SU827323A1 - Material for transferring image onto receptive surface - Google Patents

Description

and roll it with a rubberized roller followed by separation of the substrate with a pattern printed on it from the cliché.

Example 2. The operations for producing a material with a decal are carried out in the same way as in Example 1.

Use a substrate with a thickness of 10 μm and an acid-resistant paste of the following composition, May. %:

Printing ink

Polyisobutylene

Ceresin

Paraffin

Polyethylene

Example 3. Conducted analogously to example 1. However, use a substrate with a thickness of 12 μm and a paste with the following ratio of components, May. %:

Printing paint Polyisobutylene Ceresin Paraffin Polyethylene

The material made according to examples 1,2 and 3 is used to make molds with shaped forming surfaces, for which material prepared according to the invention is placed on the prepared perceiving surface of the mold, separating the substrate from the layer of acid-resistant paste by wetting it with water cotton swabs and subsequent etching of the surface with an image of an acid-resistant crust, resulting in a relief pattern on this surface.

The use of the proposed material for transferring images to a perceiving surface will allow simplifying the technology for producing decals by reducing the number of layers used and improving the quality of the transfer of images of the pattern to the shaped forming surfaces of the molds.

Formula inventions

1. A material for transferring an image and a receiving surface comprising a paper substrate and an image-bearing layer including printing ink, characterized in that, in order to simplify the technology of producing transfer images and improve the quality of image transfer of the image to the shaped forming surfaces of molds, As a substrate, paper based on 100% sulphate cellulose with a wettability of not more than 0.5 s is used, and the image-bearing layer contains polyisobutylene, ceresin, paraffin and polyethylene in the following ratio of components, May. %:

paint

15-25

n 13-20 45-55 10-20

2-5

2. Material Io p. 1, characterized in that the substrate has a thickness of 8 to 12 l.

The source of information taken into account in the examination:

1 USSR Author's Certificate No. 358201, cl. In 41 MZ / 12, 1970 (prototype).

Claims (2)

Claim 1. Material for transferring an image to a receiving surface, containing a paper substrate and an image-bearing layer including printing ink, characterized in that, in order to simplify the manufacturing technology of decals and 20 improve the quality of the transfer of image images on the shaped forming surfaces of the molds , as the substrate, paper based on 100% sulfate cellulose with a promocency of not more than 0.5 s was used, and the image-bearing layer contains polyisobutylene, ceresin, paraffin and polyethylene n in the following ratio, May. %: The material manufactured according to examples 1., 2, 30 and 3 is used for the manufacture of molds with shaped molding surfaces, for which the material made according to the invention is laid on the prepared press surface of the mold, the substrate is separated from the layer of acid-resistant paste by wetting it water using cotton swabs and carry out subsequent etching of the surface with the image of an acid-resistant paste, as a result of which a relief pattern is formed on this surface. Printing Ink Polyisobutylene Ceresin Paraffin Polyethylene 15-25 13-20 45–55 10-20 2-5 2. Material according to π. 1, characterized in that the substrate has a thickness of 8-12 microns. Source of information taken into account during the examination: 1 USSR Copyright Certificate No. 358201, cl. In 41 M3 / 12, 1970 (prototype).