SU288630A1 - CERAMIC MATERIAL - Google Patents
CERAMIC MATERIALInfo
- Publication number
- SU288630A1 SU288630A1 SU1342660A SU1342660A SU288630A1 SU 288630 A1 SU288630 A1 SU 288630A1 SU 1342660 A SU1342660 A SU 1342660A SU 1342660 A SU1342660 A SU 1342660A SU 288630 A1 SU288630 A1 SU 288630A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- ceramic material
- mgo
- coefficients
- weight
- linear expansion
- Prior art date
Description
Изобретение относитс к керамическому материалу с ннзкн.мн положительными и отринательными температурными коэффициентами линейного расширени дл изготовлени .деталей, работающих в условп .х резкого из- 5 менени те.мператур (дугогасительных камер, корпусов реостатов, стабил11знруюп;нх резопйторов , катушек и др.). Изнестеп керамический материал, включа- ю юшнй АЬОз; SiOa, MgO, LigO. Описываемый материал обладает низкими иоложительными и отрицательными термическими коэффициентами линейного расширени н вь1соки.1 пределом прочности при статическом изгибе. Это достигаетс тем, что он содержит указанные комионенты в следующих количествах, вес. %: АЬОз 42-56; 5Ю2 40; MgO 3-10; Li20 1-8. В качестве сырь используют тальк, каолин, глинозем и технпчс-скпй углекнслый литий. Конкретные составы материала приведены в табл. 1. 15 в до из ли 20 об но Т а б л-11 ц а 1 Составы .материала, вес % Компоненты подвергают мокрому иомолу шаровых мельницах на снте 10000 отв/смостатка менее 2%. Пздели оформл ют вест1Пз1мн сиособами: нрессованием, гор чим тьем, нрот жкой н другими н после cyiHKH жигают нри темнературе 1200-ISOOC. В табл. 2 приведены коэффнциент1з1 линейго расшнрени материалов.The invention relates to a ceramic material with low effective positive and negative temperature coefficients of linear expansion for the manufacture of parts working under conditions of a sharp change in temperature variations (arc-suppressing chambers, resistors, stabilizers, nx resonators, coils, etc. ). Izteptep ceramic material, including the young ABOz; SiOa, MgO, LigO. The described material has low and positive and negative thermal coefficients of linear expansion and high1.1 tensile strength during static bending. This is achieved by the fact that it contains the indicated comonents in the following amounts, weight. %: ABOZ 42-56; SiO2 40; MgO 3-10; Li20 1-8. The raw material used is talc, kaolin, alumina and techpchs-carbon black lithium. Specific compositions of the material are given in table. 1. 15 in to 20 parts of the material. Compositions, weight,% Components are subjected to wet milling ball mills on a distance of 10,000 holes / cm of residue less than 2%. The slides are decorated with West1Pz1mn in the following ways: by pressing, by hot, by gentle, by others and after cyiHKH, they burn in the temperature of 1200-ISOOC. In tab. 2 shows the coefficient of coefficients for a linear material dilution.
Таблица 2table 2
В табл. 3 приведены другие свойства материалов.In tab. 3 shows other properties of materials.
Характеристика материаловCharacteristics of materials
Предмет изобретени Subject invention
Керамический материал, включающий АЬОл, SiO2, MgO, Li2O, отличающийс тем, что, с целью достижени низких положительных и отрицательных температурных коэффициенТаблица 3Ceramic material, including Al, SiO2, MgO, Li2O, characterized in that, in order to achieve low positive and negative temperature coefficients. Table 3
тов линейного расширени и увеличени предела прочности при статическом изгибе, он содержит указанные компоненты в следуюHUIX количествах, вес. %: АЬЮз 42-56; ЗЮг 40; MgO 3-10; Li2O 1-8.Comm linear expansion and increase the strength at static bending, it contains these components in the following quantities, weight. %: ABC 42-56; SOUGH 40; MgO 3-10; Li2O 1-8.