US20040224460A1 - Self-aligned process using indium gallium arsenide etching to form reentry feature in heterojunction bipolar transistors - Google Patents
Self-aligned process using indium gallium arsenide etching to form reentry feature in heterojunction bipolar transistors Download PDFInfo
- Publication number
- US20040224460A1 US20040224460A1 US10/435,230 US43523003A US2004224460A1 US 20040224460 A1 US20040224460 A1 US 20040224460A1 US 43523003 A US43523003 A US 43523003A US 2004224460 A1 US2004224460 A1 US 2004224460A1
- Authority
- US
- United States
- Prior art keywords
- layer
- emitter
- collector
- forming
- base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
- This invention relates to a heterojunction bipolar transistor (HBT), and more specifically to a self-aligned process for fabricating emitter and base metals for a HBT that reduces base resistance.
- A heterojunction bipolar transistor (HBT) is a bipolar transistor having two adjacent layers of different materials. FIG. 1 illustrates a
conventional HBT 10. HBT 10 includes acollector 12, abase 14, anemitter 16, and anemitter cap 18. -
Emitter metal 22 andbase metals 24 are typically made in a self-aligned process. In such a process,reentry features 20 are formed inemitter 16.Reentry features 20 are ledges, overhangs, and other features with an undercut profile.Reentry features 20 are formed by selectivelywet etching emitter 16. Metal is then deposited oncap 18 andbase 14 to formemitter metal 22 andbase metals 24, respectively. Reentry features 20 create breaks inemitter metal 22 andbase metals 24 so they are not electrically shorted. - One of the goals in designing an HBT is to minimize the base resistance, which is the resistance between
emitter 16 andbase metal 24 throughbase 14. One way to minimize the base resistance is to reduce a distance D betweenemitter 16 andbase metal 24. Distance D can be reduced by controlling the shape of reentry features 20. - As described above,
reentry features 20 can be formed by selectivelywet etching emitter 16 underneath a photoresist. FIGS. 2A and 2B illustrate a wet etch of an InP (indium phosphide) emitter 16 underneath aphotoresist 21 in a direction perpendicular to the (100) wafer flat. This wet etch forms ledges in theInP emitter 16 that can be used asreentry features 20. FIG. 2B also shows a wet etch of an InGaAs (indium gallium arsenide)cap 18underneath photoresist 21. This wet etch forms ramps 23 in the InGaAscap 18 that cannot be used as reentry features. - FIGS. 2A and 2C illustrate a wet etch of the
InP emitter 16 underneathphotoresist 21 in a direction parallel to the (100) wafer flat. This wet etch forms ramps 26 in theInP emitter 16 that cannot be used as reentry features. However,ramps 26 can be used as means to run metal lines up to the top layer. - Unfortunately, experiments show that wet etching perpendicular to the (100) wafer flat produces ledges with insufficient overhangs. This is illustrated in FIG. 2B, where distance D1 from a base metal (not shown) to emitter16 (created by a first reentry feature) is not sufficient to produce the overhang necessary to separate the metal deposited on
base 14 andemitter cap 18. - FIG. 3A illustrates a wet etching of the
InP emitter 16underneath photoresist 21 in a direction 45 degrees from the (100) wafer flat. This wet etch forms four ledges that can be used as reentry features 20. Unfortunately, experiments show that precise alignment (e.g., to less than one degree) of the wafer is necessary or inconsistent ledge shapes will form. In some cases, even ramps and other shapes may form instead of ledges. This is illustrated in FIG. 3B, where a misalignment of the wafer causes the wet etch to form aramp 28 underneathphotoresist 21 instead of a ledge. - FIG. 4 illustrates an HBT30 having
reentry features 32 formed by a combination of dry and wet etch ofemitter 16. A dry etch is first used to etch bothcap 18 and emitter 16 to form vertical sidewalls down tobase 14.Emitter 16 is next wet etched underneathcap 18 to create overhangs thatform reentry features 32. Unfortunately, dry etch is not selective and thus requires precise control to avoid etching intobase 14 and causing irreversible damage toHBT 30. - Thus, what is needed is a self-aligned process for fabricating emitter and base metal contacts while reducing base resistance in an HBT without precise alignment nor precise etch control.
- In one embodiment of the invention, a method for forming a heterojunction bipolar transistor (HBT) includes forming an etch mask atop an emitter cap layer of the HBT to expose a portion of the emitter cap layer, and selectively etching the exposed portion of the emitter cap layer to (1) form a reentry feature and (2) to expose a portion of the emitter layer. The method further includes selectively etching the exposed portion of the emitter layer to expose a portion of the base layer, and forming a metal layer over the exposed portion of the base layer and the exposed portion of the emitter cap layer.
- FIGS. 1, 2A,2B, 2C, 3A, 3B, and 4 illustrate conventional heterojunction bipolar transistors.
- FIG. 5 is a flowchart of a method for a self-aligned process to form metal contacts in an HBT in accordance with one aspect of the invention.
- FIGS. 6A, 6B,6C, 6D, 6E, and 6F are cross-sections of an HBT formed by the method of FIG. 5 in one embodiment of the invention.
- FIG. 7 is a flowchart of a method for a self-aligned process to form metal contacts in an HBT in accordance with another aspect of the invention.
- FIGS. 8A, 8B,8C, and 8D are cross-sections of an HBT formed by the method of FIG. 7 in one embodiment of the invention.
- The drawings provided are for illustrative purposes. The drawings are not to scale and do not represent the actual shape of the features unless otherwise specified.
- In accordance with one aspect of the invention, an etch mask is used to selectively etch an emitter cap, instead of the emitter, in a heterojunction bipolar transistor to form reentry features for metal deposition. The reentry features allow metal contacts to self-align on the emitter cap and the base during metal deposition.
- FIG. 5 is a flowchart of a
method 50 to form reentry features in one embodiment of the invention. Instep 52, the basic HBT layers are formed as shown in FIG. 6A. The basic HBT layers include asubstrate 92, asub-collector layer 94A, acollector layer 112A, abase layer 114A, anemitter layer 116A, and an emitter cap layer 1118A. -
Substrate 92 andsub-collector layer 94A are typically InP (indium phosphide),collector layer 112A are typically InGaAs (indium gallium arsenide) or InP,base layer 114A is typically InGaAs or GaAsSb (gallium arsenide antimony),emitter layer 116A is typically InP or AlInAs (aluminum indium arsenide), andcap layer 118A is typically InGaAs. These layers are appropriately doped to form an n-p-n or a p-n-p HBT. Additional, an AlInAs layer (not shown) can be inserted between the emitter and the base to improve device performance. In one embodiment, these layers are formed by OMVPE (organometallic vapor phase epitaxy). - In
steps 54 to 58, anetch masking layer 96 is formed and patterned as shown in FIG. 6B. Specifically, instep 54,etch masking layer 96 is formed atopcap layer 118A. The material ofetch masking layer 96 is selected to produce a ledge or overhang in theInGaAs cap layer 118A whencap layer 118A is selectively etched underneathetch masking layer 96. Thus, a photoresist cannot be used as an etch mask for theInGaAs cap layer 118A as it would produce a sidewall that is a ramp instead of a ledge or overhang as shown in FIG. 2B. In one embodiment, etch maskinglayer 96 is made of nitride. Nitride can be formed by PECVD (plasma enhanced chemical vapor deposition). Alternatively, etch maskinglayer 96 is made of InP. InP can be grown by OMVPE. - In
step 56, aphotoresist layer 98 is deposited over the device area and patterned to expose a portion ofetch masking layer 96. The unexposed portion ofetch masking layer 96 defines emitter 116 (shown later in FIG. 6C). - In
step 58, the exposed portion ofetch masking layer 96 is removed by a nitride etch. In one embodiment, etch maskinglayer 96 is dry etched using reactive ion etching (RIE). Afterwards,photoresist 98 can be stripped frometch masking layer 96. - In
step 60,emitter cap 118 is formed as shown in FIG. 6C.Cap 118 is formed by selectively etchingcap layer 118A, thereby forming sidewalls with reentry features 100 and exposingemitter layer 116A. As described above, reentry features 100 are features with an undercut profile such as ledges and overhangs. In one embodiment,cap layer 118A is selectively etched by a wet etch using a solution of DI (de-ionized) water, H2SO4 (sulphuric acid), and hydrogen peroxide (e.g., at a 300:30:30 ratio). Experiments show that reentry features 100 can be consistently produced with a wet etch of theInGaAs cap layer 118A underneath a nitride or InP etch maskinglayer 96. - In
step 62,emitter 116 is formed as shown in FIG. 6C.Emitter 116 is formed by selectively etchingemitter layer 116A, thereby exposingbase layer 114A. Asemitter layer 116A is not used to create the reentry features,emitter layer 116A is selectively etched to produce a more vertical sidewall thancap layer 118A. In one embodiment,emitter layer 116A is selectively etched by a wet etch using a solution of HCl (hydrochloric acid) and H3PO4 (phosphoric acid) (e.g., at a 1:3 or 3:2 ratio). - In
step 64,etch masking layer 96 is stripped. - In
step 66, base-collector mesa (includingbase 114 and collector 112) and sub-collector mesa (including sub-collector 94) are formed as shown in FIG. 6D. Base-collector mesa is first formed by depositing and patterning a nitride mask or a photoresist to expose and etch away portions ofbase layer 114A andcollector layer 112A. Sub-collector mesa is then formed by depositing and patterning a photoresist to expose and etch away portions ofsub-collector layer 94A. Conversely, the sub-collector mesa can be formed before the base-collector mesa in some embodiments. - In
step 68,sub-collector metal contacts 110 are formed as shown in FIG. 6E. In one embodiment,sub-collector metals 110 are formed by depositing and patterning aphotoresist 108 to openwindows 115 to sub-collector 94, and depositing metal atopphotoresist 108 and throughwindows 115.Sub-collector metals 110 are typically Ti/Au or Ti/Pt/Au. Subsequently,photoresist layer 108 is stripped and the metal deposited thereon is lifted off. - In
step 70, aphotoresist layer 102 is deposited over the device and patterned to open awindow 104 to cap 118 andbase layer 114A. Metal is deposited atopphotoresist layer 102 and throughwindow 104 to formemitter metal 22 andbase metals 24. In one embodiment, metal is evaporated ontocap 118 andbase 114 using electron beam or thermal evaporator.Emitter metal 22 andbase metals 24 are typically Ti/Au (titanium gold) or Ti/Pt/Au (titanium platinum gold). Subsequently,photoresist layer 102 is stripped and the metal deposited thereon is lifted off. - In accordance with another aspect of the invention, another etch mask is used to selectively etch the base and the collector layers in the heterojunction bipolar transistor to form reentry features. The reentry features on the cap, base, and collector layers allow their respective metal contacts to be formed in a single metal deposition process.
- FIG. 7 is a flowchart of a
method 140 in one embodiment of the invention.Method 140 includessteps 52 to 64 ofmethod 50 that form the structure shown in FIG. 6C.Step 64 is followed by astep 141. - In
steps 141 to 144, a secondetch masking layer 180 is formed and patterned using aphotoresist 182 as shown in FIG. 8A. Specifically, instep 141,etch masking layer 180 is formed over the device.Etch masking layer 180 can be made of nitride. In one embodiment,etch masking layer 180 is formed by plasma enhanced chemical vapor deposition. - In
step 142,photoresist layer 182 is deposited over the device and patterned to expose a portion ofetch masking layer 180. The unexposed portion ofetch masking layer 180 defines base 114 (FIG. 8B). - In
step 144, the exposed portion ofetch masking layer 180 is removed by a non-selective etch. In one embodiment,etch masking layer 180 is dry etched using reactive ion etching (RIE). After the dry etch,photoresist 182 can be stripped frometch masking layer 180. - In
step 146,base 114 andcollector 112 are formed as shown in FIG. 8B.Base 114 andcollector 112 are formed by selectively etchingbase layer 114A andcollector layer 112A, thereby forming sidewalls with reentry features 184 and exposingsub-collector layer 94A. In one embodiment,base layer 114A andcollector layer 112A are selectively etched by a wet etch. Wetetching base layer 114A andcollector layer 112A also consistently produces reentry features due to the crystallographic nature of the wet etch with the nitride mask. This occurs in the same way as whencap 118 andemitter 116 were etched. - In
steps 148 to 152, sub-collector 94 is formed as shown in FIG. 8C. Specifically, in astep 148,etch masking layer 180 is stripped. - In
step 150, aphotoresist 186 is deposited over the device and patterned to expose portions ofsub-collector layer 94A. - In
step 152, the exposed portions ofsub-collector layer 94A are selectively etched to formtrenches 187 to isolate the HBT from other devices. In one embodiment,sub-collector layer 94A is selectively etched by a wet etch. - In
steps emitter metal 22,base metals 24, andsub-collector metals 110 are formed as shown in FIG. 8D. Specifically, instep 154, aphotoresist 188 is deposited over the device and patterned to open awindow 190 to sub-collector 94,base 114, andcap 118. - In
step 156, metal is deposited atopphotoresist 188 and throughwindow 190 to formemitter metal 22,base metals 24, andsub-collector metals 110 in one step. In one embodiment, metal is deposited by electron beam or thermal evaporation. These metals are typically Ti/Au or Ti/Pt/Au. Subsequently,photoresist layer 108 is stripped and the metal deposited thereon is lifted off. - Various other adaptations and combinations of features of the embodiments disclosed are within the scope of the invention. In one embodiment, the above process can be modified to form a double HBT where the collector is made of InP instead of InGaAs. Specifically, the InGaAs base is selectively etched but the InP collector will be time etched (either dry or wet) until the InP sub-collector is reached and metal can be deposited thereon. In this embodiment, the base mesa includes only the base while the collector mesa includes the collector and the sub-collector. Numerous embodiments are encompassed by the following claims.
Claims (17)