TW202110926A - 在熔合沈積成型中使用熱塑性聚胺甲酸酯的方法及其系統和物品 - Google Patents
在熔合沈積成型中使用熱塑性聚胺甲酸酯的方法及其系統和物品 Download PDFInfo
- Publication number
- TW202110926A TW202110926A TW109135669A TW109135669A TW202110926A TW 202110926 A TW202110926 A TW 202110926A TW 109135669 A TW109135669 A TW 109135669A TW 109135669 A TW109135669 A TW 109135669A TW 202110926 A TW202110926 A TW 202110926A
- Authority
- TW
- Taiwan
- Prior art keywords
- thermoplastic polyurethane
- polyol
- storage modulus
- tpu
- article
- Prior art date
Abstract
本發明關於固態自由製作(尤其是熔合沈積成型)用之系統及方法,及使用其製造的各種物品,其中該系統及方法利用特別適合此處理之特定熱塑性聚胺甲酸酯。可使用的熱塑性聚胺甲酸酯衍生自(a)多異氰酸酯成分,(b)多元醇成分,及(c)選用鏈延長劑成分,其中生成的熱塑性聚胺甲酸酯具有高於80℃之結晶溫度,且其100℃剪切儲存模數相對其20℃剪切儲存模數保留超過20%。
Description
本發明關於固態自由製作(尤其是熔合沈積成型)用之系統及方法,及使用其製造的各種物品,其中該系統及方法利用特別適合此處理之特定熱塑性聚胺甲酸酯。可使用的熱塑性聚胺甲酸酯衍生自(a)多異氰酸酯成分,(b)多元醇成分,及(c)選用鏈延長劑成分,其中生成的熱塑性聚胺甲酸酯具有高於80℃之結晶溫度,且其100℃剪切儲存模數相對其20℃剪切儲存模數保留超過20%。
本發明關於使用特定熱塑性聚胺甲酸酯之固態自由製作,更具體而言為熔合沈積成型。
固態自由製作(SFF)為可由電腦資料經由增材形成步驟製作任意形狀結構之技術。任何SFF之基本操作均包括將三維電腦模型分割成薄橫切面,將結果轉變成二維位置資料,且將該資料送入以逐層方式製作三維結構之控制設備。
固態自由製作意味製作方法有許多種不同的方式,包括三維印刷、電子束熔化、立體微影術、選擇性雷射燒結、積層物件製造、熔合沈積成型等。
在三維印刷法中,例如將建構材料從具有一組噴嘴之分配頭分配而在支撐結構上沈積一層。依建構材料而定,然後使用合適的裝置將該層硬化或固化。建構材料可包括形成物件之成型材料、及在建構時支撐物件之支撐材料。
固態自由製作一般用於設計相關領域,在此用於視覺化、展示、及機械原型設計。因此SFF利於以最小的模具及人力投資快速製作機能性原型。此快速原型設計因對設計者提供快速及有效的回饋而縮短產品發展循環且改良設計過程。SFF亦可用於非機能型零件之快速製作,例如用於評定設計的各態樣之目的,如美學、契合度、組裝等。另外,現已證明SFF技術可用於醫藥領域,其中在實行手術之前模塑預期成果。現已公認許多其他領域可由快速原型設計技術受益,包括但不限於建築、牙科、及整型手術,其中特定的設計及/或機能視覺化是有用的。
此種製作形式的利益日增。現已考量將許多種材料用於使用其之系統及方法,然而,現已證明難以將熱塑性聚胺甲酸酯用於這些系統及方法。其乃至少部分由於TPU材料的撓性會使強制該材料通過FDM處理設備之熔化槽具挑戰性。TPU之低結晶速率亦在將熔化流鋪放在欲建構的零件上時難以維持容許度。此外,TPU材料之大熔化範圍會使黏度控制具挑戰性。
考慮到熱塑性聚胺甲酸酯可提供的性質、及使用較習知的製作裝置製造極多種物品之吸引人組合,現在證驗及/或發展極適合固態自由製作(尤其是熔合沈積成型)之熱塑性聚胺甲酸酯的需求日增。
本發明揭示的技術提供一種固態自由製作三維物件用之系統,其包含:固態自由製作裝置,其以控制方式沈積建構材料小粒;其中該建構材料包含衍生自(a)多異氰酸酯成分,(b)多元醇成分,及(c)選用鏈延長劑成分之熱塑性聚胺甲酸酯;其中生成的熱塑性聚胺甲酸酯具有高於80℃之結晶溫度;及其中生成的熱塑性聚胺甲酸酯之100℃剪切儲存模數相對其20℃剪切儲存模數保留超過20%。
本發明揭示的技術亦提供一種製作三維物件之方法,其步驟包含:(I)操作固態自由製作物件之系統,其中該系統包含以控制方式沈積建構材料小粒之固態自由製作裝置,以形成三維物件;其中該建構材料包含衍生自(a)多異氰酸酯成分,(b)多元醇成分,及(c)選用鏈延長劑成分之熱塑性聚胺甲酸酯;其中生成的熱塑性聚胺甲酸酯具有高於80℃之結晶溫度;及其中生成的熱塑性聚胺甲酸酯之100℃剪切儲存模數相對其20℃剪切儲存模數保留超過20%。任何在此所述的熱塑性聚胺甲酸酯均可用於所述方法。
本發明揭示的技術亦提供一種由固態自由製作物件用之系統所製作的製造物件,其包含:以控制方式沈積建構材料小粒之固態自由製作裝置;其中該建構材料包含衍生自(a)多異氰酸酯成分,(b)多元醇成分,及(c)選用鏈延長劑成分之熱塑性聚胺甲酸酯;其中生成的熱塑性聚胺甲酸酯具有高於80℃之結晶溫度;及其中生成的熱塑性聚胺甲酸酯之100℃剪切儲存模數相對其20℃剪切儲存模數保留超過20%。任何在此所述的熱塑性聚胺甲酸酯均可用以製備所述物品。
在此所述的系統或方法或物品之一些具體實施例中,該熱塑性聚胺甲酸酯具有高於100℃、105℃、110℃、或甚至高於115℃、或甚至約117℃之結晶溫度。在一些具體實施例中,該結晶溫度不超過200℃、150℃、或甚至120℃。
在此所述的系統或方法或物品之一些具體實施例中,該熱塑性聚胺甲酸酯之50℃剪切儲存模數相對其20℃剪切儲存模數保留超過50%;其100℃剪切儲存模數相對其50℃剪切儲存模數保留超過42%;其150℃剪切儲存模數相對其120℃剪切儲存模數保留超過20%;或其任何組合。
在此所述的系統或方法或物品之一些具體實施例中,該熱塑性聚胺甲酸酯之50℃剪切儲存模數相對其20℃剪切儲存模數保留超過60%;其100℃剪切儲存模數相對其20℃剪切儲存模數保留超過30%;或其任何組合。
在此所述的系統或方法或物品之一些具體實施例中,該熱塑性聚胺甲酸酯之100℃剪切儲存模數相對其50℃剪切儲存模數保留超過45%;其120℃剪切儲存模數相對其100℃剪切儲存模數保留超過70%;其105℃剪切儲存模數相對其20℃剪切儲存模數保留超過5%;或其任何組合。
本發明揭示的技術亦提供在此所述的系統或方法或物品,其中固態自由製作裝置包含(a)複數個分配頭;(b)設計成對該製作裝置供應複數種建構材料之建構材料供應裝置;及(c)設計成基於選自複數個預定操作模式之操作模式而控制該製作裝置及該建構材料供應裝置之控制單元。
該固態自由製作裝置可包含及/或揭述為三維印刷、電子束熔化、立體微影術、選擇性雷射燒結、積層物件製造、熔合沈積成型、或其組合。在一些具體實施例中,固態自由製作裝置可包含及/或揭述為三維印刷、電子束熔化、立體微影術、積層物件製造、熔合沈積成型、或其組合。在一些這些具體實施例中,固態自由製作裝置可排除選擇性雷射燒結。
固態自由製作裝置可包含熔合沈積成型(FDM)裝置,其亦可稱為熔合纖絲製作(FFF)裝置。
本發明揭示的技術提供所述的系統或方法或物品,其中熱塑性聚胺甲酸酯特徵為鏈延長劑對用以製備熱塑性聚胺甲酸酯(及/或存在於熱塑性聚胺甲酸酯中)之多元醇的莫耳比例大於1.5。在其他具體實施例中,該比例大於2.0、或甚至大於3.5、3.6、3.7、或甚至大於3.8。
本發明揭示的技術提供所述的系統或方法或物品,其中熱塑性聚胺甲酸酯特徵為多元醇具有至少900之數量平均分子量。在一些具體實施例中,該多元醇具有至少900、至少1,000、至少1,500、至少1,750、或甚至約2,000之數量平均分子量。在一些具體實施例中,該多元醇可具有不超過5,000、4,000、3,000、或甚至2,500或2,000之分子量。
本發明揭示的技術提供所述的系統或方法或物品,其中熱塑性聚胺甲酸酯特徵為多異氰酸酯成分包含芳香族二異氰酸酯,例如4,4’-亞甲雙(異氰酸苯酯)。
本發明揭示的技術提供所述的系統或方法或物品,其中熱塑性聚胺甲酸酯特徵為多元醇成分包含聚醚多元醇、聚酯多元醇、或其組合。可使用的實例包括聚(四亞甲基醚二醇)、聚己二酸伸丁酯、或其組合。
本發明揭示的技術提供所述的系統或方法或物品,其中熱塑性聚胺甲酸酯特徵為鏈延長劑成分包含線形伸烷二醇,例如1,4-丁二醇。
本發明揭示的技術提供所述的系統或方法或物品,其中熱塑性聚胺甲酸酯特徵為熱塑性聚胺甲酸酯進一步包含一種或以上的著色劑、抗氧化劑(包括酚系、亞磷酸酯、硫酯、及/或胺)、抗臭氧劑、安定劑、惰性填料、潤滑劑、抑制劑、水解安定劑、光安定劑、位阻胺光安定劑、苯并三唑UV吸收劑、熱安定劑、防止變色之安定劑、染料、顏料、無機與有機填料、強化劑、或其任何組合。
本發明揭示的技術提供所述的物品,其中該物品包含烹飪與儲存器具、爐具、汽車組件、玩具、運動服、醫學裝置、個人醫學物品、複製醫學植體、牙科物品、消毒容器、帷幕、袍服、過濾器、衛生產品、尿布、膜狀物、片狀物、管子、管線、電線外套、電纜外套、農業用膜、低透氣性蔽幛、運動設備、鑄膜、吹製膜、外形、船隻及船舶組件、條板箱、容器、包裝物、實驗室器具、辦公室地墊、儀器樣品保持器、液體儲存容器、包裝材料、醫學管線與閥、片狀物、帶狀物、地毯、黏著劑、電線外皮、電纜、保護性服裝、汽車零件、塗層、發泡積層體、超模塑物品、汽車表皮、天蓬、防水布、皮革物品、屋頂構造物品、方向盤、塗層粉料、搪塑粉料、消費者耐久財、握把、手把、軟管、軟管內墊、管線、管線內墊、腳輪、溜冰輪、電腦組件、皮帶、貼布、鞋類組件、輸送帶或正時皮帶、手套、纖維、織物、或衣服。
以下藉非限制例證說明各種較佳特徵及具體實施例。
本發明揭示的技術提供用於固態自由製作三維物件及/或物品之系統。本發明亦提供使用此系統之方法、及使用此系統及/或方法所製造的物品。本發明揭示的技術提供這些其中使用特定熱塑性聚胺甲酸酯之系統、方法、及物品,更具體而言為衍生自(a)多異氰酸酯成分,(b)多元醇成分,及(c)選用鏈延長劑成分之熱塑性聚胺甲酸酯;其中生成的熱塑性聚胺甲酸酯具有高於80℃之結晶溫度;及其中生成的熱塑性聚胺甲酸酯之100℃剪切儲存模數相對其20℃剪切儲存模數保留超過20%。現已發現,所述的熱塑性聚胺甲酸酯特別適合用於固態自由製作系統及方法,尤其是熔合沈積成型。所述的熱塑性聚胺甲酸酯克服過去當將此材料用於固態自由製作(尤其是熔合沈積成型)時遭遇的障礙,且可在這些日益重要的製造方法及系統中使用這些通用材料。《熱塑性聚胺甲酸酯》
可用於本發明揭述的技術之熱塑性聚胺甲酸酯衍生自(a)多異氰酸酯成分,(b)多元醇成分,及(c)選用鏈延長劑成分;其中生成的熱塑性聚胺甲酸酯具有高於80℃之結晶溫度;及其中生成的熱塑性聚胺甲酸酯之100℃剪切儲存模數相對其20℃剪切儲存模數保留超過20%。
在此所述的TPU組成物係使用(a)多異氰酸酯成分製造。該多異氰酸酯及/或多異氰酸酯成分包括一種或以上的多異氰酸酯。在一些具體實施例中,該多異氰酸酯成分包括一種或以上的二異氰酸酯。
在一些具體實施例中,該多異氰酸酯及/或多異氰酸酯成分包括具有5至20個碳原子之α,ω-伸烷基二異氰酸酯。
合適的多異氰酸酯包括芳香族二異氰酸酯、脂肪族二異氰酸酯、或其組合。在一些具體實施例中,該多異氰酸酯成分包括一種或以上的芳香族二異氰酸酯。在一些具體實施例中,該多異氰酸酯成分本質上無、或甚至完全無脂肪族二異氰酸酯。在其他具體實施例中,該多異氰酸酯成分包括一種或以上的脂肪族二異氰酸酯。在一些具體實施例中,該多異氰酸酯成分本質上無、或甚至完全無芳香族二異氰酸酯。
可使用的多異氰酸酯之實例包括芳香族二異氰酸酯,如4,4’-亞甲雙(異氰酸苯酯) (MDI)、二異氰酸間-苯二甲酯(XDI)、二異氰酸1,4-伸苯酯、二異氰酸1,5-萘酯、與甲苯二異氰酸酯(TDI);及脂肪族二異氰酸酯,如異佛酮二異氰酸酯(IPDI)、二異氰酸1,4-環己酯(CHDI)、癸烷-1,10-二異氰酸酯、離胺酸二異氰酸酯(LDI)、1,4-丁烷二異氰酸酯(BDI)、異佛酮二異氰酸酯(PDI)、二異氰酸3,3’-二甲基-4,4’-二伸苯酯(TODI)、二異氰酸1,5-萘酯(NDI)、與二環己基甲烷-4,4’-二異氰酸酯(H12MDI)。可使用二種或以上的多異氰酸酯的混合物。在一些具體實施例中,該多異氰酸酯為MDI及/或H12MDI。在一些具體實施例中,該多異氰酸酯包括MDI。在一些具體實施例中,該多異氰酸酯包括H12MDI。
在一些具體實施例中,該熱塑性聚胺甲酸酯係以包括H12MDI之多異氰酸酯成分製備。在一些具體實施例中,該熱塑性聚胺甲酸酯係以本質上由H12MDI所組成之多異氰酸酯成分製備。在一些具體實施例中,該熱塑性聚胺甲酸酯係以由H12MDI所組成之多異氰酸酯成分製備。
在一些具體實施例中,該熱塑性聚胺甲酸酯係以包括(或本質上由…所組成、或甚至由…所組成)H12MDI、及MDI、HDI、TDI、IPDI、LDI、BDI、PDI、CHDI、TODI、與NDI至少之一的多異氰酸酯成分製備。
在一些具體實施例中,用以製備在此所述的TPU及/或TPU組成物之多異氰酸酯按重量計有至少50%之環脂肪族二異氰酸酯。在一些具體實施例中,該多異氰酸酯包括具有5至20個碳原子之α,ω-伸烷基二異氰酸酯。
在一些具體實施例中,用以製備在此所述的TPU及/或TPU組成物之多異氰酸酯包括六亞甲基-1,6-二異氰酸酯、1,12-十二烷二異氰酸酯、2,2,4-三甲基六亞甲基二異氰酸酯、2,4,4-三甲基六亞甲基二異氰酸酯、2-甲基-1,5-五亞甲基二異氰酸酯、或其組合。
在一些具體實施例中,該多異氰酸酯成分包含芳香族二異氰酸酯。在一些具體實施例中,該多異氰酸酯成分包含4,4’-亞甲基雙(異氰酸苯酯)。
在此所述的TPU組成物係使用(b)多元醇成分製造。該多元醇包括聚醚多元醇、聚酯多元醇、聚碳酸酯多元醇、聚矽氧烷多元醇、及其組合。
合適的多元醇(若有),亦可揭述為羥基封端中間物,可包括一種或以上的羥基封端聚酯、一種或以上的羥基封端聚醚、一種或以上的羥基封端聚碳酸酯、一種或以上的羥基封端聚矽氧烷、或其混合物。
合適的羥基封端聚酯中間物包括數量平均分子量(Mn)為約500至約10,000、約700至約5,000、或約700至約4,000,且通常酸數小於1.3或小於0.5之線形聚酯。分子量係檢驗終端官能基而測定,且與數量平均分子量相關。該聚酯中間物可藉以下製造:(1)一種或以上的二醇與一種或以上的二羧酸或酐之酯化反應,或(2)轉酯化反應,即一種或以上的二醇與二羧酸之酯的反應。為了獲得具有大量終端羥基之線形鏈,莫耳比例通常較佳為超過1莫耳之二醇對酸。合適的聚酯中間物亦包括各種內酯,如聚己內酯,其一般由ε-己內酯與二官能基引發劑(如二乙二醇)製造。所欲聚酯之二羧酸可為脂肪族、環脂肪族、芳香族、或其組合。合適的二羧酸,其可單獨或以混合物使用,通常具有總共4至15個碳原子且包括:琥珀酸、戊二酸、己二酸、庚二酸、辛二酸、壬二酸、癸二酸、十二碳二酸、異苯二甲酸、對苯二甲酸、環己烷二羧酸等。亦可使用以上二羧酸之酐,如苯二甲酸酐、四氫苯二甲酸酐等。己二酸為較佳二酸。被反應而形成所欲聚酯中間物之二醇可為脂肪族、芳香族、或其組合,包括以上鏈延長劑部分所述的任何二醇,且具有總共2至20個或2至12個碳原子。合適的實例包括乙二醇、1,2-丙二醇、1,3-丙二醇、1,3-丁二醇、1,4-丁二醇、1,5-戊二醇、1,6-己二醇、2,2-二甲基-1,3-丙二醇、1,4-環己烷二甲醇、伸癸二醇、伸十二碳二醇、及其混合物。
多元醇成分亦可包括一種或以上的聚己內酯聚酯多元醇。可用於在此所述技術之聚己內酯聚酯多元醇包括衍生自己內酯單體之聚酯二元醇。該聚己內酯聚酯多元醇被一級羥基封端。合適的聚己內酯聚酯多元醇可由ε-己內酯與二官能基引發劑(如二乙二醇、1,4-丁二醇、或任何在此所述的其他二醇及/或二元醇)製造。在一些具體實施例中,該聚己內酯聚酯多元醇為衍生自己內酯單體之線形聚酯二元醇。
可使用的實例包括CAPA™ 2202A,數量平均分子量(Mn)為2,000之線形聚酯二元醇,及CAPA™ 2302A,Mn為3,000之線形聚酯二元醇,其均由Perstorp Polyols Inc.市售。這些材料亦可揭述為2-oxepanone與1,4-丁二醇的聚合物。
聚己內酯聚酯多元醇可由2-oxepanone與二元醇製備,其中二元醇可為1,4-丁二醇、二乙二醇、單乙二醇、1,6-己二醇、2,2-二甲基-1,3-丙二醇、或其任何組合。在一些具體實施例中,用以製備聚己內酯聚酯多元醇之二醇為線形。在一些具體實施例中,該聚己內酯聚酯多元醇由1,4-丁二醇製備。在一些具體實施例中,該聚己內酯聚酯多元醇具有500至10,000、或500至5,000、或1,000或甚至2,000至4,000、或甚至3,000之數量平均分子量。
合適的羥基封端聚醚中間物包括衍生自具有總共2至15個碳原子之二元醇或多元醇之聚醚多元醇,在一些具體實施例中為將烷基二元醇或二醇以包含具有2至6個碳原子之環氧烷(一般為環氧乙烷或環氧丙烷、或其混合物)之醚反應。例如羥基官能性聚醚可藉由首先將丙二醇以環氧丙烷反應,繼而以環氧乙烷反應而製造。由環氧乙烷生成的一級羥基比二級羥基更具反應性,因此較佳。可使用的市售聚醚多元醇包括包含將環氧乙烷以乙二醇反應之聚(乙二醇)、包含將環氧丙烷以丙二醇反應之聚(丙二醇)、包含將水以四氫呋喃反應之聚(四亞甲醚二醇)(亦可稱為聚合四氫呋喃,且通常稱為PTMEG)。在一些具體實施例中,該聚醚中間物包括PTMEG。合適的聚醚多元醇亦包括環氧烷之聚醯胺加成物,且可包括例如包含乙二胺與環氧丙烷的反應產物之乙二胺加成物、包含二乙三胺與環氧丙烷的反應產物之二乙三胺加成物、及類似的聚醯胺型聚醚多元醇。亦可將共聚醚用於所述組成物。典型的共聚醚包括THF與環氧乙烷、或THF與環氧丙烷的反應產物。其為得自BASF之嵌段共聚物Poly THF® B、及無規共聚物poly THF® R。各種聚醚中間物通常具有大於約700之數量平均分子量(Mn
),如約700至約10,000、約1,000至約5,000、或約1,000至約2,500,其係檢驗終端官能基而測定且為平均分子量。在一些具體實施例中,該聚醚中間物包括兩種或以上的分子量不同的聚醚的摻合物,如2,000 Mn
與1,000 Mn
之PTMEG的摻合物。
合適的羥基封端聚碳酸酯包括將二醇以碳酸酯反應而製備者。美國專利第4,131,731號因揭示羥基封端聚碳酸酯及其製備而納入此處作為參考。此聚碳酸酯為線形,及具有終端羥基且本質上排除其他的終端基。重要的反應物為二醇及碳酸酯。合適的二醇選自含有4至40個、及/或甚至4至12個碳原子之環脂肪族與脂肪族二元醇,及每個分子含有2至20個烷氧基且各烷氧基含有2至4個碳原子之聚氧基伸烷二醇。合適的二元醇包括含有4至12個碳原子之脂肪族二元醇,如1,4-丁二醇、1,5-戊二醇、新戊二醇、1,6己二醇、2,2,4-三甲基-1,6-己二醇、1,10-癸二醇、氫化二亞麻二醇、氫化二油醇、3-甲基-1,5-戊二醇;及環脂肪族二醇,如1,3-環己二醇、1,4-二羥甲基環己烷、1,4-環己二醇、1,3-二羥甲基環己烷、1,4-內亞甲基-2-羥基-5-羥基甲基環己烷,以及聚伸烷二醇。依最終產物所需性質而定,用於該反應之二元醇可為單種二元醇、或二元醇的混合物。以羥基封端之聚碳酸酯中間物通常對所屬技術領域者及在文獻中為已知的。合適的碳酸酯選自由5至7員環構成的碳酸伸烷酯。適合在此使用的碳酸酯包括碳酸伸乙酯、三亞甲基碳酸酯、四亞甲基碳酸酯、碳酸1,2-伸丙酯、碳酸1,2-伸丁酯、碳酸2,3-伸丁酯、碳酸1,2-伸乙酯、碳酸1,3-伸戊酯、碳酸1,4-伸戊酯、碳酸2,3-伸戊酯、與碳酸2,4-伸戊酯。亦在此適合為二烷基碳酸酯、環脂肪族碳酸酯、與二芳基碳酸酯。二烷基碳酸酯可在各烷基中含有2至5個碳原子,且其指定實例為碳酸二乙酯與碳酸二丙酯。環脂肪族碳酸酯,尤其是二環脂肪族碳酸酯,可在各環狀結構中含有4至7個碳原子,且其可有一或二個此結構。當其中一個基為環脂肪族時,另一可為烷基或芳基。另一方面,如果其中一個基為芳基,則另一可為烷基或環脂肪族。在各芳基中含有6至20個碳原子之合適二芳基碳酸酯的實例為二苯基碳酸酯、二甲苯基碳酸酯、與二萘基碳酸酯。
合適的聚矽氧烷多元醇包括α-ω-羥基、或胺、或羧酸、或硫醇、或環氧基封端聚矽氧烷。實例包括以羥基、或胺、或羧酸、或硫醇、或環氧基封端之聚(二甲基矽氧烷)。在一些具體實施例中,該聚矽氧烷多元醇為羥基封端聚矽氧烷。在一些具體實施例中,該聚矽氧烷多元醇具有300至5,000、或400至3,000之數量平均分子量。
聚矽氧烷多元醇可藉氫化聚矽氧烷與脂肪族多羥基醇或聚氧基伸烷醇之間的脫氫反應,將醇系羥基引入聚矽氧烷主幹中而得到。
在一些具體實施例中,聚矽氧烷可由一種或以上的具有下式之化合物表示:
其中:各R1
與R2
獨立為1至4個碳原子之烷基、苄基、或苯基;各E為OH或NHR3
,其中R3
為氫、1至6個碳原子之烷基、或5至8個碳原子之環烷基;a與b各獨立為2至8之整數;c為3至50之整數。在含胺基聚矽氧烷中,E基至少之一為NHR3
。在含羥基聚矽氧烷中,E基至少之一為OH。在一些具體實施例中,R1
與R2
均為甲基。
合適的實例包括α-ω-羥基丙基封端聚(二甲基矽氧烷)、與α-ω-胺基丙基封端聚(二甲基矽氧烷),其均為市售材料。進一步實例包括聚(二甲基矽氧烷)材料與聚(環氧烷)的共聚物。
多元醇成分(若有)可包括聚(乙二醇)、聚(四亞甲醚二醇)、聚(環氧丙烷)、環氧乙烷封端聚(丙二醇)、聚(己二酸伸丁酯)、聚(己二酸伸乙酯)、聚(己二酸六亞甲酯)、聚(己二酸四亞甲酯-共聚-六亞甲酯)、聚(己二酸3-甲基-1,5-五亞甲酯)、聚己內酯二醇、聚(碳酸六亞甲酯)二醇、聚(碳酸五亞甲酯)二醇、聚(碳酸三亞甲酯)二醇、基於二聚物脂肪酸之聚酯多元醇、基於蔬菜油之多元醇、或其任何組合。
可用以製備合適的聚酯多元醇之二聚物脂肪酸的實例包括由Croda市售的Priplast™聚酯二醇/多元醇、及由Oleon市售的Radia®聚酯二醇。
在一些具體實施例中,該多元醇成分包括聚醚多元醇、聚碳酸酯多元醇、聚己內酯多元醇、或其任何組合。
在一些具體實施例中,該多元醇成分包括聚醚多元醇。在一些具體實施例中,該多元醇成分本質上無、或甚至完全無聚酯多元醇。在一些具體實施例中,用以製備TPU之多元醇成分實質上無、或甚至完全無聚矽氧烷。
在一些具體實施例中,該多元醇成分包括環氧乙烷、環氧丙烷、環氧丁烷、環氧乙基苯、聚(四亞甲醚二醇)、聚(丙二醇)、聚(乙二醇)、聚(乙二醇)與聚(丙二醇)的共聚物、表氯醇等、或其組合。在一些具體實施例中,該多元醇成分包括聚(四亞甲醚二醇)。
在一些具體實施例中,該多元醇具有至少900之數量平均分子量。在其他具體實施例中,該多元醇具有至少900、1,000、1,500、1,750之數量平均分子量,及/或至多5,000、4,000、3,000、2,500、或甚至2,000之數量平均分子量。
在一些具體實施例中,該多元醇成分包含聚醚多元醇、聚酯多元醇、或其組合。在一些具體實施例中,該多元醇成分包含聚(四亞甲醚二醇)、聚己二酸伸丁酯、或其組合。在一些具體實施例中,該多元醇成分包含聚(四亞甲醚二醇)。在一些具體實施例中,該多元醇成分包含聚己二酸伸丁酯。
在此所述的TPU組成物係使用c)鏈延長劑成分製造。鏈延長劑包括二元醇、二胺、及其組合。
合適的鏈延長劑包括相當小的多羥基化合物,例如具有2至20個、或2至12個、或2至10個碳原子之低級脂肪族或短鏈二醇。合適的實例包括乙二醇、二乙二醇、丙二醇、二丙二醇、1,4-丁二醇(BDO)、1,6-己二醇(HDO)、1,3-丁二醇、1,5-戊二醇、新戊二醇、1,4-環己烷二甲醇(CHDM)、2,2-雙[4-(2-羥基乙氧基)苯基]丙烷(HEPP)、六亞甲二醇、庚二醇、壬二醇、十二碳二醇、3-甲基-1,5-戊二醇、乙二胺、丁二胺、六亞甲二胺、與羥基乙基間苯二酚(HER)等,及其混合物。在一些具體實施例中,該鏈延長劑包括BDO、HDO、3-甲基-1,5-戊二醇、或其組合。在一些具體實施例中,該鏈延長劑包括BDO。其可使用其他的二元醇,如芳香族二醇,但是在一些具體實施例中,在此所述的TPU本質上無、或甚至完全無此材料。
在一些具體實施例中,用以製備TPU之鏈延長劑實質上無、或甚至完全無1,6-己二醇。在一些具體實施例中,用以製備TPU之鏈延長劑包括環狀鏈延長劑。合適的實例包括CHDM、HEPP、HER、及其組合。在一些具體實施例中,用以製備TPU之鏈延長劑包括芳香族環狀鏈延長劑,例如HEPP、HER、或其組合。在一些具體實施例中,用以製備TPU之鏈延長劑包括脂肪族環狀鏈延長劑,例如CHDM。在一些具體實施例中,用以製備TPU之鏈延長劑實質上無、或甚至完全無芳香族鏈延長劑,例如芳香族環狀鏈延長劑。在一些具體實施例中,用以製備TPU之鏈延長劑實質上無、或甚至完全無聚矽氧烷。
在一些具體實施例中,該鏈延長劑成分包括1,4-丁二醇、2-乙基-1,3-己二醇、2,2,4-三甲基戊-1,3-二醇、1,6-己二醇、1,4-環己烷二羥甲基、1,3-丙二醇、3-甲基-1,5-戊二醇、或其組合。在一些具體實施例中,該鏈延長劑成分包括1,4-丁二醇、3-甲基-1,5-戊二醇、或其組合。在一些具體實施例中,該鏈延長劑成分包括1,4-丁二醇。
在一些具體實施例中,該鏈延長劑成分包含線形伸烷二醇。在一些具體實施例中,該鏈延長劑成分包含1,4-丁二醇。
在一些具體實施例中,鏈延長劑對多元醇的莫耳比例大於1.5。在一些具體實施例中,鏈延長劑對多元醇的莫耳比例為至少(或大於)1.5、2.0、3.5、3.7、或甚至3.8,及/或鏈延長劑對多元醇的莫耳比例可為至多5.0、或甚至4.0。
在此所述的熱塑性聚胺甲酸酯亦可被視為熱塑性聚胺甲酸酯(TPU)組成物。在此具體實施例中,該組成物可含有一種或以上的TPU。這些TPU係將以下反應而製備:a)上述的多異氰酸酯成分;b)上述的多元醇成分;及c)上述的鏈延長劑成分,其中該反應可在觸媒存在下進行。組成物中TPU至少之一必須符合上述參數而使其適合固態自由製作,尤其是熔合沈積成型。
進行反應之手段未過度限制,且包括分批及連續處理。在一些具體實施例中,該技術涉及脂肪族TPU之分批處理。在一些具體實施例中,該技術涉及脂肪族TPU之連續處理。
本發明揭述的組成物包括上述TPU材料、及包括TPU材料與一種或以上的額外成分之TPU組成物。這些額外成分包括可摻合在此所述的TPU之其他聚合材料。這些額外的成分包括一種或以上的可加入TPU之添加劑、或含TPU之摻合物,而影響組成物之性質。
在此所述的TPU亦可摻合一種或以上的其他聚合物。可摻合在此所述的TPU之聚合物未過度限制。在一些具體實施例中,本發明揭述的組成物包括二種或以上的本發明揭述的TPU材料。在一些具體實施例中,該組成物包括至少一種本發明揭述的TPU材料、及至少一種非本發明揭述的TPU材料之一的其他聚合物。
可結合在此所述的TPU材料而使用之聚合物亦包括較習知的TPU材料,如基於非己內酯聚酯之TPU、基於聚酯之TPU、基於聚醚之TPU、或含非己內酯聚酯與聚醚基之TPU。可摻合在此所述的TPU之其他合適材料包括聚碳酸酯、聚烯烴、苯乙烯系聚合物、丙烯酸系聚合物、聚氧亞甲基聚合物、聚醯胺、聚苯醚、聚苯硫醚、聚氯乙烯、氯化聚氯乙烯、聚乙酸、或其組合。
用於在此所述的摻合物之聚合物包括同元聚合物及共聚物。合適的實例包括:(i)聚烯烴(PO),如聚乙烯(PE)、聚丙烯(PP)、聚丁烯、乙烯/丙烯橡膠(EPR)、聚氧乙烯(POE)、環烯烴共聚物(COC)、或其組合;(ii)苯乙烯系,如聚苯乙烯(PS)、丙烯腈丁二烯苯乙烯(ABS)、苯乙烯丙烯腈(SAN)、苯乙烯丁二烯橡膠(SBR或HIPS)、聚α-甲基苯乙烯、苯乙烯順丁烯二酸酐(SMA)、苯乙烯-丁二烯共聚物(SBC)(如苯乙烯-丁二烯-苯乙烯共聚物(SBS)、及苯乙烯-乙烯/丁二烯-苯乙烯共聚物(SEBS))、苯乙烯-乙烯/丙烯-苯乙烯共聚物(SEPS)、苯乙烯丁二烯乳膠(SBL)、經乙烯丙烯二烯單體(EPDM)及/或丙烯酸系彈性體(例如PS-SBR共聚物)修改SAN、或其組合;(iii)上述以外的熱塑性聚胺甲酸酯(TPU);(iv)聚醯胺,如Nylon™,包括聚醯胺6,6 (PA66)、聚醯胺1,1 (PA11)、聚醯胺1,2 (PA12)、共聚醯胺(COPA)、或其組合;(v)丙烯酸系聚合物,如聚丙烯酸甲酯、聚甲基丙烯酸甲酯、甲基丙烯酸甲酯苯乙烯(MS)共聚物、或其組合;(vi)聚氯乙烯(PVC)、氯化聚氯乙烯(CPVC)、或其組合;(vii)聚甲醛,如聚縮醛;(viii)聚酯,如聚對苯二甲酸伸乙酯(PET)、聚對苯二甲酸伸丁酯(PBT),共聚酯及/或聚酯彈性體(COPE),包括聚醚-酯嵌段共聚物,如經二醇修改聚對苯二甲酸伸乙酯(PETG)、聚乳酸(PLA)、聚羥乙酸(PGA)、PLA與PGA的共聚物、或其組合;(ix)聚碳酸酯(PC)、聚苯硫醚(PPS)、聚苯醚(PPO)、或其組合;或其組合。
在一些具體實施例中,這些摻合物包括一種或以上的選自組(i)、(iii)、(vii)、(viii)之額外聚合材料、或其一些組合。在一些具體實施例中,這些摻合物包括一種或以上的選自組(i)之額外聚合材料。在一些具體實施例中,這些摻合物包括一種或以上的選自組(iii)之額外聚合材料。在一些具體實施例中,這些摻合物包括一種或以上的選自組(vii)之額外聚合材料。在一些具體實施例中,這些摻合物包括一種或以上的選自組(viii)之額外聚合材料。
適合用於在此所述的TPU組成物之額外添加劑未過度限制。合適的添加劑包括顏料、UV安定劑、UV吸收劑、抗氧化劑、潤滑劑、熱安定劑、水解安定劑、交聯活化劑、阻燃劑、分層氧化矽、填料、著色劑、強化劑、黏附中介劑、衝擊強度調節劑、殺微生物劑、及其任何組合。
在一些具體實施例中,額外成分為阻燃劑。合適的阻燃劑未過度限制,且可包括磷酸硼阻燃劑、氧化鎂、二季戊四醇、聚四氟乙烯(PTFE)聚合物、或其任何組合。在一些具體實施例中,此阻燃劑可包括磷酸硼阻燃劑、氧化鎂、二季戊四醇、或其任何組合。磷酸硼阻燃劑之一合適實例為由Budenheim USA, Inc.市售的BUDIT 326。若有則阻燃劑成分可以全部TPU組成物的0至10重量百分比,在其他具體實施例為全部TPU組成物的0.5至10、或1至10、或0.5或1至5、或0.5至3、或甚至1至3重量百分比之量存在。
在此所述的TPU組成物亦可包括額外的添加劑,其可稱為安定劑。安定劑可包括抗氧化劑,如酚系、亞磷酸酯、硫酯、與胺,光安定劑,如位阻胺光安定劑與苯并噻唑UV吸收劑,及其他之處理安定劑及其組合。在一具體實施例中,較佳的安定劑為得自BASF之Irganox 1010、及得自Chemtura之Naugard 445。安定劑係以TPU組成物之約0.1重量百分比至約5重量百分比,在另一具體實施例為約0.1重量百分比至約3重量百分比,及在另一具體實施例為約0.5重量百分比至約1.5重量百分比之量使用。
另外,各種習知的無機阻燃劑成分均可用於該TPU組成物。合適的無機阻燃劑包括任何所屬技術領域者已知者,如金屬氧化物、金屬氧化物水合物、金屬碳酸鹽、磷酸銨、多磷酸銨、碳酸鈣、氧化銻、黏土、礦物黏土(包括滑石、高嶺土、矽灰石、奈米黏土、經常指奈米黏土之蒙脫土黏土)、及其混合物。在一具體實施例中,阻燃劑套裝包括滑石。阻燃劑套裝中的滑石促進高限氧指數(LOI)之性質。無機阻燃劑可以TPU組成物總重量之0至約30重量百分比,約0.1至約20重量百分比,在另一具體實施例為約0.5重量百分比至約15重量百分比之量使用。
仍有其他的選用添加劑可被用於在此所述的TPU組成物。該添加劑包括著色劑、抗氧化劑(包括酚系、亞磷酸酯、硫酯、及/或胺)、抗臭氧劑、安定劑、惰性填料、潤滑劑、抑制劑、水解安定劑、光安定劑、位阻胺光安定劑、苯并三唑UV吸收劑、熱安定劑、防止變色之安定劑、染料、顏料、無機與有機填料、強化劑、及其組合。
上述的全部添加劑可以這些物質之習用有效量使用。該非阻燃性添加劑可以TPU組成物總重量之約0至約30重量百分比,在一具體實施例為約0.1至約25重量百分比,及在另一具體實施例為約0.1至約20重量百分比之量使用。
這些額外的添加劑可被併入用於製備TPU樹脂之成分中或反應混合物中,或者在製造TPU樹脂之後併入。在另一種方法中可將全部材料混合TPU樹脂然後熔化,或者可將其直接併入TPU樹脂的熔化物中。
上述的TPU材料可藉包括以下步驟之方法製備:(I)反應a)上述的多異氰酸酯成分;b)上述的多元醇成分;及c)上述的鏈延長劑成分,其中該反應可在觸媒存在下進行,而生成熱塑性聚胺甲酸酯組成物。
該方法可進一步包括步驟:(II)將步驟(I)之TPU混合一種或以上的摻合物成分,其包括一種或以上的額外TPU材料及/或聚合物,包括任何上述者。
該方法可進一步包括步驟:(II)將步驟(I)之TPU組成物混合一種或以上的上述額外添加劑。
該方法可進一步包括步驟:(II)將步驟(I)之TPU組成物混合一種或以上的摻合物成分,其包括一種或以上的額外TPU材料及/或聚合物,包括任何上述者,及/或步驟:(III)將步驟(I)之TPU組成物混合一種或以上的上述額外添加劑。
雖然不希望受理論限制,但據信任何符合在此所述要求的TPU會比不符合的TPU更適合固態自由製作,尤其是熔合沈積成型。據信必要參數為相當高的結晶溫度、及相當高的增溫下之模數保留度。雖然不希望受理論限制,但據信具有相當高的結晶溫度對自由製作,尤其是熔合沈積成型,提供較佳的操作窗,且相當高的模數保留度可使熱塑性聚胺甲酸酯在處理期間維持較多的其結構整體性,其為自由製作(尤其是熔合沈積成型)之必要屬性。據信這些參數的組合提供極適合自由製作(尤其是熔合沈積成型)之TPU。
在一些具體實施例中,可用於本發明揭述的技術之TPU具有高於80℃之結晶溫度,且其100℃剪切儲存模數相對其20℃剪切儲存模數保留超過20%。
在一些具體實施例中,該TPU具有大於100℃、105℃、110℃、或甚至大於115℃、或甚至約117℃之結晶溫度。在一些具體實施例中,該結晶溫度不超過200℃、150℃、或甚至120℃。
在一些具體實施例中,該TPU之50℃剪切儲存模數相對其20℃剪切儲存模數保留超過50%;其100℃剪切儲存模數相對其50℃剪切儲存模數保留超過42%;其150℃剪切儲存模數相對其120℃剪切儲存模數保留超過20%;或其任何組合。
在一些具體實施例中,該TPU之50℃剪切儲存模數相對其20℃剪切儲存模數保留超過60%;其100℃剪切儲存模數相對其20℃剪切儲存模數保留超過30%;或其任何組合。
在一些具體實施例中,該TPU之100℃剪切儲存模數相對其50℃剪切儲存模數保留超過45%;其120℃剪切儲存模數相對其100℃剪切儲存模數保留超過70%;其105℃剪切儲存模數相對其20℃剪切儲存模數保留超過5%;或其任何組合。
在又其他具體實施例中,該TPU之剪切儲存模數對剪切損失模數交叉溫度(即剪切儲存模數G’對剪切損失模數G”的比例為1之溫度)超過170℃、或甚至超過180℃。在一些具體實施例中,除了上述的結晶溫度及剪切儲存模數保留度參數,亦有此剪切儲存模數對剪切損失模數交叉溫度。在其他具體實施例中,該剪切儲存模數對剪切損失模數交叉溫度可取代上述的剪切儲存模數保留度參數。《系統及方法》
用於本發明揭述的技術中的固態自由製作系統,尤其是熔合沈積成型系統,及使用其之方法未過度限制。應注意,本發明揭述的技術提供比其他熱塑性聚胺甲酸酯更適合固態自由製作系統,尤其是熔合沈積成型系統的特定熱塑性聚胺甲酸酯,且本發明揭述的技術之關鍵為相對益處。應注意,一些固態自由製作系統,包括一些熔合沈積成型系統,由於其設備組態、處理參數等,而可更適合用以處理特定材料,包括熱塑性聚胺甲酸酯。然而,本發明揭述的技術不聚焦在固態自由製作系統(包括一些熔合沈積成型系統)之細節,而是聚焦在提供更適合一般固態自由製作系統(尤其是一般熔合沈積成型系統)之特定熱塑性聚胺甲酸酯。
可用於本發明揭述的技術之熔合沈積成型(FDM)系統包括藉由將建構材料加熱成半液態,且依照電腦控制路徑將其擠壓,而以層接層方式建構零件之系統。該材料可從分配器如材料之半連續流動及/或纖絲而分配,或者其可如個別滴而分配。FDM用途經使用兩種材料完成一次建構。成型材料被用以組成最終作品。支撐材料亦可作為成型材料之支架。將材料纖絲從系統材料儲器進料至其印刷頭,其一般在二維平面中移動,在基座沿第三軸移動至新高度及/或平面及開始次一層之前沈積材料而完成各層。一旦系統完成建構,則使用者可將支撐材料移開,或者甚至將其溶解,而留下已可使用之零件。
本發明揭示的技術進一步提供所述的熱塑性聚胺甲酸酯在所述的系統及方法中的用途,及由其製造的物品。《物品》
在此所述的系統及方法可利用在此所述的熱塑性聚胺甲酸酯,且製造各種物件及/或物品。以本發明揭示的技術製造的物件及/或物品未過度限制。
在一些具體實施例中,該物件及/或物品包含烹飪與儲存器具、爐具、汽車組件、玩具、運動服、醫學裝置、個人醫學物品、複製醫學植體、牙科物品、消毒容器、帷幕、袍服、過濾器、衛生產品、尿布、膜狀物、片狀物、管子、管線、電線外套、電纜外套、農業用膜、低透氣性蔽幛、運動設備、鑄膜、吹製膜、外形、船隻及船舶組件、條板箱、容器、包裝物、實驗室器具、辦公室地墊、儀器樣品保持器、液體儲存容器、包裝材料、醫學管線與閥、鞋類組件、片狀物、帶狀物、地毯、黏著劑、電線外皮、電纜、保護性服裝、汽車零件、塗層、發泡積層體、超模塑物品、汽車表皮、天蓬、防水布、皮革物品、屋頂構造物品、方向盤、塗層粉料、搪塑粉料、消費者耐久財、握把、手把、軟管、軟管內墊、管線、管線內墊、腳輪、溜冰輪、電腦組件、皮帶、貼布、鞋類組件、輸送帶或正時皮帶、手套、纖維、織物、或衣服。
可用於本發明之額外物品包括珠寶、客製紀念品及/或收藏品(例如但不限於硬幣、徽章)、框架與畫框、眼鏡架、鑰匙、杯子、馬克杯、微型複製品與模型、手環、個人化公仔等。
如同所有的增材製造,此技術對於製造物品作為快速原型設計及新產品發展的零件,作為製造習用及/或單次零件的零件,或大量生產大批物品無保證及/或不可行之類似應用特別有價值。
本發明之組成物,包括其任何摻合物,更可用於極多種應用,包括透明物品,如烹飪與儲存器具,及其他物品,如汽車組件、消毒醫學裝置、纖維、紡織品、非織品、定向膜、及其他此種物品。該組成物適合汽車組件,如保險桿、格柵、裁剪部件、儀表板與儀器面板、外門與車篷組件、導流板、擋風玻璃、轂蓋、照後鏡殼、車身嵌板、保護性側墊、以及汽車、卡車、船隻、及其他交通工具相關的其他的內裝與外裝組件。
其他可由本發明之組成物形成的有用物品及貨品包括:實驗室器具,如培氧生長用之滾瓶與媒介瓶、儀器樣品窗;液體儲存容器,如儲存及血液或溶液之IV注射用之袋、囊、與瓶;包裝材料,包括用於任何醫學裝置或藥物者(包括單位劑量或其他的泡狀或氣泡包裝),及用於包覆或容納食品免受照射者。其他有用的項目包括用於任何醫學裝置之醫學管線與閥,包括注射套件、導管、及呼吸治療,以及醫學裝置或被照射的食品用之包裝材料,包括托盤,以及儲存液體(尤其是水、乳品、或果汁)容器,包括單份及大儲放容器,以及轉移裝置,如管子、軟管、管線等,包括其內墊及/或外層。在一些具體實施例中,本發明之物品為消防水管,其包括以在此所述的TPU組成物製造的內墊。在一些具體實施例中,該內墊為塗佈於消防水管內套之層。
又進一步有用的應用及物品包括:汽車物品,包括安全氣囊殼、汽車內面;生醫裝置,包括可植入裝置、心律調節器引線、人工心臟、心瓣膜、血管支架層、人工韌帶、動脈與靜脈、含醫藥活性藥劑之植體、醫藥袋、醫學管子、藥物輸送裝置(如避孕環)、及生物可吸收植體;鞋類相關物品,包括鞋面與鞋底,其中鞋底可包括內底、中底、與外底,連接任何所述部分之黏著系統,其他的鞋類部分,包括黏著劑與織物塗料、鞋釘、透氣膜、氣囊、膠囊、或流體囊、已充氣或可充氣嵌件、層壓嵌件、緩衝裝置、以微球體製造的鞋底、後跟、嵌入鞋底之輪組、可充氣鞋舌、紡織與非織品、氣味與水分吸收墊、加壓腳踝套環、眼孔與花邊、矯正裝置或嵌件、膠墊、彈性墊、屏障膜與布料、及人造皮革;高爾夫球相關物品,包括2片式與3片式高爾夫球,包括球殼與內核。
特別相關為個人化醫學物品,如為病人客製之矯具、植體、骨頭、牙科物品、血管等。例如對於特別為該病人設計植體之特定病人可使用上述系統及方法製備骨頭部分及/或植體。
除非另有指示,否則各所述化學成分之量係排除可習慣上存在於市售材料之任何溶劑或稀釋劑油,按有效化學物計而提出。然而除非另有指示,否則在此引用的各化學物或組成物應被解讀為商業級材料,其可含有異構物、副產物、衍生物、及其他通常認可在商業級出現的材料。
已知一些上述材料會在最終調配物中交互作用,使得最終調配物之成分異於最初添加者。例如(例如阻燃劑之)金屬離子會移動至其他分子之其他酸性或陰離子性位置。如此形成的產物,包括將在此所述的技術之組成物用於其意圖用途時形成的產物,不易被簡單說明。儘管如此,所有的此種修改及反應產物均包括於在此所述的技術之範圍內;在此所述的技術包含摻合上述成分而製備的組成物。
[實施例]
在此所述的技術可參考以下非限制實施例而較佳地了解。
材料。
製備數種熱塑性聚胺甲酸酯(TPU),且評估其用於熔合沈積成型之適用性。TPU-A為鏈延長劑對多元醇之莫耳比例為約1.4,及硬段含量為約50%之聚酯TPU。TPU-B為鏈延長劑對多元醇之莫耳比例為約2.0,及硬段含量為約48%之聚醚TPU。TPU-C為鏈延長劑對多元醇之莫耳比例為約3.9,及硬段含量為約52%之聚酯TPU。TPU-D為鏈延長劑對多元醇之莫耳比例為約3.7,及硬段含量為約43%之聚醚TPU。
測試各TPU材料而測定其用於熔合沈積成型之適用性。此測試結果歸納於下。所有的模數資料均藉ASTM D5279收集。
表1:FDM處理相關的TPU性質之概要
TPU-A | TPU-B | TPU-C | TPU-D | |
Tc (℃) | 73 | 99 | 102 | 117 |
Tm (℃) | 130 | 140 | 170 | 192 |
在20℃之G’ (mPa) | 37.9 | 12.4 | 36.5 | 17.1 |
在50℃之G’ (mPa) | 18.2 | 10.1 | 18.8 | 14.8 |
在100℃之G’ (mPa) | 7.4 | 4.4 | 9.0 | 7.9 |
在120℃之G’ (mPa) | 2.8 | 6.7 | 5.5 | |
在150℃之G’ (mPa) | 0.83 | 0.5 | 3.6 | 1.5 |
G’/G”交叉(℃) | 165 | 178 | 188 | 178 |
使用以上資料計算剪切儲存模數之保留百分比,且歸納於下表。
表2:剪切儲存模數保留度之概要
TPU-A | TPU-B | TPU-C | TPU-D | |
20℃至50℃之保留度 | 48% | 81% | 52% | 87% |
20℃至100℃之保留度 | 20% | 35% | 25% | 46% |
20℃至120℃之保留度 | 23% | 18% | 32% | |
20℃至150℃之保留度 | 2% | 4% | 10% | 9% |
50℃至100℃之保留度 | 41% | 44% | 48% | 53% |
100℃至120℃之保留度 | 64% | 74% | 70% | |
120℃至150℃之保留度 | 18% | 54% | 27% |
以上結果顯示,TPU-A最不適合熔合沈積成型,而TPU-B、TPU-C、與TPU-D較適合熔合沈積成型。這些結果符合迄今在熔合沈積成型系統中測試各TPU材料而得知的結果。
分子量分布可藉保持在40℃之Waters凝膠滲透層析術(GPC)測量,其裝有Waters 515型泵、Waters 717型自動取樣機、及Waters 2414型折射率偵測器。GPC條件可為溫度為40℃,管柱組為Phenogel Guard + 2x混合D (5u),300 x 7.5毫米,移動相為以250 ppm之丁基化羥基甲苯安定化的四氫呋喃(THF),流速為1.0毫升/分鐘,注設體積為50微升,樣品濃度為~0.12%,及使用Waters Empower Pro Software獲取資料。一般而言,將少量(一般為大約0.05克)聚合物溶於20毫升之安定化HPLC級THF,通過0.45微米聚四氟乙烯拋棄式過濾器(Whatman)過濾,及注射至GPC中。分子量校正曲線可使用得自Polymer Laboratories之EasiCal®聚苯乙烯標準品建立。
以上參考的各文件均納入此處作為參考,其包括任何請求優先權之先申請案,不論以上是否特別列出。提及任何文件絕非在法律上同意此文件合格作為先行技術,或者貢獻所屬技術領域者之常識。應了解,除了在實施例中或另有明確指示之處之外,本說明中所有指定材料的量、反應條件、分子量、碳原子數量等之數值均以文字「約」修飾。應了解,在此所述的上下限的量、範圍、及比例限制均可獨立組合。類似地,在此所述的技術之各要素之範圍及量可連同任何其他要素之範圍或量一起使用。
在此使用的轉折術語「包含(comprising)」,其與「包括(including)」、「含有(containing)」、或「特徵為(characterized by)」同義,為包容性或開放式,且不排除額外的未陳述要素或方法步驟。然而,在此每次述及「包含(comprising)」則意圖為該術語亦包含片語「本質上由…所組成(consisting essentially of)」及「由…所組成(consisting of)」作為替代性具體實施例,其中「由…所組成」排除任何未指定的要素或步驟,及「本質上由…所組成」可包含實際上不影響所考量的組成物或方法之基本及新穎特徵之額外的未陳述要素或步驟。即「本質上由…所組成(consisting essentially of)」可包括實際上不影響所考量的組成物之基本及新穎特徵的物質。
雖然為了例證在此所述的本發明技術之目的而已顯示特定的代表性具體實施例及細節,但其中可進行各種變化及修改而不背離本發明之範圍對所屬技術領域者為明顯的。關於此點,在此所述的本發明技術之範圍僅受以下申請專利範圍限制。
無。
無。
無。
Claims (16)
- 一種固態自由製作三維物件用之系統,其包含:固態自由製作裝置,其以控制方式沈積建構材料小粒;其中該建構材料包含衍生自(a)多異氰酸酯成分,(b)多元醇成分,及(c)選用鏈延長劑成分之熱塑性聚胺甲酸酯;其中生成的熱塑性聚胺甲酸酯具有高於80℃之結晶溫度;及其中生成的熱塑性聚胺甲酸酯之100℃剪切儲存模數相對其20℃剪切儲存模數保留超過20%。
- 一種製作三維物件之方法,其包含步驟:(I)操作固態自由製作物件之系統;其中該系統包含以控制方式沈積建構材料小粒之固態自由製作裝置;而形成三維物件;其中該建構材料包含衍生自(a)多異氰酸酯成分,(b)多元醇成分,及(c)選用鏈延長劑成分之熱塑性聚胺甲酸酯;其中生成的熱塑性聚胺甲酸酯具有高於80℃之結晶溫度;及其中生成的熱塑性聚胺甲酸酯之100℃剪切儲存模數相對其20℃剪切儲存模數保留超過20%。
- 一種由固態自由製作物件用之系統製作的製造物件,其包含:以控制方式沈積建構材料小粒之固態自由製作裝置;其中該建構材料包含衍生自(a)多異氰酸酯成分,(b)多元醇成分,及(c)選用鏈延長劑成分之熱塑性聚胺甲酸酯;其中生成的熱塑性聚胺甲酸酯具有高於80℃之結晶溫度;及其中生成的熱塑性聚胺甲酸酯之100℃剪切儲存模數相對其20℃剪切儲存模數保留超過20%。
- 如請求項1至3中任一項之系統或方法或物品,其中該固態自由製作裝置包含(a)複數個分配頭;(b)設計成對該製作裝置供應複數種建構材料之建構材料供應裝置;及(c)設計成基於選自複數個預定操作模式之操作模式而控制該製作裝置及該建構材料供應裝置之控制單元。
- 如請求項1至4中任一項之系統或方法或物品,其中該固態自由製作裝置包含熔合沈積成型裝置。
- 如請求項1至5中任一項之系統或方法或物品,其中該鏈延長劑對該多元醇的莫耳比例大於1.5。
- 如請求項1至6中任一項之系統或方法或物品,其中該多元醇具有至少900之數量平均分子量。
- 如請求項1至7中任一項之系統或方法或物品,其中該多異氰酸酯成分包含芳香族二異氰酸酯。
- 如請求項1至7中任一項之系統或方法或物品,其中該多異氰酸酯成分包含4,4’-亞甲雙(異氰酸苯酯)。
- 如請求項1至9中任一項之系統或方法或物品,其中該多元醇成分包含聚醚多元醇、聚酯多元醇、或其組合。
- 如請求項1至10中任一項之系統或方法或物品,其中該多元醇成分包含聚(四亞甲基醚二醇)、聚己二酸伸丁酯、或其組合。
- 如請求項1至11中任一項之系統或方法或物品,其中該鏈延長劑成分包含線形伸烷二醇。
- 如請求項1至12中任一項之系統或方法或物品,其中該鏈延長劑成分包含1,4-丁二醇。
- 如請求項1至13中任一項之系統或方法或物品,其中該熱塑性聚胺甲酸酯進一步包含一種或以上的著色劑、抗氧化劑(包括酚系、亞磷酸酯、硫酯、及/或胺)、抗臭氧劑、安定劑、惰性填料、潤滑劑、抑制劑、水解安定劑、光安定劑、位阻胺光安定劑、苯并三唑UV吸收劑、熱安定劑、防止變色之安定劑、染料、顏料、無機與有機填料、強化劑、或其任何組合。
- 如請求項4至14中任一項之物品,其中該物品包含烹飪與儲存器具、爐具、汽車組件、玩具、運動服、醫學裝置、個人醫學物品、複製醫學植體、牙科物品、消毒容器、帷幕、袍服、過濾器、衛生產品、尿布、膜狀物、片狀物、管子、管線、電線外套、電纜外套、農業用膜、低透氣性蔽幛、運動設備、鑄膜、吹製膜、外形、船隻及船舶組件、條板箱、容器、包裝物、實驗室器具、辦公室地墊、儀器樣品保持器、液體儲存容器、包裝材料、醫學管線與閥、鞋類組件、片狀物、帶狀物、地毯、黏著劑、電線外皮、電纜、保護性服裝、汽車零件、塗層、發泡積層體、超模塑物品、汽車表皮、天蓬、防水布、皮革物品、屋頂構造物品、方向盤、塗層粉料、搪塑粉料、消費者耐久財、握把、手把、軟管、軟管內墊、管線、管線內墊、腳輪、溜冰輪、電腦組件、皮帶、貼布、鞋類組件、輸送帶或正時皮帶、手套、纖維、織物、或衣服。
- 一種由固態自由製作用之系統製作的醫學裝置,其中該醫學裝置由以控制方式沈積建構材料小粒之固態自由製作裝置製造;其中該建構材料包含衍生自(a)多異氰酸酯成分,(b)多元醇成分,及(c)選用鏈延長劑成分之熱塑性聚胺甲酸酯;其中生成的熱塑性聚胺甲酸酯具有高於80℃之結晶溫度;及其中生成的熱塑性聚胺甲酸酯之100℃剪切儲存模數相對其20℃剪切儲存模數保留超過20%。