SU1194936A1 - Method of preparing cellulose-containing semi-finished material to manufacturing of adsorbing layer of paper sanitary articles - Google Patents
Method of preparing cellulose-containing semi-finished material to manufacturing of adsorbing layer of paper sanitary articles Download PDFInfo
- Publication number
- SU1194936A1 SU1194936A1 SU843757573A SU3757573A SU1194936A1 SU 1194936 A1 SU1194936 A1 SU 1194936A1 SU 843757573 A SU843757573 A SU 843757573A SU 3757573 A SU3757573 A SU 3757573A SU 1194936 A1 SU1194936 A1 SU 1194936A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- containing semi
- manufacturing
- finished product
- cellulose
- finished material
- Prior art date
Abstract
1. СПОСОБ ПОДГОТОВКИ ВОЛОКНИСТОГО ЦЕЛЛКШОЗОСОДЕРЖАЩЕГО ПОЛУФАБРИКАТА ДЛЯ ИЗГОТОВЛЕНИЯ АДСОРБИРУЮЩЕГО СЛОЯ БУМАЖНЫХ ИЗДЕЛИЙ САНИТАРНОГИГИЕНИЧЕСКОГО НАЗНАЧЕНИЯ путем обработки исходной суспензии полуфабриката раствором алкилбензилдиметиламмоний хлорида, последующего отлива обработанной суспензии на пресс-пате, сушки и сухого размола, отличающийс тем, что, с целью. улучшени гигиенических свойств изделий за счет снижени инициальной контаминации и повышени впитывающей способности целевого продукта, обработку суспензии осуществл ют в присутствии щелочного реагента при рН 7,0-8,5. 2. Способ по п. 1, о тли ч а ю- с S щ и и с тем,что в качестве реагента используют едкий натр,углекислый нат (Л рий или их смесь.1. METHOD OF PREPARATION improving the hygienic properties of the products by reducing the initial contamination and increasing the absorbency of the target product; the suspension is processed in the presence of an alkaline reagent at pH 7.0-8.5. 2. The method according to p. 1, about aphids and u- with S y and with the fact that as the reagent is used caustic soda, sodium carbonate (Li or their mixture.
Description
со with
соwith
О Изобретение относитс к целлкиюз но-бумажной промышленности и касает прпнзводства волокнистого полуфабри ката дл изготовлени адсорбирующег сло многослойных бумажных изделир. 11ель изобретени - улучшение гигие нических свойств изделий за счет сниже ни инициальной контаминации и повышени впитывающей способности целевого продукта. В сачестве щелочного реагента ис :i:;)j;L3yioT едкий натр, углекислый нат рий или их смесь. Алкилбензилдиметиламмоний хлорид (Катамин АБ) имеет эмпирическую фор мулу (С,., Hj, N+ Щ-) ) CL-, гп.е п 10-18. Получение волокнистого полуфабриката дл изготовлени адсорбирующего сло санитарно-гигие iiUiecKHx изделий при рН 7,0-8,5 с применением обработки волокнистой суспензии раствором Катамина АБ в присутствии щелочного реагента веде к повь иению впитывающей способности (скорости впитывани ) и уменьшению (шициальной контаминации изделий санитарно-гигиенического назначени Обработка волокнистой суспензии раствором Катамина АБ в кислой среде приводит к снижению впитывающей сг;особиости (скорости впитывани ) целевого продукта, а обработка, при рП больше чем 8,5 ведет к получению изделий санитарно-гигиенического наз начени , вызывающих раздражающее и общетоксическое действие. В качестве исходного сырь дл по лучени волокнистого полуфабриката слользуют целлюлозу сульфитную, хвойную беленую или ее смесь с древесной массой Изобретение иллюстрируетс следуюпдами примерами. Пример 1. ВолокнистьШ целлюлозосодержащий полуфабрикат готов т следующим образом. Сульфитную белёную хвойную целлюлозу распускают и подвергают обработке Катамином АБ в количестве 0,5% к массе а.с. волок ira, Роспуск осуществл ют при концент рации 1,5 в течение 15 мин. Затем суспензию разбавл ют до к.онцентрации 0,3% и добавл ют NaOH до рН 7,0. Отлив , прессование и сушку провод т стандартными методами. Затем полуфабрикат подвергают сухому размолу и определ ют впитывающую способность Инициальную контаминацию определ ют по следующей методике. Навеску исследуемого материала весом 1,0 г погружают в колбы с 50 мл стерильного физиологического раствора,, отбалтывак )т в течение 10 мин и фильтруют через мембранные фильтры с последующим посевом мембранного фильтра на поверхность м сопептонного агара. Посевы помещают втермостат при температуре 32°С и выдерживают 48 ч.. Через 48 ч подсчитывают количество выросших колоний и рассчитывают инициальную контаминацию на 1,0 г материала . П р и м е р 2. Волокнистый целлюлозосодержащий полуфабрикат готов т следующим образом. Смесь сульфитной беленой целлюлозы (75%) и древесной массы (25) распускают и подвергают обработке Катамином АБ в количестве 0,5% к массе а.с.волокна в присутствии Na СО, до рН 8,0. Отлив, прессование и сушку провод т стандартным методом. Полуфабрикат после сухого размола испытывают. . Пример 3. Волокнистый целлюлозосодержащий полуфабрикат готов т следующим образом. Сульфитную беленую хвойную целлюлозу распускают в присутствии Катамина АБ в количестве 0,5% к массе а.с. волокна. Роспуск осуществл ют при концентрации 1,5% в течение 15 мин. Затем разбавл ют до концентрации 0,3% и добавл ют смесь NaOH и Na2COj(в соотношении смеси 1:1) до рН 8,5. Пример 4. Волокнистый целлюлозосодержащий полуфабрикат готов т следующим образом. Сульфитную беленую хвойную целлюлозу распускают в присутствии Катамина АБ в количестве 0,5% к массе а.с.волокна. Роспуск осуществл ют при концентрации 1,5% в течение 15 мин. Затем разбавл ют до концентрации 0,3% и добавл ют AL2( до рН 4,5 (стандартный показатель, при котором осуществл етс отлив). Пример 5. Волокнистый целлюпозосодержащий полуфабрикат готов т следующим образом. Сульфитную беленую хвойную целлюлозу распускают в присутствии Катамина АБ в количестве 0,5% к массе а.с.волокна. Роспуск осу1цествл ют при концентрации 1,5% в течение 15 мин. Затем разбавл ют до концентрации 0,3% и добавл ют NaOH до рН 9,2. Пример 6. Волокнистый целлкшозосодержащий полуфабрикат готов т следунлщм образом. Сульфитную бе31O The invention relates to cellulose paper industry and concerns the production of fiber prefabricated kata for the manufacture of an adsorbent layer of multi-layer paper products. The goal of the invention is to improve the hygienic properties of the products by reducing the initial contamination and increasing the absorbency of the target product. As an alkaline reagent, is: i:;) j; L3yioT caustic soda, sodium carbonate, or their mixture. Alkylbenzyldimethylammonium chloride (Katamin AB) has the empirical formula (C,., Hj, N + U), CL-, g. P. 10-18. Obtaining a fibrous semi-finished product for the manufacture of an adsorbent sanitary-hygiene layer of iiUiecKHx products at pH 7.0-8.5 using a fibrous suspension treatment with Catamine AB solution in the presence of an alkaline reagent leads to an increase in absorbency (absorption rate) and a decrease (sanitary contamination of sanitary products - Hygienic Purpose The treatment of a fibrous suspension with a solution of Catamine AB in an acidic medium leads to a decrease in the absorption of cr; the individuality (absorption) of the target product, and the treatment, at P more than 8.5 leads to the production of sanitary and hygienic products that cause irritant and general toxic effects. Sulphite, softwood bleached pulp or its mixture with wood pulp is used as a raw material for obtaining a fibrous semi-finished product. Example 1 Fiber cellulose-containing semi-finished product is prepared as follows: Sulphite bleached softwood pulp is dissolved and subjected to treatment with Katamin AB in an amount of 0.5% by weight a.s. Fiber ira, Dissolution is carried out at a concentration of 1.5 for 15 minutes. The suspension is then diluted to a concentration of 0.3% and NaOH is added to a pH of 7.0. Reflux, pressing and drying are carried out by standard methods. Then, the semi-finished product is subjected to dry grinding and the absorption capacity is determined. Initial contamination is determined according to the following procedure. A weighed portion of the test material weighing 1.0 g is immersed in flasks with 50 ml of sterile saline solution, spat out for 10 minutes and filtered through membrane filters with subsequent sowing of the membrane filter onto the surface of m sopeptone agar. Crops are placed in a thermostat at a temperature of 32 ° C and incubated for 48 hours. After 48 hours, the number of grown colonies is counted and initial initial contamination is calculated for 1.0 g of the material. PRI mme R 2. A fibrous cellulose-containing semi-finished product is prepared as follows. A mixture of bleached sulphite pulp (75%) and wood pulp (25) is dissolved and subjected to treatment with Katamin AB in the amount of 0.5% by weight of a.s. fiber in the presence of Na CO, to a pH of 8.0. Reflux, pressing and drying are carried out by a standard method. The semi-finished product after dry grinding is tested. . Example 3. A fibrous cellulose-containing semi-finished product is prepared as follows. Sulphite bleached softwood pulp is dissolved in the presence of Catamine AB in an amount of 0.5% by weight of a.s. the fibers. Dissolution is carried out at a concentration of 1.5% for 15 minutes. Then it is diluted to a concentration of 0.3% and a mixture of NaOH and Na2COj (in a 1: 1 mixture ratio) is added to a pH of 8.5. Example 4. A fibrous cellulose-containing semi-finished product is prepared as follows. Sulphite bleached coniferous cellulose is dissolved in the presence of Catamine AB in the amount of 0.5% by weight of a.s.of fiber. Dissolution is carried out at a concentration of 1.5% for 15 minutes. Then it is diluted to a concentration of 0.3% and AL2 is added (to a pH of 4.5 (the standard at which reflux is effected). Example 5. A cellulose-fibrous semi-finished product is prepared as follows. Bleached softwood sulphite pulp is dissolved in the presence of Katamine AB in the amount of 0.5% by weight of the A. of the fiber. Dissolution is carried out at a concentration of 1.5% for 15 minutes, then diluted to a concentration of 0.3% and NaOH is added to a pH of 9.2. Example 6. Fibrous cellulose-containing semi-finished product is prepared as follows.
леную хвойную целлюлозу распускают в присутствии Катамина ЛБ в кпличестве 0,5% к массе .а,с,волокна. Роспуск осуществл ют при концентрации 1,5% в течение 15 мин. Затем разбавл ют до концентрации 0,3% и довод т рН до 6,3,Coniferous pine cellulose is dissolved in the presence of Katamin LB in the clientele 0.5% by weight. a, c, fiber. Dissolution is carried out at a concentration of 1.5% for 15 minutes. It is then diluted to a concentration of 0.3% and the pH is adjusted to 6.3,
Пример. Волокнистый целлкшозосодержащий полуфабрикат готов т следующим образом. Сульфитную беленую хвойную целлюлозу распускают при концентрации 1,5% в течение 15 мин. Затем разбавл ют до концент949364Example. Fibrous cellulose-containing semi-finished product is prepared as follows. Bleached softwood sulphite pulp is dissolved at a concentration of 1.5% for 15 minutes. It is then diluted to concentrate.
рации 0,3%. Химические вспомогательные вещества .не используют.с .walkie talkies 0.3%. Chemical excipients. Not used.
Пример 8. Волокнистый целлюлозосодержащий полуфабрикат готов т следующим образом.Сульфитную беленую хвойную целлкшозу распускают в присутствии алкилдиметилбензиламмоний хлорида в количестве Q,,5% к массе а.с. волокна.Роспуск осуществл ют при концентрации 1,5% в течение 15 мин. Затем разбавл ют до концентрации 0,3%. Результаты испытаний по примерам 1-8 представлены в таблице.Example 8. The fibrous cellulose-containing semi-finished product is prepared as follows. The bleached softwood sulphite cellulose is dissolved in the presence of alkyl dimethyl benzyl ammonium chloride in an amount of Q ,, 5% by weight a.s. fibers. The passage is carried out at a concentration of 1.5% for 15 minutes. It is then diluted to a concentration of 0.3%. The test results for examples 1-8 are presented in the table.
0,01 % 7 ,5 100,2 520.01% 7, 5 100.2 52
0,040.04
i,1 - 100,2 53i, 1 - 100.2 53
Смесь NaOH и A mixture of NaOH and
0,03 8,5 101,1 520.03 8.5 101.1 52
5,85.8
2525
25+325 + 3
5,75.7
2424
20+320 + 3
5,95.9
2525
25+325 + 3
Claims (2)