SK109695A3 - The bonding of bodies of refractory hard materials with the carbonaceous base - Google Patents

The bonding of bodies of refractory hard materials with the carbonaceous base Download PDF

Info

Publication number
SK109695A3
SK109695A3 SK1096-95A SK109695A SK109695A3 SK 109695 A3 SK109695 A3 SK 109695A3 SK 109695 A SK109695 A SK 109695A SK 109695 A3 SK109695 A3 SK 109695A3
Authority
SK
Slovakia
Prior art keywords
bodies
slurry
colloidal
electrolyzer
cathode
Prior art date
Application number
SK1096-95A
Other languages
English (en)
Slovak (sk)
Inventor
Jainagesh A Sekhar
Original Assignee
Moltech Invent Sa
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Moltech Invent Sa filed Critical Moltech Invent Sa
Publication of SK109695A3 publication Critical patent/SK109695A3/sk

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/64—Burning or sintering processes
    • C04B35/65—Reaction sintering of free metal- or free silicon-containing compositions
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
    • C04B35/10—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on aluminium oxide
    • C04B35/111—Fine ceramics
    • C04B35/117—Composites
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/515—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics
    • C04B35/58—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics based on borides, nitrides, i.e. nitrides, oxynitrides, carbonitrides or oxycarbonitrides or silicides
    • C04B35/5805—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics based on borides, nitrides, i.e. nitrides, oxynitrides, carbonitrides or oxycarbonitrides or silicides based on borides
    • C04B35/58064—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics based on borides, nitrides, i.e. nitrides, oxynitrides, carbonitrides or oxycarbonitrides or silicides based on borides based on refractory borides
    • C04B35/58071—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics based on borides, nitrides, i.e. nitrides, oxynitrides, carbonitrides or oxycarbonitrides or silicides based on borides based on refractory borides based on titanium borides
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B37/00—Joining burned ceramic articles with other burned ceramic articles or other articles by heating
    • C04B37/003—Joining burned ceramic articles with other burned ceramic articles or other articles by heating by means of an interlayer consisting of a combination of materials selected from glass, or ceramic material with metals, metal oxides or metal salts
    • C04B37/005—Joining burned ceramic articles with other burned ceramic articles or other articles by heating by means of an interlayer consisting of a combination of materials selected from glass, or ceramic material with metals, metal oxides or metal salts consisting of glass or ceramic material
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B41/00—After-treatment of mortars, concrete, artificial stone or ceramics; Treatment of natural stone
    • C04B41/009—After-treatment of mortars, concrete, artificial stone or ceramics; Treatment of natural stone characterised by the material treated
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B41/00—After-treatment of mortars, concrete, artificial stone or ceramics; Treatment of natural stone
    • C04B41/45—Coating or impregnating, e.g. injection in masonry, partial coating of green or fired ceramics, organic coating compositions for adhering together two concrete elements
    • C04B41/50—Coating or impregnating, e.g. injection in masonry, partial coating of green or fired ceramics, organic coating compositions for adhering together two concrete elements with inorganic materials
    • C04B41/51—Metallising, e.g. infiltration of sintered ceramic preforms with molten metal
    • C04B41/515—Other specific metals
    • C04B41/5155—Aluminium
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B41/00—After-treatment of mortars, concrete, artificial stone or ceramics; Treatment of natural stone
    • C04B41/80—After-treatment of mortars, concrete, artificial stone or ceramics; Treatment of natural stone of only ceramics
    • C04B41/81—Coating or impregnation
    • C04B41/85—Coating or impregnation with inorganic materials
    • C04B41/88—Metals
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J1/00—Adhesives based on inorganic constituents
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25C—PROCESSES FOR THE ELECTROLYTIC PRODUCTION, RECOVERY OR REFINING OF METALS; APPARATUS THEREFOR
    • C25C3/00—Electrolytic production, recovery or refining of metals by electrolysis of melts
    • C25C3/06—Electrolytic production, recovery or refining of metals by electrolysis of melts of aluminium
    • C25C3/08—Cell construction, e.g. bottoms, walls, cathodes
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
    • C04B2111/00474—Uses not provided for elsewhere in C04B2111/00
    • C04B2111/0087—Uses not provided for elsewhere in C04B2111/00 for metallurgical applications
    • C04B2111/00879—Non-ferrous metallurgy
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3231—Refractory metal oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C04B2235/3232—Titanium oxides or titanates, e.g. rutile or anatase
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/34—Non-metal oxides, non-metal mixed oxides, or salts thereof that form the non-metal oxides upon heating, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3409—Boron oxide, borates, boric acids, or oxide forming salts thereof, e.g. borax
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/40—Metallic constituents or additives not added as binding phase
    • C04B2235/402—Aluminium
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
    • C04B2235/54—Particle size related information
    • C04B2235/5418—Particle size related information expressed by the size of the particles or aggregates thereof
    • C04B2235/5436—Particle size related information expressed by the size of the particles or aggregates thereof micrometer sized, i.e. from 1 to 100 micron
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/60—Aspects relating to the preparation, properties or mechanical treatment of green bodies or pre-forms
    • C04B2235/604—Pressing at temperatures other than sintering temperatures
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/65—Aspects relating to heat treatments of ceramic bodies such as green ceramics or pre-sintered ceramics, e.g. burning, sintering or melting processes
    • C04B2235/658—Atmosphere during thermal treatment
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/02—Aspects relating to interlayers, e.g. used to join ceramic articles with other articles by heating
    • C04B2237/04—Ceramic interlayers
    • C04B2237/08—Non-oxidic interlayers
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/02—Aspects relating to interlayers, e.g. used to join ceramic articles with other articles by heating
    • C04B2237/04—Ceramic interlayers
    • C04B2237/09—Ceramic interlayers wherein the active component for bonding is not the largest fraction of the interlayer
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/30—Composition of layers of ceramic laminates or of ceramic or metallic articles to be joined by heating, e.g. Si substrates
    • C04B2237/32—Ceramic
    • C04B2237/34—Oxidic
    • C04B2237/343—Alumina or aluminates
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/30—Composition of layers of ceramic laminates or of ceramic or metallic articles to be joined by heating, e.g. Si substrates
    • C04B2237/32—Ceramic
    • C04B2237/36—Non-oxidic
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/30—Composition of layers of ceramic laminates or of ceramic or metallic articles to be joined by heating, e.g. Si substrates
    • C04B2237/32—Ceramic
    • C04B2237/36—Non-oxidic
    • C04B2237/363—Carbon
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/50—Processing aspects relating to ceramic laminates or to the joining of ceramic articles with other articles by heating
    • C04B2237/61—Joining two substrates of which at least one is porous by infiltrating the porous substrate with a liquid, such as a molten metal, causing bonding of the two substrates, e.g. joining two porous carbon substrates by infiltrating with molten silicon
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/50—Processing aspects relating to ceramic laminates or to the joining of ceramic articles with other articles by heating
    • C04B2237/62—Forming laminates or joined articles comprising holes, channels or other types of openings
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/50—Processing aspects relating to ceramic laminates or to the joining of ceramic articles with other articles by heating
    • C04B2237/70—Forming laminates or joined articles comprising layers of a specific, unusual thickness
    • C04B2237/708—Forming laminates or joined articles comprising layers of a specific, unusual thickness of one or more of the interlayers
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/50—Processing aspects relating to ceramic laminates or to the joining of ceramic articles with other articles by heating
    • C04B2237/80—Joining the largest surface of one substrate with a smaller surface of the other substrate, e.g. butt joining or forming a T-joint
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/50—Processing aspects relating to ceramic laminates or to the joining of ceramic articles with other articles by heating
    • C04B2237/84—Joining of a first substrate with a second substrate at least partially inside the first substrate, where the bonding area is at the inside of the first substrate, e.g. one tube inside another tube

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Ceramic Engineering (AREA)
  • Organic Chemistry (AREA)
  • Materials Engineering (AREA)
  • Structural Engineering (AREA)
  • Inorganic Chemistry (AREA)
  • Manufacturing & Machinery (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Electrochemistry (AREA)
  • Metallurgy (AREA)
  • Composite Materials (AREA)
  • Electrolytic Production Of Metals (AREA)
  • Ceramic Products (AREA)
  • Furnace Housings, Linings, Walls, And Ceilings (AREA)
SK1096-95A 1993-03-09 1994-03-08 The bonding of bodies of refractory hard materials with the carbonaceous base SK109695A3 (en)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US08/028,359 US5320717A (en) 1993-03-09 1993-03-09 Bonding of bodies of refractory hard materials to carbonaceous supports
PCT/IB1994/000034 WO1994020651A2 (fr) 1993-03-09 1994-03-08 Fixation de corps de materiaux refractaires durs sur des supports carbones

Publications (1)

Publication Number Publication Date
SK109695A3 true SK109695A3 (en) 1996-03-06

Family

ID=21843019

Family Applications (1)

Application Number Title Priority Date Filing Date
SK1096-95A SK109695A3 (en) 1993-03-09 1994-03-08 The bonding of bodies of refractory hard materials with the carbonaceous base

Country Status (8)

Country Link
US (2) US5320717A (fr)
EP (1) EP0688369B1 (fr)
AU (1) AU670496B2 (fr)
CA (1) CA2155203A1 (fr)
DE (1) DE69404829T2 (fr)
NO (1) NO953518L (fr)
SK (1) SK109695A3 (fr)
WO (1) WO1994020651A2 (fr)

Families Citing this family (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6001236A (en) 1992-04-01 1999-12-14 Moltech Invent S.A. Application of refractory borides to protect carbon-containing components of aluminium production cells
US5651874A (en) 1993-05-28 1997-07-29 Moltech Invent S.A. Method for production of aluminum utilizing protected carbon-containing components
US5534119A (en) * 1992-06-12 1996-07-09 Sekhar; Jainagesh A. Method of reducing erosion of carbon-containing components of aluminum production cells
US5413689A (en) * 1992-06-12 1995-05-09 Moltech Invent S.A. Carbon containing body or mass useful as cell component
WO1994024069A1 (fr) * 1993-04-19 1994-10-27 Moltech Invent S.A. Conditionnement d'elements de cellule destines a la production d'aluminium
US5486278A (en) * 1993-06-02 1996-01-23 Moltech Invent S.A. Treating prebaked carbon components for aluminum production, the treated components thereof, and the components use in an electrolytic cell
US5679224A (en) * 1993-11-23 1997-10-21 Moltech Invent S.A. Treated carbon or carbon-based cathodic components of aluminum production cells
WO1995031416A1 (fr) * 1994-05-13 1995-11-23 Micropyretics Heaters International Produits de chauffage homogeneises par frittage
US5534130A (en) * 1994-06-07 1996-07-09 Moltech Invent S.A. Application of phosphates of aluminum to carbonaceous components of aluminum production cells
EP0905284B1 (fr) 1994-09-08 2002-04-03 MOLTECH Invent S.A. Cuve d'électrolyse d'aluminium à cathode drainée
US5560809A (en) * 1995-05-26 1996-10-01 Saint-Gobain/Norton Industrial Ceramics Corporation Improved lining for aluminum production furnace
US5753163A (en) 1995-08-28 1998-05-19 Moltech. Invent S.A. Production of bodies of refractory borides
US5753382A (en) * 1996-01-10 1998-05-19 Moltech Invent S.A. Carbon bodies resistant to deterioration by oxidizing gases
US6863788B2 (en) * 2002-07-29 2005-03-08 Alcoa Inc. Interlocking wettable ceramic tiles
US20050254543A1 (en) * 2004-05-13 2005-11-17 Sgl Carbon Ag Lining for carbothermic reduction furnace
US8865301B2 (en) 2012-01-26 2014-10-21 The United States Of America, As Represented By The Secretary Of The Navy Refractory metal boride ceramics and methods of making thereof
WO2013165538A1 (fr) * 2012-05-01 2013-11-07 The Government Of The Usa, As Represented By The Secretary Of The Navy Formation de compositions carbonées de carbure de bore-nitrure de bore
CN111825470B (zh) * 2020-08-07 2022-09-16 安徽瑞蒙科技有限公司 一种用于发泡陶瓷保温板的耐火底浆及其制备、应用方法

Family Cites Families (72)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3097930A (en) * 1960-03-09 1963-07-16 Cons Beryllium Ltd Method of making a porous shape of sintered refractory material
US3111396A (en) * 1960-12-14 1963-11-19 Gen Electric Method of making a porous material
US3090094A (en) * 1961-02-21 1963-05-21 Gen Motors Corp Method of making porous ceramic articles
US3345440A (en) * 1965-06-29 1967-10-03 John M Googin Method for manufacturing foam carbon products
US3726643A (en) * 1970-04-09 1973-04-10 I Khim Fiz Akademii Nauk Method of producing refractory carbides,borides,silicides,sulfides,and nitrides of metals of groups iv,v,and vi of the periodic system
US3778249A (en) * 1970-06-09 1973-12-11 Int Nickel Co Dispersion strengthened electrical heating alloys by powder metallurgy
US3705791A (en) * 1970-09-18 1972-12-12 Wall Colmonoy Corp Cermet alloy composition
US3947363A (en) * 1974-01-02 1976-03-30 Swiss Aluminium Limited Ceramic foam filter
US3893917A (en) * 1974-01-02 1975-07-08 Alusuisse Molten metal filter
US4024056A (en) * 1975-07-21 1977-05-17 Swiss Aluminium Ltd. Filtering of molten metal
US3962081A (en) * 1975-03-28 1976-06-08 Swiss Aluminium Ltd. Ceramic foam filter
US4093524A (en) * 1976-12-10 1978-06-06 Kaiser Aluminum & Chemical Corporation Bonding of refractory hard metal
RU725326C (ru) * 1977-08-29 1993-11-15 Отделение Института химической физики АН СССР Способ получени двухслойных труб
CA1137523A (fr) * 1978-08-12 1982-12-14 Tsuneaki Narumiya Corps poreux en ceramique
JPS5556077A (en) * 1978-10-21 1980-04-24 Bridgestone Tire Co Ltd Ceramic porous body
US4333813A (en) * 1980-03-03 1982-06-08 Reynolds Metals Company Cathodes for alumina reduction cells
US4374761A (en) * 1980-11-10 1983-02-22 Aluminum Company Of America Inert electrode formulations
US4391918A (en) * 1981-01-22 1983-07-05 Swiss Aluminium Ltd. Ceramic foam filter and aqueous slurry for making same
US4405433A (en) * 1981-04-06 1983-09-20 Kaiser Aluminum & Chemical Corporation Aluminum reduction cell electrode
US4466096A (en) * 1982-03-11 1984-08-14 International Business Machines Corporation Apparatus and method for providing transmitter hierarchy control for efficient channel management
US4697632A (en) * 1982-06-11 1987-10-06 Howmet Turbine Components Corporation Ceramic porous bodies suitable for use with superalloys
US4466996A (en) * 1982-07-22 1984-08-21 Martin Marietta Corporation Aluminum cell cathode coating method
US4540475A (en) * 1982-12-30 1985-09-10 Corning Glass Works Electrolytic Al production with reactive sintered ceramic components of boride-oxide phases
US4600481A (en) * 1982-12-30 1986-07-15 Eltech Systems Corporation Aluminum production cell components
US4481052A (en) * 1983-01-28 1984-11-06 Martin Marietta Corporation Method of making refractory hard metal containing tiles for aluminum cell cathodes
US4459363A (en) * 1983-02-28 1984-07-10 The United States Of America As Represented By The United States Department Of Energy Synthesis of refractory materials
US4455211A (en) * 1983-04-11 1984-06-19 Aluminum Company Of America Composition suitable for inert electrode
AU2713684A (en) * 1983-04-26 1984-11-01 Aluminium Company Of America Electrolytic cell
US4596637A (en) * 1983-04-26 1986-06-24 Aluminum Company Of America Apparatus and method for electrolysis and float
US4582553A (en) * 1984-02-03 1986-04-15 Commonwealth Aluminum Corporation Process for manufacture of refractory hard metal containing plates for aluminum cell cathodes
US4678760A (en) * 1984-04-27 1987-07-07 Aluminum Company Of America Method of forming a substantially interwoven matrix containing a refractory hard metal and a metal compound
EP0165707B1 (fr) * 1984-05-18 1991-10-23 Sumitomo Electric Industries Limited Procédé pour le frittage de corps en céramique et corps en céramique renforcés par un métal dispersé obtenus par ce procédé
US4915905A (en) * 1984-10-19 1990-04-10 Martin Marietta Corporation Process for rapid solidification of intermetallic-second phase composites
US4985202A (en) * 1984-10-19 1991-01-15 Martin Marietta Corporation Process for forming porous metal-second phase composites
US4774052A (en) * 1984-10-19 1988-09-27 Martin Marietta Corporation Composites having an intermetallic containing matrix
US4836982A (en) * 1984-10-19 1989-06-06 Martin Marietta Corporation Rapid solidification of metal-second phase composites
US4751048A (en) * 1984-10-19 1988-06-14 Martin Marietta Corporation Process for forming metal-second phase composites and product thereof
EP0192602B1 (fr) * 1985-02-18 1992-11-11 MOLTECH Invent S.A. Electrolyse d'alumine à basse température
DE3685760T2 (de) * 1985-02-18 1993-05-19 Moltech Invent Sa Verfahren zur herstellung von aluminium, zelle zur herstellung von aluminium und anode fuer die elektrolyse von aluminium.
US4808372A (en) * 1986-01-23 1989-02-28 Drexel University In situ process for producing a composite containing refractory material
US4902457A (en) * 1986-04-07 1990-02-20 Matsushita Electric Industrial Co., Ltd. Method for manufacturing a porous material or a composite sintered product comprising zirconium oxide and a carbide
JPH0788500B2 (ja) * 1986-06-13 1995-09-27 株式会社曙ブレ−キ中央技術研究所 摩擦材料
US4699763A (en) * 1986-06-25 1987-10-13 Westinghouse Electric Corp. Circuit breaker contact containing silver and graphite fibers
US4678548A (en) * 1986-07-21 1987-07-07 Aluminum Company Of America Corrosion-resistant support apparatus and method of use for inert electrodes
ATE70094T1 (de) * 1986-08-21 1991-12-15 Moltech Invent Sa Metall-keramikverbundwerkstoff, formkoerper und verfahren zu dessen herstellung.
DE3638937A1 (de) * 1986-11-14 1988-05-26 Sigri Gmbh Kathode fuer eine schmelzflusselektrolysezelle
US4800065A (en) * 1986-12-19 1989-01-24 Martin Marietta Corporation Process for making ceramic-ceramic composites and products thereof
US4772452A (en) * 1986-12-19 1988-09-20 Martin Marietta Corporation Process for forming metal-second phase composites utilizing compound starting materials
US4975191A (en) * 1987-03-23 1990-12-04 Swiss Aluminium Ltd. Ceramic foam filter
US4900698A (en) * 1987-05-26 1990-02-13 W. R. Grace & Co.-Conn. Ceramic product and process
US4904424A (en) * 1987-05-29 1990-02-27 Hoechst Celanese Corporation Ceramic alloys from colloidal metal alloy suspensions
WO1989002489A1 (fr) * 1987-09-16 1989-03-23 Eltech Systems Corporation Collecteur de courant cathodique pour des cellules de production d'aluminium
US5015343A (en) * 1987-12-28 1991-05-14 Aluminum Company Of America Electrolytic cell and process for metal reduction
US4961778A (en) * 1988-01-13 1990-10-09 The Dow Chemical Company Densification of ceramic-metal composites
US4865701A (en) * 1988-08-31 1989-09-12 Beck Theodore R Electrolytic reduction of alumina
US5022991A (en) * 1988-09-08 1991-06-11 Corning Incorporated Thermite coated filter
US4948761A (en) * 1988-12-02 1990-08-14 Benchmark Structural Ceramics Corporation Process for making a silicon carbide composition
US4957885A (en) * 1988-10-06 1990-09-18 Benchmark Structural Ceramics Corporation Process for making a silicon carbide composition
US5030600A (en) * 1988-10-06 1991-07-09 Benchmark Structural Ceramics Corp. Novel sialon composition
US4990295A (en) * 1988-10-06 1991-02-05 Benchmark Structural Ceramics Corporation Process for making a silicon carbide composition
US5032332A (en) * 1988-10-06 1991-07-16 Benchmark Structural Ceramics Corporation Process for making a silicon carbide whisker reinforced alumina ceramic composite precursor
US5071797A (en) * 1988-10-06 1991-12-10 Benchmark Structural Ceramics Corporation Titanium carbide/alumina composite material
US5006290A (en) * 1988-10-06 1991-04-09 Benchmark Structural Ceramics Corporation Process for making a silicon carbide whisker reinforced alumina ceramic composite precursor
US5143668A (en) * 1988-10-06 1992-09-01 Benchmark Structural Ceramics Corporation Process for making a reaction-sintered carbide-based composite body with controlled combustion synthesis
US4909842A (en) * 1988-10-21 1990-03-20 The United States Of America As Represented By The United States Department Of Energy Grained composite materials prepared by combustion synthesis under mechanical pressure
WO1990007014A1 (fr) * 1988-12-20 1990-06-28 Institut Strukturnoi Makrokinetiki Akademii Nauk Sssr Procede d'obtention de matiere composite
US5158655A (en) * 1989-01-09 1992-10-27 Townsend Douglas W Coating of cathode substrate during aluminum smelting in drained cathode cells
WO1991000254A1 (fr) * 1989-06-30 1991-01-10 Institut Strukturnoi Makrokinetiki Akademii Nauk Sssr Materiau composite ceramique et son procede d'obtention
US5145619A (en) * 1990-03-26 1992-09-08 Benchmark Structural Ceramics Corporation Combustion-synthesis process for making friction materials
US5188678A (en) * 1990-08-15 1993-02-23 University Of Cincinnati Manufacture of net shaped metal ceramic composite engineering components by self-propagating synthesis
US5217583A (en) * 1991-01-30 1993-06-08 University Of Cincinnati Composite electrode for electrochemical processing and method for using the same in an electrolytic process for producing metallic aluminum
US5413689A (en) * 1992-06-12 1995-05-09 Moltech Invent S.A. Carbon containing body or mass useful as cell component

Also Published As

Publication number Publication date
US5320717A (en) 1994-06-14
AU6114394A (en) 1994-09-26
US5342491A (en) 1994-08-30
DE69404829T2 (de) 1998-04-02
NO953518D0 (no) 1995-09-07
DE69404829D1 (de) 1997-09-11
NO953518L (no) 1995-09-07
CA2155203A1 (fr) 1994-09-15
EP0688369B1 (fr) 1997-08-06
WO1994020651A3 (fr) 1994-10-27
AU670496B2 (en) 1996-07-18
WO1994020651A2 (fr) 1994-09-15
EP0688369A1 (fr) 1995-12-27

Similar Documents

Publication Publication Date Title
SK109695A3 (en) The bonding of bodies of refractory hard materials with the carbonaceous base
US5310476A (en) Application of refractory protective coatings, particularly on the surface of electrolytic cell components
US4333813A (en) Cathodes for alumina reduction cells
US5753163A (en) Production of bodies of refractory borides
CA2546635C (fr) Stabilisateurs pour des structures cathodiques contenant du diborure de titane
SK115795A3 (en) Production of carbon-based composite materials as electrolyser components of aluminium production
EP1257690B1 (fr) Procede pour munir des constituants carbones d'une cellule d'electrolyse d'un revetement protecteur
CA1239617A (fr) Pot-cathode pour cuve electrolytique de production de l'aluminium, et fabrication des elements composites pour ses parois
Boxall et al. TiB2 cathode material: Application in conventional VSS cells
US6338785B1 (en) Start-up of aluminum electrowinning cells
US20040149569A1 (en) Aluminium-wettable porous ceramic material
CN100515546C (zh) 惰性阳极组件
CA2397843A1 (fr) Revetement refractaire pour les elements d'une cellule d'electrolyse d'aluminium
US5582695A (en) Structural parts for electrolytic reduction cells for aluminum
AU690087B2 (en) Refractory/carbon components of aluminium production cells
US6146513A (en) Electrodes, electrolysis apparatus and methods using uranium-bearing ceramic electrodes, and methods of producing a metal from a metal compound dissolved in a molten salt, including the electrowinning of aluminum
EP0150007A2 (fr) Utilisation de spinelle magnésium-aluminium dans des cellules de réduction de métaux légers
CA2268931A1 (fr) Demarrage de cellules d'extraction electrolytique de l'aluminium
US20040089539A1 (en) Start-up of aluminium electrowinning cells
CN116445978A (zh) 一种用于惰性阳极铝电解槽上部的耐火保温件
EP1347080A1 (fr) Revêtement contenant silicium