Abstract

FIELD: medicine.

SUBSTANCE: method for producing a bonding paste consists in recovering erythrocytes from a blood clot, adding distilled water thereto, mixing, adding hydrochloric acid until the dark-red erythrocytes become black and the solution gets viscous, maturing the solution and adding saturated solution of sodium chloride thereto, mixing and maturing, filtering the solution, discharging sediment, adding sodium chloride powder to the filtrate until it is fully saturated and white sticky sediment appears on the surface in the certain environment.

EFFECT: method enables using waste blood to produce the bonding paste, which can be used immediately after preparation as an adhesive for medical products.

Description

Предлагаемое изобретение относится к медицине, в частности к гематологии и касается использования отходов крови для получения медицинских препаратов.The present invention relates to medicine, in particular to hematology, and relates to the use of blood wastes for the production of medications.

Задачей изобретения является исследование свойств крови и их использование для получения дополнительных препаратов из отходов крови.The objective of the invention is to study the properties of blood and their use to obtain additional drugs from blood wastes.

Способ осуществляется следующим образом.The method is as follows.

Известным способом /1/ сгусток крови делят на фибрин и темно-красную массу гемоглобина. Из фибрина делают соответствующие препараты, а полученную массу эритроцитов перемешивают и добавляют по объему 2 части дистиллированной воды, перемешивают, затем добавляют 8,3%-ную соляную кислоту серии X4 до перехода темно-красного цвета эритроцитов в черный. Консистенция массы при этом при перемешивании становится тягучей и вязкой, вязкость увеличивается примерно в 2 раза. После этого всю массу помещают в термостат при температуре 37°C и выдерживают при этой температуре 24-36 часов. Затем в полученную массу добавляют равный объем насыщенного раствора хлористого натрия и перемешивают в течении 8-15 мин, дают отстояться 30 мин. Белковая гемоглобинная масса выпадает в осадок, а надосадочная жидкость становится непрозрачной, мутной, возможно небольшое вспенивание. Надосадочную жидкость сливают в другой сосуд, остальную жидкость фильтруют. Фильтрат и надосадочную жидкость собирают и в нее добавляют сухую соль - хлористый натрий до полного насыщения - на дне сосуда должен оставаться белый осадок соли, при постоянном перемешивании. На поверхность жидкости всплывает серая клейкая масса, которая быстро прилипает к мешалке (которой мешается жидкость в банке), стенкам банки, рукам. С поверхности жидкости клейкую массу собирают ложкой или деревянной лопаткой и используют немедленно.In a known manner / 1 / a blood clot is divided into fibrin and dark red hemoglobin mass. The appropriate preparations are made from fibrin, and the resulting mass of red blood cells is mixed and 2 parts of distilled water are added by volume, mixed, then 8.3% hydrochloric acid of the X4 series is added until the dark red color of the red blood cells turns black. In this case, the mass consistency with stirring becomes viscous and viscous, the viscosity increases by about 2 times. After that, the whole mass is placed in a thermostat at a temperature of 37 ° C and maintained at this temperature for 24-36 hours. Then, an equal volume of a saturated solution of sodium chloride is added to the resulting mass and stirred for 8-15 minutes, allowed to stand for 30 minutes. Protein hemoglobin mass precipitates, and the supernatant becomes opaque, cloudy, possibly a little foaming. The supernatant is poured into another vessel, the rest of the liquid is filtered. The filtrate and the supernatant are collected and dry salt is added to it - sodium chloride until completely saturated - a white precipitate of salt should remain at the bottom of the vessel with constant stirring. A gray adhesive mass floats to the surface of the liquid, which quickly adheres to the mixer (which interferes with the liquid in the can), the walls of the can, and the hands. The adhesive mass is collected from the surface of the liquid with a spoon or wooden spatula and used immediately.

Пример получения клеящей массы An example of obtaining an adhesive mass

Была собрана кровь от домашних свиней (сгустки крови) общим объемом 3.0 л (отдельно сгустки в нем 2.2 л).Blood was collected from domestic pigs (blood clots) with a total volume of 3.0 L (separately clots in it 2.2 L).

Из этой массы сгустков выделен фибрин и жидкая часть крови (эритроциты) в объеме 1 литра. К полученной жидкой части крови добавлена дистиллированная вода объемом 2 л, перемешена. К полученной массе добавлена 8,3%-ная соляная кислота серии X4 до перехода окраски всей массы из темно-красного в черный, вязкость всей массы при этом возросла вдвое. После этого банку поставили в термостат при t° - 37°C на 28 часов. Затем в банку добавили равный объем насыщенного раствора хлористого натрия и оставили для отстаивания осадка на 40 мин, после чего профильтровали. Надосадочной жидкости в объеме собралось 4,2 л. В нее добавили избыток сухого хлористого натрия, до появления белого осадка на дне сосуда. Жидкость приобрела серовато-белый оттенок, а на поверхности появился белый липкий осадок, который медленно поднялся со дна банки. При ориентировочном взвешивании вес осадка ориентировочно ≈122 г. Полученный липкий осадок был использован немедленно для склеивания. Он хорошо клеил бумагу, картон, пальцы и руки производителя, мелкие дощечки, клеенку.From this mass of clots, fibrin and the liquid part of the blood (red blood cells) were isolated in a volume of 1 liter. To the obtained liquid part of the blood was added distilled water with a volume of 2 l, mixed. To the resulting mass was added 8.3% hydrochloric acid of the X4 series until the color of the entire mass changed from dark red to black, while the viscosity of the whole mass doubled. After that, the jar was placed in a thermostat at t ° - 37 ° C for 28 hours. Then an equal volume of a saturated solution of sodium chloride was added to the jar and left to sediment for 40 minutes, after which it was filtered. The supernatant in the volume collected 4.2 liters. An excess of dry sodium chloride was added to it until a white precipitate appeared at the bottom of the vessel. The liquid turned grayish-white, and a white, sticky precipitate appeared on the surface, which slowly rose from the bottom of the can. With approximate weighing, the weight of the precipitate is approximately ≈122 g. The obtained sticky precipitate was used immediately for bonding. He glued paper, cardboard, fingers and hands of the manufacturer, small boards, oilcloth well.

Выявленное свойство крови дает возможность несколько по-иному взглянуть на некоторые особенности крови. Хорошо известно, что эритроциты склеиваются при добавлении сыворотки, содержащей одноименные антитела. При этом образуются столбики, и если это происходит в организме, возникают тяжелые последствия. Полученная клеящая масса из эритроцитов крови дает возможность предположить наличие клеящего эффекта эритроцитов без добавления сыворотки. Не исключена возможность, что клеящие вещества не постоянно выделяются из эритроцитов, а при определенных условиях, которые требуют дальнейшего изучения.The revealed property of blood makes it possible to take a slightly different look at some of the features of blood. It is well known that red blood cells stick together when serum containing antibodies of the same name is added. In this case, columns are formed, and if this happens in the body, severe consequences arise. The resulting adhesive mass of red blood cells makes it possible to assume the presence of an adhesive effect of red blood cells without the addition of serum. It is possible that adhesives are not constantly released from red blood cells, but under certain conditions that require further study.

Технический результат использования изобретения заключается в определении склеивающего эффекта эритроцитов крови, необходимого для понимания физиологических процессов, связанных с эритроцитами, а также возможность получать клеящую массу из отходов крови, которую можно использовать в качестве клея.The technical result of the use of the invention is to determine the gluing effect of blood red blood cells, necessary for understanding the physiological processes associated with red blood cells, as well as the ability to obtain an adhesive mass from blood wastes that can be used as glue.

Т.о. предлагается способ получения клеящей массы, включающий выделение из сгустка крови эритроцитов, добавления к ним дистиллированной воды в соотношении 1:3, перемешивания, добавления 8,3% соляной кислоты до перехода темно-красного цвета эритроцитов в черный и приобретения раствором тягучей консистенции, выдерживания раствора при температуре 37°C в течение 24-36 часов и добавления в него насыщенного раствора хлористого натрия в соотношении 1:1, перемешивания и выдерживания в течение 40 мин, после чего раствор фильтруют с удалением осадка и добавляют в фильтрат порошок хлористого натрия до полного насыщения и появления на поверхности белого липкого осадка.T.O. a method for producing an adhesive mass is proposed, which includes the isolation of red blood cells from a blood clot, adding distilled water to them in a ratio of 1: 3, mixing, adding 8.3% hydrochloric acid until the dark red color of the red blood cells turns black and the solution acquires a viscous consistency, maintaining the solution at a temperature of 37 ° C for 24-36 hours and adding to it a saturated solution of sodium chloride in a ratio of 1: 1, stirring and holding for 40 minutes, after which the solution is filtered to remove the precipitate and adding the filtrate into the powder of sodium chloride to saturation and appears on the surface of a white sticky precipitate.

Источник информацииThe source of information

1. Патент №1573571 - Способ получения фибрина сгустка крови. В.А. Фигурнов, А.В. Фигурнов. 1990 г.1. Patent No. 1573571 - A method for producing fibrin of a blood clot. V.A. Figurnov, A.V. Figurnov. 1990 g.

Claims

A method of obtaining an adhesive mass, including the allocation of red blood cells from a blood clot, adding distilled water to them in a ratio of 1: 3, mixing, adding 8.3% hydrochloric acid until the dark red color of red blood cells turns black and acquiring a solution of viscous consistency, maintaining the solution at at a temperature of 37 ° C for 24-36 hours and adding to it a saturated solution of sodium chloride in the ratio 1: 1, stirring and keeping for 40 minutes, after which the solution is filtered to remove the precipitate and added to the filtrate oroshok sodium chloride to saturation and appears on the surface of a white sticky precipitate.