SU1073705A1 - Construction material humidity determination method - Google Patents
Construction material humidity determination method Download PDFInfo
- Publication number
- SU1073705A1 SU1073705A1 SU823525505A SU3525505A SU1073705A1 SU 1073705 A1 SU1073705 A1 SU 1073705A1 SU 823525505 A SU823525505 A SU 823525505A SU 3525505 A SU3525505 A SU 3525505A SU 1073705 A1 SU1073705 A1 SU 1073705A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- modulus
- elasticity
- weight
- moisture
- construction material
- Prior art date
Abstract
СПОСОБ ОПЙБДЕЛЕНИЯ ВЛАЖНОСТИ СТГОИТЕЛЬНЫХ МАТЕШАЛОВ, включающий высушивание о зазцов до посто нной массы, насыыдение их водой до стабилизации массы и определение весовой влажности на различных эташх водонаолцеии , отличающийс тем, что, с целыо определени влажности в материале конструкции, образцы готов т из материала конструкции, на этапах водоиаолценк определ ют модуль упругости, стро т градуировочную зависимость модуль упругости - весова влажность, измер ют значение модул упругости материала конструкции и по градуировочной зави мости определ ют весовую влажность материала конструкции. (Л сA METHOD OF MEASURING THE MOISTURE OF STEATING MATHESALS, including drying the bristles to a constant mass, filling them with water until the mass is stabilized, and determining the weight moisture in different ethnografts, in order to determine the moisture content in the construction material, the samples are prepared from the construction material, at the stages of water deformation, the modulus of elasticity is determined, a calibration dependence is constructed of the modulus of elasticity — the weight humidity, the value of the modulus of elasticity of the material of the structure is measured, and The weight dependence of the material of the structure is determined by the dependence. (L with
Description
со I10 Изобретение относитс к области строительных материалов, а именно к испытани м материалов , и может быть использовано дл определеин долговечности материалов строительных конструкций и сооружений. Известен способ определени влажности стро ительных материалов, включающий измерение на о газцах определенной формы влажности на различных этапах водонасыщени объемновесовым методом, измерение на тех же зтапах относительной диэлектрической проницаемости образцов, построение гртдуировочной зависимос ти относительна дазлектрическа проницаемос влажность, измерение относительной даэлектри ческой проницаемости в материале конструкции и определение по граудировочной зависимости влажности мате{жала в конструкщш 1. К ведостажам способа относ тс ограниченность его пртменени чеистыми бетонами и бетсжами га пористых заполнител х, а также выс(Жа зависимость точности измерений от влажности и температуры окружакнцей среды. НЫболее близким к изобретению вл етс способ определени влажности строительных ма термалов, включакнций высушивание до шхто нной массы, насьпцение их водой до ;ста&ишзации массы и определение весовой в ажкост Еса различных зтапах водонасыще .ни t2j. (достатсж данного способа состоит в том. что он не позвол ет определить влажносп в материй конструкции. Цель изобретени - определение влажности в nmttftoj конструкции. Цель достигаетс тем, что согласно способу ойределеши влажности строительных материалов , включающему высушивание образцов до постоЗзшой массы, насыщение водой до стабилизащш массы и определение весовой влажности на различных этапах водонасьоцени , образ -. цы готов т из материала конструкции, ,на зтапах водонасьпцени определ ют модуггъ упругости , стро т rpaf npoBOKHyro завиа мость модОль упругости - весова влажностг, измер ют значе}ше модул упругости материала конструкции и по градуировочной ивисимости определ ют весовую влажность материала конструкщш . Способ реализуетс следующим бразом. Изготавливают образец из материала конcrpyKiQiH , высушивают до посто нной массы. Определ ют модуль упругости материала образца любым из известных способов, например по скорости распространени продольных ультразвуковьгх волн. Далее образец подвергают водонасыщению. На различных этапах насыщени вплоть до стабилизапзни массы образца определ ют влажность материала объемно-весовым методом и его модуль упругости. По результатам измерений стро т градуировочную зависимость модуль упругости - весова влажность. Прин тым ранее методом (в данном случае ультразвуковым) измер ют модуль упругости материала конструкции. По полученному зна «;нию модул упругости и градунровочной зависимости определ ют значение весовой влажности материала конструкции. t Преимущество предлагаемого способ заключаетс в возможности оперативного контрол влажности конструкции по заранее построенной градуировочной зависимости с достаточной дл практики эксплуатации тошостью.I10 The invention relates to the field of building materials, namely to testing materials, and can be used to determine the durability of materials of building structures and structures. There is a known method for determining the moisture content of building materials, which includes measuring some form of moisture at various stages of water saturation using the volume-balance method, measuring the relative dielectric constant of samples on the same stages, building a calibration curve for relative humidity, measuring relative dielectric permeability in the construction material and the determination of the dependence of the moisture content of mate {sting in construction 1. To the Vedostazham Sob relates to the limitations of its use with cellular concretes and bets heaps of porous aggregates, as well as high (The dependence of measurement accuracy on humidity and temperature of the surrounding medium. The closer to the invention is a method for determining the moisture of building materials, including drying to ground mass, water saturation of them up to one hundred and ampholes of mass and determination of the weight in azhkost of Esa in various stages of water-saturated or t2j. (the availability of this method is that. that it does not allow to determine wet in the matter of construction. The purpose of the invention is to determine the humidity in the nmttftoj structure. The goal is achieved by the fact that according to the method of determining moisture of building materials, including drying the samples to a constant mass, saturating water to a stable mass, and determining the weight moisture at various stages of water concentration, the image is. These are prepared from the material of the structure, on the stages of the water flow, the modulus of elasticity is determined, the rpaf npoBOKHyro dependence of the elastic modulus — the weight humidity — is measured, the elastic modulus of the construction material is measured and the weight humidity of the material of the structure is determined from the calibration modulus. The method is implemented as follows. Make a sample of material koncrpyKiQiH, dried to constant weight. The elastic modulus of the sample material is determined by any of the known methods, for example, by the speed of propagation of longitudinal ultrasonic waves. Next, the sample is subjected to water saturation. At different stages of saturation, until the sample mass is stabilized, the moisture content of the material is determined by the volume-weight method and its modulus of elasticity. According to the measurement results, a calibration dependence of the modulus of elasticity — weight humidity is constructed. The method previously adopted (in this case, ultrasonic) measures the elastic modulus of the material of construction. From the obtained value of the modulus of elasticity and gradient dependence, the value of the weight humidity of the material of the structure is determined. t The advantage of the proposed method is the ability to quickly control the moisture content of a structure according to a pre-built calibration dependence with sufficient nausea for the practice of operation.
Claims (1)