SU138793A1 - The method of obtaining titanium enamels of light colors - Google Patents

The method of obtaining titanium enamels of light colors

Info

Publication number
SU138793A1
SU138793A1 SU681713A SU681713A SU138793A1 SU 138793 A1 SU138793 A1 SU 138793A1 SU 681713 A SU681713 A SU 681713A SU 681713 A SU681713 A SU 681713A SU 138793 A1 SU138793 A1 SU 138793A1
Authority
SU
USSR - Soviet Union
Prior art keywords
enamels
enamel
light colors
obtaining titanium
frit
Prior art date
Application number
SU681713A
Other languages
Russian (ru)
Inventor
Т.И. Болюбаш
С.А. Коган
Original Assignee
Т.И. Болюбаш
С.А. Коган
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Т.И. Болюбаш, С.А. Коган filed Critical Т.И. Болюбаш
Priority to SU681713A priority Critical patent/SU138793A1/en
Application granted granted Critical
Publication of SU138793A1 publication Critical patent/SU138793A1/en

Description

При существующей технологии получени  титановых эмалей светлых тонов краситель ввод т в шихту неред нлавлением с добавлением в бесцветную эмаль при ее размоле в щаровой мельнице. При этом во врем  обжига при разности температур +10° готовые издели  принимают разную окраску.With the existing technology for producing titanium enamels of light tones, the dye is introduced into the charge in a non-hazardous form with addition to colorless enamel during its grinding in a press mill. In this case, during firing at a temperature difference of + 10 °, the finished products take on different colors.

Предложенный способ получени  титановых эмалей обеспечивает стабильность окраски. Способ состоит в том, что в высушенную на воздухе фритту титановой эмали (например, эмали Т-148) ввод т тот или иной краситель, после чего смесь загружают в печь и вторично плав т эмаль Б течение 1 час 45 мин - 2 час при 1250-1350°.The proposed method for producing titanium enamels ensures color stability. The method consists in introducing one or another dye into the air-dried Frit of titanium enamel (for example, T-148 enamel), after which the mixture is loaded into the furnace and the enamel B is again melted for 1 hour 45 minutes - 2 hours at 1250 -1350 °.

Дл  получени  эмали лселтого цвета в фритту добавл ют 0,2% хромпика (Kz Сгг От), дл  получени  голубой эмали ввод т 1-2% окиси кобальта (Со2Оз),-а при получении эмали бежевого цвета - 5% мартанцевой руды.For the production of enamel of the best color, 0.2% chromic is added to the frit (Kz Cr 2 O), 1-2% of cobalt oxide (Co2O3) is added to make blue enamel, and 5% of the martan ore is produced when making enamel.

Издели , покрытые эмалью, приготовленной по предложенному способу , имеют светлый тон и при обжиге в температурном интервале 830-860° сохран ют стабильность окраски.The products coated with enamel prepared according to the proposed method have a light tone and, when roasting in the temperature range of 830-860 °, maintain color stability.

Предмет изобретени Subject invention

Claims (2)

1.Способ получени  титановых эмалей светлых тонов, отличающийс  тем, что, с целью получени  стабильно окрашенных эмалей, в вь1сушенную на воздухе фритту ввод т красители и подвергают ее повторному плавлению по известному режиму.1. A method of producing titanium enamels of bright colors, characterized in that, in order to obtain stably colored enamels, dyes are introduced into a dried air-dried frit and are subjected to its re-melting according to a known regime. 2.Прием выполнени  способа по п. 1, отличающийс  тем, что, с целью получени  желтой, голубой и бежевой эмалей, во фритту эмали ввод т соответственно красители: хромпика 0,2%, окиси кобальта -2% и марганцевой руды 5%.2. A method according to Claim 1, characterized in that, in order to obtain yellow, blue and beige enamels, dyes are injected into the enamel frit, respectively: chromate 0.2%, cobalt oxide -2% and manganese ore 5%.
SU681713A 1960-10-10 1960-10-10 The method of obtaining titanium enamels of light colors SU138793A1 (en)