strand glass fibers (WUCS).
  • WUCS wet use chopped strand glass fibers
  • Wet use chopped strand glass fibers may be formed by conventional processes known in the art. It is desirable that the wet use chopped strand glass fibers have a moisture content of from about 5 to about 30%, and even more desirably a moisture content of from about 5 to about 15%.
  • fibers such as natural fibers, mineral fibers, carbon fibers, ceramic fibers, and/or synthetic fibers such as polyester, polyethylene, polyethylene terephthalate, polypropylene, and/or polyparaphenylene terephthalamide (sold commercially as Kevlar®) in the bundles of fibers 10 is considered to be within the purview of the invention.
  • natural fiber is meant to indicate plant fibers extracted from any part of a plant, including, but not limited to, the stem, seeds, leaves, roots, or bast.
  • synthetic fibers in the fiber bundles gives a mat formed from the fiber bundles more flexibility or conformability to small radii.
  • synthetic fibers may act as a mat binder in later processing to hold the chopped glass fiber bundles 10 together and form a chopped strand mat. However, it is preferred that all of the fibers in the bundles 10 are glass fibers.
  • the process of forming the chopped glass fiber bundles 10 includes forming glass fibers (Step 20 ), applying a size composition to glass fibers (Step 22 ), splitting the fibers to obtain a desired bundle tex (Step 24 ), chopping wet fiber strands to a discrete length (Step 26 ), and drying the wet strands (Step 28 ) to form the chopped glass fiber bundles.
  • glass fibers 12 may be formed by attenuating streams of a molten glass material (not shown) from a bushing or orifice 30 .
  • the attenuated glass fibers 12 may have diameters of about 8 to about 23 microns, preferably from 10-16 microns.
  • an aqueous sizing composition is applied to the fibers 12 .
  • the sizing may be applied by conventional methods such as by the application roller 32 shown in FIG. 3 or by spraying the size directly onto the fibers (not shown).
  • the size protects the glass fibers 12 from breakage during subsequent processing, helps to retard interfilament abrasion, and ensures the integrity of the strands of glass fibers, e.g., the interconnection of the glass filaments that form the strand.
  • the size on the glass fibers 12 also maintains bundle integrity during the formation and subsequent processing of the glass fiber bundles 10 , such as in a wet-laid process to form a chopped strand mat (CSM).
  • CSM chopped strand mat
  • the glass fiber bundles 10 are added to a white water slurry and agitated. The slurry is then deposited onto a moving screen where a majority of the water is removed to form a web, a binder is applied, and the web is dried to remove the remaining water and cure the binder.
  • chopped glass fiber bundles 10 sized with the size composition described below remain in a bundle form or substantially in a bundle form in the white water slurry during the formation of the chopped strand mat.
  • the fibers 12 within the bundles 10 may be sized with the sizing composition so that a predetermined amount of fibers 12 disperse from the fiber bundles 10 in the slurry during agitation.
  • the size composition on the glass fibers 12 also assists in filamentizing the bundles 10 during subsequent processing steps in order to form a mat that gives an aesthetically pleasing look to the finished product.
  • SMC sheet molding compound
  • BMC bulk molding compound
  • the glass fiber bundles 10 have bundle integrity when the metal die closes and is heated so that the sheet molding compound (or BMC) can flow and fill the die to form the desired part.
  • the glass fiber bundles 10 disassociate into single fibers within the die before the flow is complete, the individual glass fibers form clumps and incompletely fill the die, thereby resulting in a defective part.
  • the glass fiber bundles 10 filamentize at that time to reduce the occurrence of or even prevent “telegraphing” or “fiber print”, which is the outline of the glass fiber bundles 10 at the part surface.
  • the size on the glass fibers 12 also assists in filamentizing the chopped glass fiber bundles 10 during future processing steps (such as molding a chopped strand mat formed of the glass fiber bundles 10 ) to form an aesthetically pleasing final product.
  • the size composition applied to the glass fibers 12 includes one or more film forming agents (such as a polyurethane film former, a polyester film former, and/or an epoxy resin film former), at least one lubricant, and at least one silane coupling agent (such as an aminosilane or methacryloxy silane coupling agent).
  • a weak acid such as acetic acid, boric acid, metaboric acid, succinic acid, citric acid, formic acid, and/or polyacrylic acids may be added to the size composition to assist in the hydrolysis of the silane coupling agent.
  • the size composition may be applied to the glass fibers 12 with a Loss on Ignition (LOI) of from about 0.05 to about 2.0% on the dried fiber. LOI may be defined as the percentage of organic solid matter deposited on the glass fiber surfaces.
  • Film formers are agents which create improved adhesion between the glass fibers 12 , which results in improved strand integrity.
  • Suitable film formers for use in the present invention include polyurethane film formers, epoxy resin film formers, and unsaturated polyester resin film formers.
  • Specific examples of film formers include, but are not limited to, polyurethane dispersions such as Neoxil 6158 (available from DSM); polyester dispersions such as Neoxil 2106 (available from DSM), Neoxil 9540 (available from DSM), and Neoxil PS 4759 (available from DSM); and epoxy resin dispersions such as PE-412 (available from AOC), NX 9620 (available from DSM), Neoxil 0151 (available from DSM), Neoxil 2762 (DSM), NX 1143 (available from DSM), AD 502 (available from AOC), Epi Rez 5520 (available from Hexion), Epi Rez 3952 (available from Hexion), Witcobond W-290 H (available from Chemtura), and Witcobond W-2
  • the size composition also includes one or more silane coupling agents.
  • Silane coupling agents enhance the adhesion of the film forming agent(s) to the glass fibers 12 and to reduce the level of fuzz, or broken fiber filaments, during subsequent processing.
  • Examples of silane coupling agents which may be used in the present size composition may be characterized by the functional groups amino, epoxy, vinyl, methacryloxy, ureido, isocyanato, and azamido.
  • Suitable coupling agents for use in the size composition are available commercially, such as, for example, y-aminopropyltriethoxysilane (A-1100 available from General Electric) and methacryloxypropyltriethoxysilane (A-174 available from General Electric).
  • the silane coupling agent may be present in the size composition in an amount of from about 5 to about 30% by weight of the active solids in the size composition, and even more preferably, in an amount of from about 10 to about 15% by weight of the active solids.
  • the size composition may include at least one lubricant to facilitate manufacturing.
  • the lubricant may be present in the size composition in an amount of from about 0 to about 15% by weight of the active solids in the size composition. Preferably, the lubricant is present in an amount of from about 5 to about 10% by weight of the active solids.
  • any suitable lubricant may be used, specific examples of lubricants suitable for use in the size composition include stearic ethanolamide, sold under the trade designation Lubesize K-12 (available from AOC); PEG 400 MO, a monooleate ester having about 400 ethylene oxide groups (available from Cognis); and Emery 6760 L, a polyethyleneimine polyamide salt (available from Cognis).
  • urethane-based film forming dispersions in combination with aminosilanes such as, for example, y-aminopropyltriethoxysilane (sold as A-1100 by General Electric) are effective in the size composition to keep the individual glass fibers 12 bundled together.
  • y-aminopropyltriethoxysilane sold as A-1100 by General Electric
  • Adding an additive such as a polyurethane-acrylic alloy to the urethane-based sizing composition has also been found to help maintain bundle integrity.
  • epoxy-based film former dispersions in combination with epoxy curatives are effective sizing compositions for use in the present invention.
  • an epoxy-based film former such as Epi-Rez 5520 and an epoxy curative such as DPC-6870 available from Resolution Performance Products forms an effective sizing composition, particularly in combination with a methacryloxy silane such as methacryloxypropyltriethoxysilane (commercially available as A-174 from General Electric).
  • unsaturated polyester resin film formers have been found to be effective in forming a useful sizing composition.
  • an unsaturated polyester resin film former such as PE-412 (an unsaturated polyester in styrene that has been emulsified in water (AOC)) or Neoxil PS 4759 (available from DSM) are effective sizes for use in the present invention.
  • Unsaturated polyester film formers may be used alone or in combination with a benzoyl peroxide curing catalyst such as Benox L-40LV (Norac Company, Inc.). The benzoyl peroxide curing catalyst catalyzes the cure (crosslinking) of the unsaturated polyester resin and renders the film surrounding the glass fibers water resistant.
  • the sizing composition may optionally contain conventional additives including antifoaming agents such as Drew L-139 (available from Drew Industries, a division of Ashland Chemical), antistatic agents such as Emerstat 6660A (available from Cognis), surfactants such as Surfynol 465 (available from Air Products), Triton X-100 (available from Cognis), and/or thickening agents.
  • additives including antifoaming agents such as Drew L-139 (available from Drew Industries, a division of Ashland Chemical), antistatic agents such as Emerstat 6660A (available from Cognis), surfactants such as Surfynol 465 (available from Air Products), Triton X-100 (available from Cognis), and/or thickening agents.
  • Additives may be present in the size composition from trace amounts (such as ⁇ about 0.1% by weight of the active solids) up to about 5% by weight of the active solids.
  • the glass fibers 12 are treated with the sizing composition, they are gathered and split into fiber strands 36 having a specific, desired number of individual glass fibers 12 .
  • the splitter shoe 34 splits the attenuated, sized glass fibers into fiber strands 36 .
  • the glass fiber strands 36 may be passed through a second splitter shoe (not shown) prior to chopping the fiber strands 36 .
  • the specific number of individual glass fibers 12 present in the fiber strands 36 (and therefore the number of splits of the glass fibers 12 ) will vary depending on the particular application for the chopped glass fiber bundles 10 .
  • the attenuated glass fibers 40 it would be necessary to split the attenuated glass fibers 40 ways to achieve a bundle of glass fibers that contain 100 fibers.
  • the bundle tex of that particular bundle of glass fibers depends on the diameter of the glass fibers forming the bundle. In the example given above where the fiber bundles contain 100 individual glass fibers, if the fiber diameter of the glass fibers is 12 microns, the calculated bundle tex is 29. If the fiber diameter is 16 microns, the calculated bundle tex is 51 g/km. It is desirable that the glass fibers 12 are split into bundles of fibers that have a specific number of individual fibers to achieve a bundle tex of about 20 to about 200 g/km, preferably from about 30 to about 50 g/km.
  • the fiber strands 36 are passed from the gathering shoe 38 to a chopper 40/cot 60 combination where they are chopped into wet chopped glass fiber bundles 42 having a length of approximately about 0.125 to about 3 inches, and preferably about 0.25 to about 1.25 inches.
  • the wet, chopped glass fiber bundles 42 may fall onto a conveyor 44 (such as a foraminous conveyor) for conveyance to a drying oven 46 .
  • the wet bundles of chopped glass fibers 42 may be collected in a container (not illustrated) for use at a later time.
  • the bundles of wet, sized chopped fibers 42 are then dried to consolidate or solidify the sizing composition.
  • the wet bundles of fibers 42 are dried in an oven 46 such as a conventional dielectric (RF) oven, a fluidized bed oven such as a Cratec® oven (available from Owens Corning), or a rotary tray thermal oven to form the chopped glass fiber bundles 10 .
  • the dried chopped glass fiber bundles 10 may then be collected in a collection container 48 .
  • greater than (or equal to) about 99% of the free water i.e., water that is external to the chopped fiber bundles 42
  • substantially all of the water is removed by the drying oven 46 . It should be noted that the phrase “substantially all of the water” as it is used herein is meant to denote that all or nearly all of the free water from the fiber bundles 42 is removed.
  • the wet bundles of glass fibers 42 are dried in a conventional dielectric (RF) oven.
  • the dielectric oven includes spaced electrodes that produce alternating high-frequency electrical fields between successive oppositely charged electrodes.
  • the wet bundles of glass fibers 42 pass between the electrodes and through the electrical fields where the high alternating frequency electrical fields act to excite the water molecules and raise their molecular energy to a level sufficient to cause the water within the wet chopped fiber bundles 42 to evaporate.
  • Dielectrically drying the bundles of wet glass fibers 42 enhances fiber-to-fiber cohesion and reduces bundle-to-bundle adhesion.
  • the dielectric energy penetrates the wet bundles of chopped glass fibers 42 evenly and causes the water to quickly evaporate, helping to keep the wet glass bundles 42 separated from each other.
  • the dielectric oven permits the wet glass fiber bundles 42 to be dried with no active method of fiber agitation as is conventionally required to remove moisture from wet fibers.
  • This lack of agitation reduces or eliminates the attrition or abrasion of fibers as is commonly seen in conventional fluidized bed and tray drying ovens due to the high air flow velocities within the ovens and the mechanical motion of the fibrous material in the beds.
  • the lack of agitation greatly increases the ability of the dielectric oven to maintain the glass fibers in bundles and not filamentize the glass fiber strands as in aggressive conventional thermal processes.
  • the wet chopped glass fiber bundles 42 may be dried in a fluidized bed oven such as a Cratec® oven or in a rotating tray oven.
  • a fluidized bed oven such as a Cratec® oven or in a rotating tray oven.
  • the wet chopped glass fiber bundles 42 are dried and the sizing composition on the fibers is solidified using a hot air flow having a controlled temperature.
  • the dried fiber bundles 10 may then passed over screens to remove longs, fuzz balls, and other undesirable matter before the chopped glass fiber bundles 10 are collected.
  • the high oven temperatures that are typically found in Cratece and rotating tray ovens allow the size to quickly cure to a very high level of cure which reduces occurrences of premature filamentization.
  • glass fibers 12 are attenuated from a bushing 30 .
  • An aqueous sizing composition as described in detail above is applied to the attenuated glass fibers 12 to form wet sized glass fibers 50 .
  • the sizing may be applied by conventional methods such as by an external application roller 32 or by spraying the size directly onto the glass fibers 12 (not shown). It is considered to be within the purview of the invention to position a size applicator internally within the heat transfer chamber 52 .
  • the wet sized glass fibers 50 then enter the heat transfer chamber 52 and ambient air is drawn into the uppermost end 54 of the heat transfer chamber 52 from circumferentially around the bushing 30 .
  • the heat transfer chamber 52 extends beneath the size applicator 32 and is positioned with the uppermost end 54 of the heat transfer chamber 52 in a sufficiently close proximity to the bushing 30 so that the air being drawn into the uppermost end 54 of the heat transfer chamber 52 is heated by the extreme heat generated by the bushing 30 .
  • the heat transfer chamber 52 is essentially circumferentially disposed about the sized glass fibers 50 so that the heated air may evaporate any water or solvent present in the size composition on the wet glass fibers 50 .
  • the heat transfer chamber 52 extends downwardly from the size applicator 32 a distance that is sufficient to dry or substantially dry the wet sized glass fibers 50 .
  • the moisture content of the glass fibers 50 is less than about 0.05%.
  • the wet glass fibers 50 travel through the heat transfer chamber 52 and exit the chamber 52 as dried glass fibers 56 .
  • Such an adiabatic process is described in detail in U.S. Pat. No.5,055,119 to Flautt et al., the content of which is hereby incorporated by reference in its entirety.
  • the dried sized glass fibers 56 are then gathered and split into dried fiber strands 58 having a specific, desired number of individual glass fibers 12 .
  • a splitter shoe 34 splits the dried sized glass fibers 56 into dried fiber strands 58 , which may then be gathered by a gathering shoe 38 into a single tow 59 for chopping. It is to be appreciated that the splitter shoe 34 may be positioned internally (not illustrated) in the heat transfer chamber 52 to split the wet glass fibers 50 into fiber strands prior to exiting the heat transfer chamber 52 . In this situation, the gathering shoe 38 may or may not be positioned within the heat transfer chamber 52 . It is also to be appreciated that the splitter shoe 34 may be positioned between the size applicator 32 and the heat transfer chamber 52 to split the glass fibers 12 prior to entering the heat transfer chamber 52 (not shown).
  • the tow of combined glass fiber strands 59 may be chopped by a conventional cot 60 and cutter 40 combination to form the dried chopped fiber bundles 10 .
  • the dried chopped fiber bundles 10 may have a length of about 0.125 to about 3 inches, and preferably a length of about 0.25 to about 1.25 inches.
  • the dried sized glass fibers 56 are split into dried bundles of fibers 58 with a bundle tex of from about 20 to about 200 g/km, and preferably from about 30 to about 50 g/km.
  • the dried, chopped glass fiber bundles 10 may fall onto a collection container 48 for storage or placed onto a conveyor for an in-line formation of a chopped strand mat (embodiment is not illustrated).
  • the dried, chopped fiber bundles 10 may be placed onto a conveyor (not shown) for conveyance to a conventional dielectric (RF) oven, a fluidized bed oven such as a Cratec® oven (available from Owens Corning), or a rotary tray thermal oven to further dry them.
  • RF dielectric
  • Cratec® oven available from Owens Corning
  • rotary tray thermal oven to further dry them.
  • the dried chopped glass fiber bundles 10 may be used to form a chopped strand mat 84 , as shown in FIG. 5 .
  • the dried chopped glass bundles 10 may be provided to a conveyor 62 by a storage container 60 .
  • the dried chopped glass fiber bundles 10 are placed into a mixing tank 64 that contains various surfactants, viscosity modifiers, defoaming agents, and/or other chemical agents with agitation to form a chopped glass fiber bundle slurry (not shown).
  • the slurry may be passed through a machine chest 66 and a constant level chest 68 to further disperse any fibers selectively released from the chopped glass fiber bundles 10 by the size composition.
  • the glass fiber bundle slurry may then be transferred from the constant level chest 68 to a head box 70 where the slurry is deposited onto a moving screen or foraminous conveyor 74 and a substantial portion of the water from the slurry is removed to form a web 72 .
  • the water may be removed from the web 72 by a conventional vacuum or air suction system (not illustrated in FIG. 5 ).
  • a binder 76 is then applied to the web 72 by a binder applicator 78 .
  • the binder-coated web 80 is then passed through a drying oven 82 to remove any remaining water and cure the binder.
  • the formed non-woven chopped strand mat 84 that emerges from the oven 82 includes randomly dispersed glass fiber bundles.
  • the non-woven chopped strand mat 84 may be rolled onto a take-up roll 86 for storage for later use.
  • the binder may be an acrylic binder, a styrene acrylonitrile binder, a styrene butadiene rubber binder, a urea formaldehyde binder, or mixtures thereof.
  • the binder is a standard thermosetting acrylic binder formed of polyacrylic acid and at least one polyol (e.g., triethanolamine or glycerine).
  • suitable acrylic binders for use in the present invention include a plasticized polyvinylacetate binder such as Vinamul 8831 (available from Celenese) and modified polyvinylacetates such as Duracet 637 and Duracet 675 (available from Franklin International).
  • the binder may optionally contain conventional additives for the improvement of process and product performance such as dyes, oils, fillers, colorants, UV stabilizers, coupling agents (e.g., aminosilanes), lubricants, wetting agents, surfactants, and/or antistatic agents.
  • additives for the improvement of process and product performance such as dyes, oils, fillers, colorants, UV stabilizers, coupling agents (e.g., aminosilanes), lubricants, wetting agents, surfactants, and/or antistatic agents.
  • the chopped glass fiber bundles 10 of the present invention may be formed at a significantly fast rate, especially when compared glass bundles formed by conventional air-laid processes. Increasing the rate of speed that the chopped glass fiber bundles can be produced permits for a higher throughput and additional product that can be sold to the customers. In addition, the chopped glass fiber bundles can be formed with low manufacturing costs since the fibers do not have to be dried and chopped in separate steps.
  • the chopped glass fiber bundles 10 when utilized in the formation of chopped strand mats in the wet process described above, provides for a mat that has a substantially uniform distribution of glass (aerial density) and is white in appearance. It is also advantageous that the wet fibers utilized to form the chopped glass fiber bundles produce little or no fuzz in the final chopped strand mat.
  • the sizing formulations set forth in Tables 1-4 were prepared in buckets as described generally below.
  • To prepare the size compositions approximately 90% of the water and, if present in the size composition, the acid(s) were added to a bucket.
  • the silane coupling agent was added to the bucket and the mixture was agitated for a period of time to permit the silane to hydrolyze.
  • the lubricant and film former were added to the mixture with agitation to form the size composition.
  • the size composition was then diluted with the remaining water to achieve the target mix solids of approximately 4.5% mix solids.
  • Epoxy Size Composition A Component of Size % by Weight of Composition Active Solids ER 5520 (a) 46.15 DPC-6870 (b) 46.15 PEG 400 MO (c) 3.08 A-174 (d) 4.62 (a) epoxy resin film forming dispersion in water (Resolution Performance Products) (b) epoxy curative (Resolution Performance Products) (c) monooleate ester (Cognis) (d) methacryloxypropyltrimethoxysilane (General Electric)
  • Each of the sizes were applied to E-glass in a conventional manner (such as a roll-type applicator as described above.
  • the E-glass was attenuated to 13 ⁇ m glass filaments in a 75 lb/hr throughput bushing fitted with 2052 hole tip plate.
  • the filaments were gathered and split 16 ways to achieve 128 filaments per glass fiber bundle and a bundle tex of about 43 g/km.
  • the glass fiber bundles were then chopped with a mechanical cot-cutter combination to a length of approximately 11 ⁇ 4 inches and gathered into a plastic pan.
  • the chopped glass fibers contained approximately 15% forming moisture. This moisture in chopped glass fiber bundles was removed in a dielectric oven (40 MHz, Radio Frequency Co.) to form dried chopped glass fiber bundles.
  • the dried chopped fiber bundles formed in accordance with the procedures set forth in Example 1 were used to form four chopped glass mats.
  • the dried chopped fiber bundles (each containing a different size composition set forth in Tables 1-4) were suspended in 250 gallon mixing tanks in which the appropriate additives (surfactants, dispersants, and the like) were added with agitation to form chopped glass fiber bundle slurry slurries.
  • the components of the white water slurry (other than water) are set forth in Table 5.
  • the glass slurries were each deposited onto a moving chain where a majority of the water was removed by a vacuum to form a web.
  • a plasticized polyvinylacetate mat binder was applied to the glass webs (Vinamul 8831 from Celenese) by a weir (curtain coater).
  • the webs were then passed through a forced air oven at 450° F. for 30 seconds to remove the remaining water from the webs, cure the binder, and form the chopped glass mats.
  • the basis weight of the mats were determined to be approximately 1 oZ/ft 2 . It was also determined that the binder was present on the mats at 5.0% by weight.
  • the mats were extremely white and visually showed excellent aerial density.
  • the chopped glass mats displayed dry tensile strengths of 30 lb in the machine direction (MD) and 25 lb in the cross-machine direction (CD).
  • Laminates were prepared from the chopped glass mats with a polyester resin (AOC R937) and catalyzed with Attofina DDM9 catalyst (2-Butanone Peroxide). To facilitate comparison, the laminates containing the inventive chopped glass fiber bundles all had a 3 oz/ft 2 basis weight and substantially equivalent thicknesses. Simulating hand layup, the laminates were formed in a hydraulic press under nominal temperature (120° F.) and pressure for about 30 minutes. Pressure, at the low end of the press range was 10,000 lb for the 14 in 2 laminates, which translates to about 50 psi. The laminates underwent post-cure in an oven for 2 hours at 200 ° F. before mechanical testing.
  • the laminates containing the inventive chopped glass fiber bundles were tested for tensile strength and flexural strength.
  • the tensile strength was determined according to the testing procedures set forth in ASTM D5083 and flexural strength was determined according to the testing procedures set forth in ASTM D790.
  • the comparative mats are set forth in Table 6. TABLE 6 Conventional Mat Description M723A 1 oz/ft 2 chopped strand mat from Owens Corning M8643 1 oz/ft 2 electrical-pultrusion grade continuous filament mat from Owens Corning M8610 1 oz/ft 2 general purpose continuous filament mat from Owens Corning
  • Each of the sizes set forth in Tables 1-4 were prepared and applied in a conventional manner to E-glass attenuated to 13 ⁇ m glass filaments in a 75 lb/hr throughput bushing fitted with 2052 hole tip plate.
  • the sized fibers were split 16 ways to achieve 128 filaments per glass fiber bundle and passed through a heat transfer chamber where air heated by the extreme heat generated by the bushing was drawn into the heat transfer chamber to dry the glass fiber bundles.
  • the dried glass fiber bundles had a bundle tex of about 43 g/km.
  • the dried glass fiber bundles were gathered into one tow and chopped with a mechanical cot-cutter combination to a length of 11 ⁇ 4 inches.
  • the chopped glass fibers were gathered into a plastic pan.
  • the glass fibers contained 0% forming moisture.
  • the dried chopped fiber bundles formed in accordance with the procedures set forth in Example 3 were used to form four chopped glass mats.
  • the dried chopped fiber bundles (each containing a different size composition set forth in Tables 1-4) were suspended in 250 gallon mixing tanks in which the appropriate additives (surfactants, dispersants, and the like) were added with agitation to form chopped glass fiber bundle slurry slurries.
  • the components of the white water slurry (other than water) are set forth in Table 7.
  • the glass slurries were each collected onto a moving chain where a majority of the water was removed by a vacuum to form a web.
  • a plasticized polyvinylacetate mat binder was applied to the glass webs (Duracet 675 from Franklin International) by a weir (curtain coater).
  • the webs were then passed through a forced air oven at 450 ° F. for 30 seconds to remove the remaining water from the webs, cure the binder, and form the chopped glass mats.
  • the basis weight of the mats were determined to be approximately 1 oz/ft 2 . It was also determined that the binder was present on the mats at 5.0% by weight. On visual observation, it was noted that the mats were extremely white and visually showed excellent aerial density.
  • the chopped glass mats displayed dry tensile strengths of 32 lb in the machine direction (MD) and 27 lb in the cross-machine direction (CD).
  • Laminates were prepared from the chopped glass mats with a polyester resin (AOC R937) and catalyzed with Attofina DDM9 catalyst (2-Butanone Peroxide). To facilitate comparison, the laminates containing the inventive chopped glass fiber bundles were all 3 oZ/ft 2 basis weight and substantially equivalent thicknesses. Simulating hand layup, the laminates were formed in a hydraulic press under nominal temperature (120° F.) and pressure for about 30 minutes. Pressure, at the low end of the press range was 10,000 lb for the 14 in 2 laminates, which translates to about 50 psi. The laminates underwent post-cure in an oven for 2 hours at 200° F. before mechanical testing.
  • Example 3 Dried chopped fiber bundles formed in accordance with the procedures set forth in Example 3 were used to form four chopped glass mats as described above in Example 4.
  • the dried chopped fiber bundles sized Polyurethane Size Composition A (Table 1) were suspended in 250 gallon mixing tanks in a white water slurry containing the components set forth in Table 7.
  • the glass slurries were each collected onto a moving chain where a majority of the water was removed by a vacuum to form a web.
  • a plasticized polyvinylacetate mat binder was applied to the glass webs (Duracet 675 or Duracet 637 from Franklin International) by a weir (curtain coater).
  • the webs were then passed through a forced air oven at 450° F. for 30 seconds to remove the remaining water from the webs, cure the binder, and form the chopped glass mats.
  • Laminates were prepared from the chopped strand mats in accordance with the procedure described above in Example 4.
  • the various samples tested (Samples 1-7) are set forth in Table 8.
  • Samples 1 and 2 contained Duracet 637 as a binder and Samples 3 and 4 contained Duracet 675 as a binder.
  • the laminates were tested for tensile strength in the machine direction (MD) and in the cross-machine direction (CD).
  • the results are set forth in Tables 10 and 11.
  • a bias in the machine direction is an advantage to the laminates because the chopped strand mat will be naturally stronger in the direction that a customer will pull it off of the roll. As a result, larger rolls may be manufactured. In addition, the additional strength would enable a customer to pull the chopped strand mat off the roll at a faster rate of speed with a less likelihood that the mat would tear.
  • the data also demonstrates superior strength for laminates formed with the chopped glass fiber bundles sized with Size Composition A compared to the controls.
  • the various experimental glass fibers are set forth below as Samples 1-10.
  • the charge was placed into a 12 inch ⁇ 18 inch tool and was molded at 10,000 psi at 265° F. for 5 minutes.
  • the laminates were tested for resistance to notched impact strength according to ASTM D256 in the 0° and 90° direction.
  • the results are set forth in Tables 12 and 13.
  • the results indicated that the glass fibers sized with the experimental size composition demonstrated at least comparable performance to the control.
  • the results were unexpected because an at least comparable impact strength was achieved by drying the glass fibers for a short period of time (30 minutes) as compared to conventional processes in which the glass is thermally dried for at least 20 hours.
  • Sample 1 Polyurethane Size Composition A (Table 1) was applied to glass fibers and dried for 6 hours a thermal oven at 265° F.
  • Sample 2 Polyurethane Size Composition A (Table 1) was applied to glass fibers and dried for 30 minutes in an RF oven followed by 1 hour in a thermal oven at 265° F.
  • Sample 3 Polyurethane Size Composition A (Table 1) was applied to glass fibers and dried for 30 minutes in an RF oven followed by 2 hours at in a thermal oven at 265° F.
  • Sample 4 Polyurethane Size Composition A (Table 1) was applied to glass fibers and dried for 30 minutes in an RF oven followed by 2 hours in a thermal oven at 265° F.
  • Sample 5 Polyurethane Size Composition A (Table 1) was applied to glass fibers and dried for 30 minutes in an RF oven followed by 2 hours in a thermal oven at 265° F.
  • Sample 6 Polyurethane Size Composition A (Table 1) was applied to glass fibers and dried for 30 minutes in an RF oven followed by 2 hours in a thermal oven at 265° F.
  • Sample 7 Polyurethane Size Composition B (Table 2) was applied to glass fibers and dried for 30 minutes in an RF oven; no post heating.
  • Sample 8 Epoxy Size Composition A (Table 3) was applied to glass fibers and dried for 30 minutes in an RF oven; no post heating.
  • Sample 9 Epoxy Size Composition A (Table 3) was applied to glass fibers and dried for 20 minutes in an RF oven; no post heating.
  • Sample 10 Polyurethane Size Composition B (Table 2) was applied to glass fibers and dried for 20 minutes in an RF oven; no post heating.
  • Sample 12 control bulk molding compound (BMC) dry use chopped strands (101C from Rio Claro, Brazil; Owens Corning).

Landscapes

  • Engineering & Computer Science (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Chemical & Material Sciences (AREA)
  • General Life Sciences & Earth Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • General Chemical & Material Sciences (AREA)
  • Geochemistry & Mineralogy (AREA)
  • Materials Engineering (AREA)
  • Organic Chemistry (AREA)
  • Mechanical Engineering (AREA)
  • General Engineering & Computer Science (AREA)
  • Textile Engineering (AREA)
  • Microbiology (AREA)
  • Biomedical Technology (AREA)
  • Biotechnology (AREA)
  • Molecular Biology (AREA)
  • Health & Medical Sciences (AREA)
  • Electromagnetism (AREA)
  • Physics & Mathematics (AREA)
  • Nonwoven Fabrics (AREA)
  • Reinforced Plastic Materials (AREA)
  • Treatments For Attaching Organic Compounds To Fibrous Goods (AREA)
  • Surface Treatment Of Glass Fibres Or Filaments (AREA)
  • Manufacture, Treatment Of Glass Fibers (AREA)
US11/224,246 2005-09-12 2005-09-12 Glass fiber bundles for mat applications and methods of making the same Abandoned US20070059506A1 (en)

Priority Applications (13)

Application Number Priority Date Filing Date Title
US11/224,246 US20070059506A1 (en) 2005-09-12 2005-09-12 Glass fiber bundles for mat applications and methods of making the same
US11/319,896 US20070057404A1 (en) 2005-09-12 2005-12-28 Compression and injection molding applications utilizing glass fiber bundles
TW095130641A TW200718537A (en) 2005-09-12 2006-08-21 Glass fiber bundles for mat applications and methods of making the same
ARP060103789 AR055405A1 (es) 2005-09-12 2006-08-30 Haces de fibra de vidrio para producir planchas y metodos para su fabricacion
PCT/US2006/034795 WO2007032988A1 (en) 2005-09-12 2006-09-08 Glass fiber bundles for mat applications and methods of making the same
KR1020087006008A KR20080067327A (ko) 2005-09-12 2006-09-08 매트용 유리 섬유 다발 및 그의 제조 방법
CA 2621606 CA2621606A1 (en) 2005-09-12 2006-09-08 Glass fiber bundles for mat applications and methods of making the same
AU2006291220A AU2006291220A1 (en) 2005-09-12 2006-09-08 Glass fiber bundles for mat applications and methods of making the same
JP2008531187A JP2009508018A (ja) 2005-09-12 2006-09-08 マット用途用のガラス繊維束およびその製造方法
EP20060814264 EP1924534A1 (en) 2005-09-12 2006-09-08 Glass fiber bundles for mat applications and methods of making the same
CNA2006800334862A CN101263091A (zh) 2005-09-12 2006-09-08 用于垫子应用的玻璃纤维束及其制备方法
BRPI0615750-5A BRPI0615750A2 (pt) 2005-09-12 2006-09-08 feixes de fibra de vidro para aplicações em tapete e métodos de fabricação do mesmo
RU2008109060/03A RU2008109060A (ru) 2005-09-12 2006-09-08 Пучки стекловолокон и способ их изготовления

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US11/224,246 US20070059506A1 (en) 2005-09-12 2005-09-12 Glass fiber bundles for mat applications and methods of making the same

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US11/319,896 Continuation-In-Part US20070057404A1 (en) 2005-09-12 2005-12-28 Compression and injection molding applications utilizing glass fiber bundles

Publications (1)

Publication Number Publication Date
US20070059506A1 true US20070059506A1 (en) 2007-03-15

Family

ID=37686006

Family Applications (1)

Application Number Title Priority Date Filing Date
US11/224,246 Abandoned US20070059506A1 (en) 2005-09-12 2005-09-12 Glass fiber bundles for mat applications and methods of making the same

Country Status (12)

Country Link
US (1) US20070059506A1 (ja)
EP (1) EP1924534A1 (ja)
JP (1) JP2009508018A (ja)
KR (1) KR20080067327A (ja)
CN (1) CN101263091A (ja)
AR (1) AR055405A1 (ja)
AU (1) AU2006291220A1 (ja)
BR (1) BRPI0615750A2 (ja)
CA (1) CA2621606A1 (ja)
RU (1) RU2008109060A (ja)
TW (1) TW200718537A (ja)
WO (1) WO2007032988A1 (ja)

Cited By (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20080160281A1 (en) * 2006-12-29 2008-07-03 Vickery Eric L Sizing composition for glass fibers
US20080299852A1 (en) * 2007-06-01 2008-12-04 Lee Jerry H C Wet-laid chopped strand fiber mat for roofing mat
US20090071617A1 (en) * 2007-09-17 2009-03-19 Huang Helen Y Methods for improving the tear strength of mats
US20090159228A1 (en) * 2007-12-21 2009-06-25 Annabeth Law Variable dispersion of wet use chopped strand glass fibers in a chopped title strand mat
US20100117265A1 (en) * 2008-11-10 2010-05-13 Klaus Friedrich Gleich Sizing composition for fibers, sized fibers and method of using to make molding compounds and frp molded products
US20100162632A1 (en) * 2008-12-30 2010-07-01 Saint-Gobain Abrasives Inc. Bonded abrasive tool and method of forming
US20110229690A1 (en) * 2007-12-21 2011-09-22 Ocv Intellectual Capital, Llc Cationic fiberglass size
US20160244362A1 (en) * 2013-09-18 2016-08-25 Surface Tech LLC Method and Composition for Reinforcing Asphalt Cement Concrete
WO2019195069A1 (en) * 2018-04-05 2019-10-10 Ocv Intellectual Capital, Llc Carbon fibers with tuned stiffness
CN110981223A (zh) * 2019-12-18 2020-04-10 安徽省宁国昊成高温材料有限公司 一种耐高温玻璃纤维及其制备方法
US20210276688A1 (en) * 2020-03-06 2021-09-09 Galactic Co., LLC Shaped Composite Vehicle Skins and Method for High Rate Manufacturing of Same
US11370704B2 (en) 2017-10-27 2022-06-28 Owens Corning Intellectual Capital, Llc Sizing compositions including weakly-coordinating anion salts and uses thereof

Families Citing this family (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102503184B (zh) * 2011-11-10 2014-03-05 山东建筑大学 一种高稳定耐温玻璃纤维浸润剂
FR3005465B1 (fr) * 2013-05-07 2015-04-17 Saint Gobain Isover Dispositif et procede de fabrication de fibres minerales par centrifugation interne
CN103911865B (zh) * 2013-12-31 2016-05-11 上海宏和电子材料有限公司 电子级玻璃纤维布封边剂材料
CN103978749B (zh) * 2014-05-20 2015-10-28 南京工业大学 一种玻璃纤维无规则架构夹芯材料及其制备方法
KR101681276B1 (ko) 2015-08-03 2016-11-30 (주)부양소재 연속루프섬유 매트 성형방법
KR101681277B1 (ko) 2015-08-03 2016-11-30 (주)부양소재 연속루프섬유 매트 성형용 엣지 정렬장치
CN105859158B (zh) * 2015-12-30 2019-01-29 巨石集团有限公司 一种低迁移率的玻璃纤维浸润剂
CN107447370B (zh) * 2017-09-15 2019-06-18 合肥工业大学 一种短切纤维连续取向的装置及方法
CN112481827B (zh) * 2020-11-23 2022-04-12 舒城娃娃乐儿童用品有限公司 一种保暖喷胶棉及其喷胶装置

Citations (26)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3837892A (en) * 1972-01-28 1974-09-24 Owens Corning Fiberglass Corp Glass fiber reinforced elastomers
US3946097A (en) * 1973-01-27 1976-03-23 Ube-Nitto Kasei Co., Ltd. Process for forming continuous fiber reinforced material embedded in thermosetting resin
US4024647A (en) * 1976-01-20 1977-05-24 Ppg Industries, Inc. Temperature controlled heater tray
US4112174A (en) * 1976-01-19 1978-09-05 Johns-Manville Corporation Fibrous mat especially suitable for roofing products
US4129674A (en) * 1972-10-27 1978-12-12 Johns-Manville Corporation Fibrous mat especially suitable for roofing products and a method of making the mat
US4200487A (en) * 1979-05-16 1980-04-29 Gaf Corporation Economical method of making high-strength glass fiber mats particularly useful for roofing products
US4242404A (en) * 1979-05-16 1980-12-30 Gaf Corporation High-strength glass fiber mat particularly useful for roofing products
US4410645A (en) * 1981-06-15 1983-10-18 Ppg Industries, Inc. Aqueous sizing composition and sized glass fibers and method
US4615946A (en) * 1985-03-29 1986-10-07 Ppg Industries, Inc. Chemically treated glass fibers for reinforcing polymeric matrices
US4637956A (en) * 1985-03-29 1987-01-20 Ppg Industries, Inc. Sized glass fibers and reinforced polymers containing same
US4762750A (en) * 1986-05-22 1988-08-09 Ppg Industries, Inc. Flexible, chemically treated bundles of fibers and process
US5055119A (en) * 1990-09-13 1991-10-08 Owens-Corning Fiberglas Corporation Method and apparatus for forming migration free glass fiber packages
US5455113A (en) * 1991-08-07 1995-10-03 Ppg Industries, Inc. Impregnated fiber bundles having independently crosslinkable polyurethane
US5514745A (en) * 1993-12-28 1996-05-07 Kawasaki Steel Corporation Mixture for melt process moldings having long fiber reinforced polypropylene and polypropylene resin and high mechanical strength molding formed therefrom
US5525180A (en) * 1993-02-05 1996-06-11 Hercules Incorporated Method for producing chopped fiber strands
US5935289A (en) * 1994-08-25 1999-08-10 Johns Manville International, Inc. Apparatus for automatic fiber manufacture
US6025073A (en) * 1997-06-04 2000-02-15 N.V. Owens-Corning S.A. High solubility size composition for fibers
US6148640A (en) * 1998-08-03 2000-11-21 Johns Manvill International, Inc. Method for making chopped fiber
US6148641A (en) * 1998-12-18 2000-11-21 Ppg Industries Ohio, Inc. Apparatus and method for producing dried, chopped strands
US20020092634A1 (en) * 2000-04-05 2002-07-18 Ahlstrom Glassfibre Oy Chopped strand non-woven mat production
US6659756B2 (en) * 1999-07-16 2003-12-09 Owens Corning Fiberglas Technology, Inc. System for preparing polymer encapsulated glass fiber pellets
US20040016093A1 (en) * 2000-03-02 2004-01-29 Christoph Lueneburger Package of strand and a method of manufacturing the same
US6767581B2 (en) * 2000-12-20 2004-07-27 Infineon Technologies Ag Process for the deposition of thin layers by chemical vapor deposition
US20070032157A1 (en) * 2005-08-05 2007-02-08 Mcgrath Ralph D Dually dispersed fiber construction for nonwoven mats using chopped strands
US20070148453A1 (en) * 2003-12-17 2007-06-28 Saint-Gobain Vetrotex France S.A. Sized glass fibres with fast impregnation for the reinforcement of polymer materials
US7276132B2 (en) * 1999-06-21 2007-10-02 Pella Corporation Method of making a reinforcing mat for a pultruded part

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1339630A (en) * 1970-07-25 1973-12-05 Siemens Ag Drying wound spools of filamentary material
CA937830A (en) * 1970-10-15 1973-12-04 Owens-Corning Fiberglas Corporation Moldable glass fiber-reinforced resin composite
FR2686828A1 (fr) * 1992-01-30 1993-08-06 Vetrotex France Sa Procede d'obtention d'un produit composite par moulage.
AU2002230452A1 (en) * 2000-11-22 2002-06-03 Owens Corning Epoxy urethane string binder

Patent Citations (27)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3837892A (en) * 1972-01-28 1974-09-24 Owens Corning Fiberglass Corp Glass fiber reinforced elastomers
US4129674A (en) * 1972-10-27 1978-12-12 Johns-Manville Corporation Fibrous mat especially suitable for roofing products and a method of making the mat
US3946097A (en) * 1973-01-27 1976-03-23 Ube-Nitto Kasei Co., Ltd. Process for forming continuous fiber reinforced material embedded in thermosetting resin
US4112174A (en) * 1976-01-19 1978-09-05 Johns-Manville Corporation Fibrous mat especially suitable for roofing products
US4024647A (en) * 1976-01-20 1977-05-24 Ppg Industries, Inc. Temperature controlled heater tray
US4200487A (en) * 1979-05-16 1980-04-29 Gaf Corporation Economical method of making high-strength glass fiber mats particularly useful for roofing products
US4242404A (en) * 1979-05-16 1980-12-30 Gaf Corporation High-strength glass fiber mat particularly useful for roofing products
US4410645A (en) * 1981-06-15 1983-10-18 Ppg Industries, Inc. Aqueous sizing composition and sized glass fibers and method
US4615946A (en) * 1985-03-29 1986-10-07 Ppg Industries, Inc. Chemically treated glass fibers for reinforcing polymeric matrices
US4637956A (en) * 1985-03-29 1987-01-20 Ppg Industries, Inc. Sized glass fibers and reinforced polymers containing same
US4762750A (en) * 1986-05-22 1988-08-09 Ppg Industries, Inc. Flexible, chemically treated bundles of fibers and process
US5055119A (en) * 1990-09-13 1991-10-08 Owens-Corning Fiberglas Corporation Method and apparatus for forming migration free glass fiber packages
US5455113A (en) * 1991-08-07 1995-10-03 Ppg Industries, Inc. Impregnated fiber bundles having independently crosslinkable polyurethane
US5525180A (en) * 1993-02-05 1996-06-11 Hercules Incorporated Method for producing chopped fiber strands
US5514745A (en) * 1993-12-28 1996-05-07 Kawasaki Steel Corporation Mixture for melt process moldings having long fiber reinforced polypropylene and polypropylene resin and high mechanical strength molding formed therefrom
US5935289A (en) * 1994-08-25 1999-08-10 Johns Manville International, Inc. Apparatus for automatic fiber manufacture
US6062048A (en) * 1994-08-25 2000-05-16 Johns Manville International, Inc. Apparatus for automating fiber manufacture with automatic fiber gathering
US6025073A (en) * 1997-06-04 2000-02-15 N.V. Owens-Corning S.A. High solubility size composition for fibers
US6148640A (en) * 1998-08-03 2000-11-21 Johns Manvill International, Inc. Method for making chopped fiber
US6148641A (en) * 1998-12-18 2000-11-21 Ppg Industries Ohio, Inc. Apparatus and method for producing dried, chopped strands
US7276132B2 (en) * 1999-06-21 2007-10-02 Pella Corporation Method of making a reinforcing mat for a pultruded part
US6659756B2 (en) * 1999-07-16 2003-12-09 Owens Corning Fiberglas Technology, Inc. System for preparing polymer encapsulated glass fiber pellets
US20040016093A1 (en) * 2000-03-02 2004-01-29 Christoph Lueneburger Package of strand and a method of manufacturing the same
US20020092634A1 (en) * 2000-04-05 2002-07-18 Ahlstrom Glassfibre Oy Chopped strand non-woven mat production
US6767581B2 (en) * 2000-12-20 2004-07-27 Infineon Technologies Ag Process for the deposition of thin layers by chemical vapor deposition
US20070148453A1 (en) * 2003-12-17 2007-06-28 Saint-Gobain Vetrotex France S.A. Sized glass fibres with fast impregnation for the reinforcement of polymer materials
US20070032157A1 (en) * 2005-08-05 2007-02-08 Mcgrath Ralph D Dually dispersed fiber construction for nonwoven mats using chopped strands

Cited By (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2008085304A2 (en) * 2006-12-29 2008-07-17 Ocv Intellectual Capital, Llc Sizing composition for glass fibers
WO2008085304A3 (en) * 2006-12-29 2008-09-18 Ocv Intellectual Capital Llc Sizing composition for glass fibers
US20080160281A1 (en) * 2006-12-29 2008-07-03 Vickery Eric L Sizing composition for glass fibers
US20080299852A1 (en) * 2007-06-01 2008-12-04 Lee Jerry H C Wet-laid chopped strand fiber mat for roofing mat
US8080171B2 (en) 2007-06-01 2011-12-20 Ocv Intellectual Capital, Llc Wet-laid chopped strand fiber mat for roofing mat
US7927459B2 (en) 2007-09-17 2011-04-19 Ocv Intellectual Capital, Llc Methods for improving the tear strength of mats
US20090071617A1 (en) * 2007-09-17 2009-03-19 Huang Helen Y Methods for improving the tear strength of mats
US20090159228A1 (en) * 2007-12-21 2009-06-25 Annabeth Law Variable dispersion of wet use chopped strand glass fibers in a chopped title strand mat
US20110229690A1 (en) * 2007-12-21 2011-09-22 Ocv Intellectual Capital, Llc Cationic fiberglass size
US20100117265A1 (en) * 2008-11-10 2010-05-13 Klaus Friedrich Gleich Sizing composition for fibers, sized fibers and method of using to make molding compounds and frp molded products
US20100162632A1 (en) * 2008-12-30 2010-07-01 Saint-Gobain Abrasives Inc. Bonded abrasive tool and method of forming
US8252075B2 (en) * 2008-12-30 2012-08-28 Saint-Gobain Abrasives, Inc. Bonded abrasive tool and method of forming
US8540785B2 (en) 2008-12-30 2013-09-24 Saint-Gobain Abrasives, Inc. Bonded abrasive tool and method of forming
US9409279B2 (en) 2008-12-30 2016-08-09 Saint-Gobain Abrasives, Inc. Bonded abrasive tool and method of forming
US20160244362A1 (en) * 2013-09-18 2016-08-25 Surface Tech LLC Method and Composition for Reinforcing Asphalt Cement Concrete
US9926672B2 (en) * 2013-09-18 2018-03-27 Surface Tech LLC Method and composition for reinforcing asphalt cement concrete
US11370704B2 (en) 2017-10-27 2022-06-28 Owens Corning Intellectual Capital, Llc Sizing compositions including weakly-coordinating anion salts and uses thereof
WO2019195069A1 (en) * 2018-04-05 2019-10-10 Ocv Intellectual Capital, Llc Carbon fibers with tuned stiffness
CN110981223A (zh) * 2019-12-18 2020-04-10 安徽省宁国昊成高温材料有限公司 一种耐高温玻璃纤维及其制备方法
CN110981223B (zh) * 2019-12-18 2022-05-03 安徽省宁国昊成高温材料有限公司 一种耐高温玻璃纤维及其制备方法
US20210276688A1 (en) * 2020-03-06 2021-09-09 Galactic Co., LLC Shaped Composite Vehicle Skins and Method for High Rate Manufacturing of Same
WO2021178730A1 (en) * 2020-03-06 2021-09-10 Galactic Co., LLC Shaped composite vehicle skins and method for high rate manufacturing of same

Also Published As

Publication number Publication date
CA2621606A1 (en) 2007-03-22
RU2008109060A (ru) 2009-10-20
KR20080067327A (ko) 2008-07-18
TW200718537A (en) 2007-05-16
AR055405A1 (es) 2007-08-22
JP2009508018A (ja) 2009-02-26
EP1924534A1 (en) 2008-05-28
AU2006291220A1 (en) 2007-03-22
CN101263091A (zh) 2008-09-10
WO2007032988A1 (en) 2007-03-22
BRPI0615750A2 (pt) 2011-05-24

Similar Documents

Publication Publication Date Title
US20070059506A1 (en) Glass fiber bundles for mat applications and methods of making the same
US20070032157A1 (en) Dually dispersed fiber construction for nonwoven mats using chopped strands
US20070057404A1 (en) Compression and injection molding applications utilizing glass fiber bundles
US5503920A (en) Process for improving parting strength of fiberglass insulation
US20110305904A1 (en) Sizing composition for glass fibers
US5900206A (en) Method of making a fibrous pack
US20110121482A1 (en) Methods of forming low static non-woven chopped strand mats
JPS5836950A (ja) ガラス繊維処理用水性組成物およびそれで処理されたガラス繊維
CA2831141C (en) Fiber glass strands and reinforced products comprising the same
EP1770072A1 (en) Method of making nonwoven fibrous mats and preforms and methods of use
US20070071973A1 (en) Method of making nonwoven fibrous mats and preforms and methods of use
US20110129608A1 (en) Methods of applying matrix resins to glass fibers
KR20220125298A (ko) 미네랄 울 기반의 절연 제품을 제조하는 방법
MX2008008476A (en) Compression and injection molding applications utilizing glass fiber bundles

Legal Events

Date Code Title Description
AS Assignment

Owner name: OWENS-CORNING FIBERGLAS TECHNOLOGY, INC., ILLINOIS

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:HAGER, WILLIAM G.;ADZIMA, LEONARD;WALDEN, DOUGLAS H.;AND OTHERS;REEL/FRAME:017170/0140;SIGNING DATES FROM 20051012 TO 20060104

AS Assignment

Owner name: OCV INTELLECTUAL CAPITAL, LLC, OHIO

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:OWENS-CORNING FIBERGLAS TECHNOLOGY, INC.;REEL/FRAME:022804/0879

Effective date: 20081121

Owner name: OCV INTELLECTUAL CAPITAL, LLC,OHIO

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:OWENS-CORNING FIBERGLAS TECHNOLOGY, INC.;REEL/FRAME:022804/0879

Effective date: 20081121

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION

AS Assignment

Owner name: OCV INTELLECTUAL CAPITAL, LLC, OHIO

Free format text: CORRECTIVE ASSIGNMENT TO CORRECT THE CORRECTIVE ASSIGNMENT TO REMOVED APPLICATION NUMBER 10/633,402 FROM THE PREVIOUSLY RECORDED REEL 022804 FRAME 0879;ASSIGNOR:OWENS-CORNING FIBERGLAS TECHNOLOGY, INC.;REEL/FRAME:023758/0769

Effective date: 20081121

Owner name: OCV INTELLECTUAL CAPITAL, LLC, OHIO

Free format text: CORRECTIVE ASSIGNMENT TO CORRECT THE CORRECTIVE ASSIGNMENT TO REMOVED APPLICATION NUMBER 10/633,402 FROM THE PREVIOUSLY RECORDED REEL 022804 FRAME 0879. PREVIOUSLY RECORDED ON REEL 022804 FRAME 0879. ASSIGNOR(S) HEREBY CONFIRMS THE OWENS-CORNING FIBERGLAS TECHNOLOGY, INC. EXECUTION DATE: 11/21/2008;ASSIGNOR:OWENS-CORNING FIBERGLAS TECHNOLOGY, INC.;REEL/FRAME:023758/0769

Effective date: 20081121