RU2609501C1 - Glaze - Google Patents

Glaze Download PDF

Info

Publication number
RU2609501C1
RU2609501C1 RU2015152396A RU2015152396A RU2609501C1 RU 2609501 C1 RU2609501 C1 RU 2609501C1 RU 2015152396 A RU2015152396 A RU 2015152396A RU 2015152396 A RU2015152396 A RU 2015152396A RU 2609501 C1 RU2609501 C1 RU 2609501C1
Authority
RU
Russia
Prior art keywords
glaze
zro
zno
sio
beo
Prior art date
Application number
RU2015152396A
Other languages
Russian (ru)
Inventor
Юлия Алексеевна Щепочкина
Original Assignee
Юлия Алексеевна Щепочкина
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Юлия Алексеевна Щепочкина filed Critical Юлия Алексеевна Щепочкина
Priority to RU2015152396A priority Critical patent/RU2609501C1/en
Application granted granted Critical
Publication of RU2609501C1 publication Critical patent/RU2609501C1/en

Abstract

FIELD: chemistry.
SUBSTANCE: glaze contains, wt. %: SiO2 40.0-50.2; Al2O3 10.0-13.0; B2O3 16.5-23.0; ZnO 4.5-7.3; Na2O 3.0-5.0; ZrO2 4.2-8.5; SrO 2.5-5.0; BeO 1.0-2.0; SnO2 1.0-2.0.
EFFECT: increased frost resistance of glaze.
1 tbl

Description

Изобретение относится к технологии силикатов, в частности к составам глазурей, которые могут быть использованы для нанесения покрытия на керамические изделия декоративно-художественного назначения.The invention relates to the technology of silicates, in particular to compositions of glazes that can be used for coating ceramic products for decorative and artistic purposes.

Известна глазурь, содержащая, мас. %: SiO2 43,56-48,44; А12O3 9,22-11,76; СаО 12,46-14,45; MgO 2,7-3,33; ZnO 0,66-1,29; Na2O 1,42-2,31; Fe2O3 2,6-3,99; B2O3 13,77-17,48; ZrO2 1,95-3,83; BaO 1,5-2,96; SO3 0,12-0,2 [1].Known glaze containing, by weight. %: SiO 2 43.56-48.44; A1 2 O 3 9.22-11.76; CaO 12.46-14.45; MgO 2.7-3.33; ZnO 0.66-1.29; Na 2 O 1.42-2.31; Fe 2 O 3 2.6-3.99; B 2 O 3 13.77-17.48; ZrO 2 1.95-3.83; BaO 1.5-2.96; SO 3 0.12-0.2 [1].

Задачей изобретения является повышение морозостойкости глазури.The objective of the invention is to increase the frost resistance of the glaze.

Технический результат достигается тем, что глазурь, включающая SiO2, Аl2O3, В2O3, ZnO, Na2O, ZrO2, дополнительно содержит SrO, BeO и SnO2, при следующем соотношении компонентов, мас. %: SiO2 40,0-50,2; А12O3 10,0-13,0; В2O3 16,5-23,0; ZnO 4,5-7,3; Na2O 3,0-5,0; ZrO2 4,2-8,5; SrO 2,5-5,0; BеО 1,0-2,0; SnO2 1,0-2,0.The technical result is achieved in that the glaze, including SiO 2 , Al 2 O 3 , B 2 O 3 , ZnO, Na 2 O, ZrO 2 , additionally contains SrO, BeO and SnO 2 , in the following ratio of components, wt. %: SiO 2 40.0-50.2; A1 2 O 3 10.0-13.0; B 2 O 3 16.5-23.0; ZnO 4.5-7.3; Na 2 O 3.0-5.0; ZrO 2 4.2-8.5; SrO 2.5-5.0; BeO 1.0-2.0; SnO 2 1.0-2.0.

В таблице приведены составы глазури.The table shows the glaze compositions.

Figure 00000001
Figure 00000001

Figure 00000002
Figure 00000002

Фритту глазури варят при температуре 1400-1480°С. Расплав гранулируют в воду и размалывают до прохождения через сетку №0056. Суспензию наносят на керамические обожженные изделия и при температуре 900-960°С закрепляют оплавлением.Frit glaze is boiled at a temperature of 1400-1480 ° C. The melt is granulated into water and ground until passing through mesh No. 0056. The suspension is applied to ceramic calcined products and at a temperature of 900-960 ° C is fixed by reflow.

Источник информацииThe source of information

1. SU 726043, С03С 8/04, 1980.1. SU 726043, C03C 8/04, 1980.

Claims (1)

Глазурь, включающая SiO2, Al2O3, B2O3, ZnO, Na2O, ZrO2, отличающаяся тем, что дополнительно содержит SrO, ВеО и SnO2, при следующем соотношении компонентов, мас.%: SiO2 40,0-50,2; Al2O3 10,0-13,0; B2O3 16,5-23,0; ZnO 4,5-7,3; Na2O 3,0-5,0; ZrO2 4,2-8,5; SrO 2,5-5,0; ВеО 1,0-2,0; SnO2 1,0-2,0.Glaze, including SiO 2 , Al 2 O 3 , B 2 O 3 , ZnO, Na 2 O, ZrO 2 , characterized in that it further comprises SrO, BeO and SnO 2 , in the following ratio of components, wt.%: SiO 2 40 0-50.2; Al 2 O 3 10.0-13.0; B 2 O 3 16.5-23.0; ZnO 4.5-7.3; Na 2 O 3.0-5.0; ZrO 2 4.2-8.5; SrO 2.5-5.0; BeO 1.0-2.0; SnO 2 1.0-2.0.
RU2015152396A 2015-12-07 2015-12-07 Glaze RU2609501C1 (en)