TW449648B - Unassemble threaded article having cured deformable coating and method of manufacturing the same - Google Patents
Unassemble threaded article having cured deformable coating and method of manufacturing the same Download PDFInfo
- Publication number
- TW449648B TW449648B TW89105236A TW89105236A TW449648B TW 449648 B TW449648 B TW 449648B TW 89105236 A TW89105236 A TW 89105236A TW 89105236 A TW89105236 A TW 89105236A TW 449648 B TW449648 B TW 449648B
- Authority
- TW
- Taiwan
- Prior art keywords
- item
- threaded
- scope
- patent application
- article
- Prior art date
Description
449648 五、發明說明（1) 發明筋.圊 本發明大體上係關於表面具備預塗敷密封劑之物件範圍 更特別地’本發明關於具有塗層或硬化材料層之螺紋物 件’其中塗層或硬化材料層係為充分可變形以便與對應之 螺紋部件相配對。 才.1關技街簡4 為了密封及閉鎖内組裝部件之目的，使用液態可聚合或 可硬化物質係在該技藝為習知。在早期，螺紋閉鎖组合物 係在裝配内組裝部件之前不久或裝配時以液態形式塗敷。 僅在配對之部件閉鎖後，組合物係以濕式塗敷並且硬化。 但是，此種閉鎖組合物不適用於許多需要高裝配速率以及 大量生產的工業（例如汽車工業）應用β 因此於這些工業已發展出使用預塗敷密封劑以及閉鎖塗 層。由於具備許多優點的緣故，預塗敷密封劑塗層目前在 此種工業上確實較佳。最初發展的預塗敷密封劑或閉鎖塗 層係沉積在螺紋扣件上，乾燥以緊鄰塗層，其中未硬化之 可聚合流體則在扣件上之乾塗層中結為膠囊或結成薄膜。 使用對應的螺紋部件（例如螺帽）裝配扣件造成微膠囊塗層 或薄膜破裂，並且造成其下之可聚合流體暴露於固化條件 下，例如無氧硬化作用。 舉例來說，美國專利U.S. Patent No. 4,325, 985描述 一種方法，其中一種可聚合的流體材料沉積在螺紋部件上 ，並且一種分開的流體薄膜形成覆套則立刻在此後塗敷其 上，藉著短暫暴露於輻射下（例如紫外線-可見光輻射）形
4 49 6fzt^ 修正 五、發明說蜗一 成細薄、固態、乾燥、不黏的薄膜。輻射硬化之流體薄膜 形成覆套則沿著深度而硬化，使可聚合之閉鎖材料保持流 體態，以便接著使配對之螺紋部件硬化。輻射可硬化之薄 膜係為一種設計為乾燥以及不黏的保護膜。 美國專利U.S. Patent No, 4, 632，944描述一種用於螺 紋閉鎖物件上雙重的硬化組合物。最初的硬化機構係藉由 例如紫外輻射光之輻射作用而引發。一種遮光劑（例如粉 末）則分散在其中，促使可聚合的溶液對表面層以外的輻 射呈不透明狀。因此乾燥不黏的外殼形成於表面上。一旦 二個工程部件裝配合一後，則之後在所剩的可聚合流體上 開始進行第二個聚合機構。 預塗敷扣件（即在螺紋上具備密封劑或閉鎖組合物之扣 件）正常係為整批運送。有時以散裝運送，其係裝載在容 器中或直接彼此接觸。依賴流體副層上保護膜之預塗敷扣 件有使運送容器中或儲存中之薄膜破裂的可能性，通常的 情況是可聚合之組合物漏出，成為無用的部件。由於洩漏 的緣故，扣件可彼此黏著，或者由於未硬化之液體污染外 部的緣故，扣件不易控制。在此種情形中，使扣件產物成 為無用。此外，由可聚合流體圍繞之薄層通常不是最終可 聚合組合物之整體部件。所生成的黏合力比不上僅單獨為 可聚合流體時最大。 已發展出另一種以未硬化液體形成薄膜之預塗敷螺紋閉 鎖產物的變體4為了密封的目的，完全硬化之乳膠塗層係 為已知的選擇之一。硬化之乳膠塗層未受到可聚合液體-之
O:\63\63068.ptc 第5頁 2001.04. 23. 005 449648 五、發明說明（3) 可能破裂，但是製 箱硬化達45分鐘或 係為使用氣艘加熱 循環。溫度通常係 方式是耗成本的， 烘箱外罩移動）開c 性。亦必須留意使 溫度。當存在生成 切成片狀並且除去 上升溫度並且使扣 必要的。此外，乳 ，特別是倘若暴露 乳膠層未擁有進一 需求的能力。 造是昂貴@ ’因為需要在相當高溫之烘 更久今日工業上所使用最普遍的方法 烘箱° 一般強制熱空氣係在烘箱内罩中 維持在155卞（68。〇 + /-1〇卞。此種乾燥 且其相對上隨著輪送帶（在傳統的工業 2之輸入與輸出端的熱損而增加無效率 溫度不達到造成塗層表面上產生蒸汽的 物時，附著完整性受到妥協，且塗層將 螺紋部件，同時產生不欲的外觀。控制 件均勾加熱，以避免水分去除太快便是 膠塗層有時變脆，並且在儲存期間剝落 在未控制的環境條件下。另外，乾燥之 步物理上適合或轉變為螺紋應用上特定 很明顯地存在對未裝配之螺紋物件的需求，其係為一種 不具備上述缺點之預塗敷物。 發明摘要 本發明係提供此種螺紋物件，以及製造螺紋物件的方法 。本發明亦&供一種使用本發明之螺紋物件之密封方法。 本發明涉及未組裝（即未聯接）之螺紋物件，例如螺帽、 螺栓、螺桿、管件等，其中至少—部分的螺紋有一種硬化 之可變形密封劑或閉鎖材料黏合之塗層。密封劑組成物係 以未硬化形式塗敷至螺紋上，且較佳係為塗敷在物件之螺 紋溝槽’並且為了完全使組合物硬化之組裝之螺紋單元上
449648 五、發明說明（4) 的固態可變形之螺紋黏合塗層，t封劑組合物受到硬化侔 件作用(即較佳為光輕射作用(例如紫外 ς二= 已= 2變形性提供已塗佈之螺紋與相= ^佈或未塗佈之螺紋物件（例如螺帽與螺栓組裝）衡接。 j配對之螺紋配件組裝期間’使密 銜接…乎沒有漏失“ in:及母聯接組裝溝針，並且由於=4 彈以及黏合特徵而提供流體緊密的密封性。因 溝槽紋部件相配部件(例如螺帽與螺栓)之螺紋 卜’、。此使對應之螺紋部件配對同時保留密封劑 =可能的。當，然’本發明亦涵蓋每一種應配封劑 螺帽與螺栓）之螺紋溝槽之塗層c t發明亦關於製造一種未組裝之螺紋物件的方法 物件螺紋溝稽上具備硬化之可變形固態密: 紋明之密封劑在與另外的螺紋物件配對前可完全在螺 件上硬化。這是與先前技藝主要的變更…組 個螺紋部件組裝後完全硬&。密封劑之可變^ 對應之螺紋配件配對。由於密封劑硬化的緣故使 w彼此緊鄰儲存，例如裝在大容器中以及船運使用， I需害怕未硬化之密封劑破裂或鄰近的部件黏在， 2卜，由於使用硬化條件的緣故’例如光硬化作用，杜 未經昂貴的熱硬化烘箱可快速且有效率地硬化，因：
$ 7頁 d 4964 8 hH-修正 _案號89105236 彳c年心月日 dk補充_ 五'發明說明（5) 地減少能耗、製造物件的期間以及製造之總成本。 圖式簡述 圖1係為未組裝之螺紋公部件之透視圖，其係以扣件形 式，包含螺紋溝槽中之硬化之可變形組合物。 圖2係為在螺紋溝槽顯現出硬化密封劑組合物之扣件之 橫切面。 圖3係為螺帽形式之未組裝螺紋母部件之透視圖。 圖4係為在螺紋溝槽顯示硬化可變形密封劑之圖3之橫切 面。 圖示符號簡單說明 1 0表示一公螺紋物件； 1 1表示一母螺紋物件； 1 2表示外螺紋； 1 3表示螺紋溝槽；及 14表示光硬化之可變形密封劑組合物。 發明詳述 許多密封劑可使用並且適用特定螺紋中部件或應用之方 法。以特殊硬度計測量之硬化密封劑的可變形性及彈性 體彈性提供符合特定目的之螺紋物件的適合性。 用於本發明之硬化之固態密封劑組合物包含彈性體之可 變形材料，例如矽酮、胺基甲酸酯、矽酮-丙烯酸酯、胺 基甲酸醋-丙烯酸醋、共聚物及其組合。硬化组合物可涵 蓋充足部分之螺紋物件的螺紋溝槽，當物件配對時提供欲 形成之密封性。通常將珠狀組合物施加於螺紋溝槽附近並 且經由暴露在光輻射下硬化。當可使用任一種適當的硬化
O:\63\63068.ptc 第8頁 2001.04.27.008 449 6 4 8 案號 89105236 吁c年匕月彡〇曰
五、發明說明（6) 機構時，為了實際考量以使用UV輻射作用為較佳’並且此 種硬化機構得到製造效率以及成本有效性。 —種用於本發明之U V可硬化之矽酮組合物的實例述於美 國專利U.S. Patent No· 5,300,608 (Chu) ’ 其係合併於 本文以供參考。此中所述之光可硬化之矽酮組合物包含以
O:\63\63068.ptc 第8a頁 2001.04.27. 009 44964 8 五、發明說明（6) 下式表示之烷氧基終端之有機聚碎氧垸： I -|HO' R2
(R^B
I (R5〇)3.<e+b)—Si—Ο- mb (R3)a -**Si-(0R^)3，(a+tj) (R4)b 其中R1、R2、R3及R4可為相同或相異，並且具有至多為l〇個 碳原子（<νΗ )之單償烴基、或鹵基或氰基取代之烴基；胪 亦可為具有至多為10個碳原子（Cho)之單價異烴基，其中 雜原子係為選自包含雜原子、〇、N所組成者；R5為烷基 (Ct_10)，較隹為甲基、乙基或異丙基；R5亦可為CH2CH2〇ch3 1為整數，a為0、1或2 ;b為0、1或2 ;且a + b為0、ι或2 。在一個特別合宜的具體實施例中，R3為曱基丙烯氧丙基 ，R4及R5為甲基，且R1及R2為甲基。烷氧基終端之有機聚石夕 氧烷可用’608專利所述之方法製備。 大體上’螺紋物件上經聚合之塗層或外層係為·—種級人 物的反應產物’其中該组合物包含約35%至約99.5%，且較 佳為約40%至約80%之硬化時可為具撓性及可變性的可硬化 聚合物；以及包含約0.5至約1〇%之適合的觸媒或自由基引 發劑。視需要而定，可包含至多為約6 5%之一或更多種填 充劑及添加劑。 在一個合宜的具體實施例令，可變形的硬化材料為一種 密封劑，其係包含一或更多種聚合的聚有機矽氧烷聚合物 及光引發劑。舉例來說’有用的可聚合之聚有機矽氧烷包
Η 449648 五、發明說明（7) 含且不限於曱基丙烯氧烷基二曱氧矽烷氧基終端之聚（二 甲基矽院氧）聚合物（例如丙烯氧甲基二甲氧矽烷氡基終端 之聚（二甲基矽烷氧））以及甲基丙烯氧丙基二甲氧甲矽烷 氧基終端之聚（二甲基矽烷氧），以及其組合物。其餘亦涵 蓋在根據前述’605專利之化學式中。 上述雙重硬化之聚合物可使用輻射、水分硬化或二者之 組合而完全硬化。為了達到有效輻射之目的，最佳可使用 例如UV及/或可見光輻射。 有效的光引發劑包含二苯甲酮及取代之二苯甲酮、乙醯 笨甲酮及取代之乙醯苯甲酮、二苯乙醇酮（benzoin)及其· 烧基酯、夾氧雜蒽酮（xanthone)及取代之夾氧雜蒽酮。合 宜之光引發劑包含二乙氧-乙醯苯曱酮、二苯乙醇酮曱醚 、二乙氧夾氧雜蒽酮、氯硫基夾氧雜蒽酮、偶氮雙異丁腈 及其組合。可見光引發劑包含comphoroquinone過氧醋引 發劑及a-芴羧酸過氧酯。特別合宜的光引發劑包含2-羥-2-甲基-1'"苯基-丙-1_ 明（講自 Darocur 1173 (EM Industries, Inc.))及2-1 基-2-(二甲胺基）-1-[ 4-嗎啉 苯基]-卜丁酮（購自 Irgacure 369 (Ciba-Giegy))。使用 足量之光引發劑以完成硬化作用，其用量以重量計通常為 約0. 5%至約10%。 有用的水分硬化觸媒包含金屬鹽類，其一般係選自鈦、 錫、锆及其組合物。即使亦可使用許多其他的觸媒（例如 述於美國專利U.S. Patent No. 4，111，890 )且在此合併於 本文以供參考，但是例如四異丙氧鈦酸鹽及四丁氧鈦酸鹽
第10頁 449648 五、發明說明（8) 特別有效。使用充足量之光引發劑以完成硬化作用， 量以重量計通常為約〇丨％至約丨。 ’、 在使用過氧自由基引發劑的情况中，此種化合物 ：如=苯過氧化氯、對“(par· —。 過氧化氫以及水解為過氧化氫之醋類 二甲酸㈣β過氡化物通常存在量以重 量計為約0.5%至約1〇% β 個合宜的具體實施例中’可變形的硬化材料包含 =胺基甲酸醋聚合物。有效的聚胺基甲酸醋聚合物包 含胺基甲酸酯-丙酸酸酯，例如脂肪募聚物，其係當硬化 時充分地變形以達到本發明之目的。這些聚合物使用量以 1量計可為約35%至約95%，且較佳以重量計為約嫩至約 6〇%。其可藉由超過一個機構製配而硬化。倘若必要時， 可藉由例如光學輻射以及室溫硬化作用β 其他有效的聚合物包含烯烴彈性體化合物，兑係當硬化 ，符合所需的可變形性以及符合密封需求。例如，可使用 =乙烯-丁二烯共聚物、丁基橡膠以及聚硫橡膠。本發明 亦涵蓋可充分變形以用於螺紋部件之熱塑性聚合物。極硬 及/或脆之可聚合成分通常不能用於本發明中，因為者裝 配時其易碎，且*能產生有效的密封。此外，部件組田裝是 =困難且不實用的，其係由於當配對之螺紋聯接時部件組 ^不能變形以及不能符合，造成使硬化之樹脂分開並且毀 壞螺紋上的塗層是必要的。 當運載硬化聚合物之螺紋部件配對時，由於施加摩擦力
第11頁 449648 五、 發明說明 (9) 的 緣 故 用 於 本發 明 之 硬化 聚 合 物 可部 分切 片 或 切 割0 狄 而 ， 該 聚 合 物 預 期 為 具 備充 分 韌 性 以及 撓性 ， 避 免粉碎 以 及 保 留 足 夠 的 黏 合 結 構以 及 對 螺 紋部 件充 分 的 附 著性 以 便 提 供 相 配 對 螺 紋 間 之密 封 功 能 ，且 在某 些 情 況 下伴 隨 閉 鎖 功 能 0 密 封 功 能 較 佳係 為 阻 擋 氣流 或流 體 9 因 此， 表 面 塗 敷 硬 化 材 料 之 發 明 的物 件 可 應 用在 例如 管 件 上 以及 其 他 涉 及 螺 紋 配 件 聯 結（其中液體或氣體可能逃逸） 之 機械 應 用 上 Q 用 來 形 成 本發 明 螺 紋 物件 上 之 硬 化材 料之 可 聚 合 聚合 組 成 物 可 包 含 大 範 圍 之 額 外的 藥 劑 例如 硬化 加 速 劑 ，即 第- 二 及 第 二 有 機 胺 有 機 金屬 錯 合 物 以及 技藝 中 已 知 之硫 醯 亞 胺 0 其 通 常 用 量 以 重 量計 為 約0. 1至約5% 其 他 添 加 劑 包含增 稠 劑、 增 塑 劑 、染 料、 潤 滑 劑 、稀 釋 劑 氣 味掩 蔽 劑 、 螯 合 劑、 抑 制 劑 、黏 著促 進 劑 Η 彈性 體 等 等 Q 最 佳 之 活 性 稀釋 劑 包 含例 如 丙 稀 酸異 莰酯 丙 醯 酸乙 氧 乙 酯 、 Ν， Ν- 甲 基 -丙稀醯胺、 丙稀酸四氫呋喃酯等化合 物 0 矽 院黏 合 促 進 劑 亦 有 效， 且 其 係 包含例如 六 甲 基 二石夕 烧 % 氧 曱 環 氧 丙 基 三 甲 氧 矽烷 、 胺 丙 基-三甲氧矽烷、 曱基 丙 烯 氧 丙 基 二 曱 氧 矽 炫 以及 其 他 習 知該 技藝 人 士 所 知之 化 合 物 Q 可 用 許 多 方 式 完 成 可 聚合 之 組 合 物對 螺紋 部 件 之 塗敷 Ο 最 佳 者 係 採 白 動 生 產 方 式塗 敷 0 浸 潰、 喷霧 成 粒 或其 他
Mi HU 44964 8 五、發明說明（10) 塗敷方式是有效的。螺紋部件之充分部分的螺紋通 部件配對時進行密封下塗敷。螺紋之塗敷量視物件之幾 形狀、尺寸以及所欲之塗敷而定。 可 在本發明的一個較佳具體實施例中，係使用一種uv 化之丙烯酸矽_醋Μ合物，當其完全在螺紋部件硬化4硬 係充分變形以便緊密地與對應之配對螺紋部件銜接。上 配件係以能夠顯現密封功能之方式配對，而未破壞 2 之總黏聚力以及結構完整性。例如以此方式銜接之管；： 現出抗軋壓1 00- 1 2 0 psi之有效密封性。此種組合物供 螺帽及螺栓以及其他螺紋構件高速製造的能力，其可1 裝線或輸送帶上對齊，並且快速地曝在訂光下。在丙歸酸 矽酮S旨可聚合化合物的情形中，任何偶然不能在uv曝照 間硬化之部分隨後在室溫下以大氣濕氣硬化。較佳為在螺 紋配件組裝前達到完全硬化。 、 在許多具體實施例中，本發明之經硬化的可變形材料具 體範圍為約25至約35之Shore硬度，以及約50%至約300%之 伸長量。在某些具體實施例中，Sh〇re硬度範圍在25至35 亦是有效的。硬度範圍將是所選用可聚合材料之函數。 本發明之螺紋物件可具有多種的金屬及/或塑膠表面。 例如可涵蓋不銹鋼、青鋼、鎳、鋁、鋅等。亦涵蓋磷酸鹽 、漆以及許多電鍍表面 '即使對許多應用而言是常見的， 但是在塗敷以及使表面可變形密封劑硬化前去除油污或清 潔扣件通常是不必要的。 回到圖式上
圖1顯示未組裝之公螺紋物件丨〇之透視圖
第13頁
修正 補充 4 49 64 8 _案號 891Q5236 五 '發明說明（12) ’其係為在表面上具備外螺紋1 2之扣件形式《部分螺紋以 及螺紋溝槽塗敷並填充光硬化之可變形密封劑組合物丨4。 圖2顯示沿著扣件縱轴之橫切面’同時顯示在溝槽1 2之密 封劑1 4。 圖3顯示母螺紋物件（π)，其在螺紋溝槽13中亦包含密 封劑1 4。圖4係為圖3之橫切面。 圖1之公螺紋扣件1 0與對應之母螺紋部件丨丨銜接，以形 成扣件組合《密封劑組合顯現在此銜接部件二者，但是實 際上可能僅在部件之一出現β通常為了應用方便，密封劑 係施加在公構件上。 螺 種類 緊密 本 商業 化組 硬化 至螺 。本 片， 本 說明 紋管 ，螺 密封 發明 化實 合物 之可 紋溝 發明 並且 發明 ，否 接合 紋充 性。 之塗 施。 塗敷 變形 槽表 之物 幾乎 可參 則重 係為另一個特別合宜的應用β不論螺紋物件 分覆蓋確保適當密封性，且較佳為得到流體 敷法非 在光硬 後接著 組合物 面，以 件未受 適當地 照以下 量百分 常快 化作 輻射 。硬 便抵 到硬 維持 非限 比係
組合物A 速，並且提供高速率之生產以及 用為選擇方法的情形中，在可硬 為較佳’以得到螺紋物件上完全 化之可變形密封劑需適當地黏著 插部件配對並且提供其密封功能 化密封劑（通常為乳膠塗層）之切 塗敷至螺紋物件之整體部件。 制之實例進一步瞭解。除非特 依據總密封劑組合物而定。 實例1
4 49 64 8 案號 89105236 年丄匕I %年4月；。曰I 修正 五、發明說明（13) 51 18 3 25 丙烯氧曱基二甲基矽烷基終端之聚 (二曱基石夕烷氧） 沉澱之矽土填充劑 黏著促進劑 曱基丙烯氧丙基二曱氧矽烷基終端之聚 (二甲基矽烷氧） 光 引 發劑 3 100 組 合 物B 反 應 稀釋 劑 49. 脂 肪 族丙 烯酸胺基曱酸酯寡聚物 45. 螢 光 染料 0. 濕 潤 劑 0. 光 引 發劑 4. 氣 味 遮蔽 劑 0. 100
組合物Β具有Shore D-2硬度為27，且伸長量為2 0 0-240%。 組合物C 曱基丙烯氧烷基二甲氧矽氧烷基終端之聚 94.0 (二甲基矽烷氧） 3. 1 1 0. 光引發劑 螢光染料 黏著促進劑 四異丙基鈦酸鹽
O:\63\63068.ptc 第15頁 2001.04. 27.016 4 d9 6 4 8 五、發明說明（13) 1 00 組合物D 反應稀釋劑 A e r 〇 s i 1石夕土增稠劑 丙烯酸乙酯彈性體 染料 光引發劑 脂肪族丙烯酸胺基曱酸酯寡聚物 黏著促進劑 42. 5 2 2 49. 4 100
組合物E 丙烯氧甲基二甲基矽烷基終端之聚 54 (二甲基矽烷氧） 沉澱之矽土填充劑 19 黏著促進劑 3 曱基丙烯氧丙基二曱氧矽烷基終端之聚 20 (二曱基矽烷氧） 光引發劑 _4 100 組合物F (市售乳膠3) 去離子水 27.71 表面活性劑 0.4 丙烯酸乳膠1 34.03
O:\63\63068.PTD 第16頁 和年4月j·
4 4 9 6 4 8 __案號 89105236 五，發明說明（15) 抗泡劑 防独制 殺真菌劑 填充劑/潤滑劑 顏料 氫氧化銨（增稠劑） 丙烯酸乳膠2 0.01 17.92 6.05 0.6812.0 100 ]Rhioplex MV-17K, Rohm & Haas 2 Acrysol ASE-6 0, Rohm & Haas 3 Vibraseal™, Loct i te Corporation 組合物G 反應稀釋劑 氣味遮蔽劑 螯合劑 光引發劑 胺基甲酸丙烯酸酯募聚物 滑劑 39 0. 5 0.1 0.75 59.55 半吋螺紋鋼製插座之螺紋溝槽分別塗佈組合物A_F。 組合物A-E係使用50 mw之UV輻射進行光硬化作用1分鐘 。組合物F(市售乳膠組成物，商品名為Vibraseal #516) 在1 5 8 °F之烘箱乾燥3 0分鐘。插座經裝配至對應的管件T型
O:\63\63068.ptc 第17頁 2001.04. 27.018
89105236 彻年斗月外日 修正 結果如以下表 管，並且在加壓下進行密封特性壓力試驗 1 & 2所示。 表1 密封試驗結果 密封劑组合物 插座#1 插座#2 C 密封的 密封的 E 密封的 漏出的 D 漏出的 漏出的 F 密封的 密封的 表2 密封試驗結果 密封劑组合物 T型裝配（2插座/T型） 90 psi空氣壓測試結果 A 插座#1 無漏出 A 插座#2 無漏出 B 插座#1 無漏出 B 插座#2 無漏出 實例3 本發明之方法提供改良的製造速率，其係由於UV硬化密 封劑之硬化速率所致。下表與係比較以同樣重量為基準之
O:\63\63068.ptc 第18頁 2001.04. 24.018 4 4a£JLB——Ί 89105236 $(?年4月ηί日 修正 aey 同量材料的乳膠丙烯酸乳化劑之烘箱乾燥速率對光可硬化 矽酮組成物之U V硬化速率。 硬化數據之產生係使用Loctite UV Curing Wand System, 983675。12毫米硬化斑點之產生係藉由將一β寸之 棍捧尖端3/4固定在塗佈表面。相對有效之輻射光在365 nm 下經測得5 0毫瓦/平方公分之輸出。同量之螺紋溝槽覆蓋 用在每一個扣件上。這些結果強調本發明之總功效以及方 便性。硬化速率以及總功效可經由適用複合的輻射來源而 進一步提高》 表3 硬化速率 扣件大小 烘箱時間 UV硬化 #10/M5 22分 25秒 1/4 M6 28分 35秒 5/16/M7&M8 32分 45秒 3/8/M9 & M8 40分 50秒 7/16/M11 42分 60秒 1/2/M12 45分 70秒 9/16/M14 54分 95秒 5/8/M16 60分 115秒 此中描述之本發明可以許多方式變化。此種變化不視為 偏離本發明的精神，並且意欲涵蓋在以下申請專利範圍。
O:\63\63068.ptc 第19頁 2001.04.24.019
Claims (1)
- 449b4b _案號89105236_如年年月曰_修正Γ 六、申清專利粑圍 L—-----3 1 .—種具硬化之可變形塗層之未組裝螺紋物件，係包含 提供對應螺紋配對部件銜接之螺紋表面，其中該螺紋表面 上具備一種聚合之固態材料，當組裝時該聚合之固態材料 係經充分變形，以符合並提供與該對應之螺紋配對部件組 裝，並且提供其間密封及/或閉鎖銜接性。 2. 如申請專利範圍第1項之物件，其中該聚合之固態材 料包含選自包含由矽酮、胺基曱酸酯、丙烯酸矽酮酯、丙 烯酸胺基甲酸酯、聚烯烴及共聚物，以及其組合。 3. 如申請專利範圍第1項之物件，其係為外部螺紋構件 之形式。 4. 如申請專利範圍第1項之物件，其係為内部螺紋構件 之形式。 5. 如申請專利範圍第1項之物件，其係為螺栓、螺桿、 螺帽、導管或軟管之形式。 6. 如申請專利範圍第1項之物件，其中該聚合之固態材 料係為包含以下組合物之反應產物： a)以重量計為約50%至約98%之一或更多種聚有機矽氧烷 聚合物；以及 b )以重量計為約0 . 1至約5 . 0 %之濕氣硬化觸媒。 7. 如申請專利範圍第6項之物件，其中成分a )係為一或 更多種甲基丙烯氧烷基二甲氧矽烷氧基終端之聚（二曱基 氧矽烷）。 8. 如申請專利範圍第1項之物件，其中完全固態之可變 形組合物具有約10%至約300 %之伸長量。O:\63\63068.ptc 第 1 頁 2001.04.27.022 4 4 9 6 4 8 案號 89105236 心1年年月？0曰 修正 六、申請專利範圍 __无 9.如申請專利範圍第1項之物件，其中該聚合之固態材 料係為包含以下組合物之反應產物： a)以重量計為約35%至約95%可聚合之聚胺基甲酸酯聚合 物；以及 b )以重量計為約0 . 0 5至約1 0 %之光引發劑。 1 0.如申請專利範圍第9項之物件，其係進一步包含曱基 丙酸反應稀釋劑。 1 1.如申請專利範圍第1 0項之物件，其中成分a )係為一 或更多種脂肪族丙烯酸胺基曱酸酯寡聚物。 1 2.如申請專利範圍第1 0項之物件，其中甲基丙酸反應 稀釋劑係選自包含丙醢酸乙氧乙酯 酸異莰酯、N，N-二曱基-丙烯醯胺 其組合。 1 3.如申請專利範圍第1項之物件 料係為包含以下組合物之反應產物： a)以重量計為約50%至約98 %之一或更多種曱基丙烯氧烷 基二甲氧矽烷氧基終端之聚（二曱基矽氧烷）； b )以重量計為約0 . 5至約1 0 %之光引發劑；及 c )以重量計為約0 . 1至約5 . 0 %之濕氣硬化觸媒。 1 4.如申請專利範圍第1 3項之物件，其中光引發劑係選 自包含二苯曱酮、二烷氧二苯甲酮 二苯乙醇酿I、Michler_及其組合。 1 5 .如申請專利範圍第1 3項之物件 係為錫、鈦或錯之金屬鹽類。 丙醯酸羥乙酯、丙烯 丙烯酸四氫呋喃酯及 其中該聚合之固態材 二烷氧乙醯苯曱酮、 其中濕氣硬化觸媒O:\63\63068.ptc 第2頁 2001.04.27.023 修正 修正 449648 7ϋ 案號 89105236 六、申請專利範圍 1 6 ,如申請專利範圍第1 5項之物件，其中該僅屬鹽類為 四異丙氧鈦酸鹽或四丁氧鈦酸鹽。 1 7.如申請專利範圍第1項之物件，其中螺紋物件係由不 錄鋼、鋅、紹、鉻、青銅、欽、鎳、塑躍·以及其組合。 1 8, —種製造螺紋物件的方法，其中螺紋物件可緊密地 與對應之螺紋部件銜接，形成密封之组合，且該方法包含 a) 提供螺紋物件； b) 將可聚合之密封劑組合物塗敷至該螺紋物件之螺紋上 ；以及 c) 聚合該密封劑組合物，提供完全硬化之可變形薄層， 以便與其他螺紋部件相配對，提供其間之密封性。 1 9.如申請專利範圍第1項之物件，其中該聚合之固態材 料具有Shore A硬度為約25至35。 2 0.如申請專利範圍第1項之物件，其中該聚合之固態材 料具有Shore D-2硬度為約2 5 - 3 2。O:\63\63068.ptc 第3頁 2001.04.27, 024