SU1076317A1 - Carbon paper coating composition - Google Patents
Carbon paper coating composition Download PDFInfo
- Publication number
- SU1076317A1 SU1076317A1 SU823530688A SU3530688A SU1076317A1 SU 1076317 A1 SU1076317 A1 SU 1076317A1 SU 823530688 A SU823530688 A SU 823530688A SU 3530688 A SU3530688 A SU 3530688A SU 1076317 A1 SU1076317 A1 SU 1076317A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- wax
- montan
- coating
- oil
- iron oxide
- Prior art date
Abstract
СОСТАВ.ПОКРЫТИЯ КОПИРОВАЛЬг НОЙ БУМАГИ, содержащий сажу, моногиддаат окиси железа, индулин, краситель метилфиолетовый, воск-монтан сьфой, воск-монтаи отбеленный, пара-, фин, масло, олеиновую кислоту, о тличающийс тем, что,с целью снижени отмарывани , сокращени времени приготовлени покрыти , и снижени в зкости расплава покрыти при 85-100с, он дополнительно содержит натрийбутадиеновый каучук с пластичностью 0,62-0,66 при следующем соотношении компонентов, мас.%: 17,0-18,0 Сажа Моногидрат 5,0-6,0 окиси железа 0,8-1,2 Индулин Краситель 2,0-3,0 метилфиолетовый Воск-монтан 18,0-20,0 сырой Воск-монтан (Л 14,8-17,6 отбеленный 3,0-4,0 Парафин 28,0-33,0 . лМасло Олеинова 3,0-4,0 кислота Натрийбутади0 ,6-1,0 еновый каучук о:) COMPOSITION OF COPYING OF PAPER'S COPY, containing soot, monoxide of iron oxide, indulin, methyl violet dye, wax-montan, bleaching wax, para-, fin, oil, oleic acid, characterized in that, in order to reduce marking, reduce the time of preparation of the coating, and reduce the viscosity of the melt coating at 85-100s, it additionally contains sodium butadiene rubber with a plasticity of 0.62-0.66 in the following ratio of components, wt.%: 17-18-18.0 Soot Monohydrate 5, 0-6,0 iron oxide 0.8-1.2 Indulin Dye 2.0-3.0 methylf Purple Wax-montan 18.0–20.0 crude Wax-montan (L 14.8–17.6 bleached 3.0–4.0 Paraffin 28.0–33.0. l Oil Oleinov 3.0–4.0 Acid Sodium Butadi, 6-1.0 ene rubber o :)
Description
Изобретение относитс к производству копировальной бумаги и может быть использовано в целлюлознобумажной промышленности при изготовленци копировальной бумаги много разового использовани дл мaшинo ., писи. Известен состав покрыти копировальной бумаги многоразового исполь зовани дл машиЬописи, содержащий сажу, моногидрат окиси железа, краситель фиолетовый диоксазиновый, краситель метилфиолетовый, воск-мон тан, вазелин, воск полиэтиленовый окисленный, сополимер этилена с винилацетатом , касторовое масло, олеи новую кислоту l . Однако такой состав не обеспечивает получени качественных копий при одновременном копировании. Наиболее близким к предлагаемому по достигаемому положительному эффекту вл етс состав покрыти копировальной бумаги, содержащий са жу, моногидрат окиси железа, индули краситель метилфиолетовый, воск-мон тан сырой, воск-монтан отбеленный, парафин, масло, олеиновую ки слоту при следующем соотношении компонентов , мас.%: сажа 14,0-16,0, моногид рат окиси железа 4,0-8,0, краситель 2,5-3,5, воск-монтан сырой 14, 18,5, воск-монтан отбеленный 16,520 ,5; парафин 3,5-7,0, масло 25,038 ,0, олеинова кислота 3,5-7,0 И Однако копировальна бумага, изг товленна с известным составом, име ет повышенное отмарывание, а сам со тав покрыти нетехнологичен. Он тре бует длительного перетира пигмента и обладает высокой в зкостью распла ва, что затрудн ет его применение в промышленных услови х, в частности затруднена перекачка расплава по рыти насосами и регулировка толщивы .покрыти , нарушаетс однородност покрыти вследствие кристаллизации покрыти при температурах ниже При хранении расплава наблюдаетс выделение частиц сажи. Цель изобретени - снижение отмарывани , сокращение времени приготов лени покрыти , снижение в зкости расплава покрыти при 85-100с. Поставленна цель достигаетс тем, что состав покрыти копировальной бумаги, содержащий сажу, моногидрат окиси железа, индулин, краситель метилфиолетовый, воск-монтан сырой, воск-монтан отбеленный, парафин , масло, олеиновую кислоту, дополнительно содержит натрийбутадиеновый каучук с пластичностью 0,620 ,66 при следующем соотношении компонентов , мас.%: Сажа 17,0-18,0 Моногидрат окиси железа 5,0-6,0 Индулин 0,8-1,2 Краситель метил фиолето-1 вый2,0-3,0 Воск-монтан сырой 18,0-20,0 Воск-монтан отбеленный 14,8-17,6 Парафин . 3 ,0-4 ,0 Масло 28,0-33,0 Олеинова кислота 3,0-4,0 Натрийбутадиеновый каучук 0,6-1,0 Используемый каучук представл ет собой высокомолекул рный твердый продукт полимеризации бутадиена в присутствии металлического натри , имеет пластичность 0,62-0,66 и молекул рную массу 1,7-105 - 1,9-10, В качестве сажи используют печную низкоструктурную сажу марок ПГМ-33Н и ПМ-40 Н с удельной условной поверхностью 28-33 , получаемую при термоокислительном разложений масл ного (ПМ-4ОН) или газомасл ного (ПГМ-33 Н) сырь . В качестве воска-монтана отбеленного используют воск-монтан дважды отбеленный, В качестве масла может быть испсйпьзовано индустриальное или касторовое масла. , Парафин может быть заменен озокеритом или церезином, В изобретении используют моногидрат окиси железа желтого цвета. При сочетании сажи,и моногидрата окиси железа в присутствии натрийбутадиенового каучука происходит процесс модификации сажи, в результате чего образуетс пигмент с новыми характеристиками, обеспечивающими снижение в зкости краски и отмарывани копировальной бумаги. Пример 1,.В емкость, снаб-.; женную рубашкой и мешалкой г загружают олеиновую кислоту и при перемешивании обезвоживают при 95-100с до прекращени вспенивани , затем постепенно добавл ют красители и продолжают перемешивание около 4 ч. На установке с магнитным смесителем готов т сажевую пасту, содержащую , мас,%: сажа ПГМ-33 Н 32,7, масло индустриальное И 20 А 55,9, железоокисный пигмент 9,9, натрийбутадиеновый каучук (пластичностью 0,66) 1,5, с дисперсностью частиц 5-10 мкм, В реактор, снабженный рубашкой и мешалкой, загружают воск-монтан сырой, воск-монтан отбеленный, парафин . Смесь расплавл ют и к полученному расплаву при перемешивании добавл ют сажевую пасту и раствор красите;|ей. Затем массу перемеривают при 100-110 С в течение 1,5ч,. Получают состав карбонового покрыти , содержащий, мас.%: сажа 17,8, моногидрат окиси железа 5,4, краситель метилфиолетовый 2,5} индулин 1,0 воск-монтат сырой 18,5, воск-монтан отбеленный 16,5, парафин 3,0, масло индустриальное 26,0, масло касторовое 5,0, кислота олеинова 3,5, натрийбутадиеновый -каучук 0,8, Полученный расплав подают на краскотерку и перетирают один раз, Приготовленные карбоновие покрыти нанос т на бумагу-основу массой 1 м 16 г при 90°С на красконанос щей машине с помощью проволочного шабера. Величина наноса 11 г/м Получают образцы черной копировальной бумаги, которые испытывают по ГОСТ 489-66 на электромеханической пишущей машине Ятрань на коли чество одновременных и последовател ных оттисков. Так же определ ют отмарывание копировальной бумаги, оценива его по оптической плотности следа, который получают на специальном приборе . Дл этого перемещают копировальную бумагу, наход щуюс в контакте с воспринимающей бумагой под нагрузкой цилиндрической головки диаметром 20 мм, которые не пере мещаютс . Покрытие отличаетс высокой стабильностью расплава, перекачи ватьс обогреваемыми насосами и не кристаллизуетс при снижении темпер туры красконанос щих валов до85с. Пример2. Состав покрыти , указанный в примере 1, приготовл ют путем смешивани раствора красителе в олеиновой кислоте, пасты техуглерода , содержащей, мас.%: сажа марки ПМ-4ОН 36,3, индустриальное масло И 20 А 62,1/ натрий-утадиеновый каучук пластичностью 0,66) 1,6 и моногидрат окиси железа 5,4, пере мешивани в течение 3 ч и последую ,щего однократного перетира на краскотерке . Получение и испытание копироваль ной бумаги, как в примере 1. Пример 3. Состав покрыти , содержащий, мас.%: сажа ПГМ« 33 Н18 железоокисный пигмент 5,0 красител метилфиолетовый жирорастворимый 2,0 индулин 1,2, воск-монтан сырой 18,0 воск-монтан отбеленный 14,8, парафин 4,0, масло индустриальное 27,0, масло касторовое 6,0, олеинова кис лота 3,0, натрийбутадиеновый каучук (с пластичностью 0,64) 1,0, Копировальную бумагу с этим покрытием изготавливают аналогично примеру 1, Показатели копировальной бума ги: число одновременных оттисков 8, число последовательных оттисков 18, отмарывание 0,18. П р и JM е р 4, покрыти . Содержащий, мас,%: сажа ПГМ-ЗЗН 17,0, железоокисный пигмент 6,0, краситель метилфиолетовый жирорастворимый 3,0, индулин 0,8, воск-монтан сырой 20,0, воск-Сонтан отбеленный 17,6, парафин 3,0, масло индустриальное 28,0, кислота олеинова 4,0, натрийбутадиеновый каучук (пластичностью 0,62) i 0,6.-Копировальную бумагу с этим . . покрытием изготавливают аналогично примеру 1. Показатели копировальной бумаги: число одновременных оттисков 8, число последовательных оттисков 15, отмарывание 0,15. Пример 5 (прототип).Согласно примеру 1 приготовл ют состав покрыти копировалеьной бумаги, содержащий , мас.%: сажа 16,0j моногидрат окиси железа 8,0краситель метилфиолетовый 2,5; индулин 1,Оjвоскмонтан сырой 17,5; воск-монтан отбеленный 16,5, парафин 3,5; масло индустриальное марки И 20 А 26,5, масло касторовое 5,0; кислота олеинова 3,5. Копировальную бумагу изготавливают согласно примеру 1. Результаты испытаний бумаги представлены в таблице. Увеличение количества сажи или моногидрата окиси железа приводит к повышению в зкости расплава покрыти , к тому же результату приводит уменьшение количества масла или парафина в предлагаемом составе покрыти . При снижении содержани сажи, моногидрата окиси железа или красителей наблюдаетс падение оптической плотности получаемых оттисков. Повышение содержани красителей, масла, парафина или олеиновой кислоты увеличивает отмарывание копировального покрыти бумаги. При уменьшении количества олеиновой кислоты ухудшаетс растворение в ней используемых красителей. Увеличение в составе покрыти количества сырого воска-монтана, парафина или уменьшение количества отбеленного воска-монтана ухудшает качество последовательных оттисков, а уменьшение количества сырого воска-монтана или увеличение количества отбеленного воска-монтана ухудшает качество одновременных оттисков. Использование натрийбутадиенового каучука в меньших количествах не.позвол ет достигнуть снижени отмарывани и в зкости расплава покрыти . Повышение количества натрийбутадиеноBoro каучука нецелёсобвразво Bcnejgg вие ухудшени копировальных свойств бумаги.The invention relates to the production of carbon paper and can be used in the pulp and paper industry in the manufacture of carbon paper for many times using for machine, writing. A reusable copying paper coating composition is known for containing carbon black, iron oxide monohydrate, violet dioxazine dye, methyl violet dye, wax montan, petroleum jelly, polyethylene oxidized wax, ethylene-vinyl acetate copolymer, castor oil, new acid l. However, such a composition does not provide high-quality copies while copying. Closest to the proposed positive effect achieved is a copier paper coating composition containing carbon dioxide, iron oxide monohydrate, induced methyl violet dye, crude wax montan, bleached wax montan, paraffin oil, oleic acid in the following ratio of components, wt.%: carbon black 14.0-16.0, iron oxide monohydrate 4.0-8.0, dye 2.5-3.5, raw wax 14, 18.5, bleached wax-montan 16.520, five; paraffin 3.5-7.0, oil 25.038, 0, oleic acid 3.5-7.0, And However, copying paper made with a known composition has an improved mark-off, and the coating itself is non-technological. It requires a long peretir of pigment and has a high viscosity of the melt, which makes it difficult to use in industrial conditions, in particular, it is difficult to transfer the melt to rut with pumps and adjust the thickness of the coating, the coating homogeneity is disturbed due to crystallization of the coating at lower temperatures. soot particles are observed. The purpose of the invention is to reduce stamping, shorten the preparation time of the coating, decrease the viscosity of the coating melt at 85-100s. The goal is achieved by the fact that the coating composition of carbon paper containing soot, iron oxide monohydrate, Indulin, methyl violet dye, raw wax-montan, bleached wax-montan, paraffin, oil, oleic acid, additionally contains sodium butadiene rubber with a plasticity of 0.620, 66 at the following ratio of components, wt.%: Soot 17.0-18-18.0 Iron oxide monohydrate 5.0-6.0 Indulin 0.8-1.2 Methyl violet-1 dye 2.0-3.0 Wax montan crude 18.0-20.0 Wax-montan bleached 14.8-17.6 Paraffin. 3, 0-4, 0 Oil 28.0-33.0 Oleic acid 3.0-4.0 Sodium-butadiene rubber 0.6-1.0 The rubber used is a high molecular weight solid polymerization product of butadiene in the presence of metallic sodium, has plasticity of 0.62-0.66 and a molecular weight of 1.7-105 - 1.9-10. As a carbon black, low-structural furnace soot of the marks ПГМ-33Н and ПМ-40 Н with a specific conditional surface 28-33, obtained with thermal oxidative decomposition of oil (PM-4ON) or gas-oil (PGM-33 N) raw material. As montan wax bleached, montan wax twice bleached is used. Industrial oil or castor oil can be used as an oil. Paraffin may be replaced by ozocerite or ceresin. The invention uses yellow iron oxide monohydrate. With the combination of carbon black and iron oxide monohydrate in the presence of sodium butadiene rubber, the process of carbon black modification takes place, resulting in a pigment with new characteristics that reduce the viscosity of paint and mark paper. Example 1. In a container; Oleic acid is loaded with a jacket and a stirrer g and stirred at 95-100s with stirring until the foaming stops, then dyes are gradually added and stirring is continued for about 4 hours. A carbon black paste is prepared with a magnetic mixer; -33 N 32.7, industrial oil AND 20 A 55.9, iron oxide pigment 9.9, sodium butadiene rubber (plasticity 0.66) 1.5, with a dispersity of particles of 5-10 microns, In a reactor equipped with a jacket and an agitator, load wax montan crude, wax montan bleached paraffin. The mixture is melted and a soot paste is added to the resulting melt with stirring, and the solution is colored; Then the mass is measured at 100-110 C for 1.5 hours ,. A carbon coating composition is obtained, containing, in wt%: carbon black 17.8, iron oxide monohydrate 5.4, methyl violet dye 2.5} indulin 1.0 crude wax 18.5, bleached wax montan 16.5, paraffin 3.0, industrial oil 26.0, castor oil 5.0, oleic acid 3.5, sodium butadiene rubber-0.8, The resulting melt is fed to the paint mill and rubbed once, the prepared carbon coating is applied to the base paper with a mass of 1 m 16 g at 90 ° C on a spray gun using a wire scraper. The size of the pump is 11 g / m. Samples of black copy paper are obtained, which are tested in accordance with GOST 489-66 on the Yatran electromechanical typewriter for the number of simultaneous and consecutive prints. The marking of the copy paper is also determined by estimating it from the optical density of the trace, which is obtained on a special instrument. To this end, transfer paper is transferred that is in contact with the receiving paper under the load of a cylindrical head with a diameter of 20 mm, which does not move. The coating is characterized by high melt stability, pumped by heated pumps, and does not crystallize when the temperature of the paint roller shafts decreases to 85 °. Example2. The coating composition specified in example 1 was prepared by mixing a dye solution in oleic acid, a paste of technical carbon containing, in wt.%: Carbon black PM-4OH 36.3, industrial oil AND 20 A 62.1 / sodium utadiene rubber plasticity 0.66) 1.6 and iron oxide monohydrate 5.4, stirring for 3 hours and the subsequent single grinding in the spray mill. Obtaining and testing copying paper as in Example 1. Example 3. Coating composition containing, in wt%: carbon black “33 H18 carbon black iron oxide pigment 5.0 dye methyl violet fat soluble 2.0 Indulin 1.2, wax-montan crude 18 , 0 wax-montan bleached 14.8, paraffin 4.0, industrial oil 27.0, castor oil 6.0, oleic acid 3.0, sodium butadiene rubber (with a plasticity of 0.64) 1.0, Copy paper with this coating is made analogously to example 1, Indicators of carbon paper: the number of simultaneous prints 8, the number of consecutive Skov 18 otmaryvanie 0.18. PRI JMer 4, cover. Containing, wt.%: Carbon black PGM-ZZN 17.0, iron oxide pigment 6.0, dye methyl-violet, fat-soluble 3.0, indulin 0.8, wax-montan crude 20.0, wax-Sontan bleached 17.6, paraffin 3 , 0, industrial oil 28.0, oleic acid 4.0, sodium butadiene rubber (plasticity 0.62) i 0.6. - Copy paper with this. . coated make analogously to example 1. Indicators of carbon paper: the number of simultaneous prints 8, the number of consecutive prints 15, mark out 0.15. Example 5 (prototype). According to example 1, a copy paper coating composition is prepared containing, in wt%: carbon black 16.0 j ferric oxide monohydrate 8.0 dye methyl-violet 2.5; Indulin 1, Ojvoskmontan crude 17.5; montan wax bleached 16.5, paraffin wax 3.5; industrial oil brand And 20 A 26.5, castor oil 5.0; oleic acid 3,5. Copy paper made according to example 1. The results of the test paper are presented in the table. Increasing the amount of carbon black or iron oxide monohydrate leads to an increase in the melt viscosity of the coating, and the result is a decrease in the amount of oil or paraffin in the proposed coating composition. With a decrease in the content of carbon black, iron oxide monohydrate or dyes, a decrease in the optical density of the resulting prints is observed. Increasing the content of dyes, oil, paraffin or oleic acid increases the marking of the copying paper. With a decrease in the amount of oleic acid, the dissolution of the dyes used in it deteriorates. Increasing the amount of raw montan wax, paraffin or reducing the amount of bleached montan wax in a coating composition worsens the quality of consecutive prints, and reducing the amount of raw montan wax or increasing the amount of bleached montan wax worsens the quality of simultaneous impressions. The use of sodium butadiene rubber in smaller quantities does not allow for the reduction of mark-off and melt viscosity of the coating. Increasing the amount of sodium butadiene Boro rubber does not make Bcnejgg a deterioration in the copying properties of paper.
Как видно из приведенных данных, крпировальна бумага с предлагаемым покрытием имеет более низкое отмарывание и пониженную в зкость карбоно ,вого покрыти по сравнению с прото- ; типом, что обеспечивает улучшение. качества копий и повыиает технологичность процесса изготовлени копировальной бумаги.As can be seen from the above data, the coping paper with the proposed coating has a lower mark out and a lower viscosity of the carbon coating than the prototype; type that provides improvement. copy quality and improves the manufacturability of the process of making copy paper.
по и by and
36,236.2
Число одновременных оттисковThe number of simultaneous prints
Число последовательных оттисков 18Number of consecutive impressions 18
Отмарывание, ед. оптической плотности 0,20 0,20Mark up, units optical density 0.20 0.20
36,236.2
46,246.2
86,486.4
42,242.2
1818
1818
1515
0,15 0,230.15 0.23
0,180.18
Claims (1)