SU1557147A1 - Polymeric composition - Google Patents
Polymeric composition Download PDFInfo
- Publication number
- SU1557147A1 SU1557147A1 SU874213177A SU4213177A SU1557147A1 SU 1557147 A1 SU1557147 A1 SU 1557147A1 SU 874213177 A SU874213177 A SU 874213177A SU 4213177 A SU4213177 A SU 4213177A SU 1557147 A1 SU1557147 A1 SU 1557147A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- kgf
- polyethylene
- strength
- aluminum powder
- composition
- Prior art date
Abstract
Изобретение относитс к строительным материалам и может быть использовано при изготовлении теплоизол ционных материалов. Целью изобретени вл етс повышение прочности композиции при изгибе при (-40)(-60)°С. Полимерна композици содержит, мас.%: полиэтилен 25-35The invention relates to building materials and can be used in the manufacture of heat insulating materials. The aim of the invention is to increase the strength of the composition during bending at (-40) (- 60) ° C. Polymer composition contains, wt%: polyethylene 25-35
т желую пиролизную смолу 3-6heavy pyrolysis resin 3-6
алюминиевую пудру 0,5-1,0aluminum powder 0.5-1.0
керамзит 48-65,5haydite 48-65,5
древесный наполнитель остальное. Композици имеет следующие показатели свойств: плотность 720-780 кг/м3 wood filler rest. The composition has the following properties: density 720-780 kg / m 3
предел прочности при изгибе в сухом состо нии 750 кгс/см2, после выдержки при -40°С 520-590 кгс/см2, при -60°С 500-580 кгс/см2. 2 табл.Flexural strength in dry condition is 750 kgf / cm 2 , after holding at -40 ° C 520-590 kgf / cm 2 , at -60 ° C 500-580 kgf / cm 2 . 2 tab.
Description
Изобретение относитс к строительным материалам и может быть использовано при изготовлении теплоизол ционных материалов.The invention relates to building materials and can be used in the manufacture of heat insulating materials.
Цель изобретени - повышение прочности композиций при изгибе при температурах -40)...(-60)°С.The purpose of the invention is to increase the strength of the compositions in bending at temperatures of -40) ... (-60) ° C.
В полимерной композиции в качестве св зующего используют полиэтилен и т желую пиролизную смолу пропан- бутановой фракции нефти, алюминиевую пудру, в качестве наполнител - измельченную древесину и дополнительно керамзит.In the polymer composition, polyethylene and propylene-butane oil heavy pyrolysis resin, aluminum powder are used as a binder, chopped wood and, additionally, expanded clay as a filler.
Приготовление композиции осуществл ют непосредственным перемешиванием всех компонентов в мешалке барабанного типа в течение 30 мин. Приготовленную смесь укладывают в пресс- форму и прессуют при 210 С и давлении 35 кгс/см в течение 7-10 мин. После охлаждени издели извлекают из пресс-формы и складируют.The preparation of the composition is carried out by directly mixing all the components in a drum-type mixer for 30 minutes. The prepared mixture is placed in a mold and pressed at 210 C and a pressure of 35 kgf / cm for 7-10 minutes. After cooling, the product is removed from the mold and stored.
Плотность и прочность композиции определ ют по стандартным методикам.The density and strength of the composition are determined by standard methods.
Состав композиции в табл.1, а свойства - в табл.2.The composition in table 1, and properties in table 2.
Claims (1)