US20030015261A1 - Process for preparing an aluminum alloy sheet with improved bendability and aluminum alloy sheet produced therefrom - Google Patents
Process for preparing an aluminum alloy sheet with improved bendability and aluminum alloy sheet produced therefrom Download PDFInfo
- Publication number
- US20030015261A1 US20030015261A1 US10/138,846 US13884602A US2003015261A1 US 20030015261 A1 US20030015261 A1 US 20030015261A1 US 13884602 A US13884602 A US 13884602A US 2003015261 A1 US2003015261 A1 US 2003015261A1
- Authority
- US
- United States
- Prior art keywords
- aluminum alloy
- weight
- aging
- sheet material
- sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- This application claims the benefit of U.S. Provisional Application Ser. No. 60/288,381, filed May 3, 2001.
- 1. Field of the Invention
- The present invention is directed to a process for preparing an aluminum alloy sheet having improved bendability and paint bake response. The invention is also directed to an aluminum alloy sheet obtained by the process.
- 2. Description of the Prior Art
- There is a continuing and growing need for improved aluminum alloys with improved properties particularly for use in the automotive industry. To be useful to the automotive industry, an aluminum alloy sheet product must possess good forming characteristics in the as-supplied temper so that it can be shaped and bent as desired. At the same time, the alloy product after shaping, painting and baking must have sufficient strength to resist dents and other impacts.
- Aluminum alloys of the AA (Aluminum Association) 6000 series are desired to have low yield strength in the as-supplied temper and high yield strength in the finished product. The low yield strength in the as-supplied temper is desirable to obtain excellent formability and reduced springback, while high yield strength in the finished product is required for adequate dent resistance at the lowest possible gauge for maximum weight savings.
- U.S. Pat. No. 5,266,130 Uchida et al., issued Nov. 30, 1993 describes a process for manufacturing an aluminum alloy sheet material having good shape fixability and bake hardenability by regulating the heat pattern in the step of cooling after the solution heat treatment. The sheet is first rapidly cooled to a quench temperature of 60 to 250° C. and then further cooled at a rate based on the specific quench temperature. One aluminum alloy containing 0.8% Si, 0.7% Mg, 0.20% Mn and 0.15% Fe included a pre-aging treatment incorporating a cooling rate of 4° C./min from 150 to 50° C. Another alloy containing 0.8% Si, 0.7% Mg, 0.30% Cu, 0.10% Mn, 0.15% Fe, 0.02% Ti and 20 ppm B was subjected to the same pre-aging treatment.
- U.S. Pat. No. 5,616,189 Jin et al., issued Apr. 1, 1997 describes an aluminum alloy containing magnesium, silicon and optionally copper in amounts suitable for the preparation of a sheet for use in the automotive industry. The patent also describes a process for preparing an aluminum alloy sheet with suitable properties for use in the automotive industry. Among aluminum alloys tested were an alloy containing 0.30% Cu, 0.50% Mg, 0.70% Si, 0.05% Mn and 0.22% Fe and another alloy containing 0.29% Cu, 0.52% Mg, 0.68% Si, 0.07% Mn and 0.21% Fe. A sheet produced from these alloys was subjected to a 5 hour pre-aging treatment at 85° C. The patent also states that sheet can be coiled at 85° C. and allowed to cool slowly to ambient at a rate less than 10° C./hour.
- It is an object of the present invention to provide an improved processing technique whereby an aluminum alloy sheet is formed which has excellent bendability and paint bake response.
- The paint bake response of conventional AA (Aluminum Association) 6000 series aluminum alloys is complex. These alloys in the as-supplied condition contain a large number of fine clusters and zones uniformly distributed throughout the matrix. During a paint cure step, some fine unstable clusters and zones re-dissolve in the matrix, while others grow in size to improve strength during hardening. The exact mechanism explaining how the bendability and paint bake response are improved is not entirely understood. It is believed that the process of the present invention slows the formation of clusters and zones and produces mostly those that do not re-dissolve during the paint cure step. Therefore, a large number of fine clusters and zones become available for nucleation of the hardening particles and hence improve aging response.
- The alloys of the present invention are automotive aluminum alloys of AA6000 series containing (in percentages by weight) 0.50-0.75% Mg, 0.7-0.85% Si, 0.15-0.35% Mn, 0.1-0.3% Fe and the balance being aluminum and incidental impurities. Preferably, the alloy also contains 0.2-0.4% Cu.
- The alloy is cast into ingots by semi-continuous casting, e.g. direct chill (DC) casting. The ingots are homogenized and hot rolled to reroll gauge, then cold rolled and solution heat treated. The heat treated sheet may be quenched to a desired initial pre-aging temperature. The sheet product thus obtained is subjected to the pre-aging procedure of this invention and this pre-aging can be either the final step of the solution heat treatment stage or it can be part of a separate reheating step.
- For the pre-aging, the sheet material starts with an initial pre-aging temperature which is at least 80° C. and may be as high as 175° C. or more. A preferred initial pre-aging temperature is in the range of 95 to 200° C., more preferably 95 to 185° C. Starting from this pre-aging temperature, the sheet material is rapidly cooled to ambient, e.g. 25° C., at a rate of more than 5° C./hour. This cooling rate is preferably in the range of 10 to 600° C./hour.
- The combination of excellent bendability and paint bake response is achieved by (a) the specific composition of the alloy and (b) the appropriate pre-aging procedure. This slows the natural aging, stabilizes yield strength at lower values and significantly improves the paint bake response in the sheet compared with conventionally produced counterparts.
- In the drawings which illustrate this invention:
- FIG. 1 shows the effect of cooling rate on yield strength (YS) for different pre-aging temperatures;
- FIG. 2 shows the effect of cooling rate on longitudinal bendability for different pre-aging temperatures; and
- FIG. 3 shows the effect of cooling rate on transverse bendability for different pre-aging temperatures.
- It is a specific objective of this invention to provide a sheet material having a low T4P yield strength and a high T8 yield strength. The low T4P yield strength promotes improved formability, particularly hemming performance without cracking. The high T8 yield strength indicates a good paint bake response, i.e. after painting and baking the sheet has sufficient strength to resist dents and withstand other impacts. For this purpose the target physical properties for the sheet products of this invention are as follows:
T4P, YS 90-120 MPa T4P, UTS >200 MPa T4P, E1 >28% ASTM, >30% (Using JIS Specimen) BEND, rmin/t <0.5 T8 (0% strain), YS >210 MPa T8 (2% strain), YS >220 MPa - The alloy used in this invention is cast by direct chill (DC) casting. The ingots are homogenized for more than 5 hours at a temperature of more than 550° C. The ingot is hot rolled to a reroll exit gauge of about 2.5-6 mm at an exit temperature of about 300-380° C. The cold roll is to about 1mm gauge and the solution heat treatment is typically at a temperature of about 530-570° C.
- When the procedure includes an interannealing step, the reroll sheet is cold rolled to an intermediate gauge of about 2.0-3.0 mm. This intermediate sheet is batch annealed at a temperature of about 345-410° C. and then further cold rolled to about 1.0 mm.
- Alloys containing 0.6% Mg, 0.8% Si, 0.25% Fe and 0.20% Mn and with or without 0.25% Cu were cast as 95 mm×228 mm ingots to carry out the experiments. The ingots were scalped, homogenized at 560° C. for 6 hours, hot rolled to 3.5 mm gauge, cold rolled to 2.1 mm in one pass, batch annealed at 360° C. for one hour and cold rolled to 0.93 mm gauge. This sheet material was solution heat treated at 560° C. for 5 minutes.
- The solution heat treated sheet material was pre-aged by cooling from different pre-aging temperatures, including 105° C., 125° C., 150° C. and 175° C. Different cooling rates were used ranging from 1.25° C./hour to 600° C./hour. YS (yield strength), UTS (tensile strength), El (total elongation), n (strain hardening index) and Bendability (r/t) were measured. This r/t ratio was determined from triplicate specimens according to the ASTM E 290C standard wrap bend test method. The minimum r/t value was obtained by dividing with the sheet thickness, the minimum radius of the mandrel that produced a crack free bend. The radius of the mandrels used for the measurements were 0.001″, 0.002″, 0.003″, 0.004″, 0.006″, 0.008″, 0.010″, 0.012″, 0.016″, 0.020″, 0.024″, 00.28″, 0.032″, 0.040″, 0.048″, 0.056″ and so on.
- The measurements were made based on T4P temper with natural aging of two and four weeks. The term “P” means that the sheet material has been pre-aged. T8 represents the YS after a simulated paint bake of 2% strain and 30 minutes at 177° C.
- Tables 1 and 2 show the mechanical properties for a sheet formed from an alloy containing 0.6% Mg, 0.8% Si, 0.25% Fe, 0.20% Mn and the balance Al and incidental impurities. From Table 1 (two weeks of natural aging) it can be seen that good combinations of low T4P yield strengths and high T8 yield strengths were obtained for a number of combinations of pre-aging temperatures between 105° C. and 175° C. and cooling rates between 20 and 600° C./hour. Particularly good results were obtained by cooling from 125° C. at 20° C./hour, 150° C. at 60° C./hour and 175° C. at 600° C./hour. Also shown in Tables 1 and 2 are results without a pre-age. The T8 properties are significantly reduced compared to the pre-age practice.
- Table 2 is similar to Table 1 except that the samples were naturally aged for four weeks. The results are not significantly different from those of Table 1. The stability of properties over time is a particularly desirable feature.
- FIGS. 1, 2 and3 show the effects of cooling rates from different start of cooling temperatures on the yield strength and bendability. FIG. 1 shows that the use of slower cooling rates from high temperatures increases the yield strength in the T4P and T8 tempers due to artificial aging and affects bendability adversely. The best combination of properties is obtained with faster cooling rates from high start of cooling temperatures as seen in Table 1.
TABLE 1 Mechanical Properties of Al-0.6% Mg-0.8% Si-0.25% Fe-0.20% Mn Alloy Pre-aged in Different Conditions and Naturally Aged for 2 Weeks Pre- aging Cooling Temp rate YS UTS Bendability (° C.) (° C./h) Temper (MPa) (MPa) % El n L T No — T4 115.2 234.8 28.1 0.28 0.21 0.21 Pre- T8 173.7 248.9 22.0 0.20 — — age 105 1.25 T4P 131.6 243.8 23.9 0.26 0.33 0.28 T8 242.0 299.6 19.1 0.15 — — 20 T4P 105.8 222.7 23.0 0.29 0.08 0.05 T8 214.7 280.3 20.1 0.17 — — 60 T4P 108.6 226.0 21.3 0.29 0.08 0.08 T8 216.6 281.8 19.7 0.16 — — 125 1.25 T4P 171.1 268.4 21.8 0.21 0.64 0.43 T8 264.2 310.7 17.6 0.12 — — 20 T4P 105.2 220.7 23.1 0.29 0.03 0.03 T8 234.0 292.7 18.4 0.15 — — 60 T4P 107.1 225.0 23.5 0.29 0.08 0.03 T8 223.1 287.4 18.7 0.16 — — 150 1.25 T4P 246.9 304.9 15.8 0.12 1.54 1.55 T8 296.8 322.0 13.2 0.08 — — 60 T4P 106.7 220.0 23.1 0.28 0.06 0.03 T8 249.5 300.6 16.6 0.13 — — 240 T4P 112.5 223.3 22.4 0.28 0.08 0.08 T8 232.3 293.1 18.2 0.15 — — 175 1.25 T4P 298.0 325.5 10.6 0.06 2.67 2.29 T8 312.3 324.0 8.5 0.05 — — 120 T4P 113.1 222.5 22.5 0.27 0.18 0.03 T8 249.3 297.0 16.4 0.13 — — 600 T4P 106.2 220.1 24.9 0.28 0.03 0.03 T8 245.9 295.9 17.1 0.13 — — -
TABLE 2 Mechanical Properties of Al-0.6% Mg-0.8% Si-0.25% Fe-0.2% Mn Alloy Pre-aged in Different Conditions and Naturally Aged for 4 Weeks Pre- aging Cooling Temp rate YS UTS Bendability (° C.) (° C./h) Temper (MPa) (MPa) % El n L T No — T4 116.7 235.5 25.8 0.28 0.21 0.16 Pre- T8 172.2 248.1 20.1 0.20 — — age 105 1.25 T4P 133.2 246.2 23.6 0.26 0.27 0.22 T8 244.5 302.4 18.8 0.15 — — 20 T4P 114.0 231.7 23.9 0.28 0.11 0.05 T8 215.2 281.4 20.1 0.17 — — 60 T4P 114.7 233.4 24.9 0.28 0.11 0.08 T8 213.0 281.4 19.5 0.17 — — 125 1.25 T4P 172.2 268.9 22.8 0.21 0.54 0.44 T8 268.0 313.9 17.2 0.12 — — 20 T4P 114.5 230.8 24.3 0.28 0.05 0.02 T8 235.6 296.3 18.3 0.15 — — 60 T4P 115.3 233.2 24.9 0.28 0.08 0.03 T8 223.1 287.7 18.9 0.16 — — 150 1.25 T4P 251.1 312.2 17.3 0.12 1.52 1.52 T8 298.3 323.6 13.4 0.08 — — 60 T4P 114.5 227.6 23.6 0.28 0.05 0.03 T8 248.1 300.9 16.6 0.13 — — 240 T4P 118.5 234.9 24.3 0.28 0.21 0.08 T8 230.5 290.4 18.3 0.16 — — 175 1.25 T4P 301.1 326.9 9.3 0.05 2.62 2.30 T8P 310.4 322.3 8.3 0.05 — — 120 T4P 120.3 225.8 22.7 0.26 0.11 0.03 T8 253.9 301.5 16.6 0.12 — — 600 T4P 119.0 227.8 23.9 0.27 0.21 0.03 T8 247.4 298.1 17.3 0.13 — — - Tables 3 and 4 summarize the average tensile properties of the 0.25% Cu containing alloy after two and four weeks of natural aging. The trends obtained from this alloy are very similar to the Cu free alloy. Generally, the artificial aging response of the alloy is better and this translates into a higher yield strength, especially in situations where cooling is carried out from high temperatures. In general, the paint bake response and bendability following cooling from 125° C. at 20° C./hour are excellent after two weeks of natural aging, although there is a slight deterioration after four weeks of natural aging.
TABLE 3 Mechanical Properties of Al-0.6% Mg-0.8% Si-0.3% Cu-0.25% Fe-0.20% Mn Alloy Pre-aged in Different Conditions and Naturally Aged for 2 Weeks Pre- aging Cooling Temp rate YS UTS Bendability (° C.) (° C./h) Temper (MPa) (MPa) % El n L T No — T4 122.5 252.8 25.8 0.29 0.27 0.16 Pre- T8 189.9 271.4 22.9 0.20 — — age 105 1.25 T4P 146.5 270.8 25.7 0.26 0.56 0.41 T8 263.1 325.7 19.9 0.15 — — 20 T4P 110.9 239.3 22.9 0.30 0.23 0.03 T8 235.1 305.8 19.8 0.16 — — 60 T4P 116.3 245.5 25.9 0.29 0.28 0.09 T8 235.5 305.2 19.5 0.16 — — 125 1.25 T4P 216.8 316.6 21.1 0.19 1.12 1.12 T8 290.8 339.3 17.6 0.12 — — 20 T4P 112.7 242.1 27.0 0.30 0.06 0.06 T8 253.7 316.6 19.1 0.15 — — 60 T4P 116.4 246.6 25.2 0.29 0.28 0.08 T8 244.1 309.8 18.1 0.15 — — 150 1.25 T4P 269.7 340.8 16.0 0.12 2.36 1.78 T8 314.2 347.4 14.2 0.09 — — 60 T4P 131.6 253.7 24.6 0.27 0.34 0.17 T8 275.5 331.3 17.3 0.13 — — 240 T4P 121.3 248.1 25.8 0.28 0.28 0.08 T8 247.4 312.2 19.1 0.15 — — 175 1.25 T4P 306.0 351.3 12.3 0.08 2.67 2.34 T8 334.0 350.1 10.3 0.06 — — 120 T4P 163.2 270.8 21.0 0.23 0.46 0.25 T8 292.0 337.4 17.4 0.11 — — 600 T4P 142.4 253.9 22.6 0.25 0.28 0.18 T8 280.4 331.7 16.5 0.12 — — -
TABLE 4 Mechanical Properties of Al-0.6% Mg-0.8% Si-0.3% Cu-0.25% Fe-0.20% Mn Alloy Pre-aged in Different Conditions and Naturally Aged for 4 Weeks Pre- aging Cooling Temp rate YS UTS Bendability (° C.) (° C./h) Temper (MPa) (MPa) % El n L T No — T4 127.0 260.0 26.6 0.28 0.33 0.22 Pre- T8 191.8 270.9 19.9 0.19 — — age 105 1.25 T4P 149.4 273.6 25.9 0.26 0.56 0.28 T8 264.7 327.9 19.7 0.15 — — 20 T4P 119.4 249.5 26.5 0.29 0.28 0.08 T8 233.1 305.1 20.3 0.17 — — 60 T4P 121.7 250.6 25.5 0.29 0.23 0.08 T8 222.0 291.2 20.1 0.17 — — 125 1.25 T4P 216.9 317.2 21.6 0.19 1.12 1.12 T8 294.1 342.6 17.9 0.12 — — 20 T4P 127.6 253.9 25.6 0.28 0.28 0.03 T8 255.3 319.8 20.0 0.15 — — 60 T4P 124.0 253.4 25.3 0.28 0.28 0.03 T8 240.5 309.2 20.1 0.16 — — 150 1.25 T4P 270.3 342.5 16.5 0.12 2.29 1.74 T8 317.3 350.0 14.7 0.09 — — 60 T4P 132.0 255.1 23.2 0.27 0.28 0.28 T8 271.9 326.8 17.8 0.13 — — 240 T4P 127.7 255.6 26.4 0.28 0.33 0.17 T8 251.3 314.2 18.3 0.15 — — 175 1.25 T4P 308.3 352.8 12.2 0.08 2.68 2.35 T8 335.9 351.6 10.5 0.06 — — 120 T4P 169.0 270.8 20.3 0.22 0.39 0.28 T8 295.0 338.2 17.0 0.11 — — 600 T4P 151.0 255.3 21.5 0.23 0.27 0.16 T8 292.5 337.0 15.4 0.11 — — - The pre-aged sheet material obtained according to this invention can be coiled for future use. It is also possible to have the alloy sheet move directly from solution heat treatment to a cleaning bath where the rapid cooling pre-aging takes place.
- It is further possible to conduct the pre-aging by starting with the pre-aging temperature and first naturally cooling the sheet in still air at a cooling rate of 1-1.5° C./hour and thereafter continuing with a rapid cooling in accordance with the pre-aging process described hereinbefore.
Claims (10)