TW202323465A - 拋光組成物及其使用方法 - Google Patents
拋光組成物及其使用方法 Download PDFInfo
- Publication number
- TW202323465A TW202323465A TW111132327A TW111132327A TW202323465A TW 202323465 A TW202323465 A TW 202323465A TW 111132327 A TW111132327 A TW 111132327A TW 111132327 A TW111132327 A TW 111132327A TW 202323465 A TW202323465 A TW 202323465A
- Authority
- TW
- Taiwan
- Prior art keywords
- weight
- polishing composition
- amine compound
- polishing
- acid
- Prior art date
Abstract
本揭露內容提供一種拋光組成物,其包括至少一第一胺、至少一第二胺以及其他組分,諸如唑。該第一胺具有一低分子量,例如120 g/mol或更低。該第二胺具有一高分子量,例如125 g/mol或更高。該等組成物可以一高銅對鉬的選擇性,來拋光包括銅及鉬或者每一者之合金的基體。
Description
本揭露內容係關於一種用於半導體產業的化學機械拋光組成物。特定而言,本揭露內容係有關於對於拋光包括銅與鉬及其合金的基體特別有利的組成物。
半導體工業不斷被驅使藉由透過製程及整合創新而進一步使裝置小型化來改良晶片效能。化學機械拋光/平坦化(CMP)係一強大的技術,因為其使許多複雜的在電晶體層級上之整合方案成為可能,藉此促進晶片密度提高。
CMP為一種用以使晶圓表面平坦化/扁平化的程序,其藉由使用基於磨蝕之物理程序同時用基於表面之化學反應來移除材料。一般而言,一CMP程序涉及對一晶圓表面施加一CMP拋光組成物(例如,一水性化學調配物)同時令該晶圓表面與一拋光墊接觸並且相對於該晶圓來移動該拋光墊。拋光組成物典型地包括一磨料組分以及溶解的化學組分,該等組分可取決於在該CMP程序期間將會與該拋光組成物以及該拋光墊相互作用之存在於該晶圓上的材料(例如,金屬、金屬氧化物、金屬氮化物、諸如氧化矽及氮化矽的介電材料等)而顯著地變化。
鉬是一種帶有極低化學反應性、高硬度、優良傳導性、強耐磨性以及高腐蝕抗性之過渡金屬。鉬也可以與其它的元素來形成雜多與合金化合物。關於其在微電子產業中的使用,鉬以及其合金可找到用途作為互連件、擴散阻障、光罩以及插塞填充材料。但是,由於其硬度、鹼性pH腐蝕易感性以及化學抗性,鉬要以一高移除率及以低缺陷率來予以拋光是困難的,其呈現一個關於含鉬基體的CMP之挑戰。
此概要係提供來介紹下文在詳細說明中進一步所描述之精選概念。此概要不意欲識別所請求標的之關鍵特徵或必要特徵,其亦不意欲用於輔助限制所請求標的之範圍。
本揭露內容係基於如下的意外發現:以一優異的腐蝕抗性之一受控方式,在一CMP程序期間,某些拋光組成物可相對於一半導體基體中的其他材料(例如,鉬)選擇性地移除銅(Cu)及/或其合金。
在一樣態中,本揭露內容的特徵為一拋光組成物,其包括:至少一磨料;至少一唑化合物;至少一第一胺化合物,該至少一第一胺化合物包含一胺基酸,其具有至多120 g/mol的一分子量;至少一第二胺化合物,其具有至少125 g/mol的一分子量;以及一水性溶劑。本揭露內容亦提供一用於拋光一基體的方法,該基體含有銅、銅之合金、鉬及鉬之合金中之至少一者。
在又另一樣態中,本揭露內容的特徵為包括下列的方法:將該先前所論述之拋光組成物施加至包含下列中之至少一者的一基體於在該基體之一表面上:包含銅、鉬、銅之一合金、鉬之一合金以及其任何組合;以及使一墊與該基體之該表面接觸且相對於該基體移動該墊。
本揭露內容係有關於拋光組成物以及使用該拋光組成物來拋光半導體基體的方法。在一些實施態樣中,本揭露內容係有關於被用來拋光基體的拋光組成物,該等基體包括至少一部分係含有銅(Cu),以及至少一部分係含有鉬(Mo)金屬。該等基體亦可或替代地包括銅之合金及/或鉬之合金。儘管銅長期以來被廣泛用作半導體基體中的一傳導組件,但鉬為半導體製造中一相對新且輕度應用的材料。鉬具有被高生產力地使用於一半導體裝置中之潛力的一塊領域,係一能有效地從一介電材料分離銅的一襯裡材料。但是,已經發現用於銅的習知拋光組成物與鉬不相容。舉例而言,它們造成高的Mo移除率以及腐蝕,包括電流腐蝕。
本揭露內容出乎意料地發現,二種胺化合物的一組合,一者具有一較高分子量(例如,大於125 g/mol)且一者為具有一低分子量(例如,低於120 g/mol)的胺基酸,在拋光包括銅與鉬兩者的基體時係為協同性的。在不受理論束縛之情況下,咸信該低分子量胺基酸作為一銅移除率增強劑作用,且具有較高分子量之該胺化合物良好地起作用以抑止鉬移除及腐蝕。在銅與鉬之間的移除率比例上的選擇性不可能基於該等胺化合物的個別表現而被預測。
圖1中示意性顯示可藉由本揭露內容之組成物拋光之一基體的一非限制性實例。基體1具有一層非傳導材料10(例如,一介電材料),其中具一溝槽20。一銅層或材料30係在溝槽20中。在一些應用中,所期望的是在溝槽20中包括一襯裡40,以從該非傳導材料分離銅層30。襯裡40可幫助防止銅電子從銅層30遷移至非傳導材料10。鉬被越來越被視為一種用於襯裡40的材料。當製造基體1時,可施加一銅覆蓋層以確保溝槽20之適當填充。因此,在拋光期間,該組成物最初可能大部分係移除銅,然後在拋光過程期間例如鉬之襯裡40的材料暴露出來時才開始移除該材料。
在一或多個實施態樣中,本文中所描述的一拋光組成物可包括:至少一磨料;至少一唑化合物;至少一第一胺化合物,該至少一第一胺化合物包含一胺基酸,其具有至多120 g/mol的一分子量;至少一第二胺化合物,其具有至少125 g/mol的一分子量;以及一水性溶劑。在一或多個實施態樣中,根據本揭露內容的一拋光組成物可包括:約0.01重量%至約50重量%的至少一磨料;約0.001重量%至約10重量%的至少一唑化合物;約0.001重量%至約18重量%的至少一第一胺化合物;約0.001重量%至約18重量%的至少一第二胺化合物;以及剩餘之重量百分比(例如,約10重量%至約99.99重量%)的一水性溶劑(例如,去離子水)。
在一或多個實施態樣中,本揭露內容提供一濃縮的拋光組成物,其可在使用之前以水來稀釋高達二倍、或高達四倍、或高達六倍、或高達八倍、或高達十倍、或高達15倍、或高達20倍。在其他實施態樣中,本揭露內容提供一使用點(POU)拋光組成物,其包含有上述的拋光組成物、水以及任擇地氧化劑。
在一或多個實施態樣中,一POU拋光組成物可包括:約0.01重量%至約25重量%的至少一磨料;約0.001重量%至約1重量%的至少一唑化合物;約0.001重量%至約8重量%的至少一第一胺化合物;約0.001重量%至約8重量%的至少一第二胺化合物;以及剩餘之重量百分比(例如,約59重量%至約99.99重量%)的一水性溶劑(例如,去離子水)。
在一或多個實施態樣中,一濃縮的拋光組成物可包括:0.02重量%至約50重量%的至少一磨料;約0.01重量%至約10重量%的至少一唑化合物;約0.01重量%至約18重量%的至少一第一胺化合物;約0.01重量%至約18重量%的至少一第二胺化合物;以及剩餘之重量百分比(例如,約4重量%至約99.98重量%)的一水性溶劑(例如,去離子水)。
在一或多個實施態樣中,本文中所描述的該等拋光組成物可包括至少一種(例如,兩種或三種)磨料。在一或多個實施態樣中,該至少一種磨料係選自由以下各者組成之群組:陽離子磨料、實質上中性磨料以及陰離子磨料。在一或多個實施態樣中,該至少一種磨料係選自由以下各者組成之群組:氧化鋁;矽氧;鈦氧;氧化鈰;氧化鋯;其等之共形成產物(亦即,氧化鋁、矽氧、鈦氧、氧化鈰或氧化鋯之共形成產物);經塗覆的磨料;經表面改質的磨料;及其混合物。在一些實施態樣中,該至少一種磨料不包括氧化鈰。在一些實施態樣中,該至少一種磨料具有一高純度,並且可具有低於約100 ppm之醇、低於約100 ppm之氨以及低於約100 ppb之一鹼性陽離子(諸如,鈉陽離子)。按一POU拋光組成物之總重量計,該磨料可以約0.01%至約12%(例如,約0.5%至約10%)或其任何子範圍之量存在。
在一或多個實施態樣中,該磨料係一種矽氧系磨料,諸如選自由以下所組成之群組的一者:膠體矽氧、燻製矽氧及其混合物。在一或多個實施態樣中,該磨料可使用有機基團及/或非矽質無機基團來予以表面改質。舉例而言,該陽離子磨料可包括式(I)之端基團:
-O
m-X-(CH
2)
n-Y (I),
其中m是一個從1至3的整數;n是一個從1至10的整數;X是Al、Si、Ti、Ce或Zr;以及Y是一個陽離子胺基或硫醇基。舉另一例而言,該陰離子磨料可包括式(I)之端基基團:
-O
m-X-(CH
2)
n-Y (I),
其中m是一個從1至3的整數;n是一個從1至10的整數;X是Al、Si、Ti、Ce或Zr;以及Y是一個酸基團。
在一或多個實施態樣中,本文中所描述的該磨料可具有一平均粒度,其係至少約1 nm (例如,至少約5 nm、至少約10 nm、至少約20 nm、至少約40 nm、至少約50 nm、至少約60 nm、至少約80 nm或至少約100 nm)到至多約1000 nm (例如,至多約800 nm、至多約600 nm、至多約500 nm、至多約400 nm、至多約200 nm或至多約150 nm)。如本文中所使用,該平均粒度(MPS)係藉由動態光散射技術來判定。在一或多個實施態樣中,該磨料可係單個化學物種(例如,矽氧粒子)之粒子,且該拋光組成物可不包括係二或更多種材料之複合物(例如,嵌入於一陶瓷基質中之矽氧粒子)的磨料。
在一或多個實施態樣中,該至少一種磨料之量係本文中所描述的該等拋光組成物之至少約0.01重量%(例如,至少約0.05重量%、至少約0.1重量%、至少約0.2重量%、至少約0.4重量%、至少約0.5重量%、至少約0.6重量%、至少約0.8重量%、至少約1重量%、至少約1.2重量%、至少約1.5重量%、至少約1.8重量%或至少約2重量%)到至多約50重量%(例如,至多約45重量%、至多約40重量%、至多約35重量%、至多約30重量%、至多約25重量%、至多約20重量%、至多約15重量%、至多約12重量%、至多約10重量%、至多約5重量%、至多約4重量%、至多約3重量%、至多約2重量%、至多約1重量%)。
在一或多個實施態樣中,本文中所描述的該等拋光組成物包括至少一種(例如,兩種或三種)唑化合物。該唑化合物不受特別限制,但是其特定實例包括:雜環唑;經取代的或未取代的三唑(例如,苯并三唑);經取代的或未取代的四唑;經取代的或未取代的二唑(例如,咪唑、苯并咪唑、噻二唑以及吡唑);以及經取代的或未取代的苯并噻唑。在本文中,一經取代的二唑、三唑或四唑係指一種藉由該二唑、三唑、或四唑中的一或二或更多個氫原子經用例如一羧基基團、一烷基基團(例如,一甲基、乙基、丙基、丁基、戊基或己基)、一鹵素基團(例如,F、Cl、Br或I)、一胺基基團或一羥基基團來取代所獲得的產物。在一或多個實施例中,該唑係選自由以下各者組成之群組:四唑、苯并三唑、甲苯基三唑、甲基苯并三唑(例如1-甲基苯并三唑、4-甲基苯并三唑及5-甲基苯并三唑)、乙基苯并三唑(例如1-乙基苯并三唑)、丙基苯并三唑(例如1-丙基苯并三唑)、丁基苯并三唑(例如1-丁基苯并三唑及5-丁基苯并三唑)、戊基苯并三唑(例如1-戊基苯并三唑)、己基苯并三唑(例如1-己基苯并三唑及5-己基苯并三唑)、5,6-二甲基苯并三唑、氯苯并三唑(例如5-氯苯并三唑)、5,6-二氯苯并三唑、1-(氯甲基)-1-H-苯并三唑、氯乙基苯并三唑、苯基苯并三唑、苄基苯并三唑、胺基三唑、胺基苯并咪唑、吡唑、咪唑、胺基四唑、腺嘌呤、苯并咪唑、噻苯達唑(thiabendazole)、1,2,3-三唑、1,2,4-三唑、1-羥基苯并三唑、2-甲基苯并噻唑、2-胺基苯并咪唑、2-胺基-5-乙基-1,3,4-噻二唑、3,5-二胺-1,2,4-三唑、3-胺基-5-甲基吡唑、4-胺基-4H-1,2,4-三唑及其組合。在不希望受理論束縛之情況下,咸信該唑化合物(諸如上文中所描述者)可用作本文中所描述的該等拋光組成物中之一有效的銅腐蝕抑制劑,以改良一半導體基體中的銅及/或其合金的及耐腐蝕性。
在一或多個實施態樣中,該至少一種唑化合物之量係本文中所描述的該等拋光組成物之至少約0.001重量%(例如,至少約0.003重量%、至少約0.005重量%、至少約0.01重量%、至少約0.03重量%、至少約0.05重量%、至少約0.1重量%、至少約0.3重量%、至少約0.5重量%、至少約1重量%、至少約1.3重量%或至少約1.5重量%)到至多約10重量%(例如,至少約9重量%、至少約8重量%、至少約7重量%、至少約6重量%、至少約5重量%、至少約4重量%、至少約3重量%、至少約2.5重量%、至多約2.2重量%、至多約2重量%、至多約1.7重量%、至多約1.5重量%、至多約1.2重量%、至多約1重量%、至多約0.7重量%、至多約0.5重量%、至多約0.2重量%、至多約0.15重量%、至多約0.1重量%、至多約0.07重量%或至多約0.05重量%)。在有一種以上的唑化合物被包括於該拋光組成物中的實施態樣當中,上述範圍可獨立地適用於每一唑化合物或者適用於在該組成物內的唑化合物之合併量。
在一或多個實施態樣中,本文中所描述的該等拋光組成物包括至少一種(例如,兩種或三種)第一胺化合物。在一或多個實施態樣中,該第一胺化合物包括一種胺基酸,其具有至多120 g/mol(例如,至多115 g/mol、至多110 g/mol、至多105 g/mol、至多100 g/mol、至多95 g/mol或至多90 g/mol)的一分子量。在一或多個實施態樣中,該至少一種第一胺化合物係選自由以下各者組成之群組:脯胺酸、甘胺酸、絲胺酸、丙胺酸或其混合物。在不希望受理論束縛之情況下,出人意料的是,該第一胺化合物可充當一用於銅之移除率增強劑。
在一或多個實施態樣中,該至少一種第一胺化合物之量係本文中所描述的該等拋光組成物之至少約0.001重量%(例如,至少約0.003重量%、至少約0.005重量%、至少約0.01重量%、至少約0.03重量%、至少約0.05重量%、至少約0.1重量%、至少約0.3重量%、至少約0.5重量%、至少約1重量%、至少約1.5重量%、至少約2重量%、至少約2.5重量%、至少約3重量%、至少約3.5重量%、至少約4重量%、至少約4.5重量%或至少約5重量%)到至多約18重量%(例如,至多約16.5重量%、至多約15重量%、至多約12.5重量%、至多約10重量%、至多約8重量%、至多約6重量%、至多約5重量%、至多約4.5重量%、至多約4重量%、至多約3.5重量%、至多約3重量%、至多約2.5重量%、至多約2重量%、至多約1.5重量%、至多約1重量%、至多約0.8重量%、至多約0.6重量%、至多約0.5重量%、至多約0.4重量%、至多約0.2重量%、至多約0.1重量%、至多約0.08重量%、至多約0.05重量%、至多約0.02重量%、至多約0.01重量%、至多約0.0075重量%或至多約0.005重量%)。
在一或多個實施態樣中,本文中所描述的該等拋光組成物包括至少一種(例如,兩種或三種)不同於該第一胺化合物的第二胺化合物。在一或多個實施態樣中,該第二胺化合物具有至少125 g/mol(例如,至少130 g/mol、至少135 g/mol、至少140 g/mol、至少145 g/mol、至少150 g/mol、至少155 g/mol、至少160 g/mol、至少165 g/mol或至少170 g/mol)的一分子量。在一或多個實施態樣中,該第二胺化合物係一胺基酸。在一或多個實施態樣中,該第二胺化合物係一個烷基胺。在一或多個實施態樣中,該第二胺化合物係選自由以下各者組成之群組:組胺酸、苯丙胺酸、麩醯胺酸、天冬胺酸、麩胺酸、精胺酸、酪胺酸、(3-胺基丙基)二乙醇胺、辛胺、癸胺、十二胺、十四胺、十五胺、十六胺、十八胺、環己胺、二環己胺、腺嘌呤、黃嘌呤、胸腺嘧啶、鳥嘌呤、異鳥嘌呤、次黃嘌呤或其混合物。
在一或多個實施態樣中,該至少一種第二胺化合物之量係本文中所描述的該等拋光組成物之至少約0.001重量%(例如,至少約0.003重量%、至少約0.005重量%、至少約0.01重量%、至少約0.03重量%、至少約0.05重量%、至少約0.1重量%、至少約0.3重量%、至少約0.5重量%、至少約1重量%、至少約1.5重量%、至少約2重量%、至少約2.5重量%、至少約3重量%、至少約3.5重量%、至少約4重量%、至少約4.5重量%或至少約5重量%)到至多約18重量%(例如,至多約16.5重量%、至多約15重量%、至多約12.5重量%、至多約10重量%、至多約8重量%、至多約6重量%、至多約5重量%、至多約4.5重量%、至多約4重量%、至多約3.5重量%、至多約3重量%、至多約2.5重量%、至多約2重量%、至多約1.5重量%、至多約1重量%、至多約0.8重量%、至多約0.6重量%、至多約0.5重量%、至多約0.4重量%、至多約0.2重量%、至多約0.1重量%、至多約0.08重量%、至多約0.05重量%、至多約0.02重量%、至多約0.01重量%、至多約0.0075重量%或至多約0.005重量%)。在不希望受理論束縛之情況下,出人意料的是,上文中所描述的該第二胺化合物可以顯著地降低鉬腐蝕(例如,降低Mo靜態蝕刻率),且亦降低在一基體上的銅及鉬之介面處的電流腐蝕之可能性。
在一或多個實施態樣中,本文中所描述的該等拋光組成物,若有需要,可包括至少一種(例如,兩種或三種) pH調節劑以將該pH調節至一所欲數值。在一些實施態樣中,該至少一種pH調節劑可以是一種酸(例如,一種有機酸或無機酸)或一種鹼(例如,一種有機鹼或無機鹼)。舉例而言,該pH調節劑可係選自由以下所組成之群組:硝酸、氫氯酸、硫酸、丙酸、檸檬酸、丙二酸、氫溴酸、氫碘酸、過氯酸、氨、氫氧化銨、氫氧化鈉、氫氧化鉀、氫氧化銫、單乙醇胺、二乙醇胺、三乙醇胺、甲基乙醇胺、甲基二乙醇胺、氫氧化四丁基銨、氫氧化四丙基銨、氫氧化四乙基銨、氫氧化四甲基銨、氫氧化乙基三甲基銨、二乙基二甲基氫氧化銨、氫氧化二甲基二丙基銨、氫氧化苄基三甲基銨、氫氧化三(2-羥乙基)甲基銨、氫氧化膽鹼及其任何組合。
在一或多個實施態樣中,該至少一種pH調節劑之量係本文中所描述的該等拋光組成物之至少約0.001重量%(例如,至少約0.005重量%、至少約0.01重量%、至少約0.05重量%、至少約0.1重量%、至少約0.2重量%、至少約0.4重量%、至少約0.5重量%、至少約1重量%或至少約1.5重量%)到至多約2.5重量%(例如,至多約2重量%、至多約1.5重量%、至多約1重量%、至多約0.5重量%、至多約0.1重量%或至多約0.5重量%)。
在一或多個實施態樣中,本文中所描述的該等拋光組成物可係酸性的或者係鹼性的。在一些實施態樣中,該等拋光組成物可具有在至少約2到至多約11之範圍內的一pH。舉例而言,該pH的範圍可係至少約2(例如,至少約2.5、至少約3、至少約3.5、至少約4、至少約4.5或至少約5)到至多約11(例如,至多約10.5、至多約10、至多約9.5、至多約9、至多約8.5、至多約8、至多約7.5、至多約7、至多約6.5、至多約6、至多約5.5、至多約5、至多約4.5或至多約4)。當該等拋光組成物是酸性的,該pH的範圍可係至少約3(例如,至少約3.5、至少約4、至少約4.5、至少約5、至少約5.5、至少約6或至少約6.5)到至多約7(例如,至多約6.5、至多約6、至多約5.5、至多約5、至多約4.5或至多約4或至多約3.5)。當該拋光組成物呈鹼性時,該pH的範圍可係至少約7.5(例如,至少約8或至少約8.5)到至多約11(例如,至多約10.5、至多約10或至多約9.5)。
在一或多個實施態樣中,本文中所描述的該等拋光組成物可包括一種溶劑(例如,一種主要溶劑),諸如一水性溶劑(例如,水或者一包括水以及一有機溶劑之溶劑)。在一些實施態樣中,該溶劑(例如,水)之量係本文中所描述的該等拋光組成物之至少約10重量%(例如,至少約15重量%、至少約20重量%、至少約25重量%、至少約30重量%、至少約35重量%、至少約40重量%、至少約45重量%、至少約50重量%、至少約55重量%、至少約60重量%、至少約65重量%、至少約70重量%、至少約75重量%、至少約80重量%、至少約85重量%、至少約90重量%、至少約92重量%、至少約94重量%、至少約95重量%或至少約97重量%)到至多約99重量%(例如,至多約98重量%、至多約96重量%、至多約94重量%、至多約92重量%、至多約90重量%、至多約85重量%、至多約80重量%、至多約75重量%、至多約70重量%或至多約65重量%)。
在一或多個實施態樣中,一種任擇的輔助溶劑(例如,一有機溶劑)可以被使用於本揭露內容的該等拋光組成物(例如,一POU或濃縮的拋光組成物)之中,其可幫助一成分(例如,一含唑腐蝕抑制劑)的溶解。在一或多個實施態樣中,該輔助溶劑可以是一或多種醇、伸烷基二醇或伸烷基二醇醚。在一或多個實施態樣中,該輔助溶劑包含有一或多種溶劑,該溶劑係選自由以下各者組成之群組:乙醇、1-丙醇、2-丙醇、n-丁醇、丙二醇、2-甲氧基乙醇、2-乙氧基乙醇、丙二醇丙基醚以及乙二醇。
在一些實施態樣中,該輔助溶劑之量係本文中所描述的該等拋光組成物之至少約0.005重量%(例如,至少約0.01重量%、至少約0.02重量%、至少約0.05重量%、至少約0.1重量%、至少約0.2重量%、至少約0.4重量%、至少約0.5重量%、至少約0.6重量%、至少約0.8重量%、至少約1重量%、至少約3重量%、至少約5重量%或至少約10重量%)到至多約15重量%(例如,至多約12重量%、至多約10重量%、至多約5重量%、至多約3重量%、至多約2重量%、至多約1重量%、至多約0.8重量%、至多約0.6重量%、至多約0.5重量%或至多約0.1重量%)。
在一或多個實施態樣中,本文中所描述的該等拋光組成物可進一步包括至少一種任擇的添加劑,該添加劑係選自由以下各者組成之群組:一氧化劑、一螯合劑、一表面活性劑、一腐蝕抑制劑以及一水溶性聚合物。
該氧化劑不受特別限制,但其特定實例包括:過硫酸銨、過硫酸鉀、過氧化氫、硝酸鐵、硝酸鈰二銨、硫酸鐵、次氯酸、臭氧、過碘酸鉀以及過乙酸。在不希望受理論束縛之情況下,咸信該氧化劑可促進在拋光過程期間材料之移除。
在一些實施態樣中,該氧化劑可係本文中所描述的該等拋光組成物之至少約0.05重量%(例如,至少約0.1重量%、至少約0.2重量%、至少約0.3重量%、至少約0.4重量%、至少約0.5重量%、至少約0.6重量%、至少約0.7重量%、至少約0.8重量%、至少約0.9重量%、至少約1重量%、至少約1.5重量%或至少約2重量%)到至多約10重量%(例如,至多約9重量%、至多約8重量%、至多約7重量%、至多約6重量%、至多約5重量%、至多約4重量%、至多約3重量%、至多約2重量%或至多約1重量%)。
在一或多個實施態樣中,該螯合劑可係選自由以下各者組成之群組:葡萄糖酸、乳酸、檸檬酸、酒石酸、蘋果酸、乙醇酸、丙二酸、甲酸、草酸、乙酸、丙酸、過乙酸、琥珀酸、乳酸、胺基乙酸、苯氧乙酸、二羥乙甘胺酸、縮二羥乙酸、甘油酸、三(羥甲基)甲基甘胺酸、丙胺酸、組胺酸、纈胺酸、苯丙胺酸、脯胺酸、麩醯胺酸、天冬胺酸、麩胺酸、精胺酸、離胺酸、酪胺酸、苯甲酸、氨、1,2-乙二磺酸、4-胺基-3-羥基-1-萘磺酸、8-羥基喹啉-5-磺酸、胺基甲磺酸、苯磺酸、羥胺O-磺酸、甲烷磺酸、m-二甲苯-4-磺酸、聚(4-苯乙烯磺酸)、聚茴香腦磺酸、p-甲苯磺酸、三氟甲烷-磺酸、乙二胺四乙酸、二伸乙基三胺五乙酸、氮基三乙酸、乙醯丙酮、胺基三(亞甲基膦酸)、1-羥基亞乙基(1,1-二膦酸)、2-膦醯基-1,2,4-丁烷三羧酸、六亞甲基二胺四(亞甲基膦酸)、乙二胺-四(亞甲基膦酸)、二伸乙基三胺五(亞甲基膦酸)、其鹽及其混合物。在不希望受理論束縛之情況下,咸信該螯合劑可充當一移除率增強劑以促進在一基體上的某些材料之移除。
在一些實施態樣中,該螯合劑可係本文中所描述的該等拋光組成物之至少約0.001重量%(例如,至少約0.002重量%、至少約0.003重量%、至少約0.004重量%、至少約0.005重量%、至少約0.006重量%、至少約0.007重量%、至少約0.008重量%、至少約0.009重量%或至少約0.01重量%)到至多約10重量%(例如,至多約8重量%、至多約6重量%、至多約5重量%、至多約4重量%、至多約2重量%、至多約1重量%、至多約0.8重量%、至多約0.6重量%或至多約0.5重量%)。
在一或多個實施態樣中,本文中所描述的該等拋光組成物也可以包括一或多種表面活性劑,該等表面活性劑係選自由以下各者組成之群組:陰離子表面活性劑、非離子表面活性劑、兩性表面活性劑、陽離子表面活性劑及其混合物。
該陽離子表面活性劑不受特別限制,但其特定實例包括脂族胺鹽以及脂族銨鹽。
該非離子表面活性劑不受特別限制,但其特定實例包括一醚型表面活性劑、一醚酯型表面活性劑、一酯型表面活性劑及一乙炔系表面活性劑。該醚型表面活性劑不受特別限制,但其特定實例包括聚乙二醇單-4-壬基苯基醚、聚乙二醇單油烯基醚以及三乙二醇單十二基醚。該醚酯型表面活性劑不受特別限制,但其的一特定實例係一甘油酯之一聚氧乙烯醚。該酯型表面活性劑不受特別限制,但其特定實例包括一聚乙二醇脂肪酸酯、一甘油酯及一山梨醇酐酯。該乙炔系表面活性劑不受特別限制,但其特定實例包括乙炔醇、乙炔甘醇及乙炔二醇的氧化乙烯加成物。
該兩性表面活性劑不受特別限制,但其特定實例包括甜菜鹼系表面活性劑。
該陰離子表面活性劑不受特定限制,但其特定實例包括羧酸鹽、磺酸鹽、硫酸鹽及磷酸鹽。該等羧酸鹽不受特別限制,但其特定實例包括脂肪酸鹽(例如,肥皂)以及烷基醚羧酸鹽。該等磺酸鹽的實例包括烷基苯磺酸鹽、烷基萘磺酸鹽以及α-烯烴磺酸鹽。該等硫酸鹽不受特別限制,但其特定實例包括高級醇硫酸鹽以及烷基硫酸鹽。該等磷酸鹽不受特別限制,但其特定實例包括烷基磷酸鹽及烷基酯磷酸鹽。
該腐蝕抑制劑不受特別限制,但其特定實例包括氫氧化膽鹼、胺基醇(例如,單乙醇胺以及3-胺基-4-辛醇)、乙二胺四(亞甲基膦酸)及其混合物。
該水溶性聚合物不受特別限制,但其特定實例包括聚丙烯醯胺、聚乙烯醇、聚乙烯吡咯烷酮、聚丙烯酸、羥乙基纖維素以及包括前所列示的該等聚合物之共聚物。在不希望受理論束縛之情況下,咸信該水溶性聚合物可充當一移除率抑制劑,以降低基體上之某些暴露材料的移除率,該等材料不意欲被移除或在拋光過程期間應以較低的一移除率移除。
在一或多個實施態樣中,該水溶性聚合物可係本文中所描述的該等拋光組成物之至少約0.01重量%(例如,至少約0.02重量%、至少約0.03重量%、至少約0.04重量%、至少約0.05重量%、至少約0.06重量%、至少約0.07重量%、至少約0.08重量%、至少約0.09重量%或至少約0.1重量%)到至多約1重量%(例如,至多約0.8重量%、至多約0.6重量%、至多約0.5重量%、至多約0.4重量%、至多約0.2重量%、至多約0.1重量%、至多約0.08重量%、至多約0.06重量%或至多約0.05重量%)。
在一或多個實施態樣中,本文中所描述的該等拋光組成物可實質上不含某些成分中之一或多者,諸如:有機溶劑;pH調節劑;四級銨化合物(例如鹽,諸如四烷基銨鹽;及氫氧化物,諸如氫氧化四甲基銨);鹼基(諸如,鹼氫氧化物);含氟化合物(例如,氟化物化合物或氟化之化合物(諸如,氟化之聚合物/表面活性劑));含矽化合物,諸如矽烷(例如,烷氧基矽烷);含氮化合物(例如,胺基酸、胺或亞胺(例如脒,諸如1,8-二氮雜雙環[5.4.0]-7-十一烯(DBU)及1,5-二氮雜雙環[4.3.0]壬-5-烯(DBN)));鹽(例如,鹵化物鹽或金屬鹽);聚合物(例如,非離子、陽離子或陰離子聚合物);無機酸(例如,氫氯酸、硫酸、磷酸或硝酸);表面活性劑(例如,陽離子表面活性劑;陰離子表面活性劑或非離子表面活性劑);塑化劑;氧化劑(例如,過氧化氫及過碘酸);腐蝕抑制劑(例如,唑或非唑腐蝕抑制劑);電解質(例如,聚電解質);及/或某些磨料(例如,氧化鈰磨料、非離子磨料、表面改質磨料、負/正帶電磨料,或陶瓷磨料複合材料)。可從該等拋光組成物排除的鹵化物鹽包括鹼金屬鹵化物(例如,鹵化鈉或鹵化鉀)或鹵化銨(例如,氯化銨),且可係氟化物、氯化物、溴化物或碘化物。如本文中所使用,一拋光組成物「實質上不含」的一成分,係指未有意添加至該拋光組成物中之一成分。在一些實施例中,本文中所描述的該等拋光組成物可具有至多約1000 ppm (例如,至多約500 ppm、至多約250 ppm、至多約100 ppm、至多約50 ppm、至多約10 ppm或至多約1 ppm)的該等拋光組成物實質上不含的以上成分中之一或多者。在一些實施例中,本文所述之該等拋光組成物可完全不含以上成分中之一或多者。
在一或多個實施態樣中,本文中所描述的該等拋光組成物可具有一針對銅及/或其合金之移除率對一針對鉬及/或其合金之移除率的一比率(亦即,一移除率比或者選擇性),其係至少約10:1(例如,至少約15:1、至少約20:1、至少約25:1、至少約30:1、至少約35:1、至少約40:1、至少約45:1、至少約50:1、至少約55:1、至少約60:1、至少約65:1或至少約70:1)到至多約1000:1(例如,或至多約500:1)。在一或多個實施態樣中,當毯覆式或圖案化晶圓具有經由物理氣相沉積(PVD)、原子層沉積(ALD)或(CVD)沉積的銅及鉬材料時,在量測拋光該等毯覆式晶圓或圖案化晶圓(例如,包括導電層、阻障層及/或介電層之晶圓)的移除率時,上文中所描述的比率可為適用的。然而,應理解,沉積該銅及鉬材料的方法可能對於它們的移除率及從而所達成的選擇性比具有影響。舉例而言,已知PVD膜在膜內具有較高程度之空位及不均勻性,使得PVD膜與ALD或CVD膜相比相對更易於移除。
在一或多個實施態樣中,當在一約1.5 psi的下壓力下執行拋光時,本文中所描述的該等拋光組成物可具有約1000 Å/min、或約1250 Å/min、或約1500 Å/min、或約1750 Å/min、或約2000 Å/min、或約2250 Å/min、或約2500 Å/min之最小銅移除率(無論是在毯覆式晶圓上抑或圖案化晶圓上)。在一或多個實施態樣中,當在一約1.5 psi之下壓力下執行拋光時,本文中所描述的該等拋光組成物可具有約1000 Å/min、或約750 Å/min、或約500 Å/min、或約250 Å/min、或約100 Å/min、或約50 Å/min、或約35 Å/min之最大鉬移除率(無論是在毯覆式晶圓上抑或圖案化晶圓上)。上文中針對銅與鉬所描述的移除率可適用於物理氣相沉積(PVD)、原子層沉積(ALD)或化學氣相沉積(CVD)沉積膜中之任何一者。
在一或多個實施態樣中,本揭露內容的特徵為一種拋光方法,其可包括:將一根據本揭露內容的拋光組成物施加至一基體(例如,一晶圓);且使一墊子(例如,一拋光墊)與該基體的該表面接觸且相對於該基體移動該墊。在一或多個實施態樣中,該基體可包括下列中之至少一者:矽氧化物(例如,四乙基正矽酸鹽(TEOS)、高密度電漿氧化物(HDP)、高縱橫比製程氧化物(HARP)或硼磷矽酸鹽玻璃(BPSG))、旋塗膜(例如,基於無機粒子之膜或基於可交聯碳聚合物之膜)、氮化矽、碳化矽、高K介電質(例如,鉿、鋁或鋯的金屬氧化物)、矽(例如,多晶矽、單晶矽或非晶矽)、碳、金屬(例如,鎢、銅、鈷、釕、鉬、鈦、鉭或鋁)或其合金、金屬氮化物(例如,氮化鈦或氮化鉭)及其混合物或組合。在一或多個實施態樣中,該拋光方法包括:將一本文中所描述的拋光組成物施加至一基體(例如,一晶圓),該基體含有銅與鉬及/或其合金於該基體之一表面上。
在一或多個實施態樣中,使用本文中所描述之拋光組成物的方法可進一步包括:經由一或多個步驟而從被該拋光組成物所處理的該基體產生一半導體裝置。舉例而言,可使用光微影術、離子植入、乾式/濕式蝕刻、電漿蝕刻、沉積(例如,PVD、CVD、ALD、ECD)、晶圓安裝、晶粒切割、封裝及測試,來從本文中所描述之拋光組成物所處理的基體產生一半導體裝置。
以下特定實施例僅解釋為例示性的,且不以任何方式限制本揭露內容之其餘部分。在無需進一步闡明之情況下,咸信熟習此藝者可基於本文中之描述而最大程度地利用本發明。
實施例
在這些實施例中,拋光係使用一AMAT Reflexion LK CMP拋光機、以一軟墊以及在200與500 mL/min之間之一拋光組成物流率來對300 mm晶圓施行,或使用一Mirra拋光機、一Fujibo H800或H804墊以及在約200與500 ml/min之間的流率來對200 mm晶圓施行。
被使用於該等實施例中的一般組成物係顯示於下面的表1中。當論述個別實施例時,將進一步詳細地解釋關於所測試組成物之差異的具體細節。
表1
組分 | 組成物之重量% |
pH調節劑(鹼) | 0.005 - 1 |
唑化合物 | 0.001 - 3 |
第一胺(MW < 120 g/mol) | 0.001 - 3 (若使用) |
第二胺(MW > 125 g/mol) | 0.001 - 2 (若使用) |
有機溶劑 | 0.001 - 1 |
磨料(矽氧) | 0.1 - 5 |
氧化劑 | 0.1 - 5 |
溶劑(DI水) | 75-99 |
pH | 4-8 |
在下文實施例中,該第一胺化合物係選自由以下各者組成之群組:脯胺酸、甘胺酸、絲胺酸、丙胺酸或其混合物。在下文實施例中,該第二胺係選自由以下各者組成之群組:組胺酸、苯丙胺酸、麩醯胺酸、天冬胺酸、麩胺酸、精胺酸、酪胺酸、肌肽、(3-胺基丙基)二乙醇胺、辛胺、癸胺、十二胺、十四胺、十五胺、十六胺、十八胺、環己胺、二環己胺、腺嘌呤、黃嘌呤、胸腺嘧啶、鳥嘌呤、異鳥嘌呤、次黃嘌呤或其混合物。
實施例1
鉬的靜態蝕刻率(SER)係藉由在45℃下將鉬試樣散浮於組成物1-4中歷經一分鐘來予以測量,而鉬/銅移除率(RR)係藉由以組成物1-4來拋光毯覆式晶圓而被測量。Cu毯覆膜被電鍍,且Mo毯覆膜藉由PVD來沉積。組成物1-4係相同的,例外之處是:(1)組成物1係一對照組且包括表1中所列出的該第一胺化合物但不包括表1中所列出的該第二胺化合物,以及(2)組成物2-4包括一第二胺化合物,其中被使用於組成物2-4中的該第二胺化合物係彼此不相同。組成物2-3包括一胺基酸作為該第二胺化合物,而組成物4包括一烷基胺化合物作為該第二胺化合物。組成物2-4包括與組成物1相同量以及類型的第一胺化合物。測試結果係彙總於下面的表2中。
表2
組成1 | 組成2 | 組成3 | 組成4 | |
Mo SER (Å/min) | 356 | 17 | 38 | 16 |
Cu RR (Å/min) | 3377 | 3419 | 3745 | 3737 |
Mo RR (Å/min) | 829 | 133 | 198 | 398 |
Cu/Mo RR比 | 4.07 | 25.7 | 18.9 | 9.38 |
結果顯示:該第二胺化合物的添加有效地降低鉬靜態蝕刻率及鉬移除率,同時些微增加銅移除率。這些樣態之組合導致組成物2-4的Cu/Mo拋光率比顯著地增加。這些結果表明:如此揭露內容中所界定的一第二胺化合物可以在一CMP程序期間被用作一針對Mo的腐蝕抑制劑。
實施例2
該等鉬及銅移除率(RR)係藉由以組成物5-6來拋光毯覆式晶圓而被測量。銅毯覆膜被電沉積,且鉬毯覆膜藉由ALD來沉積。組成物5-6係相同的,例外之處是:組成物5係一對照組且包括表1中所列出的該第一胺化合物但不包括表1中所列出的該第二胺化合物,而組成物6包括該等第一及第二胺化合物兩者。用於組成物6的該第二胺化合物係一胺基酸。測試結果係彙總於下面的表3中。
表3
組成5 | 組成6 | |
Cu RR (Å/min) | 2952 | 2603 |
Mo RR (Å/min) | 73 | 38 |
Cu/Mo比 | 40.4 | 68.5 |
結果顯示:相似於實施例1,包括該第二胺化合物降低了鉬之移除率且因此增高了Cu/Mo拋光率比。
實施例3
塔菲爾圖電流相交點(current intersection)可為在二個金屬之結合部處(例如,Cu/Mo相交處)的拋光期間發生電流腐蝕之可能性的一良好指標。塔菲爾掃描在組成物7-10中係藉由在相對於開路電壓的+/- 0.25 V之範圍中以1 mV/s之一率從低到高掃描電壓時量測電流來進行。目標金屬(例如,Cu或Mo)係用作工作電極、石墨係作為相對電極,且一飽和甘汞電極(SCE)係作為參考電極。組成物7-10係相同的,例外之處是:(1)組成物7係一對照組且包括表1中所列出的該第一胺化合物但不包括表1中所列出的該第二胺化合物,以及(2)組成物8-10包括一第二胺化合物,其中被使用於組成物8-10中的該等第二胺化合物係彼此不相同。組成物8-9包括一胺基酸作為該第二胺化合物,而組成物10包括一烷基胺化合物作為該第二胺化合物。組成物8-10亦包括與組成物7相同量以及類型的第一胺化合物。來自塔菲爾圖之電流相交點係顯示於下面的表4中。
表4
組成7 | 組成8 | 組成9 | 組成10 | |
電流相交點(µA) | 20.9 | 17 | 16.5 | 20.2 |
結果顯示:當與沒有該第二胺化合物的組成物7比較時,具有該第二胺化合物的組成物8-10具有一較低的電流相交點。這指出:當該拋光組成物包括如本揭露內容中所述的一第二胺化合物時,電流腐蝕的傾向較低。
實施例4
該等鉬及銅移除率(RR)係藉由以組成物11-16來拋光毯覆式晶圓而被測量。Cu毯覆膜被電鍍,且Mo毯覆式膜藉由PVD來沉積。該等組成物相同,但下面的表5中所指出的差異除外。組成物11僅包括單個第一胺化合物而無第二胺化合物。組成物13-16僅包括單個第二胺化合物。組成物13及15包括與該第二胺化合物相同的烷基胺。組成物14及16包括與該第二胺化合物相同的胺基酸,其係與組成物13及15中所使用者不同的一第二胺化合物。組成物12包括被使用在組成物13-16中的該等第二胺化合物兩者(亦即,兩個不相同的第二胺化合物,其中一者係一胺基酸且另一者係一烷基胺)。組成物11-12及15-16中使用相同的第一胺化合物。
表5
組成11 | 組成12 | 組成13 | 組成14 | 組成15 | 組成16 | |
第一胺化合物 | 有 | 有 | 無 | 無 | 有 | 有 |
第二胺化合物 | 無 | 有 | 有 | 有 | 有 | 有 |
Cu RR (Å/min) | 3624 | 2888 | 602 | 1441 | 3493 | 2868 |
Mo RR (Å/min) | 716 | 94 | 321 | 161 | 120 | 175 |
Cu/Mo比 | 5.1 | 30.4 | 1.9 | 8.9 | 29 | 16.4 |
結果展示,在一包括銅及鉬之基體上,於一拋光組成物中使用一第一胺化合物以及一第二胺化合物兩者,兩者如皆本揭露內容中所述,將導致一獨特的協同作用。具體而言,在沒有任何第二胺化合物的情況下(化合物11),Mo RR係高度提升且導致一低Cu/Mo移除率比。相反地,在沒有該第一胺化合物的情況下(化合物13-14),Cu移除率跌落至一不可接受之位準,而Mo RR仍保持升高,導致一低Cu/Mo移除率比。值得注意的是,包括該第一及該第二胺化合物兩者的該等組成物(化合物12及15-16)維持一高Cu RR且達成一低Mo RR,這導致一高度所期望之高Cu/Mo移除率比。當與組成物13比較時,組成物15出乎意料地顯著地降低Mo移除率,即使該第一胺化合物之存在主要是用以提高Cu移除率。
本揭露內容全文使用用語「不受特別限制」數次。儘管這指示一化學類別(例如,唑)的許多所述成員可合適於一特別用途,但並不意謂該化學類別的任何特定成員不能是特別有利或較佳的。
雖然本揭露內容已就本文中所闡述的該等示範例來予以描述,但應理解的是:可進行其他修改及變化,而不脫離如隨附申請專利範圍中所定義的本揭露內容之精神及範圍。
1:基體
10:非傳導材料
20:溝槽
30:銅層,材料
40:襯裡
圖1為可藉由本揭露內容之組成物所拋光之一基體的示意圖。
(無)
Claims (17)
- 一種拋光組成物,包含: 至少一磨料; 至少一唑化合物; 至少一第一胺化合物,該至少一第一胺化合物包含一胺基酸,其具有至多120 g/mol的一分子量; 至少一第二胺化合物,其具有至少125 g/mol的一分子量;以及 一水性溶劑。
- 如請求項1之拋光組成物,其中該至少一磨料係選自由以下各者組成之群組:氧化鋁;矽氧;鈦氧;氧化鈰;氧化鋯;氧化鋁、矽氧、鈦氧、氧化鈰或氧化鋯之共成型產物;經塗覆的磨料;經表面改質的磨料;及其混合物。
- 如請求項1或2之拋光組成物,其中該至少一磨料係以該組成物之約0.01重量%至約50重量%的量存在。
- 如請求項1-3中任一項之拋光組成物,其中該唑係選自由以下各者組成之群組:雜環唑、經取代或未經取代的三唑、經取代或未經取代的四唑、經取代或未經取代的二唑,以及經取代或未經取代的苯并噻唑。
- 如請求項1-4中任一項之拋光組成物,其中該唑係選自由以下各者組成之群組:四唑、苯并三唑、甲苯基三唑、甲基苯并三唑、乙基苯并三唑、丙基苯并三唑、丁基苯并三唑、戊基苯并三唑、己基苯并三唑、5,6-二甲基苯并三唑、氯苯并三唑、5,6-二氯苯并三唑、1-(氯甲基)-1-H-苯并三唑、氯乙基苯并三唑、苯基苯并三唑、苄基苯并三唑、胺基三唑、胺基苯并咪唑、吡唑、咪唑、胺基四唑、腺嘌呤、苯并咪唑、噻苯達唑、1,2,3-三唑、1,2,4-三唑、1-羥基苯并三唑、2-甲基苯并噻唑、2-胺基苯并咪唑、2-胺基-5-乙基-1,3,4-噻二唑、3,5-二胺基-1,2,4-三唑、3-胺基-5-甲基吡唑、4-胺基-4H-1,2,4-三唑。
- 如請求項1-5中任一項之拋光組成物,其中該至少一唑係以該組成物之約0.001重量%至約10重量%之量存在。
- 如請求項1-6中任一項之拋光組成物,其中該至少一第一胺化合物係選自由以下各者組成之群組:脯胺酸、甘胺酸、絲胺酸、丙胺酸或其混合物。
- 如請求項1-7中任一項之拋光組成物,其中該至少一第一胺化合物係以該組成物之約0.001重量%至約18重量%之量存在。
- 如請求項1-8中任一項之拋光組成物,其中該至少一第二胺化合物係一胺基酸。
- 如請求項1-8中任一項之拋光組成物,其中該至少一第二胺化合物係一烷基胺。
- 如請求項1-8中任一項之拋光組成物,其中該至少一第二胺化合物係選自由以下各者組成之群組:組胺酸、苯丙胺酸、麩醯胺酸、天冬胺酸、麩胺酸、精胺酸、酪胺酸、肌肽、(3-胺基丙基)二乙醇胺、辛胺、癸胺、十二胺、十四胺、十五胺、十六胺、十八胺、環己胺、二環己胺、腺嘌呤、黃嘌呤、胸腺嘧啶、鳥嘌呤、異鳥嘌呤、次黃嘌呤或其混合物。
- 如請求項1-11中任一項之拋光組成物,其中該至少一第二胺化合物係以該組成物之約0.001重量%至約18重量%之量存在。
- 如請求項1-12中任一項之拋光組成物,其中該組成物具有在約2至約10之範圍內的pH。
- 如請求項1-13中任一項之拋光組成物,其中針對由物理氣相沉積所沉積的膜,該組成物展現至少10:1的一Cu:Mo拋光選擇性比。
- 一種方法,其包含:將請求項1-14中任一項之該拋光組成物施加至一基體,該基體包含銅、鉬、銅之一合金、鉬之一合金及其任何組合中之至少一者在該基體之一表面上;且 使一墊與該基體之該表面接觸且相對於該基體移動該墊。
- 如請求項15的方法,其進一步包含從該基體形成一半導體裝置。
- 如請求項16之方法,其中該基體的該表面包含有藉由物理氣相沉積所沉積的銅及鉬;且 其中該銅與鉬係在一至少10:1的選擇性比下被拋光。