RU2499774C1

RU2499774C1 - Crude mixture for making expanded clay (versions)

Info

Publication number: RU2499774C1
Application number: RU2012127910/03A
Authority: RU
Inventors: Юлия Алексеевна Щепочкина
Original assignee: Юлия Алексеевна Щепочкина
Priority date: 2012-07-03
Filing date: 2012-07-03
Publication date: 2013-11-27

Abstract

FIELD: chemistry.

SUBSTANCE: according to the first version, the crude mixture for making expanded clay contains, wt %: Clay material 77.8 - 81.7, primary wool processing fibre wastes 0.2 - 0.3, saturated aqueous boric acid solution 18.0 - 22.0. According to the second version, the crude mixture for making expanded clay contains, wt %: clay material 77.8 - 81.7; primary wool processing fibre wastes 0.2 - 0.3; saturated aqueous borax solution 18.0 - 22.0.

EFFECT: high strength of expanded clay.

2 cl, 2 tbl

Description

Изобретение относится к промышленности строительных материалов и касается производства керамзитаThe invention relates to the building materials industry and for the production of expanded clay

Известна сырьевая смесь для производства керамзита» содержащая, мас.%: глинистое сырье 75,5-76,8; волокнистые отходы первичной переработки шерсти 0,9-1,4; вода - остальное [1].Known raw mixture for the production of expanded clay "containing, wt.%: Clay raw materials 75.5-76.8; fibrous waste from primary wool processing 0.9-1.4; water - the rest [1].

Задачей изобретения является повышение прочности керамзита, полученного из сырьевой смеси.The objective of the invention is to increase the strength of expanded clay obtained from a raw mix.

Технический результат достигается тем, что сырьевая смесь для производства керамзита, содержащая глинистое сырье, волокнистые отходы первичной переработки шерсти, воду, содержит борную кислоту в количестве, необходимом для образования насыщенного водного раствора, при следующем соотношении компонентов, мас.%: глинистое сырье 77,8-81,7; волокнистые отходы первичной переработки шерсти 0,2-0,3; насыщенный водный раствор борной кислоты 18,0-22,0.The technical result is achieved in that the feed mixture for the production of expanded clay, containing clay raw materials, fibrous waste from the primary processing of wool, water, contains boric acid in the amount necessary to form a saturated aqueous solution, in the following ratio of components, wt.%: Clay raw material 77, 8-81.7; fibrous waste from primary wool processing 0.2-0.3; saturated aqueous solution of boric acid 18.0-22.0.

Технический результат достигается также тем, что сырьевая смесь для производства керамзита, содержащая глинистое сырье, волокнистые отходы первичной переработки шерсти, воду, отличающаяся тем, что содержит буру в количестве, необходимом для образования насыщенного водного раствора, при следующем соотношении компонентов, мас.%: глинистое сырье 77,8-81,7; волокнистые отходы первичной переработки шерсти 0,2-0,3; насыщенный водный раствор буры 18,0-22,0.The technical result is also achieved in that the raw material mixture for the production of expanded clay, containing clay raw materials, fibrous waste from the primary processing of wool, water, characterized in that it contains borax in the amount necessary for the formation of a saturated aqueous solution, in the following ratio, wt.%: clay raw materials 77.8-81.7; fibrous waste from primary wool processing 0.2-0.3; saturated aqueous solution of borax 18.0-22.0.

В табл.1 и 2 приведены составы сырьевой смеси для производства керамзита.Tables 1 and 2 show the composition of the raw mix for the production of expanded clay.

Таблица 1Table 1 Состав №Composition No. КомпонентыComponents Прочность керамзита при сжатии, МПаExpanded clay compressive strength, MPa Глинистое сырьеClay raw materials Волокнистые отходы первичной переработки шерстиFibrous waste from primary wool processing Насыщенный водный раствор борной кислотыSaturated aqueous boric acid solution 1one 77,877.8 0,20.2 22,022.0 4-54-5 22 79,7579.75 0,250.25 20,020,0 4-54-5 33 81,781.7 0,30.3 18,018.0 4-54-5

Таблица 2table 2 Состав №Composition No. КомпонентыComponents Прочность керамзита при сжатии, МПаExpanded clay compressive strength, MPa Глинистое сырьеClay raw materials Волокнистые отходы первичной переработки шерстиFibrous waste from primary wool processing Насыщенный водный раствор бурыSaturated aqueous solution of borax 1one 77,877.8 0,20.2 22,022.0 4-54-5 22 79,7579.75 0,250.25 20.020.0 4-54-5 33 81,781.7 0,30.3 18,018.0 4-54-5

В составе сырьевой смеси используют качественное легкоплавкое глинистое сырье любых месторождений.As part of the raw material mixture, high-quality low-melting clay raw materials of any deposits are used.

Компоненты дозируют в требуемых количествах и смешивают. Из полученной сырьевой смеси формуют гранулы, которые сушат и обжигают при температуре 950-1050°C.The components are metered in the required amounts and mixed. Granules are formed from the resulting raw material mixture, which are dried and calcined at a temperature of 950-1050 ° C.

Источники информацииInformation sources

1. SU 628129, C04B 14/12, 1978.1. SU 628129, C04B 14/12, 1978.

Claims

1. The raw material mixture for the production of expanded clay, containing clay raw materials, fibrous waste from the primary processing of wool, water, characterized in that it contains boric acid in the amount necessary for the formation of a saturated aqueous solution, in the following ratio, wt.%:
clay raw materials 77.8-81.7 fibrous waste of primary processing of wool 0.2-0.3 saturated aqueous boric acid solution 18.0-22.0

2. The raw material mixture for the production of expanded clay, containing clay raw materials, fibrous waste from the primary processing of wool, water, characterized in that it contains borax in the amount necessary for the formation of a saturated aqueous solution, in the following ratio, wt.%:
clay raw materials 77.8-81.7 fibrous waste of primary processing of wool 0.2-0.3 saturated borax 18.0-22.0