TW459037B - Liquid crystal polyester resin composition - Google Patents

Liquid crystal polyester resin composition Download PDF

Info

Publication number
TW459037B
TW459037B TW86101862A TW86101862A TW459037B TW 459037 B TW459037 B TW 459037B TW 86101862 A TW86101862 A TW 86101862A TW 86101862 A TW86101862 A TW 86101862A TW 459037 B TW459037 B TW 459037B
Authority
TW
Taiwan
Prior art keywords
liquid crystal
group
crystal polyester
film
resin composition
Prior art date
Application number
TW86101862A
Other languages
Chinese (zh)
Inventor
Motonobu Furuta
Takanari Yamaguchi
Original Assignee
Sumitomo Chemical Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP22377696A external-priority patent/JP3648863B2/en
Priority claimed from JP24627596A external-priority patent/JPH1087967A/en
Priority claimed from JP8256034A external-priority patent/JPH10101909A/en
Application filed by Sumitomo Chemical Co filed Critical Sumitomo Chemical Co
Application granted granted Critical
Publication of TW459037B publication Critical patent/TW459037B/en

Abstract

This invention provides a liquid crystal polyester resin composition comprising a liquid crystal polyester (A) as the continuous phase and a rubber with a functional group reactive with the liquid crystal polyester (B) the dispersed phase. A liquid crystal polyester resin composition of the present invention excellent in heat resistance, molding processability, mechanical properties, and impact resistance and improved anisotropy of improved anisotropy of its formed article. Furthermore, it also provides a liquid crystal polyester resin composition excellent in film formation processability, gas barrier property, tensile property, banding resistance, pin resistance and high surface tension.

Description

45S 037 A7 B7 經濟部中央標準局員工消費合作社印m 五、發明説明（ 1 ) 1 | 明 領 域 1 1 本 發 明 乃 藉 射 出 成 形 或 擠 壓 成 形 等 方 法 製 造 薄 膜 成 1 1 I 形 物 等 用 之 液 晶 聚 m 樹 脂 組 κβ· 既 邏... 物 有 關 者 0 請 處 閱 1 1 I 知 抟 #r p 説 明 1 | 1 1 液 晶 聚 酯 有 異 於 聚 ilkj, m 苯 二 甲 酸 乙 二 酯 或 聚 對 苯 二 甲 酸 背 Φ 之 1 I 丁 二 酯 等 結 晶 性 聚 酯 由 於 其 分 子 m 直 * 卽 使 於 熔 融 狀 況 注 f 1 1 下 亦 不 會 絡 合 而 形 成 具 有 液 晶 狀 m 的 多 分 域 構 造 項 再 填 1 (P o ) y d 〇 m a > η St Γ U c t u r e) * Μ 低 剪 切 力 其 分 子 鐽 顯 示 傾 向 本 頁 1 沿 流 動 方 向 取 向 的 行 為 9 因 此 般 被 稱 為 向 熱 型 液 晶 ·»-· 1 I (Theraotro pi C 1 i q u id C r y S t a i )聚合物。 因為其特異行 1 1 為 t 向 熱 性 極 佳 » 可 容 易 製 得 0 . 2 " -0 .5 隱Ώ 左 右 的 薄 壁 成 形 1 1 物 * 而 且 該 成 形 物 具 備 高 強 度 % 高 m 性 等 優 點 0 然 而 却 有 訂 1 各 向 異 性 極 大 的 缺 點 0 再 者 其 制 振 性 能 或 耐 衝 擊 性 亦 不 足 1 I 1 成 形 加 工 溫 度 過 高 ， 所 以 己 往 其 用 途 有 限 0 外 • 一 般 1 | 而 液 晶 聚 酯 較 tm te 昂 亦 為 問 題 所 在 0 1 因 此 具 有 液 晶 聚 m 之 優 異 的 耐 熱 性 .、 機 械 性 能 成 1 I 形 加 工 性 m 衝 擊 性 成 形 物 之 各 向 異 性 播 得 改 善 > 且價 1 1 廉 的 液 晶 聚 eta 館 樹 脂 組 成 物 之 出 現 一 向 為 芾 場 所 期 待 C 1 1 曰 本 專 利 特 開 昭 56 -U5357號公報曽掲示箸含有可熔 1 1 融加 工 的 聚 合 物 及 各 向 異 性 熔 融 體 形 成 性 聚 合 物 之 樹 脂 組 1 1 成 物 锗 各 向 異 性 熔 融 m 形 成 性 聚 合 物 加 入 可 熔 融 加 I 的 1 | 聚 合 物 而 改 善 可 熔 融 加 工 的 聚 合 物 之 加 I 性 能 〇 例 如 舉 出 1 I 於 聚 伸 苯 基 醚 聚 苯 乙 烯 混 合 物 中 加 入 液 晶 聚 酯 等 〇 1 1 | 另 外 i B 本 待 開 平 2- 97555號公報中， 記載著以改善 1 1 ^紙張尺度適用中國國家標準（CNS ) A4規格（210X297公釐） ft 7 Λ 1 A7 B7 經濟部中央標率局員工消費合作社印敢 五、發明説明（ 2 ) 1 I 傾 接 耐 熱 性 為 百 的 » 於 液 晶 聚 酷 内 配 合 各 種 聚 伸 芳 基 氣 化 1 1 I 物 而 成 的 樹 脂 組 成 物 C 1 1 然 而 » 通 常 於 成 型 溫 度 較 离 的 液 晶 聚 酯 内 1 配 合 以 成 1 1 請 1 | 形 溫 度 較 低 的 聚 伸 苯 基 醚 等 非 晶 性 高 分 子 而 成 的 組 成 物 9 先 閱 1 1 1 | 其 組 成 物 之 熔 融 加 I 性 雖 得 以 改 善 > 但 在 高 溫 成 形 加 工 時 背 面 1 之 1 » 配 合 樹 脂 會 發 生 熱 分 解 » 而 有 引 起 成 形 物 外 觀 不 良 等 問 注 意 1 事 1 題 存 在 另 外 該 Μ 成 物 尚 有 耐 熱 性 > 機 械 性 能 耐 衝 擊 項 再 1 ▲ .L 性 等 不 足 之 問 覼 存 在 C 寫 頁 1 又 > Η 本 特 開 昭 57 -40551 m 公 報 1 特 開 平 2 - 102257 號 、—- 1 1 公 報 等 分 別 掲 示 有 由 液 晶 聚 酯 及 芳 族 聚 磺 酸 酯 而 成 的 組 成 1 1 物 t 其 酎 熱 性 或 迪 械 性 能 等 亦 不 甚 充 足 〇 1 i 又 * 曰 本 特 開 昭 58 -201 8 50號公報， 特開平1 -121 357 訂 1 號 公 報 * 特 開 平 1 - 193351 號 公 報 1 歐 洲 專 利 EP 672 7 2 / A2號 i j 公 報 t 特 開 平 7 - 304936號 公 報 等 亦 記 載 有 關 於 液 晶 性 高 分 i 1 子 内 配 合 例 如 甲 基 丙 烯 酸 縮 水 甘 油 酯 及 a -烯烴類之共聚 1 1 物 而 成 的 組 成 物 i 但 其 耐 衝 擊 性 或 抗 拉 強 度 等 機 械 性 質 仍 1 1 然 有 待 更 加 改 善 〇 1 1 美 國 專 利 第 521607 3號公報中記載著使用環氧化橡稼 1 1 及 液 晶 聚 合 物 之 成 形 物 1 此 乃 與 使 建 缠 相 之 環 氣 化 橡 膠 交 1 1 聯 、的 熱 硬 化 型 聚 物 有 關 者 0 1 1 方 面 J 就 薄 膜 原 料 之 觀 點 而 _ί_» 9 液 晶 聚 酯 乃 係 1 I 種 藉 強 分 子 間 相 互 作 用 在 熔 融 狀 m 下 分 會 定 (取） 向 為 其 1 1 I 待 激 之 聚 酸 C 因 此 i 由 於 其 強 分 子 間 相 互 作 用 及 分 子 定 向 1 1 1 » 除 對 液 晶 聚 m 而 言 熟 知 的 高 強 度 % 古 两 彈 性 率 高 耐 熱 性 1 1 本紙張尺度適用^國國家標準（CNS ) Λ4規格（210X297公釐） 4 38 70 1 A7 B7 經濟部中央標準局員工消費合作社印製 五、發明説明（ 3 ) 1 等 性 能 外 再 加 上 具 有 阻 氣 性 等 功 能 之 薄 膜 材 料 1 及 被 期 1 1 待 大 量 生 産 C 1 1 然 而 液 晶 聚 酯 不 同 於 聚 對 苯 二 甲 酸 乙 二 酯 或 聚 對 苯 二 1 甲 酸 丁 二 酯 等 芳 族 聚 酯 由 於 其 分 子 剛 直 即 使 在 熔 融 狀 況 請 處 閱 1 1 I 下 亦 不 會 絡 合 • 顯 示 出 分 子 鐽 顯 箸 的 流 動 方 向 定 向 » 卽 使 讀 背 δ 1 1 徹 弱 的 剪 切 力 亦 能 使 熔 融 粘 度 速 下 降 ， 溫 度 上 升 亦 使 之 注 意 1 1 I 熔 融 拈 度 急 速 下 降 ♦ 而 熔 融 時 表 現 掻 端 低 的 熔 融 拉 力 0 因 事 項 再 1 1 丄 此 在 熔 融 狀 態 下 極 難 維 持 其 形 狀 t 再 由 於 分 子 定 向 較 難 取 填 寫 本 -1 I 得 經 緯 性 能 之 平 衡 * 棰 端 情 況 下 曾 沿 分 子 定 向 方 向 而 裂 開 頁 、*·· 1 1 » 所 以 在 薄 膜 成 形 ’ 吹 塑 成 形 等 領 域 内 存 在 箸 缺 乏 實 用 性 1 1 等 重 大 問 題 0 因 此 % 由 液 晶 聚 酯 製 成 而 能 發 揮 液 晶 聚 酯 之 j I 功 能 的 薄 膜 直 未 能 實 用 化 0 訂 關 於 此 種 液 晶 聚 酯 1 Η 本 特 開 昭 52 -1095787號公 報 或 1 i 特 開 昭 58 -317187號公報中記載有將已單軸定向的液晶聚 1 ί 酯 薄 膜 ， 於 為 消 除 強 度 各 向 異 性 之 方 向 上 予 以 粘 接 而 成 積 1 1 靥 物 1 但 其 生 産 性 不 佳 同 時 尚 有 薄 膜 剝 離 之 問 題 0 1 美國專利第4975312號公報， 世界專利wo 9 0 1 570 6 號 1 1 公 報 等 記 載 有 藉 旋 轉 環 形 模 (R i η 8 d i e )之 方 法 以 消 除 液 晶 1 I 聚 酷 的 各 向 異 性 之 技 U 〇 % 外 i 恃 開 昭 62 - 2 5 5 1 3號公 報 ， 1 [ 待 開 昭 63 -95930號公 報 » 特 開 昭 6 3 - 2 42 5 1號公 報 中 亦 提 示 1 1 m T 模 法 之 特 殊 技 轄 〇 然 而 該 等 均 % 利 用 非 常 恃 殊 的 成 形 1 1 法 以 缓 和 由 於 分 子 定 向 引 起 的 各 向 異 性 9 其 成 本 高 而 薄 膜 1 1 化 有 其 極 限 * 缺 少 實 用 性 等 缺 酤 存 在 0 1 1 又 » 曰 本 特 開 昭 62-187033號公報， 特開昭64- -69323 1 1 本紙張尺度適用中國國家標隼（CNS ) A4規格（210X297公釐） 5 3 8 7 0 1 459037 A7 B7 經濟部中央標隼局員工消費合作社印製 五、發明説明（ 4 ) 1 | 號 公 報 t 待 開 平 2 - 17δ 0 1 6 號 公 報 % 待 開 平 2- 253919號公 報 1 I » 特 開 平 2- 253920號 公 報 t 持 開 平 2 - 25 3 949號公報 t 持 開 1 I 平 2- 25 3 9 50號公 報 等 記 載 有 液 晶 聚 酯 及 熱 塑 性 樹 脂 間 之 多 請 1 1 I 層 積 層 Η Λ 多 層 積 層 薄 膜 等 相 B9 關 者 9 由 於 液 晶 聚 酯 之 定 向 閲 讀 1 1 較 大 * 加 上 層 間 有 粘 接 曆 介 在 因 此 容 易 發 生 剝 離 現 象 背 1 之 1 注 1 以 致 液 晶 聚 m 本 身 具 有 之 阻 氣 性 i 耐 熱 性 等 性 能 降 低 或 製 意 事 1 造 薄 膜 困 難 等 問 題 存 在 〇 項 再 填 % 本 頁 1 丄 另 一 方 面 r 為 使 液 晶 高 分 之 各 向 異 性 緩 和 而 得 高 強 j 度 之 液 晶 聚 酯 薄 膜 1 亦 t 試 吹 m 成 形 製 造 薄 膜 者 0 'w·· 1 [ 吹 脹 成 形 製 膜 法 指 將 擠 壓 機 中 經 予 熔 融 温 煉 的 樹 脂 1 1 I t 镑 具 有 琿 狀 缝 口 之 模 頭 擠 m 出 筒 狀 熔 融 體 r 其 中 導 人 一 1 1 訂 定 量 的 空 氣 並 使 吹 脹 ί 在 冷 却 薄 膜 圓 周 下 製 成 筒 狀 薄 膜 之 1 方 法 〇 1 1 上 述 例 子 例 如 於 曰 本 特 開 昭 63 -1 7 3 6 2 0號公報 特 1 開 平 3 - 2 8 8 623號公報 特開平4 -4 1 2 6號公報、 特開平 1 吟. 4 - 502 3 3號公報、 或待開平4 -4 9 0 2 6號公 報 等 記 載 有 液 晶 聚 1 I SI 之 吹 脹 成 形 製 膜 的 方 法 1 均 俗 利 用 特 殊 成 形 薄 膜 設 備 1 i I 或 以 限 定 構 造 之 液 晶 聚 酯 為 製 造 對 象 * 或 在 槿 端 限 制 條 件 1 1 I 下 的 吹 脹 成 形 方 法 等 s 所 以 難 能 廣 泛 採 用 0 同 時 t 所 得 的 1 1 薄 m 之 拉 伸 性 或 阻 氣 性 等 不 甚 充 足 > 欲 予 薄 層 化 亦 有 困 難 1 1 甚 至 有 成 本 高 等 問 題 存 在 0 而 且 所 得 的 薄 膜 亦 有 來 自 市 1 1 場 上 指 摘 的 諸 市 場 上 也 被 指 如 拉 伸 性 m 曲 性 不 良 或 阻 1 I 氣 性 不 足 ·、 容 易 發 生 針 孔 表 面 張 力 低 印 刷 性 不 良 等 各 1 I 種 缺 點 存 在 1 本紙張尺度適用中國國家標準（CNS ) Λ4規格（21〇Χ2π公釐） 6 3 870 1 4 5 9 0 3 7 B7 經濟部中央標準局員工消費合作社印製 五、發明説明（5 ) 1 I 食 品 或 翳 療 用 途 之 殺 菌 軟 袋 材 料 或 可 直 立 的 軟 袋 用 包 1 1 I 裝 材 料 方 面 i 相 閿 的 開 發 研 究 成 果 多 有 所 在 C 1 1 例 如 曰 本 待 開 62 -1 0 3 1 3 9號公報中即掲示箸以表面上 I 1 請 1 I 乾 電 鍍 著 矽 之 樹 脂 薄 膜 作 為 構 成 成 分 的 殺 菌 軟 袋 (R e t or t 先 閱 1 I 讀 1 I P 〇 U C h) 用 包 裝 材 料 〇 背 1 之 1 恃 開 平 1 - 308826號 公 報 則 掲 示 箸 以 乙 烯 -乙烯醇共聚 注 意 1 I 事 1 物 為 主 成 分 之 殺 菌 軟 袋 用 包 裝 材 料 0 項 -g- 1 填 特 開 平 2 _ 1801 29號 公 報 則 掲 7J\ 著 由 乙 烯 -乙烯醇共聚 頁 1 物 薄 膜 或 偏 一 氣 乙 烯 共 聚 物 薄 膜 等 選 擇 而 製 成 的 殺 菌 軟 袋 、· 1 1 0 蒸 鍍 鋁 薄 膜 或 蒸 鍍 或 塗 布 矽 等 無 機 物 等 等 之 薄 m 無 法 1 1 1 在 徹 波 爐 中 使 用 1 同 時 i 基 底 樹 脂 薄 膜 之 耐 熱 性 不 足 或 焚 訂 1 燒 時 會 有 灰 分 殘 留 等 多 種 缺 點 存 在 而 受 使 用 者 指 摘 0 1 I 另 外 t 使 用 聚 偏 二 氮 乙 烯 薄 膜 時 t 殺 菌 處 理 時 耐 熱 性 1 1 不 充 足 或 使 用 後 焚 燒 時 會 發 生 廢 氣 問 題 等 亦 備 受 指 摘 0 1 1 » 又 使 用 乙 烯 -乙烯酵共聚物薄膜、 乙 酸 乙 烯 酯 共 1 | 聚 物 薄 膜 或 聚 酯 薄 膜 寺 0 亦 有 耐 熱 性 蒸 汽 阻 氣 性 及 耐 水 1 1 性 不 足 等 問 題 存 在 0 1 1 另 一 方 面 » 鋁 箔 在 殺 菌 軟 袋 用 包 裝 材 料 方 面 使 用 極 為 1 1 普 遍 ，但不能在檝波觼使用， 同時使用後也不能焚燒處理 1 I 或 對 於 金 腸 探 测 器 會 發 生 應 等 而 有 諸 多 待 解 決 的 問 題 ! I 點 〇 i I 恃 開 平 2 _ 26 1 456 號 公 報 ·、 特 開 平 5 - 27 87 47 號 公 報 特 1 1 1 開 平 7 - 237281 號 公 報 、 持 開 平 7- 241967號 公 報 等 掲 示 有 由 1 1 本紙張尺度適用中國國家標準（CNS ) A4規格（210X2的公1 ) 7 3 8 70 1 A7 B7 經濟部中央標準局員工消費合作社印裝 五、發明説明（ 6 ) 1 I 多 層 積 層 薄 膜 而 成 的 直 立 的 軟 袋 或 其 包 裝 材 料 相 鼸 資 料 1 1 ! 0 然 而 多 層 稹 層 薄 膜 製 m 困 難 、 成 本 高 層 間 容 易 發 生 1 1 1 請 1 I m 離 等 問 題 迄 今 仍 未 解 決 C 先 閱 1 I 讀 1 百 前 t 市 場 上 極 為 期 待 阻 氣 性 、 成 形 加 工 性 良 好 耐 背 1 之 1 熱 性 優 越 同 時 又 能 利 用 徹 波 瀘 加 溫 之 殺 菌 軟 袋 用 包 裝 材 注 童 1 事 1 料 之 出 現 〇 項 再 填 1 1 雖 然 ( 業 界 刖 亦 廣 泛 使 用 各 種 具 有 阻 氣 性 之 容 器 寫 本 頁 1 然 而 現 有 的 阻 氣 性 容 器 皆 無 法 充 分 湛 足 市 場 上 之 需 求 C 例 1 如 阻 氣 性 容 器 之 必 須 而 充 分 之 要 求 特 性 t 除 優 異 的 阻 氣 性 1 1 之 外 * 包 括 可 以 提 供 撤 波 嫌 加 溫 使 用 » 食 品 殺 餚 軟 袋 包 裝 1 ! 材 料 用 途 方 面 可 加 熱 處 理 等 的 耐 熱 性 ί 容 器 本 體 容 易 進 行 訂 | 薄 膜 化 之 成 形 加 工 性 1 使 用 後 之 回 數 C 容 易 廢 棄 處 理 等 市 1 1 場 上 之 多 種 要 求 ♦ 然 而 習 用 的 阻 氣 性 容 器 無 法 充 分 滿 足 該 1 1 等 要 求 0 1 1 例 如 聚 丙 烯 之 阻 氣 性 不 足 肯 乙 烯 -乙酸乙烯酯共聚物 1 在 吸 濕 狀 況 下 胆 氣 性 顯 箸 降 低 > 同 時 耐 熱 性 亦 不 足 0 聚 偏 1 1 一 氛 乙 烯 則 有 耐 熱 性 飫 » 又 因 含 有 氛 原 子 而 有 廢 棄 時 污 染 1 1 環 境 的 問 題 0 1 | , 聚 對 苯 二 甲 酸 乙 二 m 亦 俗 附 熱 性 不 足 t m 汽 阻 氣 性 不 ί I 良 等 缺 點 存 在 C 1 1 I 乙 烯 -乙酸乙烯酯共聚物或聚對苯二甲酸乙二酯上蒸 1 1 I 鍍 以 矽 鋁 等 無 機 物 而 成 的 阻 氣 性 材 料 或 熱 塑 性 樹 脂 上 1 1 粘 阽 以 鋁 箔 等 而 成 的 阻 氣 性 材 料 、 其 耐 熱 性 不 足 且 有 薄 膜 t 1 本紙張尺度適用中國國家標準（CNS ) A4規格（210X297公釐） 8 3 8 7 0 1 經濟部中央標準局員工消費合作社印製 五、發明説明（7 ) · 剝離等缺點，同畤使用金隱之材料亦有不能利用撤波瀘加 溫等問題存在。 質輕而有阻氣性的樹脂之中空成形體容器，現在廣範 地薩用在食品、飲料、工業用藥品或化粧品等包裝用途。 例如由乙烯-乙烯醇共聚物、聚偏二氛乙烯、聚對苯二甲 酸乙二酯等樹脂而成的中空成形體容器皆為周知常用者。 然而以上述樹脂材料吹塑成形而得中空成形體容器，其耐 熱性或阻氣性均不甚充足。又，在高溫下填充内容物於容 器時，或利用高溫液醱洗淨容器時，上述樹脂材料之容器 會有丽熱性不足等問題。 雖然眾所爾知液晶聚酯具備優異的附熱性及阻氣性， 然而由於液晶聚酯各向異性較大，又熔融粘度亦低，故較 難利用吹塑成形方法製得液晶聚酯之良好的中空成形體容 器C 由液晶聚酯或液晶聚酯組成物而成的成形體容器之相 鼷資料，例如於日本特開昭6 1 - 1 9 2 7 6 2號公報中記載有將 液晶聚酯及特定構迪之聚酯而成的樹脂組成物加以熔融成 形為中空成形體C 另外，日本特開平2 - 2 6 Ο δ 4 6號公報、特開平3 - 2 6 9 0 5 4 號公報上亦記載有關以聚對苯二甲酸乙二酿及液晶聚酯之 摻混物經予成形而得阻氣性優良的容器。 日本特開平1-289826號公報中記載有由聚對苯二甲酸 乙二酯層及液晶聚酯靥而成的積靨體之成形物。另外，曰 本待開平4- 1 663 20號公報亦記載有由特定構造之液晶聚酷 (請先閲讀背面之注意事項再填寫本頁) 本纸張尺度適用中國國家標準（CNS ) Λ4規格（210 X 297公釐） 9 38 7 0 1 A7 B7 經濟部中央標準局員工消費合作社印繁 五、發明説明（ δ ) 1 I 製 得 容 器 之 製 造 方 法 〇 1 1 I 然 而 任 一 種 方 法 均 由 於 樹 脂 之 成 形 加 X 性 能 不 良 肇 較 1 1 I 難 製 成 外 觀 良 好 的 成 形 體 容 器 » 同 時 生 産 效 率 低 > 或 容 器 請 處 閲 1 1 I 之 阻 氣 性 不 充 足 等 缺 點 存 在 9 迄 今 仍 無 法 充 分 滿 足 市 場 上 1 I 讀 1 1 之 需 求 〇 背 面 1 之 1 另 一 方 面 » 於 汽 車 産 業 領 域 由 於 市 場 上 之 需 求 t 多 年 注 意 1 I 事 1 由 考 慮 質 量 輕 成 形 加 工 性 強 度 設 計 自 由 度 等 之 觀 點 項 再 1 填 r 檢 討 開 發 研 究 塑 膠 質 製 汽 油 箱 〇 寫 本 頁 1 例 如 聚 乙 烯 樹 脂 具 有 優 異 的 成 形 加 工 性 及 強 度 等 i 然 •Sw-* 1 1 而 對 於 汽 油 之 阻 絶 性 不 足 0 1 1 曰 本 特 公 平 1 - 1 40 4 9號公報中記載有由聚醛胺、 聚酯 1 1 乙 烯 -乙酸乙烯酯共聚物中選擇其阻氣性層， 由改質聚 訂 1 烯 m 層 等 形 成 的 多 層 中 空 成 形 m 之 燃 料 油 箱 〇 1 1 曰 本 特 開 平 4- 47938號公報中亦記載由聚醯胺1、 高 1 | 密 度 聚 乙 烯 層 改 質 高 密 度 聚 乙 烯 層 等 而 成 的 多 層 中 空 成 1 形 體 之 燃 料 油 箱 〇 1 | 然 而 以 聚 酷 按 層 為 阻 絶 層 之 上 述 燃 料 油 箱 其 汽 油 阻 1 1 隔 性 不 足 » 又 對 於 混 合 有 甲 醇 等 混 合 醇 類 燃 料 » 更 顯 示 阻 1 1 絶 性 不 足 之 缺 點 〇 1 1 日本待開平6 -191296號公報中記載有使用芳族聚醯 1 1 胺 及 耐 綸 6 之 共 聚 合 聚 m 胺 層 為 阻 絶 性 層 由 改 質 高 密 度 1 | 聚 乙 缔 層 « 高 密 度 聚 乙 烯 層 等 多 層 構 造 之 中 空 成 形 體 而 成 1 1 的 汽 車 用 燃 料 油 箱 C 1 1 I 又 a 曰 本 待 開 平 6' -21889 1 號 公 報 中 亦 記 載 以 聚 乙 烯 及 1 1 本紙張尺度適用中國國家標準{ CNS ) A4規格（210X297公釐） 10 387 0 1 45903 7 A7 1 B7 經濟部中央標準局員工消費合作社印製 五、發明説明（9 ) 1 I 聚 胺 等 之 摻 混 物 為 阻 絶 性 層 的 多 層 成 形 物 之 燃 料 油 箱 0 1 1 I 曰 本 待 開 平 7 - 5 2 3 33號公報亦記載含有於乙烯- 乙 烯 酵 1 1 1 共 聚 物 内 配 合 熱 塑 性 樹 脂 而 成 樹 脂 組 成 物 製 得 的 多 靥 構 迆 1 I 請 1 I 物 而 成 之 燃 料 用 油 箱 j 待 開 平 7 - 40 9 98號公報中記載有耐 先 閱 1 I 讀 1 I 燃 性 發 泡 塑 隱 相 關 資 料 0 背 © 1 I 之 1 然 而 上 述 燃 料 油 箱 中 I 均 有 汽 油 阻 絶 性 或 對 由 汽 油 及 意 I 事 i 甲 醇 混 合 而 成 的 所 謂 汽 油 醇 有 阻 絶 性 不 足 之 問 題 » 另 外 ， 項 再 1 丄 為 保 持 高 阻 絶 性 掻 有 加 厚 樹 脂 層 之 需 要 C 鳥 頁 1 又 * 油 箱 為 多 層 構 造 物 構 造 9 由 層 間 剝 離 等 引 起 的 各 ·· t 種 問 題 I 迄 今 仍 未 能 解 決 C 1 1 發 泡 樹 脂 之 板 Η 薄 膜 等 成 形 物 » 由 於 質 量 輕 而 bb 較 1 1 強 軔 * 因 此 > 在 包 裝 材 料 建 築 材 料 工 業 設 備 辦 公 室 訂 1 用 設 備 缓 衝 材 料 等 領 域 内 廣 範 使 用 然 而 市 場 上 1 特 別 1 I 是 電 氣 用 品 電 子 機 器 汽 車 零 件 等 領 域 對 已 往 m 品 具 1 I 有 耐 熱 性 或 機 械 性 能 較 優 異 的 發 泡 樹 脂 之 出 現 更 加 期 待 著 1 1 0 液 晶 聚 m 基 本 上 乃 俗 能 滿 足 上 述 要 求 物 性 之 樹 脂 * 早 1 1 1 就 檢 討 研 究 該 種 發 泡 體 C 例 如 美 國 專 利 第 442906 1號公報 1 i 中 記 載 具 備 特 定 m 骨 幹 構 造 之 芳 族 聚 酯 發 泡 0 曰 本 特 公 1 1 平、2 - 4 2 0 99號公報中掲示著由特定液晶聚合物而成的聚合 1 | 物 發 泡 體 特 開 平 3 - 17 9 042 號 公 報 亦 記 載 液 晶 聚 合 物 之 發 1 I 泡 成 形 物 之 製 造 方 法 C 又 特 公 平 5 - -259 C 1號公報中記載著 1 1 I 含 有 液 晶 聚 酯 及 不 活 性 填 充 劑 之 發 泡 體 Η 相 關 資 料 0 本 1 1 1 待 開 平 4- -3 ] 80 39 號 公 報 記 載 規 定 發 泡 體 ηα 単 位 之 直 徑 的 液 晶 1 1 11 本紙張尺度適用中國國家標準（CNS ) Λ4規格（210X297公釐） 3 870 1 Ί 5 9 Ο 3 Τ Α7 Β7 經濟部中央標準局員工消費合作社印聚 五、發明説明（1 〇 ) 聚 合 物 發 泡 醱 t 特 公 平 7 - 7 4 2 8 5號公報中記載著限定構造 的 液 晶 聚 合 物 而 成 的 發 泡 樹 脂 成 形 物 C 然 而 習 用 的 液 晶 聚 合 物 之 發 泡 體 t 其 發 泡 成 形 醱 之 各 向 異 性 大 而 機 槭 性 能 不 足 > 或 外 觀 不 良 高 價 等 各 種 缺 點 依 然 存 在 0 發 明 .2^ 摘 沭 本 發 明 欲 解 決 之 課 題 在 於 提 供 可 得 保 持 著 液 晶 聚 酯 之 有 優 異 的 耐 熱 性 Ή 機 械 性 能 、 且 成 形 加 工 性 耐 衝 擊 性 良 好 各 向 異 性 m 1 改 良 的 成 形 物 » 且 形 成 薄 膜 性 阻 菊) 性 、 拉 伸 性 耐 彎 曲 性 耐 針 孔 性 皆 優 異 t 成 膜 加 工 性 亦 良 好 而 得 表 面 張 力 大 的 薄 膜 * 價 格 又 低 廉 的 液 晶 聚 酯 樹 脂 組 成 物 C 換 § 之 λ 本 發 明 之 目 的 在 提 供 ； 1 . 以由（ 甲 )成分， 液晶聚酯為連鑛相的（ 乙 )成分之與液 晶 聚 m 有 反 應 性 的 功 能 基 之 橡 膠 為 分 散 柑 作 為 其 特 擻 之 液 晶 聚 酯 樹 脂 組 成 物 » 以 及 2 · 由（甲 )成分液晶聚酯5 6 . 0 ^ -99 . 9重量％及（ 乙 )成分之 與 液 晶 聚 酯 有 反 應 性 的 功 能 基 之 橡 膠 44 .0 0 · 1重量％而 成 的 液 晶 聚 酯 拐 脂 組 成 物 0 另 外 * 本 發 明 亦 提 供 成 形 物 、 容 器 管 子 揀 選 器 ϋΆ m 維 ·、 塗 布 材 料 食 品 包 裝 薄 膜 Ί m 品 包 裝 薄 膜 -·» 電 子 材 料 包 裝 薄 膜 等 用 途 上 使 用 之 液 晶 聚 酯 組 成 物 C 發 明 詳 細 説 明 本 發 明 之 液 晶 聚 酯 樹 脂 Μ 成 物 其 中 ( 甲 成 分 之 液 晶 \ 0 本紙張尺度適用中國國家標準（CNS ) Α4規格（210X297公釐） 3 8 70 1 請 閱 背 面 ί 事 項 再 ύ 寫 本 頁 η A7 __B7 _五、發明説明（1 1 ) 聚酯係被稱為向熱性液晶聚合物之聚酯。 具體而言，舉例如 成 組 所 酸 羧 基 羥 族， 芳成 及組 以所 醇酸 元羧 二 基 族羥 芳族 及芳 酸的 羧類 Ί!, 二 種 族同 芳不 由由 而 應 反 酸 , 羧 成基 組羥 所族 醇 芳 元與 二 酯 族聚 芳 等 代醋 取 二 核乙 及酸 酸甲 羧 二 二 苯 族對 芳 聚 由由 族 芳 述 上 代 取 以 物 生 衍 用 酯 成 形 40等 在該 ， 用 等使 者可 得亦45S 037 A7 B7 Printed by the Consumers' Cooperative of the Central Standards Bureau of the Ministry of Economic Affairs. 5. Description of the Invention (1) 1 | Ming Field 1 1 The present invention is used to make films into 1 1 I-shaped objects by injection molding or extrusion molding. Liquid crystal polymethane resin group κβ · Existing logic ... Related parties 0 Please read 1 1 I 知 抟 #rp Description 1 | 1 1 Liquid crystal polyester is different from poly ilkj, m ethylene phthalate or poly Crystalline polyesters such as phthalate back Φ 1 I succinate, etc. Due to their molecular m Straight * 卽 in the molten state Note f 1 1 will not be complexed to form a multi-domain structural item with a liquid crystal m 1 (P o) yd omma > η St Γ U cture) * Μ Low shear force, its molecular 鐽 display tends to show the tendency on this page 1 Orientation in the direction of flow 9 Therefore, it is generally called a thermotropic liquid crystal · »-· 1 I (Theraotro pi C 1 iqu id C ry S t a i) polymer. Because its specific line 1 1 is excellent in t-direction thermal properties »0.2 " -0.5 .5 can be easily produced 1 to 1 thin-walled molding * and the molded product has the advantages of high strength, high m, etc. 0 However, it has the shortcomings of 1. The anisotropy is very great. 0 Furthermore, its vibration damping performance or impact resistance is also less than 1 I 1. The molding processing temperature is too high, so its use has been limited. 0 Outside • General 1 | And liquid crystal polyester Compared with tm te Ang, it is also the problem 0. Therefore, it has excellent heat resistance of liquid crystal poly m., Mechanical properties 1 I-shaped workability m improved anisotropy of impact molding > and price 1 1 cheap The appearance of the resin composition of the liquid crystal poly-eta building has always been a place to look forward to. C 1 1 Japanese Patent Application Laid-Open No. Sho 56-U5357 shows that it contains fusible 1 1 melt-processable polymers and anisotropic melt forming polymer. Resin Group 1 1 Germanium Anisotropic melting m forming polymer by adding 1 polymer that can be melted and added I | Improve the I performance of melt-processable polymers. For example, 1 I added liquid crystal to polyphenylene ether polystyrene mixture Polyester, etc. 〇1 1 | In addition, i B To be published in Kaiping No. 2-97555, it is stated that to improve 1 1 ^ paper size applies Chinese National Standard (CNS) A4 specification (210X297 mm) ft 7 Λ 1 A7 B7 Economy Ministry of Standards and Standards Bureau Staff Consumer Cooperatives Co., Ltd. Yin Dang V. Invention Description (2) 1 I Tilting heat resistance of one hundred »Resin composition made by mixing various polyarylidene gasification 1 1 I objects in liquid crystal polymer C 1 1 However, it is usually used in a liquid crystal polyester with a relatively low molding temperature. 1 It is compounded into 1 1 Please 1 | A composition made of amorphous polymers such as polyphenylene ether with a lower molding temperature. 9 Read 1 1 1 | Although the melt-addition properties of the composition are improved > but the back surface 1 of 1 during high temperature forming processing »the resin will thermally decompose» and cause the appearance of the molded product to be bad. 1 matter 1 problem exists There is still heat resistance > mechanical properties, impact resistance, and then 1 ▲ .L and other insufficiencies 覼 there are C write pages 1 and > Η JP-A-Sho 57 -40551 m gazette 1 JP-A No. 2-102257, --- 1 1 Bulletins and the like show the composition made of liquid crystal polyester and aromatic polysulfonate, respectively. 1 1 The substance t is not sufficient in heat resistance or dispersing performance. 0 i i * Japanese Patent Application Publication No. 58- Publication No. 201 8 50, Japanese Patent Application Laid-Open No. 1-121 357, Published Japanese Patent Application No. 1 * Japanese Patent Publication No. 1-193351, European Patent EP 672 7 2 / A2, Japanese Patent Publication No. 7-304936 The paper also describes the composition i obtained by blending, for example, a copolymer 1 1 of glycidyl methacrylate and a-olefins in the liquid crystal high fraction i 1, but its mechanical properties such as impact resistance and tensile strength It is still 1 1 but needs to be further improved. 1 US Patent No. 521607 3 describes the use of epoxidized oak 1 1 and a liquid crystal polymer molded product 1 This is a cross-linked ring gasified rubber 1 1 The related parties of thermosetting polymers are 0 1 1 and J. From the viewpoint of film raw materials _ί_ »9 Liquid crystal polyester is a type I. It is determined by the strong molecular interaction under the melting state m. Its 1 1 I polyacrylic acid to be excited, so i due to its strong intermolecular interaction and molecular orientation 1 1 1 »In addition to the high strength% well-known for liquid crystal poly m, high elasticity and high heat resistance 1 1 paper Applicable national standards (CNS) Λ4 specification (210X297 mm) 4 38 70 1 A7 B7 Printed by the Consumer Cooperatives of the Central Standards Bureau of the Ministry of Economic Affairs 5. Description of the invention (3) 1 In addition to properties such as film materials with gas barrier properties 1 1 1 To be mass-produced C 1 1 However, liquid crystal polyesters are different from aromatic polyesters such as polyethylene terephthalate or polybutylene terephthalate 1 due to their molecular rigidity. Reading 1 1 will not complex under I. • Shows the molecular orientation of the flow direction »卽 makes the reading back δ 1 1 The weak shear force can also reduce the melt viscosity speed, and the temperature rise also pays attention to 1 1 I The melting degree decreases sharply. ♦ The melting tension at the end of the melt is low. 0 due to the matter. 1 1 极 It is extremely difficult to maintain its shape in the molten state. T It is difficult to fill in this because of molecular orientation. Performance Equilibrium * In the case of 棰 -end, the page has been cracked along the direction of molecular orientation, * ·· 1 1 »So there is no practicality in the field of film forming, blow molding, etc. 1 1 and other major problems 0 Therefore,% by liquid crystal polyester Films made to fulfill the function of the liquid crystal polyester j I have not been put into practical use. 0 This liquid crystal polyester 1 Η Japanese Patent Laid-Open No. 52-1095787 or Japanese Patent Laid-Open No. 58-317187 It is described that a uniaxially-oriented liquid crystal poly 1 polyester film is bonded in a direction to eliminate strength anisotropy. 1 1 靥 1 but its poor productivity is similar to the problem of film peeling. 0 1 U.S. Patent No. 4,975,312, World Patent Wo 9 0 1 570 6 No. 1 1 Gazette and the like describe a method of eliminating liquid crystal by rotating a ring die (R i η 8 die). 〇% 外 i 恃 开 昭 62-2 5 5 1 3, 1 [Publication 63-95930 to be published »JP 6-3-2 42 5 The special technique of 1 1 m T-molding method is also suggested in the 1st publication. However, they all use very special moldings. 1 1 Method to alleviate the anisotropy due to molecular orientation 9 The cost is high and the thin film 1 1 has its limits * The lack of practicality and other defects exists 0 1 1 Also »Japanese Patent Application Publication No. 62-187033, Japanese Patent Application Publication No. 64- -69323 1 1 This paper size is applicable to China National Standard (CNS) A4 (210X297 mm) 5 3 8 7 0 1 459037 A7 B7 Printed by the Consumers' Cooperative of the Central Standards Bureau of the Ministry of Economic Affairs ) 1 | Announcement t To be published 2-17δ 0 1 6% Announcement to be published 2-253919 1 I »Announcement No. 2-253920 t Continued kai 2-25 3 949 Announced t OPEN 1 I 2- 25 3 9 No. 50 and other documents describe that there are many liquid crystal polyesters and thermoplastic resins. 1 1 I Laminated Η Λ Multi-layered laminated film and other phases B9 Gatekeeper 9 Due to the orientation reading of the liquid crystal polyester 1 1 Larger * With the adhesion between layers, peeling is easy to occur. Back 1 to 1 Note 1 As a result, the liquid crystal poly m has its own gas barrier properties i Heat resistance and other properties are reduced Or there are problems such as the difficulty of making a film. 项 Refill%. This page 1 丄 On the other hand, r is a liquid crystal polyester film 1 with a high degree of j to ease the high anisotropy of the liquid crystal. 0'w ·· 1 for film forming and manufacturing [Inflation film forming method refers to extruding a melted and tempered resin in an extruder 1 1 I t pound with a sipe-shaped die head to extrude a cylindrical melt r One of the methods is to introduce a certain amount of air and inflate it. 1 Method to make a cylindrical film under the cooling film circle. 0 1 1 The above example is described in, for example, Japanese Patent Publication No. 63 -1 7 3 6 2 0 JP 1 Kaihei 3-2 8 8 623 JP 6 Hei 4-4 1 2 6 JP Hei 1 yin. 4-502 3 JP 3 or 4 to 4 9 0 2 and other documents describe a method of forming a film by inflation molding of liquid crystal poly 1 I SI. 1 Special use of special molding film equipment 1 i I or a liquid crystal polyester with a limited structure as a manufacturing object * or restrictions on hibiscus Conditions 1 1 I, such as inflation molding methods, so it is difficult to widely use 0 1 t obtained at the same time t 1 thin m stretchability or gas barrier properties are not enough > thinning is also difficult 1 1 There are even problems with high cost, and the resulting film also comes from the market. 1 1 In the market, it has been pointed out in various markets, such as stretchability, poor flexibility, or resistance. I. Insufficient gas, and pinhole surface tension is easy to occur. Each of the 1 types of shortcomings, such as low printability, has 1 paper size applicable to China Standard (CNS) Λ4 specification (21〇 × 2π mm) 6 3 870 1 4 5 9 0 3 7 B7 Printed by the Consumer Cooperatives of the Central Standards Bureau of the Ministry of Economic Affairs 5. Description of the invention (5) 1 I Sterilization for food or therapeutic purposes Soft bag materials or upright soft bag bags 1 1 I The development and research results of i-phase materials are mostly found in C 1 1 For example, the Japanese version of the book is to be published 62-1 0 3 1 3 I 1 Please sterilize soft bag with 1 I dry plated silicon resin film on the surface (R et or t read 1 I read 1 IP 〇UC h) with packing material 〇1 back 1 恃 Kaiping 1-308826 Announcement No. 掲 shows that ethylene-vinyl alcohol copolymerization attention 1 I things 1 matter-based packaging materials for sterilization soft bags 0 item-g- 1 Fill in JP 2_ 1801 Announcement No. 29 7J \ The thickness of the sterilization soft bag made from the selection of ethylene-vinyl alcohol copolymerization film or vinylene copolymer film, etc., 1 1 0 vapor-deposited aluminum film or vapor-deposited or coated inorganic substances such as silicon, etc. 1 1 1 Use in a microwave oven 1 At the same time i The base resin film has insufficient heat resistance or incineration 1 There are many shortcomings such as ash residue during firing and it is criticized by users 0 1 I In addition t uses polyvinylidene dichloride film Heat resistance during sterilization treatment 1 1 Insufficient or exhaust gas problems during incineration after use. It is also criticized. 0 1 1 »Also use ethylene-vinyl acetate copolymer film, vinyl acetate copolymer 1 | polymer film or polymer Ester film temple 0 also has problems such as heat resistance, vapor and gas resistance, and water resistance. 1 1 Insufficient properties such as 0 1 1 On the other hand »Aluminum foil is used in sterilization soft bags The use of packaging materials is extremely common, but it cannot be used in a wave, and it cannot be incinerated after use, or there will be many problems to be solved for the gold bowel detector! I 点 〇i I 恃Kaiping 2 _ 26 1 456 ·, JP 5-27 87 47 JP 1 1 1 Kaiping 7-237281, Kaiping 7-241967, etc. It is stated that 1 1 This paper size is applicable to Chinese national standards (CNS) A4 specification (210X2 male 1) 7 3 8 70 1 A7 B7 Printed by the Consumer Cooperatives of the Central Standards Bureau of the Ministry of Economic Affairs 5. Description of the invention (6) 1 I Upright soft bag made of multiple laminated films or its packaging Material phase information 1 1! 0 However, it is difficult to make multi-layer thin films, and costs are prone to occur between high-rises. 1 1 1 Please ask 1 I m separation and other issues have not been resolved so far. C Read 1 I Read 1 hundred ago t The market is extremely looking forward to gas barrier properties and good formability. Back 1 1 Excellent thermal properties and packaging materials for sterilized soft bags that can be warmed with Teppo 注(The industry also widely uses various gas-barrier containers to write this page.1 However, none of the existing gas-barrier containers can fully meet the needs of the market. C Example 1 If the gas-barrier container is required, the required characteristics are sufficient. Excellent gas barrier properties beyond 1 1 * Including the use of warming for de-waves possible »Food killing food soft bag packaging 1! Heat resistance such as heat treatment in material use ί The container body is easy to order | Thin film forming process Performance 1 The number of times after use C Easy to dispose of the city 11 Various requirements on the market ♦ However, the conventional gas barrier capacity The device cannot fully meet the 1 1 and other requirements. 0 1 1 For example, the gas barrier properties of polypropylene are insufficient. Ken ethylene-vinyl acetate copolymer 1 has a significantly reduced bile properties under hygroscopic conditions. At the same time, the heat resistance is also less than 0. 1 1 Ethylene has heat resistance 饫 »Pollution when discarded because it contains atmospheric atoms 1 1 Environmental problems 0 1 |, Polyethylene terephthalate m also has insufficient heat resistance tm Vapour barrier properties I Good and other shortcomings C 1 1 I Ethylene-vinyl acetate copolymer or polyethylene terephthalate steamed on 1 1 I Gas barrier material or thermoplastic resin coated with inorganic materials such as silicon aluminum, etc. 1 1 Tack气 Gas barrier materials made of aluminum foil, etc., which have insufficient heat resistance and have a thin film t 1 This paper size is applicable to China National Standard (CNS) A4 specifications (210X297 mm) 8 3 8 7 0 1 Employees of the Central Standards Bureau of the Ministry of Economic Affairs Printed by Consumer Cooperatives , Described the invention (7) and peeling and other shortcomings, Zhi with gold material also can not take advantage of hidden withdraw isothermal wave Lu added problems. Light-weight and gas-barrier resin hollow molded product containers are now widely used for packaging applications such as food, beverages, industrial pharmaceuticals, and cosmetics. For example, hollow molded product containers made of resins such as ethylene-vinyl alcohol copolymer, polyvinylidene chloride, and polyethylene terephthalate are well-known and commonly used. However, a hollow molded container obtained by blow molding with the above resin material has insufficient heat resistance or gas barrier properties. In addition, when the contents are filled in a container at a high temperature, or when the container is washed with a high-temperature liquid, the container of the resin material may have problems such as insufficient thermal properties. Although it is well known that liquid crystal polyesters have excellent heat resistance and gas barrier properties, it is difficult to obtain liquid crystal polyesters by blow molding because of its high anisotropy and low melt viscosity. The hollow molded body container C of the molded body container made of a liquid crystal polyester or a liquid crystal polyester composition, for example, is described in Japanese Patent Application Laid-Open No. 6 1-1 9 2 7 6 2 A resin composition made of an ester and a specific polyester is melt-molded into a hollow molded body C. In addition, Japanese Patent Application Laid-Open No. 2-2 6 Ο δ 4 and Japanese Patent Application Laid-Open No. 3-2 6 9 0 5 4 The above also describes a container having excellent gas barrier properties obtained by preforming a blend of polyethylene terephthalate and liquid crystal polyester. Japanese Patent Application Laid-Open No. 1-289826 describes a molded article of a stacked body composed of a polyethylene terephthalate layer and a liquid crystal polyester. In addition, the Japanese Patent Publication No. 4- 1 663 20 also describes the specific structure of the liquid crystal polymer cool (please read the precautions on the back before filling this page) This paper size applies the Chinese National Standard (CNS) Λ4 specification ( (210 X 297 mm) 9 38 7 0 1 A7 B7 Employees' Cooperatives of the Central Standards Bureau of the Ministry of Economy Yin Fan 5. Description of the Invention (δ) 1 I Manufacturing method for making containers 〇1 1 I However, any method is due to the resin Poor performance in forming plus X. Compared with 1 1 I, it is difficult to make a molded body container with good appearance »At the same time, the production efficiency is low> or the container please read 1 1 I Insufficient gas barrier properties and other shortcomings 9 There are still not enough to meet the market so far On the 1 I read the demand of 1 1 on the back 1 of the other hand »in the automotive industry due to market demand t years of attention 1 I matter 1 by considering light weight Dimensional aspects such as design flexibility, strength, design freedom, etc. Fill in r to review and develop a plastic gasoline tank. Write this page 1 For example, polyethylene resin has excellent molding processability and strength, etc. • Sw- * 1 1 and Gas barrier is insufficient for gasoline. 0 1 1 Japanese Patent Publication No. 1-1 40 4 9 describes that the gas barrier layer is selected from polyalmine and polyester 1 1 ethylene-vinyl acetate copolymer. Modified polymer fuel tanks of multilayer hollow molding m formed of modified polyene 1 m layers, etc. 〇1 1 Japanese Patent Application Publication No. 4-47938 also describes polyimide 1, high 1 | density polyethylene layer modified high density Multi-layer hollow fuel tanks made of polyethylene layers, etc. 01 | However, the above fuel tanks with Juku layer as the barrier layer have gasoline resistance of 1 1 and insufficient barrier properties. Blended with mixed alcohol fuels such as methanol »It also shows the shortcomings of resistance 1 1 Insufficient resistance 〇1 1 Japanese Unexamined Patent Publication No. 6-191296 describes the use of aromatic polyfluorene 1 1 amine and nylon 6 copolymerization polymer m The amine layer is a barrier layer. Modified high-density 1 | Polyethylene layer «High-density polyethylene layer and other hollow structures with a multilayer structure. 1 1 Fuel tank for automobiles C 1 1 I and a 6'-21889 No. 1 also states that polyethylene and 1 1 paper sizes are applicable to the Chinese National Standard {CNS) A4 (210X297 mm) 10 387 0 1 45903 7 A7 1 B7 Employee Consumer Cooperatives of the Central Standards Bureau of the Ministry of Economic Affairs Printed 5. Description of the invention (9) Fuel tank for multi-layer molded articles with blends of 1 I polyamines as barrier layers. 0 1 1 I Japanese Patent Publication No. 7-5 2 3 33 also contains Ethylene-vinylase 1 1 1 copolymer blended with thermoplastic resin Multi-layer structure made from resin composition 1 I Please request 1 I fuel tank for fuel j To be opened 7-40 9 98 First reading 1 I read 1 I flammable foam plastic Related information 0 Back © 1 I 1 However, I in the above fuel tanks have gasoline barrier properties or lack of barrier properties to the so-called gasoline alcohols which are made by mixing gasoline and methanol. »In addition, 1 保持 In order to maintain high resistance 掻 A thick resin layer is required. C bird page 1 * The fuel tank is a multi-layer structure 9 Various problems caused by peeling between layers, etc. I have not yet solved C 1 1 Sheets made of foamed resin 成形 Films and other molded articles »bb is better than 1 1 because of its light weight 轫 * Therefore > In the package Materials, building materials, industrial equipment, office equipment, 1 equipment, buffer materials, and other widely used in the field. However, the market is 1 special 1 I is electrical appliances, electronic equipment, automotive parts, and other fields. 1 I has good heat resistance or mechanical properties. The appearance of foamed resin is more expected. 1 1 0 Liquid crystal poly m is basically a resin that can meet the above-mentioned physical properties. * As early as 1 1 1 Review and study of this kind of foam C. For example, US Patent No. 442906 1 Gazette 1 i Aromatic Polyester Foam with Specific m Backbone Structure is described in Japanese Patent Publication No. 1 1 Flat, 2-4 2 0 99, which shows a polymer 1 made of a specific liquid crystal polymer | Kaiping No. 3-17 9 042 also describes the development of liquid crystal polymers. 1 I Method for manufacturing foamed products. C-Fair 5--259 C. No. 1 describes that 1 1 I contains liquid crystal polyester and inactive filler. Foam Relevant information 0 This 1 1 1 To be Kaiping 4- -3] 80 39 describes the liquid crystal that specifies the diameter of the ηα 単 position of the foam 1 1 11 This paper size applies the Chinese National Standard (CNS) Λ4 specification (210X297 mm) ) 3 870 1 Ί 5 9 Ο 3 Τ Α7 Β7 Printed by the Consumers' Cooperative of the Central Bureau of Standards of the Ministry of Economic Affairs 5. Description of the invention (1 〇) Polymer foam 酦 t special fair 7-7 4 2 8 5 A foamed resin molded product C of a liquid crystal polymer with a limited structure. However, conventional liquid crystal polymer foams t have a large anisotropy in foam molding and insufficient mechanical properties, or poor appearance and high prices. There are still 0 inventions. 2 ^ Abstract: The problem to be solved by the present invention is to provide a liquid crystal polyester with excellent heat resistance, mechanical properties, and good formability and impact resistance. Property m 1 Improved molded product »Also formed thin film resistance Chrysanthemum) Excellent performance, stretchability, bending resistance, pinhole resistance, t film forming processability is also good, resulting in a film with high surface tension * Low cost LCD polymer Ester resin composition C for λ of the present invention The purpose of the present invention is to provide: 1. A rubber having a functional group that is reactive with liquid crystal polym with (B) component consisting of (A) component and liquid crystal polyester as a mineral phase Liquid crystal polyester resin composition for dispersing citrus as its special property »and 2. · Liquid crystal polyester composed of (a) component 5 6 0-99.9 wt% and (b) component having reactivity with liquid crystal polyester Functional base rubber 44.0 0 · 1% by weight of liquid crystal polyester grease composition 0 In addition * The present invention also provides molded articles, container and tube pickers ϋΆ m dimension, coating materials food packaging films Ί m products Packaging film- · » Liquid crystal polyester composition C used for electronic material packaging film and other applications. Detailed description of the invention The liquid crystal polyester resin M product of the present invention is (a component of the liquid crystal \ 0) This paper size applies to China National Standard (CNS) A4 specification (210X297 (Mm) 3 8 70 1 Please read the matter on the back and write this page η A7 __B7 _V. Description of the invention (1 1) Polyester is a polyester called thermotropic liquid crystal polymer. Specifically, for example, the carboxyl hydroxyl group of the acid group, the aromatic group and the carboxylic acid group of the hydroxydicarboxylic acid group hydroxyaromatic group and the carboxylic acid group of the aromatic acid group! Carboxylated hydroxy group alcohol aromatics and diester polyaromatic vinegars take dinuclear ethyl and acid methyl carboxydiphenyl di-para-arylene to form by esterification from the family narrative to the natural derivatives 40 Wait for it

者 物 融 熔 性 異 向 各 成 形 能 下 以 P 外 另 芳 r 酸 羧 本 但 例 為 造 構 列 下 舉 可 位 單 〇 造 酸構 羧複 基重 羥之 族酯 芳聚 及 晶 醇液 元 該 二 族 者 定 限 所 例 施 實 等 此 受 .三— 並 明 發 (請先閱讀背面之注意事項再填寫本頁) --ί 訂 經濟部中央標率局員工消費合作社印製 本紙張尺度適用中國國家標準（CNS ) Λ4規格（210X 297公釐） 3 11 3870 1 A7 B7 五、發明説明) 芳族二羧酸由來之重複構造單位 cmmmo cmho chmoThe melting and anisotropy of the material can be reduced to P and other aromatic acid carboxylic acids. However, the examples are listed below. The acid esters of carboxylic acid, carboxylic acid, and heavy hydroxyl group esters are aromatic and crystalline alcohols. The implementation of the limits of the two ethnic groups is subject to this. Three-and Mingfa (please read the precautions on the back before filling out this page)-Order the paper size printed by the Staff Consumer Cooperative of the Central Standards Bureau of the Ministry of Economic Affairs Applicable to Chinese National Standard (CNS) Λ4 specification (210X 297 mm) 3 11 3870 1 A7 B7 V. Description of the invention) The repeating structural unit derived from aromatic dicarboxylic acid cmmmo cmho chmo

X c=o c=o c=o 素 鹵 示 X /1 基 芳 基X c = o c = o c = o

CUMOCUMO

C ΠΗΟC ΠΗΟ

c MHO (請先閱讀背面之注意事項再填寫本頁) i 訂 經濟部中央標準局員工消費合作社印製 c=o c=oc MHO (Please read the notes on the back before filling out this page)

o so s

c=oc = o

CUMUO 本紙張尺度適用中國國家標準（CNS ) Λ4規格（210 X 297公釐） 14 3 87 0 1 A7 B7CUMUO This paper size applies to Chinese National Standard (CNS) Λ4 size (210 X 297 mm) 14 3 87 0 1 A7 B7

本紙張尺度適用中國國家標準（CNS ) A4規格（210 X 297公釐） 1 E； ^ fi 7 A 1 五、發明説明（13 ) 源自芳族二元醇之重複構造單位： A7 五、發明説明（14 )This paper size applies the Chinese National Standard (CNS) A4 specification (210 X 297 mm) 1 E; ^ fi 7 A 1 V. Description of the invention (13) Repeated structural units derived from aromatic diols: A7 V. Invention Instructions (14)

CH2CH2

ο 0-0ο 0-0

οο

Μ H2CίΗ02 c c—c-c SΜ H2CίΗ02 c c—c-c S

οο

οο

ο -------：——{:,—— (請先閱讀背面之注意事項再填寫本頁)ο -------: —— {:, —— (Please read the notes on the back before filling this page)

SS

οο

、tT 經濟部中央標準局員工消費合作社印製 本紙張尺度適用中國國家標隼{ CNS ) A4規格（210 X 297公釐） 16 3 8 7 0 1 459037 A7 B7 五、發明説明（15 位 單 造 構 複 重 之 酸 羧 基 羥 族 芳 白 源, TT Printed by the Consumers' Cooperative of the Central Bureau of Standards of the Ministry of Economic Affairs The paper size is applicable to the Chinese national standard {CNS) A4 (210 X 297 mm) 16 3 8 7 0 1 459037 A7 B7 V. Description of the invention (15 digits) Carboxylic acid, hydroxy, aromatic, white source

cnNOcnNO

c=oc = o

c=oc = o

有 含 酯 聚 基 烷 素 ® 示 晶 液 的 佳 尤 而 衡 均 之 性 Η 加 f ~τ·: -11-_* in·'^ m n 1^1 一SJ'n (請先聞讀背面之注意事項再填寫本頁) 經濟部中央標準局員工消費合作社印製It has a good balance of properties with ester-containing polyalkylene ® crystals. Η f ~ τ ·: -11 -_ * in · '^ mn 1 ^ 1 (SJ'n) (Please fill in this page for attention) Printed by the Consumer Cooperatives of the Central Bureau of Standards of the Ministry of Economic Affairs

c MHO 耳 莫 ο 3 少 至 之 量 總 占 位 單 造 構 複 , 重 者述 位上 單 有 造含 構為 複者 重佳 的更 而 者 本紙張尺度適用中國國家標準（CNS ) Λ4規格（2〗0X297公釐） 7 11 387 0 1 A7 B7c MHO 耳 莫 ο 3 The least amount of the total placeholders is used to construct the complex, the more important ones are the ones that contain the structures that are better than the more complex ones, and the paper standards are applicable to the Chinese National Standard (CNS) Λ4 specifications ( 2〗 0X297 mm) 7 11 387 0 1 A7 B7

本紙張尺度適用中國國家標準（CNS ) Λ4規格（210X 297公釐） jj 3 8 70 1 五、發明説明（l 〇 五、發明説明（〗7 ) A7 B7This paper size applies to the Chinese National Standard (CNS) Λ4 specification (210X 297 mm) jj 3 8 70 1 V. Description of the invention (105) Description of the invention (7) A7 B7

___II___I _/ *___ m. mi i ml Bn^i ^^^1 V ^^^1 In nn fn mt —Tr^i l\s' (請先閱讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標準（CNS ) A4規格（210X297公釐） 19 3870 1 A7 B7 五、發明説明（1 8 (VI)___II___I _ / * ___ m. Mi i ml Bn ^ i ^^^ 1 V ^^^ 1 In nn fn mt —Tr ^ il \ s' (Please read the precautions on the back before filling this page) This paper size applies Chinese National Standard (CNS) A4 specification (210X297 mm) 19 3870 1 A7 B7 V. Description of invention (1 8 (VI)

C (請先閲讀背面之注意事項再填寫本頁} c=oC (Please read the notes on the back before filling out this page) c = o

上述液晶聚酯（I)〜（VI)之製造方法傈記載於例如日 本特公昭47-47870號公報、特公昭63-3888號公報、特公 昭63-3891號公報、待公昭56-〗8016號公報、特公平 2-51523號公報等c 其中較佳者為（丨）、（II)、 （IV)之組合，更佳者為（I) ,(ί I)之組成。 本發明之液晶聚酯樹脂組成物中，要求高耐熱性之領 域，以採用ί甲）成分之液晶聚酯含有下列重複構造單位 (a.Μ為30〜80莫耳％、重複構造單位（b’）為0〜10莫耳％ 、重複構造單位（c')為10〜25莫耳％、重複構造單位（(T) 為10〜35莫耳％而成的液晶聚酯為較宜。 本紙張尺度適用中國國家標準（CNS ) A4規格（210X297公釐） £ 〇 3870 1 訂 經濟部中央標準局員工消費合作社印製 五、發明説明（1 9 A7 B7The manufacturing methods of the liquid crystal polyesters (I) to (VI) are described in, for example, Japanese Patent Publication No. 47-47870, Japanese Patent Publication No. 63-3888, Japanese Patent Publication No. 63-3891, and Japanese Patent Publication No. 56- 〖8016. Gazette, Japanese Patent Publication No. 2-51523, etc. c Among them, the combination of (丨), (II), (IV) is preferred, and the composition of (I), (ίI) is more preferred. In the liquid crystal polyester resin composition of the present invention, in the field requiring high heat resistance, the liquid crystal polyester using the component A contains the following repeating structural unit (a.M is 30 to 80 mol%, repeating structural unit (b A liquid crystal polyester made of 0 to 10 mol%, a repeating structural unit (c ') of 10 to 25 mol%, and a repeating structural unit ((T) of 10 to 35 mol%) is preferred. Paper size applies to Chinese National Standard (CNS) A4 (210X297 mm) £ 〇3870 1 Order printed by the Consumer Cooperatives of the Central Standards Bureau of the Ministry of Economic Affairs 5. Description of invention (1 9 A7 B7

--Ο - At—Ο—j— ( d ') 經濟部中央標準局員工消費合作社印製 (上式中，Ar·示二價芳基）。 本發明之液晶聚酯樹脂組成物中（乙）成分為具備能與 (甲）成分之液晶聚酯有反應性的功能基之橡膠。 上述橡膠之意義如新販的高分子辭典（日本高分子學 會编，1988年，朝會書店發行）所載於室溫下具有橡_彈 性的高分子化合物皆包括之。其具鱧例舉有天然橡膠、丁 二烯聚合物、了二烯-苯乙烯共聚物[無規共聚物，嵌段共 聚物（包含SEBS橡膠或SBS橡膠等），接枝共聚物等皆包括 之Ί,或其加氳化合物、異戊二烯聚合物、氮化丁二烯聚 合物、丁二烯-丙烯腈共聚物、異丁烯聚合物、異丁烯-丁 二烯共聚物橡膠、異丁烯-異戊二烯共聚物、丙烯酸酯-乙 烯条共聚物橡膠、乙烯-丙烯共聚物橡繆、乙烯-丁烯共聚 物橡膠、乙烯-丙烯-苯乙烯共聚物捸膠、苯乙烯-異戊二 r .... ..... 21 本紙張尺度適用中國國家標準（CNS ) A4规格（210 X 297公釐） 3 870 1 ----^------ ^------訂------{1 (請先閱讀背面之注意事項再填寫本頁) r 459037 β7 五、發明説明（2G ) 烯共聚物橡曬、苯乙烯-丁烯共聚物、苯乙烯*乙烯-丙烯 共聚物橡膠、全氟橡膠、含氟橡_、氨丁二烯橡膠.、丁基 橡謬、矽氧橡驟、乙烯-丙烯-非共_二烯共聚物橡暖、碕 醇橡膠、多硫化橡駿、聚胺酯橡膠、聚醚橡匾（例如聚環 氣丙烷等）、環氣氣丙烷橡膠、聚酯彈性體、聚醒胺彈性 體等。其中以丙烯酸醱-乙烯条共聚物較宜，最佳為 (甲基）丙烯酸酯-乙烯糸共聚合物橡謬。 該橡_類化合物無論用任何方法製造（例如乳化聚合 法、溶液聚合法等）、或利用任何催化劑（例如過氧化物、 三烷基鋁、鹵化鋰、鎳条催化劑等）製造者皆可利用； 上述與液晶聚_有反應性之功能基.衹要能與液晶聚 酯具有反鼴性即可並無其他限制，具體例舉有環氣基、噁 唑基、胺基等.其中以環氣基較宜。具有環氣基之功能基 中，最佳為縮水甘油基。具有縮水甘油基之單體中，以不 飽和羧酸縮水甘油、不飽和縮水甘油基乙醚等最常被利用 0 經濟部中央標準局員工消費合作社印製 (請先閱讀背面之注意事項再填寫本頁) 將與液晶聚酯有反應性之功能基導入橡嚷中之方法並 無特別限制，可按照一般常見方法進行之。例如於合成橡 _之過程中，藉共聚合反應導入具有該功能基之單體亦為 一 |1可行方法，另外，利闬接枝共聚合度應將具有該功能 基之單體導入橡瞜中亦鼷可行的。 本發明之與液晶聚酯有反應性的功能基之（乙）成分橡 _的較佳具醱例舉有（甲基）丙烯酸酯-乙烯-不飽和羧酸縮 水甘油酯及/或不飽和縮水甘油基乙隧共聚物橡 本紙張尺度適用中國國家標率（CNS ) A4規格（210X297公釐） 22 38 7 0 1 經濟部中央標準局員工消費合作社印裝 4 h Q Ο ^ 7 〜wx ‘ *·.‘. t. A 7 B7 五、發明説明（2】） 上述共聚物橡瞟之主要構成成分之（甲基）丙烯酸酯乃 由丙烯酸或甲基丙烯酸與酵類而得的酷類。該醇類以碩數 為丨至8個之醇類為較宜。該（甲基）丙烯酸酯之具體例舉 有丙烯酸甲酯、甲基丙烯酸甲酯、丙烯酸正丁酯、甲基丙 烯酸正丁酯、丙烯酸第三丁酯、甲基丙烯酸第三丁酯、丙 烯酸2 -乙基己酯、甲基丙烯酸2 -乙基己酯等c又該（甲基） 丙烯酸酯類除可單獨使用外，亦可以二種以上合併使用。 賦與不飽和羧酸縮水甘油酯單位及不飽和縮水甘油基 乙醚單位之化合物分別以下列一般式（1 )及（2 )表示之， R—C—0—CH，一 CH—CH7 … 11 \ ~ ⑴ 0 〇 (上式内，R示具有乙烯条不飽和鍵結之碳數為2〜13 之烴基。> R 一 X—CH〗一CH—CH2 { ί \ \/ ㈡ (上式内，R示具有乙烯系不飽和鍵結之硝數為2〜18 之烴基.Z為-CH2-0 -或 - 具體而言，不飽和羧酸縮水甘油基酯之例舉有丙烯酸 縮水甘油基酯、甲基丙烯酸縮水甘油基酯、衣康酸二縮水 本紙張尺度適用中國國家標準（cns ) A4規格（2ίοX297公釐） 2 3 3870 1 ----------¢- 一------訂------广 I (請先閱讀背面之注意事項再填寫本頁) Μ Β7 經濟、部中央標準局員工消費合作社印製 五、 發明説明（22 ) 1 1 甘 油 基 酯 Λ 丁 烯 基 三 羧 酸 -n 縮 水 甘 油 基 酿 對 -苯乙烯羧 1 I I 酸 縮 水 甘 油 基 酯 等 〇 1 1 f 不 飽 和 縮 水 甘 油 基 Μ 之 例 舉 有 乙 烯 基 縮 水 甘 油 基 m Λ fV 請 1 1 I 丙 烯 基 縮 水 甘 油 基 m 等 C 先 閱 讀 1 I 上 述 (甲基）丙 烯 酸 酯 ™乙稀- 不 飽 和 羧 酸 縮 水 甘 油 基 酷 背 面 之 1 及 / 或 不 飽 和 m 水 甘 油 基 酵 共 聚 合 物 橡 膠 之 製 m % 例 如 可 注 意 % 1 I 利 用 藉 白 由 基 引 發 劑 所 進 行 之 塊 狀 聚 合 反 應 、 乳 化 合 反 項 再 填 1 丄 應 、 或 溶 液 聚 合 反 應 等 般 方 法 而 逹 成 C 又 t 其 典 型 的 聚 % 本 頁 、 I 合 反 m 可 參 考 曰 本 待 公 昭 46 -45085號 公 報 特 開 昭 61 - 1 1 I 1 2 7 7 0 9號公 報 等 所 記 載 的 方 法 » 例 如 於 能 産 生 白 由 基 之 聚 1 1 I 合 反 應 引 發 劑 共 存 下 » 以 5 0 0k g/ cm 2以上鼷力， 40〜300 1 1 溫 度 條 件 下 裂 造 之 0 訂 1 上 述 (甲基）丙 烯 酸 酯 _乙烯- 不 飽 和 羧 酸 縮 水 甘 油 基 m 1 1 及 / 或 不 飽 和 縮 水 甘 油 基 醚 共 聚 合 物 橡 膠 之 構 成 分 比 率 1 1 I 以 (甲基）丙 烯 酸 酯 tJCf 単 位 在超過40重 量 % 未 滿97重 量 % 為 i 宜 ί 其 中 更 宜 在 45 70重 里 % 範 |sg> 圍 乙 烯 早 位 以 3 重 量 % 1 1 以 上 * 未 滿50重 量 % 為 宜 其 中 更 宜 在 1 0 49重 量 % 範 圍 1 1 t 不 飽 和 m 酸 縮 水 甘 油 基 酯 及 / 或 不 飽 和 縮 水 甘 油 基 m 單 1 1 位 以 〇. 1 - -30重量為宜， 最宜在0 .5 2 0重 量 % 範 圍 〇 1 l 上 述 (甲基）丙烯酸酯 含 量 低 於40重 量 % 時 » 橡 _ 彈 性 [ j 會 降 低 t 該 組 成 物 之 改 良 耐 衝 擊 性 效 果 變 小 又 (甲基）丙 1 I 烯 酸 酯 含 量 高於97重 量 % 時 該 共 聚 Π 物 橡 膠 之 脆 化 點 變 1 I 高 t 而 該 組 成 物 在 低 溫 下 之 機 械 性 質 曰 降 低 而 不 宜 0 1 1 I 又 9 不 飽 和 羧 酸 縮 水 甘 油 基 酯 及 / 或 不 飽 和 编.水 甘 油 1 1 2 4 本紙張尺度適用中國國家標準（CNS ) Α4規格（210X 297公釐） 3 8 7 0 1 A7 B7 經濟部中央標準局員工消費合作社印製 五、發明説明（23 ) 1 I 基 Agi m 含 量 未滿 0. 1重董％ ί時， 液晶聚酯樹脂組成物之耐衝 1 I 擊 性 會 下 降， 又含量 超 過30重 量 % 時 1 該 組 成 物 之 阐 性 可 1 1 I 能 會 降 低 而不 *銳。 f·~·V 讀 1 ! I 上 述 (甲基）丙烯 酸 酯 _乙稀- 不 飽 和 羧 酸 縮 水 甘 油 基 醋 閱 I 讀 背 1 I 及 / 或 不 飽和 縮水甘 油 基 m 共 聚 合 物 橡 駿 t 除 含 有 上 述 1 之 1 I (甲基）丙烯酸 酯、乙 烯 及 不 飽 和 羧 酸 總 水 甘 油 基 酯 不 飽 注 意 1 I 事 1 和 縮 水 甘 油基 醚外， 尚 可 含 有 其 他 可 共 聚 合 的 其 他 單 體 成 項 再 1 丄 分 0 上 述 單體 成分， 例 如 異 丁 烯 、 苯 乙 烯 及 其 衍 生 物 乙 爲 Λ'· 頁 1 酸 乙 烯 醱 、四 氟乙烯 及 氟 丙 烯 等 鹵 化 烯 烴 等 C 1 I 上 述 (甲基）丙烯 酸 酯 -乙烯- 不 飽 和 羧 酸 編 水 甘 油 基 酯 1 1 I 及 / 或 不 飽和 縮水甘 油 基 醚 共 聚 物 橡 顏 之 (乙）成 分 * 其 孟 1 1 訂 1 納 粘 度 (M ο ο n e y Vise 0 S it y )在 3〜70範圍， 以3 30者 為 較 宜 f 以 4〜25者為最宜。 上述孟納粘度偽依日本工業規格 1 [ J IS K6 30 0在100它下 使 用 大 轉 子 而 测 定 之 粘 度 值 〇 1 I 本 發 明之 (乙）成 分 亦 可 使 用 具 有 與 液 晶 聚 m 有 反 應 性 1 的 功 能 基 之丙 烯酸酯 条 橡 m 0 該 丙 烯 酸 酷 糸 橡 膠 乃 由 具 有 1 I 下 列 —- 般 式（3 1 1 1 H^C — CR1' 1 1 1 C = I 0 (3 ) ! I OR1 1 [ (上式内， R 1示硝數為] •-«w 1 8之 烷 基 或 氰 基 烷 基 1 R T ί 1 I 示 氫 原 子 或甲 基） 1 1 I 般 式 (4) r 1 1 本紙張尺度適用中國國家標辛（CNS ) Λ4規格（210Χ297公釐） 25 38 7 0 1 459037 A7 A7 B7 五、發明説明（24 ) H^C-CRl'--〇-At—〇—j— (d ') Printed by the Consumer Cooperative of the Central Bureau of Standards of the Ministry of Economic Affairs (in the above formula, Ar · indicates a divalent aryl group). The component (B) in the liquid crystal polyester resin composition of the present invention is a rubber having a functional group capable of reacting with the liquid crystal polyester of the component (A). The meaning of the above-mentioned rubbers is included in the polymer dictionary of new vendors (edited by the Japanese Polymer Society, published in 1988, issued by the Korean Society Bookstore), and all polymer compounds having rubber elasticity at room temperature are included. Examples include natural rubber, butadiene polymers, and diene-styrene copolymers [random copolymers, block copolymers (including SEBS rubber or SBS rubber, etc.), graft copolymers, etc. Or its compound, isoprene polymer, nitrided butadiene polymer, butadiene-acrylonitrile copolymer, isobutylene polymer, isobutylene-butadiene copolymer rubber, isobutylene-isoprene Diene copolymer, acrylate-ethylene strip copolymer rubber, ethylene-propylene copolymer rubber, ethylene-butene copolymer rubber, ethylene-propylene-styrene copolymer rubber, styrene-isoprene .. .. ..... 21 This paper size applies to China National Standard (CNS) A4 (210 X 297 mm) 3 870 1 ---- ^ ------ ^ ------ Order- ----- {1 (Please read the notes on the back before filling this page) r 459037 β7 V. Description of the invention (2G) olefin copolymer rubber, styrene-butene copolymer, styrene * ethylene-propylene Copolymer rubber, perfluoro rubber, fluorine-containing rubber, styrene-butadiene rubber, butyl rubber, silicone rubber, ethylene-propylene-non-co-diene copolymer rubber, Alcohol rubber, polysulfide rubber, polyurethane rubber, polyether rubber plaque (such as polypropane, etc.), gas propane rubber, polyester elastomer, polyamine elastomer, etc. Among them, fluorene acrylate-ethylene bar copolymer is more suitable, and the most preferred is (meth) acrylate-ethylene fluorene copolymer. The rubber compound can be produced by any method (such as emulsion polymerization method, solution polymerization method, etc.) or using any catalyst (such as peroxide, trialkyl aluminum, lithium halide, nickel bar catalyst, etc.). The above-mentioned functional groups that are reactive with liquid crystal poly. There are no other restrictions as long as they have anti-reactive properties with liquid crystal polyester. Specific examples include ring gas groups, oxazole groups, amine groups, etc. Air-based is more appropriate. Among functional groups having a ring gas group, a glycidyl group is most preferred. Among the monomers with glycidyl groups, unsaturated carboxylic acid glycidyl, unsaturated glycidyl ether, etc. are most commonly used. 0 Printed by the Consumer Cooperatives of the Central Standards Bureau of the Ministry of Economic Affairs (please read the precautions on the back before filling in this Page) There is no particular limitation on the method for introducing functional groups reactive with the liquid crystal polyester into the rubber jacket, and it can be performed according to a common method. For example, in the process of synthesizing rubber, it is also a feasible method to introduce a monomer having the functional group by copolymerization reaction. In addition, the degree of graft copolymerization should be used to introduce the monomer having the functional group into the rubber. China is also feasible. Preferred examples of the (B) component rubber of the functional group reactive with liquid crystal polyester of the present invention include (meth) acrylate-ethylene-unsaturated carboxylic acid glycidyl ester and / or unsaturated glycidyl ester. Glyceryl ethylene tunnel copolymer rubber paper size applicable to China National Standard (CNS) A4 specification (210X297 mm) 22 38 7 0 1 Printed by the Consumer Cooperatives of the Central Standards Bureau of the Ministry of Economic Affairs 4 h Q Ο ^ 7 ~ wx '* ·. '. T. A 7 B7 V. Description of the invention (2)) The (meth) acrylic acid ester, which is the main constituent of the above-mentioned copolymer oak, is a cool type derived from acrylic acid or methacrylic acid and yeast. The alcohol is preferably an alcohol having a large number of eight to eight. Specific examples of the (meth) acrylate include methyl acrylate, methyl methacrylate, n-butyl acrylate, n-butyl methacrylate, third butyl acrylate, third butyl methacrylate, and acrylic acid 2 -Ethylhexyl ester, 2-ethylhexyl methacrylate, etc. c. The (meth) acrylic esters can be used alone or in combination of two or more kinds. The compounds that impart unsaturated glycidyl carboxylic acid units and unsaturated glycidyl ether units are represented by the following general formulae (1) and (2), respectively, R—C—0—CH, —CH—CH7… 11 \ ~ ⑴ 0 〇 (In the above formula, R represents a hydrocarbon group having 2 to 13 carbon atoms having unsaturated bonds in the vinyl. ≫ R—X—CH】 —CH—CH2 {ί \ \ / ㈡ (inside the above formula R represents a hydrocarbon group having 2 to 18 nitrates having an ethylenically unsaturated bond. Z is -CH2-0-or-Specifically, glycidyl acrylate is exemplified by glycidyl acrylate , Glycidyl methacrylate, dicondensation of itaconic acid This paper applies the Chinese national standard (cns) A4 specification (2ίοX297 mm) 2 3 3870 1 ---------- ¢-1- ---- Order ------ Guang I (please read the notes on the back before filling this page) Μ Β7 Printed by the Consumer Cooperatives of the Central Standards Bureau of the Ministry of Economic Affairs and Ministry of Finance 5. Description of the invention (22) 1 1 Glyceryl Ester Λ butenyl tricarboxylic acid-n glycidyl p-styrenecarboxylic acid 1 II glycidyl ester etc. 1 1 f Unsaturated glycidyl group M is exemplified by vinyl glycidyl group m Λ fV Please 1 1 I Propylene glycidyl group m, etc. C Read 1 I The above (meth) acrylate ™ ethylene-unsaturated Carboxylic acid glycidyl 1 and / or unsaturated m water glycerol-based fermentation copolymer rubber m% For example, you can pay attention to% 1 I use block polymerization reaction and emulsification by using a radical initiator Fill in the reverse term with 1 reaction method, or solution polymerization reaction to form C and t. Its typical poly%. This page, I, and m can be referred to Japanese Patent Publication No. 46-45085 JP 61- 1 Methods described in 1 I 1 2 7 7 0 9 and the like »For example, in the presence of a 1 1 I complex reaction initiator capable of producing white benzyl group» With a force of 50 kg / cm 2 or more, 40 to 300 1 1 Cracking under temperature 0 Order 1 The above (meth) acrylate _Ethylene-unsaturated carboxylic acid glycidyl m 1 1 and / or the composition ratio of unsaturated glycidyl ether copolymer rubber 1 1 I The (meth) acrylate tJCf is more than 40% by weight and less than 97 % By weight should be i, which is more suitable at 45 to 70% by weight. Fan | sg > The early position of the surrounding ethylene is 3% by weight 1 1 or more * Less than 50% by weight is more suitable, which is more preferably in the range of 1 0 49% by weight 1 1 t The unsaturated m acid glycidyl ester and / or the unsaturated glycidyl m single 11 position is preferably from 0.1 to -30 weight, and most preferably in the range of 0.5 2 0 wt%. The above (methyl ） When the content of acrylate is less than 40% by weight »Rubber _ Elasticity [j will reduce t The effect of improving the impact resistance of the composition will be small, and when the content of (meth) prop 1 I acrylate is more than 97% by weight, the copolymerization Π The brittleness point of the rubber becomes 1 I high t, and the mechanical properties of the composition at low temperature are reduced and it is not suitable 0 1 1 I 9 Glycidyl ester of unsaturated carboxylic acid and / or unsaturated. Glycerin 1 1 2 4 This paper size is applicable to Chinese National Standard (CNS) A4 specification (210X 297 mm) 3 8 7 0 1 A7 B7 Ministry of Economic Affairs Printed by the Consumer Standards Cooperative of the Central Bureau of Standards 5. Description of the invention (23) When the content of 1 I-based Agi m is less than 0.1% by weight, the impact resistance of the liquid crystal polyester resin composition will decrease, and the content When it exceeds 30% by weight, 1 the composition may be declarative, and 1 I may be reduced without being sharp. f · ~ · V Read 1! I The above (meth) acrylates_ethene-unsaturated carboxylic acid glycidyl vinegar. I read back 1 I and / or unsaturated glycidyl m copolymers. Contains 1 of 1 I (meth) acrylate, ethylene and unsaturated carboxylic acid total water glyceryl esters. Note 1 I matter 1 and glycidyl ether, but may also contain other copolymerizable other monomers. Item 1 1 0 0 The above monomer components, such as isobutylene, styrene, and its derivatives B are Λ '· Page 1 Halogenated olefins such as ethylene fluorene, tetrafluoroethylene, and fluoropropylene, etc. C 1 I The (meth) acrylic acid Ester-Ethylene-Unsaturated Carboxylic Acid Glycidyl Ester 1 1 I and / or Unsaturated Glycidyl Ether Copolymer (B) Ingredients * Its Meng 1 1 Order 1 Nano Viscosity (M ο ο ney Vise 0 S it y) In the range of 3 to 70, 3 to 30 is more suitable. F 4 to 25 is most suitable. The above Menner viscosity is in accordance with Japanese Industrial Standards 1 [J IS K6 30 0 Viscosity value measured using a large rotor at 100%. 1 I The (B) component of the present invention can also be used. Functional base of acrylate strip rubber m 0 This acrylic rubber is made of 1 I with the following—-general formula (3 1 1 1 H ^ C — CR1 '1 1 1 C = I 0 (3)! I OR1 1 [(In the above formula, R 1 shows the nitrate number is]]-«w 1 8 alkyl or cyanoalkyl 1 RT ί 1 I shows a hydrogen atom or a methyl group) 1 1 I General formula (4) r 1 1 This paper size is applicable to Chinese National Standard Xin (CNS) Λ4 specification (210 × 297 mm) 25 38 7 0 1 459037 A7 A7 B7 V. Description of the invention (24) H ^ C-CRl '

I C = 0 (4)I C = 0 (4)

I 〇—R2 -〇—R3 (上式内，R2示磺數為1〜12之伸烷基，R3示磺數為 1〜1 2之烷基） 及一般式（5 > R4I 〇—R2 -〇-R3 (In the above formula, R2 shows an alkylene group having a sulfonic number of 1 to 12, R3 shows an alkyl group having a sulfonic number of 1 to 12) and the general formula (5 > R4

H^C ~ C t 厂、 C 二0 (” 0—^Rj-C — o 1 (上式内，R4示氫原子或甲基，R5示硝數為3〜3〇之伸 烷基，R6示碩數為1〜20之烷基或其衍生物，n為1〜20之 整數）所示的群體1出的至少一種單體為主成分者。 經濟部中央標準局員工消費合作社印製 (請先閱讀背面之注意事項再填寫本瓦) 輿液晶聚酯有反應性的功能基之種類，例如環氣基、 噁唑基、胺基等可供使用，其中以環氣基為宜。具有.環氣 基之功能基之例舉以縮水甘油基為較佳。含有编水甘油基 之單體，以使用不飽和羧酸縮水甘油基酯.、不飽和縮水甘 油基醚等為較宜。 上述以一般式（3)所示的丙烯酸烷基酯之具體化合物， 可列舉計有：丙烯酸甲酯、丙烯酸乙酯、丙烯酸丙酯、丙 烯酸丁酯、丙烯酸戊酯、丙烯酸己酯、丙烯酸辛酯、丙烯 酸2 -乙基己酯、丙烯酸壬酯、丙烯酸癸酿、丙烯酸十二烷 本紙張尺度適用中國國家標準（CNS ) Α4規格（21〇X297公釐） 26 3 8 7 0 1 Β7 經濟部中央標率局貝工消費合作社印製H ^ C ~ C t factory, C 2 0 ("0— ^ Rj-C — o 1 (In the above formula, R4 represents a hydrogen atom or a methyl group, R5 represents an alkylene group having a nitrate number of 3 to 30, and R6 The number of alkyl groups or their derivatives is 1 to 20, and n is an integer of 1 to 20). At least one monomer from group 1 is the main component. Printed by the Consumer Cooperative of the Central Standards Bureau of the Ministry of Economic Affairs ( Please read the precautions on the back before filling in this tile.) The types of reactive functional groups of liquid crystal polyesters, such as ring gas groups, oxazolyl groups, amine groups, etc. are available. Among them, ring gas groups are preferred. Glycidyl is preferred as the functional group of the ring gas group. For monomers containing glycidyl, unsaturated glycidyl ester of unsaturated carboxylic acid, unsaturated glycidyl ether, etc. are more suitable. Specific examples of the specific compound of the alkyl acrylate represented by the general formula (3) include methyl acrylate, ethyl acrylate, propyl acrylate, butyl acrylate, pentyl acrylate, hexyl acrylate, and octyl acrylate. , 2-ethylhexyl acrylate, nonyl acrylate, acrylic decanol, dodecyl acrylate Chinese National Standard (CNS) Α4 Specification (21〇X297 mm) 26 3 8 7 0 1 Β7 Ministry of Economic Affairs Bureau of the Central standard rate HIGHLAND consumer cooperatives printed

五、 發明説明（2 5 ) 1 I m 、 丙 烯 酸 氰 基 乙 m Λ/ί- 寺 0 1 1 I 又 ， 上 述 一 般 式 (4)所示的丙烯酸烷氣基烷基酯之具 1 1 體 化 合 物 > 可 列 舉 計 有 • » 例 如 丙 烯 酸 甲 氣 基 乙 酯 丙 m 酸 1 1 請 1 1 乙 氣 基 乙 酯 丙 烯 酸 丁 氧 基 乙 m Λ 丙 烯 酸 乙 氣 基 两 酯 等 0 先 閱 | 1 1 可 使 用 上 述 化 合 物 之 1 種 或 2 種 以 上 作 該 丙 烯 酸 酯 % 類 背 面 t 之 1 橡 _ 之 主 要 成 分 C 意 1 事 1 本 發 明 之 (乙） 成 分 之 丙 烯 酸 酯 系 橡 m 之 構 成 成 分 * 必 項 再 填 1 1 要 時 可 使 用 —1 種 不 飽 和 titr 早 m 而 該 αα 単 體 像 可 樹 由 上 逑 一 般 Μ 本 — 頁 1 式 (3 )〜（5 )所示 的 化 合 物 中 選 出 的 至 少 —· 種 nts 體 能 行 共 聚 、· 1 合 反 應 者 為 限 C 1 1 上 述 不 飽 和 US' 军 腰 之 例 舉 有 苯 乙 烯 、 α -甲基苯乙烯、 1 1 丙 烯 腈 鹵 化 苯 乙 烯 甲 基 丙 烯 腈 丙 烯 醯 胺 甲 基 丙 烯 訂 1 酷 胺 乙 烯 基 絜 N - m 甲 基 丙 烯 Μ 胺 Ί 乙 酸 乙 晞 酯 氣 化 1 | 乙 烯 偏 二 氱 乙 烯 丙 烯 酸 苯 甲 酯 甲 基 丙 烯 酸 、 衣 康 酸 1 I 富 馬 酸 馬 來 酸 等 0 1 1 本 發 明 中 所 使 用 丙 烯 酸 m 糸 橡 m I 其 孟 納 拈 度 在 1 3〜70範圍者為佳， 以4 60範圍者 為 更 佳 〇 1 I 本 發 明 之 (乙）成 分 t 尚 可 採 rrt 1 Τ,,Ι ΓΡ 含 有 環 氣 基 之 乙 烯 % 芳 1 I 族 烴 化 合 物 -共鈪二烯烀嵌段共聚物棟圃。 上述嵌段共聚 i I 合 物 乃 % 由 (a )以乙烯条芳族烴化合物為主體之鍵區及（b) 1 I 共 扼 二 烯 烴 化 合 物 為 主 體 之 鐽 區 而 成 的 嵌 段 共 聚 物 再 行 環 1 1 I 氣 化 處 理 而 得 的 橡 賺 t 或 將 上 述 嵌 段 it .f % 聚 物 之 加 氫 化 合 物 1 1 I 施 以 環 氧 化 處 理 而 得 的 橡 駿 0 1 上 述 乙 烯 % 芳 族 烴 化 合 物 -共軛二烯烴化合物嵌段共 t I 本紙張尺度適用中國國家標率（CNS ) Λ4规格（210 X 297公釐） 2 γ 38701 A7 B7 經濟部中央標準局員工消費合作杜印製 五、 發明説明（26 ) 1 I 聚 物 或 其 加 氫 化 合 m 可 按 照 例 如 曰 本 持 公 昭 40 -23798號 1 I 公 報 9 恃 開 昭 59 -133 203號公報等所記載的已知方法而製 1 1 诰 之 〇 >K 1 I 請 1 I 上 述 芳 族 烴 化 合 物 之 具 體 例 舉 有 苯 乙 烯 乙 烯 基 甲 苯 先 閱 1 讀 1 % 二 乙 烯 基 苯 a -甲基苯乙烯、 對- 甲 基 苯 乙 烯 乙 烯 基 背 & 1 之 1 禁 等 0 其 中 以 採 用 苯 乙 烯 為 較 宜 0 注 意 1 I 事 1 上 述 共 軛 二 烯 烴 化 合 物 之 具 歴 例 舉 有 丁 二 烯 異 戊 項 -S- 1 導 烯 間 戊 二 烯 1 , 3 - 戊 二 烯 、 3 - 丁 基 -1 ，3 -辛二烯等。 其 寫 頁 1 中 以 採 用 丁 二 烯 及 異 戊 烯 為 較 宜 C 1 I 本 發 明 之 (乙） 成 分 橡 m * 以 其 結 晶 熔 解 熱 量 在 3 J/g 以 1 1 下 者 為 宜 C 另 外 4 該 (乙）成 分 之 橡 膠 在 必 要 時 可 行 硫 化 處 1 1 理 而 可 用 作 硫 化 橡 m 0 上 述 硫 化 處 理 可 利 用 多 功 能 性 有 機 訂 1 酸 多 功 能 性 胺 化 物 眯 唑 化 合 物 等 而 達 成 製 造 的 > 但 1 1 不 限 定 在 上 述 方 法 0 1 I 本 發 明 中 » 較 佳 的 液 晶 聚 酷 樹 脂 Μ 成 物 乃 僳 由 (甲） 成 1 1 成 分 之 連 鑲 相 的 液 晶 聚 m 和 (乙）成 分 之 分 散 相 的 橡 膠 而 成 » 1 I 可 提 供 具 備 優 異 的 阻 氣 性 耐 熱 性 及 機 械 強 度 之 液 晶 聚 酯 1 I 樹 脂 組 成 物 〇 I 1 本 發 明 所 使 用 的 液 晶 聚 酯 樹 脂 組 成 分 中 t (甲）成 分 及 1 1 (乙J成 分 之 tb 率 S 以 (甲）成 分 在 56 .0 99 .9重 量 % 範 圍 ， 1 1 其 中 以 65 ,0 99 .9重 量 % 為 較 宜 1 以 在 70 9 8重 量 % 範 圍 1 1 為 最 宜 j (乙）成 分 在 44 .0 0 . 1重垦％範圍， 其中以 1 | 35 .0 ^*w 0 . 1重量％為較宜， 以在30〜2重 量 % 範 圍 為 £3 取 宜 〇 1 1 I 田 ί甲）成 分 未 渴56 . 0重 量 % 時 9 該 組 成 物 之 耐 熱 性 曰 1 1 本紙張尺度適用中國國家標準（CNS ) Λ4規格（210 X 297公釐） 28 3 8 7 0 1 A7 B7 經濟部中央標準局員工消費合作社印製 五、 發明説明（2 7 ) 1 I 下 降 而 不 宜 1> 又 t (甲） 成 分 超 過 9 9 .9 重 量 % 時 * 該 組 成 物 ! | 之 成 膜 性 之 改 良 效 果 不 足 9 價 格 亦 較 昂 貴 而 不 宜 1 1 本 發 明 中 * 製 造 液 晶 聚 酯 樹 脂 組 成 物 之 方 法 並 無 特 別 fV 1 I 請 1 I 限 制 可 藉 周 知 方 法 進 行 〇 例 如 在 溶 液 狀 態 下 混 合 各 成 分 先 閱 I 讀 1 I 後 * 籍 蒸 發 去 除 溶 劑 t 或 在 溶 劑 中 使 之 沈 澱 而 製 成 0 由 工 背 1 之 1 I 業 生 産 觀 點 而 言 ί 以 熔 融 狀 態 下 將 各 成 分 加 以 混 練 之 方 法 注 意 1 1 ψ 1 為 較 宜 0 熔 融 m 練 時 可 採 用 —l 般 使 用 之 οσ 単 軸 或 雙 軸 擠 壓 機 項 再 1 d t 各 種 揑 合 機 等 混 練 裝 置 C 其 中 以 雙 軸 高 效 混 練 機 為 較 宜 馬 4- 今、 〇 頁 1 1 熔 融 混 練 時 * 混 練 裝 備 之 擠 筒 設 定 溫 度 以 200〜360 V. 1 1 範 圍 為 宜 * 其 中 以 230〜350 X： 範 圍 為 較 宜 1 1 m 練 之 際 9 各 成 分 可 先 用 滾 桶 式 拌 合 墟 m 或 韓 蘇 Μ 合 機 訂 1 (H e η Π S c h e 1 IB i X er)等設備加以混合均勻， 但必要時亦可 1 I 省 略 上 述 混 合 步 驟 1 直 接 分 別 定 量 供 料 至 混 練 裝 置 中 處 理 1 1 1 C 本 發 明 所 使 用 的 液 晶 聚 酯 樹 脂 組 成 物 中 1 必 要 時 尚 可 1 / 1 | 添 加 無 機 媾 充 劑 該 無 機 镇 充 劑 之 具 體 例 舉 有 磺 酸 Β 滑 I i 石 粘 土 氣 化 矽 硝 酸 m 硫 酸 、 二 ^ΙίΠι/ 氧 化 鈦 > 氧 化 鋁 1 1 石 ySr. W 玻 璃 鱗 片 玻 璃 纖 維 碳 m 雒 氣 化 鉛 m 維 ·» 氣 1 1 化 矽 氧 化 鋁 纖 維 % 棚 酸 氧 化 鋁 晶 鬚 、 钛 酸 押 m 維 等 r, 1 I 本 發 明 所 使 用 的 液 晶 聚 m 樹 脂 組 成 物 中 » 必 要 時 尚 可 1 I 添 加 有 機 填 充 劑 ，、 抗 氣 化 劑 熱 安 定 劑 光 安 定 劑 *1 耐 燃 1 t I 劑 、 滑 劑 Λ 抗 靜 電 劑 無 機 或 有 機 % 色 料 防 m 劑 \ 交 聯 1 1 I 剤 發 泡 m 's 螢 光 剤 > 表 而 平 滑 劑 1 表 面 光 澤 改 良 劑 含 1 1 本紙張尺度適用中國國家標準（CNS ) A4規格（210X297公釐） 29 38 7 0 1 459037 A7 B7 經濟部中央標_局員工消費合作社印製 五、 發明説明 ) 1 | 氟 樹 脂 等 脫 模 改 良 劑 等 0 該 添 加 劑 可 在 製 造 過 程 中 或 製 造 1 1 後 之 加 工 過 程 中 添 加 使 用 C 1 1 m 練 後 之 該 樹 脂 組 成 分 可 利 用 射 出 成 形 法 > 擠 Μ 成 形 y·~·s 1 1 請 1 j 法 或 其 他 各 種 成 形 法 成 形 之 〇 % 外 f 亦 可 以 不 經 過 混 練 過 先 鬩 1 讀 1 1 程 * 而 在 射 出 成 形 或 擠 壓 成 形 時 予 以 乾 摻 合 » 在 熔 融 加 I 背 1 之 1 操 作 中 進 行 1 練 成 為 本 發 明 樹 脂 組 成 物 i 亦 可 直 接 製 得 成 注 意 1 I 形 加 X 品 事 項 再 J 上 述 樹 脂 組 成 物 之 成 膜 方 法 » 一 般 利 用 擠 壓 機 將 上 述 寫 未 w- 頁 1 方 法 製 得 的 液 晶 聚 醋 樹 脂 組 成 物 加 以 熔 融 混 練 後 S ΐ» 由 經 •s， 1 由 模 頭 擠 壓 的 熔 融 樹 脂 抽 拉 成 液 晶 聚 m 樹 脂 組 成 物 薄 膜 1 1 另 外 t 亦 可 不 經 過 預 先 混 練 過 程 > 成 形 時 將 各 成 分 予 以 乾 1 1 擦 合 1 妖 /»»> 後 在 熔 融 加 X 操 作 中 混 練 成 樹 m 組 成 物 t 亦 可 直 訂 1 接 製 得 成 形 加 X 品 C 楔 頭 般 使 用 T 模 或 琛 狀 縫 型 模 頭 C 1 | 使 用 T 楔 成 形 薄 膜 時 t 經 擠 壓 機 熔 融 m 練 過 的 液 晶 聚 1 1 | 酯 樹 脂 組 成 物 1 通 常 經 過 朝 向 下 方 之 T 模 而 成 為 薄 層 狀 的 1 1 熔 融 物 t 然 後 經 加 壓 滾 筒 依 順 向 取 向 拉 伸 棍 牽 引 η 1 上 述 成 膜 時 ， 擠 壓 機 之 設 定 條 件 視 組 成 物 之 組 成 分 而 1 1 選 T3K 俾 適 宜 條 件 1 一 般 擠 壓 機 之 擠 同 設 定 溫 度 在 200〜360 1 範 圍 為 宜 » 其 中 以 23〇~ 350 V. 範 圍 為 較 宜 0 超 出 上 述 溫 度 1 I 範 圍 時 t 組 成 物 或 發 生 熱 分 解 或 不 易 成 膜 而 不 宜 0 1 I T 模 (2 )之縫隙間距在c .2 2 . 0 d m範圍， 其中以C .2 1 1 I 1 2n π ) 鲁較宜； 本發明之液晶聚酯樹酯組成物薄膜之膜厚 1 1 I 可 控 制 在 1 - -1 000 W Π a範 圍 t __. 般 實 用 上 常 用 之 膜 厚 在 5 - •>w 1 1 100 u n 1範 圍 者 〇 本 發 明 之 液 晶 聚 酯 樹 脂 組 成 物 薄 膜 之 拉 伸 1 1 本紙張尺度適用中國國家標準（cns ) A4規格（2iox297公釐） 3 8 7 0 1V. Description of the invention (2 5) 1 I m, cyanoacrylic acid m Λ / ί- temple 0 1 1 I, and a 1 1-body compound of an alkane alkyl alkyl acrylate represented by the general formula (4) above > Examples include • »For example, methyl ethyl acrylate, acrylic acid, m 1 1 Please 1 1 ethyl ethyl acrylate, butoxyethyl acrylate m Λ ethyl ethyl acrylate, etc. 0 Read First | 1 1 Available One or two or more of the above-mentioned compounds are used as the acrylate%. The main component of the rubber _ is the main ingredient C. Matter 1 The acrylate of the present invention (B) is the constituent component of the rubber m. Mandatory field 1 1 May be used when needed—1 unsaturated titr early m, and the αα carcass image can be selected from the above general M. — Page 1 Compounds shown by formulas (3) to (5) At least --- nts physical copolymerization, 1-reaction is limited to C 1 1 The above unsaturated US 'military waist is exemplified by styrene, α-methylstyrene, 1 1 acrylonitrile halogenated styrene methyl Acrylonitrile acrylamine methacrylamide 1 coolamine vinyl amine N-m methacrylic acid amine amine acetic acid ethyl acetate gasification 1 | ethylene vinylidene vinyl acrylate methacrylic acid methacrylic acid, itaconic acid 1 I Fumaric acid, maleic acid, etc. 0 1 1 Acrylic acid m 糸 oak m I used in the present invention is preferably in the range of 1 to 70, and more preferably in the range of 4 to 60. 1 I (B) Component t can still be used. Rrt 1 T ,, 1 ΓP ethylene containing cyclic gas group% aromatic 1 Group I hydrocarbon compound-co-diene fluorene block copolymer building block. The above block copolymer i I compound is a block copolymer composed of (a) a bond region mainly composed of an ethylene aromatic hydrocarbon compound and (b) a 1 I conjugated diene compound as a main region. Line 1 1 I rubber obtained by gasification treatment or oak block obtained by subjecting the above block it .f% polymer hydrogenation compound 1 1 I to epoxidation treatment 0 1 above ethylene% aromatic hydrocarbon Compound-conjugated diene compound block co-t I This paper size applies to China's National Standard (CNS) Λ4 specification (210 X 297 mm) 2 γ 38701 A7 B7 Employees' cooperation of the Central Standards Bureau of the Ministry of Economic Affairs DESCRIPTION OF THE INVENTION (26) 1 I polymer or hydrogenated m thereof can be prepared according to a known method described in, for example, Japanese Patent Publication No. 40-23798 No. 1 I Bulletin 9 Japanese Patent Application No. 59-133 No. 203诰 之 〇 > K 1 I Please 1 I Specific examples of the above aromatic hydrocarbon compounds are phenethyl Vinyl toluene first read 1 Read 1% divinylbenzene a-methylstyrene, p-methylstyrene vinyl back & 1 of 1 forbidden 0 Among them, styrene is preferred 0 Note 1 I matter 1 Examples of the above-mentioned conjugated diene compounds include butadiene isoprene-S-1, leadene, diprene 1, 3-pentadiene, 3-butyl-1, 3-octadiene, etc. . In the first page, butadiene and isopentene are preferred. C 1 I The (B) component of the present invention, m *, is based on the heat of crystal melting at 3 J / g, and the lower 1 1 is preferred. C 4 The rubber of the (B) component can be vulcanized if necessary. 1 1 It can be used as a vulcanized rubber m 0 The above vulcanization treatment can be made using a multifunctional organic resin, an acid multifunctional amidated oxazole compound, etc. & gt However, 1 1 is not limited to the above method 0 1 I In the present invention »A preferred liquid crystal polymer M product is a liquid crystal polymer m composed of (a) to 1 1 components and (b) component Made of rubber with dispersed phase »1 I Liquid crystal polyester 1 I Resin composition having excellent gas barrier heat resistance and mechanical strength 〇 1 1 Liquid crystal polyester used in the present invention The t (A) component and 1 1 (the tb ratio S of the B component is in the range of 56.99.99% by weight of the (A) component, and 1 1 is 65,09.9% by weight. Optimum 1 is in the range of 70 9 8 wt% 1 1 is the most suitable j (B) component is in the range of 44.0 0. 1 reclamation%, of which 1 | 35.0 ^ * w 0.1 is the most suitable In the range of 30 ~ 2% by weight, it is appropriate to be £ 3. The composition is not thirsty. 56.0% by weight. 9 The heat resistance of the composition is 1 1 This paper applies the Chinese national standard (CNS) ) Λ4 specification (210 X 297 mm) 28 3 8 7 0 1 A7 B7 Printed by the Consumer Cooperatives of the Central Standards Bureau of the Ministry of Economic Affairs 5. Description of the invention (2 7) 1 I is not suitable for a drop 1 > Also t (A) The component exceeds 9 9 .9% by weight * The composition! | The improvement of film-forming properties is less than 9 The price is also more expensive and not suitable 1 1 In the present invention * There is no special fV 1 I method for manufacturing the liquid crystal polyester resin composition Please limit the 1 I by well-known methods. For example, mixing the ingredients in a solution state, read I first, read 1 I, and then * make it by evaporation to remove the solvent t or make it precipitate in the solvent. From the production point of view, the method of mixing the ingredients in the molten state is noted. 1 1 ψ 1 is more suitable. 0 Melting m can be used during training. － Σ is generally used for 単 或 or biaxial extruder, and 1 dt. Kneading equipment C and other kneading equipment C Among them, a two-shaft high-efficiency kneading machine is more suitable. 4-Today, 〇 Page 1 1 During melt kneading * The extruder setting temperature of the kneading equipment is 200 ~ 360 V. 1 1 The range is appropriate * Among which 230 ~ 350 X: The range is more suitable for 1 1 m. On the occasion of training, 9 ingredients can be mixed with drum type or Han Su M first. (H e η Π S che 1 IB i X er) and other equipment to mix evenly, but if necessary, 1 I can omit the above mixing step 1 and directly feed the materials to the kneading device separately for processing 1 1 1 C Liquid crystal polyester resin composition 1 Necessary fashion 1/1 | Addition of inorganic rhenium filler Specific examples of this inorganic ballast include sulfonic acid B slip I i stone clay gasification silicon nitric acid m sulfuric acid, two ^ ΙίΠι / oxidation Titanium> alumina 1 1 stone ySr. W glass flakes glass fiber carbon m 雒 gaseous lead m dimension · »gas 1 1 siliconized alumina fiber% shed acid alumina whiskers, titanic acid m dimension etc. r, 1 I In the liquid crystal polym resin composition used in the present invention »If necessary, I can add 1 organic filler, anti-gasification agent, thermal stabilizer, light stabilizer * 1 flame retardant 1 t I agent, lubricant Λ antistatic agent inorganic Or organic% colorant anti-m agent \ cross-linking 1 1 I 剤 foam m 's Bright &smooth; Table and smoothing agent 1 Surface gloss improver containing 1 1 This paper size applies Chinese National Standard (CNS) A4 specifications (210X297 mm) 29 38 7 0 1 459037 A7 B7 Central Standard of the Ministry of Economic Affairs_Staff Consumer Cooperatives Printing 5 、 Description of the invention) 1 | Fluorine resin and other mold release improvers, etc. 0 This additive can be added during the manufacturing process or after the processing of 1 1 using C 1 1 m. The resin composition can be used for injection. Molding method> Extrusion M molding y · ~ · s 1 1 Please use 0% of the 1 j method or other various molding methods. The outer f can also be used without injection molding. Dry blending during molding »Perform 1 in the operation of melting and adding I back 1 to 1 to form the resin composition i of the present invention. It can also be prepared directly. Xiang Zai J The film forming method of the above resin composition »Generally, the liquid crystal polyacetate resin composition prepared by the above method is melt-kneaded with an extruder S ΐ» by warp · s, 1 by a mold The molten resin squeezed by the head is drawn into a liquid crystal polym resin composition film 1 1 In addition, t can also be dried without undergoing the pre-kneading process > during the molding, the ingredients are dried 1 1 rubbing 1 demon / »» > In the X operation, it is mixed into a tree m. The composition t can also be ordered directly. It can be formed by adding X product C. Wedges use T-die or chen seam-shaped die C 1 | When using T-wedge to form film, t is melted by the extruder. m The trained liquid crystal poly 1 1 | ester resin composition 1 usually passes through a T-die facing downward to become a thin layer of 1 1 melt t and then is pulled by a pressure roller in a forward-oriented stretching rod to pull η 1 The above film formation Extruder The setting conditions depend on the composition of the composition. 1 1 Choose T3K. 俾 Suitable conditions 1 The extrusion temperature of the general extruder is set to 200 ~ 360 1. The range is suitable »Among them, 23 ～ 350 V. The range is more suitable. 0 Exceeding When the temperature is in the range of 1 I, the composition of t may be thermally decomposed or difficult to form a film, which is not suitable for the gap interval of 0 1 IT mode (2) in the range of c .2 2. 0 dm, where C .2 1 1 I 1 2n π ) Lu is more suitable; the film thickness of the liquid crystal polyester resin composition film of the present invention is 1 1 I can be controlled in the range of 1--1 000 W Π a. w 1 1 100 un 1 In the range of the stretching of the liquid crystal polyester resin composition film of the present invention 1 1 This paper size is applicable to China National Standard (cns) A4 specification (2iox297 mm) 3 8 7 0 1

ή R Α7 Β7 經濟部中央標準局員工消費合作社印製 五、發明説明（2 9 ) 1 I tb 率 (0 r a ft r θ t 1 0 )在 1 1 "W 40 .0 範 圍 〇 1 1 另 外 > 也 可 以 製 得 由 T 模 擠 壓 該 樹 脂 m 成 物 之 雙 軸 拉 1 1 伸 薄 膜 0 1 I 請 1 1 本 發 明 中 製 造 液 晶 聚 酷 樹 脂 組 成 物 薄 勝 時 » 所 採 用 雙 先 閱 I 讀 1 I 軸 拉 伸 方 法 並 無 特 别 限 制 具 體 言 之 » 將 Ηί 出 擠 ary Μ 機 之 T 模 背 \6 1 之 1 擠 壓 出 的 本 發 明 組 成 物 之 熔 融 物 先 按 縱 向 (Μ a c hi n e 注 意 古 1 I d i re C t 1 0 η , 簡稱為Μ 1)) 進 行 ntt 單 軸 拉 伸 9 後 按 播 向 Ψ 項 再 ά 1 (Τ r a n s re s e d i r e c U ο η t 簡 稱 T D )逐次拉伸之方法， 或由 寫 木 -V、 頁 1 τ 楔 擠 壓 出 的 薄 片 同 時 於 MD ί TD方 向 拉 伸 之 方 法 3 尚有 1 由 T 模 擠 壓 出 的 未 經 拉 伸 板 Η 利 用 雙 軸 拉 伸 機 拉 幅 機 寺 1 i 逐 次 或 同 時 拉 伸 等 之 雙 軸 拉 伸 的 方 法 均 可 採 用 C 1 1 無 m 利 用 上 述 任 何 方 法 成 膜 溫 度 以 本 發 明 液 晶 聚 酯 訂 1 樹 脂 組 成 物 之 開 始 流 動 溫 度 η 去 6 0 f 以 上 至 開 始 流 動 漶 度 1 1 加 上 60 t： 以 τ 之 溫 度 範 圍 為 宜 其 中 以 開 始 流 動 溫 度 以 上 1 I 至 開 始 流 動 溫 度 加 3 0 以 下 溫 度 範 圍 内 進 行 成 m 加 工 為 取 1 1 佳 〇 1 又 T 模 之 縫 隙 間 距 以 0 . 2 " -1 .2 HI 範 圔 為 較 宜 〇 拉 伸 1 1 倍 率 視 成 形 方 法 而 決 定 其 適 當 值 C 例 如 利 用 雙 軸 拉 伸 機 拉 1 1 伸 時 1 拉 伸 倍 率 (拉伸後長度/原來長度） 而 言 * 縱 向 拉 伸 1 1 方 -向 及 横 向 拉 伸 方 向 之 拉 伸 倍 率 採 用 1 . 2〜2 0 . 〇範圍， 其 ! 1 中 以 使 用 1 . 5， - 5 . 0範 圍 為 較 宜 拉 伸 倍 率 小 於 1 . 2時. 抗 I I 抗 物 性 有 下 降 之 慮 而 若 大 於 2C • C 時 3 薄 膜 平 滑 性 卽 不 充 1 1 I 分 〇 1 1 | 使 用 璟 狀 缝 隙 之 m 頭 的 吹 腊 OR 成 形 薄 膜 時 t 所 得 的 液 晶 1 i 本紙張尺度適用中國國家標隼（CNS ) A4規格（2]OX 297公釐） 3 1 3 8 7 0 1ή R Α7 Β7 Printed by the Consumer Cooperatives of the Central Standards Bureau of the Ministry of Economic Affairs 5. Description of the invention (2 9) 1 I tb rate (0 ra ft r θ t 1 0) is in the range 1 1 " W 40.0 range 0 1 1 In addition > Biaxial pulling of the resin m product by a T die 1 1 stretch film 0 1 I Please 1 1 When the liquid crystal polymer resin composition of the present invention is thin and thin »Double read I used Read 1 There is no particular limitation on the I-axis stretching method. Specifically »Extrude the T die back of the Μ machine. 6 1 -1 Extrude the melt of the composition of the present invention first in the longitudinal direction (Μ ac hi ne Note that ancient 1 I di re C t 1 0 η, abbreviated as M 1)) After performing the ntt uniaxial stretching 9 and pressing the broadcast direction 再 item 1 (Τ rans re sedirec U ο η t abbreviated as TD) successively stretching Method, or wedge squeeze by writing wood-V, page 1 τ Method for simultaneously extruding the extruded sheet in the MD TD direction 3 There is still 1 unstretched sheet extruded by T die The biaxial stretching method can use C 1 1 without m. Using any of the above methods, the film-forming temperature of the liquid crystal polyester of the present invention can be set to 1. The starting flow temperature η of the resin composition is 6 0 f or more to the beginning of the flow rate 1 1 plus Upper 60 t: It is appropriate to use a temperature range of τ, in which the temperature range from 1 I above the starting flow temperature to 30 ° below the starting flow temperature is processed into m to take 1 1 and the gap between T molds is 0. 2 " -1 .2 HI Fan Ye is more suitable. 0 stretch 1 1 magnification depends on the forming method. The appropriate value C. For example, using a biaxial stretcher 1 1 stretch 1 stretch ratio (length after stretching / Original length) in terms of * longitudinal stretch 1 The stretching ratio in the 1-direction and the transverse stretching direction is in the range of 1.2 to 20.0. Among them, 1.5 is used in the range of 1., and the range of -5.0 is more suitable when the stretching ratio is less than 1.2. Anti-II physical properties may be reduced and if it is greater than 2C • 3, the film smoothness will not be filled 1 1 I min. 0 1 1 | Liquid crystal 1 obtained when t is formed using a m-head blown OR with a crevice-shaped gap i This paper size applies to China National Standard (CNS) A4 (2) OX 297 mm 3 1 3 8 7 0 1

A A7 B7 經濟部中央標率局員工消費合作社印製 五、發明説明（30 ) I | 聚 m 樹 脂 組 成 物 供 料 至 備 有 環 狀 縫 隙 模 頭 之 熔 融 混 練 擠 壓 1 1 機 C 在 擠 筒 設 定 溫 度 200 - -360 V 下 S 宜 為 在 230〜350 V 下 1 1 進 行 熔 融 混 練 會 再 由 擠 壓 farte m 之 環 狀 縫 隙 向 上 方 或 往 下 方 擠 1 I 請 1 I 壓 出 熔 融 樹 脂 使 成 筒 狀 薄 勝 IrK C 琿 狀 縫 隙 間 距 通 常 在 0 . 1〜 先 閱 | 讀 I \ 5 a η範園， 其中以0 .2 2 Ώ η範圍為較佳s 環狀縫隙之直徑 背 1 之 1 通 常 在 20 1000 範 圍 i 其 中 以 25 6 0 0 m IB範圍為較佳。 注 黃 i 事 1 經 熔 融 擠 壓 出 的 筒 狀 熔 融 樹 脂 薄 膜 於 縱 向 方 向 牽 拉 項 1 再 4 丄 同 時 * 由 筒 狀 薄 膜 内 餹 以 空 氣 或 不 活 性 氣 Biw 體 (例如氮氣等） % 太 -V — 个 頁 1 吸 人 其 中 * η 此 於 向 與 其 垂 直 的 m 向 (TD) 使 薄 膜 吹 脹 、^< 1 拉 伸 而 成 C 1 1 本 發 明 中 k 利 用 液 晶 聚 酯 樹 脂 組 成 物 之 吹 脹 成 形 薄 膜 1 1 時 ， 其 吹 脹 倍 半 為 1 . 5〜1 0範圍， 較宜的縱向拉伸倍率為 訂 | 1 . 5〜40範圍， 1 1 吹 脹 成 形 薄 膜 時 之 設 定 條 件 在 上 述 範 圍 之 外 時 可 能 ffitt 现i 1 1 | 獲 得 厚 度 均 勻 且 無 縐 紋 之 高 強 度 的 液 晶 聚 酯 樹 脂 組 成 物 薄 1 1 m 而 不 宜 D 1 經 吹 腺 的 薄 膜 > 利 用 空 窗 冷 或 水 冷 却 法 冷 却 其 周 綠 1 1 後 9 經 過 夾 棍 (η i P r ο I 1 ) 而 予 牽 引 C 1 [ 吹 脹 成 形 薄 膜 時 1 m 液 晶 聚 酯 樹 脂 組 成 物 之 組 成 « 而 I | 選 擇 能 使 筒 狀 熔 融 薄 膜 成 為 厚 度 均 一 且 表 面 平 滑 狀 態 之 吹 1 I 脹 條 件 D ] I 本 發 明 中 所 得 液 晶 聚 酯 樹 脂 組 成 物 薄 膜 厚 度 並 無 特 別 1 i 限 制 1 但 以 1 〜50C η Β厚度3 鸟較宜， 其中以] 200 W 1 1範 圍 1 1 為 最 宜 〇 1 ] 本紙張尺度適用中國國家標準（cns ) A4規格（2丨〇乂297公釐） 3 2 3 8 7 0 1 B7 經濟部中央標準局員工消費合作社印製 五、 發明説明（ 3 1 ) 1 I 液 晶 聚 酯 樹 脂 組 成 物 薄 膜 必 要 時 可 再 施 加 表 面 處 理 1 1 1 C 上 述 表 面 處 理 方 法 之 例 舉 有 電 輋 處 理 電 漿 處 理 ·> 火 請 1 1 先 1 焰 處 理 濺 鍍 處 理 > 溶 劑 處 理 等 C 閱 1 f 1 本 發 明 的 電 子 組 件 包 裝 材 料 僳 由 依 照 上 述 方 法 製 得 液 ώ 之 注 I 晶 聚 酯 樹 脂 組 成 物 薄 膜 而 構 成 本 發 明 之 電 子 組 件 包 裝 材 意 事 1 項 I 料 可 使 用 在 例 如 積 體 電 路 電 晶 體 二 極 管 電 容 器 壓 再 填 1 電 元 件 寄 存 器 等 片 型 電 子 組 件 之 包 裝 用 途 C 寫 本 頁 1 上 述 電 子 組 件 包 裝 材 料 之 具 體 例 舉 有 葙 連 m 構 成 提 供 ·-—^ 1 f 收 容 電 子 組 零 件 用 收 容 袋 之 壓 花 載 物 帶 及 提 供 可 密 封 於 該 1 I 載 物 帶 之 覆 蓋 帶 而 成 的 m 子 組 件 包 裝 容 器 0 1 1 訂 上 逑 覆 蓋 帶 可 使 用 按 照 上 述 本 發 明 方 法 所 製 得 之 液 晶 1 聚 酯 樹 脂 組 成 物 簿 膜 1 1 又 I 另 外 的 載 物 帶 可 利 用 按 照 上 述 方 法 所 m 得 的 液 晶 1 1 聚 酷 樹 脂 組 成 物 薄 膜 再 經 過 加 熱 壓 化 輥 進 行 壓 化 加 工 處 理 1 而 製 成 0 其 他 > 例 如 田 成 形 薄 膜 時 1 m 先 在 T 模 下 方 設 置 1 | 壓 花 棍 i 再 進 行 樹 脂 成 形 薄 膜 之 同 時 進 行 壓 化 加 X 處 理 亦 1 I 製 成 0 1 1 [ 本 發 明 中 亦 可 以 利 闬 液 晶 m m 樹 脂 組 成 物 薄 膜 1 1 (丙） 成 分 之 不 包 括 m 晶 聚 酯 與 液 晶 聚 m 樹 脂 m 成 物 之 熱 塑 1 I 性 樹 脂 薄 膜 經 Ψ 積 層 而 成 的 薄 膜 供 上 述 載 物 帶 使 用 1 1 上 逑 熱 塑 性 樹 脂 之 m 成 分 只 要 不 是 液 晶 聚 m 或 液 晶 聚 1 1 m 樹 脂 組 成 物 並 未 予 特 別 限 制 1 例 如 可 採 用 聚 -乙 烯 % 聚 1 I 丙 烯 乙 烯 3 •烯 m 共 聚 物 等 聚 烯 烴 聚 苯 乙 烯 \ 聚 m 酸 1 ‘紙張尺度適用中國國家標率（CNS ) A4規格（210 X； 297公釐） 33 ο 〇 ? Λ η A7 B7 經濟部中央標準局員工消費合作社印繁 五、 發明説明（32 ) 1 | 酯 聚 對 苯 二 甲 酸 乙 二 酷 或 聚 對 笨 二 甲 酸 丁 二 酯 等 聚 m 1 1 聚 縮 m 聚 醅 胺 Λ 聚 伸 苯 基 > 聚 m 厢 Λ 乙 烯 -乙酸乙烯 1 1 酯 共 聚 物 ·、 聚 氣 乙 烯 ·、 聚 偏 二 氣 乙 烯 、 聚 伸 基 硫 醚 含 1 I 請 1 I 樹 脂 等 C 其 中 以 使 用 聚 乙 烯 > 聚 丙 烯 飞 乙 烯 -C (* 烯 烴 共 先 閲 | 讀 ! \ 聚 物 聚 對 苯 二 甲 酸 乙 二 酯 為 較 佳 0 熱 塑 性 樹 脂 可 藉 其 一 背 面 1 之 1 種 或 — 棰 以 上 混 入 而 製 成 薄 膜 C 本 發 明 中 的 熱 塑 性 樹 脂 包 注 意 ί [ 括 分 子 鍵 中 導 λ 功 能 基 而 變 性 之 改 質 熱 塑 性 樹 脂 在 内 〇 事 項 再 1 1 d 丄, 上 述 稍 層 薄 膜 之 製 造 方 法 並 無 待 別 限 制 C 將 各 構 成 成 寫 今·— 頁 1 分 之 熔 融 樹 脂 於 楔 頭 内 彙 流 後 * 由 模 頭 擠 壓 之 方 法 1 或 將 1 各 熔 融 樹 脂 白 模 頭 擠 壓 後 再 行 積 層 之 方 法 1 或 進 入 模 頭 之 1 1 前 將 各 熔 融 體 樹 脂 彙 流 後 由 模 頭 擠 壓 之 方 法 等 > 依 其 的 1 1 而 選 擇 適 當 的 製 造 方 法 C! 訂 I 本 發 明 之 液 晶 聚 m 樹 脂 紐 成 物 成 形 物 可 稱 各 稱 成 形 方 1 1 法 製 成 C 例 如 上 述 之 藉 T 模 熔 融 擠 壓 法 % 吹 脹 成 膜 法 射 1 1 | 出 成 形 法 或 加 熱 模 壓 法 等 先 得 液 晶 聚 館 樹 脂 組 成 物 薄 m 1 1 或 板 Η 後 1 再 使 用 加 熱 設 備 加 熱 % 軟 化 上 述 薄 膜 或 板 片 i 1 然 後 固 定 於 模 型 上 * 經 去 除 成 形 物 内 氣 體 而 使 薄 膜 或 板 Η 1 ! 阽 緊 於 模 型 上 之 所 謂 真 空 成 形 方 法 C 同 樣 經 去 除 板 片 或 薄 ! 1 膜 内 之 氣 體 ί 同 時 導 人 加 壓 空 氣 使 板 Η 或 薄 糢 貼 緊 於 模 型 ί | 之 壓 空 成 形 方 法 ί m 將 被 夾 持 於 陰 楔 内 之 加 熱 板 片 或 薄 膜 1 I f 锗 模 塞 壓 λ 模 型 内 1 經 真 空 吸 引 使 之 阽 緊 於 模 上 的 肋 m 1 1 | 模 法 等 皆 可 採 用 C 1 t I 另 外 • 不 預 先 經 過 熔 融 混 練 過 程 > 將 組 成 分 之 錠 粒 在 1 1 成 形 時 乾 摻 合 i 經 予 熔 融 混 練 而 成 形 為 本 發 明 之 樹 脂 組 成 1 1 本紙張尺度適用中國國家標準（cns ) λ4規格（2i〇x297公釐） 3 4 3 3 7 0 1 459037 at B7 經濟部中央標率局員工消費合作社印製 五、 發明説明（3 3 ) 1 1 物 1 再 直 接 製 成 薄 暌 或 板 Η 0 i 1 1 本 發 明 中 » 液 晶 聚 m 樹 脂 組 成 物 薄 膜 或 薄 片 之 成 形 容 1 1 1 器 > 就 其 形 狀 而 言 » 圓 形 容 器 時 • 該 容 器 深 度 與 容 器 上 ΛΜΙ 端 1 1 請 1 I P 徑 間 比 率 (下文中稱此比率為深徑比率（d r aw i η ε ) 以 1 / 先 閱 I ή 1 1 100以上為較宜， 以1 / 1 0以上為最宜。 方形容器時， 該容 背 面 1 之 1 器 深 度 與 容 器 開 P 部 分 之 最 長 對 角 線 長 度 間 比 率 (下文中， f 事 I 稱 此 比 率 為 深 徑 bh 率 )以1 /1 00以 為 較 宜 * 以 在 1 / 1 0 以 上 為 項 再 填 1 丄, 最 宜 〇 寫 本 頁 1 本 發 明 中 * 液 晶 聚 酯 樹 脂 組 成 物 成 形 物 之 表 面 • 必 要 1 1 時 可 施 加 表 面 處 理 0 上 述 表 面 處 理 方 法 例 如 電 甭 處 理 1 1 電 漿 處 理 火 焰 處 理 濺 鑛 處 理 溶 劑 處 理 等 0 1 1 本 發 明 之 成 形 物 亦 可 為 由 上 述 液 晶 聚 酯 樹 脂 組 成 物 訂 1 而 成 的 層 與 液 晶 聚 酯 以 外 之 埶 塑 性 樹 脂 組 成 物 層 之 積 層 物 ί 1 構 成 C 述 熱 塑 性 樹 脂 可 利 用 上 述 熱 塑 性 樹 脂 0 1 I 本 發 明 中 * 液 晶 聚 m 樹 m 組 成 物 層 及 熱 塑 性 樹 脂 層 可 1 1 利 用 壓 粘 法 粘 接 i 其 中 以 熱 壓 粘 法 粘 接 為 較 宜 0 粘 接 時 t I I 液 晶 聚 酯 樹 脂 組 成 物 層 熱 塑 性 樹 m 層 之 間 可 介 以 拈 著 劑 1 1 層 C 1 i 上 述 粘 著 劑 之 例 舉 有 熱 熔 m 拈 著 劑 聚 胺 m 粘 著 劑 或 1 1 含 環 氧 基 共 聚 物 寺 C 1 1 本 發 明 之 殺 菌 軟 袋 用 包 裝 材 料 * 可 藉 熱 封 缄 法 將 上 述 1 I 液 晶 聚 酯 樹 脂 組 成 物 薄 膜 按 照 所 定 尺 寸 加 工 而 製 成 0 1 I 又 上 述 將 樹 脂 薄 膜 成 形 為 袋 狀 而 供 殺 m 軟 袋 或 成 1 1 j 形 為 獨 立 1*1. 性 之 袋 狀 而 提 供 可 直 立 的 軟 袋 用 C 1 1 本紙張尺度適用中國國家標準（CNS ) A4規格（210 X 297公釐） 35 387 0 1 Α7 Β7 經濟部中央標隼局員工消費合作社印製 五、 發明説明4 ) 1 I 殺 阑 軟 袋 或 可 直 立 的 軟 袋 t 可 製 成 三 面 經 熱 封 的 形 狀 \ 1 I ， 四 面 經 埶 封 緘 的 形 狀 枕 狀 形 狀 > 直 立 狀 形 狀 或 箱 中 1 1 f 袋 形 狀 等 各 種 形 態 而 使 用 0 >«V I 請 I 本 發 明 之 殺 菌 軟 袋 或 可 直 立 的 軟 袋 用 包 裝 材 料 ， 亦 可 无 閱 I 讀 1 I 樑 用 於 上 述 液 晶 聚 酯 樹 脂 組 成 物 薄 膜 上 層 積 以 其 他 熱 塑 性 背 1 之 1 I 樹 脂 薄 膜 而 成 的 稍 層 狀 薄 膜 C 注 意 1 I 事 ! 上 述 液 晶 聚 酯 樹 脂 組 成 物 薄 暌 以 外 之 其 他 熱 塑 性 樹 脂 項 再 1 4 m 膜 並 無 特 別 限 制 » 例 如 聚 乙 烯 聚 丙 烯 等 聚 烯 烴 薄 膜 • 寫 今〜 頁 1 聚 對 苯 二 甲 酸 乙 二 酯 % 聚 對 苯 二 甲 酸 丁 二 酯 等 聚 酷 薄 膜 ; Sw-· 1 1 聚 m 胺 薄 膜 '1 聚 笨 乙 烯 丙 烯 酸 酯 条 樹 脂 含 m 樹 脂 聚 1 1 1 m 酸 酯 聚 醚 碾 聚 伸 苯 基 通 、 聚 伸 苯 基 醚 等 薄 膜 較 宜 採 1 1 訂 1 用 3 其 中 以 聚 烯 烴 薄 膜 為 取 佳 使 用 上 述 積 層 薄 膜 於 本 發 明 之 殺 镇 軟 袋 或 可 直 立 的 軟 1 1 袋 用 包 裝 材 料 時 * 必 要 時 t 可 在 液 晶 聚 酷 樹 脂 組 成 物 薄 膜 1 | 及 其 他 的 塑 性 樹 脂 m 膜 之 間 t 使 用 熱 熔 m 粘 箸 劑 .、 聚 胺 1 酯 粘 箸 m 等 藉 以 提 升 各 積 層 間 之 粘 箸 強 度 C 1 I 上 述 積 層 薄 膜 於 殺 a 軟 袋 」: 之 使 闬 形 m yUi<- t 並 無 特 別 限 1 I I 制 C 將 液 晶 聚 酯 樹 脂 組 成 物 薄 膜 作 為 外 層 i 其 他 熱 塑 性 樹 1 1 脂 薄 膜 作 為 與 内 容 物 接 觸 之 内 層 而 成 形 之 外 < 尚 可 利 用 其 ! 1 他 熱 塑 性 樹 脂 薄 膜 將 液 晶 聚 酯 樹 m 組 成 物 薄 膜 夾 成 三 明 治 1 1 狀 夾 而 予 成 形 0 [ I 本 發 明 中 * 殺 菌 軟 袋 或 M. 立 的 軟 袋 可 在 將 容 器 中 予 1 I 以 脱 氣 的 狀 態 下 或 容 器 中 用 氮 氣 等 不 活 性 氣 jsjir m 镇 充 狀 態 1 1 I 下 使 用 之 0 1 1 本紙張尺度適用中國國家標率（CNS ) Λ4規格（210X297公釐） 36 3 8 7 0 1 A7 B7 經濟部中央標準局員工消費合作社印製 五、' 發明説明（ 35 ) 1 1 上 述 殺 菌 軟 袋 或 可 直 立 的 軟 袋 可 提 供 咖 哩 、 魚 類 ·、 畜 1 1 1 肉 類 % 柴 魚 粉 Λ 調 味 料 ·、 水 果 飲 料 ·» 點 滴 輸 液 用 袋 等 食 1 1 品 飲 料 fTJ 翳 療 用 包 裝 材 料 等 廣 範 用 途 ：> 一~V 1 | 請 1 | 本 發 明 之 中 空 成 形 物 容 器 之 製 造 方 法 1 可 採 用 各 種 吹 先 閱 I 讀 1 I 脹 成 形 方 法 0 例 如 熔 融 擠 壓 出 的 管 狀 型 坯 在 未 冷 却 前 吹 脹 背 面 1 之 1 成 形 之 擠 壓 吹 脹 成 形 方 法 (直接吹脹成形方法> S 或 利 用 射 注 意 1 事 1 出 成 形 法 成 形 型 还 » 妫 後 利 用 吹 脹 成 形 的 射 入 吹 塑 成 形 方 項 再 1 丄 法 f 或 在 吹 脹 成 形 時 進 行 拉 伸 的 拉 伸 吹 腺 成 形 方 法 等 1 視 填 寫 頁 1 目 的 而 可 選 擇 通 當 的 吹 眼 成 形 方 法 '·» 1 吹 脹 成 形 方 法 中 * 中 空 成 形 機 之 擠 筒 設 溫 度 及 模 頭 1 ί 設 定 溫 度 在 200〜360 X： 範 圍 為 宜 * 其 中 以 230〜350 V， 範 圍 1 1 為 更 宜 C 訂 1 吹 脹 成 形 時 導 入 型 坯 中 之 氣 體 並 無 待 別 限 制 t — 般 使 1 I 用 空 氣 較 適 宜 0 ! j 由 上 述 含 有 液 晶 聚 對 脂 組 成 物 而 成 之 層 由 熱 塑 性 1 丄 樹 脂 層 (但不包括液晶聚酯及液晶聚酯樹脂組成物在内） 而 1 成 之 橫 層 構 造 物 構 成 的 中 空 成 形 物 容 器 亦 包 括 於 本 發 明 範 1 1 圍 C 1 1 上 述 熱 塑 性 樹 (但不包括液晶聚酯及液晶聚酯樹脂 [ 1 組 成 物 在 内 )以含有由聚烯烴、 聚苯乙烯、 聚磺酸酯、 聚 1 1 酯 聚 縮 聚 m 胺 '、 聚 伸 苯 基 醚 聚 m m -、 乙 烯 -乙酸 函 1 I 乙 烯 酯 、 聚 偏 二 氣 乙 烯 、 聚 伸 苯 基 埯 m 含 氟 樹 脂 等 選 出 1 1 1 的 至 少 一 種 者 為 佳 其 中 以 聚 烯 η 、 聚 酯 醯 m 等 熱 塑 1 1 1 性 樹 脂 為 最 佳 0 1 1 本紙張尺度適用中國國家標準（CNS ) A4規格（210X 297公釐） 3 7 3 870 1 B7 五、 發明説明（3 6 ) 1 I 本 發 明 中 之 積 層 構 造 體 至 少 由 二 種 以 上 之 上 述 方 法 製 1 1 I 得 的 液 晶 聚 酯 樹 脂 組 成 物 層 及 熱 性 樹 脂 層 間 之 積 層 物 * 該 1 1 I 層 稱 造 以 外 » 尚 可 在 液 晶 聚 酯 樹 脂 組 成 物 m ft3 之 兩 面 曆 積 以 請 [ 1 t 熱 塑 性 樹 脂 層 而 構 成 三 層 構 造 5 或 由 液 晶 聚 96 樹 脂 組 成 物 先 閱 讀 1 臑 舆 熱 塑 性 樹 脂 層 交 互 層 積 而 構 成 五 層 構 造 亦 可 另 外 > 背 面 1 之 1 尚 可 能 使 用 上 述 液 晶 聚 酯 樹 脂 組 成 物 層 或 熱 塑 性 樹 脂 層 以 注 意 拳 1 1 外 之 層 間 之 積 層 物 0 1 再 1 丄 由 上 述 積 層 體 而 成 的 中 空 成 形 物 容 器 » 可 藉 前 述 吹 脹 本 百 I 成 形 方 法 製 造 之 〇 積 層 體 之 吹 脹 成 形 法 中 可 由 複 數 擠 壓 \ 1 I 機 將 各 履 樹 脂 以 熔 融 狀 態 » 擠 m 至 具 有 相 同 圓 形 狀 通 路 之 1 1 同 一 模 頭 於 模 頭 内 蹙 合 各 層 1 m 成 型 坯 i 同 時 利 用 氣 體 I 1 壓 力 使 型 坯 膨 眼 緊 密 粘 阽 於 金 曝 模 之 所 謂 多 層 吹 脹 法 而 1 丁 1 製 得 本 發 明 之 中 空 成 形 物 容 器 Λ 1 1 本 發 明 之 具 液 晶 聚 酯 樹 脂 組 成 物 層 及 熱 塑 性 樹 脂 層 之 1 1 積 屬 構 造 體 而 成 的 中 空 成 形 物 容 器 1 可 善 加 利 用 其 成 形 加 1 X 性 耐 熱 性 阻 氣 性 % 汽 油 阻 絶 性 汽 油 醇 阻 絶 性 而 較 1 I 適 合 使 用 於 燃 料 用 容 器 C 1 I 1 上 述 燃 料 用 容 器 1 構 成 積 層 構 造 體 之 熱 塑 性 樹 脂 以 採 1 i 用 聚 烯 烴 為 佳 ί 其 中 以 密 度 為 〇. 9 4 —W 0 . 9 8 0 , 極限粘度為 1 1 2- -7d 1 / @ 之 高 密 度 聚 乙 烯 最 佳 ζ> 1 1 本 發 明 之 發 泡 成 形 物 f 至 少 由 含 有 上 述 ί ψ ，成 分 及 1 1 (乙） 成 分 之 液 晶 聚 酯 樹 脂 組 成 物 經 成 形 而 製 成 例 如 將 對 1 1 以 ( Ψ 成 分 及 (乙 成 分 之 口 計 為 100重毚 分計 含有 (丙 ) 1 1 成 分 發 泡 劑 0 1， 一 15重量4 分之液晶聚酯彳 衝脂M j 戎 物經 ψ 戎 i 1 本紙張尺度適用中國國家標隼（CNS ) A4规格（210X 297公釐） 38 38701 A7 B7 經濟部中央標準局員工消費合作社印製 五、發明説明) 1 I 形 而 製 成 〇 1 1 上 述 發 泡 劑 視 0 的 而 由 市 售 的 發 泡 剤 中 選 擇 適 當 種 類 1 1 而 使 用 〇 該 發 泡 劑 之 具 體 例 舉 有 磺 酸 氳 納 硪 酸 氫 m m 1 I 酸 押 磺 酸 氛 m 化 硼 鈉 β 氮 化 偶 氮 m 酸 酷 胺 (下 請 先 閲 1 1 文 中 或簡稱為ADCA)、 偶氮雙甲酸胺（下 文 中 或 簡 稱 為 AB F A 讀 背 1 1 I )Λ 偶氮雙異丁睛（下 文 中 或 簡 稱 為 AZDA)、 N ,K 1 — 一 硝 基 五 之 注 意 1 1 酉 甲 四 胺 (下文中或簡稱為DPT)、 Ν ,Ν ϊ 一 二 亞 硝 基 -N ,N t · 二 ψ 項 再 1 1 甲 基 酞 酸 醯 胺 Λ 苯 磺 m 醯 胼 (下文中或簡稱為B S Η )、 對- 甲 填 寫 * 九 今一 苯 磺 醯 m (下文中或簡稱為TSH)、 Ρ ,Ρ f — 氣 化 雙 苯 磺 m 酸 肼 頁 1 1 (下文中或簡稱為0 B S Η )、 對 -甲苯磺醯氛基脲（下 文 中 m 簡 1 1 稱為TSSC)、 3肪二B秦等。 1 1 又 » 本 發 明 中 也 可 以 使 用 氣 體 作 為 發 泡 劑 而 製 成 發 泡 訂 | 成 形 物 〇 該 時 必 須 在 熔 融 樹 脂 中 將 氣 體 分 散 均 勻 而 進 行 發 1 I 泡 處 理 上 述 氣 am 體 之 具 體 例 舉 有 Μ 氣 二 氣 化 m 、 碳 氣 化 1 1 I 合 物 氣 化 m 氟 化 合 物 等 C 1 1 發 泡 劑 種 類 之 選 擇 視 樹 脂 組 成 物 之 成 形 加 工 溫 度 由 1 發 泡 劑 之 分 解 溫 度 以 接 近 上 述 成 形 加 工 溫 度 者 中 選 闬 適 當 1 ! 者 為 宜 0 1 1 樹 脂 尚 未 充 分 熔 解 過 程 中 * 發 泡 劑 分 解 時 i 或 樹 脂 兀 I 1 金.熔解 而 發 泡 劑 之 分 解 未 充 分 進 展 時 i 發 泡 成 形 物 會 出 現 1 1 發 外 觀 不 良 或 氣 泡 直 徑 不 均 勻 而 無 法 形 成 發 泡 成 形 物 等 1 1 缺 點 産 生 C 1 1 1 本 發 明 可 提 供 耐 熱 性 ff 異 的 液 晶 聚 酯 樹 脂 m 成 物 之 發 1 1 泡 成 形 物 c 宜 採 用 高 溫 下 可 分 解 - 泡 的 發 泡 劑 其 中 以 1 1 本紙張尺度適用中國國家標準（CNS ) Λ4規格（2丨0X297公釐） 39 3 8 7 0 1 'r 459037 A7 _____B7 五、發明説明（38 ) 使用磺酸鉀、ΑΒΡΑ、三肼三嗪、ADCA、DPT、OBSH、TSSC 等發泡劑為最適宜。 本發明中的發泡劑用Μ.以（甲）成分及（乙）成分之合 計100重量份計，採用0.1〜15重量份為適宜c 發泡劑用量未達0.1重量份時.顯然失去發泡效果， 而超過15重量份時，發泡物外觀不良，強度亦降低而不理 想。 本發明中，液晶聚酯樹脂組成物能表現優異的成膜加 工性、柔軟性、阻氣性、闸熱性等，其原因雖然未詳，據 推測可能是由（甲）成分之液晶聚酯與（乙）成分之橡_之間 産生某些反應所致。 育旃Μ 本發明藉實施例詳述之。實施例僅為例舉，因此，本 發明範圍不受實施例之局限不待説明。 (1 )(甲）成分之液晶聚酯 (i)於備有椋形搜拌翼之聚合反應構中，饋入對-乙 醯氧基苯甲酸（1 0 . 8 k s , 6 0 ο ο 1),對苯二甲酸（2 . 4 9 k g , 經濟部中央標準局員工消費合作社印製 (請先鬩讀背面之注意事項再填寫本頁) 15|!1〇〗），間苯二甲酸（0.01(8,511〇1)及4,4'-二乙醯氣基 二苯（5.45kg, 20.2ιβ〇1),然後在籠罩氤氣條件下褪拌並 升溫至330t而聚合反應1小時，反應中一面去除所副産 的乙酸一面在強力Μ拌下進行聚合作用。然後逐漸冷却反 應条，在200Τ：下將所得的聚合物取出反慝条外。所得的 聚合物铥細川徹粒公司製之錘磨機加以粉碎成為2·5πιπι以 下的粒狀物。然後在旋轉茁中籠罩氮氣條件下以28〇υ處 本紙張尺度適用中國國家標準（CNS ) Α4規格（2!0Χ297公釐） 40 38 7 0 1 /] ^ (2 n q 7 A7 B7 五、發明説明（39 ) 理3小時，而得流動溫度為3 2 4 °C之由下列重複結構單位 而成的全芳族聚酯e 上述流動溫度乃指使用曰本島津製作所製诰的高化式 流動測試機CPT-500型，將每分種以升溫速度加熱的樹 脂，於100kgf/cn2之負載下，由内徑1, mnt,長度lOmm之噴 嘴擠出時，熔融粘度示48000泊（poise)時之溫度c 下文中以（甲-1 )簡稱所得的上述液晶聚酯。本聚合物 在加壓下，340 1以上時顯示光學各向異性。液晶聚酯 (甲-1 )之重複結構單位如下所示： (請先閱讀背面之注意事項再填寫本頁)A A7 B7 Printed by the Consumer Cooperatives of the Central Standards Bureau of the Ministry of Economic Affairs 5. Description of the invention (30) I | Poly m resin composition is fed to a melt-kneading extrusion equipped with a ring gap die 1 1 Machine C is extruding Setting temperature 200--360 V S should be 230 ~ 350 V 1 1 Melt kneading will squeeze upward or downward from the annular gap of farte m 1 I Please 1 I Press out the molten resin to make Cylindrical thin win IrK C 珲 gap distance is usually 0.1 ~ read first | read I \ 5 a η Fan Yuan, where the range of 0.2 2 Ώ η is better Usually in the range of 20 1000 i, the range of 25 6 0 m IB is preferred. Note yellow matter 1 The cylindrical molten resin film extruded by the melt extrusion in the longitudinal direction 1 and 4 丄 At the same time * from the inside of the cylindrical film with air or inert gas Biw gas (such as nitrogen, etc.)% too- V — page 1 attracts people * η This is to blow the film in the m-direction (TD) perpendicular to it and ^ < 1 stretch to form C 1 1 In the present invention, k is used to blow the liquid crystal polyester resin composition. When the expanded film 1 1 is formed, the inflation half of the film is in the range of 1.5 to 10, and the preferred longitudinal stretching ratio is set to be in the range of 1.5 to 40. The setting conditions for the 1 1 blown formed film are as described above. Outside the range, it is possible to ffitt the current i 1 1 | obtain a high-strength liquid crystal polyester resin composition with a uniform thickness and no crepe, thin 1 1 m, not suitable for D 1 gland-blown film > use an empty window Or water-cooling method to cool its perimeter green 1 1 and then pass the clamp rod (η i Pr ο I 1) to pull C 1 [1 m composition of liquid crystal polyester resin composition when inflating a film «And I | Blown cylindrical molten film with uniform thickness and smooth surface 1 I Swelling conditions D] I The thickness of the liquid crystal polyester resin composition film obtained in the present invention is not particularly 1 i limited 1 but within 1 to 50C η Β thickness 3 birds More suitable, among which] 200 W 1 1 range 1 1 is the most suitable 〇1] This paper size applies Chinese National Standard (cns) A4 specification (2 丨 〇 乂 297 mm) 3 2 3 8 7 0 1 B7 Ministry of Economic Affairs Printed by the Consumer Standards Cooperative of the Central Bureau of Standards 5. Description of the Invention (3 1) 1 I Liquid crystal polyester resin composition film can be further applied with surface treatment if necessary 1 1 1 C Examples of the surface treatment methods mentioned above include electrolysis and plasma treatment ≫ Fire please 1 1 first 1 flame treatment sputter treatment > solvent treatment, etc. C 1 f 1 The electronic component packaging material of the present invention is made of a liquid crystal polyester resin composition film prepared in accordance with the above method. Component packaging materials 1 item I materials can be used in, for example, integrated circuit transistors, diodes, capacitors, and refills. 1 Packaging of chip electronic components such as electrical component registers. C Write this page. 1 Specific examples of the packaging materials for electronic components mentioned above are Coupling m configuration provides ----- ^ 1 f embossed carrier tape for the storage bag for storing electronic group parts and m sub-assembly packaging container provided with a cover tape that can be sealed to the 1 I carrier tape 0 1 1 order The cover tape can be used according to the invention The liquid crystal 1 polyester resin composition film 1 1 and 1 produced by the method can be used for the other carrier tape to use the liquid crystal 1 1 poly resin composition film obtained by the method described above and then pressed by a heating and pressing roller. Processing 1 to make 0 Others> For example, when forming a film, 1 m is set under the T die 1 | embossing stick i, and then the resin is formed into a film while being pressed and treated with X and also 1 I is made into 0 1 1 [In the present invention, a liquid crystal mm resin composition film 1 1 (c) may be used, and the thermoplastic 1 I resin film, which does not include m-crystalline polyester and liquid crystal polym resin m, is a film formed by lamination. For the use of the above-mentioned carrier tape, the 1 component of the m thermoplastic resin is not limited as long as it is not a liquid crystal poly m or a liquid crystal poly 1 1 m resin composition. 1 For example, poly-ethylene% may be used. 1 I Propylene ethylene 3 Polyolefin polystyrene such as olefin m copolymer \ Poly m acid 1 'Paper size applies to China National Standard (CNS) A4 specification (210 X; 297 mm) 33 ο 〇 Λ η A7 B7 Staff Consumer Cooperative of the Central Bureau of Standards, Ministry of Economic Affairs, Yin Fan V. Invention Description (32) 1 | Ester Polyethylene terephthalate or Polybutylene terephthalate, etc. Poly m 1 1 Polycondensation m Polyamine Λ Poly Polyphenylene > Polymethylene Λ Ethylene-vinyl acetate 1 1 Ester copolymer ·, Polyethylene ·, Polyvinylidene diene, Polyethylene sulfide containing 1 I Please 1 I Resin, etc. C Among them, polyethylene is used > Polypropylene Ethylene-C (* olefins are read together first | read! \ Polymer polyethylene terephthalate is preferred 0 Thermoplastic resin can be made by mixing one of its back 1 or — 棰 or more Forming film C The thermoplastic tree in the present invention Including attention [including the modified thermoplastic resin modified by the λ functional group in the molecular bond, including the modified thermoplastic resin, the matter is 1 1 d 丄, the method of manufacturing the above-mentioned thin film is not limited, and each component is written as this ... Page 1 of the molten resin converges in the wedge * Method 1 of extrusion by the die or method 1 of laminating the molten resin white die 1 or lamination of each of the resin before entering the die 1 1 Method for extruding a molten resin by a die after converging, etc. > Choosing an appropriate manufacturing method according to 1 1 of it C! Order I The liquid crystal poly m resin formed article of the present invention can be called each forming side 1 1 to make C. For example, the above-mentioned method uses T-die melt extrusion method% blown film-forming method to shoot 1 1 | out molding method or heating molding method, etc. first obtain the liquid crystal polymer resin composition thin m 1 1 or plate Η after 1 Make again Use a heating device to soften the above-mentioned film or sheet i 1 and then fix it on the model. * The so-called vacuum forming method C, which is to make the film or sheet 成形 1! Thin! 1 At the same time, the gas in the film is induced by pressurized air to make the plate or thin mold close to the mold. The method of pressure forming is m The heating plate or film to be held in the female wedge 1 I f Germanium plug pressure λ In the model 1 Vacuum sucked to tighten the ribs on the mold m 1 1 | Molding method can use C 1 t I In addition • Without prior melt-kneading process > Ingot composition Dry blending during molding 1 1 Melting and kneading to form the resin composition of the present invention 1 1 This paper size applies the Chinese National Standard (cns) λ4 specification (2i0x297 mm) 3 4 3 3 7 0 1 459037 at B7 Employee Consumer Cooperatives, Central Standards Bureau, Ministry of Economic Affairs Preparation 5. Description of the invention (3 3) 1 1 物 1 and then directly made into a thin sheet or sheet Η 0 i 1 1 In the present invention »Liquid crystal poly m resin composition film or sheet forming capacity 1 1 1 device > about it In terms of shape »For a round container • The depth of the container and the ΛΜΙ end on the container 1 1 Please 1 IP ratio between diameters (hereafter referred to as the ratio of depth to diameter (dr aw i η ε)) 1 / read first price 1 More than 1 100 is more suitable, and more than 1/10 is most suitable. In the case of a square container, the ratio between the depth of 1 on the back of the container and the longest diagonal length of the P-part of the container (hereinafter, f event I will call this ratio the depth diameter bh ratio) is preferably 1/1 00 * Fill in 1 1 above 1/1 0, it is best to write this page. 1 In the present invention * The surface of the liquid crystal polyester resin composition molded article • If necessary, 1 can be applied with a surface treatment. 0 Surface treatment methods such as above Electrolytic treatment 1 1 Plasma treatment Flame treatment Spattering treatment Solvent treatment, etc. 0 1 1 The molded article of the present invention may also be a layer made of the above-mentioned liquid crystal polyester resin composition and a plastic resin other than liquid crystal polyester The laminated material of the composition layer ί 1 constitutes the thermoplastic resin described in C. The above-mentioned thermoplastic resin can be used. 0 1 I In the present invention * liquid crystal polymer m tree m The composition layer and the thermoplastic resin layer can be bonded by pressure bonding method i. Among them, thermocompression bonding method is preferred. 0 When bonding, t II liquid crystal polyester resin composition layer thermoplastic tree m layer can be interposed. Adhesive 1 1 Layer C 1 i Examples of the above adhesives include hot melt m Adhesive polyamine m Adhesive or 1 1 Epoxy group-containing copolymer C 1 1 Packaging for sterilizing soft bags of the present invention Material * The 1 I liquid crystal polyester resin composition film can be processed into a predetermined size by heat sealing method to make 0 1 I. The resin film can be formed into a bag shape to form a soft bag or a 1 1 j shape. For stand-alone 1 * 1. Bag-like products, it is provided for upright soft bags. C 1 1 This paper size is applicable to China National Standard (CNS) A4 (210 X 297 mm) 35 387 0 1 Α7 Β7 Central Standard of the Ministry of Economic Affairs Printed by the Bureau's Consumer Cooperatives V. Invention Description 4) 1 I anti-apical soft bag or upright soft bag t can be made into three-sided heat-sealed shape \ 1 I, four-side sealed shape pillow-shaped shape > upright shape or box 1 1 f bag shape and other various 0 > «VI Please I The sterilization soft bag of the present invention or the packaging material for a soft bag that can stand upright can also be used without reading I Read 1 I Beam is used to laminate the above liquid crystal polyester resin composition film with other thermoplastics Back 1 of 1 Slightly layered film made of I resin film C Note 1 I matter! The thermoplastic resin items other than the above-mentioned liquid crystal polyester resin composition thin film 1 4 m film is not particularly limited »such as polyethylene polypropylene Other Polyolefin Films • Written Today ~ Page 1 Polyethylene terephthalate, polybutylene terephthalate, and other cool films; Sw- · 1 1 polym amine film '1 polybenzyl acrylate strip resin containing m resin poly 1 1 1 m polyester polyether mill poly Films such as phenylene ether and polyphenylene ether are more suitable for use. 1 1 Order 1 for use 3 Among them, polyolefin films are preferred. The above-mentioned laminated films are used in the killer soft bags or upright soft 1 1 bags of the present invention. For packaging materials * If necessary, t can be used between the liquid crystal polymer resin film 1 | and other plastic resin m film t hot melt m adhesives, polyurethane 1 ester m Adhesive strength C 1 I The above laminated film is used to kill a soft bag ": It has no particular limitation on the shape of my yUi <-t 1 II. C. The liquid crystal polyester resin composition film is used as the outer layer i Other thermoplastic trees 1 1 The lipid film acts as an inner layer in contact with the contents Out of shape < Still use it! 1 Other thermoplastic resin film sandwiches the liquid crystal polyester tree m composition film into a sandwich 1 1 shape to preform 0 [I In the present invention * Sterilization soft bag or M. standing soft The bag can be degassed in the container with 1 I or inert gas such as nitrogen in the container. JSjir m 1 1 I used under 0 1 1 This paper size applies to China National Standards (CNS) Λ4 Specifications (210X297 mm) 36 3 8 7 0 1 A7 B7 Printed by the Consumers' Cooperative of the Central Standards Bureau of the Ministry of Economic Affairs 5. Description of the invention (35) 1 1 The above sterilized soft bags or upright soft bags can provide curry and fish · , Livestock 1 1 1 Meat% Ficus powder Λ Seasoning ·, Fruit Drinks · »Infusion bags for infusion and other food 1 1 drink fTJ Packaging materials for medical treatment etc. Wide range of uses: > 1 ~ V 1 | Please 1 | This In the invention Various methods can be used to manufacture the empty molded container. Read 1 I 1 I Blow molding method 0 For example, the tubular parison melt-extruded is blown before the back surface 1 to 1 is formed by the extrusion blow molding method ( Direct inflation molding method > S or use injection attention 1 thing 1 out of the molding method molding type »Then use injection blow molding method of inflation molding and then 1 method f or stretch during inflation molding According to the purpose of filling out page 1, you can choose the proper blow molding method '· »1 of the blow molding methods * The extrusion tube setting temperature of the hollow molding machine and the die head 1 ί Set the temperature at 200 ~ 360 X: The range is suitable * Among them 230 ~ 350 V, the range 1 1 is more suitable C Order 1 Introduced into the parison during inflation molding Gas does not need to be restricted t — Generally, 1 I is more suitable for use with air. 0! J The layer made of the above-mentioned composition containing liquid-crystalline polyethylene terephthalate is made of thermoplastic resin 1 (but not including liquid crystal polyester and liquid crystal polyester resin) The hollow molded product container composed of a 10% horizontal layer structure is also included in the scope of the present invention. The above-mentioned thermoplastic tree (but does not include liquid crystal polyester and liquid crystal polyester resin [1 composition Included) Contains polyolefins, polystyrene, polysulfonates, poly 1 1 ester polycondensation polyamines, polyphenylene ether poly mm-, ethylene-acetic acid, 1 I vinyl esters, and polyvinylidene dichloride. At least one of 1 1 1 is preferably selected from ethylene, polyphenylene fluorene, m, fluororesin, etc. Among them, thermoplastic 1 1 1 such as polyene η, polyester 醯 m, etc. are the best. 0 1 1 This paper size is applicable China National Standard (CNS) A4 Specification (210X 297 (Centi) 3 7 3 870 1 B7 V. Description of the invention (3 6) 1 I The laminated structure in the present invention is prepared by using at least two or more of the above methods 1 1 I liquid crystal polyester resin composition layer and thermal resin layer Laminates * The 1 1 I layer is not made »It is still possible to stack on both sides of the liquid crystal polyester resin composition m ft3 to ask for [1 t thermoplastic resin layer to form a three-layer structure 5 or a liquid crystal poly 96 resin composition Read 1 First, the thermoplastic resin layers are laminated alternately to form a five-layer structure. In addition, the back side 1 of 1 may also use the above-mentioned liquid crystal polyester resin composition layer or thermoplastic resin layer to pay attention to the layering between the layers物 0 1 再 1 丄 Hollow molded product container made of the above-mentioned laminated body »Inflatable forming method of laminated body that can be manufactured by the aforementioned inflation method In the process, multiple resins can be extruded in multiple stages. The machine can be used to extrude resins in the molten state »Extrude m to 1 with the same circular path 1 1 The same die is combined with each layer 1 m in the die. The so-called multi-layer inflation method in which the parison puffs are tightly adhered to the gold exposure mold, and the hollow molded product container of the present invention Λ 1 1 is obtained. 1 The liquid crystal polyester resin composition layer and the thermoplastic resin layer of the present invention 1 1 Hollow molded product container made up of structures. 1 It can make good use of its shape. 1 X heat resistance, gas barrier,% gasoline resistance, gasoline alcohol resistance. 1 I is more suitable for fuel containers C 1 I 1 The above-mentioned fuel container 1 The thermoplastic resin constituting the laminated structure is preferably made of polyolefin for 1 i. Among them, the density is 0.9 4 -W 0. 9 8 0, and the limiting viscosity is 1 1 2- -7d 1 / @ 之 高密Optimum polyethylene ζ > 1 1 The foamed molded article f of the present invention is made from a liquid crystal polyester resin composition containing at least the above ψ, components and 1 1 (B) components. Ψ Ingredients and ingredients (Part B is 100 parts by weight, part content contains (C) 1 1 Ingredient foaming agent 0 1, 1, 15 parts by weight 4 Liquid crystal polyester 彳 Creamer M 物 经 Rong i 1 copy Paper size applies to China National Standard (CNS) A4 specification (210X 297 mm) 38 38701 A7 B7 Printed by the Consumer Cooperatives of the Central Standards Bureau of the Ministry of Economic Affairs 5. Description of the invention 1 I Shaped and made 〇1 1 The above foaming agent Depending on 0, an appropriate type 1 1 is selected from commercially available foamed osmium and used. Specific examples of the foaming agent include sulfonate sulfonate hydrogen mm 1 I acid sulfonate m sodium sodium boride β nitrogen Azoamine acyl amide (please read below 1 or ADCA for short), azobiscarboxylic acid amine ( Hereinafter, or abbreviated as AB FA, read back 1 1 I) Λ azobisisobutyl (hereinafter referred to as AZDA), N, K 1 — Note of mononitropentafluorene 1 1 Abbreviated as DPT), Ν, Ν ϊ dinitroso-N, N t · di ψ terms and then 1 1 methylphthalic acid amine Λ benzenesulfon m 醯 胼 (hereinafter or simply BS Η), p- A fill in * Jiu Jinyi benzenesulfonium m (hereinafter referred to as TSH), P, P f — vaporized bisbenzenesulfon m m hydrazine Page 1 1 (hereinafter or referred to as 0 BS Η), p-toluene Amidocarbazone (hereinafter referred to as TSSC), 3-diphenyldiamine, and the like. 1 1 Also »In the present invention, it is also possible to use a gas as a foaming agent to make a foam staple | molded article. At this time, it is necessary to disperse the gas uniformly in the molten resin to perform a specific example of the above-mentioned gas am foam treatment. For example, there are M gas two gasification m, carbon gasification 1 1 I compound gasification m fluorine compounds and other C 1 1 foaming agent types are selected depending on the molding processing temperature of the resin composition from the decomposition temperature of the 1 foaming agent to be close to The above molding processing temperature is selected as appropriate. 1 is preferred. 0 1 1 The resin is not fully melted. * When the foaming agent is decomposed i or resin I 1 gold. Melting occurs when the decomposition of the foaming agent does not progress sufficiently. Foam moldings may appear 1 1 Poor appearance or non-uniform bubble diameter to form foamed moldings, etc. 1 1 Disadvantages C 1 1 1 The present invention can provide heat resistance ff Different liquid crystal polyester resin m The hair of the product 1 1 Foam molding c should be decomposable at high temperature-Foaming foaming agent of which 1 1 This paper size applies Chinese National Standard (CNS) Λ4 specification (2 丨 0X297 (Mm) 39 3 8 7 0 1 'r 459037 A7 _____B7 V. Description of the invention (38) The use of potassium sulfonate, APBA, trihydrazine triazine, ADCA, DPT, OBSH, TSSC and other foaming agents is the most suitable. The foaming agent used in the present invention is M. Based on a total of 100 parts by weight of the components (A) and (B), using 0.1 to 15 parts by weight as appropriate. C When the amount of the blowing agent is less than 0.1 parts by weight. When the foaming effect exceeds 15 parts by weight, the appearance of the foam is poor, and the strength is also reduced, which is not desirable. In the present invention, the liquid crystal polyester resin composition can exhibit excellent film-forming processability, softness, gas barrier properties, and heat-shielding properties. Although the reason is unknown, it is speculated that the liquid crystal polyester of the component (a) and B) Caused by some reactions between the components of the oak. The present invention is described in detail by examples. The examples are merely examples, and therefore, the scope of the present invention is not limited by the examples and need not be explained. (1) The liquid crystal polyester (i) of the component (i) is fed into p-acetoxybenzoic acid (10.8 ks, 6 0 ο ο 1 ), Terephthalic acid (2.49 kg, printed by the Consumer Cooperative of the Central Standards Bureau of the Ministry of Economic Affairs (please read the precautions on the back before filling out this page) 15 |! 1〇〗), isophthalic acid ( 0.01 (8,511〇1) and 4,4'-diethylfluorenylbiphenyl (5.45kg, 20.2ιβ〇1), then, under the conditions of the radon gas, it was stirred down and heated to 330t to polymerize for 1 hour. During the reaction Polymerization was carried out under strong M stirring while removing by-product acetic acid. Then the reaction bar was gradually cooled, and the obtained polymer was taken out of the reaction bar at 200T. The obtained polymer was produced by Hosokawa Torushima Corporation. The mill is pulverized into granules of less than 2.5 microns. Then, under the condition of nitrogen blanket in a rotary mill, the Chinese paper standard (CNS) A4 size (2! 0 × 297 mm) is applied at 28 ° at 40 38 7 0 1 /] ^ (2 nq 7 A7 B7 V. Description of the invention (39) After processing for 3 hours, the flow temperature is 3 2 4 ° C. The above-mentioned flow temperature of the unit is a wholly aromatic polyester e. The above-mentioned flow temperature refers to a type of high-temperature flow tester CPT-500 made by Shimadzu Shimadzu Corporation. Under load, when extruded from a nozzle with an inner diameter of 1, mnt and a length of 10 mm, the melt viscosity shows the temperature at 48000 poise. C The above-mentioned liquid crystal polyester obtained by (A-1) for short. Under pressure, the optical anisotropy is displayed when it is above 340 1. The repeating structural unit of liquid crystal polyester (A-1) is as follows: (Please read the precautions on the back before filling this page)

、1T 經濟部中央標準局員工消費合作社印製 15 : 5:20 .(ii)於備有梳形攙拌翼之聚合反_槽中.饋入對-羥 基苯甲酸（16,6kh, 12. Imol)及6-羥基-2-萘甲酸（8,4kg, 4,5B〇丨）以及醋酐（18.6kg, 18.2ιβο1),然後在籠罩氮氣中 攪拌下升溫，在320Τ下反喔1小時，然後在2.0t〇rr·之減 壓下，於3 2 0 t、聚合反應〗小時。反應中繼鑛排出所副産 本紙張尺度適用中國國家標準（CNS ) A4規格（210 X 297公釐） 4 1 3 8 70 1 …， A7 B7 五、發明説明（40)Printed at 15: 5:20 by the Consumer Cooperatives of the Central Standards Bureau of the Ministry of Economic Affairs, 1T. (Ii) In a polymerized counter-tank with comb-shaped mixing wings. Feed p-hydroxybenzoic acid (16, 6kh, 12. Imol) and 6-hydroxy-2-naphthoic acid (8,4kg, 4,5B〇 丨) and acetic anhydride (18.6kg, 18.2ιβο1), and then heated under stirring in a blanket of nitrogen, and reacted at 320T for 1 hour, Then, under a reduced pressure of 2.0 t rr ·, the polymerization reaction was carried out at 3 2 0 t for 1 hour. By-products from the reaction relay mine discharge This paper size applies Chinese National Standard (CNS) A4 specifications (210 X 297 mm) 4 1 3 8 70 1…, A7 B7 V. Description of the invention (40)

的乙酸於反應系外。然後逐漸冷却反應系.在〗80它下將 製得的聚合物取出反應系外C 所得的聚合物按上述（i )項所示相同方法粉碎後.在 旋轉茁中籠罩氮氣條件下以2 4 0 t)處理5小時，而得流動 溫度為2 7 0 Π ,具有下記重複結構單位之粒子狀全芳族聚 酯，並以（甲-2)簡稱所得該液晶聚酯。該聚合物在加壓下 ,280t以上時顯示光學各向異性。 液晶聚酯（甲~2)之重複結構單位如下所示： (請先閱讀背面之注意事項再填寫本頁)Of acetic acid outside the reaction system. Then the reaction system is gradually cooled. The polymer obtained is taken out of the reaction system outside C under 80, and the polymer obtained is pulverized according to the same method as shown in item (i) above. Under a condition of nitrogen in a rotary mill, 2 4 0 t) treatment for 5 hours to obtain a particulate wholly aromatic polyester having a flow temperature of 270 0 Π, having the following repeating structural unit, and the liquid crystal polyester obtained by (A-2) for short. The polymer exhibits optical anisotropy at pressures above 280t. The repeating structural unit of liquid crystal polyester (A ~ 2) is as follows: (Please read the precautions on the back before filling this page)

經濟部中央標率局負工消費合作社印製 (i i ί )使用U n丨c h i c a公司製造的液晶聚酯樂透朗 L C - 5 Ο Ο Ο ,該液晶聚酯之主要原料成分為聚對苯二甲酸乙 二酯及對-羥基苯甲酸。下文中簡稱此聚合物為（甲-3)。 (2> (乙）成分之（甲基）丙烯酸酯-乙烯-不飽和羧酸酯橡 曝： (U桉照日本恃開昭61-127709號公報中實施例5所 記載方法製得丙烯酸甲酯/乙烯/甲基丙烯酸縮水甘油基 酯=510/3 8.7/2.3(重量比），孟納粘度為15之橡_。上 述孟納粘度乃按照日本工業規格JIS K 6 3 00在100X1下用大 轉子測定而得之值β本橡瞟在下文中或簡稱為乙-1。 本紙張尺度適用中國國家標準（CMS ) Α4規格（210Χ297公釐） 42 3 8 7 0 1 經濟部中央標準局員工消費合作社印製 A7 B7 五、發明説明（41 ) (ii)按照日本特開昭6 1-127709號公報中實施例5所 記載方法製得丙烯酸甲酯/乙烯/甲基丙烯酸縮水甘油基 酯=5 6 . 0 / 4 0 . 7 / 3 , 3 (重量比丨，孟納拈度為1 2之橡_。本 橡膠在下文中或簡稱為乙-2。Printed by the Central Standards Bureau of the Ministry of Economic Affairs of the Consumer Cooperative (ii ί) uses the liquid crystal polyester Lotto LC-5 Ο Ο Ο manufactured by Unica Corporation. The main raw material component of the liquid crystal polyester is polyparaphenylene terephthalate. Ethylene formate and p-hydroxybenzoic acid. This polymer is hereinafter referred to as (A-3). (2) (B) Component (meth) acrylate-ethylene-unsaturated carboxylic acid ester rubber exposure: (U) According to the method described in Example 5 of Japanese Patent Application Laid-Open No. 61-127709, methyl acrylate was prepared. / Ethylene / glycidyl methacrylate = 510/3 8.7 / 2.3 (weight ratio), rubber with a Menner viscosity of 15. The above Menner viscosity is larger than 100X1 in accordance with Japanese industrial specifications JIS K 6 3 00 The value obtained from the measurement of the rotor β This rubber 瞟 is hereinafter referred to as B-1 for short. This paper size is applicable to the Chinese National Standard (CMS) A4 specification (210 × 297 mm) 42 3 8 7 0 1 Staff Consumer Cooperative of the Central Standards Bureau of the Ministry of Economic Affairs Print A7 B7 5. Description of the invention (41) (ii) Prepare methyl acrylate / ethylene / glycidyl methacrylate according to the method described in Example 5 of Japanese Patent Application Laid-Open No. 6 1-127709 = 5 6 0/4 0. 7/3, 3 (weight ratio 丨, the rubber with a Menner's degree of 1 2 _. This rubber is hereinafter referred to as B-2.

(i ί i )按照日本特開昭6 - 1 2 7 7 0 9號公報中實施例 5所記載方法製得丙烯酸甲酯/乙烯，/甲基丙烯酸縮水甘 油基酯= 52·5/45·0/2·5(重量比），孟納粘度為20之橡_ 。本橡膠在下文中或簡稱為乙-3C (ίν)含環氣基之丙烯酸酯条橡_ (日本Zean公司製造 Nipol AR31:孟納拈度Π0011)為36)。下文中簡稱之為 乙-4。 (V )含環氣基之丙烯酸酯糸橡曙（日本z e a η公司製造 N i ρ 〇丨A R 5 1 :盂納粘度（1 0 0 )為5 5 ) e下文中簡稱之為 乙-5。(i ί i) According to the method described in Example 5 of Japanese Patent Application Laid-Open No. 6-1 2 7 7 0 9, methyl acrylate / ethylene, / glycidyl methacrylate = 52 · 5/45 · 0/2 · 5 (weight ratio), rubber with a Menner viscosity of 20. This rubber is hereinafter referred to as B-3C (ίν) ring-containing acrylate acrylic rubber (Nipol AR31 manufactured by Japan Zean Co., Ltd .: Menger Π0011) as 36). Hereinafter referred to as B-4. (V) Acrylic acid ester containing ring gas group (N i ρ 〇 丨 A R 5 1 manufactured by Japanese company z e a η): The nano-viscosity (100) is 5 5) e is hereinafter referred to as B-5.

(vi) Kumpulan Guthrie BHD公司製品，環氣化天然 橡_ ENR25,下文中或簡稱之為乙-6C (νίΠ環氣化苯乙烯-丁二烯嵌段共聚合物（Daicai化 學工業公司製品，epofend A1005: 丁二烯/苯乙烯= 60/40,重量比）。下文中簡稱之為乙-7。 (3 )射出成形物之物性潮定方法 拉伸物性：製成ASTM4號拉伸啞鈴形試依據ASTM D63 8所記載方法_定抗拉強度，伸長率。 艾佐德衝擊試驗（Izod impact test):按照日本工業 標準JIS K7110所示，以缺口試H(厚度為3.2βιβι)在室溫及 ----------1------ΪΤ------拉丨 (請先閱讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標準（CNS ) A4規格（210X297公釐） 43 3 8 7 0 1 經濟部中央標隼局員工消費合作社印製 A7 B7 五、發明説明（42 ) -3 Ο 下進行衝擊試驗。 硬度：依據/\ S T Μ 0 7 8 5所示方法，測定其洛克威爾硬 度（Rockwel丨hardness,以I?表示其值）。 負載撓曲溫度（TDUL):製成TDUL測定用試片（長度 1 2 7 π a X 寛度 1 2 · 7 η η X 厚度 6 . 4 ra οι),依據 A S T H D 64 8 所示 方法测定其T D U U負載為1 8 . ¢5 k g )。 (4 )薄膜物性測定方法 透氣率：依照JiS K7126 A法（壓差法）在20t條件下 潮定。其表示單位為cc/ia2，24hr· latnt。 水蒸汽透過率：依照JIS Z0208所示方法（杯法）在 40 相對濕度90%之條件下測定。其表示箪位為g/n)2. 2 4 h r * 1 a t m 〇 又，氣透氡率及水蒸汽透過率均換算為薄膜厚度 2 Γ> //_ m下求得e 拉伸物性：依據JIS Z1727所示方法製成2號形試Η, 測定縱向（HD)及横向（TD)之拉伸物理c 耐摺曲性試驗：按照薄膜積層材料之縱向及横向方向 各自裁切試料，分別使用東徉精機公司製HIT耐摺曲性試 驗機（Folding Endurance tester MIT-D塑）.依據 JISP-8U5所示方法，在負載lkgf,摺曲角度135度，摺曲 面曲率半徑liain，摺曲速度每分鐘175次，進行耐摺曲性試 驗，進行至薄膜裂斷為止，求得摺曲次數。 摺曲疲勞針孔試驗：使用東洋精機公司製之G e 1 b 〇 1'1〇¥16510「5〇〇〇83型，將薄膜固定後，以摺曲速率4〇「91!1 (請先閲讀背面之注意事項再填寫本頁) 訂 本紙張尺度適用中國國家標準（CNS ) Λ4規格（210 X 297公釐） 44 38 7 0 1 A7 B7 經濟部中央標準局員工消費合作社印製 五、 發明説明（43 ) 1 1 進 行 薄 膜 摺 曲 1 0 0 0 次 t 然 後 將 薄 膜放 置 於 白 紙 上，塗 布 墨 1 I 水 於 該 薄 膜 上 1 再 按 照 下 列 標 準 評估 摺 曲 疲 勞 針孔性 0 1 1 I 〇 示 薄 膜 下 之 白 紙 上 未 染 有 墨水 0 ^--N 請 先 閱 讀 1 1 X 示 薄 膜 下 之 白 紙 上 染 有 墨 水。 1 表 面 張 力 • 按照J IS K6768所示方法， 在薄膜上塗布 背 之 1 t 以 曰 本 和 光 純 藥 公 司 製 造 的 濕 濡 試藥 i 然 後 依 據濕儒 試 驗 注 意 φ 1 1 法 求 得 薄 膜 之 表 面 張 力 0 又 該 測 定分 成 未 處 理 薄膜， 以 及 項 再 ik t L, 使 用 曰 本 春 0 電 氣 公 司 製 電 犟 處 理機 以 1 . 1 K W输出功率， 寫 本 頁 1 表 面 處 理 就 其 處 理 後 立 卽 及 經 4個 星 期 後 之 薄膜測 定 0 、« 1 I (5 ) 射 出 成 形 及 薄 膜 之 成 形 1 1 1 按 表 1 中 所 記 載 組 成 將 各 組 成分 及 安 定 劑 同時使 用 韓 1 1 蘇 U 合 機 混 合 後 再 藉 曰 本 製 鋼 公司 製 TEZ- 30型雙軸擠 壓 訂 1 機 > 在 擠 茼 設 定 溫 度 2 δ 0 〜3 5 0 υ (實施例1 3及比較例 1 I 1〜4刖 採用350 TC， 實施例4 5及比較例5 6則採用3 1 0 υ 1 1 ， 實 施 例 6 比 較 例 7 則 採 用 2 80 1)) 螺 桿 旋 轉數2 0 0「 pm 1 條 件 下 混 練 * 而 得 錠 粒 樹 脂 組 成 物， 提 供 射 出 成形及 薄 膜 1 I 成 形 用 r.) 射 出 成 形 Α» ·Γρ 二*A 0¾ 使 用 曰 精 樹脂 工 業 公 司 製之 1 1 I PS40E5ASE型射出成形機， 在成形溫度280 35 0 t： (¾ 施 例 1 1 1〜3及 tb 較 例 1 ^ - 4則 採 用 3 5 0 °C , 酋施例4 5及比較例 i i 5〜6則 採 用 310t〕， 實施例6 及比較例7 則採用2f40 t ), 1 i 模 具 溫 度 80 下 射 出 成 形 1 提 供 測定 試 Φα 用 途 ,其結 果 示 1 1 於 表 1 C 1 I 1 例 1 . 2苻（+,較例1 3 1 m 練 所 得 的 鍵 粒 組 成 物 * 利 用2 0 m it 1直 徑 之 單軸擠 壓 她 Xm i 1 4 5 本紙張尺度適用中國國家標準（CNS ) A4现格（210 Χ297公釐） 3 8 7 0 1 459037 A7 B7 五、發明説明（44 ) (曰本田邊塑_機槭公司製品），擠筒及T模設定在350C, 由寬度為IOOhiid,縫隙間距為0.3〜0.8idb之T模擠壓，由 定型棍捲取製成未拉伸薄膜。此薄膜藉雙軸拉伸試驗設備 (東洋精機公司製品），在拉伸溫度3 3 0Γ,拉伸倍率（MDX TD)為2·7Χ2.7條件下同時進行雙軸拉伸，由各個試料分 別製得厚度為1 δ〜2 9 // m之薄膜，再進行各項物性測定e 其評估結果不於表1. ： 窗旆例：¾〜.卜卜較例4〜7 按照表1中所示組成而得的錠粒組成物為試料，利用 備有圓筒形模頭的45®!«直徑之單軸擠壓機s擠筒溫度設定 在290〜352 °C(實施例3及fcb較例4為352C,實施例4〜5 及比較例5〜6為3 1 0 t ,實施例6及比較例7為2 9 0 ), 以旋轉速度δ 0 r p in進行熔融混練.由直徑1 0 0 ra nt ,模唇間距 為模頭設定溫度為290〜352t(實施例3及比較例 4為352它，實施例4〜5及比較例5〜6為31〇υ,宵施例6 及比較例7為2901)之圓筒形模頭向上方擠出熔融樹脂， 該筒狀薄膜中空處壓λ乾燥空氣使膨脹成為筒狀薄膜，繼 之冷却後，經過夾棍以捲取速度每分鐘1 5〜2 0 m ,製得厚 度為1 8〜3 7 μ η之液晶聚酯樹脂組成物薄膜。 .該液晶聚酯樹脂組成物薄膜之縱向捲取方向（Μ I)方向） ,横向捲取方向（TD方向）之拉伸倍率藉壓入乾燥空氣量， 薄膜捲取速度而控制c本試驗中，MD方向之拉伸倍率為 2 . 5〜4 . 0 ,横向方向之吹脹Irb率為4 . 1〜5 . 9。所得的液晶 聚酯樹脂組成物薄膜之物性值合併示於表1 。 4 6 (請先閲讀背面之注意事項再填寫本頁) 訂 經濟部中央標準局員工消費合作社印聚 本紙張尺度適用中國國家標準（CNS ) A4規格（210 X 297公釐） 3 8 7 0 1 (ί - 3 0 3 7 a? Β7 五、發明説明（45 )(vi) Product of Kumpulan Guthrie BHD company, ring gasified natural rubber _ ENR25, hereinafter referred to simply as B-6C (νίΠ ring gasified styrene-butadiene block copolymer (Product of Daicai Chemical Industry Company, epofend A1005: Butadiene / styrene = 60/40, weight ratio. Hereinafter referred to simply as B-7. (3) Physical properties of injection molding. Tide determination method. Stretching physical properties: made into ASTM No. 4 tensile dumbbell test. According to the method described in ASTM D63 8_ determine the tensile strength and elongation. Izod impact test: According to the Japanese Industrial Standard JIS K7110, the notch test H (thickness 3.2βιβι) at room temperature and ---------- 1 ------ ΪΤ ------ Pull 丨 (Please read the precautions on the back before filling this page) This paper size applies to China National Standard (CNS) A4 Specification (210X297mm) 43 3 8 7 0 1 Printed by the Consumer Cooperatives of the Central Bureau of Standards of the Ministry of Economic Affairs A7 B7 V. Description of the invention (42) -3 〇 The impact test is performed. Hardness: according to / ST Μ 0 7 8 The method shown in 5 is used to measure its Rockwell hardness (the value is expressed by I?). Load deflection temperature (TDUL): TDUL measurement test piece (length 1 2 7 π a X Width of the 1 2 · 7 η η X a thickness of 6. 4 ra οι), A S method shown in FIG. 64 8 T H D measured in accordance with its T D U U load 1 8. ¢ 5 k g). (4) Measurement method of film physical properties Air permeability: According to JiS K7126 A method (differential pressure method) at 20t. Its unit is cc / ia2, 24hr · latnt. Water vapor transmission rate: measured in accordance with the method (cup method) shown in JIS Z0208 under a condition of 40% relative humidity 90%. Its position is g / n) 2. 2 4 hr * 1 atm 〇 In addition, the air permeability and water vapor transmission rate are converted into the film thickness 2 Γ > // _ m to obtain e tensile properties: basis JIS Z1727 method was used to make a test piece No. 2 to measure the tensile physical properties in the longitudinal direction (HD) and the transverse direction (TD). HIT Folding Endurance tester MIT-D plastic manufactured by Toyo Seiki Co., Ltd. According to the method shown in JISP-8U5, the load is 1kgf, the bending angle is 135 degrees, the bending radius of the curved surface is liain, and the bending speed is 175 times per minute, a bending resistance test was performed, and the film was cracked to determine the number of bending times. Bending fatigue pinhole test: G e 1 b 〇1'1〇 ¥ 16510 "5000083 model manufactured by Toyo Seiki Co., Ltd. was used, and the film was fixed at a bending rate of 40 ° 91 · 1 (please first Read the notes on the back and fill in this page again.) The size of the paper used for this edition applies to the Chinese National Standard (CNS) Λ4 specification (210 X 297 mm) 44 38 7 0 1 A7 B7 Explanation (43) 1 1 Perform film bending 1 0 0 0 times t then place the film on white paper, apply ink 1 I water on the film 1 and evaluate the bending fatigue pinhole property according to the following criteria 0 1 1 I 〇 The white paper under the film is not stained with ink 0 ^-N Please read 1 1 X The white paper under the film is stained with ink. 1 Surface tension • Apply the back of 1 to the film according to the method shown in J IS K6768 t Use the wet test reagent i manufactured by Japan Wako Pure Chemicals Co., Ltd. and then follow the wet test to pay attention to the φ 1 1 method to obtain the surface tension of the film. The measurement was divided into an untreated film and an item ik t L. The output was 1.1 KW using an electric ballast processing machine made by Harumoto Electric Co., Ltd., written on this page. Weekly film measurement 0, «1 I (5) Injection molding and film molding 1 1 1 Mix the components and stabilizers with the composition described in Table 1 using the Korean 1 1 Su U machine, and then borrow TEZ-30 Model Biaxial Extrusion Binding Machine 1 made by Ben Steel Co., Ltd. > Set temperature 2 δ 0 ~ 3 5 0 υ at Extrusion (Example 1 3 and Comparative Example 1 I 1 to 4) using 350 TC, Example 4 5 and Comparative Example 5 6 use 3 1 0 υ 1 1, Example 6 Comparative Example 7 use 2 80 1)) Number of screw rotations 2 0 0 ″ pm 1 to knead * to obtain a pellet resin composition, Provide injection molding and film 1 I for molding r.) Injection molding A »· Γρ 2 * A 0¾ Use 1 1 I PS40E manufactured by Seiko Resin Industry Co., Ltd. 5ASE injection molding machine, at a molding temperature of 280 35 0 t: (¾ Example 1 1 1 ~ 3 and tb Comparative Example 1 ^-4 uses 3 50 ° C, Example 4 5 and Comparative Example ii 5 ~ 6 uses 310t], Example 6 and Comparative Example 7 use 2f40 t), 1 i injection molding at a mold temperature of 80 1 provides measurement test Φα application, the results are shown in Table 1 C 1 I 1 Example 1.2苻 （+, Comparative example 1 1 1 m Key bond composition ** Use 20 m it 1 diameter uniaxial extrusion Xm i 1 4 5 This paper size applies Chinese National Standard (CNS) A4 210 x 297 mm) 3 8 7 0 1 459037 A7 B7 V. Description of the invention (44) (said Honda edge plastic_machine maple company products), the extruder and T-die set at 350C, the width is 100OOid, the gap distance is 0.3 T-die extrusion of ~ 0.8idb, rolled by a shaped stick to make an unstretched film. This film was subjected to biaxial stretching at the same time under the conditions of a stretching temperature of 3 3 0Γ and a stretching ratio (MDX TD) of 2 · 7 × 2.7 by means of a biaxial tensile test device (manufactured by Toyo Seiki Co., Ltd.). A thin film having a thickness of 1 δ to 2 9 // m was prepared, and various physical properties were measured. The evaluation results are not shown in Table 1. Example of window: ¾ ~. Comparative example 4 ~ 7 The ingot composition shown in the composition is a sample. A 45®! «Diameter uniaxial extruder with a cylindrical die is used to set the extruder temperature to 290 to 352 ° C. (Examples 3 and fcb compare Example 4 is 352C, Examples 4 to 5 and Comparative Examples 5 to 6 are 3 1 0 t, and Example 6 and Comparative Example 7 are 2 9 0), melt-kneading is performed at a rotation speed δ 0 rp in. From the diameter 1 0 0 ra nt, die lip distance is 290 ~ 352t for die set temperature (Example 3 and Comparative Example 4 are 352, Example 4 ~ 5 and Comparative Examples 5 ~ 6 are 31 °, Example 6 and comparison The molten resin was extruded upwards from the cylindrical die of Example 2901). The hollow of the cylindrical film was pressurized with λ dry air to expand into a cylindrical film. After cooling, it was passed through a pinch at a winding speed of 15 ~ 2 0 m to obtain a liquid crystal polyester resin composition film having a thickness of 18 to 37 μηη. The stretching ratio of the liquid crystal polyester resin composition film in the longitudinal winding direction (M I direction) and the transverse winding direction (TD direction) is controlled by the amount of dry air and the film winding speed. The stretching ratio in the MD direction is 2.5 to 4.0, and the inflation Irb ratio in the lateral direction is 4.1 to 5.9. The physical properties of the obtained liquid crystal polyester resin composition film are shown in Table 1 together. 4 6 (Please read the notes on the back before filling out this page) Order the printed papers of the Consumer Cooperatives of the Central Bureau of Standards of the Ministry of Economic Affairs. The paper size is applicable to the Chinese National Standard (CNS) A4 (210 X 297 mm) 3 8 7 0 1 (ί-3 0 3 7 a? Β7 V. Description of the invention (45)

i2Fff;git«H i3ffi对 ibwH 經濟部中央標隼局員工消費合作社印製 l、t?.s!J5e3§n, EPDH esp「neE50e 划«怼神U00d)"77 撇技闽!輥，B ο n d f si s t 7 L (iNlixiaElis^-aa/-ffl^al^as^^tiiimainCJJT/so/^llflllit.as^flwiokiLcl^) 撕姣alisn.m^砷逋 ssssikasend F-101 MFR = 0.28(g/Ionin) 比較例7 比較例6 1 卜b較例5 比較例4 實施例6 實施例5 實施例4 宵施例3 比較例3 比較例2 1吐較例ί 實施例2 荠施例1 —~ 一；t> Ο 1 OC-J Co 3» CO 1 Ni A-2 100 CT：> -ΟΙ ο 私i Co 00 ί rs? Oo^s. Oo 1 ro o i h_l coa> N> 1 CO^> Λ-1 100 〇〇> ro 1 A-l 91 £ 〇 Ο ο ο rooc 03 1 CO PO 1 ?22 00 J Ο 〇 ο r—CO 〇〇 l· H-l iDCC Λ 03 组成 ί重量％) 〇 i* 一 Cs? ,Ν) ο 仆 Lo 〇 0 〇 〇 仆 ►—(Ό c〇 二 ο 〇 o 其他 CO ο Co 〇〇 ΟΠ Ul s 0〇 00 cn CO 231 ^ L* η w m g ϊ « 00 vS1 s » n m Br a 9π 兹 h? Μ CO CO PO oo tj\ fO ¢-^ r OJ CO CO ΟΪ 3QV. 1150 1430 1700 1090 1230 I860 2080 丨™ ㈣ ]240 1610 1740 1720 (kg/cR2) 抗拉強度 1 拉渖試驗 4^· CO 5.9 1—* ο 5.δ ¢0 'j 19.8 1—« -0 0 〇n c〇 L»J i*3 CJ1 <〇 9.8 (¾) 伸長率 σ> οο 105 R 105 yfj 09 y<3 ΟΪ JO 00 00 00 CD Z^D ¢/1 ¢0 oc R 100 ί R 100 <0 y〇 <J3 0〇 硬度 不能成膜 不能成膜 不能成糗 不能成膀 〇J fs5 CO ro ¢0 ¢0 1不能成膜 不能成11 N> 厚度 υ % Η$ 1 ) 1 1 〇 <LH 0 〇 a 〇 A 1 1 〇 〇 ¢-0 轉 w綱 1 1 1 1 00 〇 o 0 CO 〇 1 1 〇 00 0 透氣率 \ cc/w2 24br . at·) t t 1 1 1840 2580 ! ! 3130 2030 2290 1 1 2240 2δ7〇 <P 苕 m 1 1 ί 1 1590 2210 2880 1940 1980 1 1 1870 2350 1 1 i 1 6.1 0 CO oo Οϊ CO 1 1 〇 〇〇 ο w g 伸長苤〖％) 1 1 f 1 ! 8.3 ZTi 15.3 <_n 1 1 〇〇 ro ΟΊ * 1 .t#先聞#背面之 訂 本紙張尺度適用中國國家標準（CNS ) A4規格（210 X 297公釐） 47 38701i2Fff; git «H i3ffi prints l, t? .s! J5e3§n, EPDH esp" neE50e delineation «怼 神 U00d) " 77 to ibwH employees of the Central Bureau of Standards of the Ministry of Economic Affairs " ο ndf si st 7 L (iNlixiaElis ^ -aa / -ffl ^ al ^ as ^^ tiiimainCJJT / so / ^ llflllit.as ^ flwiokiLcl ^) tear alisn.m ^ arsenic ssssikasend F-101 MFR = 0.28 (g / Ionin) Comparative example 7 Comparative example 6 1 bb Comparative example 5 Comparative example 4 Example 6 Example 5 Example 4 Example 3 Comparative example 3 Comparative example 2 Example 1 Example 2 荠 Example 1 — ~ I; t > Ο 1 OC-J Co 3 »CO 1 Ni A-2 100 CT: > -ΟΙ ο private i Co 00 ί rs? Oo ^ s. Oo 1 ro oi h_l coa > N > 1 CO ^ & gt Λ-1 100 〇〇 > ro 1 Al 91 £ 〇〇 ο rooc 03 1 CO PO 1? 22 00 J Ο 〇ο r—CO 〇〇l · Hl iDCC Λ 03 Composition ί wt%) 〇i *一 Cs ?, Ν) ο 〇Lo 〇0 〇〇〇► —— (Ό c〇 二 ο 〇o Other CO ο Co 〇〇〇Ο Ul s 0〇00 cn CO 231 ^ L * η wmg ϊ «00 vS1 s» nm Br a 9π z h? Μ CO CO PO oo tj \ fO ¢-^ r OJ CO CO ΟΪ 3QV. 1150 1430 1700 1090 1230 I860 2080 丨 ™ ㈣] 240 1610 1740 1720 (kg / cR2) Tensile strength 1 Tensile test 4 ^ · CO 5.9 1— * ο 5.δ ¢ 0 'j 19.8 1— «-0 0 〇nc〇L» J i * 3 CJ1 < 〇9.8 (¾) Elongation σ > οο 105 R 105 yfj 09 y < 3 ΟΪ JO 00 00 00 CD Z ^ D ¢ / 1 ¢ 0 oc R 100 ί R 100 < 0 y〇 < J3 0〇 Hardness can not be formed film can not be formed film can not be formed 糗 J fs5 CO ro ¢ 0 ¢ 0 1 cannot be formed film cannot be formed 11 N > thickness υ% Η $ 1) 1 1 〇 < LH 0 〇 a 〇A 1 1 〇〇 ¢ -0 Turn to W 1 1 1 1 00 〇o 0 CO 〇1 1 〇 0 0 Air permeability \ cc / w2 24br. at ·) tt 1 1 1840 2580!! 3130 2030 2290 1 1 2240 2δ7〇 < P 苕 m 1 1 ί 1 1590 2210 2880 1940 1980 1 1 1870 2350 1 1 i 1 6.1 0 CO oo 〇ϊ CO 1 1 〇〇〇ο wg elongation (%) 1 1 f 1! 8.3 ZTi 15.3 < _n 1 1 〇〇ro 〇Ί * 1 .t # 先 闻 # The size of the paper on the back of the paper applies the Chinese National Standard (CNS) A4 (210 X 297 mm) 47 38701

7 7 A B 經濟部中央樣準局員工消費合作社印製 五、發明説明（46 ) 表1(績) 薄 膜 物 性 耐摺由 &試驗 摺曲疲勞 表 面張力（dyn/cm) HD TD 針機試驗 未處理 處理後立即*4 四星期後 實施例1 >100,000 >100,000 〇 38 >40 >40 實施例2 >100,000 >100,000 〇 38 >40 >40 比較例1 一 — — — 一 — 比較例2 — — — — 一 tb較例3 >100,000 >100,000 〇 38 >40 >40 實施例3 >100,000 >100,000 〇 38 >40 >40 實施例4 >100,000 >100,000 〇 38 >40 >40 實施例5 >100,000 >100,000 〇 38 >40 >40 實施例6 >100,000 >100,000 〇 38 >40 >40 比較例4 — — — 一 — — 比較例5 — 一 — — 一 一 比較例6 — — 一 — 一 一 比較例7 — — — — — — *4電犟處理 (請先閱讀背面之注意事項再填寫本頁)7 7 AB Printed by the Consumer Cooperative of the Central Bureau of Procurement, Ministry of Economic Affairs 5. Description of the invention (46) Table 1 (achievement) The physical properties of the film are resistant to bending & test Fatigue Surface Tension (dyn / cm) Immediately after the treatment * 4 Four weeks later Example 1 > 100,000 > 100,000 〇38 > 40 > 40 Example 2 > 100,000 > 100,000 〇38 > 40 > 40 Comparative Example 1 I — — — 1 — Comparative Example 2 — — — — One tb Comparative Example 3 > 100,000 > 100,000 〇38 > 40 > 40 Example 3 > 100,000 > 100,000 〇38 > 40 > 40 Example 4 > 100,000 > 100,000 〇38 > 40 > 40 Example 5 > 100,000 > 100,000 〇38 > 40 > 40 Example 6 > 100,000 > 100,000 〇38 > 40 > 40 Comparative Example 4 — — — One — — Comparative Example 5 — One — — One One Comparative Example 6 — — One — One One Comparative Example 7 — — — — — — * 4Electric treatment (please read the precautions on the back before filling this page)

*1T 本紙張尺度適用中國國家標準（CMS ) A4規格（210X 297公釐） 3 8701 48 經濟部中央標準局員工消費合作社印製 A7 B7五、發明説明（47 ) 甯旃例7〜ίί . 屮較例8〜1 1 按照表2所示組成之各組成物以韓蘇混合機混合，使 用日本製鋼公司製ΪΕΖ-30型之雙軸擠壓機.依據表2所示 擠筒溫度，螺桿旋轉數ISOrpra條件熔融混練而得組成物 該組成物用日精樹脂工業公司製P S 4 0 E 5 A S E型之射出成形 機，依據表2所記載之擠筒溫度，模具溫度進行射出成形 Ο 該組成物之錠粒物利用備有圓筒形模頭之30ntm直徑之 單軸擠壓機f依據表2所記載之擠筒溫度，旋轉速度 SOrpinT培融混練，由直徑50ram,模唇距離1.2mm,按照 表2記載之模頭設定溫度下的圓筒形楔頭朝上方擠_熔融 樹脂，該筒狀薄膜之中空處壓入乾燥空氣使筒狀薄膜膨脹 ，繼之冷却後經過夾棍，以捲取速度每分鐘9η牽引而得液 晶聚酯樹脂組成物薄膜。 該液晶聚酯樹脂組成物薄膜之縱向捲取方向，及横向 方向之拉伸倍率，藉由壓入之乾燥空氣量.薄膜捲取速度 而控制之。該捲取速度，縱向方向之拉伸倍率，横向方向 之吹脹比率以及薄膜厚度示於表2 。所得的液晶聚酯樹脂 組成物薄膜之物性示於表3 。 ' 又，薄膜之熱分解溫度利用曰本島津製作所製造之熱 解重量分析機（Thermograuiffietic Ana丨yzer TGA-50型）， 就大約l〇M之薄膜，在籠罩氮氣中每分幢之升溫條件 下加熱，求得開始分解之溫度c ----------^ 、------訂—------^ I (請先閱讀背面之注意事項再填寫本頁) 本紙張尺度適用中國囤家標準（CNS ) Λ4規格（210X 297公釐） 4 9 38 7 0 1 經濟部中央標準局員工消費合作社印繁 在 59 Ο 37 Α7 Β7 五、發明説明（4 8 ) 組成(重童％) 熔融混 練條件 射出成 形條件 成 膜 條 件 成分 成分 其他 擠筒設 擠筒設 擠筒設 擠筒設 MD拉伸 吹脹 定溫度 定溫度 定溫度 定溫度 (甲） (乙） 成分 (V) (V) (V.) (V.) 倍率 比率 實施例7 甲-1 乙-4 78 22 0 350 350 350 350 14.1 4.4 比較例8 甲-1 100 0 0 350 350 350 350 不能成膜 — 比較例9 甲-1 ill 78 0 22 350 350 350 350 8.4 3.7 實施例8 甲-2 乙-5 92 δ 0 310 310 310 310 10.7 6.1 實施例9 甲-2 乙-5 68 32 0 310 310 310 310 7.6 4.8 比較例10 甲-2 100 0 0 310 310 310 310 不能成膜 一 比較例11 甲-2 ί： 2 92 0 8 310 310 310 310 不能成膜 $1住友化學工業公司製品，乙烯-甲基丙烯酸縮水甘油基酯共聚合物，Bondfast_2 .C(組成：乙烯/甲基丙烯酸縮水甘油基酯=94/6重量比，MFRdgOt，2.16kg> = 3g/10min.) *2住友化學工業公司製品，乙烯-丙烯-二烯共聚物橡_，esPrent Ε301(盂納粘度 (1001)=55)0 (請先閱讀背面之注意事項再填寫本頁) -丄 本紙張尺度適用中國國家標率（CNS ) A4规格（21〇 X 297公釐） 50 38 7 0 1* 1T This paper size applies the Chinese National Standard (CMS) A4 specification (210X 297 mm) 3 8701 48 Printed by the Consumers Cooperative of the Central Standards Bureau of the Ministry of Economic Affairs A7 B7 V. Description of the invention (47) Example 7 ~ ί. 屮 Comparative example 8 ~ 1 1 Each composition according to the composition shown in Table 2 is mixed with a Korean-Soviet mixer, and a double-shaft extruder made by Japan Steel Co., Ltd. ZEZ-30 is used. According to the extrusion barrel temperature shown in Table 2, the number of screw rotations ISOrpra The composition was obtained by melt-kneading under conditions. The composition was injection-molded using a PS 4 0 E 5 ASE type injection molding machine manufactured by Nissei Resin Industry Co., Ltd. according to the extrusion barrel temperature and mold temperature described in Table 2. 0 Use a single-shaft extruder with a diameter of 30 ntm equipped with a cylindrical die head. Mix and knead according to the extruder temperature and rotation speed SOrpinT described in Table 2. The diameter is 50 ram and the die lip distance is 1.2 mm. The cylindrical wedge at the set temperature of the die head is squeezed upward toward the molten resin. The hollow space of the cylindrical film is pressurized with dry air to expand the cylindrical film. After cooling, the cylindrical film is passed through the clamping rod at a winding speed of 9η per minute. Traction The polyester resin composition film. The longitudinal winding direction of the liquid crystal polyester resin composition film and the stretching ratio in the transverse direction are controlled by the amount of dry air pressed in. The film winding speed. The winding speed, the draw ratio in the longitudinal direction, the inflation ratio in the transverse direction, and the film thickness are shown in Table 2. The physical properties of the obtained liquid crystal polyester resin composition film are shown in Table 3. 'Also, the thermal decomposition temperature of the thin film was measured by a thermogravimetric analyzer (Thermograuiffietic Ana 丨 yzer TGA-50) manufactured by Shimadzu Corporation, and the temperature of each thin film was about 10M under the temperature rising condition of each block in a blanket of nitrogen. Heating, find the temperature at which decomposition starts c ---------- ^, -------- order -------- ^ I (Please read the precautions on the back before filling in this page) This paper size is applicable to China Store Standard (CNS) Λ4 specification (210X 297 mm) 4 9 38 7 0 1 The staff consumer cooperative of the Central Standards Bureau of the Ministry of Economic Affairs is printed at 59 〇 37 Α7 Β7 V. Description of the invention (4 8) (Heavy boy%) Melt-kneading conditions Injection molding conditions Film-forming conditions Ingredients Components Other squeeze cylinders Set squeeze cylinders Set squeeze cylinders Set squeeze cylinders MD Stretch inflation Constant temperature Constant temperature Constant temperature Constant temperature (A) (B) Ingredients ( V) (V) (V.) (V.) Magnification ratio Example 7 A-1 B-4 78 22 0 350 350 350 350 14.1 4.4 Comparative Example 8 A-1 100 0 0 350 350 350 350 No film formation— Comparative Example 9 A-1 ill 78 0 22 350 350 350 350 8.4 3.7 Example 8 A- 2 B-5 92 δ 0 310 310 310 310 10.7 6.1 Example 9 A-2 B-5 68 32 0 310 310 310 310 7.6 4.8 Comparative Example 10 A-2 100 0 0 310 310 310 310 No Comparative Example 11 A-2 ί: 2 92 0 8 310 310 310 310 Cannot form a film $ 1 Product of Sumitomo Chemical Industries, ethylene-glycidyl methacrylate copolymer, Bondfast_2 .C (composition: ethylene / glycidyl methacrylate) Base ester = 94/6 weight ratio, MFRdgOt, 2.16kg > = 3g / 10min.) * 2 Product of Sumitomo Chemical Industry Co., Ltd., ethylene-propylene-diene copolymer rubber, esPrent Ε301 (viscosity (1001) = 55 ) 0 (Please read the notes on the back before filling in this page)-This paper size applies the Chinese National Standard (CNS) A4 specification (21〇X 297 mm) 50 38 7 0 1

經濟、邵中央標準局員工消費合作社印製 、發明説明（49 ) 表3 組域 “重 *%) 射出成 形品物 薄 膜 物 性 成分 成分 其他 性概 厚度 分解開 水蒸氣透過率 透氣率(CC/ID2. (96) (u ») 始溫度 (g/«2,24hr. 24hr.atai) (甲） (Z) 成分 .atm) 實施例7 甲-1 Z-4 78 22 0 241 29 舰 0.4 0.3 bb較例8 甲-1 100 0 0 258 一 一 — — 比較例9 甲-1 η 78 0 22 232 37 427 0.Γ) 0.4 實施例8 甲-2 乙-5 92 8 0 179 18 476 0.4 0.3 菁施例9 甲-2 乙-5 68 31 0 155 43 433 0.4 0.4 比較例K) 甲胃2 100 0 0 183 — — — — 比較例11 甲-2 ¢2 92 0 8 154 — 一 一 一 幻住友化學工業公司製品•乙烯-甲基丙烯酸環氧丙酯共聚物，膨多第12C,(組成：乙烯/ 甲基丙烯酸環氣丙酯=汹/6重量比，KFR(19〇t：，2.16ks)=3g/l〇*in·) 坨住友化學工業公司製品，乙烯-丙烯-二烯烴共聚物楝膠，愛士布職观們尼粘度(loot )=55) 本紙張尺度適用中國國家標準（CNS ) A4規格（2l〇X297公釐） 3 8 7 0 1 -----^-----{------ΪΤ------A _ (請先閱讀背面之注意事項再填寫本頁) A7 B7 經濟部中央標準局員工消費合作社印製 五、 發明説明（ 50 ) 1 1 旃 例 1 〇 11 t-h 較 例 1 2 14 i 按 照 表 4 所 記 載 之 組 成 將 各 成 分 用 韓 蘇 混 ϋ 機 混 合 後 1 1 1 » 使 用 B 本 製 铜 公 司 製 之 TEZ - 30型 之 雄 又 軸 擠 壓 m 调 » 以 表 4 請 閱 if 1 1 所 示 條 件 混 練 1 製 得 樹 m 組 成 物 之 錠 粒 9 提 供 射 出 成 形 及 1 薄 膜 成 形 用 0 射 出 成 形 試 Η 利 用 e 精 樹 脂 I 業 公 司 製 之 背 ιέ 之 1 Ί PS40E5ASE型射出成形機， 依照表4 中所示條件進行射出 注 意 事 1 f 成 形 1 供 測 SAl 用 0 其 結 果 示 於 表 4 〇 項 再 1 覆 蓋 帶 之 成 膜 * 將 樹 脂 錠 粒 Μ 備 有 圓 筒 形 模 頭 之 4 5 si is 馬 本 頁 1 直 徑 之 «ΓΤ rpi 軸 擠 壓 機 1 按 照 表 5 中 所 示 條 件 下 熔 融 混 * 由 1 I 直 徑 5 0 ia m 模 唇 間 距 1 . 5 ϊπ ΙΒ之圓筒形模頭向上方擠壓熔融 1 1 I 樹 脂 ， 壓 入 乾 燥 空 氣 在 該 茼 狀 薄 膜 之 中 空 處 i 使 筒 狀 薄 膜 1 1 訂 1 膨 脹 f m 之 ， 冷 却 後 m ικΧ 夾 棍 而 製 成 液 晶 樹 脂 組 成 物 9 供 覆 蓋 帶 用 t 成 形 為 薄 膜 時 之 吹 脹 比 率 m 向 方 向 之 拉 伸 倍 率 1 1 示 於 表 5 C 1 I 另 外 » 載 物 帶 之 成 膜 可 使 用 覆 蓋 帶 成 膜 時 所 採 用 相 1 同 裝 置 按 照 表 6 所 示 條 件 對 樹 脂 錠 粒 進 行 成 膜 0 所 得 的 1 I 薄 膜 繼 以 楔 壓 成 形 機 » 於250〜300它 下 f 進 行 壓 <h 加 工 i 1 1 1 使 於 薄 膜 上 製 成 長 X 寬 =2 0 in ID > <2 0 m 深為5 01 之 □ 袋 狀 物 1 1 而 製 成 載 物 帶 1 1 壓 化 加 工 後 用 肉 眼 觀 察 外 觀 r 以 薄 膜 上 不 産 生 m 紋 * 1 1 能 精 確 地 成 形 為 P 袋 狀 者 評 估 為 優 良 品 ί ΠΓ 刖 視 為 不 良 品 1 I 0 外 t 加 熱 至 260 〜3 10 t： 的 覆 蓋 帶 壓 粘 於 上 述 壓 花 加 工 i I 後 之 載 物 帶 上 評 估 其 熱 封 性 冷 却 後 用 肉 眼 觀 察 兩 者 界 1 1 I 面 » 界 面 上 無 裂 紋 或 剝 離 而 粘 著 性 良 好 者 視 為 優 良 品 否 1 1 本紙張尺度適用中國國家標準（CNS ) Λ4規格（210 X 297公釐〉 52 3 8 7 0 1 經濟部中央標準局員工消費合作社印製 A7 ____B7_ 五、發明説明（Η ) 刖視為不良品。所得結果示於表6 , 又所得覆蓋帶用，載物帶用之各種薄膜之透氣性，水 蒸汽透過性分別示於表5及表6 , 表4 I - - - - - - ...... ....... —I H 1 -I 冬 II 1 - - --- -- - 1 ml I m - (請先閲讀背面之注意事項再填寫本頁) 組成（重量％) 溶融混練條件 射出成形條件 射出成 形品 物性 成分 成分 其他 擠筒設 螺桿轉 射出成 楔具 TDUL 定溫度 數rpm 形溫度 溫度 (甲） (乙） 成分 1C V V 實施例10 甲-1 乙-1 78 22 0 350 200 350 80 235 比較例12 甲-1 100 0 0 350 200 350 80 265 比較例13 甲-1 η 78 0 22 350 200 350 80 197 實施例11 甲-2 乙-1 92 8 0 290 200 290 80 181 比較例14 甲-2 100 0 0 290 200 290 80 183 Ο住友化學工業公司製品，低密度聚乙烯F-101 本紙張尺度適用中國國家標準（CNS ) Λ4規格（210X 297公釐） 53 3 8 7 0 1 五、發明説明（"2 ) A7 B7 經濟部中央標準局員工消費合作社印製 *1帘对左《3:艄妗到遒卽，蒴输师雑2ITF-101 比較例14 實施例11 比較例13 比較例12 實施例10 I 甲-2 100 1 i甲-2 i 92 -<Ι -Η ΟΟ 1 甲-1 100 00 1 t—i 成分 (甲） ^1 樹脂組成（重量部） 〇 (N 〇〇 1 ο 〇 ^ (N ΓΟ 1 成分 (乙） _1 〇 ο N? ι—* ro 〇 〇 1 其他 成分 292 292 352 352 π 352丨 擠筒 設定 溫度 (t) m 哋 m 满 m 〇0 〇 〇0 ο ΟΟ CC 〇0 螺桿 轉數 ΓΡΒ 1 ! 294 1_ 1 I 1 294 ι_ 354 i_ 354 354 模頭設 定溫度 (V) ………1 1 不能成膜 σ> 不能成膜 不能成膜 ts5 ι 吹脹比率 不能成膜 1_ 〇ϊ 〇〇 1 1 i不能成膜 1_ 不能成膜 -0 | ί 拉伸倍率 i CO 1 1 篇 薄膜厚度 瑚 m m m ί$ 1 ο C?s 1 1 Ο cn CC/CH2 atm. 24hr 透氧度 1 ο 1 1 ο g/ro2 a to. 24hr 水蒸氣 透過度 谢5 ^i^i- ^^^1 .1^1 m HI I tm ml r^n -- -- _ ..... ---- i :、一flJ (請先閱讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標準（CNS ) Λ4規格（210X297公釐） 3 8 7 0 1 459037 A7 B7 五、發明説明（53 ) 經濟部中央標準局員工消費合作社印製 比較例14 實施例11 比較例13 比較例12 實施例10 H-* ΓΠ 〇 ΤΠ Ο 1 ζ〇 -ffi ΓΟ ! ro ^ « OO 1 S s 〇 丄 〇0 1 1—* -1 成分1 1 1 (甲）丨 樹脂組成（重量部） 〇 (N 〇〇 i — o 〇 ro IN N? 1 ι—* 成分 (乙） 〇 o ΓΌ N5 〇 Ο 其他 成分 ΓΟ ς〇 rs5 ro CO PC OJ tn ro W U1 [Ο 05 cn ro Μ m m a m m 寺 oo ο g g 〇〇 〇 g 螺桿 轉數 ΓΡΒ ! .i fO CO ς〇 w iLn CC CJ1 o〇 Cjrj -1 | 模頭設i 定溫度 (它） 1 不能成膜 CJl to 不能成膜 不能成膜 N5 CD -1 丨 吹脹比率 不能成模 私 oo 不能成膜 不能成膜 00 01 拉伸倍率 1 oo I 1 办 ro ΐ: 曰 薄膜厚度 驚 漥 m m 1 o CO 1 1 o cc/cm2 atm. 24hr 1 透氧率 .1 o oo 1 t o 1—* g/m2 atm. 24hr 水蒸氣 透過率 1 良好 1 1 良好 1_ m h贫 1 ^Hl· 1 1 熱封性 1_ 谢6 n - - I m nn 1 I I In ^ ^^^1 l^n I . - I --- _1 一aJ i ._ (請先閱讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標準（CNS ) A4規格（2丨0X297公釐） 55 3870 1 4 5 ί：ί π · . / …f Α7 Β7 經濟部中央標準局員工消費合作社印製 五、 發明説明（54 ) 1 | 宵 施 例 12 1 3 — f-h 較 例 1 5 1 1 按 照 表 7 所 示 組 成 之 各 成 分 » 及 安 定 m 同 時 使 甩 韓 銶 1 1 混 合 機 混 合 » 再 藉 曰 本 製 m 公 司 製 品 之 TEX - 30型 之 雙 軸 擠 •·~·«· 1 I 壓 機 » 按 照 表 7 所 記 載 條 件 (擠筒設定溫度為2 9 3 )進行 請 先 1 熔 融 混 練 而 得 組 成 物 C 閲 背 1 1 該 組 成 物 之 錠 it* 使 用 備 有 圓 茼 形 楔 頭 之 50 mm 直 徑 之 ttrt 单 δ 之 .丨 注 1 軸 擠 壓 機 9 依 據 表 7 所 示 條 件 熔 融 擠 壓 t 由 直 徑 50 m na » 模 意 事 1 S I 唇 問 距 1 . 5 m Bt之圓筒形模頭， 按照表7 所示條件向上方擠 再 1 1., 壓 熔 融 樹 脂 9 壓 入 乾 燥 空 氣 於 該 筒 狀 薄 膜 之 中 處 i 使 ftfr: 茼 % 本 1 狀 薄 膜 m 脹 « 妷 後 冷 却 1 經 夾 棍 而 得 液 晶 聚 酯 樹 脂 組 成 物 頁 、«_， 1 1 薄 膜 C 1 1 該 液 晶 聚 m 樹 脂 組 成 物 薄 膜 之 縱 向 捲 取 方 向 (MD方向） 1 1 1 横 向 方 向 (TD方向） 之 拉 伸 倍 率 由 壓 人 乾 燥 空 氣 量 * 薄 1 訂 膜 捲 取 速 度 而 控 制 之 肯 該 時 横 向 方 向 之 吹 脹 比 率 » 縱 向 方 1 | 向 之 拉 伸 倍 率 如 表 7 所 示 C 所 得 液 晶 聚 m 樹 脂 組 成 物 薄 膜 1 I 之 氣 am m. 透 過 率 示 於 表 8 0 1 1 由 上 述 薄 膜 利 用 熱 封 器 製 成 三 面 經 熱 封 的 殺 m 軟 袋 * 1 . 填 充 已 調 理 的 咖 m 後 1 該 殺 Μ 軟 袋 之 袋 P 部 分 用 熱 封 器 封 1 I η 使 用 曰 阪 製 作 所 公 司 製 造 的 高 溫 高 壓 調 理 殺 菌 試 驗 機 1 1 在 130f下殺閨處理30分鐘。 1 ] 殺 m 處 理 後 之 該 殺 軟 袋 包 裝 材 料 之 水 蒸 汽 透 過 率 f 1 [ 透 氣 率 示 於 表 8 〇 該 殺 菌 軟 袋 經 殺 舗 處 理 後 k 在 70 下 貯 1 1 存 40 曰 後 開 啓 封 P I 檢 査 内 容 物 未 TJt. 現 有 變 質 情 形 C 1 I hh 較 Λ 1 6 ]7 1 1 就 市 售 的 聚 偏 二 氮 乙 烯 (PVDC) 塗 布 聚 酸 胺 薄 膜 r 乙 烯 1 1 -乙酸乙ί 希酯共聚物薄膜， 按照上述相同方ί 去進行試驗^ 1 I 所 得 結 果 合 併 示 於 表 8 1 1 本紙張尺度適用中國國家標率（CNS ) Λ4規格（210X297公釐） 56 3 8701 A7 Β7 五、發明説明（5S ) 經濟部中央標準局負工消費合作社印製 二ffF对存姻 Η 艚妗aiisn, SBR , SBR1 502 (W 笼菹渐(loorf) =012) 比較例15 實施例1 3 實施例12 〇〇 . — 1 Η-* — 1 1—1· ,〇 -ffl p 1 ΪΟ 成分 (甲） m St .«s llnril 卿 Wn 〇 —㈧ <£> 1 (N ίΟ 1 ! 成分 〇 ο -1 其他| 丨 成分 345 345 I i I 293 擠筒設 定溫度 ft:) 熔融混練條件 200 200 200 -1 螺桿 轉數 r pm 345 345 293 擠筒設 定溫度 it·) Μ m ¢0 ίΟ Ο -1 螺桿 轉數 r ρπ 345 345 297 模頭設 定溫度 (V ) 不能成睽 1 05 — cr» 吹脹比率 1 c_n i__> σι CO 拉伸 倍率 1 c〇 oo 薄膜 厚度 0Ί (請先閱讀背面之注意事項再填寫本頁)Economy, Shao Central Bureau of Standards printing, invention description of employees' cooperatives (49) Table 3 Group field "weight *%) Injection molded product film Physical properties Composition composition Other properties Thickness decomposition Water vapor transmission rate Air permeability (CC / ID2. ( 96) (u ») Initial temperature (g /« 2,24hr. 24hr.atai) (A) (Z) Composition.atm Example 7 A-1 Z-4 78 22 0 241 29 Ship 0.4 0.3 bb 8 A-1 100 0 0 258 One --- Comparative Example 9 A-1 η 78 0 22 232 37 427 0.Γ) 0.4 Example 8 A-2 B-5 92 8 0 179 18 476 0.4 0.3 9 A-2 B-5 68 31 0 155 43 433 0.4 0.4 Comparative Example K) Stomach 2 100 0 0 183 — — — — Comparative Example 11 A-2 ¢ 2 92 0 8 154 — One by one Sumitomo Chemical Industries Company Products • Ethylene-Glycidyl Methacrylate Copolymer, No. 12C, (Composition: Ethylene / Cyclopropyl Methacrylate = Way / 6 Weight Ratio, KFR (19〇t :, 2.16ks) = 3g / l〇 * in ·) Product of Sumitomo Chemical Industry Co., Ltd., ethylene-propylene-diene copolymer rubber, Ashbuy Guan Manni viscosity (loot) = 55) The paper size is applicable to Chinese National Standard (CNS) A4 specification (2l0 × 297mm) 3 8 7 0 1 ----- ^ ----- {---- --ΪΤ ------ A _ (Please read the notes on the back before filling out this page) A7 B7 Printed by the Consumers' Cooperative of the Central Standards Bureau of the Ministry of Economic Affairs 5. Description of the invention (50) 1 1 旃 例 1 〇11 th Comparative Example 1 2 14 i Mix the ingredients with a Korean-Soviet mixing machine according to the composition described in Table 4 1 1 1 »Use B Tex-30 model made by our copper company. Table 4 Please read the conditions shown in if 1 1 and mix 1 to obtain the ingots of the tree m composition 9 to provide injection molding and 1 for film molding 0 injection molding test Η Use of E-Resin I Industry Co., Ltd. 1 Ί PS40E5ASE Injection molding machine, according to the conditions shown in Table 4 injection precautions 1 f molding 1 for testing SAl with 0 The results are shown in Table 4 ○ and 1 film formation of the cover tape * Resin pellets M prepared With cylindrical die 4 5 si is on the page 1 «ΓΤ rpi shaft extruder 1 diameter melted under the conditions shown in Table 5 * from 1 I diameter 5 0 ia m lip distance 1.5 The cylindrical die of 之 π ΙB squeezes and melts the 1 1 I resin upwards, presses dry air into the hollow space of the 茼 -shaped film i to make the cylindrical film 1 1 to 1 and expands to fm, and after cooling, it is made by stick Liquid crystal resin composition 9 For the cover tape, the inflation ratio m when forming into a film, and the stretch ratio in the direction 1 1 are shown in Table 5 C 1 I In addition »For the film formation of the carrier tape, the cover tape can be used for film formation The same 1 device was used to form the resin ingots into a film according to the conditions shown in Table 6. The 1 I film obtained was then pressed by a wedge press forming machine »at 250 to 300 ° f < h processing i 1 1 1 Make length X width = 2 0 in ID > < 2 0 m on the film □ bag 1 5 1 Made of carrier tape 1 1 Observe the appearance with the naked eye after pressing r No m-stripes are produced on the film * 1 1 Those who can be accurately formed into a P-bag shape are evaluated as good products ΠΓ 刖 are regarded as defective products 1 I 0 outside t Heating to 260 to 3 10 t: The cover tape is pressure-bonded to the carrier tape after the above embossing process i I to evaluate its heat-sealability. After cooling, observe the two boundaries with the naked eye. 1 1 I surface »No cracks on the interface or Those with good peelability and good adhesion are regarded as good products. No 1 1 This paper size applies the Chinese National Standard (CNS) Λ4 specification (210 X 297 mm) 52 3 8 7 0 1 Printed by the Consumer Cooperative of the Central Standards Bureau of the Ministry of Economic Affairs A7 ____B7_ V. Description of the Invention (Η) 刖 is regarded as defective. The results are shown in Table 6, and the air permeability and water vapor permeability of the various films used in the cover tape and carrier tape are shown in Table 5 and Table 6, and Table 4 I------.... .. ....... —IH 1 -I Winter II 1-------1 ml I m-(Please read the precautions on the back before filling this page) Composition (% by weight) Melting and mixing Condition injection molding Condition injection molding Physical properties Component composition Other extruded barrel set screw rotation injection wedge TDUL Constant temperature rpm Shape temperature temperature (A) (B) Component 1C VV Example 10 A-1 B-1 78 22 0 350 200 350 80 235 Comparative Example 12 A-1 100 0 0 350 200 350 80 265 Comparative Example 13 A-1 η 78 0 22 350 200 350 80 197 Example 11 A-2 B-1 92 8 0 290 200 290 80 181 Comparative Example 14 A-2 100 0 0 290 200 290 80 183 〇 Product of Sumitomo Chemical Industries, low-density polyethylene F-101 This paper size applies the Chinese National Standard (CNS) Λ4 specification (210X 297 mm) 53 3 8 7 0 1 V. Description of the invention (" 2) A7 B7 Staff consumption of the Central Bureau of Standards of the Ministry of Economic Affairs Printed by the agency * 1 Curtain to the left "3: 艄 妗 到 遒 卽, 雑 出 蒴 雑 2ITF-101 Comparative Example 14 Example 11 Comparative Example 13 Comparative Example 12 Example 10 I A-2 100 1 iA-2 i 92-< Ι-Η ΟΟ 1 A-1 100 00 1 t-i component (A) ^ 1 resin composition (weight part) 〇 (N 〇〇1 ο 〇 ^ (N ΓΟ 1 component (B) _1 〇 ο N? ι— * ro 〇〇1 Other ingredients 292 292 352 352 π 352 丨 Extruder set temperature (t) m 哋 m full m 〇0 〇〇0 ο 〇〇 CC 〇0 Screw rotation number ΓΡΒ 1! 294 1_ 1 I 1 294 ι_ 354 i_ 354 354 Die set temperature (V) ...... 1 1 No film formation σ > No film formation σ5 inflation rate No film formation 1_ 〇ϊ 〇〇1 1 i No film formation 1_ can not form a film-0 | ί stretch ratio i CO 1 1 piece of film thickness mmmmm ί $ 1 ο C? S 1 1 Ο cn CC / CH2 atm. 24hr oxygen permeability 1 ο 1 1 ο g / ro2 a to 24hr water vapor transmission rate thanks 5 ^ i ^ i- ^^^ 1 .1 ^ 1 m HI I tm ml r ^ n--_ ..... ---- i: 、 一 flJ (Please (Please read the notes on the back before filling out this page) This paper size applies to Chinese National Standards (CNS ) Λ4 specification (210X297 mm) 3 8 7 0 1 459037 A7 B7 V. Description of invention (53) Comparative Example 14 printed by the Consumer Cooperatives of the Central Standards Bureau of the Ministry of Economic Affairs Example 14 Comparative Example 13 Comparative Example 12 Example 10 H- * ΓΠ 〇ΤΠ Ο 1 ζ〇-ffi ΓΟ! Ro ^ «OO 1 S s 〇 丄 〇0 1 1— * -1 Ingredient 1 1 1 (A) 丨 Resin composition (weight part) 〇 (N 〇〇i — o 〇ro IN N? 1 ι— * Ingredient (B) 〇o ΓΌ N5 〇〇 Other ingredients Γ〇 ς5 ro CO PC OJ tn ro W U1 [〇 05 cn ro Μ mmamm Temple oo ο gg 〇〇〇g screw Number of revolutions ΓΡΒ! .I fO CO ς〇w iLn CC CJ1 o〇Cjrj -1 | Die set temperature (it) 1 No film formation CJl to No film formation No film N5 CD -1 丨 Blow ratio Molding private oo can not be filmed can not be filmed 00 01 stretch ratio 1 oo I 1 ro ro ΐ: said film thickness is astonishing mm 1 o CO 1 1 o cc / cm2 atm. 24hr 1 oxygen permeability. 1 o oo 1 to 1— * g / m2 atm. 24hr water vapor transmission rate 1 good 1 1 good 1_ mh lean 1 ^ Hl · 1 1 heat sealability 1_ thank 6 n--I m nn 1 II In ^ ^^^ 1 l ^ n I.-I --- _1 一 aJ i ._ (Please read the precautions on the back before filling this page) This paper size applies to China National Standard (CNS) A4 (2 丨 0X297 mm) 55 3870 1 4 5 ί: ί · π ·. /… f Α7 Β7 Printed by the Consumers' Cooperative of the Central Standards Bureau of the Ministry of Economic Affairs 5. Description of the Invention (54) 1 | Xiaoshi Example 12 1 3 — fh Comparative Example 1 5 1 1 Composition as shown in Table 7 Ingredients »and stable m at the same time to mix the Han 銶 1 1 mixer» Then borrow the TEX-30 type biaxial extruder made by the Japanese company m ·· ~ · «· 1 I press» according to Table 7 Record the conditions (set temperature of the extruder is 2 9 3). Please perform 1 melting and kneading to obtain the composition C. Read back 1 1 The ingot of the composition it * Use a 50 mm diameter ttrt single δ with a round wedge丨 Note 1 Shaft extruder 9 Melt extrusion according to the conditions shown in Table 7 by diameter 50 m na »Mould matter 1 S I. A cylindrical die with a lip distance of 1.5 m Bt is squeezed upwards according to the conditions shown in Table 7. 1. Press the molten resin 9 into the dry air in the cylindrical film. I Make ftfr:茼% This 1-shaped film m swells «妷 After cooling 1 The liquid crystal polyester resin composition sheet obtained by sandwiching,« _, 1 1 film C 1 1 The longitudinal winding direction of the liquid crystal poly m resin composition film (MD direction ) 1 1 1 The stretching ratio in the transverse direction (TD direction) is controlled by the amount of dry air pressure * Thin 1 The film winding speed should be controlled in the transverse direction at that time »Longitudinal 1 | Stretching ratio in the direction The liquid crystal polym resin composition film 1 obtained by C as shown in Table 7 is shown in Table 8. The transmittance is shown in Table 8 0 1 1 The above-mentioned film is made of a heat-sealable m-killed soft bag on three sides * 1 After filling the conditioned coffee m, the heat-sealing device is used for the P part of the soft-killer bag. Feng 1 I η used a high-temperature and high-pressure conditioning sterilization test machine manufactured by Yosaka Manufacturing Co., Ltd. 1 1 for 30 minutes at 130f. 1] The water vapor transmission rate f 1 of the soft-killing packaging material after the m-killing treatment [Permeability is shown in Table 8 〇 After the kraft-killing treatment, the sterilization soft bag is stored at 70 under 1 1 and stored at 40 after opening. The content of the PI inspection is not TJt. The existing deterioration situation C 1 I hh is more than Λ 1 6] 7 1 1 Commercially available polyvinylidene dichloride (PVDC) coated polyimide film r Ethylene 1 1-Ethyl acetate copolymerization The film is tested according to the same method as above ^ 1 I The results obtained are shown in Table 8 1 1 The paper size is applicable to the Chinese National Standard (CNS) Λ4 specification (210X297 mm) 56 3 8701 A7 B7 V. Description of the invention (5S) Printed by the Central Bureau of Standards of the Ministry of Economic Affairs and Consumer Cooperatives to print two FFF pairings Ηaiisn, SBR, SBR1 502 (Worf = 012) Comparative Example 15 Example 1 3 Example 12 〇 〇. — 1 Η- * — 1 1—1 ·, 〇-ffl p 1 Ϊ〇 Ingredient (A) m St. «S llnril Qing Wn 〇 -㈧ < £ > 1 (N ίΟ 1! Ingredients οο -1 Others | 丨 Composition 345 345 I i I 293 Extruder set temperature ft :) Melt kneading conditions 200 200 200 -1 Screw revolution r pm 345 345 293 Extruder set temperature it ·) Μ m ¢ 0 ίΟ Ο -1 Screw revolution r ρπ 345 345 297 Die set temperature (V) cannot be set to 睽 1 05 — cr »Blowing ratio 1 c_n i __ > σι CO stretch ratio 1 c〇oo Film thickness 0Ί (Please read the precautions on the back first (Fill in this page again)

l1T 本紙張尺度適用中國國家標準（CNS ) Α4規格（210Χ297公釐） 57 3 8 7 0 1 A7 Β? 五、發明説明（56 ) 經濟部中央標準局—工消費合作社印裝l1T This paper size is applicable to Chinese National Standard (CNS) A4 specification (210 × 297 mm) 57 3 8 7 0 1 A7 Β? V. Description of invention (56) Printed by the Central Bureau of Standards of the Ministry of Economic Affairs—Industrial and Consumer Cooperatives

表8 組成(重量％) 物 性 氣體透 過性 殺菌處理後氣體透過性 透氧率 水蒸汽 透氧率 水蒸汽 内容物 成分 成分 其他 透過率 透過率 變化*3 (cc/cffl2 (g/cm2 (cc/cm2 (g/cm2 (甲） (乙） 成分 24hr. 24hr. 24hr. 24hr. latra) latffl) latm) latm) 實施例12 甲-2 乙-1 91 9 0 0.3 0.5 0.4 0.4 0 實施例13 甲-1 乙-7 81 19 0 0.4 0.4 0.5 0.4 〇 比較例16 ¢1 0 0 100 7.4 9.2 17.3 20.5 X 比較例17 *2 0 0 100 1.7 5.5 39.2 9.8 XTable 8 Composition (wt%) Physical Gas Permeability Gas Permeability Oxygen Permeability Water Vapor Oxygen Permeability Water Vapor Content Components Other Variations Transmittance Changes After Sterilization Treatment * 3 (cc / cffl2 (g / cm2 (cc / cm2 (g / cm2 (A) (B) Ingredients 24hr. 24hr. 24hr. 24hr. latra) latffl) latm) latm) Example 12 A-2 B-1 91 9 0 0.3 0.5 0.4 0.4 0 Example 13 A- 1 B-7 81 19 0 0.4 0.4 0.5 0.4 〇 Comparative Example 16 ¢ 1 0 0 100 7.4 9.2 17.3 20.5 X Comparative Example 17 * 2 0 0 100 1.7 5.5 39.2 9.8 X

*1東洋紡績公司製品，PTDC塗布聚醯胺薄膜，商品名為Hadene Κη8002。 *2 Kura「ay公司製品，乙烯-乙酸乙烯酯共聚物薄膜，商品名為Eva] EF-XIC ί3 Ο示内容物未發生變質。 X示色香等内容物發生變質C 本紙張尺度適用中國國家標率（CNS ) A4規格（210X297公釐） 5 8 38701 (請先閱讀背面之注意事項再填寫本頁) A7 B7 五、發明説明（57 ) 就中空成形物按照下述方法進行物性測定。 瓶子厚度：測定瓶子胴部3處之厚度，再求其平均值 氣氣透過率：使用摩登控制公司製迤的OZTRAN-1.00型 式，在23 0%相對濕度條件下，求得每一瓶容量為 1 500 CC之透氣率。 瓶子收縮率：以填充熱水前之糚子内容積avt，將 95 t之熱水裝入瓶子内，保持10分鐘後除去熱水，以瓶子 在恢復室溫時之内容積為V2,由100%求得 瓶子之收縮率。 汽油透過率，汽醇透過率：於杯子内裝入5 C C之汽油 (日本出光石油公司製、一般汽油、商品名為Z e a s ),依拣 «ί I S Z 2 0 8 0所示方法，測定2 3 Ό ,相對濕度S 0 %條件下之 汽油透過率c另外，杯子中放人上述汽油4 C C及1 C C之甲醇 ,按照相同方法測定得汽酵透過率。 耐摔落性：所得成形物容器中裝滿水，由〗6ib高處摔 落後，以肉眼觀察容器外觀，依據下列檫準評估之。 〇示容器未發生裂紋。 X示容器發生裂紋。 啻揄例〜15乃1+,較例18〜19 先將表9中所示組成之各成分以韓蘇混合機棍合後， 再使用日本製钢公司製品之雙軸擠壓機TEX-30型ί在擠简 設定溫度35〇υ ,螺桿旋轉速度220rpm條件下熔融混練， 而得液晶聚酯樹脂組成物之錠粒。 (請先閱讀背面之注意事項再填寫本頁) 訂 經濟部中央標準局員工消費合作社印製 本紙張尺度適用中國國家標隼（CNS ) A4規格（210X297公釐） 59 3 6 7 0 1 459037 A7 經濟部中央標準局員工消費合作社印11 B7五、發明説明（5 8 ) 然後使用布拉格公司製品之吹脹成形機BM- 3 04型，以 螺捍徑50i»b,螺桿旋轉速度30rpnt,模頭徑2 5.5nm,噴嘴 徑22πιιβ,擠筒設定溫度350 °C,模頭溫度352Ό.空氣吹入 壓力2 , 2 k s / c n 2 ,循環時間2 5秒，冷却時間1 5秒之條件下， 進行該組成物錠粒之擠壓吹腺成形，製得容量1500CC之方 形瓶子C 所得瓶子施以物性測定，其結果示於表9 。 窖施例1 6〜1 8及酧例2 0〜：η 以表9中所示組成，除TEX-30型之擠筒設定溫度為 2901,吹脹成形機之擠筒設定溫度為2901,模頭溫度為 290 10之外，其餘皆按照實施例1 4所示相同方法成形為瓶 子，並進行其物性測定。所得結果示於表9 e 啬旃例1 9 使用多層直接吹脹裝置，於成形體外層用之蟋捍徑 50η®之單軸擠壓機工，將昭和電工公司製造的高密度聚乙 烯（商品名為秀麗克（Sholex)4551H, MFR=0,05g/l〇mm.密 度為0.9 45g/Cm3)在螺捍轉速度12〇rpm，擠筒設定溫度 2351條件下熔融，螺捍徑50miB之成形體内層闬之單軸擠 壓機I則將啻施例〗7之液晶聚酯樹脂組成物之錠粒，以轉 速、3 5「p m ,擠筒設定溫度2 9 5 下進行熔融。 其次，分別由各攒壓機將熔融物導流至各模頭，模頭 設定溫度295 °C下在模頭内部以多技管方式匯流後積層各 層後，由模頭擠壓至模具中，藉導入空氣之直接吹脹法， 製成内容積為2500CC之方形瓶子： (請先閱讀背面之注意事項再填寫本頁) 訂 本紙張尺度適用中國國家標準（CNS ) A4規格（2〗0X297公釐） 60 3 8 7 0 1 4 5? Π 3 7 a? 一_^_ 五、發明説明（59 ) 由該瓶子取得試Η,測定其汽油透過率、汽醇透過率 度 厚 層 I-W- — 夕 層 内 得 求 察 觀 鏡 徹 顯 藉 面 裁 片 試 又 表 於 示 果 結 得 聚無 晶 但 液 ， 用行 改進 粒法 錠方 物之 成19 組例 脂施 樹宵 酯 照 聚按 晶 皆 液餘 的其 用 ， rT 所 夕. 17粒 例錠 施之 實-2 甲 酯 物 形 成 的 好 良 得 造 製 法 (請先聞讀背面之注意事項再填寫本頁) 、1Τ 經濟部中央標準局員工消費合作社印製 本紙張尺度適用中國國家標準（CNS ) A4規格（210X297公釐） 1L 6 3 8 7 0 1 五、發明説明（60 ) 表9 經濟部中央標準局員工消費合作社印製 組成（重量％) 物 性 成分 成分 其他 瓶子厚度 透氧率 瓶子收 (cc/bottle 縮率 外觀 (甲） (乙} 成分 (u m) day * atm) (%) 實施例14 甲-1 乙-1 ¢1 67 33 0 43 0.13 〜0 0 實施例15 甲-1 乙-2 91 9 0 62 0.04 〜 0 〇 比較例18 甲-1 100 0 0 不能成膜 — — — 比較例19 甲-1 *2 67 0 33 不能成膜 一 — 宵施例16 甲-2 乙-6 78 22 0 33 0.12 0.01 〇 實施例17 甲-2 乙-2 ¢1 86 14 0 59 0.03 〜0 〇 實施例18 甲-3 乙-1 92 8 0 77 1.05 0.1 〇 比較例20 甲-2 100 0 0 不能成膜 — — 比較例21 0 0 100 66 5.9 14 〇* 1 Products of Toyobo Co., Ltd., PTDC coated polyamide film, trade name Hadene KK 8002. * 2 Kura "Products of Ay Company, ethylene-vinyl acetate copolymer film, trade name Eva] EF-XIC ί3 〇 indicates that the contents have not deteriorated. X indicates that the contents such as color fragrance have deteriorated. C This paper is applicable to Chinese national standards. Rate (CNS) A4 specification (210X297 mm) 5 8 38701 (Please read the precautions on the back before filling out this page) A7 B7 V. Description of the invention (57) Physical properties of the hollow molded product shall be determined according to the following method. Bottle thickness : Measure the thickness of the three parts of the bottle, and then calculate the average gas transmission rate: Use the OZTRAN-1.00 type made by Modern Control Co., Ltd., at 23 0% relative humidity, and find the capacity of each bottle is 1,500 The air permeability of CC. Bottle shrinkage rate: Use the volume of acacia before filling with hot water, avt, put 95 t of hot water into the bottle, hold it for 10 minutes, remove the hot water, and use the internal volume of the bottle when it is returned to room temperature For V2, the shrinkage of the bottle is obtained from 100%. Gasoline transmission rate, gasoline alcohol transmission rate: 5 CC gasoline (made by Japan Idemitsu Petroleum Corporation, general gasoline, trade name Z eas) in the cup, according to the pick «Ί ISZ 2 0 8 0 method, Determine the gasoline transmission rate c under the condition of relative humidity S 0%. In addition, put the above gasoline 4 CC and 1 CC methanol in the cup, and measure the fermentation fermentation transmission rate according to the same method. The container was filled with water and fell from a height of 6ib. Observe the appearance of the container with the naked eye and evaluate it according to the following criteria. ○ indicates that the container does not crack. X indicates that the container has cracked. Example ~ 15 is 1+, Comparative Examples 18 to 19 The ingredients shown in Table 9 were first kneaded with a Korean-Soviet mixer, and then a biaxial extruder TEX-30 manufactured by Japan Steel Corporation was used to set the temperature at 35 °. υ, melting and kneading under the condition of screw rotation speed of 220rpm, to obtain the tablets of liquid crystal polyester resin composition. (Please read the precautions on the back before filling this page) Order the paper size printed by the Consumer Cooperatives of the Central Standard Bureau of the Ministry of Economic Affairs Applicable to China National Standards (CNS) A4 (210X297 mm) 59 3 6 7 0 1 459037 A7 Printed by the Consumer Cooperatives of the Central Standards Bureau of the Ministry of Economic Affairs 11 B7 V. Description of the invention (5 8) Then use the products of Prague Forming machine BM- 3 04 The screw diameter is 50i »b, the screw rotation speed is 30rpnt, the die diameter is 25.5nm, the nozzle diameter is 22πιβ, the extruder setting temperature is 350 ° C, and the die temperature is 352Ό. Air blowing pressure 2, 2 ks / cn 2, circulation Under the conditions of time of 25 seconds and cooling time of 15 seconds, the composition was extruded and blown into a gland to form a square bottle C with a capacity of 1500CC. The obtained bottle was subjected to physical property measurement. The results are shown in Table 9. Example 1 6 ~ 18 and Example 2 0 ~: η The composition is shown in Table 9, except that the extruder set temperature of the TEX-30 model is 2901, and the extruder set temperature of the inflation molding machine is 2901. The head temperature was 290-10 and the rest were formed into bottles according to the same method as shown in Example 14 and the physical properties were measured. The results obtained are shown in Table 9e. Example 1 9 Using a multi-layer direct inflation device, a uniaxial extruder with a diameter of 50 η was used for forming the outer layer. A high-density polyethylene (trade name) manufactured by Showa Denko Corporation was used. Sholex 4551H, MFR = 0,05g / 10mm. Density 0.9 45g / Cm3) Melted at a screw rotation speed of 120rpm and a set temperature of squeeze cylinder 2351, a screw with a diameter of 50miB The uniaxial extruder I of the inner layer was melted at a rotation speed of 35 pm and a set temperature of 2 95 of the liquid crystal polyester resin composition of Example 7 below. Each pressing machine guides the melt to each die. The die set temperature is 295 ° C, which is converged in a multi-technical tube inside the die. After the layers are laminated, the die is squeezed into the die. The direct inflation method is used to make a square bottle with a volume of 2500CC: (Please read the precautions on the back before filling in this page) The size of the paper is applicable to the Chinese National Standard (CNS) A4 specification (2〗 0X297 mm) 60 3 8 7 0 1 4 5? Π 3 7 a? A _ ^ _ V. Description of the invention (59) Test obtained from the bottle, Determine its gasoline transmission rate and vapor alcohol transmission rate. Thick layer IW--In the evening layer, you need to look at the mirror to show the surface cutting test and show that the fruit is agglomerated without crystal, but the liquid method is used. The composition of the prescription is 19 groups of examples of lipids, tree esters, and polyethers, which are used for the remaining liquid, rT. 17 examples of ingots of Shishishi-2 methyl esters. Good manufacturing method (please read the back first) (Please note this page before filling in this page). 1T The paper printed by the Central Consumers' Bureau of the Ministry of Economic Affairs, Consumer Cooperatives. The paper size is applicable to the Chinese National Standard (CNS) A4 specification (210X297 mm) 1L 6 3 8 7 0 1 V. Description of the invention (60 ) Table 9 Composition printed by the Consumer Cooperative of the Central Bureau of Standards of the Ministry of Economic Affairs (% by weight) Physical composition ingredients Other bottle thickness Oxygen permeability Bottle collection (cc / bottle shrinkage appearance (A) (B) Composition (um) day * atm) (%) Example 14 A-1 B-1 ¢ 1 67 33 0 43 0.13 to 0 0 Example 15 A-1 B-2 91 9 0 62 0.04 to 0 〇 Comparative Example 18 A-1 100 0 0 Film — — Comparative Example 19 -1 * 2 67 0 33 Cannot form a film — Example 16 A-2 B-6 78 22 0 33 0.12 0.01 〇 Example 17 A-2 B-2 ¢ 1 86 14 0 59 0.03 ～ 0 〇 Example 18 A-3 B-1 92 8 0 77 1.05 0.1 〇 Comparative Example 20 A-2 100 0 0 No film formation — Comparative Example 21 0 0 100 66 5.9 14 〇

*1示低於檢驗下限 *2住友化學工業公司製品，乙烯-丙烯-二烯条橡膠EPDM SpreneE50U( 孟納粘度（1000=53) *3聚對苯二甲酸乙二酯（對數粘度：0.8K 本紙張尺度適用中國國家標準（CMS ) A4規格（2I0X W7公釐） 62 3 8 7 0 ] (請先聞讀背面之注意事項再填寫本頁) 訂 五、發明説明（ 6 ] A7 B7 經濟部中央標华局員工消費合作社印製 ίΐ Ββία 蝻H^>alssin,Mal砘翊^揉郅卽汾詾.彌af(shoiex)4551H, rr 垄 ΓΟ ΓΟ m 渔 m Μ塒 m fit· 酿齣 缴 3r 滋 鍤 m St i ο τ> 妗 ΠΏ — -σ 芥 ⑺ — m m m 菡 iXB 趣 1 ¢0 〇 〇 ^ 铜 巴筛 雜 a 溃 〇 〇 〇 σ> ^ ^ 3f ω oq ^ % \ S： , Q 43Τ ^ stJ m 巴· 藤 1 〇> ο ι—ι. Ο ^ ^ ΰύ 173 ^ Μ 、 碑 ，〇 ™ 已.‘ m 稱 I ο 轼 围 谢一 0 I ----‘：-------訂------1 I (請先閱讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標率（CNS) Λ4規格（210X297公釐） 3 8 7 0 1 A7 459037 B7 五、發明説明（62 ) 使用下列化合物作為（丙）成分之發泡劑。 (請先閱讀背面之注意事項再填寫本頁) 三胼三時：費濃化I公司（Finons Industial Chemical)製品，簡稱為C-2。 發泡物之物性按照下述方法評估之。 拉伸試驗：依據ASTM [)638所示方法.就縱向方向（擠 壓方向）及橘向方向雙方向潮定抗拉強度及伸長率c 發泡成形物之形狀：所得發泡成形物，依據下列標準 藉光學顯微鏡觀察評估之。 〇示發泡成形物由徹細均勻的氣泡所形成。 X示發泡成形物形狀不均且由直徑分散性較大而不均 勻的氣泡所形成。 啻例例0殆hh較例：> 2〜2 4 按照表11中所示組成，將（甲）成分、（乙）成分及其他 成分等用韓蘇混合機混合後，使用池貝鐵工公司製品之 P C Μ - 3 0型雙軸擠壓機，在擠筒設定溫度2 9 5 υ ,螺桿轉速 為60γρβι條件下進行混練。 經濟部中央標準局員工消費合作社印製* 1 indicates lower than the lower limit of inspection. * 2 Sumitomo Chemical Industries Co., Ltd., ethylene-propylene-diene rubber EPDM SpreneE50U (Menner viscosity (1000 = 53) * 3 polyethylene terephthalate (logarithmic viscosity: 0.8K This paper size applies the Chinese National Standard (CMS) A4 specification (2I0X W7 mm) 62 3 8 7 0] (Please read the precautions on the back before filling out this page) Order 5. Description of the invention (6) A7 B7 Ministry of Economic Affairs Printed by the Consumer Standards Cooperative of the Central Standardization Bureau of the People's Republic of China ίΐ Ββία 蝻 H ^ > alssin, Mal 砘 翊 ^ 郅 卽 郅 卽 Fen 詾. Miaf (shoiex) 4551H, rr ridge ΓΟ ΓΟ m fish m Μ 埘 m fit锸 m St i ο τ > 妗 ΠΏ — -σ mustard — mmm 菡 iXB Fun 1 ¢ 0 〇〇 ^ Cuba sieve a 〇〇〇σ > ^ ^ 3f ω oq ^% \ S:, Q 43Τ ^ stJ m 巴 · 藤 1 〇 > ο ι—ι. 〇 ^ ^ ΰύ 173 ^ Μ, stele, 〇 ™ has been. 'm called I ο 轼 围 谢 一 0 I ----': ----- --Order ------ 1 I (Please read the precautions on the back before filling this page) This paper size is applicable to China National Standards (CNS) Λ4 specifications (210X297 mm) 3 8 7 0 1 A7 459037 B7 V. Description of the invention (62) The following compounds are used as the (C) component of the foaming agent. (Please read the precautions on the back before filling out this page) Three or three hours: Finons Industial Chemical The product is abbreviated as C-2. The physical properties of the foam are evaluated according to the following methods. Tensile test: According to the method shown in ASTM [) 638. The tide resistance is measured in both the longitudinal direction (extrusion direction) and the orange direction. Tensile strength and elongation c Shape of the foamed molded product: The obtained foamed molded product was evaluated by observation with an optical microscope according to the following criteria. ○ indicates that the foamed molded product is formed of fine and uniform bubbles. X shows the foamed molded product. The shape is uneven and is formed by bubbles with large and uneven diameter dispersion. 啻 Example Example 0 殆 hh Comparative Example: > 2 ~ 2 4 According to the composition shown in Table 11, the component (A) and (B) After mixing the ingredients and other ingredients with a Korean-Soviet mixer, use a PC BM-30 type twin-shaft extruder made by Ikebe Iron Works to perform kneading at a set temperature of the extruder of 2 9 5 υ and a screw speed of 60γρβι. Member of the Central Standards Bureau of the Ministry of Economic Affairs Printed consumer cooperatives

所得錠粒混合以表1 1所示組成之發泡_後，籍備有 Τ模之田邊塑暖機械公司製品之單軸擠壓機，在擠筒設定 溫度2 9 7 UC ,螺捍轉速度2 0 r ρ m ,模頭設定溫度2 9 7 °C .由 T模設定寛度lOOnia,縫隙間距3mm之T模擠壓製得發泡板 Η。所得板Η之物性示於表1 U 3 8 70 1 本紙張尺度適用中國國家標準（CNS ) Α4規狢（210Χ297公釐） 5 9 017 A7 B7 五、發明説明（6 3 ) 經濟部中央橾準局員工消費合作社印製 45>1讲对泠儋 Η 濉>>Miiaa, Epl (sprs E505 (141¾ 葫滿(100 tn =77r 芯(-«KmiK (ίΝ)Μ.^泗»萚洚冰^卟|+鈔一锻适进进_ 比較例24 比較例23 實施例20 C〇 1 ΓΟ 甲-2 100 05 X ΓΟ 1 成分 (甲） 組成（重量％) 〇 〇 M IN 办 1 1»· 成分 (乙） to *—1 〇 〇 -1 其他 成分 丙-2 8.0 i 丙-2 8.0 CO 3 " 1 Ο EO 發泡劑 t2 ： 重量部： 0.98 (g/cc) 密度 550 1490 1050 (k g / c si2) MD 抗拉強度 C71 〇〇 -0 <—* LO % (%) MD 伸長率 190 910 930 (kg/cnt2) TD 抗拉強度 CO CO 1—» fC <jn (%) 伸長率 to 1.8 (MO/TD) 拉抗 |強度比 X X 〇 發泡 成形 i體形 狀 i- Ϊ1 (請先鬩讀背面之注意事項再填寫本頁) 訂 本紙張尺度適用中國國家標準（CNS ) Α4規格（210Χ297公釐） 3 8 7 0 1 A7 B7 經濟部中央標準局負工消費合作社印製 五、 發明説明（64 ) 1 I 按 照 下 述 方 法 進 行 殺 m 軟 袋 用 途 之 容 器 的 評 估 〇 J 1 I 深 徑 比 率 ： 圓 形 容 器 指 容 器 深 度 及 容 器 上 上山 □ 徑 間 之 1 1 tb 率 « 方 形 容 器 指 容 器 深 度 及 容 器 π 部 分 的 最 長 對 角 線 長 Ν 1 I 請 I 度 間 之 tb 率 C 先 閱 I 讀 1 | 耐 摔 落 試 驗 - 容 器 充 滿 水 以 封 蓋 材 料 密 封 後 * 由 1 HI商 背 面 1 之 1 摔 落 後 檢 查 衝 擊 破 m 情 形 C. 注 意 靠 1 I M. 熱 1 p (r 〇 r t )試 驗 ; 項 再 1 導 1 外 觀 : 於 成 形 物 容 器 内 填 充 市 售 咖 _ 用 封 蓋 材 料 密 Η - r ·. 頁 封 後 ί 利 用 问 溫 高 壓 調 理 殺 菌 試 驗 機 9 於 120它下進行¢50 1 1 分 鐘 之 加 熱 殺 m 處 理 妖 < t »> 後 按 照 下 列 標 準 評 估 容 器 外 觀 η 1 1 〇 示 外 觀 無 W 化 • 内 容 物 亦 無 洩 漏 現 象 广 1 1 X 示 外 觀 發 生 W 形 杻 曲 〇 訂 1 另 外 貯 存 該 容 器 30曰 後 再 啓 用 1 按 下 述 標 準 進 行 評 1 1 估 0 1 I 0 示 内 容 物 之 色 香 等 均 無 變 化 0 1 X 示 内 容 物 之 色 香 等 發 生 變 化 C· 1 | 1 1 按 照 表 1 2中所示 配 方 tb 率 * 將 各 成 分 用 韓 蘇 混 合 機 温 1 I 合 S 再 使 用 曰 本 製 鋼 公 司 製 品 之 TEX- 30型 雙 軸 擠 壓 m i 依 1 1 據 表 1 2中 所 示 條 件 下 進 行 熔 融 混 練 而 得 組 成 物 0 1 1 該 組 成 物 之 錠 粒 用 備 有 圓 筒 形 模 頭 之 5 0 Hi ί 徑 之 卑 軸 擠 1 I 壓 機 1 在 擠 筒 設 定 溫 度 3 5 0 °C , 螺桿旋轉速度60r P (V 下 熔 融 1 I 擠 壓 j 由 直 徑 5 0 in BI , 模 唇 間 距 1 5 Q η， 模頭設定溫度3 4 8 t ! 1 | 之 圓 筒 形 模 頭 向 上 方 擠 出 熔 融 樹 脂 量 隨 λ 乾 燥 '.f U· 氣 於 該 简 1 1 本紙張尺度適用中國國家標率（CNS ) A4規格（2丨0X297公釐） 66 3 8 7 0 1 經濟部中央標準局員工消費合作社印製 A7 B7 五、發明説明（65 ) 狀薄膜之中空處，使筒狀薄膜膨脹，逐次冷却後，經夾辊 以捲取速度1 5 IB / m i η ,製得液晶聚酯樹脂組成物薄膜。 薄膜在縱向方向之拉伸倍率為2 . 9 ,吹脹比率為3 . 2。 又，厚度、摺曲性、透氣性等物性示於表12中。 使用真空壓空成肜機於加熱溫度330 f下，將該薄膜 成形為]20X 200cm,深度為3 0mBi之方形容器。 所得容器外觀良好。該容器之深徑比率，摔落衝擊試 驗，加熱殺®試驗等結果示於表]2。 fch較例25 將組成改為表1 2所示之外.其餘均按照實施例2 1.所示 同樣方法進行熔融混練，再進行吹脹成膜，但無法製得良 好的薄膜。 審饰例22The obtained ingots were mixed with foaming composition having the composition shown in Table 11. After that, a single-shaft extruder equipped with a T-die of the Tanabe Plastic Heating Machinery Co., Ltd. was set at a temperature of 2 9 7 UC at the extrusion barrel, and the screw speed was maintained. 2 0 r ρ m, die set temperature 2 97 ° C. T-die set with lion 100nia, T-die with gap gap of 3mm to produce foamed board Η. The physical properties of the obtained board are shown in Table 1. U 3 8 70 1 This paper size applies Chinese National Standard (CNS) A4 (210 × 297 mm) 5 9 017 A7 B7 V. Description of the invention (6 3) Central standard of the Ministry of Economic Affairs Printed by the Bureau ’s Consumer Cooperatives 45> 1 Lecture Conversation gt > > Miiaa, Epl (sprs E505 (141¾ Human (100 tn = 77r core (-``KmiK (ίΝ) Μ. ^ Si) 萚 洚 冰) ^ Porch | + note one forging is suitable_ Comparative Example 24 Comparative Example 23 Example 20 C〇1 ΓΟ A-2 100 05 X ΓΟ 1 Ingredient (A) Composition (% by weight) 〇〇M IN Office 1 1 »· Ingredient (B) to * —1 〇〇-1 Other ingredients C-2 8.0 i C-2-8.0 CO 3 " 1 EO Foaming agent t2: Weight part: 0.98 (g / cc) Density 550 1490 1050 (kg / c si2) MD tensile strength C71 〇〇-0 < — * LO% (%) MD elongation 190 910 930 (kg / cnt2) TD tensile strength CO CO 1— »fC < jn (%) elongation Rate to 1.8 (MO / TD) tensile resistance | strength ratio XX 〇 Foam molding i-body shape i- Ϊ1 (Please read the precautions on the back before filling this page) The paper size of the paper is applicable to the Chinese National Standard (CNS) Α4 specification( 210 × 297 mm) 3 8 7 0 1 A7 B7 Printed by the Consumers ’Cooperative of the Central Bureau of Standards of the Ministry of Economic Affairs 5. Description of the invention (64) 1 I Evaluation of the container used for m-bags according to the following methods: 0 J 1 I Deep Diameter ratio: round container refers to the depth of the container and the uphill of the container □ 1 1 tb ratio between diameters «square container refers to the depth of the container and the longest diagonal length of the π part of the container N 1 I Please read the tb ratio between I degrees C I read 1 | Drop resistance test-After the container is filled with water and sealed with a cover material * After 1 1 HI quotient on the back of the 1st drop check the impact of m. Case C. Note that 1 I M. Heat 1 p (r 〇rt) Test; Item 1 guide 1 Appearance: Fill the molded product container with commercial coffee _ sealed with a cover material-r ·. Cover Use a temperature and pressure high-pressure conditioning sterilization tester 9 at 120 ° 50 1 1 minute heating to kill m treatment monsters < t »> Then evaluate the container appearance according to the following criteria η 1 1 〇 shows that the appearance is not W • Content There is no leakage phenomenon. 1 1 X shows that the appearance of W-shaped warping occurs. 0 Order 1 In addition, store the container 30 days before use. 1 Evaluate according to the following standards. 1 1 Evaluate 0 1 I 0 No change in color, fragrance, etc. 0 1 X shows the change of color, fragrance, etc. of the contents C · 1 | 1 1 According to the formula tb ratio shown in Table 1 2 * The ingredients are mixed with a Korean-Soviet mixer 1 I and S, and then TEX products manufactured by Benben Steel are used. -30-type biaxial extrusion mi 1 1 according to the conditions shown in Table 1 2 melt-kneading to obtain the composition 0 1 1 The ingot of the composition is used with a 5 0 Hi cylinder equipped with a cylindrical die Of Shaft extrusion 1 I Press machine 1 Set temperature at extrusion barrel 3 5 0 ° C, Screw rotation speed 60r P (Melting at V 1 I Extrusion j by diameter 50 0 in BI, Die lip pitch 1 5 Q η, Die set The temperature is 3 4 8 t! 1 | The cylindrical die head extrudes the amount of molten resin upwards and dries with λ '. F U · Gas to the Jane 1 1 This paper size is applicable to China National Standard (CNS) A4 specifications (2丨 0X297mm) 66 3 8 7 0 1 Printed A7 B7 by the Consumer Cooperatives of the Central Standards Bureau of the Ministry of Economic Affairs 5. Description of the Invention (65) The hollow space of the film is expanded, and the cylindrical film is expanded. The take-up speed was 15 IB / mi η to prepare a liquid crystal polyester resin composition film. The stretch ratio of the film in the longitudinal direction was 2.9, and the inflation ratio was 3.2. In addition, physical properties such as thickness, bending property, and air permeability are shown in Table 12. The film was formed into a square container with a depth of 30 mBi by using a vacuum pressure forming machine at a heating temperature of 330 f. The resulting container had a good appearance. The depth-to-diameter ratio, drop impact test, and heat-kill® test of the container are shown in Table 2]. fch Comparative Example 25 The composition was changed to those shown in Table 1 2 except that the rest were melt-kneaded in the same manner as shown in Example 2 1. and then blown to form a film, but a good film could not be obtained. Trial example 22

組成分配方比率改為表1 2所示條件之外，其餘皆依照 實施例2 1所示相同方法進行熔融混練，所得錠粒經由模頭 間隙1.5mm,模頭寬度6 5 0ιη«π,楔頭設定溫度之T模 熔融擠壓，經由夾棍設定溫度為170 t之夾棍後捲取薄膜， 所得薄膜物性示於表1 2。然後，使用真空壓空成形機於加 熱溫度2 3 6 t下，將該薄膜成形為上部口徑6 0 m m ,底部口 徑5 0 m «ι ,深度8 0 m ra之圓形杯子，其外觀良好而無杻曲現象 。其評估結果示於表1 2 c 比較JL2A 替代實施例22之組成物，改用甲-2之外，其餘皆抟照 實施例2 2所示相同條件進行熔融混練，所得錠粒按照宵施 本紙張尺度適用中國國家標準（CNS ) Λ4規格（210X297公釐） 6 7 3 8 7 0 1 (請先鬩讀背面之注意事項再填寫本頁) -β 459 03 7 A7 B7 經濟部中央標準局員工消費合作社印製 五、 發明説明（ 66 ) 1 1 例22所示 相 同 條 件 下 經 由 T 模 熔 融 擠 壓 0 所 得 板 Η 物 性 示 1 1 於 表 12 C 該 板 Η 試 用 實 施 例 22所 示 柑 同 條 件 進 行 容 器 之 成 1 I 形 製 造 » 但 無 法 製 得 良 好 之 成 形 物 0 請 1 1 奮施例23 先 鬩 讀 1 按 照 表 12中 所 示 組 成 之 外 * 其 餘 皆 依 照 實 施 例 2 m 示 背 面 1 之 1 同 樣 方 法 進 行 熔 融 混 練 C 所 得 錠 經 由 模 頭 間 隙 1 . 2 πι m c 注 意 1 1 模 頭 寬 度 65 0m 模頭設定溫度3 0 3 1C 之 T 楔 熔 融 擠 壓 * 經 項 1 填 丄 棍 設 定 溫 度 為 1701之夾棍捲取薄膜， 該薄膜之物性示於 寫 本 頁 装 表 I 1 2 〇 V^ 1 繼 之 i 於 該 f# 膜 上 塗 布 以 東 洋 M 〇 r t on 公 司 製 造 的 雙 液 1 I 型 硬 化 聚 胺 m % 粘 著 劑 A D315 , 待溶劑乾燥後在塗布面上 1 I 層 積 以 2 5 U mii度之東洋紡續公司製造的聚對苯二甲酸乙 1 訂 [ 二 酯 薄 膜 E 500 0 , 於 2 4 0 下 加 熱 加 壓 而 得 稹 層 薄 膜 C 該 Ϊ4 1 1 膜 再 經 模 壓 加 工 而 成為6 0 X 67 01 i 深 度 為 10 之 方 形 容 器 1 1 C 其 評 估 結 果 示 於 表 12 C 1 | 明 Μ 效 本 發 明 之 液 晶 聚 m 樹 脂 組 成 物 具 備 優 異 的 耐 熱 性 成 1 1 形 加 X 性 機 槭 性 質 ， 尤 其 是 耐 衝 擊 性 、 拉 伸 物 性 特 別 優 1 1 異 » 可 改 善 成 形 物 之 各 向 異 性 0 同 時 價 廉 又 能 改 善 成 膜 加 t 1 工 性 ，因此， 由該組成物所製成薄膜， 具備非常優良的阻 1 I 氣 拉 伸 性 * 耐 m 曲 性 耐 針 孔 性 1 同 時 其 表 面 張 力 亦 j i | 大 C 發 揮 上 述 特 性 可 廣 於 使 甩 於 成 形 物 容 器 管 子 、 板 Η 1 1 1 1 殺 菌 軟 袋 > 纖 維 塗 布 材 料 d 食 品 藥 品 電 子 器 材 1 1 等 包 裝 用 薄 膜 〇 1 本紙張尺度適用中國國家標率（CNS ) A4規格（210 X Μ ?公釐） 68 3 870 1 9 5The composition distribution ratio was changed to the conditions shown in Table 12. The rest were melt-kneaded according to the same method as in Example 21. The obtained ingots passed through the die gap of 1.5 mm, the die width of 6 5 0 η π, wedge. The T-die at the set temperature was melted and extruded, and the film was taken up through a clamping stick with a setting temperature of 170 t. The physical properties of the obtained film are shown in Table 12. Then, using a vacuum pressure forming machine at a heating temperature of 2 3 6 t, the film was formed into a round cup with an upper diameter of 60 mm, a bottom diameter of 50 m «ι, and a depth of 80 m ra. The appearance was good and No curling. The evaluation results are shown in Table 1 2 c. Compare the composition of JL2A instead of Example 22, and use A-2 instead. The rest are melt-kneaded according to the same conditions as shown in Example 2 2. Paper size applies Chinese National Standard (CNS) Λ4 specification (210X297 mm) 6 7 3 8 7 0 1 (Please read the precautions on the back before filling out this page) -β 459 03 7 A7 B7 Staff of Central Standards Bureau, Ministry of Economic Affairs Printed by a consumer cooperative V. Description of the invention (66) 1 1 The same conditions as shown in Example 22 are obtained through a T-die melt extrusion. 0 The properties of the plate 示 are shown in Table 12 C. The plate is used in the same conditions as in Example 22 Carry out the container 1 I-shaped manufacturing »but can not produce a good shaped product 0 Please 1 1 Fen Example 23 First read 1 According to the composition shown in Table 12 * The rest are in accordance with Example 2 m 1 Melt and knead in the same way C The ingot obtained through the die Gap 1. 2 π mc Note 1 1 Die width 65 0m Die set temperature 3 0 3 1C T-wedge melt extrusion * Warranty item 1 Fill the stick with a set temperature of 1701 to roll the film. The physical properties of the film are shown On the writing page, install the table I 1 2 0V ^ 1 followed by i on this f # film coated with the two-liquid 1 I-type hardened polyamine m% adhesive A D315 manufactured by Toyo Mortor on, wait for the solvent to dry On the coating surface, 1 I was laminated with polyethylene terephthalate manufactured by Toyobo Co., Ltd. at a degree of 2 5 U mii [diester film E 500 0, and heated and pressed at 240 to obtain a pseudo-layer film. C This Ϊ4 1 1 film is then molded into a 6 0 X 67 01 i square container with a depth of 10 1 1 C The evaluation results are shown in Table 12 C 1 | Ming M The liquid crystal poly m resin composition of the present invention has Excellent heat resistance into 1 1 The properties of X-forming organic maple, especially the impact resistance and tensile properties are particularly excellent. 1 1 Differential »Can improve the anisotropy of the formed product 0. At the same time, it can improve the workability of film formation and t 1 at low cost. Therefore, this composition The film made of the material has very good resistance 1 I gas stretchability * resistance to m bending resistance pinhole resistance 1 At the same time its surface tension is also ji | Big C The above characteristics can be widely used to make the container pipe, Board Η 1 1 1 1 Sterilized soft bag > Fiber coating material d Food and pharmaceutical electronic equipment 1 1 Packaging film 〇1 This paper size is applicable to China National Standard (CNS) A4 specification (210 X Μ? Mm) 68 3 870 1 9 5

TT

7 7 A B 五、發明説明（67 ) ^ wiiN-a- s^§n^$i 經濟部中央標準局員工消費合作社印製 實施例23 比較例沈 實臟2 比較例26 實施例21 〇> ^ 〇〇 i eo s -ffl ° ώ S f ro 05 i os 上 ^ 1 組成(重量％) 乙-2 32 ο 乙-2 10 1 〇 ro IN ^ t 成分 乙 〇 ο ο ro 4¾. o -1 其他 成分 GO 〇 cn <Γ\ 〇〇 g OO δ Ca> -1 擠筒設 定溫度 (V) 1 -1 熔解混練條件 3 μ·»! ο t—<* 含 1—» o 3霜窃 a m m g 1«» ro ο ΐΟ ro 不能成膜 CO ΐΟ κ 调 m 8 s Ο < 10,000 \/ h··* s s o 1 N/ pM* o s o 摺曲試驗㈣ -1 >100,000 < 10,000 >100,000 1 V s § ο k? ο o f o 03 05 ^ s' * m ο ΓΟ ο μ—* o 1—* I o a& ·、ί CQ e >魏 •w 3ff *砘 ϊο 不能 成膜 o 0〇 1 2/23.3 深徑比 〇 1 o I 〇 捭落 試驗 〇 i o f 〇 遍 加熱殺菌 ο I 〇 1 O 内容物 S2 (請先閱讀背面之注意事項再填寫本頁) -裝 訂 本紙張尺度適用中國國家標準（CNS ) A4規格（2]0Χ297公釐） 69 3 8 7 0 17 7 AB V. Description of the invention (67) ^ wiiN-a-s ^ §n ^ $ i Printed by the Consumer Cooperatives of the Central Bureau of Standards of the Ministry of Economic Affairs Example 23 Comparative Example Sink 2 Comparative Example 26 Example 21 〇 > ^ 〇〇i eo s -ffl ° FREE S f ro 05 i os on ^ 1 composition (wt%) B-2 32 ο B-2 10 1 〇ro IN ^ t ingredient B〇ο ο ro 4¾. O -1 Other ingredients GO 〇cn < Γ \ 〇〇g OO δ Ca > -1 Extrusion set temperature (V) 1 -1 Melting and kneading conditions 3 μ · »! Ο t— < * Contains 1—» o 3 Frost theft ammg 1 «» ro ο ΐΟ ro cannot form a film CO ΐΟ κ tone m 8 s Ο < 10,000 \ / h ·· * sso 1 N / pM * oso flex test -1 > 100,000 < 10,000 > 100,000 1 V s § ο k? Ο ofo 03 05 ^ s' * m ο ΓΟ ο μ— * o 1— * I o a & ·, ί CQ e > Wei • w 3ff * 砘 ϊο Can not form a film o 0〇 1 2 / 23.3 Depth-to-diameter ratio 〇1 o I 〇Drop test 〇iof 〇pass heat sterilization ο I 〇1 O Content S2 (Please read the precautions on the back before filling this page) Standard (CNS) A4 specification 2] 0Χ297 mm) 6938701

Claims (1)

__ 經濟部中央標準局員工福利委員會印製 附 州一 2 H3 X：7 第86101862號專利申請案 ;i： 申請專利範圍修正本 一種液晶聚酯樹脂組成物，其中含有65 量 (甲）成分之液晶聚酿作為連纊相，Μ及35.0〜0.1重 % (乙）成分之具備與液晶聚酯有反應性的功能基之 橡膠作為分散相而成者；其中（乙）成分中之與液晶聚酯 有反應性的功能基係環氧基，噁唑基或胺基。 2 .如申請專利範圍第1項之液晶聚酷樹脂組成物，其中 含有？0〜98重量？ί (甲）成分之液晶聚酯以及30〜2重量 % (乙）成分之具備與液晶聚酯有反應性的功能基之橡 膠而成者。 3. 如申請專利範圍第1項之液晶聚醅樹脂組成物，其中（ 乙）成分中之與液晶聚酯有反應性的功能基係環氧基。 4. 如申請專利範圍第3項之液晶聚酿樹脂組成物，其中（ 乙）成分係由（甲基）丙烯酸酯-乙烯-不飽和羧酸縮水甘 油基酯及/或不飽和縮水甘油基醚共聚合物橡膠而成 者。 5. 如申請專利範圍第4項之液晶聚酯樹脂組成物，其中（ 乙）成分中之（甲基）丙烯酸酯係含有由丙烯酸甲酿，甲 基丙烯酸甲酯，丙烯酸正丁酯，甲基丙烯酸正丁酯， 丙烯酸第三丁酯，甲基丙烯酸第三丁酯，丙烯酸2 -乙 基己酯，甲基丙烯酸2 -乙基己酯選出的至少一種者。 6. 如申請專利範圍第4項之液晶聚酯樹脂組成物，其中（ Β)成分係由40重量％以上，未滿97重量％之（甲基）丙 本紙張尺度適用中國國家標準（CNS )Α4規格（ 210X 297公釐）1 3 8 7 0 1 經濟部中央標準局員工福利委員會印製 _____H3_ 烯酸酯單位，3重虽？^以上未滿50重量％之乙烯單位以及0.1〜30重量？ί之不飽和羧酸縮水甘油基酯及/或不 飽和縮水甘油基醚單位而成旳共聚合物。7. 如申請專利範圍第3填之液晶聚酯樹脂組成物，其中（ 乙）成分之孟納粘度係在3〜70範圍者。8. 如申請專利範圍第4項之液晶聚酯樹脂姐成物，其中（ 乙）成分之孟納粘度係在3〜30範圍者。 9. 如申請專利範圍第3項之液晶聚酯樹脂組成物，其中.( 乙）成分係由Μ乙烯系芳族烴化合物為主體之（a)鐽區 與以共軛系二烯化合物為主體之（b)鍵區而成的嵌段共 聚合物經環氧化而得的橡膠，或該嵌段共聚合物之加 氫化合物經環氧化而得的橡膠。10. 如申請專利範圍第1項之液晶聚醅樹脂組成物，其中（ 甲）成分之液晶聚酯係含有下式__ Printed Fuzhou No. 2 H3 X: 7 Patent Application No. 86101862 by the Staff Welfare Committee of the Central Bureau of Standards of the Ministry of Economic Affairs; i: The scope of the patent application is amended by a liquid crystal polyester resin composition containing 65 parts (a) of the Liquid crystal polymerization as the flail phase, M and 35.0 ~ 0.1% by weight (B) The rubber with a functional group reactive with the liquid crystal polyester is prepared as the dispersed phase; of which (B) of the component is polymerized with the liquid crystal The ester has a reactive functional group which is an epoxy group, an oxazolyl group or an amine group. 2. If the liquid crystal polymer resin composition of item 1 of the patent application scope contains, 0 ~ 98 weight? (1) A liquid crystal polyester of the component (A) and a rubber having 30 to 2% by weight (B) of a component having a functional group reactive with the liquid crystal polyester. 3. For example, the liquid crystal polyfluorene resin composition in the scope of patent application, wherein the functional group of the component (B) which is reactive with the liquid crystal polyester is an epoxy group. 4. The liquid crystal polyresin composition according to item 3 of the patent application, wherein the (B) component is composed of (meth) acrylate-ethylene-unsaturated carboxylic acid glycidyl ester and / or unsaturated glycidyl ether Made of copolymer polymer rubber. 5. The liquid crystal polyester resin composition according to item 4 of the patent application, wherein the (meth) acrylate in the (B) component contains methacrylic acid, methyl methacrylate, n-butyl acrylate, methyl At least one selected from n-butyl acrylate, third butyl acrylate, third butyl methacrylate, 2-ethylhexyl acrylate, and 2-ethylhexyl methacrylate. 6. For example, the liquid crystal polyester resin composition in the scope of patent application No. 4 in which the component (B) is composed of 40% by weight or more and less than 97% by weight of (meth) acrylic paper. The Chinese National Standard (CNS) Α4 specifications (210X 297 mm) 1 3 8 7 0 1 Printed by the Staff Welfare Committee of the Central Standards Bureau of the Ministry of Economic Affairs _____H3_ acrylate units. ^ Ethylene units above 50% by weight and 0.1 to 30% by weight? The unsaturated glycidyl carboxylic acid ester and / or the unsaturated glycidyl ether unit form a fluorene copolymer. 7. For the liquid crystal polyester resin composition filled in the third patent application scope, the (B) component has a Menner viscosity in the range of 3 to 70. 8. For example, the liquid crystal polyester resin product of item 4 of the patent application, in which the (B) component has a Menner viscosity in the range of 3 to 30. 9. For example, the liquid crystal polyester resin composition of the scope of application for patent No. 3, in which (B) is composed of (a) a fluorene region and a conjugated diene compound as the main component, which are mainly composed of M vinyl aromatic hydrocarbon compounds. (B) A rubber obtained by epoxidizing a block copolymer formed by a bond region, or a rubber obtained by epoxidizing a hydrogenation compound of the block copolymer. 10. For example, the liquid crystal polyfluorene resin composition of the scope of patent application, wherein the liquid crystal polyester of the component (a) contains the following formula c OUO ^ 者 % 耳 莫 ο 3 之 揖 整 占 少 至 位 單 構 结 複 重 的 示 表 中 其 物 成 組 脂 樹 酷 聚 晶 液 之 項 第 圍 範 利 專 請 Ψ 如 甲 芳 與 醇 元二 族 芳 及 酸 羧二 族 芳 由 係 酯 聚 晶 液 之 分 物 成 組 脂 樹 酯 聚 。 晶 者液 得之 製項 而 1 應第 反圍 經範 酸利 羧專 基請 羥申 族如甲 中 其 經 酸 羧 基 羥 族 芳 的 類 -f ί 種 同 不 合 組 係 酯 聚 晶 液 之 分 成 中 其 物 成 姐 脂 樹 酯 聚 晶 液 之 項 li 。 第 者 圍 得 範 利 βττ3Λ 而 專 應 請 反 申 予 如 本紙張尺度適用中國國家標準（CNS )Α4規格（210Χ 297公纪 2 3 8 7 0 1 H3 甲）成分之液晶聚酯係由下式c OUO ^ %% 莫莫 ο 3 in the table shows that the structure of the unitary structure is complex and the weight of the structure is shown in the table. It is composed of a group of fatty resins. The two-group aromatics and acid-carboxylic two-group aromatics are composed of the ester polycrystalline liquid to form a resin resin. According to the product obtained from the crystal solution, 1 should be divided into the basic formula of the acid and carboxylic acid, and the hydroxyl group of the hydroxyl group, such as the aromatic carboxyl group of the hydroxyl group -f. It is the item li of sister resin polycrystalline liquid. The first one is Fan Li βττ3Λ and should be counter-claimed. If this paper size applies the Chinese National Standard (CNS) A4 specification (210 × 297 cm 2 3 8 7 0 1 H3 A), the liquid crystal polyester is based on the following formula: -〇—CH2CH7 〇-c-^SVcsi II 〇 〇-〇-CH2CH7 〇-c- ^ SVcsi II 〇 〇 經濟郎中央標準局員工福利委員會印製Printed by the Employees' Welfare Committee of the Central Standards Bureau 表示的重複结構單位而成者。 15.如申請專利範圍第1項之液晶聚酯樹脂組成物，其中（ 甲）成分之液晶聚酯係由下式 本紙張娜中國国觀祕嫌（膨細3 3 8 7 0 1 459037 H3 c =〇Represented by repeating structural units. 15. The liquid crystal polyester resin composition according to item 1 of the scope of patent application, wherein the liquid crystal polyester of the component (A) is composed of the following formula. = 〇 者 成 而 位 單 構 结 複 重 的 示 表 中 其 物 成 組 脂 樹 酯 聚 晶 液 之 項 1* 第 圍 IB Asn 利 專 請 申 如 甲 式 下 由 係 0 聚 晶 液 之 分The structure of the unitary structure is shown in the table. The item of the resin resin polycrystalline liquid is 1 * No. IB Asn. Please apply as follows: CUO 經濟部中央標芈局員工福利委t貝會印製 用 用成 可 可製 , , 而 物 物伸 成 成拉 組 組軸 脂 脂雙 樹 樹或 醅 酯伸 聚 聚拉 。 晶 晶軸 者液 液單 成之 之經 而項 項再 位 1 1 壓 單第 第擠 構圍 。圍融 结範者 範熔 複利 膜利模 重專薄 專 T 的請 成請由 示申 製申經 表如 於如於 者 膜 薄 用 用脂 可 可樹 ， , 酯 物 物聚 成 成晶 組 組液 脂 脂該 樹 樹括 酯 酯包 聚。聚不 晶者 晶與 液 膜液膜 之 薄之薄 項 成項的 1 製 1 成 第 而第而 園 形圍物 範 成範成 利脹利組 專 吹專該 請 Μ 請由 申 加申將 如於如於 本紙張尺度適用中S國家標準（CNS)A4規格（210X 297公货）4 3 8 7 0 1 459 H3 經濟部中央標準局員工福利委w會印製 層中酯醛合烯類 中及共 該 中 中帶 中徑及上 曆 其酸縮聚乙種 其物經 由。其。其物 其直度以 二 ，碳聚共 .一 ，成脂 中者 ，者 ，載 .口深10 少 物聚-烴 醚少 物組樹 其 科物 物物花 物器器1/ 至 成-酯烯硫至 成脂性 * 材成裝成壓 成容容為 經 組烯二 -基之 姐樹塑 物装組包組及 組 及-率 , 脂乙丁 f 苯出 脂酯熱 成包脂件脂帶 脂度中比 膜 樹苯酸烯伸選 樹聚之 組用樹組樹蓋 樹深器之 薄 酯聚甲乙聚等 酯晶内 酯袋酯子酯覆 酯器容間 的聚 ，二 ，-脂 聚液在 聚軟聚 電聚之 聚 容形度 成 晶烯苯 砸烯樹 晶將物 晶菌晶 於晶成 晶 ，方長 而 液丙對醚乙氟 液頭成。液殺液用液製。液 中外線 脂。之聚聚 聚氯含 之模組 者之於 之係之 所者之 器另角 樹者項 ， ， ，二 ， 項壓脂膜 項用項 膜項膜 物項容 -對 性膜20烯酯醚偏物21擠樹薄 1 係 1 薄 1 薄裝 1 形上長 塑薄第乙二 基聚合 第共酯狀第膜第的第的包第圓以最 熱狀圍 聚乙苯 -聚 圍 之聚層 圍薄圍 成圍得件園得10之 的層 範由酸 伸烯共 範 上晶積 範的範 而範而 組範所1/分 内積利脂甲聚乙酯 利M液成利成利物利物子利 物為部 在成 專樹二.，氯烯。專層 該製專 而專成 專成電 專成率Π 物 構請性苯胺聚 乙者請雙括而 請物請 組請組於請 驵比開 成而申 塑對醯 * 酸成申 用包壓 申成申 該申該 用申該 之器。 姐積如熱聚聚物乙 而如使不擠如組如由如由係如由間容者 本紙張尺度適用中國國家標準（CNS)A4規格（210X297公釐）5 3 8 7 0 1 ____H3_27.如申請專利範圍第1項之液晶聚醒樹脂組成物，其中Μ由該姐成物而成的板片或薄膜為覆蓋材料，藉此粘著 封酷 密聚 申脂 如樹 者 器 容 用 袋 軟 有 容 收 於 成範 組利 脂專 樹請 物 成 組CUO, the Ministry of Economic Affairs, the Central Bureau of Standards and Welfare Committee of the Welfare Committee of the Ministry of Economic Affairs will print the use of cocoa, and the objects are stretched into the pull group of the group of lipid trees, or polyester esters. The crystal axis is the history of the formation of liquid and liquid elements, and the terms are repositioned. Fans who can melt the compound fan, compound film, mold, thin film, T, please apply for the application form, such as the fat cocoa tree, thin film for the film, the esters are aggregated into a crystal group Liquid-lipid resins include ester-polyester-coated polymers. The polycrystalline crystal and the thin and thin item of the liquid film and the liquid film are made into a 1-by-1 form, and the garden-shaped enclosures Fan Cheng Fan Chengli and the profit-making group are specifically invited to apply. Please apply by Shen Jiashen As in this paper, the national standard (CNS) A4 specification (210X 297 public goods) is applicable to this paper standard. 4 3 8 7 0 1 459 H3 The esters and alkenes in the printing layer of the Central Bureau of Standards and Staff Welfare Committee of the Ministry of Economic Affairs The middle diameter of the middle and middle band and the history of its acid polycondensation are through. its. The straightness of the object is two, the carbon is co-polymerized, the one that is fattening, the one, and the carrier. The mouth depth is 10. The poly-hydrocarbon ether is less. The tree is a family of things. Esterene sulfide to fat-forming property * Material is packed into a compacted package containing the diene-based sister tree plastic packaging package and the group and the rate, the diethyl butyrate f phenylene ester thermally formed fat-coated parts Polyester with a specific ratio of membrane phthalic acid in the lipid band. The group of trees is used to cover the depth of the tree. The thin esters of polymethyl methacrylate and other esters of lactones and esters are covered with polyester. -The lipopolyester is formed into a crystalline styrene, styrene, benzene, and benzene crystalline tree by crystallizing the polyacrylamide, and the liquid crystal is formed by liquid acrylic acid and ethyl fluoride liquid. Liquid killer is made of liquid. Liquid and external fat. The poly-polychloride-containing modules are based on the nature of the system, and the other angles are the items, ,,, and two. Lipid-pressing membranes. Partial 21 Squeeze the tree thin 1 Series 1 Thin 1 Thin package 1 Shapely long plastic thin ethylenediyl polymer co-ester-like film No. of the first circle of the first circle to surround the polystyrene-polystyrene polymer layer The thickness of the thin layer is 10 layers. The range of the product range is 10. The range of the crystal product range on the acid range is the same as the range of the product range. Liverpool and Liverpool is a ministry tree, Chlorene. The level of the system, the level of the system, the level of the system, the rate of the industry, the structure of the request, aniline polyethylene, please enclose, please ask for the group, please set the group, please compare the open and apply for plastics. Shen Cheng applied for the application. The sister product is like thermal polymer B and if it is not crowded, it is not as tight as the group. If you are by the system, the size of this paper applies the Chinese National Standard (CNS) A4 specification (210X297 mm) 5 3 8 7 0 1 ____H3_27. For example, the liquid crystal polymer resin composition of the first patent application scope, in which the plate or film made of the product of the sister is used as a covering material, so as to adhere to a tightly sealed polystyrene resin container bag. Soft and content in the Cheng Fan group =口 申 部 D 第 物 成 晶酲菌 液聚殺 之 。晶於 項者液用 26器 4 # 第^.^|< 器 軺 利*«·4;ί^1> 専分 現„,,除ί—= Department of Oral Application Department D, the crystal formation fungus solution to kill. Crystals used in Xiangzhe 26 26 4 # ^^ 用 係 物 成 組 脂 樹 酯 聚 晶 液 之 項 1Λ 第 圍 範 利 專 請 甲 如 者 器 容 物 形 成 空 中 於 中 其 物 成 組 脂 樹 篚 聚 晶 疲 之 項 1Χ 第 園 範 利 專 請 申 如 0 聚 晶 液 該 括 包 不 及 以 層 一 少 至 的 成 而 物 成 姐 該 由 構 係 層 一 少 至 之 物 成 ΓΠ"} 脂 樹 性 塑 熱 的 內 在 物 成 組 脂 樹 者 器 容 物 形 成 空 中 成 成 〇 組 者 脂成 樹製 酯而 聚彤 晶 成 液塑 之吹 項藉 30係 第器 或 容 項 物 29形 第成 圍 空 範中 利該 專中 請其 申 , 如物 中 其 物 成 組 脂 樹 酯 聚 晶 液 之 項 ο 3 第 圍 範 利 專 請 申 如 為 度 密 係 脂 樹 性 塑 熱 7 2 為 度 占 ί— 限 極 經濟部中央標準局員工福利委員备Η印製 中 其 物 。 成者 姐 器 脂容 樹用 酯料 聚燃 晶 成 液構 。 之 於 者項用 烯30係 乙第器 聚圍容 度範物 密利形 高專成 之請空 /g申中 dl如該 本纸張尺Α適用中國國家棉準（CNS )Α4規格（210X297公货）6 3 8 7 0 1 __ 經濟部中央標準局員工福利委員會印製 附 州一 2 H3 X：7 第86101862號專利申請案 ;i： 申請專利範圍修正本 一種液晶聚酯樹脂組成物，其中含有65 量 (甲）成分之液晶聚酿作為連纊相，Μ及35.0〜0.1重 % (乙）成分之具備與液晶聚酯有反應性的功能基之 橡膠作為分散相而成者；其中（乙）成分中之與液晶聚酯 有反應性的功能基係環氧基，噁唑基或胺基。 2 .如申請專利範圍第1項之液晶聚酷樹脂組成物，其中 含有？0〜98重量？ί (甲）成分之液晶聚酯以及30〜2重量 % (乙）成分之具備與液晶聚酯有反應性的功能基之橡 膠而成者。 3. 如申請專利範圍第1項之液晶聚醅樹脂組成物，其中（ 乙）成分中之與液晶聚酯有反應性的功能基係環氧基。 4. 如申請專利範圍第3項之液晶聚酿樹脂組成物，其中（ 乙）成分係由（甲基）丙烯酸酯-乙烯-不飽和羧酸縮水甘 油基酯及/或不飽和縮水甘油基醚共聚合物橡膠而成 者。 5. 如申請專利範圍第4項之液晶聚酯樹脂組成物，其中（ 乙）成分中之（甲基）丙烯酸酯係含有由丙烯酸甲酿，甲 基丙烯酸甲酯，丙烯酸正丁酯，甲基丙烯酸正丁酯， 丙烯酸第三丁酯，甲基丙烯酸第三丁酯，丙烯酸2 -乙 基己酯，甲基丙烯酸2 -乙基己酯選出的至少一種者。 6. 如申請專利範圍第4項之液晶聚酯樹脂組成物，其中（ Β)成分係由40重量％以上，未滿97重量％之（甲基）丙 本紙張尺度適用中國國家標準（CNS )Α4規格（ 210X 297公釐）1 3 8 7 0 1Use the system to form a group of resin resin polycrystalline liquid item 1 Λ No. Fan Li specially asks a person such as the container to form an object in the air to form a group of fatty resin poly crystal fatigue item 1 × No. Fan Li special application For example, 0 polycrystalline liquid should not be included as much as a layer, but it should be made from a structure layer as few as possible. ΓΠ "} The internal plasticity of the resin is composed of the resin of the resin. Forming a group of 0 into a group of fat into a resin ester and polycrystalline crystal into a plastic blown by the 30 series of equipment or items 29 form the enclosure of the empty fan Zhongli invited the application, such as Item of the group of resin resin polycrystalline liquid ο 3 Fan Li specially requested to apply for the degree of dense resinous plastic heat 7 2 for the degree of accountancy-Seal of Staff Welfare Committee of the Central Standards Bureau of the Ministry of Economy Making things in the system. Sisters and sisters of the fat-condensation tree use polyesters to burn and crystallize into liquid structure. For those who use the ene 30 series of the second device poly-enclosed content range of the Milli-shaped high-level college, please empty / g Shen Zhong dl If this paper rule A applies to China National Cotton Standard (CNS) A4 specifications (210X297 Public goods) 6 3 8 7 0 1 __ Printed by Fuzhou No. 2 H3 X: 7 Patent Application No. 86101862 for Employee Welfare Committee of the Central Standards Bureau of the Ministry of Economic Affairs; i: The scope of the patent application is to amend a liquid crystal polyester resin composition. Among them, liquid crystal polymerization containing 65 content of (a) component is used as the flail phase, and M and 35.0 to 0.1% by weight (b) of rubber having a functional group reactive with liquid crystal polyester is used as the dispersed phase; (B) Among the components, the functional group reactive with the liquid crystal polyester is an epoxy group, an oxazolyl group, or an amine group. 2. If the liquid crystal polymer resin composition of item 1 of the patent application scope contains, 0 ~ 98 weight? (1) A liquid crystal polyester of the component (A) and a rubber having 30 to 2% by weight (B) of a component having a functional group reactive with the liquid crystal polyester. 3. For example, the liquid crystal polyfluorene resin composition in the scope of patent application, wherein the functional group of the component (B) which is reactive with the liquid crystal polyester is an epoxy group. 4. The liquid crystal polyresin composition according to item 3 of the patent application, wherein the (B) component is composed of (meth) acrylate-ethylene-unsaturated carboxylic acid glycidyl ester and / or unsaturated glycidyl ether Made of copolymer polymer rubber. 5. The liquid crystal polyester resin composition according to item 4 of the patent application, wherein the (meth) acrylate in the (B) component contains methacrylic acid, methyl methacrylate, n-butyl acrylate, methyl At least one selected from n-butyl acrylate, third butyl acrylate, third butyl methacrylate, 2-ethylhexyl acrylate, and 2-ethylhexyl methacrylate. 6. For example, the liquid crystal polyester resin composition in the scope of patent application No. 4 in which the (B) component is composed of 40% by weight or more and less than 97% by weight of (meth) acrylic paper. The Chinese National Standard (CNS) Α4 size (210X 297mm) 1 3 8 7 0 1
TW86101862A 1996-02-19 1997-02-18 Liquid crystal polyester resin composition TW459037B (en)