TWI853844B - 無鹼玻璃板 - Google Patents
無鹼玻璃板 Download PDFInfo
- Publication number
- TWI853844B TWI853844B TW108136429A TW108136429A TWI853844B TW I853844 B TWI853844 B TW I853844B TW 108136429 A TW108136429 A TW 108136429A TW 108136429 A TW108136429 A TW 108136429A TW I853844 B TWI853844 B TW I853844B
- Authority
- TW
- Taiwan
- Prior art keywords
- alkali
- sro
- bao
- mgo
- mol
- Prior art date
Abstract
本發明的無鹼玻璃板的特徵在於：玻璃組成中的Li2
O+Na2
O+K2
O的含量為0 mol%～0.5 mol%，楊氏模量為78 GPa以上，應變點為680℃以上，液相溫度為1450℃以下。
Description
本發明是有關於一種無鹼玻璃板，尤其是有關於一種適合於有機電致發光(electroluminescence，EL)顯示器的無鹼玻璃板。
有機EL顯示器等電子元件由於為薄型且動態圖像顯示優異，並且消耗電力亦低，因此用於可撓性元件或行動電話的顯示器等的用途。
作為有機EL顯示器的基板，廣泛使用玻璃板。對於該用途的玻璃板，主要要求以下特性。
(1)為了防止於在熱處理步驟中成膜的半導體物質中鹼離子發生擴散的事態，基本不含鹼金屬氧化物，即無鹼玻璃(玻璃組成中的鹼金屬氧化物的含量為0.5mol%以下)；(2)為了使玻璃板低廉化，生產性優異、尤其是熔融性或耐失透性優異；(3)於低溫多晶矽(low temperature poly silicon，LTPS)製程中，為了減低玻璃板的熱收縮，應變點高。
[專利文獻1]日本專利特開2012-106919號公報
[發明所欲解決之課題]
且說，有機EL元件亦廣泛擴展至有機EL電視。有機EL電視的面板尺寸大幅大於行動製品。預想今後增強對玻璃板的大型化、薄型化的要求。玻璃板越大型化、薄型化，玻璃板越容易彎曲，容易產生各種不良情況。
由玻璃製造商成形的玻璃板雖經過切斷、緩冷、檢查、清洗等步驟，但於該些步驟中，將玻璃板投入形成有多段架的盒中並加以搬出。該盒通常可於形成於左右的內側面的架上載置玻璃板的相對的兩邊並在水平方向上加以保持，但大型且薄的玻璃板的彎曲量大，因此在將玻璃板投入盒時，玻璃板的一部分與盒接觸而破損，在搬出時，容易大幅擺動而變得不穩定。此種形態的盒亦被電子元件製造商使用，因此產生相同的不良情況。
進而，有機EL元件越大型化、薄型化，玻璃板越容易彎曲，因此有有機EL電視的圖像面看起來變形之虞。
為了解決該問題，有效的是提高玻璃板的楊氏模量（Young’s modulus）來減低彎曲量的方法。
另外，如上所述，於LTPS製程中，為了減低玻璃板的熱收縮，需要提高玻璃板的應變點。
但是，若欲提高玻璃板的楊氏模量與應變點，則玻璃組成的平衡崩潰，熔融性或耐失透性容易下降，玻璃板的生產性容易下降。結果，玻璃板的原板成本會高漲。
因此，本發明是鑒於所述情況而發明出，其技術性課題為提供一種生產性優異且應變點與楊氏模量充分高的無鹼玻璃板。
[解決課題之手段]
本發明者反覆進行了多種實驗，結果發現，藉由對無鹼玻璃板的玻璃特性進行嚴格限制而可解決所述技術性課題，從而作為本發明來提出。即，本發明的無鹼玻璃板的特徵在於：玻璃組成中的Li2
O+Na2
O+K2
O的含量為0 mol%～0.5 mol%，楊氏模量為78 GPa以上，應變點為680℃以上，液相溫度為1450℃以下。此處，「Li2
O+Na2
O+K2
O」是指Li2
O、Na2
O及K2
O的合計量。「楊氏模量」是指藉由彎曲共振法進行測定而得的值。再者，1 GPa相當於約101.9 Kgf/mm2
。「應變點」是指基於美國材料與試驗協會（American Society for Testing and Materials，ASTM）C336的方法進行測定而得的值。「液相溫度」是指將通過標準篩30目（500 μm）而殘留於50目（300 μm）中的玻璃粉末放入鉑舟（platinum boat）中，於溫度梯度爐中保持24小時後，結晶析出的溫度。
另外，本發明的無鹼玻璃板較佳為：作為玻璃組成，以mol%計而含有58%～68%的SiO2
、11%～18%的Al2
O3
、1.5%～6%的B2
O3
、0%～0.5%的Li2
O+Na2
O+K2
O、4%～10%的MgO、2%～10%的CaO、2%～13%的SrO+BaO。此處，所謂「SrO+BaO」，是指SrO+BaO的合計量。
另外，本發明的無鹼玻璃板較佳為：作為玻璃組成，以mol%計而含有58%～67%的SiO2
、11%～18%的Al2
O3
、1.5%～6%的B2
O3
、0%～0.5%的Li2
O+Na2
O+K2
O、4%～10%的MgO、2%～10%的CaO、1.5%～8%的SrO、1.5%～8%的BaO，實質不含As2
O3
、Sb2
O3
。此處，所謂「實質不含As2
O3
、Sb2
O3
」，是指玻璃組成中的As2
O3
、Sb2
O3
的含量分別未滿0.05%的情況。
另外，本發明的無鹼玻璃板較佳為進而含有0.001 mol%～1 mol%的SnO2
。
另外，本發明的無鹼玻璃板較佳為應變點為690℃以上。
另外，本發明的無鹼玻璃板較佳為楊氏模量高於80 GPa。
另外，本發明的無鹼玻璃板較佳為30℃～380℃的溫度範圍內的平均熱膨脹係數為30×10-7
/℃～50×10-7
/℃。此處，「30℃～380℃的溫度範圍內的平均熱膨脹係數」可利用膨脹計進行測定。
另外，本發明的無鹼玻璃板較佳為液相黏度為104.5
dPa·s以上。此處，「液相黏度」是指液相溫度下的玻璃的黏度，可利用鉑球提拉法進行測定。
另外，本發明的無鹼玻璃板較佳為用於有機EL元件。
本發明的無鹼玻璃板較佳為：作為玻璃組成，以mol%計而含有58%～72%的SiO2
、11%～18%的Al2
O3
、1.5%～6%的B2
O3
、0%～0.5%的Li2
O+Na2
O+K2
O、0%～10%的MgO、0%～10%的CaO、0%～8%的SrO、0%～8%的BaO，進而佳為含有58%～68%的SiO2
、11%～18%的Al2
O3
、1.5%～6%的B2
O3
、0%～0.5%的Li2
O+Na2
O+K2
O、4%～10%的MgO、2%～10%的CaO、2%～13%的SrO+BaO；特佳為含有58%～67%的SiO2
、11%～18%的Al2
O3
、1.5%～6%的B2
O3
、0%～0.5%的Li2
O+Na2
O+K2
O、4%～10%的MgO、2%～10%的CaO、1.5%～8%的SrO、1.5%～8%的BaO，實質不含As2
O3
、Sb2
O3
。以下示出如所述般限定各成分的含量的理由。再者，於各成分的含量的說明中，除有特別說明的情況以外，%表達表示mol%。
SiO2
為形成玻璃骨架的成分。若SiO2
的含量過少，則熱膨脹係數變高，密度增加。因此，SiO2
的下限量較佳為58%，進而佳為59%，進而佳為60%，進而佳為61%，進而佳為62%，進而佳為63%，最佳為64%。另一方面，若SiO2
的含量過多，則楊氏模量下降，進而，高溫黏度變高，熔融時所需的熱量變多，熔融成本高漲，並且有產生由SiO2
原料的熔融殘留引起的不良而成為良率下降的原因之虞。另外，方矽石（cristobalite）等的失透結晶容易析出，液相黏度容易下降。因此，SiO2
的上限量較佳為72%，進而佳為71%，進而佳為70%，進而佳為69.5%，進而佳為69%，進而佳為68%，最佳為67%。
Al2
O3
為形成玻璃骨架的成分，且是提高楊氏模量的成分，進而是使應變點上昇的成分。若Al2
O3
的含量過少，則楊氏模量容易下降，且應變點容易下降。因此，Al2
O3
的下限量較佳為11%，更佳為11.2%，更佳為11.4%，進而佳為11.6%，進而佳為11.8%，最佳為12%。另一方面，若Al2
O3
的含量過多，則富鋁紅柱石（mullite）等的失透結晶容易析出，液相黏度容易下降。因此，Al2
O3
的上限量較佳為18%，更佳為17%，更佳為16%，進而佳為15.5%，進而佳為15%，最佳為14%。
以mol%比計，SiO2
/Al2
O3
較佳為4.2～5.8，更佳為4.5～5.5，特佳為4.8～5.3。若SiO2
/Al2
O3
過小，則應變點及/或耐失透性容易下降。另一方面，若SiO2
/Al2
O3
過大，則楊氏模量及/或熔融性容易下降。再者，「SiO2
/Al2
O3
」是指SiO2
的含量除以Al2
O3
的含量而得的值。
B2
O3
為提高熔融性或耐失透性的成分。若B2
O3
的含量過少，則熔融性或耐失透性容易下降。因此，B2
O3
的下限量較佳為1.5%，更佳為1.8%，更佳為2.0%，進而佳為2.2%，進而佳為2.4%，最佳為2.5%。另一方面，若B2
O3
的含量過多，則楊氏模量或應變點容易下降。因此，B2
O3
的上限量較佳為6%，更佳為5.7%，更佳為5.3%，進而佳為5.0%，進而佳為4.8%，最佳為4.5%。
以mol%比計，Al2
O3
/B2
O3
較佳為3～7.5，更佳為3.5～6，特佳為4～5。若Al2
O3
/B2
O3
過小，則楊氏模量容易下降。另一方面，若Al2
O3
/B2
O3
過大，則耐失透性容易下降。再者，「Al2
O3
/B2
O3
」是指Al2
O3
的含量除以B2
O3
的含量而得的值。
Li2
O、Na2
O及K2
O的合計量為0%～0.5%，較佳為0%～0.2%，更佳為0%～0.15%。若Li2
O、Na2
O及K2
O的合計量過多，則有導致於在熱處理步驟中成膜的半導體物質中鹼離子發生擴散的事態之虞。
MgO於鹼土類金屬氧化物中為顯著提高楊氏模量的成分。若MgO的含量過少，則熔融性或楊氏模量容易下降。因此，MgO的下限量較佳為0%，更佳為2%，更佳為2.5%，進而佳為3%，進而佳為3.5%，進而佳為4%，進而佳為4.2%，最佳為4.5%。另一方面，若MgO的含量過多，則富鋁紅柱石等的失透結晶容易析出，液相黏度容易下降。因此，MgO的上限量較佳為10%，更佳為9.5%，更佳為9%，進而佳為8.5%，進而佳為8%，進而佳為7.5%，進而佳為7%，進而佳為6.8%，最佳為6.5%。
以mol%比計，（Al2
O3
+MgO）/B2
O3
較佳為3.5～10，更佳為4～8，特佳為4.5～6。若（Al2
O3
+MgO）/B2
O3
過小，則楊氏模量容易下降。另一方面，若（Al2
O3
+MgO）/B2
O3
過大，則耐失透性容易下降。再者，「（Al2
O3
+MgO）/B2
O3
」是指Al2
O3
與MgO的合計量除以B2
O3
的含量而得的值。
CaO為不使應變點下降而降低高溫黏性並顯著提高熔融性的成分。另外，為提高楊氏模量的成分。若CaO的含量過少，則熔融性容易下降。因此，CaO的下限量較佳為0%，更佳為2%，更佳為2.5%，進而佳為2.8%，進而佳為3%，進而佳為3.5%，進而佳為3.8%，最佳為4%。另一方面，若CaO的含量過多，則有熱膨脹係數不合理地變高之虞。因此，CaO的上限量較佳為10%，更佳為9.8%，更佳為9.5%，進而佳為9%，進而佳為8.8%，進而佳為8.5%，進而佳為8%，進而佳為7.8%，最佳為7.5%。
SrO為提高耐失透性的成分，進而是不使應變點下降而降低高溫黏性並提高熔融性的成分。另外，為抑制液相黏度的下降的成分。若SrO的含量過少，則難以享有所述效果。因此，SrO的下限量較佳為0%，更佳為0.1%，更佳為0.2%，進而佳為0.3%，進而佳為0.4%，進而佳為0.5%，進而佳為0.7%，進而佳為0.8%，最佳為超過1%。另一方面，若SrO的含量過多，則熱膨脹係數與密度容易增加。因此，SrO的上限量較佳為8%，更佳為7.5%，更佳為7%，進而佳為6.5%，最佳為6%。
BaO為提高耐失透性的成分。若BaO的含量過少，則難以享有所述效果。因此，BaO的下限量較佳為0%，更佳為0.2%，更佳為0.5%，進而佳為1%，進而佳為1.3%，最佳為1.5%。另一方面，若BaO的含量過多，則楊氏模量容易下降，且熱膨脹係數與密度容易增加。因此，BaO的上限量較佳為10%，更佳為8%，更佳為7%，進而佳為6%，進而佳為5%，進而佳為4%，最佳為3.6%。
若MgO、CaO、SrO及BaO的合計量過少，則熔融性容易下降。因此，MgO、CaO、SrO及BaO（RO）的合計量的下限較佳為13%，更佳為14%，更佳為15%，進而佳為15.2%，最佳為15.5%。另一方面，若MgO、CaO、SrO及BaO的合計量過多，則熱膨脹係數與密度容易增加。因此，MgO、CaO、SrO及BaO（RO）的合計量的上限較佳為24%，更佳為22%，更佳為21%，進而佳為20%，最佳為19%。
若SrO與BaO的合計量過少，則耐失透性與熔融性容易下降。因此，SrO與BaO的合計量的下限較佳為0%，更佳為1%，更佳為1.5%，進而佳為2%，最佳為2.5%。另一方面，若SrO與BaO的合計量過多，則楊氏模量容易下降，且熱膨脹係數與密度容易增加。因此，SrO與BaO的合計量的上限較佳為13%，更佳為10%，更佳為8%，進而佳為7%，進而佳為6%，最佳為5%。
以mol%比計，（MgO+CaO）/（SrO+BaO）較佳為2.1～10，更佳為3～7，特佳為4～5。若（MgO+CaO）/（SrO+BaO）過小，則楊氏模量容易下降。另一方面，若（MgO+CaO）/（SrO+BaO）過大，則耐失透性容易下降。再者，「（MgO+CaO）/（SrO+BaO）」是指MgO與CaO的合計量除以SrO與BaO的合計量而得的值。
除所述成分以外，例如亦可添加以下成分作為任意成分。再者，就確實享有本發明的效果的觀點而言，所述成分以外的其他成分的含量以合計量計較佳為10%以下、尤其是5%以下。
ZnO為提高熔融性的成分。但是，若大量含有ZnO，則玻璃容易失透，且應變點容易下降。ZnO的含量較佳為0%～5%、0%～3%、0%～2%、尤其是0%～未滿1%。
P2
O5
為提高應變點的成分，並且是可顯著抑制鈣長石（anorthite）等鹼土類鋁矽酸鹽系的失透結晶的析出的成分。但是，若大量含有P2
O5
，則玻璃容易分相。P2
O5
的含量較佳為0%～2.5%，更佳為0.0005%～1.5%，進而佳為0.001%～0.5%，特佳為0.005%～0.3%。
以mol%比計，Al2
O3
/（10000×P2
O5
）較佳為0.12～10，更佳為0.2～5，特佳為0.3～2。若Al2
O3
/（10000×P2
O5
）過小，則楊氏模量容易下降。另一方面，若Al2
O3
/（10000×P2
O5
）過大，則鈣長石等鹼土類鋁矽酸鹽系的失透結晶容易析出。再者，「Al2
O3
/（10000×P2
O5
）」是指Al2
O3
的含量除以P2
O5
的含量的10000倍而得的值。
TiO2
為降低高溫黏性並提高熔融性的成分，並且是抑制曝曬（solarization）的成分，但若大量含有TiO2
，則玻璃著色，透過率容易下降。TiO2
的含量較佳為0%～2.5%，更佳為0.0005%～1%，進而佳為0.001%～0.5%，特佳為0.005%～0.1%。
以mol%比計，Al2
O3
/（1000×TiO2
）較佳為0.1～10，更佳為0.6～4，特佳為1.1～1.6。若Al2
O3
/（1000×TiO2
）過小，則楊氏模量容易下降。另一方面，若Al2
O3
/（1000×TiO2
）過大，則熔融性或耐曝曬性容易下降。再者，「Al2
O3
/（1000×TiO2
）」是指Al2
O3
的含量除以TiO2
的含量的1000倍而得的值。
Y2
O3
、Nb2
O5
、La2
O3
中具有提高應變點、楊氏模量等的作用。該些成分的合計量及個別含量較佳為0%～5%，更佳為0%～1%，進而佳為0%～0.5%。若Y2
O3
、Nb2
O5
、La2
O3
的合計量及個別含量過多，則密度或原料成本容易增加。
SnO2
為於高溫區域具有良好的澄清作用的成分，並且是提高應變點的成分，且是使高溫黏性下降的成分。SnO2
的含量較佳為0%～1%、0.001%～1%、0.01%～0.5%、尤其是0.05%～0.3%。若SnO2
的含量過多，則SnO2
的失透結晶容易析出。再者，若SnO2
的含量少於0.001%，則難以享有所述效果。
如上所述，SnO2
適合作為澄清劑，但只要不損及玻璃特性，則可添加F、SO3
、C或Al、Si等金屬粉末分別至5%為止（較佳為至1%為止、尤其是至0.5%為止）作為澄清劑。另外，亦可添加CeO2
等至5%為止（較佳為至1%為止、尤其是至0.5%為止）作為澄清劑。
As2
O3
、Sb2
O3
作為澄清劑亦有效。但是，就環境的觀點而言，本發明的無鹼玻璃板實質不含該些成分。進而，若含有As2
O3
，則有耐曝曬性下降的傾向。
Cl為促進玻璃配合料的初期熔融的成分。另外，若添加Cl，則可促進澄清劑的作用。作為該些的結果，可使熔融成本低廉化並且實現玻璃製造窯的長壽命化。但是，若Cl的含量過多，則應變點容易下降。因此，Cl的含量較佳為0%～3%，更佳為0.0005%～1%，特佳為0.001%～0.5%。再者，作為Cl的導入原料，可使用氯化鍶等鹼土類金屬氧化物的氯化物或氯化鋁等原料。
Fe2
O3
為以原料雜質的形式混入的成分，且是使電阻率下降的成分。Fe2
O3
的含量較佳為0質量ppm～300質量ppm、80質量ppm～250質量ppm、尤其是100質量ppm～200質量ppm。若Fe2
O3
的含量過少，則原料成本容易高漲。另一方面，若Fe2
O3
的含量過多，則熔融玻璃的電阻率上昇而難以進行電熔融。
本發明的無鹼玻璃板較佳為具有以下特性。
30℃～380℃的溫度範圍內的平均熱膨脹係數較佳為30×10-7
/℃～50×10-7
/℃、32×10-7
/℃～48×10-7
/℃、33×10-7
/℃～45×10-7
/℃、34×10-7
/℃～44×10-7
/℃、尤其是35×10-7
/℃～44×10-7
/℃。若如此，則容易與TFT中所使用的Si的熱膨脹係數匹配。
楊氏模量為78 GPa以上，較佳為超過78 GPa、80 GPa以上、尤其是81 GPa以上。若楊氏模量過低，則容易產生因玻璃板的彎曲所引起的不良情況。
應變點為680℃以上，較佳為超過680℃、690℃以上、尤其是700℃以上。若如此，則於LTPS製程中，可抑制玻璃板的熱收縮。
液相溫度為1450℃以下，較佳為未滿1210℃、1200℃以下、尤其是1190℃以下。若如此，則容易防止在玻璃製造時產生失透結晶而生產性下降的事態。進而，由於容易利用溢流下拉（over flow down draw）法來成形，因此容易提高玻璃板的表面品質，並且可使玻璃板的製造成本低廉化。再者，液相溫度為耐失透性的指標，液相溫度越低，耐失透性越優異。
液相黏度較佳為104.8
dPa·s以上、105.0
dPa·s以上、105.2
dPa·s以上、尤其是105.3
dPa·s以上。若如此，則在成形時，不易產生失透，因此容易利用溢流下拉法來成形，結果，可提高玻璃板的表面品質，且可使玻璃板的製造成本低廉化。再者，液相黏度為耐失透性與成形性的指標，液相黏度越高，耐失透性與成形性越提高。
高溫黏度102.5
dPa·s下的溫度較佳為1650℃以下、1600℃以下、1580℃以下、尤其是1560℃以下。若高溫黏度102.5
dPa·s下的溫度過高，則難以使玻璃配合料熔解，玻璃板的製造成本高漲。再者，高溫黏度102.5
dPa·s下的溫度相當於熔融溫度，該溫度越低，熔融性越提高。
β-OH為表示玻璃中的水分量的指標，若使β-OH下降，則可提高應變點。另外，即便於玻璃組成相同的情況下，β-OH小者的應變點以下的溫度下的熱收縮率亦變小。β-OH較佳為0.30/mm以下、0.25/mm以下、0.20/mm以下、0.15/mm以下、尤其是0.10/mm以下。再者，若β-OH過小，則熔融性容易下降。因此，β-OH較佳為0.01/mm以上、尤其是0.03/mm以上。
作為使β-OH下降的方法，可列舉以下方法。（1）選擇含水量低的原料。（2）向玻璃中添加使β-OH下降的成分（Cl、SO3
等）。（3）使爐內環境中的水分量下降。（4）於熔融玻璃中進行N2
起泡。（5）採用小型熔融爐。（6）增多熔融玻璃的流量。（7）採用電熔融法。
此處，「β-OH」是指使用傅立葉轉換紅外光譜法（Fourier transform infrared spectroscopy，FT-IR）測定玻璃的透過率，並使用下述數式1而求出的值。
[數式1]
β-OH=（1/X）log（T1
/T2
）
X：板厚（mm）
T1
：參照波長3846 cm-1
下的透過率（%）
T2
：羥基吸收波長3600 cm-1
附近的最小透過率（%）
本發明的無鹼玻璃板較佳為利用溢流下拉法成形而成。溢流下拉法是使熔融玻璃自耐熱性的槽狀結構物的兩側溢出，且使溢出的熔融玻璃於槽狀結構物的下端匯流，並且向下方延伸成形而製造玻璃板的方法。溢流下拉法中，應成為玻璃板的表面的面不接觸槽狀耐火材料，而以自由表面的狀態來成形。因此，可廉價地製造未研磨且表面品質良好的玻璃板，薄型化亦容易。
除溢流下拉法以外，例如亦可利用下拉（down draw）法（流孔下引（slot down）法等）、浮動（float）法等來成形玻璃板。
於本發明的無鹼玻璃板中，板厚並無特別限定，較佳為未滿0.7 mm、0.6 mm以下、0.5 mm以下、尤其是0.4 mm以下。板厚越薄，越可實現有機EL元件的輕量化。板厚可利用玻璃製造時的流量或拉板速度等來調整。
本發明的無鹼玻璃板較佳為用於有機EL元件、尤其是有機EL電視。有機EL電視的用途中，於玻璃板上製作多個的元件後，按照每個元件進行分割切斷，從而實現降低成本（cost down）（所謂的多倒角（multiple chamfering））。本發明的無鹼玻璃板的液相溫度低且液相黏度高，因此容易成形大型的玻璃板，可確實地滿足此種要求。
[實施例]
以下，基於實施例對本發明進行說明。再者，以下實施例僅為例示。本發明並不受以下實施例任何限定。
表1～表14示出本發明的實施例（試樣No.1～試樣No.137）與比較例（試樣No.138～試樣No.141）。
[表1]
| No.1 | No.2 | No.3 | No.4 | No.5 | No.6 | No.7 | No.8 | No.9 | No.10 | ||
| 玻璃組成 （mol%） | SiO2 | 64.9 | 61.9 | 64.9 | 62.4 | 63.4 | 62.9 | 60.4 | 60.9 | 59.5 | 61.7 |
| Al2 O3 | 12.0 | 12.0 | 12.0 | 12.5 | 12.5 | 12.0 | 12.5 | 12.0 | 12.5 | 12.5 | |
| B2 O3 | 5.0 | 5.0 | 2.0 | 5.0 | 5.0 | 5.0 | 5.0 | 4.0 | 4.0 | 5.0 | |
| Li2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| Na2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| MgO | 6.0 | 7.0 | 7.0 | 8.0 | 8.0 | 7.0 | 6.0 | 8.0 | 8.5 | 8.0 | |
| CaO | 6.0 | 7.0 | 7.0 | 5.0 | 4.0 | 5.0 | 6.0 | 8.0 | 7.6 | 3.0 | |
| SrO | 3.0 | 3.5 | 3.5 | 3.5 | 3.5 | 5.0 | 4.0 | 3.0 | 4.0 | 6.8 | |
| BaO | 3.0 | 3.5 | 3.5 | 3.5 | 3.5 | 3.0 | 6.0 | 4.0 | 3.8 | 3.0 | |
| SnO2 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | |
| P2 O5 | 0.002 | 0.002 | 0.003 | 0.002 | 0.011 | 0.005 | 0.002 | 0.003 | 0.011 | 0.002 | |
| TiO2 | 0.012 | 0.012 | 0.012 | 0.012 | 0.01 | 0.008 | 0.013 | 0.012 | 0.012 | 0.011 | |
| Cl | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | |
| SiO2 /Al2 O3 | 5.41 | 5.16 | 5.41 | 4.99 | 5.07 | 5.24 | 4.83 | 5.08 | 4.76 | 4.94 | |
| Al2 O3 /B2 O3 | 2.40 | 2.40 | 6.00 | 2.50 | 2.50 | 2.40 | 2.50 | 3.00 | 3.13 | 2.50 | |
| Li2 O+Na2 O+K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| （Al2 O3 +MgO）/B2 O3 | 3.60 | 3.80 | 9.50 | 4.10 | 4.10 | 3.80 | 3.70 | 5.00 | 5.30 | 4.10 | |
| RO | 18.0 | 21.0 | 21.0 | 20.0 | 19.0 | 20.0 | 22.0 | 23.0 | 23.9 | 20.8 | |
| SrO+BaO | 6.0 | 7.0 | 7.0 | 7.0 | 7.0 | 8.0 | 10.0 | 7.0 | 7.8 | 9.8 | |
| （MgO+CaO）/（SrO+BaO） | 2.00 | 2.00 | 2.00 | 1.86 | 1.71 | 1.50 | 1.20 | 2.29 | 2.06 | 1.12 | |
| Al2 O3 /（10000×P2 O5 ） | 0.60 | 0.60 | 0.40 | 0.63 | 0.11 | 0.24 | 0.63 | 0.40 | 0.11 | 0.63 | |
| Al2 O3 /（1000×TiO2 ） | 1.00 | 1.00 | 1.00 | 1.04 | 1.25 | 1.50 | 0.96 | 1.00 | 1.04 | 1.14 | |
| CTE[×10-7 /℃] | 41.9 | 45.6 | 45.2 | 43.6 | 42.1 | 44.7 | 49.5 | 48.3 | 49.4 | 45.5 | |
| 密度[g/cm3 ] | 2.62 | 2.69 | 2.70 | 2.67 | 2.66 | 2.68 | 2.78 | 2.72 | 2.74 | 2.72 | |
| 楊氏模量[GPa] | 80 | 81 | 83 | 82 | 81 | 81 | 80 | 83 | 84 | 82 | |
| Ps[℃] | 690 | 681 | 708 | 690 | 693 | 690 | 682 | 688 | 688 | 689 | |
| Ta[℃] | 745 | 733 | 762 | 743 | 747 | 743 | 735 | 738 | 737 | 742 | |
| Ts[℃] | 966 | 940 | 976 | 953 | 962 | 955 | 939 | 939 | 931 | 949 | |
| 104 dPa·s[℃] | 1267 | 1220 | 1267 | 1233 | 1250 | 1238 | 1214 | 1204 | 1186 | 1225 | |
| 103 dPa·s[℃] | 1421 | 1366 | 1416 | 1378 | 1398 | 1385 | 1356 | 1346 | 1321 | 1365 | |
| 102.5 dPa·s[℃] | 1522 | 1461 | 1513 | 1471 | 1493 | 1481 | 1446 | 1434 | 1406 | 1459 | |
| TL[℃] | 1130 | 1154 | 1217 | 1202 | 1220 | 1205 | 1154 | 1165 | 1161 | 1212 | |
| Log10 ηTL | 5.3 | 4.6 | 5.3 | 4.6 | 4.6 | 4.6 | 5.6 | 4.8 | 4.6 | 4.5 |
[表2]
| No.11 | No.12 | No.13 | No.14 | No.15 | No.16 | No.17 | No.18 | No.19 | No.20 | ||
| 玻璃組成 （mol%） | SiO2 | 60.4 | 58.3 | 58.0 | 60.4 | 62.9 | 62.4 | 62.4 | 64.4 | 62.4 | 62.4 |
| Al2 O3 | 12.5 | 14.0 | 15.2 | 14.5 | 12.5 | 12.5 | 12.5 | 12.5 | 12.5 | 12.5 | |
| B2 O3 | 5.0 | 4.0 | 4.5 | 5.0 | 5.0 | 5.0 | 5.0 | 5.0 | 5.0 | 5.0 | |
| Li2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| Na2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| MgO | 8.0 | 8.0 | 7.0 | 8.0 | 5.0 | 8.0 | 8.0 | 8.0 | 8.0 | 8.0 | |
| CaO | 5.0 | 8.0 | 7.0 | 3.0 | 9.0 | 5.0 | 3.0 | 3.0 | 5.0 | 3.0 | |
| SrO | 5.0 | 2.5 | 4.0 | 3.5 | 1.5 | 3.5 | 4.5 | 1.8 | 1.8 | 2.3 | |
| BaO | 4.0 | 5.1 | 4.2 | 5.5 | 4.0 | 3.5 | 4.5 | 5.3 | 5.3 | 6.8 | |
| SnO2 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | |
| P2 O5 | 0.003 | 0.011 | 0.011 | 0.002 | 0.005 | 0.003 | 0.002 | 0.005 | 0.003 | 0.002 | |
| TiO2 | 0.012 | 0.011 | 0.01 | 0.008 | 0.013 | 0.012 | 0.011 | 0.012 | 0.012 | 0.011 | |
| Cl | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | |
| SiO2 /Al2 O3 | 4.83 | 4.16 | 3.82 | 4.17 | 5.03 | 4.99 | 4.99 | 5.15 | 4.99 | 4.99 | |
| Al2 O3 /B2 O3 | 2.50 | 3.50 | 3.38 | 2.90 | 2.50 | 2.50 | 2.50 | 2.50 | 2.50 | 2.50 | |
| Li2 O+Na2 O+K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| （Al2 O3 +MgO）/B2 O3 | 4.10 | 5.50 | 4.90 | 4.50 | 3.50 | 4.10 | 4.10 | 4.10 | 4.10 | 4.10 | |
| RO | 22.0 | 23.6 | 22.2 | 20.0 | 19.5 | 20.0 | 20.0 | 18.0 | 20.0 | 20.0 | |
| SrO+BaO | 9.0 | 7.6 | 8.2 | 9.0 | 5.5 | 7.0 | 9.0 | 7.1 | 7.1 | 9.1 | |
| （MgO+CaO）/（SrO+BaO） | 1.44 | 2.11 | 1.71 | 1.22 | 2.55 | 1.86 | 1.22 | 1.55 | 1.83 | 1.21 | |
| Al2 O3 /（10000×P2 O5 ） | 0.42 | 0.13 | 0.14 | 0.73 | 0.25 | 0.42 | 0.63 | 0.25 | 0.42 | 0.63 | |
| Al2 O3 /（1000×TiO2 ） | 1.04 | 1.27 | 1.52 | 1.81 | 0.96 | 1.04 | 1.14 | 1.04 | 1.04 | 1.14 | |
| CTE[×10-7 /℃] | 47.4 | 49.2 | 47.7 | 44.1 | 44.9 | 43.6 | 44.3 | 40.7 | 43.9 | 44.6 | |
| 密度[g/cm3 ] | 2.73 | 2.77 | 2.76 | 2.75 | 2.65 | 2.67 | 2.71 | 2.67 | 2.69 | 2.74 | |
| 楊氏模量[GPa] | 82 | 85 | 84 | 82 | 80 | 82 | 81 | 80 | 81 | 80 | |
| Ps[℃] | 684 | 693 | 700 | 696 | 692 | 690 | 689 | 694 | 688 | 686 | |
| Ta[℃] | 735 | 743 | 751 | 749 | 746 | 743 | 743 | 749 | 741 | 740 | |
| Ts[℃] | 937 | 934 | 942 | 956 | 958 | 953 | 955 | 971 | 953 | 955 | |
| 104 dPa·s[℃] | 1205 | 1183 | 1188 | 1228 | 1241 | 1233 | 1240 | 1272 | 1238 | 1247 | |
| 103 dPa·s[℃] | 1344 | 1314 | 1315 | 1365 | 1391 | 1378 | 1386 | 1427 | 1386 | 1396 | |
| 102.5 dPa·s[℃] | 1433 | 1394 | 1396 | 1452 | 1483 | 1471 | 1480 | 1523 | 1478 | 1489 | |
| TL[℃] | 1176 | 1157 | 1182 | 1207 | 1179 | 1202 | 1207 | 1223 | 1187 | 1188 | |
| Log10 ηTL | 4.8 | 4.9 | 4.6 | 5.0 | 4.9 | 4.6 | 4.9 | 5.0 | 5.1 | 5.5 |
[表3]
| No.21 | No.22 | No.23 | No.24 | No.25 | No.26 | No.27 | No.28 | No.29 | No.30 | ||
| 玻璃組成 （mol%） | SiO2 | 64.9 | 64.9 | 64.9 | 64.9 | 64.9 | 64.9 | 65.9 | 65.9 | 65.9 | 65.9 |
| Al2 O3 | 14.0 | 14.0 | 14.0 | 14.0 | 14.0 | 14.0 | 13.0 | 13.0 | 13.0 | 13.0 | |
| B2 O3 | 4.0 | 4.0 | 4.0 | 4.0 | 4.0 | 4.0 | 4.0 | 4.0 | 4.0 | 4.0 | |
| Li2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| Na2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| MgO | 6.0 | 5.0 | 5.0 | 4.0 | 4.0 | 4.0 | 7.0 | 6.0 | 6.0 | 5.0 | |
| CaO | 7.0 | 8.0 | 7.0 | 9.0 | 8.0 | 7.0 | 7.0 | 8.0 | 7.0 | 9.0 | |
| SrO | 2.0 | 2.0 | 2.5 | 2.0 | 2.5 | 3.0 | 1.5 | 1.5 | 2.0 | 1.5 | |
| BaO | 2.0 | 2.0 | 2.5 | 2.0 | 2.5 | 3.0 | 1.5 | 1.5 | 2.0 | 1.5 | |
| SnO2 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | |
| P2 O5 | 0.003 | 0.003 | 0.003 | 0.004 | 0.004 | 0.004 | 0.005 | 0.005 | 0.003 | 0.003 | |
| TiO2 | 0.012 | 0.012 | 0.011 | 0.011 | 0.012 | 0.011 | 0.012 | 0.012 | 0.012 | 0.012 | |
| Cl | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | |
| SiO2 /Al2 O3 | 4.64 | 4.64 | 4.64 | 4.64 | 4.64 | 4.64 | 5.07 | 5.07 | 5.07 | 5.07 | |
| Al2 O3 /B2 O3 | 3.50 | 3.50 | 3.50 | 3.50 | 3.50 | 3.50 | 3.25 | 3.25 | 3.25 | 3.25 | |
| Li2 O+Na2 O+K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| （Al2 O3 +MgO）/B2 O3 | 5.00 | 4.75 | 4.75 | 4.50 | 4.50 | 4.50 | 5.00 | 4.75 | 4.75 | 4.50 | |
| RO | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | |
| SrO+BaO | 4.0 | 4.0 | 5.0 | 4.0 | 5.0 | 6.0 | 3.0 | 3.0 | 4.0 | 3.0 | |
| （MgO+CaO）/（SrO+BaO） | 3.25 | 3.25 | 2.40 | 3.25 | 2.40 | 1.83 | 4.67 | 4.67 | 3.25 | 4.67 | |
| Al2 O3 /（10000×P2 O5 ） | 0.47 | 0.47 | 0.47 | 0.35 | 0.35 | 0.35 | 0.26 | 0.26 | 0.43 | 0.43 | |
| Al2 O3 /（1000×TiO2 ） | 1.17 | 1.17 | 1.27 | 1.27 | 1.17 | 1.27 | 1.08 | 1.08 | 1.08 | 1.08 | |
| CTE[×10-7 /℃] | 38.9 | 39.7 | 39.8 | 40.3 | 40.5 | 41.2 | 40.4 | 38.9 | 39.1 | 39.4 | |
| 密度[g/cm3 ] | 2.59 | 2.59 | 2.61 | 2.59 | 2.61 | 2.63 | 2.55 | 2.56 | 2.58 | 2.56 | |
| 楊氏模量[GPa] | 83 | 82 | 82 | 82 | 81 | 81 | 83 | 83 | 82 | 82 | |
| Ps[℃] | 717 | 716 | 715 | 716 | 715 | 715 | 712 | 713 | 712 | 712 | |
| Ta[℃] | 772 | 771 | 770 | 771 | 771 | 771 | 767 | 768 | 767 | 767 | |
| Ts[℃] | 993 | 992 | 992 | 992 | 993 | 944 | 989 | 991 | 989 | 989 | |
| 104 dPa·s[℃] | 1282 | 1283 | 1288 | 1284 | 1293 | 1287 | 1282 | 1282 | 1285 | 1284 | |
| 103 dPa·s[℃] | 1430 | 1433 | 1439 | 1434 | 1444 | 1437 | 1433 | 1432 | 1438 | 1437 | |
| 102.5 dPa·s[℃] | 1526 | 1529 | 1536 | 1531 | 1544 | 1534 | 1531 | 1530 | 1539 | 1536 | |
| TL[℃] | 1177 | 1216 | 1205 | 1230 | 1210 | 1215 | 1184 | 1185 | 1181 | 1208 | |
| Log10 ηTL | 5.0 | 4.6 | 4.8 | 4.5 | 4.7 | 4.5 | 4.9 | 4.9 | 5.0 | 4.7 |
[表4]
| No.31 | No.32 | No.33 | No.34 | No.35 | No.36 | No.37 | No.38 | No.39 | No.40 | ||
| 玻璃組成 （mol%） | SiO2 | 65.6 | 65.6 | 66.9 | 66.9 | 66.9 | 66.9 | 66.9 | 66.9 | 65.9 | 65.9 |
| Al2 O3 | 13.0 | 13.1 | 12.0 | 12.0 | 12.0 | 12.0 | 12.0 | 12.0 | 14.0 | 14.0 | |
| B2 O3 | 4.0 | 4.0 | 4.0 | 4.0 | 4.0 | 4.0 | 4.0 | 4.0 | 3.0 | 3.0 | |
| Li2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| Na2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| MgO | 5.1 | 5.1 | 8.0 | 7.0 | 7.0 | 6.0 | 6.0 | 6.0 | 6.0 | 5.0 | |
| CaO | 7.4 | 7.8 | 7.0 | 8.0 | 7.0 | 9.0 | 8.0 | 7.0 | 7.0 | 8.0 | |
| SrO | 2.4 | 2.2 | 1.0 | 1.0 | 1.5 | 1.0 | 1.5 | 2.0 | 2.0 | 2.0 | |
| BaO | 2.4 | 2.2 | 1.0 | 1.0 | 1.5 | 1.0 | 1.5 | 2.0 | 2.0 | 2.0 | |
| SnO2 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | |
| P2 O5 | 0.004 | 0.003 | 0.005 | 0.005 | 0.004 | 0.005 | 0.004 | 0.003 | 0.003 | 0.003 | |
| TiO2 | 0.012 | 0.012 | 0.012 | 0.012 | 0.011 | 0.012 | 0.012 | 0.012 | 0.011 | 0.011 | |
| Cl | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | |
| SiO2 /Al2 O3 | 5.03 | 5.02 | 5.58 | 5.58 | 5.58 | 5.58 | 5.58 | 5.58 | 4.71 | 4.71 | |
| Al2 O3 /B2 O3 | 3.26 | 3.28 | 3.00 | 3.00 | 3.00 | 3.00 | 3.00 | 3.00 | 4.67 | 4.67 | |
| Li2 O+Na2 O+K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| （Al2 O3 +MgO）/B2 O3 | 4.54 | 4.56 | 5.00 | 4.75 | 4.75 | 4.50 | 4.50 | 4.50 | 6.67 | 6.33 | |
| RO | 17.2 | 17.2 | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | |
| SrO+BaO | 4.8 | 4.3 | 2.0 | 2.0 | 3.0 | 2.0 | 3.0 | 4.0 | 4.0 | 4.0 | |
| （MgO+CaO）/（SrO+BaO） | 2.62 | 2.99 | 7.50 | 7.50 | 4.67 | 7.50 | 4.67 | 3.25 | 3.25 | 3.25 | |
| Al2 O3 /（10000×P2 O5 ） | 0.33 | 0.44 | 0.24 | 0.24 | 0.30 | 0.24 | 0.30 | 0.40 | 0.47 | 0.47 | |
| Al2 O3 /（1000×TiO2 ） | 1.09 | 1.09 | 1.00 | 1.00 | 1.09 | 1.00 | 1.00 | 1.00 | 1.27 | 1.27 | |
| CTE[×10-7 /℃] | 40.0 | 39.9 | 36.7 | 37.6 | 38.0 | 38.4 | 38.7 | 39.3 | 38.7 | 39.6 | |
| 密度[g/cm3 ] | 2.59 | 2.59 | 2.52 | 2.52 | 2.54 | 2.53 | 2.54 | 2.57 | 2.59 | 2.59 | |
| 楊氏模量[GPa] | 81 | 81 | 83 | 82 | 82 | 82 | 81 | 81 | 83 | 83 | |
| Ps[℃] | 709 | 708 | 708 | 708 | 708 | 707 | 706 | 706 | 726 | 727 | |
| Ta[℃] | 765 | 764 | 763 | 763 | 763 | 762 | 762 | 762 | 781 | 782 | |
| Ts[℃] | 989 | 989 | 986 | 987 | 989 | 986 | 987 | 988 | 1003 | 1003 | |
| 104 dPa·s[℃] | 1292 | 1289 | 1291 | 1291 | 1287 | 1286 | 1291 | 1292 | 1297 | 1297 | |
| 103 dPa·s[℃] | 1447 | 1443 | 1445 | 1452 | 1442 | 1442 | 1446 | 1450 | 1447 | 1448 | |
| 102.5 dPa·s[℃] | 1548 | 1543 | 1546 | 1556 | 1542 | 1544 | 1550 | 1552 | 1544 | 1545 | |
| TL[℃] | 1209 | 1190 | 1217 | 1232 | 1222 | 1211 | 1185 | 1162 | 1227 | 1247 | |
| Log10 ηTL | 4.7 | 4.9 | 4.6 | 4.5 | 4.6 | 4.7 | 5.0 | 5.2 | 4.6 | 4.4 |
[表5]
| No.41 | No.42 | No.43 | No.44 | No.45 | No.46 | No.47 | No.48 | No.49 | No.50 | ||
| 玻璃組成 （mol%） | SiO2 | 65.9 | 65.9 | 65.9 | 65.9 | 66.9 | 66.9 | 66.9 | 66.9 | 66.9 | 66.9 |
| Al2 O3 | 14.0 | 14.0 | 14.0 | 14.0 | 13.0 | 13.0 | 13.0 | 13.0 | 13.0 | 13.0 | |
| B2 O3 | 3.0 | 3.0 | 3.0 | 3.0 | 3.0 | 3.0 | 3.0 | 3.0 | 3.0 | 3.0 | |
| Li2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| Na2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| MgO | 5.0 | 4.0 | 4.0 | 4.0 | 7.0 | 6.0 | 6.0 | 5.0 | 5.0 | 5.0 | |
| CaO | 7.0 | 9.0 | 8.0 | 7.0 | 7.0 | 8.0 | 7.0 | 9.0 | 8.0 | 7.0 | |
| SrO | 2.5 | 2.0 | 2.5 | 3.0 | 1.5 | 1.5 | 2.0 | 1.5 | 2.0 | 2.5 | |
| BaO | 2.5 | 2.0 | 2.5 | 3.0 | 1.5 | 1.5 | 2.0 | 1.5 | 2.0 | 2.5 | |
| SnO2 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | |
| P2 O5 | 0.003 | 0.003 | 0.003 | 0.002 | 0.003 | 0.003 | 0.003 | 0.003 | 0.003 | 0.003 | |
| TiO2 | 0.013 | 0.012 | 0.011 | 0.012 | 0.012 | 0.012 | 0.011 | 0.012 | 0.012 | 0.012 | |
| Cl | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | |
| SiO2 /Al2 O3 | 4.71 | 4.71 | 4.71 | 4.71 | 5.15 | 5.15 | 5.15 | 5.15 | 5.15 | 5.15 | |
| Al2 O3 /B2 O3 | 4.67 | 4.67 | 4.67 | 4.67 | 4.33 | 4.33 | 4.33 | 4.33 | 4.33 | 4.33 | |
| Li2 O+Na2 O+K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| （Al2 O3 +MgO）/B2 O3 | 6.33 | 6.00 | 6.00 | 6.00 | 6.67 | 6.33 | 6.33 | 6.00 | 6.00 | 6.00 | |
| RO | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | |
| SrO+BaO | 5.0 | 4.0 | 5.0 | 6.0 | 3.0 | 3.0 | 4.0 | 3.0 | 4.0 | 5.0 | |
| （MgO+CaO）/（SrO+BaO） | 2.40 | 3.25 | 2.40 | 1.83 | 4.67 | 4.67 | 3.25 | 4.67 | 3.25 | 2.40 | |
| Al2 O3 /（10000×P2 O5 ） | 0.47 | 0.47 | 0.47 | 0.70 | 0.43 | 0.43 | 0.43 | 0.43 | 0.43 | 0.43 | |
| Al2 O3 /（1000×TiO2 ） | 1.08 | 1.17 | 1.27 | 1.17 | 1.08 | 1.08 | 1.18 | 1.08 | 1.08 | 1.08 | |
| CTE[×10-7 /℃] | 40.0 | 40.2 | 40.6 | 41.1 | 38.0 | 38.4 | 39.0 | 39.3 | 39.6 | 39.4 | |
| 密度[g/cm3 ] | 2.61 | 2.59 | 2.62 | 2.64 | 2.56 | 2.56 | 2.58 | 2.56 | 2.58 | 2.60 | |
| 楊氏模量[GPa] | 83 | 83 | 82 | 82 | 84 | 84 | 83 | 83 | 82 | 82 | |
| Ps[℃] | 726 | 727 | 725 | 725 | 723 | 722 | 721 | 721 | 720 | 720 | |
| Ta[℃] | 782 | 783 | 782 | 782 | 779 | 777 | 777 | 777 | 776 | 776 | |
| Ts[℃] | 1004 | 1004 | 1005 | 1006 | 1001 | 1000 | 1002 | 1000 | 1001 | 1003 | |
| 104 dPa·s[℃] | 1302 | 1300 | 1303 | 1307 | 1300 | 1301 | 1305 | 1303 | 1306 | 1309 | |
| 103 dPa·s[℃] | 1453 | 1450 | 1456 | 1459 | 1453 | 1455 | 1460 | 1457 | 1462 | 1466 | |
| 102.5 dPa·s[℃] | 1550 | 1548 | 1554 | 1558 | 1552 | 1554 | 1563 | 1557 | 1562 | 1567 | |
| TL[℃] | 1216 | 1251 | 1253 | 1249 | 1199 | 1208 | 1210 | 1239 | 1216 | 1211 | |
| Log10 ηTL | 4.8 | 4.4 | 4.4 | 4.5 | 4.9 | 4.8 | 4.9 | 4.6 | 4.8 | 4.9 |
[表6]
| No.51 | No.52 | No.53 | No.54 | No.55 | No.56 | No.57 | No.58 | No.59 | No.60 | ||
| 玻璃組成 （mol%） | SiO2 | 67.9 | 67.9 | 67.9 | 67.9 | 67.9 | 65.9 | 65.9 | 64.9 | 64.9 | 65.9 |
| Al2 O3 | 12.0 | 12.0 | 12.0 | 12.0 | 12.0 | 13.0 | 13.0 | 14.0 | 14.0 | 13.0 | |
| B2 O3 | 3.0 | 3.0 | 3.0 | 3.0 | 3.0 | 4.0 | 4.0 | 4.0 | 4.0 | 4.0 | |
| Li2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| Na2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| MgO | 8.0 | 7.0 | 7.0 | 6.0 | 6.0 | 5.0 | 5.0 | 7.0 | 6.0 | 7.0 | |
| CaO | 7.0 | 8.0 | 7.0 | 8.0 | 7.0 | 8.0 | 7.0 | 6.0 | 6.0 | 6.0 | |
| SrO | 1.0 | 1.0 | 1.5 | 1.5 | 2.0 | 2.0 | 2.5 | 2.0 | 2.5 | 2.0 | |
| BaO | 1.0 | 1.0 | 1.5 | 1.5 | 2.0 | 2.0 | 2.5 | 2.0 | 2.5 | 2.0 | |
| SnO2 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | |
| P2 O5 | 0.004 | 0.004 | 0.005 | 0.004 | 0.004 | 0.003 | 0.003 | 0.003 | 0.003 | 0.003 | |
| TiO2 | 0.013 | 0.012 | 0.012 | 0.012 | 0.012 | 0.011 | 0.012 | 0.012 | 0.012 | 0.012 | |
| Cl | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | |
| SiO2 /Al2 O3 | 5.66 | 5.66 | 5.66 | 5.66 | 5.66 | 5.07 | 5.07 | 4.64 | 4.64 | 5.07 | |
| Al2 O3 /B2 O3 | 4.00 | 4.00 | 4.00 | 4.00 | 4.00 | 3.25 | 3.25 | 3.50 | 3.50 | 3.25 | |
| Li2 O+Na2 O+K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| （Al2 O3 +MgO）/B2 O3 | 6.67 | 6.33 | 6.33 | 6.00 | 6.00 | 4.50 | 4.50 | 5.25 | 5.00 | 5.00 | |
| RO | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | |
| SrO+BaO | 2.0 | 2.0 | 3.0 | 3.0 | 4.0 | 4.0 | 5.0 | 4.0 | 5.0 | 4.0 | |
| （MgO+CaO）/（SrO+BaO） | 7.50 | 7.50 | 4.67 | 4.67 | 3.25 | 3.25 | 2.40 | 3.25 | 2.40 | 3.25 | |
| Al2 O3 /（10000×P2 O5 ） | 0.30 | 0.30 | 0.24 | 0.30 | 0.30 | 0.43 | 0.43 | 0.47 | 0.47 | 0.43 | |
| Al2 O3 /（1000×TiO2 ） | 0.92 | 1.00 | 1.00 | 1.00 | 1.00 | 1.18 | 1.08 | 1.17 | 1.17 | 1.08 | |
| CTE[×10-7 /℃] | 36.0 | 37.5 | 37.9 | 38.6 | 39.1 | 39.7 | 40.0 | 38.3 | 39.3 | 38.5 | |
| 密度[g/cm3 ] | 2.52 | 2.53 | 2.55 | 2.55 | 2.57 | 2.58 | 2.60 | 2.58 | 2.60 | 2.57 | |
| 楊氏模量[GPa] | 84 | 84 | 83 | 83 | 83 | 82 | 82 | 83 | 82 | 82 | |
| Ps[℃] | 718 | 717 | 716 | 717 | 715 | 712 | 710 | 718 | 716 | 712 | |
| Ta[℃] | 774 | 773 | 772 | 773 | 771 | 768 | 766 | 772 | 772 | 767 | |
| Ts[℃] | 998 | 998 | 999 | 1001 | 999 | 990 | 991 | 991 | 993 | 990 | |
| 104 dPa·s[℃] | 1304 | 1304 | 1306 | 1306 | 1315 | 1292 | 1294 | 1283 | 1288 | 1288 | |
| 103 dPa·s[℃] | 1461 | 1461 | 1464 | 1465 | 1483 | 1446 | 1448 | 1432 | 1438 | 1440 | |
| 102.5 dPa·s[℃] | 1570 | 1570 | 1567 | 1568 | 1592 | 1548 | 1548 | 1530 | 1535 | 1539 | |
| TL[℃] | 1244 | 1258 | 1222 | 1221 | 1234 | 1201 | 1198 | 1193 | 1200 | 1193 | |
| Log10 ηTL | 4.5 | 4.4 | 4.7 | 4.7 | 4.7 | 4.8 | 4.9 | 4.8 | 4.8 | 4.9 |
[表7]
| No.61 | No.62 | No.63 | No.64 | No.65 | No.66 | No.67 | No.68 | No.69 | No.70 | ||
| 玻璃組成 （mol%） | SiO2 | 65.9 | 64.9 | 64.9 | 65.9 | 65.9 | 66.9 | 66.9 | 65.9 | 65.9 | 65.9 |
| Al2 O3 | 13.0 | 14.0 | 14.0 | 13.0 | 13.0 | 12.0 | 12.0 | 14.0 | 14.0 | 14.0 | |
| B2 O3 | 4.0 | 4.0 | 4.0 | 4.0 | 4.0 | 4.0 | 4.0 | 3.0 | 3.0 | 3.0 | |
| Li2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| Na2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| MgO | 6.0 | 6.0 | 6.0 | 6.0 | 6.0 | 7.0 | 6.0 | 7.0 | 6.0 | 5.0 | |
| CaO | 6.0 | 7.0 | 7.0 | 7.0 | 7.0 | 6.0 | 6.0 | 6.0 | 6.0 | 6.0 | |
| SrO | 2.5 | 4.0 | 0.0 | 4.0 | 0.0 | 2.0 | 2.5 | 2.0 | 2.5 | 3.0 | |
| BaO | 2.5 | 0.0 | 4.0 | 0.0 | 4.0 | 2.0 | 2.5 | 2.0 | 2.5 | 3.0 | |
| SnO2 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | |
| P2 O5 | 0.003 | 0.003 | 0.003 | 0.003 | 0.003 | 0.004 | 0.003 | 0.003 | 0.002 | 0.002 | |
| TiO2 | 0.012 | 0.012 | 0.012 | 0.012 | 0.012 | 0.012 | 0.012 | 0.011 | 0.011 | 0.011 | |
| Cl | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | |
| SiO2 /Al2 O3 | 5.07 | 4.64 | 4.64 | 5.07 | 5.07 | 5.58 | 5.58 | 4.71 | 4.71 | 4.71 | |
| Al2 O3 /B2 O3 | 3.25 | 3.50 | 3.50 | 3.25 | 3.25 | 3.00 | 3.00 | 4.67 | 4.67 | 4.67 | |
| Li2 O+Na2 O+K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| （Al2 O3 +MgO）/B2 O3 | 4.75 | 5.00 | 5.00 | 4.75 | 4.75 | 4.75 | 4.50 | 7.00 | 6.67 | 6.33 | |
| RO | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | 17.0 | |
| SrO+BaO | 5.0 | 4.0 | 4.0 | 4.0 | 4.0 | 4.0 | 5.0 | 4.0 | 5.0 | 6.0 | |
| （MgO+CaO）/（SrO+BaO） | 2.40 | 3.25 | 3.25 | 3.25 | 3.25 | 3.25 | 2.40 | 3.25 | 2.40 | 1.83 | |
| Al2 O3 /（10000×P2 O5 ） | 0.43 | 0.47 | 0.47 | 0.43 | 0.43 | 0.30 | 0.40 | 0.47 | 0.70 | 0.70 | |
| Al2 O3 /（1000×TiO2 ） | 1.08 | 1.17 | 1.17 | 1.08 | 1.08 | 1.00 | 1.00 | 1.27 | 1.27 | 1.27 | |
| CTE[×10-7 /℃] | 39.6 | 38.7 | 39.0 | 38.7 | 39.3 | 38.4 | 39.2 | 38.2 | 39.3 | 40.4 | |
| 密度[g/cm3 ] | 2.60 | 2.56 | 2.61 | 2.55 | 2.60 | 2.56 | 2.59 | 2.59 | 2.61 | 2.63 | |
| 楊氏模量[GPa] | 81 | 83 | 82 | 83 | 81 | 82 | 81 | 84 | 83 | 82 | |
| Ps[℃] | 710 | 718 | 715 | 713 | 710 | 707 | 707 | 727 | 726 | 725 | |
| Ta[℃] | 766 | 773 | 771 | 768 | 766 | 762 | 762 | 782 | 782 | 782 | |
| Ts[℃] | 991 | 990 | 992 | 988 | 990 | 988 | 989 | 1002 | 1010 | 1006 | |
| 104 dPa·s[℃] | 1294 | 1281 | 1285 | 1282 | 1291 | 1291 | 1296 | 1298 | 1303 | 1308 | |
| 103 dPa·s[℃] | 1450 | 1430 | 1434 | 1432 | 1443 | 1450 | 1455 | 1449 | 1454 | 1461 | |
| 102.5 dPa·s[℃] | 1551 | 1528 | 1531 | 1531 | 1542 | 1552 | 1556 | 1547 | 1552 | 1559 | |
| TL[℃] | 1178 | 1220 | 1186 | 1213 | 1162 | 1170 | 1180 | 1200 | 1205 | 1191 | |
| Log10 ηTL | 5.1 | 4.6 | 4.9 | 4.6 | 5.2 | 5.1 | 5.0 | 4.9 | 4.9 | 5.1 |
[表8]
| No.71 | No.72 | No.73 | No.74 | No.75 | No.76 | No.77 | No.78 | No.79 | No.80 | ||
| 玻璃組成 （mol%） | SiO2 | 65.9 | 65.9 | 64.9 | 64.9 | 64.9 | 64.9 | 66.9 | 66.9 | 67.9 | 67.9 |
| Al2 O3 | 13.0 | 14.0 | 14.0 | 14.0 | 14.0 | 13.0 | 13.0 | 13.0 | 12.0 | 12.0 | |
| B2 O3 | 3.0 | 4.0 | 5.0 | 5.0 | 5.0 | 5.0 | 4.0 | 4.0 | 3.0 | 3.0 | |
| Li2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| Na2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| MgO | 7.0 | 6.0 | 6.0 | 6.0 | 6.0 | 6.0 | 6.0 | 6.0 | 6.0 | 6.0 | |
| CaO | 6.0 | 6.0 | 6.0 | 6.0 | 6.0 | 7.0 | 7.0 | 6.0 | 7.0 | 7.0 | |
| SrO | 2.5 | 2.0 | 2.0 | 4.0 | 0.0 | 2.0 | 1.0 | 2.0 | 4.0 | 0.0 | |
| BaO | 2.5 | 2.0 | 2.0 | 0.0 | 4.0 | 2.0 | 2.0 | 2.0 | 0.0 | 4.0 | |
| SnO2 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | |
| P2 O5 | 0.003 | 0.003 | 0.003 | 0.004 | 0.003 | 0.003 | 0.004 | 0.004 | 0.003 | 0.003 | |
| TiO2 | 0.011 | 0.011 | 0.011 | 0.011 | 0.001 | 0.002 | 0.001 | 0.002 | 0.001 | 0.002 | |
| Cl | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | |
| SiO2 /Al2 O3 | 5.07 | 4.71 | 4.64 | 4.64 | 4.64 | 4.99 | 5.15 | 5.15 | 5.66 | 5.66 | |
| Al2 O3 /B2 O3 | 4.33 | 3.50 | 2.80 | 2.80 | 2.80 | 2.60 | 3.25 | 3.25 | 4.00 | 4.00 | |
| Li2 O+Na2 O+K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| （Al2 O3 +MgO）/B2 O3 | 6.67 | 5.00 | 4.00 | 4.00 | 4.00 | 3.80 | 4.75 | 4.75 | 6.00 | 6.00 | |
| RO | 18.0 | 16.0 | 16.0 | 16.0 | 16.0 | 17.0 | 16.0 | 16.0 | 17.0 | 17.0 | |
| SrO+BaO | 5.0 | 4.0 | 4.0 | 4.0 | 4.0 | 4.0 | 3.0 | 4.0 | 4.0 | 4.0 | |
| （MgO+CaO）/（SrO+BaO） | 2.60 | 3.00 | 3.00 | 3.00 | 3.00 | 3.25 | 4.33 | 3.00 | 3.25 | 3.25 | |
| Al2 O3 /（10000×P2 O5 ） | 0.43 | 0.47 | 0.47 | 0.35 | 0.47 | 0.43 | 0.33 | 0.33 | 0.40 | 0.40 | |
| Al2 O3 /（1000×TiO2 ） | 1.18 | 1.27 | 1.27 | 1.27 | 14.00 | 6.50 | 13.00 | 6.50 | 12.00 | 6.00 | |
| CTE[×10-7 /℃] | 40.1 | 37.6 | 37.5 | 37.4 | 38.0 | 39.3 | 37.4 | 37.8 | 38.8 | 39.5 | |
| 密度[g/cm3 ] | 2.61 | 2.57 | 2.57 | 2.54 | 2.59 | 2.57 | 2.55 | 2.56 | 2.55 | 2.60 | |
| 楊氏模量[GPa] | 83 | 82 | 82 | 82 | 81 | 81 | 82 | 82 | 83 | 81 | |
| Ps[℃] | 717 | 721 | 711 | 713 | 713 | 704 | 715 | 715 | 716 | 714 | |
| Ta[℃] | 772 | 777 | 767 | 768 | 768 | 758 | 771 | 771 | 772 | 770 | |
| Ts[℃] | 993 | 999 | 989 | 988 | 991 | 978 | 997 | 998 | 997 | 999 | |
| 104 dPa·s[℃] | 1293 | 1301 | 1282 | 1278 | 1284 | 1273 | 1299 | 1306 | 1308 | 1314 | |
| 103 dPa·s[℃] | 1446 | 1457 | 1431 | 1426 | 1433 | 1424 | 1452 | 1462 | 1468 | 1475 | |
| 102.5 dPa·s[℃] | 1545 | 1551 | 1527 | 1522 | 1529 | 1523 | 1555 | 1564 | 1572 | 1578 | |
| TL[℃] | 1222 | 1195 | 1188 | 1178 | 1171 | 1160 | 1223 | 1213 | 1245 | 1186 | |
| Log10 ηTL | 4.6 | 5.0 | 4.9 | 5.0 | 5.1 | 5.1 | 4.7 | 4.8 | 4.5 | 5.1 |
[表9]
| No.81 | No.82 | No.83 | No.84 | No.85 | No.86 | No.87 | No.88 | No.89 | No.90 | ||
| 玻璃組成 （mol%） | SiO2 | 64.9 | 64.9 | 65.9 | 66.9 | 65.9 | 66.9 | 66.9 | 67.9 | 66.9 | 65.9 |
| Al2 O3 | 14.0 | 14.0 | 14.0 | 14.0 | 14.0 | 14.0 | 14.0 | 14.0 | 13.0 | 14.0 | |
| B2 O3 | 4.0 | 4.0 | 4.0 | 4.0 | 4.0 | 4.0 | 3.0 | 3.0 | 4.0 | 4.0 | |
| Li2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| Na2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| MgO | 7.0 | 7.0 | 6.0 | 6.0 | 6.0 | 6.0 | 6.0 | 6.0 | 6.0 | 6.0 | |
| CaO | 6.0 | 6.0 | 7.0 | 7.0 | 6.0 | 6.0 | 7.0 | 7.0 | 5.0 | 5.0 | |
| SrO | 4.0 | 0.0 | 1.0 | 0.0 | 1.5 | 0.5 | 1.0 | 0.0 | 2.5 | 2.5 | |
| BaO | 0.0 | 4.0 | 2.0 | 2.0 | 2.5 | 2.5 | 2.0 | 2.0 | 2.5 | 2.5 | |
| SnO2 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | |
| P2 O5 | 0.011 | 0.005 | 0.004 | 0.003 | 0.01 | 0.008 | 0.008 | 0.008 | 0.006 | 0.006 | |
| TiO2 | 0.001 | 0.002 | 0.002 | 0.002 | 0.002 | 0.002 | 0.001 | 0.002 | 0.002 | 0.002 | |
| Cl | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | |
| SiO2 /Al2 O3 | 4.64 | 4.64 | 4.71 | 4.78 | 4.71 | 4.78 | 4.78 | 4.85 | 5.15 | 4.71 | |
| Al2 O3 /B2 O3 | 3.50 | 3.50 | 3.50 | 3.50 | 3.50 | 3.50 | 4.67 | 4.67 | 3.25 | 3.50 | |
| Li2 O+Na2 O+K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| （Al2 O3 +MgO）/B2 O3 | 5.25 | 5.25 | 5.00 | 5.00 | 5.00 | 5.00 | 6.67 | 6.67 | 4.75 | 5.00 | |
| RO | 17.0 | 17.0 | 16.0 | 15.0 | 16.0 | 15.0 | 16.0 | 15.0 | 16.0 | 16.0 | |
| SrO+BaO | 4.0 | 4.0 | 3.0 | 2.0 | 4.0 | 3.0 | 3.0 | 2.0 | 5.0 | 5.0 | |
| （MgO+CaO）/（SrO+BaO） | 3.25 | 3.25 | 4.33 | 6.50 | 3.00 | 4.00 | 4.33 | 6.50 | 2.20 | 2.20 | |
| Al2 O3 /（10000×P2 O5 ） | 0.13 | 0.28 | 0.35 | 0.47 | 0.14 | 0.18 | 0.18 | 0.18 | 0.22 | 0.23 | |
| Al2 O3 /（1000×TiO2 ） | 14.00 | 7.00 | 7.00 | 7.00 | 7.00 | 7.00 | 14.00 | 7.00 | 6.50 | 7.00 | |
| CTE[×10-7 /℃] | 38.0 | 38.6 | 37.2 | 35.3 | 37.7 | 36.0 | 37.2 | 35.4 | 38.2 | 37.9 | |
| 密度[g/cm3 ] | 2.61 | 2.61 | 2.56 | 2.53 | 2.58 | 2.55 | 2.56 | 2.54 | 2.56 | 2.58 | |
| 楊氏模量[GPa] | 84 | 83 | 83 | 83 | 83 | 83 | 84 | 84 | 81 | 82 | |
| Ps[℃] | 718 | 716 | 719 | 723 | 719 | 723 | 730 | 733 | 714 | 720 | |
| Ta[℃] | 772 | 771 | 776 | 780 | 775 | 779 | 786 | 790 | 771 | 776 | |
| Ts[℃] | 989 | 992 | 998 | 1004 | 999 | 1005 | 1009 | 1015 | 998 | 1000 | |
| 104 dPa·s[℃] | 1276 | 1286 | 1291 | 1305 | 1295 | 1304 | 1310 | 1322 | 1306 | 1299 | |
| 103 dPa·s[℃] | 1422 | 1434 | 1442 | 1464 | 1444 | 1456 | 1462 | 1482 | 1466 | 1450 | |
| 102.5 dPa·s[℃] | 1519 | 1531 | 1538 | 1571 | 1542 | 1553 | 1561 | 1592 | 1572 | 1549 | |
| TL[℃] | 1178 | 1207 | 1192 | 1270 | 1189 | 1266 | 1221 | 1285 | 1211 | 1195 | |
| Log10 ηTL | 4.9 | 4.7 | 4.9 | 4.3 | 5.0 | 4.3 | 4.8 | 4.3 | 4.8 | 5.0 |
[表10]
| No.91 | No.92 | No.93 | No.94 | No.95 | No.96 | No.97 | No.98 | No.99 | No.100 | ||
| 玻璃組成 （mol%） | SiO2 | 66.9 | 66.4 | 66.9 | 66.9 | 67.4 | 67.6 | 66.7 | 65.8 | 68.7 | 67.5 |
| Al2 O3 | 14.0 | 14.5 | 14.0 | 14.0 | 13.5 | 13.1 | 14.0 | 13.0 | 12.5 | 12.2 | |
| B2 O3 | 3.0 | 3.0 | 3.0 | 3.0 | 3.0 | 2.9 | 3.0 | 3.9 | 2.9 | 2.8 | |
| Li2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| Na2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| MgO | 6.0 | 6.0 | 6.0 | 6.0 | 6.0 | 6.2 | 5.1 | 6.1 | 7.1 | 7.1 | |
| CaO | 6.0 | 6.0 | 6.0 | 6.0 | 6.0 | 6.1 | 6.1 | 6.1 | 5.2 | 5.8 | |
| SrO | 2.0 | 2.0 | 3.0 | 1.0 | 2.0 | 2.0 | 2.0 | 1.5 | 1.3 | 1.3 | |
| BaO | 2.0 | 2.0 | 1.0 | 3.0 | 2.0 | 2.0 | 3.0 | 3.5 | 2.1 | 3.2 | |
| SnO2 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | |
| P2 O5 | 0.007 | 0.011 | 0.002 | 0.003 | 0.011 | 0.011 | 0.002 | 0.005 | 0.003 | 0.002 | |
| TiO2 | 0.002 | 0.013 | 0.012 | 0.011 | 0.011 | 0.01 | 0.008 | 0.013 | 0.012 | 0.011 | |
| Cl | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | |
| SiO2 /Al2 O3 | 4.78 | 4.58 | 4.78 | 4.78 | 4.99 | 5.17 | 4.75 | 5.07 | 5.48 | 5.51 | |
| Al2 O3 /B2 O3 | 4.67 | 4.83 | 4.67 | 4.67 | 4.50 | 4.48 | 4.73 | 3.29 | 4.37 | 4.36 | |
| Li2 O+Na2 O+K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| （Al2 O3 +MgO）/B2 O3 | 6.67 | 6.83 | 6.67 | 6.67 | 6.50 | 6.60 | 6.46 | 4.85 | 6.85 | 6.86 | |
| RO | 16.0 | 16.0 | 16.0 | 16.0 | 16.0 | 16.3 | 16.2 | 17.2 | 15.8 | 17.3 | |
| SrO+BaO | 4.0 | 4.0 | 4.0 | 4.0 | 4.0 | 4.1 | 5.0 | 5.0 | 3.5 | 4.5 | |
| （MgO+CaO）/（SrO+BaO） | 3.00 | 3.00 | 3.00 | 3.00 | 3.00 | 3.03 | 2.23 | 2.44 | 3.56 | 2.84 | |
| Al2 O3 /（10000×P2 O5 ） | 0.20 | 0.13 | 0.70 | 0.47 | 0.12 | 0.12 | 0.70 | 0.26 | 0.42 | 0.61 | |
| Al2 O3 /（1000×TiO2 ） | 7.00 | 1.12 | 1.17 | 1.27 | 1.23 | 1.31 | 1.75 | 1.00 | 1.05 | 1.11 | |
| CTE[×10-7 /℃] | 37.2 | 37.0 | 37.1 | 37.4 | 37.4 | 37.4 | 38.4 | 39.7 | 39.2 | 39.7 | |
| 密度[g/cm3 ] | 2.58 | 2.58 | 2.56 | 2.59 | 2.57 | 2.57 | 2.61 | 2.61 | 2.58 | 2.61 | |
| 楊氏模量[GPa] | 84 | 84 | 84 | 83 | 83 | 83 | 83 | 81 | 83 | 82 | |
| Ps[℃] | 731 | 733 | 733 | 733 | 728 | 727 | 730 | 714 | 727 | 718 | |
| Ta[℃] | 787 | 789 | 789 | 789 | 785 | 784 | 787 | 727 | 784 | 775 | |
| Ts[℃] | 1011 | 1011 | 1011 | 1013 | 1010 | 1012 | 1014 | 993 | 1014 | 1002 | |
| 104 dPa·s[℃] | 1312 | 1308 | 1311 | 1317 | 1315 | 1319 | 1318 | 1296 | 1326 | 1310 | |
| 103 dPa·s[℃] | 1466 | 1458 | 1463 | 1471 | 1469 | 1474 | 1472 | 1449 | 1483 | 1465 | |
| 102.5 dPa·s[℃] | 1564 | 1556 | 1562 | 1570 | 1568 | 1574 | 1571 | 1548 | 1585 | 1566 | |
| TL[℃] | 1202 | 1239 | 1214 | 1208 | 1197 | 1188 | 1204 | 1155 | 1220 | 1158 | |
| Log10 ηTL | 5.0 | 4.6 | 4.9 | 5.0 | 5.1 | 5.2 | 5.0 | 5.4 | 4.9 | 5.4 |
[表11]
| No.101 | No.102 | No.103 | No.104 | No.105 | No.106 | No.107 | No.108 | No.109 | No.110 | ||
| 玻璃組成 （mol%） | SiO2 | 67.2 | 67.2 | 68.4 | 68.1 | 67.9 | 67.9 | 67.9 | 66.9 | 67.4 | 67.1 |
| Al2 O3 | 12.3 | 12.2 | 12.5 | 12.7 | 13.0 | 12.5 | 13.0 | 13.0 | 13.1 | 13.5 | |
| B2 O3 | 3.4 | 2.6 | 2.9 | 5.1 | 2.8 | 2.8 | 2.8 | 3.8 | 3.7 | 2.8 | |
| Li2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| Na2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| MgO | 7.2 | 8.1 | 8.1 | 5.4 | 5.1 | 6.1 | 5.6 | 6.1 | 6.1 | 5.6 | |
| CaO | 6.4 | 7.3 | 4.5 | 5.2 | 6.6 | 6.6 | 6.6 | 6.6 | 6.5 | 6.6 | |
| SrO | 1.3 | 1.3 | 2.3 | 0.0 | 1.5 | 2.0 | 0.5 | 1.5 | 1.5 | 1.5 | |
| BaO | 2.1 | 1.2 | 1.2 | 3.4 | 3.0 | 2.0 | 3.5 | 2.0 | 1.5 | 2.8 | |
| SnO2 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | |
| P2 O5 | 0.005 | 0.003 | 0.002 | 0.011 | 0.002 | 0.005 | 0.003 | 0.004 | 0.003 | 0.003 | |
| TiO2 | 0.012 | 0.012 | 0.011 | 0.01 | 0.008 | 0.013 | 0.012 | 0.009 | 0.01 | 0.009 | |
| Cl | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | |
| SiO2 /Al2 O3 | 5.49 | 5.49 | 5.49 | 5.36 | 5.21 | 5.42 | 5.22 | 5.14 | 5.17 | 4.97 | |
| Al2 O3 /B2 O3 | 3.57 | 4.66 | 4.25 | 2.51 | 4.59 | 4.50 | 4.59 | 3.38 | 3.50 | 4.76 | |
| Li2 O+Na2 O+K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| （Al2 O3 +MgO）/B2 O3 | 5.66 | 7.73 | 7.01 | 3.57 | 6.40 | 6.70 | 6.58 | 4.97 | 5.14 | 6.74 | |
| RO | 17.0 | 17.9 | 16.1 | 14.0 | 16.2 | 16.7 | 16.2 | 16.2 | 15.7 | 16.5 | |
| SrO+BaO | 3.4 | 2.5 | 3.5 | 3.4 | 4.5 | 4.0 | 4.0 | 3.5 | 3.0 | 4.3 | |
| （MgO+CaO）/（SrO+BaO） | 4.00 | 6.07 | 3.66 | 3.06 | 2.59 | 3.17 | 3.06 | 3.61 | 4.19 | 2.82 | |
| Al2 O3 /（10000×P2 O5 ） | 0.25 | 0.41 | 0.62 | 0.12 | 0.65 | 0.25 | 0.43 | 0.33 | 0.44 | 0.45 | |
| Al2 O3 /（1000×TiO2 ） | 1.02 | 1.02 | 1.13 | 1.27 | 1.63 | 0.96 | 1.08 | 1.45 | 1.31 | 1.50 | |
| CTE[×10-7 /℃] | 37.9 | 38.1 | 38.3 | 38.5 | 38.3 | 38.0 | 37.5 | 36.6 | 38.4 | 40.4 | |
| 密度[g/cm3 ] | 2.56 | 2.55 | 2.56 | 2.59 | 2.57 | 2.59 | 2.56 | 2.53 | 2.59 | 2.62 | |
| 楊氏模量[GPa] | 82 | 84 | 84 | 79 | 82 | 82 | 82 | 82 | 82 | 83 | |
| Ps[℃] | 713 | 721 | 726 | 714 | 726 | 722 | 727 | 717 | 719 | 728 | |
| Ta[℃] | 768 | 775 | 782 | 772 | 783 | 778 | 784 | 774 | 776 | 784 | |
| Ts[℃] | 994 | 996 | 1010 | 1007 | 1013 | 1006 | 1013 | 999 | 1003 | 1010 | |
| 104 dPa·s[℃] | 1298 | 1293 | 1318 | 1325 | 1323 | 1314 | 1322 | 1303 | 1306 | 1315 | |
| 103 dPa·s[℃] | 1456 | 1446 | 1474 | 1485 | 1481 | 1472 | 1481 | 1457 | 1461 | 1470 | |
| 102.5 dPa·s[℃] | 1558 | 1545 | 1574 | 1586 | 1582 | 1572 | 1584 | 1556 | 1560 | 1571 | |
| TL[℃] | 1183 | 1208 | 1247 | 1197 | 1202 | 1188 | 1181 | 1173 | 1180 | 1200 | |
| Log10 ηTL | 5.1 | 4.8 | 4.6 | 5.1 | 5.1 | 5.2 | 5.3 | 5.2 | 5.2 | 5.1 |
[表12]
| No.111 | No.112 | No.113 | No.114 | No.115 | No.116 | No.117 | No.118 | No.119 | No.120 | ||
| 玻璃組成 （mol%） | SiO2 | 66.8 | 67.4 | 68.2 | 67.9 | 67.9 | 67.9 | 67.2 | 67.4 | 67.4 | 67.4 |
| Al2 O3 | 13.0 | 12.3 | 12.5 | 12.7 | 12.8 | 13.0 | 12.2 | 12.0 | 12.0 | 12.0 | |
| B2 O3 | 3.0 | 2.8 | 3.0 | 3.0 | 3.0 | 3.0 | 2.8 | 2.0 | 2.0 | 2.0 | |
| Li2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| Na2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| MgO | 5.1 | 7.0 | 6.0 | 6.0 | 5.8 | 5.7 | 7.1 | 6.5 | 6.5 | 6.5 | |
| CaO | 6.6 | 6.2 | 6.5 | 6.3 | 6.5 | 6.3 | 7.3 | 7.0 | 7.0 | 6.0 | |
| SrO | 2.5 | 1.2 | 1.7 | 1.7 | 1.4 | 1.4 | 1.3 | 3.0 | 2.0 | 4.0 | |
| BaO | 3.0 | 3.0 | 2.0 | 2.3 | 2.6 | 2.6 | 2.2 | 2.0 | 3.0 | 2.0 | |
| SnO2 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | |
| P2 O5 | 0.004 | 0.004 | 0.003 | 0.003 | 0.003 | 0.003 | 0.004 | 0.003 | 0.003 | 0.003 | |
| TiO2 | 0.009 | 0.011 | 0.01 | 0.01 | 0.01 | 0.01 | 0.01 | 0.01 | 0.01 | 0.009 | |
| Cl | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | |
| SiO2 /Al2 O3 | 5.14 | 5.48 | 5.46 | 5.35 | 5.33 | 5.22 | 5.52 | 5.62 | 5.62 | 5.62 | |
| Al2 O3 /B2 O3 | 4.39 | 4.39 | 4.17 | 4.23 | 4.25 | 4.33 | 4.40 | 6.00 | 6.00 | 6.00 | |
| Li2 O+Na2 O+K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| （Al2 O3 +MgO）/B2 O3 | 6.12 | 6.89 | 6.17 | 6.23 | 6.17 | 6.23 | 6.95 | 9.25 | 9.25 | 9.25 | |
| RO | 17.2 | 17.4 | 16.2 | 16.3 | 16.3 | 16.0 | 17.8 | 18.5 | 18.5 | 18.5 | |
| SrO+BaO | 5.5 | 4.2 | 3.7 | 4.0 | 4.0 | 4.0 | 3.5 | 5.0 | 5.0 | 6.0 | |
| （MgO+CaO）/（SrO+BaO） | 2.12 | 3.14 | 3.38 | 3.08 | 3.06 | 3.00 | 4.12 | 2.70 | 2.70 | 2.08 | |
| Al2 O3 /（10000×P2 O5 ） | 0.32 | 0.31 | 0.42 | 0.42 | 0.43 | 0.43 | 0.30 | 0.40 | 0.40 | 0.40 | |
| Al2 O3 /（1000×TiO2 ） | 1.44 | 1.12 | 1.25 | 1.27 | 1.28 | 1.30 | 1.22 | 1.20 | 1.20 | 1.33 | |
| CTE[×10-7 /℃] | 39.1 | 38.9 | 37.7 | 38.1 | 37.8 | 37.3 | 39.1 | 40.9 | 41.6 | 41.2 | |
| 密度[g/cm3 ] | 2.57 | 2.59 | 2.56 | 2.57 | 2.57 | 2.57 | 2.57 | 2.61 | 2.62 | 2.63 | |
| 楊氏模量[GPa] | 82 | 83 | 82 | 82 | 82 | 82 | 83 | 84 | 83 | 83 | |
| Ps[℃] | 721 | 719 | 726 | 723 | 725 | 728 | 717 | 722 | 721 | 721 | |
| Ta[℃] | 778 | 775 | 783 | 780 | 783 | 786 | 773 | 777 | 776 | 777 | |
| Ts[℃] | 1004 | 1001 | 1010 | 1008 | 1011 | 1016 | 996 | 999 | 1000 | 1000 | |
| 104 dPa·s[℃] | 1310 | 1309 | 1318 | 1316 | 1320 | 1326 | 1300 | 1302 | 1305 | 1304 | |
| 103 dPa·s[℃] | 1466 | 1465 | 1476 | 1473 | 1477 | 1482 | 1455 | 1456 | 1461 | 1460 | |
| 102.5 dPa·s[℃] | 1566 | 1566 | 1576 | 1575 | 1578 | 1583 | 1556 | 1557 | 1562 | 1560 | |
| TL[℃] | 1227 | 1183 | 1201 | 1196 | 1191 | 1207 | 1192 | 1218 | 1204 | 1236 | |
| Log10 ηTL | 4.7 | 5.2 | 5.1 | 5.1 | 5.2 | 5.1 | 5.0 | 4.7 | 4.9 | 4.6 |
[表13]
| No.121 | No.122 | No.123 | No.124 | No.125 | No.126 | No.127 | No.128 | No.129 | No.130 | ||
| 玻璃組成 （mol%） | SiO2 | 67.4 | 68.4 | 68.4 | 68.4 | 68.4 | 67.2 | 67.5 | 67.2 | 67.2 | 67.2 |
| Al2 O3 | 12.0 | 12.0 | 12.0 | 12.0 | 12.0 | 13.0 | 13.0 | 13.3 | 13.0 | 13.0 | |
| B2 O3 | 2.0 | 2.0 | 2.0 | 2.0 | 2.0 | 4.0 | 3.7 | 3.7 | 3.7 | 3.7 | |
| Li2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| Na2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| MgO | 6.5 | 6.5 | 6.5 | 6.5 | 6.5 | 6.0 | 6.0 | 6.0 | 6.3 | 6.0 | |
| CaO | 8.0 | 8.0 | 7.0 | 7.0 | 6.0 | 6.5 | 6.5 | 6.5 | 6.5 | 6.5 | |
| SrO | 2.0 | 1.0 | 2.0 | 1.0 | 3.0 | 1.5 | 1.5 | 1.5 | 1.5 | 1.5 | |
| BaO | 2.0 | 2.0 | 2.0 | 3.0 | 2.0 | 1.7 | 1.7 | 1.7 | 1.7 | 2.0 | |
| SnO2 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | |
| P2 O5 | 0.003 | 0.004 | 0.003 | 0.003 | 0.003 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | |
| TiO2 | 0.01 | 0.01 | 0.009 | 0.01 | 0.01 | 0.008 | 0.007 | 0.009 | 0.008 | 0.008 | |
| Cl | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | |
| SiO2 /Al2 O3 | 5.62 | 5.70 | 5.70 | 5.70 | 5.70 | 5.17 | 5.19 | 5.05 | 5.17 | 5.17 | |
| Al2 O3 /B2 O3 | 6.00 | 6.00 | 6.00 | 6.00 | 6.00 | 3.25 | 3.51 | 3.59 | 3.51 | 3.51 | |
| Li2 O+Na2 O+K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| （Al2 O3 +MgO）/B2 O3 | 9.25 | 9.25 | 9.25 | 9.25 | 9.25 | 4.75 | 5.14 | 5.22 | 5.22 | 5.14 | |
| RO | 18.5 | 17.5 | 17.5 | 17.5 | 17.5 | 15.7 | 15.7 | 15.7 | 16.0 | 16.0 | |
| SrO+BaO | 4.0 | 3.0 | 4.0 | 4.0 | 5.0 | 3.2 | 3.2 | 3.2 | 3.2 | 3.5 | |
| （MgO+CaO）/（SrO+BaO） | 3.63 | 4.83 | 3.38 | 3.38 | 2.50 | 3.91 | 3.91 | 3.91 | 4.00 | 3.57 | |
| Al2 O3 /（10000×P2 O5 ） | 0.40 | 0.30 | 0.40 | 0.40 | 0.40 | 1.30 | 1.30 | 1.33 | 1.30 | 1.30 | |
| Al2 O3 /（1000×TiO2 ） | 1.20 | 1.20 | 1.33 | 1.20 | 1.20 | 1.63 | 1.86 | 1.48 | 1.63 | 1.63 | |
| CTE[×10-7 /℃] | 40.4 | 39.0 | 39.1 | 39.4 | 39.8 | 37.1 | 37.1 | 37.2 | 37.4 | 37.8 | |
| 密度[g/cm3 ] | 2.60 | 2.57 | 2.58 | 2.60 | 2.60 | 2.54 | 2.54 | 2.55 | 2.55 | 2.56 | |
| 楊氏模量[GPa] | 84 | 84 | 84 | 83 | 83 | 82 | 83 | 82 | 83 | 82 | |
| Ps[℃] | 722 | 725 | 725 | 725 | 726 | 720 | 723 | 724 | 722 | 721 | |
| Ta[℃] | 778 | 782 | 782 | 782 | 783 | 776 | 780 | 781 | 778 | 777 | |
| Ts[℃] | 999 | 1008 | 1009 | 1009 | 1010 | 1002 | 1006 | 1006 | 1003 | 1003 | |
| 104 dPa·s[℃] | 1300 | 1315 | 1323 | 1322 | 1319 | 1309 | 1314 | 1309 | 1307 | 1308 | |
| 103 dPa·s[℃] | 1455 | 1473 | 1480 | 1480 | 1477 | 1462 | 1468 | 1463 | 1460 | 1462 | |
| 102.5 dPa·s[℃] | 1554 | 1574 | 1584 | 1582 | 1579 | 1560 | 1566 | 1561 | 1558 | 1561 | |
| TL[℃] | 1216 | 1219 | 1201 | 1210 | 1222 | 1182 | 1169 | 1197 | 1182 | 1172 | |
| Log10 ηTL | 4.7 | 4.8 | 5.1 | 5.0 | 4.9 | 5.2 | 5.4 | 5.0 | 5.2 | 5.3 |
[表14]
| No.131 | No.132 | No.133 | No.134 | No.135 | No.136 | No.137 | No.138 | No.139 | No.140 | No.141 | ||
| 玻璃組成 （mol%） | SiO2 | 67.6 | 68.1 | 67.9 | 68.3 | 67.4 | 67.6 | 67.5 | 70.9 | 57.9 | 57.7 | 67.9 |
| Al2 O3 | 12.3 | 12.3 | 12.3 | 12.3 | 13.0 | 13.1 | 13.2 | 12.0 | 13.0 | 14.0 | 19.0 | |
| B2 O3 | 2.8 | 2.8 | 2.8 | 2.8 | 3.7 | 3.4 | 3.3 | 5.0 | 9.0 | 5.0 | 2.0 | |
| Li2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| Na2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| MgO | 7.0 | 6.5 | 6.8 | 6.5 | 6.1 | 6.1 | 6.1 | 4.0 | 8.0 | 8.0 | 4.0 | |
| CaO | 6.2 | 6.2 | 6.2 | 6.2 | 6.5 | 6.5 | 6.5 | 4.0 | 5.0 | 3.0 | 4.0 | |
| SrO | 1.4 | 1.4 | 1.5 | 1.5 | 1.5 | 1.5 | 1.6 | 2.0 | 1.8 | 2.3 | 2.0 | |
| BaO | 2.6 | 2.6 | 2.4 | 2.3 | 1.5 | 1.7 | 1.7 | 2.0 | 5.3 | 10.0 | 2.0 | |
| SnO2 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | |
| P2 O5 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.011 | 0.005 | 0.002 | 0.008 | |
| TiO2 | 0.008 | 0.009 | 0.008 | 0.008 | 0.008 | 0.008 | 0.008 | 0.01 | 0.008 | 0.013 | 0.012 | |
| Cl | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | |
| SiO2 /Al2 O3 | 5.50 | 5.54 | 5.52 | 5.55 | 5.17 | 5.16 | 5.11 | 5.91 | 4.45 | 4.12 | 3.57 | |
| Al2 O3 /B2 O3 | 4.39 | 4.39 | 4.39 | 4.39 | 3.50 | 3.85 | 4.00 | 2.40 | 1.44 | 2.80 | 9.50 | |
| Li2 O+Na2 O+K2 O | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 1.0 | 2.0 | 0.0 | 0.0 | 0.0 | 0.0 | |
| （Al2 O3 +MgO）/B2 O3 | 6.89 | 6.71 | 6.82 | 6.71 | 5.15 | 5.65 | 5.85 | 3.20 | 2.30 | 4.40 | 11.00 | |
| RO | 17.2 | 16.7 | 16.9 | 16.5 | 15.7 | 15.8 | 15.9 | 12.0 | 20.0 | 23.3 | 12.0 | |
| SrO+BaO | 4.0 | 4.0 | 3.9 | 3.8 | 3.0 | 3.2 | 3.3 | 4.0 | 7.1 | 12.3 | 4.0 | |
| （MgO+CaO）/（SrO+BaO） | 3.30 | 3.18 | 3.33 | 3.34 | 4.20 | 3.94 | 3.82 | 2.00 | 1.83 | 0.89 | 2.00 | |
| Al2 O3 /（10000×P2 O5 ） | 1.23 | 1.23 | 1.23 | 1.23 | 1.30 | 1.31 | 1.32 | 0.11 | 0.26 | 0.70 | 0.24 | |
| Al2 O3 /（1000×TiO2 ） | 1.54 | 1.37 | 1.54 | 1.54 | 1.63 | 1.64 | 1.65 | 1.20 | 1.63 | 1.08 | 1.58 | |
| CTE[×10-7 /℃] | 38.9 | 38.9 | 38.8 | 38.2 | 36.8 | 36.9 | 36.3 | 33.1 | 44.7 | 50.7 | 32.1 | |
| 密度[g/cm3 ] | 2.58 | 2.58 | 2.58 | 2.57 | 2.53 | 2.55 | 2.55 | 2.50 | 2.68 | 2.90 | 2.58 | |
| 楊氏模量[GPa] | 83 | 83 | 83 | 83 | 83 | 83 | 83 | 78 | 79 | 81 | 86 | |
| Ps[℃] | 720 | 721 | 722 | 723 | 720 | 724 | 725 | 715 | 654 | 679 | 759 | |
| Ta[℃] | 777 | 778 | 779 | 780 | 777 | 781 | 782 | 776 | 703 | 731 | 818 | |
| Ts[℃] | 1002 | 1006 | 1005 | 1009 | 1004 | 1007 | 1007 | 1025 | 905 | 929 | 1043 | |
| 104 dPa·s[℃] | 1311 | 1318 | 1315 | 1321 | 1311 | 1313 | 1314 | 1361 | 1169 | 1197 | 1350 | |
| 103 dPa·s[℃] | 1465 | 1474 | 1470 | 1476 | 1466 | 1466 | 1469 | 1538 | 1304 | 1332 | 1488 | |
| 102.5 dPa·s[℃] | 1564 | 1573 | 1570 | 1576 | 1564 | 1563 | 1567 | 1653 | 1387 | 1413 | 1582 | |
| TL[℃] | 1170 | 1179 | 1178 | 1186 | 1174 | 1192 | 1184 | 1207 | 1100 | 1131 | >1450 | |
| Log10 ηTL | 5.3 | 5.3 | 5.3 | 5.2 | 5.3 | 5.1 | 5.2 | 5.3 | 5.3 | 6.4 | 無法測定 |
首先，將以成為表中的玻璃組成的方式調合玻璃原料而成的玻璃配合料放入鉑坩堝中，於1600℃～1650℃下熔融24小時。在玻璃配合料熔解時，使用鉑攪拌棒加以攪拌，進行均質化。繼而，使熔融玻璃流出至碳板上而成形為板狀後，於緩冷點附近的溫度下緩冷30分鐘。針對所獲得的各試樣，對30℃～380℃的溫度範圍內的平均熱膨脹係數CTE、密度、楊氏模量、應變點Ps、緩冷點Ta、軟化點Ts、高溫黏度104
dPa·s下的溫度、高溫黏度103
dPa·s下的溫度、高溫黏度102.5
dPa·s下的溫度、液相溫度TL及液相溫度TL下的黏度log10
ηTL進行評價。
30℃～380℃的溫度範圍內的平均熱膨脹係數CTE是利用膨脹計進行測定而得的值。
密度是藉由周知的阿基米德（Archimedes）法進行測定而得的值。
楊氏模量是指利用周知的共振法進行測定而得的值。
應變點Ps、緩冷點Ta、軟化點Ts是基於ASTM C336及C338的方法進行測定而得的值。
高溫黏度104
dPa·s、高溫黏度103
dPa·s、高溫黏度102.5
dPa·s下的溫度是利用鉑球提拉法進行測定而得的值。
液相溫度TL是將通過標準篩30目（500 μm）而殘留於50目（300 μm）中的玻璃粉末放入鉑舟中，於溫度梯度爐中保持24小時後，結晶析出的溫度。
液相黏度log10
ηTL是利用鉑球提拉法來測定液相溫度TL下的玻璃的黏度而得的值。
根據表1～表14而明確，試樣No.1～試樣No.137的玻璃組成被限制為規定範圍，因此楊氏模量為80.1 GPa以上，應變點為681℃以上，液相溫度為1285℃以下，液相黏度為104.29
dPa·s以上，因此認為：生產性良好，可減低LTPS製程中的熱收縮，且即便進行大型化、薄型化，亦不易產生由彎曲引起的不良情況。因此，試樣No.1～試樣No.137適合於有機EL元件的基板。
另一方面，試樣No.138的高溫黏度102.5
dPa·s下的溫度高至1653℃，楊氏模量低至77.5 GPa。試樣No.139的應變點低至654℃。試樣No.140的30℃～380℃的溫度範圍內的平均熱膨脹係數高至50.7×10-7
/℃，應變點低至679℃。試樣No.141的液相溫度高於1450℃，無法測定液相黏度。
[產業上的可利用性]
本發明的無鹼玻璃板適合作為有機EL元件、尤其是有機EL電視的基板，除此以外，亦適合於液晶顯示器等平板顯示器基板；電荷耦合元件（Charge Coupled Device，CCD）、等倍接近式固體攝像元件（Contact Image Sensor，CIS）等的影像感測器用的蓋玻璃；太陽電池用的基板及蓋玻璃；有機EL照明用基板等。
無
Claims (10)
- 一種無鹼玻璃板，其特徵在於：玻璃組成中的Li2O+Na2O+K2O的含量為0mol%~0.5mol%，楊氏模量為78GPa以上，應變點為680℃以上，液相溫度為1450℃以下，以mol%計含有58%~70%的SiO2、11.4%~18%的Al2O3及4%~7.5%的MgO，以mol%比計Al2O3/B2O3為3~7.5，以mol%比計，Al2O3/(1000×TiO2)為0.1~10。
- 如申請專利範圍第1項所述的無鹼玻璃板，其中作為玻璃組成，以mol%計進而含有58%~68%的SiO2、1.5%~6%的B2O3、2%~10%的CaO及2%~13%的SrO+BaO。
- 如申請專利範圍第1項所述的無鹼玻璃板，其中作為玻璃組成，以mol%計進而含有58%~67%的SiO2、1.5%~6%的B2O3、2%~10%的CaO、1.5%~8%的SrO及1.5%~8%的BaO，實質不含As2O3及Sb2O3。
- 如申請專利範圍第1項至第3項中任一項所述的無鹼玻璃板，其進而含有0.001mol%~1mol%的SnO2。
- 如申請專利範圍第1項至第3項中任一項所述的無鹼玻璃板，其中應變點為690℃以上。
- 如申請專利範圍第1項至第3項中任一項所述的無鹼玻璃板，其中楊氏模量高於80GPa。
- 如申請專利範圍第1項至第3項中任一項所述的無鹼玻璃板，其中30℃~380℃的溫度範圍內的平均熱膨脹係數為 30×10-7/℃~50×10-7/℃。
- 如申請專利範圍第1項至第3項中任一項所述的無鹼玻璃板，其中液相黏度為104.5dPa．s以上。
- 如申請專利範圍第1項至第3項中任一項所述的無鹼玻璃板，其用於有機電致發光元件。
- 如申請專利範圍第1項至第3項中任一項所述的無鹼玻璃板，其中CaO的含量為2mol%~5.8mol%。