TW201702361A - 液晶組合物及液晶顯示元件 - Google Patents

液晶組合物及液晶顯示元件 Download PDF

Info

Publication number
TW201702361A
TW201702361A TW105103383A TW105103383A TW201702361A TW 201702361 A TW201702361 A TW 201702361A TW 105103383 A TW105103383 A TW 105103383A TW 105103383 A TW105103383 A TW 105103383A TW 201702361 A TW201702361 A TW 201702361A
Authority
TW
Taiwan
Prior art keywords
carbon atoms
fluorine
group
substituted
liquid crystal
Prior art date
Application number
TW105103383A
Other languages
English (en)
Other versions
TWI563071B (zh
Inventor
guo-liang Yuan
Kui Wang
yun-xia Qiao
Wei Wang
yan-li Dong
Original Assignee
Shijiazhuang Chengzhi Yonghua Display Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shijiazhuang Chengzhi Yonghua Display Materials Co Ltd filed Critical Shijiazhuang Chengzhi Yonghua Display Materials Co Ltd
Application granted granted Critical
Publication of TWI563071B publication Critical patent/TWI563071B/zh
Publication of TW201702361A publication Critical patent/TW201702361A/zh

Abstract

本發明提供了一種液晶組合物，包含一種或多種式Ⅰ所示化合物、一種或多種式Ⅱ所示化合物以及式Ⅱ-A所示化合物；其中，□Ⅰ□Ⅱ□Ⅱ-A 其中各取代基均給出其定義。 本發明所提供的組合物具有低黏度γ1、適中的介電異方性Δε、適中的雙折射性Δn，可以實現液晶顯示的快速回應。

Description

液晶組合物及液晶顯示元件
本發明涉及液晶顯示領域，具體涉及一種液晶組合物及包含該液晶組合物的液晶顯示元件或液晶顯示器。
目前，液晶化合物的應用範圍拓展的越來越廣，其可應用於多種類型的顯示器、電光元件、感測器等中。用於上述顯示領域的液晶化合物的種類繁多，其中向列型液晶應用最為廣泛。向列型液晶已經應用在無源TN、STN矩陣顯示器和具有TFT有源矩陣的系統中。
對於薄膜電晶體技術（TFT-LCD）應用領域，近年來市場雖然已經非常巨大，技術也逐漸成熟，但人們對顯示技術的要求也在不斷的提高，尤其是在實現快速回應，降低驅動電壓以降低功耗等方面。液晶材料作為液晶顯示器重要的光電子材料之一，對改善液晶顯示器的性能發揮重要的作用。
作為液晶材料，需要具有良好的化學和熱穩定性以及對電場和電磁輻射的穩定性。而作為薄膜電晶體技術（TFT-LCD）用液晶材料，不僅需要具有如上穩定性外，還應具有較寬的向列相溫度範圍、合適的雙折射率各向異性、非常高的電阻率、良好的抗紫外線性能、高電荷保持率以及低蒸汽壓等性能。
對於動態畫面顯示應用，消除顯示畫面殘影和拖尾，要求液晶具有很快的回應速度，因此要求液晶具有較低的旋轉黏度γ1 ；另外，對於可擕式設備，為了降低設備能耗，希望液晶的驅動電壓盡可能低；而對於電視等用途的顯示器來說，對於液晶的驅動電壓要求不是那麼的低。
液晶化合物的黏度，尤其是旋轉黏度γ1 直接影響液晶加電後的回應時間，不管是上升時間（ton ）還是下降時間(toff )，都與液晶的旋轉黏度γ1 成正比關係，上升時間（ton ）由於與液晶盒和驅動電壓有關，可以藉由加大驅動電壓的方法與降低液晶盒厚度來調節；而下降時間(toff )與驅動電壓無關，主要是與液晶的彈性常數與液晶盒厚度有關，厚度的下降會降低下降時間(toff )，而不同顯示模式下，液晶分子的運動方式不一樣，TN、IPS、VA三種模式分別與平均彈性常數K、扭曲彈性常數、彎曲彈性常數成反比關係。
依照液晶連續體理論，各種不同的液晶在外力（電場、磁場）作用下發生形變後，會藉由分子間的相互作用，會“回彈”回原來的形狀；同樣的，液晶也是由於分子間的相互作用力形成“黏度”。液晶分子的微小變化，會使液晶的常規參數性能發生明顯的變化，這些變化有的是有一定規律的，有的似乎不易找到規律，對於液晶分子間的相互作用也會產生明顯的影響，這些影響非常微妙，至今也沒有形成很完善的理論解釋。
液晶的黏度與液晶分子結構有關，研究不同液晶分子形成的液晶體系的黏度與液晶分子結構之間的關係是液晶配方工程師的重要任務之一。
本發明的目的在於提供一種液晶組合物及包含該液晶組合物的液晶顯示元件或液晶顯示器，該液晶組合物具有較低的黏度，可以實現快速回應，同時具有適中的介電異方性Δε、適中的雙折射性Δn、高的對熱和光的穩定性。包含該液晶組合物的液晶顯示元件或液晶顯示器具有較寬的向列相溫度範圍、合適的雙折射率各向異性、非常高的電阻率、良好的抗紫外線性能、高電荷保持率以及低蒸汽壓等性能。
為了實現上述有益技術效果，本發明提供了一種液晶組合物，液晶組合物包含一種或多種式Ⅰ所示化合物、一種或多種式Ⅱ所示化合物，以及式Ⅱ-A所示化合物，其中Ⅰ、Ⅱ、Ⅱ-A。
其中，Y1 表示F或H，Y2 表示F、OCF3 、CF3 或OCF2 H，並且Y1 、Y2 不能同時表示F；
R1 、R2 、R3 各自獨立地表示碳原子數為1～9的烷基、氟取代的碳原子數為1～9的烷基、碳原子數為1～9的烷氧基、氟取代的碳原子數為1～9的烷氧基、碳原子數為2～9的鏈烯基、氟取代的碳原子數為2～9的鏈烯基、碳原子數為3～8的鏈烯氧基或氟取代的碳原子數為3～8的鏈烯氧基；
、各自獨立地表示1,4-亞苯基、1,4-亞環己基或1,4-亞環己烯基。
本發明所提供的液晶組合物必須包含至少一種式Ⅰ所示化合物，以及必須包含式Ⅱ所示化合物中式Ⅱ-A所示化合物，還可以包含一種或多種式Ⅱ所示化合物中除式Ⅱ-A以外的其他化合物。
作為較佳方案，本發明所提供的液晶組合物不包含含有-CN的液晶化合物，並且不包含含有吡啶或嘧啶環的液晶化合物。
本發明進一步較佳不含有稠環結構的液晶化合物。
本發明所提供的液晶組合物Δn[589nm, 25℃] ＞0.08，Δε[1KHz, 25℃] ＞2，清晰點Cp＞70.0℃，旋轉黏度γ1 [25℃]在40～110mPa·s之間。
本發明所提供的液晶組合物，其中式Ⅰ所示化合物較佳質量含量為1～20%；式Ⅱ-A所示化合物較佳含量為20～40%，式Ⅱ所示化合物較佳含量為25～55%；
本發明的液晶組合物不包含含有-CN結構的液晶成分以及含有吡啶、嘧啶環化合物。-CN具有很大的永久偶極矩，電子雲較為豐富，易於吸附陽離子從而導致液晶電學性能的下降，比如電荷保持率VHR、電阻率ρ、功耗等；吡啶、嘧啶環化合物由於在UV下電子易於受到激發而導致品質下降。
稠環結構液晶分子往往不具備好的線性，黏度偏大，含有這些成分不利於改善液晶的回應速度。
式Ⅰ所示化合物較佳為式Ⅰ1～Ⅰ7所示化合物：Ⅰ1、Ⅰ2、Ⅰ3、Ⅰ4、Ⅰ5、Ⅰ6、Ⅰ7。
其中，R1 各自獨立地表示碳原子數為1～9的烷基、氟取代的碳原子數為1～9的烷基、碳原子數為1～9的烷氧基、氟取代的碳原子數為1～9的烷氧基、碳原子數為2～9的鏈烯基、氟取代的碳原子數為2～9的鏈烯基、碳原子數為3～8的鏈烯氧基或氟取代的碳原子數為3～8的鏈烯氧基；
一種或多種式Ⅱ所示化合物包含式Ⅱ-A所示化合物以及較佳包含Ⅱ1～Ⅱ10所示化合物中的一種或多種化合物，其中Ⅱ1、Ⅱ2、Ⅱ3、Ⅱ4、Ⅱ5、Ⅱ6、Ⅱ7、Ⅱ8、Ⅱ9、Ⅱ10。
式Ⅰ所示化合物普遍具有與其他液晶良好的互溶性，而且具有較高的清晰點CP，一般在200℃以上，但是隨著R1 烷基鏈長度而變化，烷基鏈較長時，清晰點CP會更高，Y1 、Y2 的變化也會改變CP，氟原子多往往會帶來CP下降，同時介電異方性Δε上升，OCF3 會帶來CP相對於F大約10℃以上的上升。
式Ⅰ所示化合物介電異方性Δε較大，在9～20之間，由於取代基OCF3 、CF3 電負性較大以及與氟原子形成的累積效應，Ⅰ3、Ⅰ4、Ⅰ7、Ⅰ8所示化合物具有較大的永久偶極矩，因而介電異方性Δε相對較大，達到15或更大。
式Ⅰ5、Ⅰ6、Ⅰ7、Ⅰ8所示化合物具有三聯苯共軛體系，相對於式Ⅰ1、Ⅰ2、Ⅰ3、Ⅰ4所示化合物聯苯共軛體系大，式Ⅰ5、Ⅰ6、Ⅰ7、Ⅰ8所示化合物具有較大的雙折射性Δn。分別適用於調配較大或較小Δn的液晶混合物。
式Ⅱ所示化合物具有很低的旋轉黏度γ1 、接近中性的介電異方性Δε、較小的雙折射性Δn，在改善液晶黏度、低溫性能具有優勢。不同的烷基取代基對液晶的旋轉黏度γ1 、清晰點CP都具有影響，一般的較長的烷基鏈或烯基鏈會加大液晶的旋轉黏度γ1 同時提高清晰點CP，但是式Ⅱ-A所示化合物γ1 最低。
本發明所提供的液晶組合物，還可以加入一種或多種式Ⅲ所示化合物Ⅲ
其中，R4 表示碳原子數為1～9的烷基、氟取代的碳原子數為1～9的烷基、碳原子數為1～9的烷氧基、氟取代的碳原子數為1～9的烷氧基、碳原子數為2～9的鏈烯基、氟取代的碳原子數為2～9的鏈烯基、碳原子數為3～8的鏈烯氧基或氟取代的碳原子數為3～8的鏈烯氧基；
表示1,4-亞苯基、1,4-亞環己基或1,4-亞環己烯基。
本發明所提供的液晶組合物，其中式Ⅲ所示化合物較佳質量含量為5～20%。
式Ⅲ所示化合物具體較佳為：、、、、、、、、、、、。
式Ⅲ所示化合物雙折射性Δn適中，介電異方性Δε在5～9之間，較低的旋轉黏度γ1 ，清晰點CP一般在120℃以上，可用於調節混合液晶CP、Δn、Δε、γ1 等參數。式Ⅲ所示化合物中，較佳R1 表示C1 ～C5 的直鏈烷基的化合物。
在本發明所提供的液晶組合物，還可以加入式一種或多種式Ⅳ所示化合物，其中Ⅳ
其中，R5 表示碳原子數為1～9的烷基、氟取代的碳原子數為1～9的烷基、碳原子數為1～9的烷氧基、氟取代的碳原子數為1～9的烷氧基、碳原子數為2～9的鏈烯基、氟取代的碳原子數為2～9的鏈烯基、碳原子數為3～8的鏈烯氧基或氟取代的碳原子數為3～8的鏈烯氧基；
n表示0，1；
（F）表示H或F。
本發明所提供的液晶組合物，其中式Ⅳ所示化合物較佳質量含量為5～20%。
式Ⅳ所示化合物中，較佳R1 表示C1 ～C5 的直鏈烷基的化合物。式Ⅳ所示化合物具有適中的Δε、較高的CP，較低的黏度適用於調節液晶的黏度、CP、Δε。
式Ⅳ所示化合物另外較佳為：Ⅳ-1、Ⅳ-2、Ⅳ-3、Ⅳ-4 。
本發明所提供的液晶組合物，還可以加入一種或多種式Ⅴ所示化合物，其中Ⅴ
其中，R6 、R7 各自獨立地表示碳原子數為1～9的烷基、氟取代的碳原子數為1～9的烷基、碳原子數為1～9的烷氧基、氟取代的碳原子數為1～9的烷氧基、碳原子數為2～9的鏈烯基、氟取代的碳原子數為2～9的鏈烯基、碳原子數為3～8的鏈烯氧基或氟取代的碳原子數為3～8的鏈烯氧基；
Y3 、Y4 表示H或F，但不能同時為F；
表示1,4-亞苯基、1,4-亞環己基或1,4-亞環己烯基。
本發明所提供的液晶組合物，其中式Ⅴ所示化合物較佳質量含量為2～15%。
式Ⅴ所示化合物，較佳R6 、R7 表示C1 ～C5 的直鏈烷基的化合物。式Ⅴ所示化合物具有很高的CP，有利於拓展液晶的使用溫度範圍。
式Ⅴ所示化合物另外較佳為：、、、。
式Ⅴ所示化合物R6 、R7 較佳C1 ～C5 直鏈烷基。
本發明所提供的液晶組合物，還可以加入一種或多種式Ⅵ所示化合物Ⅵ
其中，R8 表示碳原子數為1～9的烷基、氟取代的碳原子數為1～9的烷基、碳原子數為1～9的烷氧基、氟取代的碳原子數為1～9的烷氧基、碳原子數為2～9的鏈烯基、氟取代的碳原子數為2～9的鏈烯基、碳原子數為3～8的鏈烯氧基或氟取代的碳原子數為3～8的鏈烯氧基；
表示1,4-亞苯基、1,4-亞環己基或1,4-亞環己烯基；
表示1,4-亞苯基、氟代1,4-亞苯基、1,4-亞環己基或1,4-亞環己烯基；
R9 表示F、碳原子數為1～9的烷基、氟取代的碳原子數為1～9的烷基、碳原子數為1～9的烷氧基、氟取代的碳原子數為1～9的烷氧基、碳原子數為2～9的鏈烯基、氟取代的碳原子數為2～9的鏈烯基、碳原子數為3～8的鏈烯氧基或氟取代的碳原子數為3～8的鏈烯氧基。
本發明所提供的液晶組合物，其中式Ⅵ所示化合物較佳質量含量為5～30%。
式Ⅵ所示化合物另外較佳為：Ⅵ-1、Ⅵ-2、Ⅵ-3、Ⅵ-4、Ⅵ-5。
式Ⅵ-1、Ⅵ-2所示化合物為介電異方性Δε接近中性，低的旋轉黏度γ1 ，清晰點較高，K值較大，可以用於調配液晶的K值以及γ1 ，從而實現快速回應。三聯苯類Ⅵ-5所示化合物由於具有較大的共軛體系，因而具有很大的雙折射性Δn，尤其適用於調配大折射率的混合液晶。
本發明所提供的液晶組合物，還可以加入一種或多種式Ⅶ所示化合物Ⅶ
其中，R10 表示碳原子數為1～9的烷基、氟取代的碳原子數為1～9的烷基、碳原子數為1～9的烷氧基、氟取代的碳原子數為1～9的烷氧基、碳原子數為2～9的鏈烯基、氟取代的碳原子數為2～9的鏈烯基、碳原子數為3～8的鏈烯氧基或氟取代的碳原子數為3～8的鏈烯氧基；
表示1,4-亞苯基、氟代1,4-亞苯基、1,4-亞環己基、1,4-亞環己烯基和/或1,4-亞環己基中一個或不相連的兩個CH2 被氧取代所形成的基團中的一種或多種；
p表示2或3。
本發明所提供的液晶組合物，其中式Ⅶ所示化合物較佳質量含量為5～55%。
式Ⅶ所示化合物另外較佳為：、、、、、、、、、。
式Ⅶ所示化合物具有較大的介電異方性Δε，低的旋轉黏度γ1 ，可以用於調配液晶混合物用以降低液晶驅動電壓、加快顯示元件的回應速度。
本發明所提供的液晶組合物，在包含或者不包含式Ⅲ、式Ⅳ、式Ⅴ、式Ⅵ、式Ⅶ所示化合物的基礎上，還可以包含有一種或多種式Ⅷ-1、Ⅷ-2和/或Ⅷ-3所示的含有環烷基的化合物，其中Ⅷ-1、Ⅷ-2、Ⅷ-3。
其中，、、、各自獨立地表示1,4-亞環己基、1,4-亞環己基中一個或兩個不相連的CH2被O取代所形成的基團、1,4-亞苯基和/或氟代的1,4-亞苯基中的一種或多種；
Z1 、Z2 、Z3 各自獨立地表示單鍵、-CF2 O-或-CH2 O-；
m、k、g各自獨立地表示1、2或3；
i表示0、1或2；
R11 表示F、碳原子數為1～9的烷基、氟取代的碳原子數為1～9的烷基、碳原子數為1～9的烷氧基、氟取代的碳原子數為1～9的烷氧基、碳原子數為2～9的鏈烯基、氟取代的碳原子數為2～9的鏈烯基、碳原子數為3～8的鏈烯氧基或氟取代的碳原子數為3～8的鏈烯氧基；
R12 表示碳原子數為1～5的烷基、氟取代的碳原子數為1～5的烷基、碳原子數為1～5的烷氧基、氟取代的碳原子數為1～5的烷氧基、碳原子數為2～5的鏈烯基、氟取代的碳原子數為2～5的鏈烯基、碳原子數為3～5的鏈烯氧基或氟取代的碳原子數為3～5的鏈烯氧基。
式Ⅷ所示化合物不含有柔軟的端基烷基鏈，因而具有較強的剛性，液晶分子之間相對作用的改變，表現出較大的K值、較高的CP。
Ⅷ-1所示化合物較佳：、、、、、、。
Ⅷ-2所示化合物較佳：、、、、、、、。
Ⅷ-3所示化合物較佳：、、。
液晶組合物各成分的不同比例，會表現出略有差異的性能，比如介電異方性Δε、雙折射性Δn、液晶的向列相轉化為液體的轉變溫度點CP、低溫下穩定性都會有所差異，可以應用於不同類型的顯示元件，但是相同的特點是其旋轉黏度γ1 較低。應用於液晶顯示元件，可以實現快速回應。
本發明所提供的液晶化合物中還可以加入各種功能的摻雜劑，摻雜劑含量較佳0.01～1%之間，這些摻雜劑主要是抗氧化劑、紫外線吸收劑、手性劑。
抗氧化劑、紫外線吸收劑較佳為：、、、、、。
S表示1～10的整數。
手性劑較佳為（左旋或右旋）：、、、、。
本發明還涉及包含上述任意一種液晶組合物的液晶顯示元件或液晶顯示器；顯示元件或顯示器為有源矩陣顯示元件或顯示器或無源矩陣顯示元件或顯示器。
液晶顯示元件或液晶顯示器較佳有源矩陣定址液晶顯示元件或液晶顯示器。
有源矩陣顯示元件或顯示器具體為TN-TFT或IPS-TFT液晶顯示元件或顯示器。
本發明所提供的液晶組合物具有較低的黏度，可以實現快速回應，同時具有適中的介電異方性Δε、適中的雙折射性Δn、高的對熱和光的穩定性。
包含本發明所提供的液晶組合物的液晶材料，不但具有良好的化學和熱穩定性以及對電場和電磁輻射的穩定性。而且，作為薄膜電晶體技術（TFT-LCD）用液晶材料，還具有較寬的向列相溫度範圍、合適的雙折射率各向異性、非常高的電阻率、良好的抗紫外線性能、高電荷保持率以及低蒸汽壓等性能。
下面結合具體實施例對本發明作進一步闡述，但本發明並不限於以下實施例。所述方法如無特別說明均為常規方法。所述原料如無特別說明均能從公開商業途徑而得。所述百分比如無特別說明，均為品質百分比。
下述實施例中，
CP表示清晰點，直接使用WRX-1S顯微熱分析儀測定，設定升溫速率為3℃/min。
Δn表示雙折射性（589nm，20℃），
Δε表示介電異方性 (25℃，1KHz，HP4284A，5.2微米TN左旋盒) ，
γ1 表示20℃時旋轉黏度（mpas），VHR (%)代表電荷保持率（5V, 60Hz, 20℃），ρ（×1013 Ω·cm）代表電阻率（20℃）
電壓保持率VHR（%)的測試儀與電阻率ρ(×1013 Ω·cm)均為TOYO06254和TOYO6517型液晶物性評價系統（測試溫度20℃，時間16ms ，測試盒為7.0微米）。
實施例1
Δε[1KHz, 20℃]：9.5
Δn[589nm, 20℃]：0.115
Cp：118℃
γ1：160mPa.s。
實施例2
Δε[1KHz, 20℃]：4.4
Δn[589nm, 20℃]：0.095
Cp：130℃
γ1：177mPa.s。
實施例3
Δε[1KHz, 20℃]：10.1
Δn[589nm, 20℃]：0.110
Cp：79℃
γ1 ：76mPa.s。
實施例4
Δε[1KHz, 20℃]：9
Δn[589nm, 20℃]：0.105
Cp：100℃
γ1 ：99mPa.s。
實施例5
Δε[1KHz, 20℃]：9.0
Δn[589nm, 20℃]：0.155
Cp：104℃
γ1：109mPa.s。
實施例6
Δε[1KHz, 20℃]：5.6
Δn[589nm, 20℃]：0.107
Cp：112℃
γ1：121mPa.s。
實施例7
Δε[1KHz, 20℃]：5.3
Δn[589nm, 20℃]：0.114
Cp：150℃
γ1：300mPa.s。
由以上實施例可以看出：本發明的液晶組合物具有較低的旋轉黏度γ1 ，用於液晶顯示，可以實現快速回應。尤其適合於TN、IPS模式用液晶材料。
無
無
無

Claims (10)

  1. 一種液晶組合物，其包含一種或多種式Ⅰ所示化合物、一種或多種式Ⅱ所示化合物以及式Ⅱ-A所示化合物：Ⅰ、Ⅱ、Ⅱ-A； 其中，Y1 表示氟(F)或氫(H)，Y2 表示氟(F)、三氟甲氧基(OCF3 )、三氟甲基(CF3 )或二氟甲氧基(OCF2 H)，並且Y1 、Y2 不能同時表示氟(F)； R1 、R2 、R3 各自獨立地表示碳原子數為1～9的烷基、氟取代的碳原子數為1～9的烷基、碳原子數為1～9的烷氧基、氟取代的碳原子數為1～9的烷氧基、碳原子數為2～9的鏈烯基、氟取代的碳原子數為2～9的鏈烯基、碳原子數為3～8的鏈烯氧基或氟取代的碳原子數為3～8的鏈烯氧基；、各自獨立地表示1,4-亞苯基、1,4-亞環己基或1,4-亞環己烯基。
  2. 如申請專利範圍第1項所述之液晶組合物，其中，一種或多種該式Ⅰ所示化合物為式Ⅰ1至式Ⅰ7所示化合物中的一種或多種：Ⅰ1、Ⅰ2、Ⅰ3、Ⅰ4、Ⅰ5、Ⅰ6、Ⅰ7； 其中，R1 各自獨立地表示碳原子數為1～9的烷基、氟取代的碳原子數為1～9的烷基、碳原子數為1～9的烷氧基、氟取代的碳原子數為1～9的烷氧基、碳原子數為2～9的鏈烯基、氟取代的碳原子數為2～9的鏈烯基、碳原子數為3～8的鏈烯氧基或氟取代的碳原子數為3～8的鏈烯氧基； 一種或多種式Ⅱ所示化合物包含式Ⅱ1至式Ⅱ10所示化合物中的一種或多種化合物：Ⅱ1、Ⅱ2、Ⅱ3、Ⅱ4、Ⅱ5、Ⅱ6、Ⅱ7、Ⅱ8、Ⅱ9、Ⅱ10。
  3. 如申請專利範圍第1項或第2項所述之液晶組合物，其進一步包含一種或多種式Ⅲ所示化合物：Ⅲ； 其中，R4 表示碳原子數為1～9的烷基、氟取代的碳原子數為1～9的烷基、碳原子數為1～9的烷氧基、氟取代的碳原子數為1～9的烷氧基、碳原子數為2～9的鏈烯基、氟取代的碳原子數為2～9的鏈烯基、碳原子數為3～8的鏈烯氧基或氟取代的碳原子數為3～8的鏈烯氧基；表示1,4-亞苯基、1,4-亞環己基或1,4-亞環己烯基。
  4. 如申請專利範圍第1項或第2項所述之液晶組合物，其進一步包含一種或多種式Ⅳ所示化合物：Ⅳ； 其中，R5 表示碳原子數為1～9的烷基、氟取代的碳原子數為1～9的烷基、碳原子數為1～9的烷氧基、氟取代的碳原子數為1～9的烷氧基、碳原子數為2～9的鏈烯基、氟取代的碳原子數為2～9的鏈烯基、碳原子數為3～8的鏈烯氧基或氟取代的碳原子數為3～8的鏈烯氧基； n表示0，1； （F）表示氫(H)或氟(F)。
  5. 如申請專利範圍第1項或第2項所述之液晶組合物，其進一步包含一種或多種式Ⅴ所示化合物：Ⅴ； 其中，R6 、R7 各自獨立地表示碳原子數為1～9的烷基、氟取代的碳原子數為1～9的烷基、碳原子數為1～9的烷氧基、氟取代的碳原子數為1～9的烷氧基、碳原子數為2～9的鏈烯基、氟取代的碳原子數為2～9的鏈烯基、碳原子數為3～8的鏈烯氧基或氟取代的碳原子數為3～8的鏈烯氧基； Y3 、Y4 表示氫(H)或氟(F)，但不能同時為氟(F)；表示1,4-亞苯基、1,4-亞環己基或1,4-亞環己烯基。
  6. 如申請專利範圍第1項或第2項所述之液晶組合物，其進一步包含一種或多種式Ⅵ所示化合物：Ⅵ； 其中，R8 表示碳原子數為1～9的烷基、氟取代的碳原子數為1～9的烷基、碳原子數為1～9的烷氧基、氟取代的碳原子數為1～9的烷氧基、碳原子數為2～9的鏈烯基、氟取代的碳原子數為2～9的鏈烯基、碳原子數為3～8的鏈烯氧基或氟取代的碳原子數為3～8的鏈烯氧基；表示1,4-亞苯基、1,4-亞環己基或1,4-亞環己烯基；表示1,4-亞苯基、氟代1,4-亞苯基、1,4-亞環己基或1,4-亞環己烯基； R9 表示氟(F)、碳原子數為1～9的烷基、氟取代的碳原子數為1～9的烷基、碳原子數為1～9的烷氧基、氟取代的碳原子數為1～9的烷氧基、碳原子數為2～9的鏈烯基、氟取代的碳原子數為2～9的鏈烯基、碳原子數為3～8的鏈烯氧基或氟取代的碳原子數為3～8的鏈烯氧基。
  7. 如申請專利範圍第1項或第2項所述之液晶組合物，其進一步包含有一種或多種式Ⅶ所示化合物：Ⅶ； 其中，R10 表示碳原子數為1～9的烷基、氟取代的碳原子數為1～9的烷基、碳原子數為1～9的烷氧基、氟取代的碳原子數為1～9的烷氧基、碳原子數為2～9的鏈烯基、氟取代的碳原子數為2～9的鏈烯基、碳原子數為3～8的鏈烯氧基或氟取代的碳原子數為3～8的鏈烯氧基；表示1,4-亞苯基、氟代1,4-亞苯基、1,4-亞環己基、1,4-亞環己烯基和/或1,4-亞環己基中一個或不相連的兩個CH2 被氧取代所形成的基團中的一種或多種； p表示2或3。
  8. 如申請專利範圍第1項至第2項中任一項所述之液晶組合物，其進一步包含一種或多種式Ⅷ-1所示化合物、一種或多種式Ⅷ-2所示化合物及/或一種或多種式Ⅷ-3所示化合物：Ⅷ-1、Ⅷ-2、Ⅷ-3； 其中，、、、各自獨立地表示1,4-亞環己基、1,4-亞環己基中一個或兩個不相連的CH2 被氧(O)取代所形成的基團、1,4-亞苯基和/或氟代的1,4-亞苯基中的一種或多種； Z1 、Z2 、Z3 各自獨立地表示單鍵、二氟甲氧基橋鍵(-CF2 O-)或甲氧基橋鍵(-CH2 O-)； m、k、g各自獨立地表示1、2或3； i表示0、1或2； R11 表示氟(F)、碳原子數為1～9的烷基、氟取代的碳原子數為1～9的烷基、碳原子數為1～9的烷氧基、氟取代的碳原子數為1～9的烷氧基、碳原子數為2～9的鏈烯基、氟取代的碳原子數為2～9的鏈烯基、碳原子數為3～8的鏈烯氧基或氟取代的碳原子數為3～8的鏈烯氧基； R12 表示碳原子數為1～5的烷基、氟取代的碳原子數為1～5的烷基、碳原子數為1～5的烷氧基、氟取代的碳原子數為1～5的烷氧基、碳原子數為2～5的鏈烯基、氟取代的碳原子數為2～5的鏈烯基、碳原子數為3～5的鏈烯氧基或氟取代的碳原子數為3～5的鏈烯氧基。
  9. 一種液晶顯示元件，其包含如申請專利範圍第1項至第8項中任一項所述之液晶組合物，該液晶顯示元件為有源矩陣顯示元件或無源矩陣顯示元件。
  10. 如申請專利範圍第9項所述之液晶顯示元件，其中，該有源矩陣顯示元件為TN-TFT或IPS-TFT液晶顯示元件。
TW105103383A 2015-07-13 2016-02-02 液晶組合物及液晶顯示元件 TW201702361A (zh)