TH13229C3 - Pigment products that are well distributed in cement materials and manufacturing processes are - Google Patents

Abstract

Revised 21/03/2017 This invention aims to develop a highly dispersed pigment product as dry powder. There is a mixture of calcium carbonate substances. And precipitate silica with wax as a feature additive This invention uses a dry process. That use a grinder or blender or shear mixer And add calcium carbonate powder To make colored powder Can mix into With building materials Which has good cement composition Without liquid It is a polymer substance or a dispersing agent as an intermediate and faster than general pigments. In helping distribution The pigment can be mixed with cement, building materials such as portland cement. White cement, mortar, ready-made mortar Including adhesive mortar Can be homogeneous with other ingredients without the formation of dots Used in plastering work or working on the wall surface of the building. This highly dispersed inorganic pigment has optimum physical properties of the pigment powder surface. Can be mixed with cement binder Portland including Portland cement White cement Mortar ready-made Including the adhesive mortar, which in this invention uses wax to help the pigments spread well and not clump when stored for use, extending the storage time for further use. ---------------------------- This invention is the development of a highly dispersed pigment product. In the form of dry powder by the color powder of this invention It is an inorganic pigment. Which can be mixed with building materials That has better cement composition faster than general pigments, such as Portland cement White cement Mortar ready-made Including adhesive mortar By mixing homogeneous with other ingredients of building materials. Not included as a point to be seen when there is Applying by means of plaster or paint On the wall surface of the building This highly dispersed inorganic pigment has optimum physical properties of the pigment powder surface. Can be mixed with cement binder Port lad without liquid In addition, no polymer or dispersing agent is needed to aid dispersion.

Claims (9)

Disclaimer (all) which will not appear on the advertisement page: EDIT 21/03/2017 1. Pigment products dispersed in cement materials. Its characteristic is an inorganic pigment with a co-compound of calcium carbonate. And precipitate silica with wax as an additive. Properties 2. Pigment products dispersed in cement material in claim 1, where the pigment mixture is inorganic by The metal oxides are oxides of iron, titanium, iron, chromium, cobalt, manganese and magnesium. The average particle size is between 1-10 microns in the amount of 20-80 parts by weight. 3. Pigments dispersed in cement materials. In any of the 1 or 2 claims Where the ingredients Of the pigment powder is inorganic The metal oxides are titanium, chromium, cobalt, manganese and magnesium. The optimum particle size is between 1-10 microns. 4. Pigment products dispersed in cement materials. Claim 1, where the calcium carbonate mixture contains more than 80% of the calcium carbonate and the particle size is between 5-20 microns in an amount of 30-90 parts by weight. 5. Pigments dispersed in Cement material Claim 1, where the presipitet silica mixture has an average particle size of between 5-10 microns in a volume of 20-60 parts by weight 6. Pigment products dispersed in cement. In claim 1 or 5, where the precipitate silica mixture has an aggregate density of less than 0.1 g / cm3, 7. Pigments dispersed in cement materials. In Claim 1, where the wax mixture is a derivative of ethylene wax, the amount is 1-10 parts by weight. 8. The process for producing pigment products dispersed in cement materials in Claim 1. - 7 any one where the procedure consists of: a. Mixing the color powder with calcium carbonate; b. Mixing the mixture with the silica powder. With a high shear mixer c. Add ethylene wax to the mixture in item B and continue to mix. 9. The process for producing pigment products dispersed in cement material in claim 1, where Mixer High shear with spin cycle between 800-3000 rpm, the optimum speed is between 800-1500 rpm 1 0. The process of producing pigment products dispersed in cement material in claim 1, where the machine mix High shear, mixing time is 3 - 60 minutes, optimal time is between 5 - 45 minutes ---------------------------- 1. Pigment products dispersed in cement materials. Its characteristic is the inorganic pigment powder with a co-compound of calcium carbonate. And precipitate silica with wax as a property additive 2. Pigment products dispersed in cement materials. In Claim 1, where the pigment mixture is inorganic, the metal oxide elements are titanium, iron, chromium, cobalt, manganese and magnesium. And the average particle size is between 1-10 microns in volume 20-80 parts by weight. 3. Pigments dispersed in cement materials. In any one of the 1 or 2 claims Where the ingredients Of the pigment powder is inorganic By Nantes, the metal oxides are titanium, chromium, cobalt, manganese and tanganese. And the optimum particle size is between 2-6 microns 4. Pigment products dispersed in cement materials. In claim 1, the calcium carbonate mixture contains more than 80% of the calcium carbonate and the particle size is between 5-20 microns at an amount of 30-90 parts by weight. 5. Pigment products dispersed in cement materials. In claim 1, the mixture of precipitated silica has an average particle size of 5-10 microns in a volume of 20-60 parts by weight. 6. Pigment products dispersed in cement materials. In Claim 1 or 5, where the Precipitetchilica mixture has a total density of less than 0.1 g / cm3. 7. Pigments dispersed in cement materials. In Claim 1, where the wax mixture is a derivative of ethylene wax, the amount is 1-10 parts by weight. 8. Process for producing pigments that dispersed in cement materials. In any of the claims 1-7 where the procedure consists of: A. Mixing the color powder with calcium carbonate b. Mix the ingredients in the clause with the Shilica powder. With a high shear mixer c. Add ethylene wax to the mixture in item B and continue mixing. 9. Process for producing colored powder products distributed in cement material in claim 1, where the mixer High shear with spin cycle between 800-3000 rpm, the optimum speed is between 80-1500 rpm 1 0. The process of producing pigment products dispersed in cement material in claim 1, where the machine mix High shear, mixing time between 3-60 minutes, reasonable time between 5-45 minutes.