SU916457A1 - Aventurine glass composition - Google Patents

Aventurine glass composition Download PDF

Info

Publication number
SU916457A1
SU916457A1 SU802904815A SU2904815A SU916457A1 SU 916457 A1 SU916457 A1 SU 916457A1 SU 802904815 A SU802904815 A SU 802904815A SU 2904815 A SU2904815 A SU 2904815A SU 916457 A1 SU916457 A1 SU 916457A1
Authority
SU
USSR - Soviet Union
Prior art keywords
glass
mdo
aventurine
glass composition
cao
Prior art date
Application number
SU802904815A
Other languages
Russian (ru)
Inventor
Viktor A Karyakin
Yurij D Kruchinin
Aleksandr A Sazonov
Olga A Kochetova
Original Assignee
Kirov Sp Pk Naladochnoj Organi
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kirov Sp Pk Naladochnoj Organi filed Critical Kirov Sp Pk Naladochnoj Organi
Priority to SU802904815A priority Critical patent/SU916457A1/en
Application granted granted Critical
Publication of SU916457A1 publication Critical patent/SU916457A1/en

Description

22

Изобретение относится к составам авантюриновых стекол, используемых The invention relates to compositions of aventurine glasses used ΤίΟ2 РеОΤίΟ 2 ReO 0,1-0,4 0,01-2,0 0.1-0.4 0.01-2.0 в качестве декоративного материала as a decorative material Иа20Eeyore 2 0 2,51-4,49 2.51-4.49 при отделке зданий и сооружений. when decorating buildings and structures. 5 5 0,1-1,7 0.1-1.7 Известно авантюриновое суекпо [1] The famous aventurine suekpo [1] , Сг2°Э, Cr 2 ° Oe .1,01-3,51 .1.01-3.51 следующего состава, вес.%: the following composition, wt.%: 2,02-7,2 2.02-7.2 5102 50,88-57,98510 2 50.88-57.98 Недостатком Disadvantage указанных стекол явля- these glasses are А120э 1,56-1,72A1 2 0 e 1.56-1.72 ется довольно ι pretty ι низкая термостойкость. low heat resistance. Ре-0, 0*57-0,64 Re-0, 0 * 57-0.64 Цель изобретения - увеличение The purpose of the invention is to increase Сг20- 0,79-0,89Cg 2 0- 0.79-0.89 термостойкости heat resistance стекла. glass. СаО · 30,34-35,45 CaO30.34-35.45 ю Yu МдО 6,63~7,55 MDO 6.63 ~ 7.55 Поставленная цель достигается тем The goal is achieved by МпО 2,07-2,82 MPO 2.07-2.82 что известное what is famous авантюриновое стекло, aventurine glass, ΤΐΟ2 0,05-0,06ΤΐΟ 2 0.05-0.06 включающее 5 ΐ 0 including 5 ΐ 0 2.* А1 2θ3* Г2’2. * A1 2θ3 * G 2 ' Наиболее близким к предлагаемому Closest to the proposed СаО, МдО, Иа-О CaO, MdO, IA-O , содержит указанные contains specified по технической сущности и достигае- on the technical nature and achievement компоненты в следующем количестве, components in the following quantity мому результату является авантюрино- my result is adventurous мас.%: wt.%: вое стекло [2^] следующего состава, voe glass [2 ^] of the following composition, А120^A1 2 0 ^ 3,70-4,95 3.70-4.95 вес.%: the weight.%: Ре203 Re 2 0 3 0,45-0,79 0.45-0.79 510а 52,0-57,0510 a 52.0-57.0 20 Сг20^20 Cr 2 0 ^ 2,45-6,25 2.45-6.25 АкО, 7,0-8,75 AkO, 7.0-8.75 СаО CaO 23,50-30,20 23.50-30.20 СаО 21,0-24,5 CaO 21.0-24.5 МдО MDO 5,85-10,00 5.85-10.00 МдО 2,51-4,51 MDO 2.51-4.51 Иаг0Ia g 0 0,20-10,50 0.20-10.50 МпО 0,1-0,5 MPO 0.1-0.5 5ίθχ 5ίθχ Остальное: Rest:

916457 4916457 4

Стекло для улучшения декоративного эффекта дополнительно содержит Р 1»5*8,5 мас.$.Glass to improve the decorative effect additionally contains P 1 "5 * 8.5 wt. $.

Отвешенные компоненты шихты тщательно перемешивают. Шихту увлажняют 5 при перемешивании до 3*5%. Варку стекла осуществляют при 1400-1450°С, после полного осветления стекломассы ее выдерживают при 1300-1350еС в течение 0,5 ч. юSuspended components of the mixture are thoroughly mixed. The mixture is moistened 5 with stirring to 3 * 5%. Glass is melted at 1400-1450 ° C, after complete clarification of the glass, it is maintained at 1300-1350 e C for 0.5 hours

Формование изделий осуществляют в металлические рамки при температуре стекломассы 1260- 1300РС. Отформованное изделие отжимают приЧ|550-б00вС и постепенно охлаждают до 50-60 С.The products are molded into metal frames at a glass temperature of 1260–1300RS. The molded product is wrung out at H | 550-b00 in C and gradually cool to 50-60 C.

В табл. 1 приведены конкретные сос тавы стекол.In the table. 1 shows specific glass compositions.

Физико-химические свойства предлагаемых стекол представлены в табл.2.Physico-chemical properties of the proposed glasses are presented in table.2.

Как видно из данных табл. 2, синтезированные стекла обладают более высокой термостойкостью по сравнению с известными.As can be seen from the data table. 2, synthesized glasses have a higher heat resistance compared to known ones.

Таблица 1Table 1

Стекло Glass г g Содержание, вес Content, weight Л L 5102 510 2 А,2°3 A, 2 ° 3 [ Ре2°3[ Re 2 ° 3 | Сг20г || Cg 2 0 g | СаО | CaO | МдО MDO Ма20Ma 2 0 ί:.. ί: .. 1 one 53,00 53.00 3,92 3.92 о;48 about; 48 2,46 2.46 30,00 ; 30.00; 9,93 9.93 0,21 0.21 2 2 57,06 57.06 4,17 4, 17 0,59 0.59 3,28 3.28 27,56 27.56 6,66 6.66 0,68 0.68 - - 3 3 55,29 55.29 4,11 4.11 0,58 0.58 6,22 6.22 27,14 27.14 6,46 6.46 0,20 0.20 - - 4 four 53,30 53.30 3,83 3.83 0,54 0.54 5,80 5.80 25,29 25.29 6,02 6.02 1,96 1.96 3,26 3.26 ί ‘ 5 ί ' 5 47,33 47.33 3,72 3.72 0,69 0.69 2,46 2.46 23,54 23.54 5,87 5.87 10,48 10.48 5,91 5.91

Таблица 2table 2

------ Стекло ------ Glass Плотность, Density, ---------- Термостой- ---------- Heat resistant ------- Истира- ------- Istira — Водостой- - Waterproof Химическая устойчивость Chemical resistance КТР KTR 10'3кг/м3 10 ' 3 kg / m 3 кость, bone, ние, 2 кг/м 2 kg / m кость, bone, по отношению in relation к to 1 град·10 1 deg10 град.с hail гидролитический класс hydrolytic class н2оn 2 about НС 1 NA 1 Нг504 N g 50 4 МаОН 1 к Maon 1 k

1 one 2,80 2.80 5Ю+15 5Y + 15 0,82 0.82 2 2 2,80 2.80 . 540±5 . 540 ± 5 0,84 0.84 3 3 2,81 2.81 530+5 530 + 5 .0,80 .0.80 4 four 2,81 2.81 515+10 515 + 10 0,81 0.81 5 5 2,80 2.80 5 Ю±10 5 S ± 10 0,77 0.77 Формула Formula изобретения inventions

99,60 93,16 97,64 99,83 66,4899.60 93.16 97.64 99.83 66.48

Claims (2)

1 99,60 93,16 97,64 99,83 66,48 1 99,5493,0397,1699,67 71,62 1 99,48 93,85 97,50 99,45 69,355 1 99,2872,5097,^099,58 73,28 1 99,23 50,16 91,42 99,85 104,091 99.60 93.16 97.64 99.83 66.48 1 99.5493.0397.1699.67 71.62 1 99.48 93.85 97.50 99.45 69.355 1 99.2872.5097, ^ 099.58 73.28 1 99.23 50.16 91.42 99.85 104.09 1. Авантюриновое стекло, включаю- 55 щее $ίθ£, А1 , Ре203, ССаО,1. Aventurine glass, including 55 $ ίθ £, A1, Pe 2 0 3 , CCaO, МдО, Ма^О, отличающее‘с я тем, что, с целью повышения термостойкости, оно содержит указанные ком поненты в следующем количестве, мас.% 3,70*4,95MdO, Ma ^ O, characterized in that, in order to increase heat resistance, it contains the indicated components in the following amount, wt.% 3.70 * 4.95 0,45*0,79 2,45-6,25 23,50-30,200.45 * 0.79 2.45-6.25 23.50-30.20 А1<2_0A1 <2_0 Ре^О^ ^г2°3Re ^ O ^ ^ r 2 ° 3 СаОCaO МдО 5,85-10,00MdO 5.85-10.00 Иа2О 0,20-10,50Eeyore 2 O 0.20-10.50 510 £ Остальное510 £ Else 2. Стекло по π. 1, о т л и чающее с я тем, что, с целью улучше- 5 ния декоративного эффекта, оно дополнительно содержит Г 1,5-8,5 масД:2. Glass by π. 1, with the fact that, in order to improve the decorative effect, it additionally contains G 1.5-8.5 wtD:
SU802904815A 1980-04-01 1980-04-01 Aventurine glass composition SU916457A1 (en)