SU896489A1 - Method of testing for stress relaxation in bending - Google Patents
Method of testing for stress relaxation in bending Download PDFInfo
- Publication number
- SU896489A1 SU896489A1 SU772609591A SU2609591A SU896489A1 SU 896489 A1 SU896489 A1 SU 896489A1 SU 772609591 A SU772609591 A SU 772609591A SU 2609591 A SU2609591 A SU 2609591A SU 896489 A1 SU896489 A1 SU 896489A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- sample
- wedge
- slot
- testing
- stress relaxation
- Prior art date
Description
II
Изобретение относитс к испытани м материалов и может быть использовано при испытании на релаксацию напр жений при изгибе кольцевых металлических образцов.The invention relates to the testing of materials and can be used in stress relaxation tests when bending circular metal samples.
Известен способ испытани на релаксацию напр жений при изгибе, заключающийс в том; что кольцевой металлический образец с прорезью нагружают с помощью клина, который вставл ют в прорезь, нагревают нагруженный образец в печи, затем извлекают его из печи, вынимают клин и определ ют величину релаксированного напр жени по изменению ширины прорези 1.A known method of stress relaxation testing is: That an annular metal sample with a slot is loaded by means of a wedge that is inserted into the slot, the loaded sample is heated in the furnace, then removed from the furnace, the wedge is removed and the value of the relaxed voltage is determined by changing the width of the slot 1.
Недостатком способа вл етс низка точность , поскольку дл измерени изменени ширины прорези образец необходимо извлечь из печи, что измен ет температурный режим.The disadvantage of this method is low accuracy, since to measure the change in the width of the slot, the sample must be removed from the furnace, which changes the temperature.
Цель изобретени - .повышение точности путем исключени перерывов в испытании, св занных с извлечением образца из печи.The purpose of the invention is to improve accuracy by eliminating interruptions in testing associated with the extraction of the sample from the furnace.
Дл достижени поставленной цели используют клин из металлических частей, разделенных изолирующей прокладкой, к концам образца прикладывают раздвигающую их силуTo achieve this goal, a wedge of metal parts separated by an insulating gasket is used, and their force is applied to the ends of the sample.
через выведенные из печи т ги, а рюлаксированное напр жение определ ют по величине зтой силы в момент нарушени контакта между образцом и клином.through the rods removed from the furnace, and the relaxed voltage is determined by the magnitude of this force at the time of the breakdown of contact between the sample and the wedge.
На чертеже изображена схема, реализующа предлагаемый способ.The drawing shows a scheme that implements the proposed method.
Способ осуществл ют следующим образом.The method is carried out as follows.
Кольцевой металлический образец 1 с прорезью , сконструированный в виде бруса, равного сопротивлени изгибу, нагружают с помо10 щью клина, который вставл ют в прорезь. Клин выполнен из двух металлических частей 2 и 3, разделенных изолирующей прокладкой 4 и подсоединенных через провода 5 к измерительному прибору 6, фиксирующему наличие электIS рического контакта между част ми 2 и 3 и образцом 1. Дл удобства изготовлени и использовани часть 2 может быть выполнена в виде пластины, а часть 3 - составной в виде пластины и мерного клина. Пластины с изо20 лирующей прокладкой 4 могут использоватьс неоднократно, а мерный клин должен быть сменным и его толщина определ етс заданной величиной деформа1даи. Если части 2 и 3 изгоAn annular metal sample 1 with a slot, constructed in the form of a bar equal to the bending resistance, is loaded with a wedge, which is inserted into the slot. The wedge is made of two metal parts 2 and 3, separated by an insulating gasket 4 and connected via wires 5 to measuring device 6, which fixes the presence of electrical contact between parts 2 and 3 and sample 1. For convenience of manufacture and use, part 2 can be made as a plate, and part 3 - a composite in the form of a plate and a measuring wedge. Plates with an insulating gasket 4 can be used repeatedly, and the measuring wedge must be replaceable and its thickness is determined by the specified deformation value dai. If parts 2 and 3 of isg
Claims (1)