SU1270655A1 - Method of determining critical moisture content of ceramic mass - Google Patents

Method of determining critical moisture content of ceramic mass Download PDF

Info

Publication number
SU1270655A1
SU1270655A1 SU843759792A SU3759792A SU1270655A1 SU 1270655 A1 SU1270655 A1 SU 1270655A1 SU 843759792 A SU843759792 A SU 843759792A SU 3759792 A SU3759792 A SU 3759792A SU 1270655 A1 SU1270655 A1 SU 1270655A1
Authority
SU
USSR - Soviet Union
Prior art keywords
samples
humidity
mass
determining
nost
Prior art date
Application number
SU843759792A
Other languages
Russian (ru)
Inventor
Юрий Васильевич Богачев
Владимир Васильевич Перегудов
Original Assignee
Алтайский политехнический институт им.И.И.Ползунова
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Алтайский политехнический институт им.И.И.Ползунова filed Critical Алтайский политехнический институт им.И.И.Ползунова
Priority to SU843759792A priority Critical patent/SU1270655A1/en
Application granted granted Critical
Publication of SU1270655A1 publication Critical patent/SU1270655A1/en

Abstract

Изобретение относитс  к анализу стрс1ительных материалов и позвол ет снизить трудоемкость и повысить точность определени  критической .влажности ( ) керамических масс. Способ заключаетс  в том, что формуют из керамической массы два образца в виде плиток. Измер ют массу образцов до сушки и после сушки до посто нной массы и вычисл ют влажность исходных образцов по формуле U(m -mo/m) 100%, где Шо - исходна  масса образца, т - масса образца после сушки до посто нной массы. Вычисл ют относительную усаДку образцов по формуле 1The invention relates to the analysis of building materials and reduces the labor intensity and improves the accuracy of determining the critical moisture content () of the ceramic masses. The method consists in forming two samples in the form of tiles from a ceramic mass. Measure the mass of the samples before drying and after drying to constant mass and calculate the moisture content of the original samples using the formula U (m -mo / m) 100%, where Sho is the initial mass of the sample, and t is the mass of the sample after drying to constant mass. Calculate the relative size of the samples using formula 1

Description

Изобретение относитс  к анализу строительных материалов, в частност к способам определени  керамических масс, и мЛкет быть использовано при подборе составов формовочных масс облицовочной и стеновой строительНой-керамики . Цель изобретени  - снижение тру .доемкости и повышение точности опре делени  критиче)СКОЙ влажности керамических масс ( Пример. Формуют из керамической массы два образца - плитки размером 100 х 100 х 10 мм с различными начальными влажност ми. Мас са пегрвой плитки т, 182,7 г, масса второй плитки ,6. Дл  измерени  воздушной усадки на свежесформо ванные плитки острыми ножками штанг циркул  нанос т метки по диагонал м через 100 мм. Плитки высушивают до посто нной массы при комнатной температуре. Измер ют массу плиток после сушки: масса первой плитки mj, 152,8rj; масс второй П.ПИТКИ ,6 г. После сушки средн   длина между метками на первой плитке 1,92,1 мм средн   длина между метками на второй плитке ,5 мм. вычисл ют влажность образцов по формуле Исходна  влажность первого образ Гт - 182,7-152,8 19,6%. 152,8 Исходна  влажность второго образ 180,6-147,6 100% 22,4% 147,6 Вычисл ют относительную усадку образцов по формуле 100 - L 100 100-92,1 ,9%; 100 100-86,5 , QQ ,5%. Вычисл ют критическую влажностьThe invention relates to the analysis of building materials, in particular, to methods for determining ceramic masses, and mLet to be used in the selection of molding masses of facing and wall construction ceramics. The purpose of the invention is to reduce the labor capacity and increase the accuracy of determining the criticality of the SKY humidity of the ceramic masses (Example. Two samples are formed from the ceramic mass - tiles of 100 x 100 x 10 mm in size with different initial humidity. Mass of green tiles t, 182, 7 g, mass of the second tile, 6. For measuring air shrinkage, the freshly formed tiles with sharp legs of the rods are circulating marks diagonally across 100 mm. The tiles are dried to constant mass at room temperature. The mass of the tiles is measured after drying: the mass of the first tiles mj, 152,8rj; mass of the second P.PITKI, 6 g. After drying, the average length between the marks on the first tile is 1.92.1 mm and the average length between the marks on the second tile, 5 mm, calculate the moisture content of the samples using the formula Initial moisture of the first image Gt - 182.7-152.8 19.6%. 152.8 Initial moisture content of the second image 180.6-147.6 100% 22.4% 147.6 Calculate the relative shrinkage of the samples using the formula 100 - L 100 100-92 , 1, 9%; 100 100-86.5, QQ, 5%. Calculate the critical humidity

-Ui-l.-U2  -Ui-l.-U2

иand

ICP .-.ICP .-.

13,5-19,6 -7,9.-22,4 13.5-19.6 -7.9.-22.4

13,5-7,9 1э,//о.13.5-7.9 1e, // o.

55 ф55 f

ормула изобретени formula of invention

Способ определени  критической влажности керамических масс, включаю5 Дл  определени  точности аналкэа о среднему арифметическому значеию предварительно производ т расет необходимого объема выборки. ак, при среднем квадратическом тклонении ,0%, допустимой .порешности ,5% и доверительной вео тности ,95 объем выборки п оставл ет 15 наблюдений. В этом слуае средние арифметические значени  составл ют дл  данного способа 14,1%, а дл  способа-прототипа 14,0%. Мера точности оцениваетс  также редней квадратичной погреишостью, ычисл емой по формуле , где л и - сумма квадратов случайных погрешностей, п - число наблюений . Дл  предлагаемого способа Р55 „ , 1 ° Дл  способа-прототипа 1,06. Точность предлагаемого способа выше , поскольку . В таблице приведены данные, пйдтверждающие более высокую точность предлагаемого способа при сушке по среднеквадратичной погрешности в сопоставлении со способом-прототиnoMj дл  выборки из 15 наблюдений. Необходимость и достаточность определени  на базе двух образцов с различной влажностью исходит из того, что наклон пр мых зависимости влажности от усадки в интервале усадочных  влений, т.е. в интервалах Ug -Окр и П -UXP , одинаков. Усадка образцов происходит до влажности Ицр , величина которой не зависит от начальной влажности, а зависит лишь от состава данной массы. Это позвол ет осуществить расчет UKP по указанной формуле, не осуществл   посто нного контрол  и многочисленных измерений и взвешиваний образцов в процессе высушивани  до посто нной массы, и дает возможность более точно определить критическую влажность, так как нет графических построений.The method for determining the critical moisture content of ceramic masses includes: 5 To determine the accuracy of analka, the arithmetic mean value is pre-made to calculate the required sample size. So, with the mean square declination, 0%, permissible error, 5% and confidence, 95 the sample size n leaves 15 observations. In this case, the average arithmetic values are 14.1% for this method, and 14.0% for the prototype method. The accuracy measure is also estimated by the mean square error, calculated using the formula, where l and is the sum of the squares of random errors, and n is the number of observations. For the proposed method P55, 1 ° For the prototype method 1.06. The accuracy of the proposed method is higher because. The table shows the data confirming the higher accuracy of the proposed method during drying according to the rms error in comparison with the PrototyphoMj method for a sample of 15 observations. The necessity and sufficiency of determination on the basis of two samples with different humidity comes from the fact that the slope of the direct dependence of humidity on shrinkage in the interval of shrinkage effects, i.e. in the intervals Ug -Ocr and P -UXP, the same. Shrinkage of the samples occurs to the Icr moisture, the value of which does not depend on the initial moisture, but depends only on the composition of the mass. This allows the UKP to be calculated using the specified formula, not continuously monitoring and numerous measurements and weighing of samples during the drying process to a constant mass, and makes it possible to more accurately determine the critical humidity, since there are no graphical constructions.

щий формование образцов из массы, измерение их исходной влажности, сушку образцов до посто нной массы.forming samples from the mass, measuring their initial humidity, drying the samples to a constant weight.

критической влажности ведут по формулеcritical moisture lead by the formula

- 1г U.-ti и- 1g U.-ti and

Claims (1)

55 Формула изобретения55 The claims Способ определения критической влажности керамических масс, включаю3 щий формование образцов из массы, измерение их исходной влажности, сушку образцов до постоянной массы, определение в процессе высушивания относительной усадки образцов и последующее определение критической влажности, отличающ тем, что, с целью снижения кости и повышения точности ния, формуют два образца с начальной влажностью и определениеA method for determining the critical humidity of ceramic masses, including forming samples from the mass, measuring their initial humidity, drying the samples to constant mass, determining the relative shrinkage of the samples during drying, and then determining the critical humidity, characterized in that, in order to reduce bone and increase accuracy form, form two samples with initial moisture and determination 1270655 4 критической влажности UKP ведут по формуле1270655 4 critical humidity U KP lead by the formula Um>Um> t2 U, -lt иг где и й с я трудоемопределеразличнойt 2 U, -l t and r where and th with I labor is indefinitely D, - относительная усадка и влажность первого образца, 7', t и U2 - относительная усадка и влажность второго образца,D, is the relative shrinkage and humidity of the first sample, 7 ', t and U 2 is the relative shrinkage and humidity of the second sample, L, иL and Способ-прототипPrototype method Предлагаемый способThe proposed method Крити- Criti Случайная Random Квадрат Square Критичес- Critical Случайная Random Квадрат Square ческая cheskaya погреш- wrong случайной random кая влаж- Kaya wet погреш- wrong случай- happening- влаж- wet ность, nost погреш- wrong ность, nost ность, nost ной по- Noah ность, nost Δ, % Δ ,% ности, nosti UKp , 7>U K p, 7> Λ , 7, Λ, 7, грешное sinful U кр , 7 U cr, 7 — - Δ Л Δ L ти, tee
13,0 13.0 -1,0 -1.0 1,00 1.00 13,3 13.3 -0,8 -0.8 0,64 0.64 13,0 13.0 -1,0 -1.0 1,00 1.00 13,5 13.5 - -0,6 - -0.6 0,36 0.36 13,1 13.1 -0,9 -0.9 0,81 0.81 13,8 13.8 -о,з oo 0,09 0.09 14,1 14.1 +0,1 +0.1 0,01 0.01 14,2 14.2 +0,1 +0.1 0,01 0.01 13,7 13.7 -0,3 -0.3 0,09 0.09 13,0 13.0 -1,1 -1.1 1,21 1.21 15,0 15.0 + 1,0 + 1.0 1,00 1.00 14,8  14.8 +0,7 +0.7 0,49 0.49 15,8 15.8 + 1,8 + 1.8 3,24 3.24 13,7 13.7 . -0,4 . -0.4 0,16 0.16 12,2 12,2 1,8 1.8 3,24 3.24 15,4 15.4 + 1,3 + 1.3 1,69 1,69 14,8 14.8 +0,8 +0.8 0,64 0.64 13,7 13.7 -0,4 -0.4 0,16 0.16 13,1 13.1 -0,9 -0.9 0,81 0.81 14,4 14,4 +0,3 +0.3 0,09 0.09 13,5 13.5 -0,5 -0.5 0,25 0.25 14,1 14.1 0,0 0,0 0,00 0.00 16,0 16.0 + 2,0 + 2.0 4,00 4.00 15,7 15.7 + 1,6 + 1.6 2,56 2,56 13,4 13,4 -0,6 -0.6 0,36 0.36 14,2 14.2 +0,1 +0.1 0,01 0.01 14,1 14.1 +0,1 +0.1 0,01 0.01 13,9 13.9 -0,2 -0.2 0,04 0.04 14,7 14.7 +0,7 +0.7 0,.49 0 .49 14,3 14.3 +0,2 +0.2 0,04 0.04 £209,5 £ 209.5 -0,5 -0.5 16,95 16.95 212,1 212.1 0,5 0.5 7,55 7.55 ВНИИПИ VNIIIPI Заказ Order 6235/45 6235/45 Тираж 778 Circulation 778 Подписное Subscription Произв. Mfr. -полигр. -polyger. пр-тие, production г. Ужгород, Uzhhorod ул. Проектная st. Design , 4 , 4
SU843759792A 1984-06-22 1984-06-22 Method of determining critical moisture content of ceramic mass SU1270655A1 (en)