TW201435014A - 聚伸烷基碳酸酯二醇漆料組合物 - Google Patents

聚伸烷基碳酸酯二醇漆料組合物 Download PDF

Info

Publication number
TW201435014A
TW201435014A TW103106437A TW103106437A TW201435014A TW 201435014 A TW201435014 A TW 201435014A TW 103106437 A TW103106437 A TW 103106437A TW 103106437 A TW103106437 A TW 103106437A TW 201435014 A TW201435014 A TW 201435014A
Authority
TW
Taiwan
Prior art keywords
polyalkylene carbonate
paint composition
weight
composition
group
Prior art date
Application number
TW103106437A
Other languages
English (en)
Inventor
Ji-Yeon Choi
Seung-Gweon Hong
Yong-Gu Lee
Gyu-Hoe Kim
Original Assignee
Sk Innovation Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sk Innovation Co Ltd filed Critical Sk Innovation Co Ltd
Publication of TW201435014A publication Critical patent/TW201435014A/zh

Abstract

本發明係提供一種聚伸烷基碳酸酯漆料組合物，其係一種預塗覆金屬(PCM)之漆料組合物，其可應用於有高硬度需求的多種用途如建築用途、家庭用途、塗覆於容器、或類似者。本發明之組合物可作為具有低煙霧密度，及相對於現有積層鋼板及高光澤膜而言，受火燃燒時有毒氣體與煙霧的排放顯著減少的PCM漆料。此外，本發明可提供一高硬度漆料組合物，其因為優良的對金屬材料黏著性質以及優良的耐久性，可有益地應用於用在家電用品的PCM印刷鋼板。

Description

聚伸烷基碳酸酯二醇漆料組合物
本申請案聲明2013年2月26日於韓國專利局申請之韓國專利申請號10-2013-0020500、及2014年2月18日於韓國專利局申請之韓國專利申請號10-2014-0018616之優先權，彼等之揭露係全文併於此處做為參考。
本發明係關於一種聚伸烷基碳酸酯二醇漆料組合物。
根據相關技術，家用鋼板係藉由將預塗覆金屬(pre-coated metal；PCM)後處理，或先處理一鋼板再粉漆該處理過的鋼板而製成。然而，由於近來對於家電用品品質增進的趨勢，在現有的單色PCM及粉漆面板上，必須實現不同的色彩及多種光澤。因此，已有應用以墨水印刷的PCM積層方法。
相對於漆料上漆系統，藉由PCM積層方法附接在鋼板上的積層，具有優良的光澤，且不需要分離的墨水印刷處理。然而，由於該積層僅藉由一黏著劑而附接，相較於漆料，還有許多例如與材料黏著不良、防蝕性、防水性、及耐性的劣化等問題。
此外，該積層係一150至160微米的膜，其厚度較漆料的塗覆膜更厚，且可能過度增加品質增進的成本。
再者，由於墨水已印刷於積層膜上，於設計及電器用品公司處可能難以獨立地控制其設計。又，於火災時，由於有毒氣體毒害或大量的煙霧所造成的傷害可能增加。
於以上問題中，為了滿足消費者之品質增進，已嘗試使用4-塗覆3-焙烤系統，其中提供可於上漆線上進行墨水印刷的上漆設備，且透明漆料係由濕疊濕(wet-on-wet)方法上漆。在此墨水印刷系統中，可進行薄膜上漆，其相較於積層膜可改進塗覆膜的物理性質，且藉由塗覆下漆料-基底漆料-墨水-透明漆料之系統，可獲得經濟效益。然而，在以上方法中使用現有樹脂的情況下，可能難以達成低煙霧密度、所欲的漆料黏著性質、耐性、及相似性質。
於此同時，脂肪族聚碳酸酯樹脂係一環保的材料，因其優良的可處理性及生物可分解性，應用於多種領域。然而，由於脂肪族聚碳酸酯樹脂具低彈性且容易破裂，脂肪族聚碳酸酯樹脂的應用受到限制。因此，需要將脂肪族聚碳酸酯樹脂與多種樹脂摻合的技術，以改進熱穩定性或機械性質。
舉例而言，US 4,946,884(專利文獻1)揭露一種樹脂組合物，其包含聚伸丙基碳酸酯，與聚甲基丙烯酸甲酯(PMMA)或一黏結劑熔融混合，用於陶瓷或金屬粉體的成型操作；但僅將聚伸丙基碳酸酯與一異相的樹脂摻合，對於增進物理性質仍有限制。
互穿聚合物網(interpenetrating polymer network；IPN)係一種多組分系統化合物，其中至少一組分具有交聯結構，且至少一組分係於另一組分存在下聚合或交聯，使得聚合物鏈彼 此互穿。在IPN中，由於交聯結構使得聚合物鏈程度高，可抑制聚合物摻合物中常產生的相分離，且IPN具有兩組分連續地形成的雙相連續結構，而可增進多種物理性質。
因此，需要一種應用IPN結構以將聚伸丙基碳酸酯應用於一PCM積層膜，並克服PCM積層膜的限制，以更加提升應用範圍的技術。
[相關技術文獻] [專利文獻]
(專利文獻1)US 4,946,884(1990年8月7日)
本發明之一具體實施態樣係關於提供一環保的聚伸烷基碳酸酯漆料組合物，其於燃燒時幾乎不產生煙霧或有毒氣體，且藉由高密度交聯而顯著增進機械性質及耐性。
此外，本發明之一具體實施態樣係關於提供一聚伸烷基碳酸酯漆料組合物，其可具有優良的金屬黏著力，展現與相關技術之PCM漆料相較相等或更優良的塗覆膜表現，而又具有薄的厚度，且具有優良的經濟效率。
一般而言，一聚伸烷基碳酸酯漆料組合物係含有：(a)一聚伸烷基碳酸酯二醇樹脂，其OH值為3至10毫克(以KOH計)/公克且重量平均分子量(MW)為1,000至30,000公克/莫耳；(b)一多元醇化合物，其OH值為51至61毫克(以KOH計)/公克且重量平均分子量(MW)為200至300,000公克/莫耳； (c)一固化劑；(d)一固化催化劑；以及(e)一有機溶劑。
該(a)聚伸烷基碳酸酯二醇樹脂與該(b)多元醇化合物之重量混合比可為65：35至95：5。
該固化劑可為選自以下群組之一或多者：基於聚胺的化合物以及基於聚異氰酸酯的化合物。
該組合物可含有，以該組合物之總重計，0.1至30重量%的該固化劑以及0.01至0.5重量%的該固化催化劑。
該固化催化劑可選自以下群組之一或多者：十二烷基苯磺酸、二月桂酸丁基錫、對甲苯磺酸、二壬基萘磺酸、以及二壬基萘二磺酸。
該聚伸烷基碳酸酯漆料組合物可更包含選自以下群組之一或多者：一無機填料，其係由碳酸鈣、碳酸鎂、硫酸鈣、硫酸鎂、氧化鋅、氧化鎂、氧化鋁、氧化鈣、氧化鈦、氫氧化鈣、氫氧化鎂、氫氧化鋁、微晶質矽石、發煙矽石、天然沸石、合成沸石、膨潤土、及黏土所形成；一丙烯酸分散劑；一基於聚矽氧的消泡劑；以及一顏料。
該聚伸烷基碳酸酯漆料組合物可更包含選自以下群組之任一種或至少二種添加劑：染料、抗氧化劑、防曬劑、抗靜電劑、防結塊劑、增滑劑、混合劑、穩定劑、增黏劑、螢光增白劑、熱穩定劑、光穩定劑、紫外線吸收劑、以及潤滑劑。
以下，將詳細描述一聚伸烷基碳酸酯漆料組合物。下列將描述的本發明之具體實施態樣係提供作為例示，以使本發明的概念可有效傳達給本發明相關領域具通常知識者。在此，若無其他定義，本說明書中所使用的技術用語及科學用語具有本發明相關領域具通常知識者所理解的一般意義，而以下敘述中將省略使本發明意義模糊的已知功能以及配置。
發明人進行研究以發展一種環保的漆料組合物，其可具有低煙霧密度，預防產生有毒氣體，實現優良的機械性質、可處理性、耐性、色彩實現性質、光澤性質、及耐溶劑性。其結果，發明人發現在以一混合比例將一聚伸烷基碳酸酯二醇樹脂與一多元醇化合物混合，並包含一固化劑、一固化催化劑、及一溶劑，同時調整該等化合物的OH值與重量平均分子量的情況下，可以增強其與金屬的黏著力，且塗覆膜硬度、衝擊強度、及剝離性質與前述的效果可顯著的改進，而完成本發明。
根據本發明一具體實施態樣，一聚伸烷基碳酸酯漆料組合物可包含：(a)一聚伸烷基碳酸酯二醇樹脂，其OH值為3至10毫克(以KOH計)/公克且重量平均分子量(MW)為1,000至30,000公克/莫耳；(b)一多元醇化合物，其OH值為51至61毫克(以KOH計)/公克且重量平均分子量(MW)為200至30,000公克/莫耳；(c)一固化劑；(d)一固化催化劑；以及(e)一有機溶劑。
於本發明中，該聚伸烷基碳酸酯二醇樹脂係作為主要樹脂，該多元醇化合物係作為輔助樹脂，而可增加相容性，且可引致快速且有效率的固化反應。尤其是，該聚伸烷基碳酸酯漆 料組合物由於不同的固化反應速率而具有互穿聚合物網(IPN)結構，故可改進交聯密度，因此可改進物理性質。
於本發明中，該聚伸烷基碳酸酯可使用羅列於由SK新技術公司所提出的先前文獻(韓國專利公開號2008-0015454；2009-0090154；2010-067593；及2010-0013255)中的聚伸烷基碳酸酯。
該聚伸烷基碳酸酯可藉由二氧化碳與至少一種選自以下群組之環氧化合物共聚合反應而製備，該群組包含：(C2-C20)氧化烯(alkyleneoxide)，其係經鹵素、(C1-C20)烷氧基、(C6-C20)芳氧基、或(C6-C20)芳(C1-C20)烷(芳烷)氧基而取代或未經取代；(C4-C20)環氧化烯(cycloalkyleneoxide)，其係經鹵素、(C1-C20)烷氧基、(C6-C20)芳氧基、或是(C6-C20)芳(C1-C20)烷(芳烷)氧基而取代或未經取代；以及(C8-C20)氧化苯乙烯(styreneoxide)，其係經鹵素、(C1-C20)烷氧基、(C6-C20)芳氧基、(C6-C20)芳(C1-C20)烷(芳烷)氧基、或是(C1-C20)烷基而取代或未經取代。
較佳地，該聚伸烷基碳酸酯係聚伸丙基碳酸酯。於聚伸丙基碳酸酯中，其係由二氧化碳與環氧丙烷反應而合成，來自二氧化碳的碳酸根與環氧丙烷彼此交聯；且以核磁共振(NMR)分析結果而言，環氧丙烷鍵結成的醚鍵結可佔3莫耳%或更少。
於本發明中，該聚伸烷基碳酸酯二醇樹脂之重量平均分子量可為1,000至30,000公克/莫耳。當聚伸烷基碳酸酯二醇樹脂之重量平均分子量低於1,000公克/莫耳時，抗衝擊性、耐性、及機械強度將降低；而其重量平均分子量高於35,000公克/莫耳時，可分散性、光澤性質、及耐溶劑性將被劣化，且可能無法順 利進行固化反應。
該聚伸烷基碳酸酯二醇樹脂係本發明之主要樹脂，其具有例如優良的機械強度及可處理性等物理性質。然而，由於聚伸烷基碳酸酯二醇樹脂的OH值過低而無法使IPN反應充分地進行以增加交聯密度，故混入多元醇化合物作為輔助樹脂，使得讓聚伸烷基碳酸酯漆料組合物具有IPN結構的IPN反應可以有效進行。
該多元醇化合物之重量平均分子量可較佳為200至30,000公克/莫耳，更佳為15,000至25,000公克/莫耳。
作為該多元醇化合物，可使用包含選自以下群組之一或多種：聚酯多元醇、聚醚多元醇、及聚碳酸酯多元醇。
於本發明中，較佳的多元醇化合物係聚碳酸酯二醇樹脂。
該多元醇化合物之OH值可為51至61毫克(以KOH計)/公克，酸值可為0.5毫克(以KOH計)/公克或以下。在此情況下，聚伸烷基碳酸酯二醇樹脂與多元醇化合物之重量混合比可為65：35至95：5以改進固化度、光澤性質、機械性質、可處理性、經濟效率等。重量混合比較佳為70：30至95：5，更佳為80：20至95：5。可依據所選定的物理性質調整重量混合比。
於本發明中，聚伸烷基碳酸酯之玻璃轉換溫度較佳為30至40℃。若玻璃轉換溫度不在前述範圍之內，塗覆膜的可處理性或硬度可能劣化。
此外，於總體漆料組合物中，該聚伸烷基碳酸酯之含量可為25至65重量%。當聚伸烷基碳酸酯之含量少於20重量 %的情況下，由於難以於進行上漆處理的同時調整塗覆膜的厚度，上漆需以薄的方式進行，使得漆料的可上漆性劣化，且在含有顏料的情況下，顏料的黏著力可能下降。此外，在其含量高於65重量%的情況下，由於難以於進行上漆處理的同時調整黏度，平整度及消泡性質可能劣化，而可能產生爆裂或類似者。
於本發明中，固化劑可包括以下群組之一或多者：基於聚胺的化合物以及基於聚異氰酸酯的化合物。
較佳地，該基於聚胺的化合物係一基於三聚氰胺的化合物。基於三聚氰胺的化合物之實例可包括：六甲氧基甲基三聚氰胺、六乙氧基甲基三聚氰胺、六丙氧基甲基三聚氰胺、六丁氧基甲基三聚氰胺、六戊氧基甲基三聚氰胺、六己氧基甲基三聚氰胺、及類似者，唯不需侷限於此。
基於聚異氰酸酯的化合物之實例可包括：2,4-三氯乙烯二異氰酸酯(2,4-trilene diisocyanate)、2,6-三氯乙烯二異氰酸酯(2,6-trilene diisocyanate)、氫化三氯乙烯二異氰酸酯(hydrogenated trilene diisocyanate)、1,3-二甲苯二異氰酸酯、1,4-二甲苯二異氰酸酯、二苯甲烷-4,4-二異氰酸酯、1,3-雙異氰酸甲基環己烷(1,3-bisisocyanatemethyl cyclohexane)、四甲基二甲苯二異氰酸酯、1,5-萘二異氰酸酯、2,2,4-三甲基亞己基二異氰酸酯(2,2,4-trimethyl hexamethylene diisocyanate)、2,4,4-三甲基亞己基二異氰酸酯(2,4,4-trimethyl hexamethylene diisocyanate)、三苯基甲烷三異氰酸酯、及類似者，唯不需侷限於此。
於本發明中，固化劑可賦予包括塗覆膜硬度及耐性等機械性質，且根據所選定的固化劑，可調整固化劑之用量。較 佳地，以漆料組合物之總重計，該固化劑的含量可為0.1至30重量%。舉例而言，在使用丁基化三聚氰胺甲醛樹脂的情況，其用量可為2至20重量%；而在使用亞己基二異氰酸酯三聚物的情況，其用量可為0.5至5重量%。
在此情況下，較佳地，該基於聚胺的化合物以及基於聚異氰酸酯的化合物同時反應以形成樹脂的IPN結構，但亦可依序反應。
本發明所使用的溶劑可包括能夠溶解聚伸烷基碳酸酯的溶劑。只要溶劑並不會溶解用於濕疊濕系統中基底所包含墨水的樹脂，即不需特別限制該溶劑。舉例而言，可使用酮、醚、酯、醇、或類似者。特定而言，可使用丙二醇甲醚乙酸酯(propylene glycol monomethyl ether acetate；PMA)、甲乙酮(MEK)、或類似者。在此情況下，可適當調整溶劑的含量，但較佳將PMA與MEK以體積比0.5至1.5：1混合使用。更佳地，PMA與MEK係以體積比0.8至1.2：1混合使用，且以組合物之總重計，可使用0.5至70重量%的溶劑。
於本發明中，固化催化劑可與固化劑一起包含而使用。舉例而言，可使用二異氰酸酯及丁基化三聚氰胺甲醛樹脂作為固化劑。此情況下，可使用選自以下群組之任一種或至少二種固化催化劑：十二烷基苯磺酸、二月桂酸丁基錫(DBTDL)、對甲苯磺酸、二壬基萘磺酸、以及二壬基萘二磺酸。在此情況下，以組合物之總重計，可使用0.01至0.5重量%的固化催化劑。
根據本發明一例示性具體實施態樣的聚伸丙基碳酸酯漆料組合物可更包含選自以下群組之一或至少二種添加劑：顏 料；無機填料，其係由碳酸鈣、碳酸鎂、硫酸鈣、硫酸鎂、氧化鋅、氧化鎂、氧化鋁、氧化鈣、氧化鈦、氫氧化鈣、氫氧化鎂、氫氧化鋁、微晶質矽石、發煙矽石、天然沸石、合成沸石、膨潤土、及黏土所形成；丙烯酸分散劑；以及基於聚矽氧的消泡劑。
做為顏料，可使用任一種選自以下群組者：二氧化鈦、青藍、洋紅、黃色顏料、及其混合物。以組合物之總重計，該顏料的含量可為0.1至30重量%。
根據本發明，為使顏料穩定且增加分散性，可以使用無機填料例如黏土(如有機黏土等)、或發煙矽石、或類似者。以組合物之總重計，該無機填料的含量可為0.001至5重量%，較佳0.01至2重量%。在此情況下，該無機填料可於維持其他物理性質時，更賦予消光(matte)或類似的效果。此外，該組合物可更包含分散劑、流平劑、上色劑、防沉澱劑、防鬆弛劑。即類似者，且其含量可分別為0.01至5重量%。
於本發明中，為改進平整度及消泡性質，可更包含選自以下群組之任一或多者：丙烯酸化合物、基於乙烯基之化合物、及基於矽之化合物。舉例而言，已有由BYK公司所製造之143、356、410、2163、及2105等。特定而言，於根據本發明之組合物中，在其包含丙烯酸改質聚酯樹脂的情況下，可顯著改進其平整度、消泡性質、光澤性質、及膜可形成性。此外，根據本發明之組合物具有優良的溶劑能力以確保其平整度並增加漆料的光澤性質。舉例而言，PMA-MEK溶劑系統對於聚伸烷基碳酸酯樹脂具有優良的溶劑能力，故漆料的平整度優良，且可增加無機顏料顆粒的分散穩定性。在此情況下，為了增加顏料的穩定性，可 使用0.001至5重量%的黏土或發煙矽石，唯本發明並不需侷限於此。
較佳地，該聚伸烷基碳酸酯漆料組合物係於180至280℃下焙烤10秒至1分鐘。
此外，於本發明中，為了視需要改進物理性質，可更包含選自以下群組之任一種或至少二種添加劑：染料、抗氧化劑、防曬劑、抗靜電劑、防結塊劑、增滑劑、混合劑、穩定劑、增黏劑、螢光增白劑、熱穩定劑、光穩定劑、紫外線吸收劑、以及潤滑劑。
此外，本發明可提供一種成型體，其係包含前述聚伸烷基碳酸酯二醇漆料組合物。
以下將由所附實施例更完整地理解並領會本發明，且所附之實施例係用於描述本發明，而非限制本發明。
[實施例1]
將70重量份的重量平均分子量為25,000公克/莫耳、分子鏈兩端包括羥基、且玻璃轉換溫度為35℃之聚伸丙基碳酸酯二醇(PPC二醇)，與150重量份的由環己烷及甲乙酮(MEK)以重量比1：1混合而得之溶劑置入一金屬罐中並攪拌，而獲得一混合溶液。於攪拌該混合溶液同時，將100重量份的二氧化鈦緩慢置入該混合溶液中，之後將直徑2至3毫米的玻璃珠置入其中，並使用一壓碎機式分散設備將該混合物進行分散一小時。在此情況下，使用研磨計測量平均顆粒尺寸，並調整至5微米或以下。將20重量份的聚碳酸酯二醇(PCDL)樹脂、20重量份的三聚氰胺、以及10重量份的由環己烷及甲乙酮(MEK)以重量比1：1混 合而得之溶劑加入該分散系中並攪拌。此外，於其中加入0.1重量份的BYK-180以作為分散穩定劑，並攪拌。之後，於其中緩慢加入0.5重量份對甲苯磺酸、及0.5重量份十二烷基苯磺酸以作為固化催化劑，而製備聚伸丙基碳酸酯漆料組合物。
在上漆之前，該漆料組合物係以PMA稀釋至上漆黏度(25℃下，以4號Ford杯計80秒)。
所稀釋的PPC漆料組合物係作為頂層塗覆漆，使用一輥塗機上漆於一電鍍(GI)鋼板(0.4T)上，上漆厚度15微米，且該鋼板係經一環氧型底漆上漆(乾塗覆厚度5微米)；之後於224℃焙烤30秒，而製造用於測試物理性質的試樣。
測試該塗覆膜物理性質所獲得的結果係顯示於以下表1中。
[實施例2]
以實施例1之相同方法製備漆料組合物，唯調整聚伸烷基碳酸酯二醇樹脂、聚碳酸酯二醇、及三聚氰胺之用量，分別為65重量份、30重量份、及15重量份。
[實施例3]
以實施例1之相同方法製備漆料組合物，唯調整聚伸烷基碳酸酯二醇樹脂、聚碳酸酯二醇、及三聚氰胺之用量，分別為75重量份、25重量份、及15重量份。
[實施例4]
以實施例1之相同方法製備漆料組合物，唯調整聚伸烷基碳酸酯二醇樹脂、聚碳酸酯二醇、及三聚氰胺之用量，分別為70重量份、40重量份、及20重量份。
[實施例5]
以實施例1之相同方法製備漆料組合物，唯調整聚伸烷基碳酸酯二醇樹脂、聚碳酸酯二醇、及三聚氰胺之用量，分別為98重量份、2重量份、及20重量份。
[實施例6]
以實施例1之相同方法製備漆料組合物，唯將聚碳酸酯二醇改為使用聚醚二醇。
[實施例7]
以實施例3之相同方法製備漆料組合物，唯將聚碳酸酯二醇改為使用聚醚二醇。
[比較實施例1]
以實施例1之相同方法製備漆料組合物，唯改為使用重量平均分子量為40,000公克/莫耳之聚伸丙基碳酸酯二醇。
[比較實施例2]
以實施例1之相同方法製備漆料組合物，唯將三聚氰胺改為使用亞甲基二苯基異氰酸酯(MDI)，其用量相同。
[比較實施例3]
以實施例1之相同方法製備漆料組合物，唯將三聚氰胺改為使用2,4-二胺基-6-苯基-s-三，其用量相同。
如表1所示，可發現根據本發明之實施例，其光澤性質及可處理性優良，且由於優良的硬度、衝擊及剝離性質，可改進其耐性。相反地，可發現於使用分子量大的PPC樹脂的比較實施例1，其反應性低，因此硬度下降，其物理性質劣化。
因此，已確認根據本發明的聚伸丙基碳酸酯二醇漆料組合物具有優良的相容性、可處理性、光澤性質、抗溶劑性、塗覆膜硬度、衝擊及剝離性質、以及黏著性，故該聚伸丙基碳酸酯二醇漆料組合物可用於多種家庭用領域等，以及例如建築用途。
根據本發明的聚伸烷基碳酸酯漆料組合物具有優點在於，該組合物係環保的，且具有優良的相容性、可處理性及耐性。
此外，該聚伸烷基碳酸酯漆料組合物可具有優點在於其煙霧密度低、鮮少產生有毒氣體，且該組合物可藉由高密度交聯顯著提昇機械性質，而具有優良的塗覆膜硬度、衝擊強度、及剝離性質，且具有優良的對金屬黏著力。
更進一步，根據本發明的聚伸烷基碳酸酯漆料組合物可實現優良的色彩並具有高光澤度及優良的耐溶劑性等，因此該聚伸烷基碳酸酯漆料組合物可多方應用於PCM上漆領域，而用於家庭用途、建築用途、交通器具之外裝材料等類似者。

Claims (9)

  1. 一種聚伸烷基碳酸酯漆料組合物，其包含：(a)一聚伸烷基碳酸酯二醇樹脂，其OH值為3至10毫克(以KOH計)/公克且重量平均分子量(MW)為1,000至30,000公克/莫耳；(b)一多元醇化合物，其OH值為51至61毫克(以KOH計)/公克且重量平均分子量(MW)為200至30,000公克/莫耳；(c)一固化劑；(d)一固化催化劑；以及(e)一有機溶劑。
  2. 如請求項1之聚伸烷基碳酸酯漆料組合物，其中該(a)聚伸烷基碳酸酯二醇樹脂與該(b)多元醇化合物之重量混合比係65：35至95：5。
  3. 如請求項1之聚伸烷基碳酸酯漆料組合物，其中該多元醇化合物係聚碳酸酯二醇樹脂。
  4. 如請求項1之聚伸烷基碳酸酯漆料組合物，其中該固化劑係選自以下群組之一或多者：基於聚胺的化合物以及基於聚異氰酸酯的化合物。
  5. 如請求項1之聚伸烷基碳酸酯漆料組合物，其中該組合物係含有，以該組合物之總重計，0.1至30重量%的該固化劑以及0.01至0.5重量%的該固化催化劑。
  6. 如請求項1之聚伸烷基碳酸酯漆料組合物，其中該固化催化劑係選自以下群組之一或多者：十二烷基苯磺酸、二月桂酸 丁基錫、對甲苯磺酸、二壬基萘磺酸、以及二壬基萘二磺酸。
  7. 如請求項1之聚伸烷基碳酸酯漆料組合物，更包含選自以下群組之一或多者：一無機填料，其係由碳酸鈣、碳酸鎂、硫酸鈣、硫酸鎂、氧化鋅、氧化鎂、氧化鋁、氧化鈣、氧化鈦、氫氧化鈣、氫氧化鎂、氫氧化鋁、微晶質矽石、發煙矽石、天然沸石、合成沸石、膨潤土、及黏土所形成；一丙烯酸分散劑；一基於聚矽氧的消泡劑；以及一顏料。
  8. 如請求項1之聚伸烷基碳酸酯漆料組合物，更包含選自以下群組之任一種或至少二種添加劑：染料、抗氧化劑、防曬劑、抗靜電劑、防結塊劑、增滑劑、混合劑、穩定劑、增黏劑、螢光增白劑、熱穩定劑、光穩定劑、紫外線吸收劑、以及潤滑劑。
  9. 一種成型體，其係由如請求項1至8之任一項之聚伸烷基碳酸酯漆料組合物所製成。
TW103106437A 2013-02-26 2014-02-26 聚伸烷基碳酸酯二醇漆料組合物 TW201435014A (zh)