SU283591A1 - ALLOY FOR STEEL REDUCTION - Google Patents
ALLOY FOR STEEL REDUCTIONInfo
- Publication number
- SU283591A1 SU283591A1 SU1356599A SU1356599A SU283591A1 SU 283591 A1 SU283591 A1 SU 283591A1 SU 1356599 A SU1356599 A SU 1356599A SU 1356599 A SU1356599 A SU 1356599A SU 283591 A1 SU283591 A1 SU 283591A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- alloy
- steel
- steel reduction
- magnesium
- reduction
- Prior art date
Description
Известны оплавы дл раскислени стали, содержащие алюминий, маргаиец, кремний, железо и фосфор.Alloys for the deoxidation of steel containing aluminum, marganite, silicon, iron and phosphorus are known.
Дл улучшени качества стали и предотвращени рассыпани снлаза предложено вводить в него .магний -при следующем соотношении компонентов, вес. %:In order to improve the quality of steel and prevent the disintegration of the cash, it has been proposed to inject .magnesium in the following ratio of components, weight. %:
10-6010-60
25-60 2-15 0,06- 0,6 0,3- 0,6 Остальное.25-60 2-15 0.06- 0.6 0.3- 0.6 The rest.
Введение в сплав магни в количестве 0,3- 0,6% ПОЗВОЛЯЛО повысить его стойкость при хранении на воздухе. Сплав .или не рассыпаетс со.всем или показывает очень слабые признаки рассыпани после тридцати суток хранени на воздухе. Применение описываемого снлава обеспечивает быстрое и полноеThe introduction of magnesium in the amount of 0.3-0.6% in the alloy has enabled to increase its stability when stored in air. The alloy does not spill completely or shows very weak signs of scattering after thirty days of storage in air. The use of the described snlave provides a quick and complete
удаление из жидкой стали продуктов раскислени , Позвол ет получать более чистую сталь по неметаллическим включени м. Сплав пригоден дл вьшлавки рафинированного ферромарганца .removal of deacidification products from liquid steel. It allows to get cleaner steel by nonmetallic inclusions. The alloy is suitable for refined ferromanganese smelting.
Предмет изобретени Subject invention
Сплав дл раскислени стали, содержащий марганец, кремний, алюминий, фосфор, железо , отличающийс тем, что, с целью улучшени качества стали и нредотвращени его рассынани , в него введен магний при следующем соотношении компонентов, вес. %:An alloy for deoxidizing steel containing manganese, silicon, aluminum, phosphorus, iron, characterized in that, in order to improve the quality of steel and prevent its dispersion, magnesium is introduced into it in the following ratio of components, weight. %:
10-6010-60
МарганецManganese
25-6025-60
КремнийSilicon
2-152-15
АлюминийAluminum
ФосфорPhosphorus
0,06- 0,6 0,3- 0,60.06-0.6 0.3-0.6
МагнийMagnesium
Остальное.Rest.
ЖелезоIron