SE505408C2 - Surface-cladding elements made of hardened wood and methods for making such elements - Google Patents
Surface-cladding elements made of hardened wood and methods for making such elementsInfo
- Publication number
- SE505408C2 SE505408C2 SE9401590A SE9401590A SE505408C2 SE 505408 C2 SE505408 C2 SE 505408C2 SE 9401590 A SE9401590 A SE 9401590A SE 9401590 A SE9401590 A SE 9401590A SE 505408 C2 SE505408 C2 SE 505408C2
- Authority
- SE
- Sweden
- Prior art keywords
- compression
- wood
- blank
- thin
- substance
- Prior art date
Abstract
Description
505 408 bättrat ytbeklädnadselement av den inledningsvis angivna typen, vid vilket de ovan beskrivna olägenheterna är eli- minerade. 505 408 improved surface cladding element of the initially indicated type, in which the above-described disadvantages are eli- mined.
Det i enlighet med uppfinningen för detta ändamål föreslagna ytbeklädnadselementet kännetecknas i första hand av att det i elementet ingående materialet är kraftigt kom- primerat i elementets breddriktníng.It in accordance with the invention for this purpose proposed surface cladding element is characterized in the first place that the material contained in the element is strongly primed in the width direction of the element.
Uppfinningen grundar sig på insikten om att anledningen till de vid de tidigare kända ytbeklädnadselementen förekomman- de olägenheterna är att dessa genomgående varit kraftigt kom- primerade i riktningen för deras tjocklek, dvs. i mot bredd- riktningen vinkelrät riktning. Genom att i enlighet med upp- finningen utföra elementen kraftigt komprimerade i breddrikt- ningen i stället för i tjockleksriktningen är det möjligt att förhindra att eventuellt inträngande fukt kommer att ge upphov till någon nämnvärd svällning hos trämaterialet i elementen, eftersom en dylik svällning kan uppträda enbart om det kompri- merade materialet av den inträngande fukten kan bibringas en dimensionsökning i med komprimeringsriktningen närmelsevis parallell riktning. Någon sådan dimensionsökning kan dock icke äga rum hos de enligt uppfinningen utförda ytbeklädnads- elementen sedan dessa fastlimmats pà det aktuella underlaget.The invention is based on the realization that the reason to those present in the previously known surface cladding elements. the disadvantages are that these have consistently been strongly primed in the direction of their thickness, i.e. against width direction perpendicular direction. By, in accordance with perform the elements strongly compressed in the width direction instead of in the thickness direction it is possible to prevent any ingress of moisture from occurring to any appreciable swelling of the wood material in the elements, since such swelling can occur only if the compression the increased material of the penetrating moisture can be imparted a dimensional increase in with the compression direction approximately parallel direction. However, such a dimension increase can do not take place in the surface cladding embodiments according to the invention. the elements after these have been glued to the relevant substrate.
Vidare resulterar den enligt uppfinningen föreslagna komprimeríngen av trämaterialet i ytbeklädnadselementen i att man erhåller en starkt förbättrad fasthàllning av eventuella i nämnda material förekommande kvistar, eftersom dessa vid komprimeringen kommer att fastklämmas i elementen av det omgivande materialet i respektive element.Furthermore, the result according to the invention results the compaction of the wood material in the cladding elements in that one obtains a greatly improved retention of any twigs present in said material, since these during compression will be clamped in the elements of the surrounding material in each element.
Uppfinningen avser även ett sätt för framställning av ytbeklädnadselement av hàrdgjort trä, som består av läng- sträckta, tunna, platta stycken av massivt trä, vilka uppvisar en med deras längdriktning i huvudsak parallell fiberriktning och är hárdgjorda genom kraftig komprimering av dem i deras breddriktning. Detta sätt kännetecknas i första hand av att ett flertal dylika element framställes samtidigt genom att ett lángsträckt ämne av trä med generellt kvadratisk eller rektangulär tvärsektion underkastas en kraftig komprimering av detsamma i en mot dess längdriktning tvärgàende riktning BNSDOCI D: 505 408 genom att ett högt presstryck appliceras mot två motstàende sidor hos ämnet, varvid ämnet antingen utgöres av ett enda sammanhängande trästycke, som efter nämnda komprimering uppdelas utmed med riktningen för nämnda komprimering i huvudsak parallella, på kort avstånd från varandra liggande plan i och för bildande av ett flertal separata, làngsträckta, tunna, platta trästycken, eller ämnet är bildat av ett fler- tal i förväg framställda separata, làngsträckta, tunna, platta trästycken, vilkas smalkanter bildar nämnda båda motstàende ytor hos ämnet.The invention also relates to a method for producing surface cladding elements of hardened wood, consisting of elongated stretched, thin, flat pieces of solid wood, which exhibit one with their longitudinal direction substantially parallel fiber direction and are hardened by vigorously compressing them into theirs width direction. This method is primarily characterized by that a plurality of such elements are produced simultaneously by an elongated wooden blank with a generally square or rectangular cross section is subjected to heavy compression of the same in a direction transverse to its longitudinal direction BNSDOCI D: 505 408 by applying a high pressure to two opposites sides of the substance, the substance either being a single one continuous piece of wood, as after said compaction divided along the direction of said compression in substantially parallel, at short distances from each other plane in order to form a plurality of separate, elongate, thin, flat pieces of wood, or the blank is formed by a multi- speech pre-produced separate, elongated, thin, flat pieces of wood, the narrow edges of which form the said two opposites surfaces of the substance.
I syfte att undvika risken för att den kraftiga komp- rimeringen skall ge upphov till av en kraftig expansion hos ämnet i mot komprimeringsriktningen tvärgáende riktning orsaka- de skador pà ämnet är det lämpligt att under nämnda komprime- ring hindra ämnet från att expandera i mot dess längdriktning och riktningen för nämnda komprimering tvärgàende riktning.In order to avoid the risk that the strong comp- the rhyme should give rise to a strong expansion of the substance in the direction opposite to the compression direction causes the damage to the substance, it is appropriate that during the said prevent the substance from expanding in its longitudinal direction and the direction of said compression transverse direction.
Företrädesvis kan ämnet härvid före den kraftiga komprimeringen av det underkastas en mindre komprimering i en mot ämnets längdriktning och riktningen för den kraftiga komprimeringen tvärgàende riktning och hållas komprimerat i denna riktning under genomförandet av den kraftiga komprimeringen.Preferably, the substance can do this before the heavy compression of it is subjected to a minor compression in one against the substance longitudinal direction and the direction of the strong compression transverse direction and kept compressed in this direction during the implementation of the heavy compression.
För att säkerställa att man skall erhålla en exakt, förutbestämd bredd hos ytbeklädnadselementen och släta, plana ytor vid dessas smalkanter kan ämnet efter den kraftiga komprimeringen av det underkastas en hyvling eller slipning vid nämnda båda motstàende sidor hos detsamma.To ensure that an accurate, predetermined width of the cladding elements and smooth, flat surfaces at their narrow edges can the subject after the strong the compression of it is subjected to a planing or grinding at said two opposite sides of the same.
I syfte att underlätta komprimeringen av ämnet och åstadkomma förbättrade kvalitativa egenskaper hos det kompri- merade materialet bör man före komprimeringen av ämnet uppvärma detta till en temperatur av åtminstone cirka 60°C, företrädes- vis cirka 80°C - cirka 90°C, och utföra komprimeringen medan ämnet alltjämt befinner sig i uppvärmt tillstànd.In order to facilitate the compression of the substance and achieve improved qualitative properties of the compression the material should be heated before compaction of the substance this to a temperature of at least about 60 ° C, preferably show about 80 ° C - about 90 ° C, and perform the compression while the substance is still in a heated state.
BNSDOCID: 505 408 Uppfinningen beskrivs nedan ytterligare under hänvis- ning till bifogade ritningar, pà vilka fig. 1 visar en ändvy av ett för utnyttjande vid framställning av ett flertal ytbeklädnadselement enligt uppfin- ningen avsett ämne av massivt trä, åskádliggörande detta place- rat i en för komprimering av ämnet avsedd press, fig. 2 en motsvarande ändvy av ämnet, âskàdliggörande detta i ett medelst pressen komprimerat tillstànd, fig. 3 en ändvy av ämnet efter uttagning av detta ur pressen, fig. 4 en ändvy av ämnet efter avhyvling av tvà mot- stående sidor hos detta och fig. 5 en ändvy av ett genom uppsägning av ämnet enligt fig. 4 framställt ytbeklädnadselement enligt uppfin- ningen.BNSDOCID: 505 408 The invention is further described below with reference to to the accompanying drawings, on which Fig. 1 shows an end view of one for use at manufacture of a plurality of cladding elements according to the invention intended for solid wood, illustrating this in a press intended for compaction of the substance, Fig. 2 is a corresponding end view of the blank, detrimental this in a state compressed by the press, Fig. 3 is an end view of the blank after removal of this watch the press, Fig. 4 is an end view of the blank after planing out two standing sides of this and Fig. 5 is an end view of one by termination of the blank according to Fig. 4, surface cladding element according to the invention ningen.
Med 10 betecknas i fig. 1 ett långsträckt ämne av massivt trä med generellt kvadratisk tvärsektion, vilket är avsett att utnyttjas för framställning av ett flertal ytbekläd- nadselement av hàrdgjort trä, vilka har formen av làngsträckta, tunna, platta stycken av massivt trä, som är kraftigt komprime- rade i sin breddriktning. Ämnet 10 visas i fig. 1 placerat i en generellt med ll betecknad press. Denna press ll innefattar ett pressbord 12, pá vilket ämnet 10 vilar, samt ett pá pressbordet 12 sta- tionärt anbringat sidostöd 13 och en likaledes på pressbordet 12 stationärt anbringad konsol 14, som uppbär ett antal hydraul- cylindrar 15, vilka bildar manöverorgan för en med hjälp av dem i riktning mot sidostödet 13 i horisontell led fram och äter förskjutbar pressplatta 16. Vidare innefattar pressen ll även ett i riktning mot och fràn pressbordet 12 i vertikal led rörligt pressverktyg 17, som vid sin nedre ände är försett med en pressplatta 18.In Fig. 1, 10 denotes an elongate blank of solid wood with generally square cross section, which is intended to be used for the manufacture of a plurality of surface coatings hardwood elements, which are in the form of elongated, thin, flat pieces of solid wood, which are highly compressed in its width direction. The blank 10 is shown in Fig. 1 placed in a generally with ll designated press. This press ll comprises a press table 12, on which the blank 10 rests, and one on the press table 12 side-mounted side support 13 and one likewise on the press table 12 stationary mounted bracket 14, which carries a number of hydraulic cylinders 15, which form actuators for one by means of them in the direction of the side support 13 in the horizontal direction forward and eat displaceable press plate 16. Furthermore, the press 11 also includes one in the direction of and from the press table 12 in the vertical direction movable press tool 17, which is provided at its lower end with a press plate 18.
Sedan ämnet 10 placerats i pressen ll bibringas det genom förflyttning av pressplattan 16 mot sidostödet 13 i den i fig. 1 med pilen A markerade riktningen en svag kompri- mering i sidled. Denna sidokomprimering av ämnet 10 kan uppgå till cirka 3% - cirka 5%, vilket innebär att ämnets utsträck- BNSDOCID: 505 408 ning i sidled minskas med motsvarande procenttal. Pressplattan 16 kvarhàlles sedan med hjälp av hydraulcylindrarna 15 i det aktuella, i fig. 2 visade läget.After the blank 10 is placed in the press 11, it is imparted by moving the press plate 16 towards the side support 13 in the direction marked in Fig. 1 by the arrow A a weak compression mering laterally. This lateral compression of the blank 10 may amount to to about 3% - about 5%, which means that the substance BNSDOCID: 505 408 laterally is reduced by the corresponding percentage. The press plate 16 is then retained by means of the hydraulic cylinders 15 therein current, the position shown in Fig. 2.
Den av pressverktyget 17 uppburna pressplattan 18 sänkes härefter i den i fig. 1 med pilen B markerade riktningen ned mot ämnet 10 för att åstadkomma en kraftig komprimering av detta i höjdled i och för hårdgöring av trämaterialet i ämnet 10. Storleken av den med hjälp av pressplattan 18 åstad- komna komprimeringen av ämnet 10 i höjdled kan uppgå till flera tiotals procent. Exempelvis kan den för ett av furu eller gran bestående ämne uppgå till cirka 50% - cirka 60%, medan den för ett ämne som består av ett hårdare träslag, t.ex. ek, björk eller bok, kan uppgå till cirka 20% - cirka 30%.The press plate 18 supported by the press tool 17 is then lowered in the direction marked with the arrow B in Fig. 1 down towards the blank 10 to effect a strong compression of this in height in order to harden the wood material in the substance 10. The size of it produced by means of the press plate 18 the compression of the blank 10 in height can amount to several tens of percent. For example, it can for one of pine or spruce consisting of about 50% - about 60%, while that of a substance consisting of a harder kind of wood, for example oak, birch or beech, can amount to about 20% - about 30%.
Den erforderliga tiden för genomförande av den önskade kraftiga komprimeringen av ämnet 10 med hjälp av pressplattan 18 kan uppgå till någon eller några minuter. Sedan ämnet 10 bibringats önskad komprimering kvarhålles pressplattan 18 i nedsänkt läge under en ytterligare tid av några minuter.The time required for the implementation of the desired vigorous compression of the blank 10 by means of the press plate 18 can amount to one or a few minutes. Then the topic 10 If the desired compression is imparted, the press plate 18 is retained in the lowered position for an additional period of a few minutes.
I fig. 2 visas pressplattorna 16 och 18 båda i sina slutliga komprimeringslägen. För att illustrera den kompression som ämnet 10 bibringas med hjälp av de båda pressplattorna har den ursprungliga ytterkonturen hos ämnet 10 i fig. 1 inritats med punktstreckade linjer.In Fig. 2, the press plates 16 and 18 are both shown in their final ones compression modes. To illustrate the compression that the blank 10 is imparted by means of the two press plates have the original outer contour of the blank 10 in Fig. 1 is plotted with dotted lines.
Sedan den önskade hàlltiden för pressplattan 18 gått till ända, àterföres de båda pressplattorna 18 och 16 till sina i fig. 1 visade utgångslägen, varpå ämnet 10 kan uttagas ur pressen ll. Ämnet 10 kommer härvid inom en relativt kort tid att àterfjädra i höjdled, dvs. i riktning för den kraftiga komprimeringen av detsamma, och anta den i fig. 3 visade formen.After the desired holding time of the press plate 18 has elapsed to the end, the two press plates 18 and 16 are returned to their initial positions shown in Fig. 1, whereupon the blank 10 can be removed from the press ll. The blank 10 comes within a relatively short time time to spring back in height, ie. in the direction of the powerful the compression thereof, and assume the shape shown in Fig. 3.
Såsom jämförelse visas i fig. 3 med punktstreckade linjer även ämnets ursprungliga ytterkontur och den kontur som det bibringas under den i fig. 2 illustrerade komprimeringen.For comparison, Fig. 3 is shown in phantom also the original outer contour of the substance and the contour as it imparted during the compression illustrated in Fig. 2.
Pâ grund av den kraftiga komprimeringen av ämnet 10 i höjdled kommer ämnet även att expandera något i sidled så snart press- plattan 16 àterförts till sitt utgångsläge.Due to the high compression of the blank 10 in height the substance will also expand slightly laterally as soon as the plate 16 is returned to its initial position.
Sedan återfjädringen till den i fig. 3 visade formen BNSDOCID: 505 408 ägt rum, kan ämnet 10 underkastas en hyvling eller slipning vid dess övre och undre sidor, så att det kommer att erhålla den i fig. 4 med heldragna linjer visade formen.Then the resilience to the shape shown in Fig. 3 BNSDOCID: 505 408 occurred, the blank 10 may be subjected to planing or grinding its upper and lower sides, so that it will obtain it in Fig. 4 the shape shown in solid lines.
Härpà kan ämnet uppdelas i ett flertal enskilda av hàrdgjort trä bestående ytbeklädnadselement 19 av i fig. 5 visat slag genom delning av det utmed med riktningen för den kraftiga komprimeringen parallella, på kort avstånd fràn varand- ra liggande plan. Denna uppdelning av ämnet 10 i ett flertal separata ytbeklädnadselement 19 kan på i fig. 4 med punkt- streckade linjer antytt sätt ske genom en sàgning av ämnet.Here, the subject can be divided into a number of individual parts hardened wood consisting of surface cladding element 19 of in Fig. 5 shown stroke by dividing it along with the direction of it strong compression parallel, at a short distance from each other lying landscape. This division of the blank 10 into a plurality separate surface cladding elements 19 can be shown in Fig. 4 with dashed lines the way indicated by a sawing of the blank.
De pà ovan beskrivet sätt framställda ytbeklädnads- elementen 19 kommer att bestå av làngsträckta, tunna, platta trästycken, som är kraftigt komprimerade i sin breddriktning.The surface coatings prepared as described above the elements 19 will consist of elongated, thin, flat pieces of wood, which are heavily compressed in their width direction.
Vid användning av ytbeklädnadselementen 19 fastlimmas dessa med en bredsida hos dem i anliggning mot det aktuella under- laget, varvid de fixeras effektivt mot svällning i breddled på grund av eventuell inträngande fukt.When using the surface cladding elements 19, these are glued with a broad side of them in relation to the current sub- the team, whereby they are fixed effectively against swelling in width due to possible penetrating moisture.
För att undvika det materialspill som uppkommer vid en efter komprimeringen av ämnet 10 företagen uppsägning av detta i ett flertal separata tunna, platta trästycken kan man alternativt utnyttja ett ämne, som är bildat av ett flertal i förväg framställda separata, lángsträckta, tunna, platta trästycken, vilkas smalkanter får bilda de båda motstáende, för det höga presstrycket utsatta ytorna hos ämnet. Dessa separata trästycken kan med fördel vara framställda genom spån- fri klyvning av ett större trästycke, varvid de i det för komprimering avsedda ämnet kan inta sina ursprungliga lägen i förhållande till varandra. ßNsoocloz To avoid the material spillage that occurs at one after the compression of the substance 10 companies termination of this can be done in several separate thin, flat pieces of wood alternatively utilize a substance, which is formed by a plurality pre-made separate, elongated, thin, flat pieces of wood, the narrow edges of which may form the two opposing, the surfaces of the blank exposed to the high pressure. These separate pieces of wood can advantageously be made by chipboard. free splitting of a larger piece of wood, leaving them in it for compression intended substance can assume its original positions in relation to each other. ßNsoocloz
Claims (6)