Description
1one
Изобретение относитс к металлургии, в частности к технологии получени тонколистового проката и касаетс обработки металлов давлением.The invention relates to metallurgy, in particular, to the technology for the production of sheet steel and relates to the processing of metals by pressure.
Известен способ изготовлени листа изgA known method of making a sheet of
сплава, включающий изготовление исходной заготовки непрерывным литьем и последующую гор чую прокатку заготовки, осуществл емую в несколько проходов со степенью обжати 49-51%, причем, по меньшей мере, |Q один проход провод т при степени обжати 85-95% и прокатку зачанчивают при температуре заготовки 230-270 С, а температура валков не контролируетс 1. Известный способ позвол ет получить лист толщиной 5alloy, including the manufacture of the original billet by continuous casting and subsequent hot rolling of the billet, carried out in several passes with a reduction rate of 49-51%, with at least | Q single-pass being carried out at a reduction rate of 85-95% and rolling at a workpiece temperature of 230-270 ° C, and the temperature of the rolls is not controlled 1. The known method allows to obtain a sheet with a thickness of 5
Ю мм из сплава на основе щшка. Основным недостатком известного способа вл етс необходимость проведени гор чей прокати с больщими степен ми обжати , что делает его неприемлемым дл сплавов, обладающих ну- 20 левыми характеристиками пластичности, в частности дл сплавов эвтектических составов, например, золото-олово. Зти сплавы обладают нулевой пластичностью и ударной в зкостью и их прин то считать неспособными 25U mm from the alloy on the basis of cheek The main disadvantage of this method is the need to carry out hot rolling with high degrees of reduction, which makes it unacceptable for alloys that have low plasticity characteristics, in particular for eutectic alloys, such as gold-tin. These alloys have zero ductility and toughness and are generally considered incapable of 25
подвергатьс обработке давлением , в том числе прокатке и штамповке.subjected to pressure treatment, including rolling and stamping.
Цель изобретени - получение тонкой пластичной ленты толщиной О,1-О,2 мм из эвтектического сплава золото-олово.The purpose of the invention is to obtain a thin plastic tape of thickness O, 1-O, 2 mm from a gold-tin eutectic alloy.
Это достигаетс тем, что заготовку изготовл ют непрерывны литьем при температуре сплава 305:325 С и температуре пресс-формы 285-305 С, а прокатку провод т при одинаковой температуре валков и заготовки 180-200°С со скоростью 5-8 м/мин со степенью обжати за один проход О,21 ,0%.This is achieved by the fact that the billet is manufactured by continuous casting at an alloy temperature of 305: 325 C and a mold temperature of 285-305 C, and rolling is carried out at the same temperature of the rolls and billet 180-200 ° C at a speed of 5-8 m / min. with the degree of compression in one pass O, 21, 0%.
Claims (1)
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
SU2172889A SU547242A1 (en) | 1975-09-19 | 1975-09-19 | Method of making metal tape |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
SU2172889A SU547242A1 (en) | 1975-09-19 | 1975-09-19 | Method of making metal tape |
Publications (1)
Publication Number | Publication Date |
---|---|
SU547242A1 true SU547242A1 (en) | 1977-02-25 |
Family
ID=20631939
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
SU2172889A SU547242A1 (en) | 1975-09-19 | 1975-09-19 | Method of making metal tape |
Country Status (1)
Country | Link |
---|---|
SU (1) | SU547242A1 (en) |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
RU2785130C2 (en) * | 2016-06-02 | 2022-12-05 | Танака Кикинзоку Когио К.К. | Golden sprayed target |
US11569074B2 (en) | 2016-06-02 | 2023-01-31 | Tanaka Kikinzoku Kogyo K.K. | Gold sputtering target |
-
1975
- 1975-09-19 SU SU2172889A patent/SU547242A1/en active
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
RU2785130C2 (en) * | 2016-06-02 | 2022-12-05 | Танака Кикинзоку Когио К.К. | Golden sprayed target |
US11569074B2 (en) | 2016-06-02 | 2023-01-31 | Tanaka Kikinzoku Kogyo K.K. | Gold sputtering target |
US11817299B2 (en) | 2016-06-02 | 2023-11-14 | Tanaka Kikinzoku Kogyo K.K. | Gold sputtering target |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
FR2447753A1 (en) | PROCESS FOR MANUFACTURING GRINDING BODIES WITH AXIAL SYMMETRY IN FERROUS ALLOY AND NEW GRINDING BODIES OBTAINED BY THIS PROCESS | |
KR890003976A (en) | High strength, heat resistant aluminum alloys and methods of manufacturing articles processed therefrom | |
KR920701500A (en) | Method for manufacturing low earing aluminum alloy strip | |
ES466461A1 (en) | Method of producing machine wire by continuous casting and rolling | |
GB1270926A (en) | Improvements in and relating to a method of making metal articles | |
SU547242A1 (en) | Method of making metal tape | |
FR2382287A1 (en) | "BLACK MANUFACTURING" PROCESS AT RELATIVELY LOW TEMPERATURES OF FORGED MOLYBDENE AND MOLYBDENE ALLOY PRODUCTS AND NEW PRODUCTS THUS OBTAINED | |
KR970014875A (en) | METHOD FOR MANUFACTURING MOISTURE MATERIAL FOR COPY ALLOY FOR STEEL STEEL CASTING AND METHOD THEREOF | |
RU2094139C1 (en) | Method and apparatus for manufacture of continuously cast steel billets | |
US3584368A (en) | Titanium fabrication | |
US5174363A (en) | Process for producing shape strips of metals | |
US3099592A (en) | Process of annealing low carbon steel | |
SU660770A1 (en) | Method of making blades from double-phase titanium alloys | |
SU1117337A1 (en) | Method of machining sheet blanks from aluminium-base alloys | |
JPH06322493A (en) | Production of high strength aluminum alloy | |
SU644560A1 (en) | Method of producing stainless still strip for safety razor blades | |
SU648297A1 (en) | Method of making rolled sections of bearing steel | |
SU1509143A1 (en) | Method of producing foil from magnesium alloys | |
SU439193A1 (en) | Crystallizer | |
SU1126615A1 (en) | Method for heat treating high-alloy steels | |
SU901339A1 (en) | Method of treatment of alluminium-based alloy sheet materials | |
SU623643A1 (en) | Method of making castings by pressing of liquid metal | |
SU677783A1 (en) | Metal foil manufacturing method | |
SU449958A1 (en) | The method of producing sheets of dispersion-strengthened alloys | |
SU579341A1 (en) | Method of manufacturing elongated articles and semifinished products from refractory metals |