SU1500633A1 - Glass composition - Google Patents

Glass composition Download PDF

Info

Publication number
SU1500633A1
SU1500633A1 SU874361895A SU4361895A SU1500633A1 SU 1500633 A1 SU1500633 A1 SU 1500633A1 SU 874361895 A SU874361895 A SU 874361895A SU 4361895 A SU4361895 A SU 4361895A SU 1500633 A1 SU1500633 A1 SU 1500633A1
Authority
SU
USSR - Soviet Union
Prior art keywords
glass
cao
crystallization
cost
glass composition
Prior art date
Application number
SU874361895A
Other languages
Russian (ru)
Inventor
Pavel D Sarkisov
Valerij G Smirnov
Yavuz S Mustafaev
Arif Z Askerov
Original Assignee
Azerb T Inst
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Azerb T Inst filed Critical Azerb T Inst
Priority to SU874361895A priority Critical patent/SU1500633A1/en
Application granted granted Critical
Publication of SU1500633A1 publication Critical patent/SU1500633A1/en

Description

Изобретение относится к составам железосодержащих черных стекол типа "Марблит", которые применяются в качестве строительных и облицовочных материалов» С целью снижения кристаллизации в области температур выработки и себестоимости стекла-оно содержит, мас.%: Ре20э 40-50; Ыа20 5-10; СаО 15-30; 810г 4,5-6,0; А1г03 15-30. Температура выработки (1§7“ =2) 1200-1260°С» Область кристаллизации стекол 850-1150°С. 1 табл.The invention relates to compositions of iron-containing black glass type "Marblit", which are used as building and facing materials. "To reduce crystallization in the temperature range of production and cost of glass-it contains, wt.%: Fe 2 0e 40-50; Na 2 0 5-10; CaO 15-30; 810 g 4.5-6.0; A1 g 0 3 15-30. Temperature of generation (1§7 “= 2) 1200-1260 ° С” The area of crystallization of glasses is 850-1150 ° С. 1 tab.

Изобретение относится к стеклоделию, а именно к составам стекол типа "Марблит", которые могут найти применение в качестве строительных и облицовочных материалов, а также в мебельной промышленности.The invention relates to glassmaking, and in particular to the composition of glass type "Marblit", which can be used as building and facing materials, as well as in the furniture industry.

Цель изобретения - снижение кристаллизации в области температур выработки и себестоимости стекла.The purpose of the invention is the reduction of crystallization in the temperature range of production and cost of glass.

В качестве основного сырьевого материала для варки стекла используют красный илам Кировобадского алюминиевого завода, а также мел, соду, глинозем.Red silts from the Kirovobad aluminum plant, as well as chalk, soda, and alumina are used as the main raw material for glass melting.

Варку стекла осуществляют в тигельной печи в шамотном или кварцевом тиглях емкостью 1-3 л при 1450— 1500°С в нейтральной или слабоокислительной газовой среде, выработку методом свободного литья, прокатывание - металлическим валом, а также ручным прессованием в металлических формах размерами 100· 100·5 и 200·200* х10 мм.Glass is brewed in a crucible furnace in a fireclay or quartz crucibles with a capacity of 1-3 liters at 1450–1500 ° C in a neutral or slightly oxidizing gaseous medium, the production by the method of free casting, rolling by a metal shaft, and also by manual pressing in metal forms with dimensions of 100 · 100 · 5 and 200 · 200 * h10 mm.

сwith

££

В таблице приведены конкретные составы стекол и их свойства.The table shows the specific compositions of glasses and their properties.

Стекло с использованием красного , шлама обладает пониженной склонностью к кристаллизации в широкой области температур и низкой стоимостью, что позволяет широко применять его в производстве строительных и облицовочных материалов типа "Марблит", коврово-мозаичных плиток стеклокремнизита, а также в качестве покрытий тепличных сооружений и др. .Glass using red sludge has a low tendency to crystallization in a wide range of temperatures and low cost, which allows it to be widely used in the production of building and veneering materials such as Marlit, carpet-mosaic tiles of glass creams, as well as coatings of greenhouse structures, etc. .

Claims (1)

Формула изобретенияClaim 5Ц 15006335TS 1500633 Стекло, включающее Ге203, Иа^О, СаО, 3ΐ02, отличающееся тем, что, с целью снижения кристаллизации в области температур выработки и себестоимости стекла, оно дополнительно содержит А1г03 при следующем соотношении компонентов, масД;Glass, including Ge 2 0 3 , Ia ^ O, CaO, 3ΐ0 2 , characterized in that, in order to reduce crystallization in the temperature range of production and cost of glass, it additionally contains A1 g 0 3 in the following ratio of components, masd; 33 15006331500633 4four 40-5040-50 5-105-10 15-30 .,15-30., ГR Рег0 5Re g 0 5 Ν&ζ0Ν & ζ 0 СаОCao 8ϊΟ2 8ϊΟ 2 А1г03 A1 g 0 3 4,5-6,04.5-6.0 15-3015-30 Показатели Indicators Стекло по примеру Glass by example ' 1 ' one - 1 - one > т > t 4 four Состав, мас.% Composition, wt.% 50,0 50.0 45,0 45.0 40,0 40.0 48 48 А12оз A1 2 o C 16,5 16.5 15,0 15.0 25,0 25.0 22,0 22.0 СаО Cao 20,7 20.7 30,0 30.0 20,5 20.5 15,0 15.0 «аг0"A g 0 6,8 6.8 5,0 5.0 10,0 10.0 9,4 9.4 5ίθζ 5ίθζ 6,0 6.0 5,0 5.0 4,5 4.5 5,6 5.6 Температурцая область максимальной Maximum temperature area кристаллизации, 0 С 850-1100crystallization, 0 С 850-1100 850-1150 850-1150 90-1050 90-1050 900-1000 900-1000 Температура выра- Temperature of ботки (1^=2), °С Стоимость шихты, workings (1 ^ = 2), ° С Cost of charge, 1240 1240 1260 1260 1200 1200 1215 1215 руб/т rub / t 6,40 6.40 5,30 5.30 24,04 24.04 16,77 16.77
SU874361895A 1987-11-13 1987-11-13 Glass composition SU1500633A1 (en)