SU315955A1 - PROTECTIVE TERMOMETER TIP - Google Patents
PROTECTIVE TERMOMETER TIPInfo
- Publication number
- SU315955A1 SU315955A1 SU1435082A SU1435082A SU315955A1 SU 315955 A1 SU315955 A1 SU 315955A1 SU 1435082 A SU1435082 A SU 1435082A SU 1435082 A SU1435082 A SU 1435082A SU 315955 A1 SU315955 A1 SU 315955A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- protective
- tip
- termometer
- coating
- corundum
- Prior art date
Description
Изобретение может быть использовано в пирометрах, например термоэлектрических дл измерени температур до 1600°С газовых окислительных сред, содержащих пылевидные частицы, в состав которых вход т окислы , например, лселеза и кремни .The invention can be used in pyrometers, for example, thermoelectric for measuring temperatures up to 1600 ° C, gas oxidizing media containing dust particles, which include oxides, for example, selenium and silicon.
Известен защитный нако 1ечник термометра , состо щий из керамического чехла, покрытого слоем обмазки из шамотного порошка или мертел на св зке из жидкого стекла.A protective thermometer is known, consisting of a ceramic sheeting covered with a layer of chamotte powder or dead on a bond of liquid glass.
Основное назначение этой обмазки - ослабление термических ударов нри резком изменении температуры.The main purpose of this coating is to reduce the thermal shock of an abrupt temperature change.
Однако така защитна арматура нмеет р д недостатков.However, such protective fittings have several disadvantages.
Св зка (жидкое стекло) .при минерализации покрывает корундо-вый чехол глазурью, проникающей в поры чехла, что при изменении температур ,в рабочем интервале приводит к его деформации и разрушению.Binding (liquid glass). When mineralized, it covers the corundum sheath with glaze that penetrates the pores of the sheath, which, as temperatures change, in the working range leads to its deformation and destruction.
Вследствие существенного различи коэффициентов температурного расширени материала корундового чехла и обмазки, а также химического взаимодействи пыли газовой атмосферы с об.мазкой при действии переменной температуры покрытие довольно быстро разрушаетс , обнал а корундовый чехол.Due to the significant difference in the thermal expansion coefficients of the corundum sheath material and the coating, as well as the chemical interaction of the gas atmosphere dust with the lubricant under the action of a variable temperature, the coating is quite quickly destroyed and the corundum case is exposed.
пыли до момента своего разрушени , после чего наличие глазури на поверхности чехла существенно увеличивает веро тность образовани легкоплавких соединений При попадании пыли с окислами железа на незащищенную поверх ;ость, что снижает продолжительность службы защитной арматуры.dust until its destruction, after which the presence of glaze on the surface of the cover significantly increases the probability of formation of low-melting compounds. If dust with iron oxides gets on the unprotected surface, it reduces the service life of the protective fittings.
Целью настогицего изобретени вл етс повышение срока службы защитного наконечника термометра в окислительной атмосфере с пылью, содержащей окислы железа и кремнп .The aim of the present invention is to increase the service life of the protective tip of the thermometer in an oxidizing atmosphere with dust containing iron oxides and silica.
Эта цель достигаетс тем, что нарулчный слой защитного наконечника выполнен из магнезиальной Шпинели.This goal is achieved by the fact that the rounded protective tip layer is made of magnesian Spinel.
На чертеже приведен наконечник, где /- KopyiLTOiJbni чехол, 2 - покрытие, выполненное нз магнезиальной шпинели.The drawing shows the tip, where / is a Kopyiltoibni case, 2 is a coating made by magnesian spinel.
Корундовый плкопечник / выполн ет роль защитного чехла по отношению к датчику, а по от1юшению к покрытию - роль несущей конструкции.Corundum plc pusher / plays the role of a protective cover in relation to the sensor, and in relation to the coating - the role of the supporting structure.
Покрытие 2 из магнезиальной шпинели выполн ет роль защитного сло , предохран ющего орундовый наконечник / от контакта с пылевидными частицами и ослабл ющего тепловые удары, действующие на защитный Г1аконечник.The magnesia spinel coating 2 serves as a protective layer that protects the handpiece / from contact with dust particles and attenuates thermal shocks acting on the protective tip.
с о,кислами металла, например железа и кремни , имеет близкий к коруиду коэффициент термичеекого расширени и достаточно прочно сцепл етс с иоверхпостыо корундового наконечника. Покрытие из : 1агнезиальной шпинели мож}10 выполнить путем нанесени на корундовый наконечник маесы, содержащей окислы алюмини и .магни с добавкой чаеов- рской глины и асбеста, а также аллюмофосфатную с лоследуюгцей сушкой и обжигом ири температуре 13001400°С .o, acidic metals such as iron and silicon, has a coefficient of thermal expansion close to coruid, and it adheres sufficiently firmly to the uppermost corundum tip. The coating of: 1 magnesia spinel can be performed 10 by applying to the corundum tip a mixture containing aluminum oxides and magnesi with the addition of tea clay and asbestos, as well as alluminophosphate with subsequent drying and roasting at a temperature of 1300–1400 ° C.
Продолжительность службы такого наконечника в рабочих услови х (Б атмосфере воздухопровода гор чего дуть доменной нечи ) почти вдвое превышает ность службы двухслойного катной обмазки.The length of service of such a tip under operating conditions (B atmosphere of the hot air duct blowing blast furnace) is almost twice as long as the service of a two-layer cat coating.
Предмет изобретени Subject invention
Защитный наконечник термометра, содержащий двухслойный керамический блок, зиутренний слой которого выполнен из корунда , отличающийс тем, что, с целью повышени срока службы в окислительной газовой атмосфере с пылью, содержащей окислы железа и кремни , наружный слой защитного наконечника выполнен из маг)езиальной щнинели.A protective tip of the thermometer containing a two-layer ceramic block, the outer layer of which is made of corundum, characterized in that, in order to increase the service life in an oxidizing gas atmosphere with dust containing oxides of iron and silicon, the outer layer of the protective tip is made of a magical element.
%4%four