Description
(54) КОМПОЗИЦИЯ ПОКРОВНОЙ МАССЫ РУБЕРОИДА(54) COMPOSITION OF BLOOD MATERIAL RUBEROID
1one
Изобретение относитс к строительньом материалам, а именно на основе битума, используемым при производстве -материалов типа ру бероида.The invention relates to building materials, namely, based on bitumen, used in the manufacture of b-bit materials.
Известны композиции, имеющие пониженную горючесть, на основе битума хлорпарафина и различных добавок 1 и 2 .Known compositions having reduced flammability, based on chlorine paraffin bitumen and various additives 1 and 2.
Известные битумные композиции не обладают достаточной огнестойкостью. Снижение горючести кс /1позиций путем увеличени содержани хлорпарафина (20-40%) ведет к ухудшению их физикомеханических свойств (температуры разм гчени , теплостойкости, прочности на разрыв), что ограничивает область их применени .Known bitumen compositions do not have sufficient fire resistance. Reducing the flammability of the kc / 1 positions by increasing the content of chlorine paraffin (20-40%) leads to a deterioration of their physical and physical properties (softening temperature, heat resistance, tensile strength), which limits their field of application.
Введение минеральных наполнителей (известь, асбест) в количестве 1215% не обеспечивает достаточно высокой в зкости композиций, необходимой дл уменьшени стенани под действием огн , а также необходимой атмосферостойкости .The introduction of mineral fillers (lime, asbestos) in the amount of 1215% does not provide a sufficiently high viscosity of the compositions necessary to reduce the walling under the action of fire, as well as the required weather resistance.
Наиболее близкой к изобретениюпо составу и достигаемому эффекту вл етс композици , вк.пючаю ца битум , хлорпарафин н тальк 3.Closest to the invention of the composition and effect achieved is the composition, in which the pulp bitumen, chloroparaffin and talc 3.
Однако данна композици обладает всеми недостатками, присущими другим известнЕлм композици м.However, this composition has all the disadvantages inherent in other known compositions.
Цель насто щего изобретени повышение огнестойкости композиции дл покрыти рубероида.The purpose of the present invention is to increase the fire resistance of the composition for coating roofing material.
Поставленна цель достигаетс тем, что композици покровной массы рубероида, включающа битум и хлорпарафин, дополнительно содержит нефелиновый : антипирен и буру при следующем соотношении компонентов, вес.%:This goal is achieved by the fact that the composition of the covering mass of roofing material, including bitumen and chloroparaffin, further contains nepheline: fire retardant and borax in the following ratio of components, wt.%:
Битум45,0-57,0Bitum45.0-57.0
Хлорпарафин -10,0-20,0Chloroparaffin -10.0-20.0
Нефелиновый антипирен 30,0-40,0 Бура3,0-5,0Nepheline flame retardant 30.0-40.0 Bura3.0-5.0
В композицию ввод т хлорпарафины с содержанием хлора 50-70% или их смесь. Получение покровной массы дл рубероида на основе предложенной композиции осуществл ют обычным способом - механическим перемешиванием с соблюдением следующего пор дка введени компонентов; в битум:нефоЛ1Ж , хлорпарафин, бура.Chlorine paraffins with a chlorine content of 50-70% or their mixture are introduced into the composition. The preparation of coating mass for roofing material on the basis of the proposed composition is carried out in the usual way - by mechanical agitation, following the next order of introduction of the components; in bitumen: nepl1l, chloroparaffin, borax.
Примеры конкретного исполнени композиции предстап..пены в табл. 1.Examples of specific performance of the composition are pre-stage. Foams in table. one.
ьч /.Ui l / ui
Таблица 1Table 1
ripc:uio.4 «(.-it не ( , 1ripc: uio.4 "(.-it not (, 1
Priority Applications (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| SU782593604A SU697540A1 (en) | 1978-03-16 | 1978-03-16 | Ruberoid mass coating composition |
Applications Claiming Priority (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| SU782593604A SU697540A1 (en) | 1978-03-16 | 1978-03-16 | Ruberoid mass coating composition |
Publications (1)
| Publication Number | Publication Date |
|---|---|
| SU697540A1 true SU697540A1 (en) | 1979-11-15 |
Family
ID=20754886
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| SU782593604A SU697540A1 (en) | 1978-03-16 | 1978-03-16 | Ruberoid mass coating composition |
Country Status (1)
| Country | Link |
|---|---|
| SU (1) | SU697540A1 (en) |
Cited By (1)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| RU2460834C1 (en) * | 2011-06-06 | 2012-09-10 | Закрытое акционерное общество "ТехноНИКОЛЬ" | Multi-layer bitumen-polymer material and method of its production |
-
1978
- 1978-03-16 SU SU782593604A patent/SU697540A1/en active
Cited By (2)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| RU2460834C1 (en) * | 2011-06-06 | 2012-09-10 | Закрытое акционерное общество "ТехноНИКОЛЬ" | Multi-layer bitumen-polymer material and method of its production |
| EP2532515A1 (en) | 2011-06-06 | 2012-12-12 | Joint Stock Company "Technonicol" | Multilayer bituminous-polymeric material and method for producing same |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| SU697540A1 (en) | Ruberoid mass coating composition | |
| US4414385A (en) | Concrete comprising sulfur, cyclopentadiene oligomers, aggregate and glass fibers | |
| US2400563A (en) | Filled asphalt and asphalt coated roofing compositions | |
| US1751690A (en) | Waterproof fire-resistant plastic composition | |
| SU893944A1 (en) | Raw mixture for producing fire-resistant coating | |
| US2252169A (en) | Oil-treated mineral wool | |
| RU2142969C1 (en) | Method of preparing bitumen-polymer-based compositions for waterproofing materials | |
| US3667977A (en) | Explosion-proof asbestos-cement shapes | |
| US2042096A (en) | Heat insulation material and process of making same | |
| SU1597374A1 (en) | Method of producing bitumen emulsion mastic | |
| US1544215A (en) | Heat-insulating composition | |
| US4242144A (en) | Bituminous mixed composition and filler for same containing non-hygroscopic crystal water-containing substances | |
| SU907042A1 (en) | Coating composition | |
| SU1779677A1 (en) | Stock mixture for producing heat-insulating building material | |
| US3751291A (en) | Fire resistant asphalt roofing | |
| SU1010093A1 (en) | Composition for making insulating materials | |
| US1379590A (en) | Flexible plastic composition | |
| SU808442A1 (en) | Composition for making roofing papes | |
| RU2144907C1 (en) | Bitumen composition | |
| SU742450A1 (en) | Mastic | |
| SU698944A1 (en) | Raw mixture for preparing cellular concrete | |
| SU925919A1 (en) | Raw mixture for making heat- and sound insulating products | |
| RU2098442C1 (en) | Roofing cold mastic | |
| US1589512A (en) | Cement-asphalt composition of matter | |
| SU1728173A1 (en) | Composition for manufacturing heat insulated articles |