TWI668256B - 基於保留特定波長之透光材料,其隔熱複合材料及其複合載體 - Google Patents
基於保留特定波長之透光材料,其隔熱複合材料及其複合載體 Download PDFInfo
- Publication number
- TWI668256B TWI668256B TW107130816A TW107130816A TWI668256B TW I668256 B TWI668256 B TW I668256B TW 107130816 A TW107130816 A TW 107130816A TW 107130816 A TW107130816 A TW 107130816A TW I668256 B TWI668256 B TW I668256B
- Authority
- TW
- Taiwan
- Prior art keywords
- light
- transmitting material
- red
- specific wavelength
- wavelength
- Prior art date
Abstract
本發明係提供一基於保留特定波長之透光材料,其隔熱複合材料及其複合載體,其中,該透光材料係用以保留特定之光波長,使特定區段之光波長得以通過該透光材料;本發明係可應用於植物之培育,使光波長之特定區段為可調節植物生長的光波長範圍,以提高植物行光合作用之效果,使促進植物生長;並可藉由添加隔熱材料,使達致夏天隔熱、冬天保溫之效果,以提供植物適性之生長環境,藉以提升農作物生長效率,進而提高產率,藉可有助於解決人類之糧食問題者。
Description
本發明係提供一種基於保留特定波長之透光材料,其隔熱複合材料及其複合載體,尤指一種可使僅促進植物生長之光波長得以通過,藉以提升植物生長之生長速率者。
按,21世紀以來,由於工業技術日益增進,全球人口也急速增長,人類的糧食供求是當前需要解決的課題之一;然而,隨科技發展,相關產業大量使用石化燃料,導致全球暖化造成各地氣候極端變化,導致動植物之生長受到抑制而短缺,再加上地球人口數急遽成長,故已衍生嚴重之糧食問題;是以,近年來常見於透過溫室農業以及有機農業或農棚之開發,以提升農作物產量,期能解決人類之糧食問題。
為調節適用於植物生長之環境,故一般而言習見之農業用披覆材料主要為塑膠膜或塑膠網,如歐盟專利第1095964B1號及美國專利第5138792號所示者,藉以構築形成一溫室,以達致遮蔭、防蟲、保溫或隔熱之效果,惟,塑膠膜及塑膠網皆仍具有隔熱、不透氣之問題。
此外,植物生長通常需要陽光,光環境是植物生長發育不可缺少的重要因素之一,依據「Photo morphogenesis in Plant」之文獻記載,在太陽光中波長範圍400nm至520nm的藍光和波長範圍610nm至720nm的紅光,對植物光合作用影響最大,而當太陽光進入大氣層時,約有5%紫外光、45%可見光與50%紅外光能量分佈,其中有部分光波長將導致抑制生長,而部分者則可促進於植物生長,是以,近年來針對光波長的選擇應用在植物生長之研究繁多,如中國大陸專利第1038252號、我國專利第I463942號、美國專利第8505237號及美國專利第5953857號四案所述者,即係利用覆蓋物之透光材料以篩選保留特定波長之光線,並排除不利於植物生長之光線波長,藉以提升植物之生長效率;惟,波長為315nm至400nm之紫外光,其可抑制莖之徒長、避免葉片黃化,且可增加葉綠素、並能促進花青素形成,有助於植物之增豔效果,並對人體有諸多助益,此外,紫外光亦可促進蛋白質及有機酸類之合成,且可提高種子之發芽率,具有增加作物產量之優點,然此為前述專利案所未提及者,故前述專利案係令其透光材料可通過之光波長最短者僅為400nm至500nm,其對於植物生長之促進仍有限。
習知另使用LED照明應用於農業植栽,如美國專利第20160353672號及中國大陸第105246322號二案所述,藉以透過LED可日夜不斷提供植物在不同階段生長給予不同光源的調整,加速植株成長,然而,雖單一LED光源之耗電量低,然其累積後之所需電量仍極為可觀,其亦將導致能源之耗費及地球暖化之缺失。
有鑑於此,吾等發明人乃潛心進一步研究光波長對植物生長之影響,並著手進行研發及改良,期以一較佳發明以解決上述問題,且在經過不斷試驗及修改後而有本發明之問世。
爰是,本發明之目的係為解決前述問題,為達致以上目的,吾等發明人提供一種基於保留特定波長之透光材料,其包含:一透光材料,其包含一透光基材及一隔熱材料,該隔熱材料係選自由氧化錫銻(ATO)、氧化銦錫(ITO)、二氧化鈦、二氧化矽、氧化鋅、氧化鎢所組成之群組中之至少其一者;該透光材料係用以保留波長於750 nm以下中的特定區段之光波長,使所述光波長得以通過該透光基材;該特定區段為:區段A:320nm至380nm;區段B:400nm至550nm;區段C:650nm至750nm;且於一光線穿透該透光材料後,於該特定區段之平均穿透率分別為:區段A:5至35%之間;區段B:30至70%之間;區段C:15至65%之間;其中,該光線可為一自然光源(太陽光)。
據上所述之基於保留特定波長之透光材料,其中, 該透光基材包括有機顏料,該有機顏料係選自由C.I.紅色 PR48:1、C.I.紅色 PR48:2、C.I.紅色 PR48:3、C.I. 紅色 PR53-1、C.I.紅色 PR101、C.I.紅色 PR102、C.I. 紅色PR122、C.I. 紅色 PR146、C.I. 紅色 PR168、C.I. 紅色 PR176、C.I. 紅色 PR185、C.I. 紅色 PR188、C.I. 紅色 PR254、C.I. 藍色 PB15:0、C.I. 藍色 PB15:1、C.I. 藍色 PB15:2、C.I. 藍色 PB15:3、C.I. 藍色 PB15:4、C.I. 藍色 PB15:6、C.I. 紫色 PV 19、C.I. 紫色 PV 23、C.I. 紫色 PV 32所組成之群組中之至少其一者。
本發明另提供一種基於保留特定波長之透光材料之複合載體,其具有如申請專利範圍第1或2項所述之基於保留特定波長之透光材料,其更包含一載體,該載體為熱塑性或熱固性之聚合物,或生物可分解塑料。
據上所述之基於保留特定波長之透光材料之複合載體,其中,該載體為熱塑性或熱固性之聚合物,該聚合物係選自由聚乙烯(Polyethylene, PE)、低密度聚乙烯(Low Density Polyethylene , LDPE)、線性低密度聚乙烯(Linear Low Density Polyethylene, LLDPE)、聚丙烯(Polypropylene, PP)、聚氯乙烯(PolyVinyl Chloride , PVC)或聚乙烯醋酸乙烯酯(Ethylene Vinyl Acetate, EVA)、聚甲基丙烯酸甲酯(poly(methyl methacrylate), PMMA),聚碳酸酯(Polycarbonate, PC),聚對苯二甲酸乙二酯(Polyethylene terephthalate, PET) 所組成之群組中之至少其一者。
據上所述之基於保留特定波長之透光材料之複合載體,其中,該載體為生物可分解塑料,該生物可分解塑料係選自由聚乳酸 (Polylactide, PLA)、聚丁二酸丁二醇酯(Polybutylene succinate, PBS)、聚丁二酸-己二酸-丁二酯共聚物(Polybutylene succinate adipate, PBSA) 、聚對苯二甲酸-己二酸-丁二酯共聚物(Poly(butylene adipate-co-terephthalate), PBAT)、聚羥基烷酸酯(Polyhydroxyalkanoates, PHA)、聚己内酯(Polycaprolactone, PCL)、聚乙烯醇(Polyvinyl alcohol, PVA)、纖維素奈米纖維(Cellulose Nanofiber, CNF)所組成之群組中之至少其一者。
據上所述之基於保留特定波長之透光材料之複合載體,其中,該載體係與該透光材料混合形成一組合物,該組合物為單層或多層之薄膜、編織網、遮蔽板、編織布或塑膠布者。
據上所述之基於保留特定波長之透光材料之複合載體,其中,該有機顏料之重量百分比係介於0.2至1%之間,該隔熱材料之重量百分比係介於0.2至1%之間。
據上所述之基於保留特定波長之透光材料之複合載體,更包含一添加物,該添加物為係選自由生物分解劑、抗氧化劑、光穩定劑、加工助劑、抗靜電劑、填料、增強材料,防霧劑所組成之群組中之至少其一者。
據上所述之基於保留特定波長之透光材料之複合載體,其中,該添加物之重量百分比係介於0.1至1%之間。
本發明另提供一種基於保留特定波長之透光材料之複合載體應用於農業之用途,其係將如申請專利範圍第3項所述之基於保留特定波長之透光材料之複合載體覆設於至少一作物與一光源之間。
本發明主要係可應用於農業,並主要透過篩選欲保留太陽光之波長,使保留特定區段之光波長得以通過透光材料,藉以提高植物行光合作用的效果,加速植物生長;並藉由結合隔熱材料,使在全球暖化的高溫環境中,可降低溫度,有助於農作物成長,於冬季時亦可有助於溫室保溫之效果,而複合載體可為熱塑性或熱固性之聚合物,或為生物可分解塑料,以製備形成薄膜、編織網、遮蔽板、編織布或塑膠布,以利於建置溫室、戶外棚架,或用以披覆於植物之生長空間處,藉以同時達致促進植物生長、隔熱及驅蟲之功效者。
關於吾等發明人之技術手段,茲舉數種較佳實施例配合圖式於下文進行詳細說明,俾供 鈞上深入了解並認同本發明。
本發明所定義之「保留特定波長」,係指可令特定區段之光波長可予穿透者。
本發明係一種基於保留特定波長之透光材料,其包含:
一透光材料,其包含一透光基材及一隔熱材料,該隔熱材料係選自由氧化錫銻(ATO)、氧化銦錫(ITO)、二氧化鈦、二氧化矽、氧化鋅、氧化鎢所組成之群組中之至少其一者;
該透光材料係用以保留波長於750 nm以下中的特定區段之光波長,使所述光波長得以通過該透光基材;該特定區段為:
區段A:320nm至380nm;
區段B:400nm至550nm;
區段C:650nm至750nm;
不僅於此,雖區段A、區段B及區段C皆有助於植物生長,惟其比例仍須予以控制,方能使植物有較佳之生長量,故本發明於一光線穿透該透光材料後,於該特定區段之平均穿透率分別為:
區段A:5至35%之間;
區段B:30至70%之間;
區段C:15至65%之間。
藉此,本發明係藉由更進一步控制各區段之平均穿透率,藉以提高較佳之植物生長適性之光波長及其強度。
本發明主要係利用具全光譜之光線照射該透光材料後,使位於區段A、區段B及區段C之光波長可予穿透該透光材料;就全光譜之光線而言,其係為利用自然之太陽光,因太陽光係具有全光譜,且屬具吸收譜線(夫朗和斐譜線)之連續光譜,而關於太陽光譜中的暗特徵譜線僅具數條單一波長之光線,其對於植物生長之影響甚小而可予忽略,故光照來源仍以無須額外耗損能源之太陽光為較佳者。
本發明對區段A、區段B及區段C之光波長之保留範圍,及其穿透後之強度配置,主要係因區段A之光波長可促進花青素形成、蛋白質及有機酸類之合成,而就花青素而言,其除有助於植物之增豔效果外,對人體亦具有諸多助益,故其顯具有增加作物產量及提升營養之效果;而就區段B及區段C而言,因光係植物行光合作用的能量來源,而植物感受外界環境的光受體包括光敏色素(Phytochrome)以及隱花色素(Cryptochrome, CRY),而這些光受體對於光譜的敏感性不同(即吸收不同波長範圍),透過這些光受體來接收光質、光量與光照的變化,進而引發不同反應來完成植物的生長發育,其中光敏色素主要感受紅光(620~700nm)及近紅外光(700~800nm),光敏色素作用為影響植物形態;隱花色素是植物感受藍光與近紫外線(330-390nm)區域的一種藍色受體,其主要吸收峰分別為370nm、420nm、450nm以及480nm;隱花色素可調控植物光合作用,對於植物生長發育具有調節作用,例如幼苗階段控制植物幼莖生長、幼苗去黃化反應以及開花週期調節等;而區段C則係屬紅、近紅外光,可被葉綠素強烈吸收,並可表現較強之光週期作用。
此外,本發明之透光材料係可抑制750nm以下之區段A、區段B及區段C以外之光波長,使其穿透率至約5%、10%、15%、20%或25%以下,並且其穿透率需低於區段A,以降低其對植物生長之影響;而就750nm以上之光波長,則可選擇性保留或濾除,因其並不顯著影響植物之生長,故本發明僅對750nm以下之區段A、區段B及區段C進行光波長之保留及穿透強度之控制。
其中針對區段B及區段C的平均穿透率範圍比例在1:2至9:2之間;較佳為1:2至3:1之間;其中若藍光比例減小,植物生長激素會減少,導致植株生長與開花延遲;反之若紅光偏多,則葉綠素吸收率較低,影響植物的光合作用與生長速度。
在一具體之實施例中,該透光材料為或包括有機顏料,該有機顏料係選自由C.I.紅色 PR48:1、C.I.紅色 PR48:2、C.I.紅色 PR48:3、C.I. 紅色 PR53-1、C.I.紅色 PR101、C.I.紅色 PR102、C.I. 紅色PR122、C.I. 紅色 PR146、C.I. 紅色 PR168、C.I. 紅色 PR176、C.I. 紅色 PR185、C.I. 紅色 PR188、C.I. 紅色 PR254、C.I. 藍色 PB15:0、C.I. 藍色 PB15:1、C.I. 藍色 PB15:2、C.I. 藍色 PB15:3、C.I. 藍色 PB15:4、C.I. 藍色 PB15:6、C.I. 紫色 PV 19、C.I. 紫色 PV 23、C.I. 紫色 PV 32所組成之群組中之至少其一者;本發明中,單一或多重混合之有機顏料皆可達致前述光波長保留範圍及其穿透後之強度,並可使用單一或多種有機顏料進行製備。
對於透光材料之複合載體而言,在一實施例中,係更包含一載體,該載體為熱塑性或熱固性之聚合物,或生物可分解塑料;其中,當載體為熱塑性或熱固性之聚合物時,該聚合物係選自由聚乙烯(Polyethylene, PE)、低密度聚乙烯(Low Density Polyethylene , LDPE)、線性低密度聚乙烯(Linear Low Density Polyethylene, LLDPE)、聚丙烯(Polypropylene, PP)、聚氯乙烯(PolyVinyl Chloride , PVC)或聚乙烯醋酸乙烯酯(Ethylene Vinyl Acetate, EVA)、聚甲基丙烯酸甲酯(poly(methyl methacrylate), PMMA),聚碳酸酯(Polycarbonate, PC),聚對苯二甲酸乙二酯(Polyethylene terephthalate, PET) 所組成之群組中之至少其一者;而於該載體為生物可分解塑料時,該生物可分解塑料係選自由聚乳酸 (Polylactide, PLA)、聚丁二酸丁二醇酯(Polybutylene succinate, PBS)、聚丁二酸-己二酸-丁二酯共聚物(Polybutylene succinate adipate, PBSA) 、聚對苯二甲酸-己二酸-丁二酯共聚物(Poly(butylene adipate-co-terephthalate), PBAT)、聚羥基烷酸酯(Polyhydroxyalkanoates, PHA)、聚己内酯(Polycaprolactone, PCL)、聚乙烯醇(Polyvinyl alcohol, PVA)、纖維素奈米纖維(Cellulose Nanofiber, CNF)所組成之群組中之至少其一者。
在另一實施例中,聚合物亦可為熱塑性彈性體,該熱塑性彈性體係選自由天然橡膠(Natural rubber, NR)、聚丁二烯橡膠 (Polybutadiene rubber, BR)、苯乙烯 - 丁二烯橡膠(Styrene butadiene rubber, SBR)、丁腈橡膠如丙烯腈一丁二烯橡膠(Nitrile butadiene rubber, NBR)、乙烯丙烯橡膠(Ethylene propylene monomer rubber, EPM)、乙烯丙烯二烯烴單體橡膠(Ethylene propylene diene monomer rubber, EPDM)所組成之群組中之至少其一者。
並在一應用中,該載體係與該透光材料混合形成一組合物,其混合製備方式係屬習知技術,故在此不予贅述,該組合物為單層或多層之薄膜、編織網、遮蔽板、編織布或塑膠布,以介於光源(如:太陽光)照射位置與植物間之面或空間為範疇,據以直接披覆植物生長空間之周圍,或其受太陽光照射之面,或構築形成溫室或戶外棚架者,使達致防風、驅蟲之目的,並能予以達致前述促進植物生長之效果。
另就組成比例而言,該有機顏料之重量百分比係介於0.2至1%之間,較佳者為0.3至0.6%之間;該隔熱材料之重量百分比係介於0.2至1%之間,較佳者為0.2至0.6%之間,使其添加不影響透光材料之對於區段A、區段B及區段C光波長之保留;而其餘部分者為載體。
在一較佳之實施例中,本發明於製成時,所採隔熱材料之粒徑係200nm以下,較佳為100nm以下,藉可有助於維持透光材料之透光性。
在另一實施例中,亦可依照需求而添加一添加物,該添加物為係選自由生物分解劑、抗氧化劑、光穩定劑、加工助劑、抗靜電劑、填料、增強材料,防霧劑所組成之群組中之至少其一者;該添加物之重量百分比係介於0.1至1%之間,較佳者為0.2至0.5%之間,使其添加不影響透光材料之對於區段A、區段B及區段C光波長之保留,而有機顏料及隔熱材料之重量百分比則同如前述,藉以賦予組合物具有添加物所屬種類之對應效果。
需特別說明的是,雖保留之光波長係位於區段A、區段B及區段C內,惟仍有在太陽光照射下使得光量強度太高或不足之疑慮,藉以於光量強度太高時,可能致使植物表面水分蒸散過快而葉燒,光量強度不足時則導致植物吸收不佳而養分失調;是以,有機顏料、隔熱材料及添加物之較佳範圍,皆為避免影響透光材料的透光性,並維持本發明所保留之特定區段及平均穿透率。
據上所述,茲舉具體實施例說明如下:
[實施例1]
分別將41克之3%氧化鎢以及12.5克之C.I. 紫色 PV 23混入196克之LDPE(低密度聚乙烯),並藉由單軸擠出機以200℃至250℃之溫度進行混練,以T字模擠出後,經一滾輪製成0.12mm厚之組合物透光薄膜,所得之組合物透光薄膜各成份之重量比例為:氧化鎢:0.5%、C.I. 紫色 PV 23:0.5%,其餘為LDPE;其光譜圖如第1圖所示。
[實施例2]
分別將0.83克之60%二氧化鈦與2.5克之30%C.I. 藍色 PB15:3混入246.67克之LDPE,並藉由單軸擠出機以200℃至250℃之溫度進行混練,以T字模擠出後,經一滾輪製成0.11mm厚之組合物透光薄膜,所得之組合物透光薄膜各成份之重量比例為:二氧化鈦:0.2%、C.I. 藍色 PB15:3:0.3%,其餘為LDPE;其光譜圖如第2圖所示。
[比較例]
將250克之LDPE,藉由單軸擠出機以200℃至250℃之溫度混練,以T字模擠出後,經滾輪製成0.12mm厚之薄膜,所得之該薄膜之組成分之重量比例為100% LDPE。
[實驗1]
將前述實施例1、實施例2及比較例所製得之組成物薄膜進行覆蓋,並置於氣溫為31℃之環境下,經遠紅外線燈連續照射四小時後,該比較例之覆蓋區域下的表面溫度為45℃,觀察實施例1與實施例2之組成物薄膜覆蓋區域與環境溫度之溫差,其實驗結果係如下表1所示: 【表1】
實施例1 | 實施例2 | 比較例 | |
隔熱材料種類/ 重量百分比 | 氧化鎢 0.5% | TiO2 0.2% | -- |
有機顏料種類/ 重量百分比 | C.I. 紫色 PV 23 0.5% | C.I. 藍色 PB15:3 0.3% | -- |
聚合物種類/ 重量百分比 | LDPE 99% | LDPE 99.5% | LDPE 100% |
厚度(μm) | 120 | 110 | 120 |
總重 (重量百分比) | 100% | 100% | 100% |
區段A 平均穿透率 | 23.7 | 8.3 | 68 |
區段B 平均穿透率 | 35.1 | 57.1 | 78 |
區段C 平均穿透率 | 59.4 | 19.5 | 84 |
經遠紅外線燈連續照射四小時後之環境溫度 | 45℃ | 45℃ | 45℃ |
實際測量溫度 | 41℃ | 42℃ | 45℃ |
環境溫差 | 4℃ | 3℃ | 0℃ |
由上表1可見,將本發明之組合物薄膜置放於紅外光線下,實施例1與實施例2之組成物薄膜覆蓋區域的表面溫度,分別和環境溫度相差為4℃、3℃,相對於比較例而言,證明本發明具有隔熱效果。
另,就實施例1及實施例2之組合物薄膜以Agilent公司型號為Cary 60 UV-Vis的紫外可見分光光度計測量,依據量測資料計算平均穿透率(T%)資料如上表1所示,可證本發明之複合載體相對於比較例而言,具有可保留特定區段之光波長。
以下利用實施例1與比較例進行葉菜類之作物種植試驗,以茲確認本發明具有促進植物生長快速之功效。
[實驗2]
本實驗係透過種植作物菠菜、甜A菜及莧菜,並將菠菜、甜A菜及莧菜個別之菜苗移植至48公升,含有培養土之塑料盤,並分別將實施例1與比較例製得之組合物薄膜架設在塑料盤上約30公分高,並放置於一光源(太陽光)下,在不額外施加肥料營養之情形下,觀察菠菜、甜A菜及莧菜之生長結果,如下表2所示: 【表2】
比較例 | 實施例1 | |||
植株高度(cm) | 葉綠素含量(μg/ml) | 植株高度(cm) | 葉綠素含量(μg/ml) | |
菠菜 | 14 (第21天) | 7.12 | 24 (第21天) | 12.79 |
甜A菜 | 25 (第25天) | 10.02 | 53 (第25天) | 15.65 |
莧菜 | 31 (第17天) | 9.66 | 50 (第17天) | 13.35 |
其中,關於葉綠素含量檢測方法與計算,係取完整之植株中,無病蟲害且葉色一致之葉片,經洗淨後去除葉梗,於烘箱中以60℃恆溫3小時以去除水分;乾燥後秤取0.5克之葉片,加入100ml 95%乙醇,而後於瓶口用封口膜密封並以鋁箔紙包覆,在室溫下避光萃取24小時;後將萃取液先以離心機離心10分鐘後再以紫外分光儀測量665nm和645nm處之吸光度值,以葉綠素包括葉綠素a及葉綠素b之含量計算葉綠素總含量,其中,葉綠素a及葉綠素b之含量計算係如下數學式1所示: 【數學式1】 葉綠素a(μg/ml)=13.7A665-5.76A645 葉綠素b(μg/ml)=25.8A645-7.60A665
其中,A665及A645係光波長於665nm、645nm下之吸收值;而葉綠素總含量為葉綠素a及葉綠素b含量之加總。
如前所述,顯見本發明經區段A至區段C之穿透率之控制後,相較於比較例之結果,顯見本發明確實可顯著提升植物之生長,有助於促進農業之發展。
綜上所述,本發明所揭露之技術手段確能有效解決習知等問題,並達致預期之目的與功效,且申請前未見諸於刊物、未曾公開使用且具長遠進步性,誠屬專利法所稱之發明無誤,爰依法提出申請,懇祈 鈞上惠予詳審並賜准發明專利,至感德馨。
惟以上所述者,僅為本發明之數種較佳實施例,當不能以此限定本發明實施之範圍,即大凡依本發明申請專利範圍及發明說明書內容所作之等效變化與修飾,皆應仍屬本發明專利涵蓋之範圍內。
無
第1圖係實施例1穿透率(T%)對波長(λ)之光譜圖。 第2圖係實施例2穿透率(T%)對波長(λ)之光譜圖。
Claims (9)
- 一種基於保留特定波長之透光材料,其包含:一透光材料,其包含一透光基材及一隔熱材料,該隔熱材料係選自由氧化錫銻(ATO)、氧化銦錫(ITO)、二氧化鈦、二氧化矽、氧化鋅、氧化鎢所組成之群組中之至少其一者;該透光基材包括有機顏料,該有機顏料係選自由C.I.紅色PR48:1、C.I.紅色PR48:2、C.I.紅色PR48:3、C.I.紅色PR53-1、C.I.紅色PR101、C.I.紅色PR102、C.I.紅色PR122、C.I.紅色PR146、C.I.紅色PR168、C.I.紅色PR176、C.I.紅色PR185、C.I.紅色PR188、C.I.紅色PR254、C.I.藍色PB15:0、C.I.藍色PB15:1、C.I.藍色PB15:2、C.I.藍色PB15:3、C.I.藍色PB15:4、C.I.藍色PB15:6、C.I.紫色PV 19、C.I.紫色PV 23、C.I.紫色PV 32所組成之群組中之至少其一者;且該有機顏料及該隔熱材料之比例為1:5至5:1之間;該透光材料係用以保留波長於750nm以下中的特定區段之光波長,使所述光波長得以通過該透光基材;該特定區段為:區段A:320nm至380nm;區段B:400nm至550nm;區段C:650nm至750nm;且於一光線穿透該透光材料後,於該特定區段之平均穿透率分別為:區段A:5至35%之間;區段B:30至70%之間;區段C:15至65%之間。
- 一種基於保留特定波長之透光材料之複合載體,其具有如申請專利範圍第1項所述之基於保留特定波長之透光材料,其更包含一載體,該載體為熱塑性或熱固性之聚合物,或生物可分解塑料。
- 如申請專利範圍第2項所述之基於保留特定波長之透光材料之複合載體,其中,該載體為熱塑性或熱固性之聚合物,該聚合物係選自由聚乙烯(Polyethylene,PE)、低密度聚乙烯(Low Density Polyethylene,LDPE)、線性低密度聚乙烯(Linear Low Density Polyethylene,LLDPE)、聚丙烯(Polypropylene,PP)、聚氯乙烯(PolyVinyl Chloride,PVC)或聚乙烯醋酸乙烯酯(Ethylene Vinyl Acetate,EVA)、聚甲基丙烯酸甲酯(poly(methyl methacrylate),PMMA),聚碳酸酯(Polycarbonate,PC),聚對苯二甲酸乙二酯(Polyethylene terephthalate,PET)所組成之群組中之至少其一者。
- 如申請專利範圍第2項所述之基於保留特定波長之透光材料之複合載體,其中,該載體為生物可分解塑料,該生物可分解塑料係選自由聚乳酸(Polylactide,PLA)、聚丁二酸丁二醇酯(Polybutylene succinate,PBS)、聚丁二酸-己二酸-丁二酯共聚物(Polybutylene succinate adipate,PBSA)、聚對苯二甲酸-己二酸-丁二酯共聚物(Poly(butylene adipate-co-terephthalate),PBAT)、聚羥基烷酸酯(Polyhydroxyalkanoates,PHA)、聚己內酯(Polycaprolactone,PCL)、聚乙烯醇(Polyvinyl alcohol,PVA)、纖維素奈米纖維(Cellulose Nanofiber,CNF)所組成之群組中之至少其一者。
- 如申請專利範圍第2至4項中任一項所述之基於保留特定波長之透光材料之複合載體,其中,該載體係與該透光材料混合形成一組合物,該組合物為單層或多層之薄膜、編織網、遮蔽板、編織布或塑膠布者。
- 如申請專利範圍第2至4項中任一項所述之基於保留特定波長之透光材料之複合載體,其中,該有機顏料之重量百分比係介於0.2至1%之間,該隔熱材料之重量百分比係介於0.2至1%之間。
- 如申請專利範圍第6項所述之基於保留特定波長之透光材料之複合載體,更包含一添加物,該添加物為係選自由生物分解劑、抗氧化劑、光穩定劑、加工助劑、抗靜電劑、填料、增強材料,防霧劑所組成之群組中之至少其一者。
- 如申請專利範圍第7項所述之基於保留特定波長之透光材料之複合載體,其中,該添加物之重量百分比係介於0.1至1%之間。
- 一種基於保留特定波長之透光材料之複合載體應用於農業之用途,其係將如申請專利範圍第2項所述之基於保留特定波長之透光材料之複合載體覆設於至少一作物與一光源之間。