RU2562073C1

RU2562073C1 - Furnace charge for porous filler production

Info

Publication number: RU2562073C1
Application number: RU2014142495/03A
Authority: RU
Inventors: Юлия Алексеевна Щепочкина
Original assignee: Юлия Алексеевна Щепочкина
Priority date: 2014-10-21
Filing date: 2014-10-21
Publication date: 2015-09-10

Abstract

FIELD: construction.

SUBSTANCE: furnace charge for porous filler production contains, wt %: montmorillonite clay 95.5-97.0, coal 1.0-1.5 ground until passing through the mesh No. 0.63, kaolin 1.0-1.5 sifted through the mesh No. 5, impregnated with saturated water solution of solution sodium borate and wood sawdust 1.0-1.5 dried up to humidity no more than 6%.

EFFECT: increase of strength of the porous filler produced from furnace charge.

1 tbl

Description

Изобретение относится к производству пористых заполнителей для бетонов.The invention relates to the production of porous aggregates for concrete.

Известна шихта для производства пористого заполнителя, содержащая, мас.%: глина монтмориллонитовая 35,0-38,0; выгорающая добавка (уголь) 5,0-6,0; доломит 36,0-50,0 [1].A known mixture for the production of porous aggregate, containing, wt.%: Clay montmorillonite 35,0-38,0; burnable additive (coal) 5.0-6.0; dolomite 36.0-50.0 [1].

Задачей изобретения является повышение прочности пористого заполнителя, полученного из шихты.The objective of the invention is to increase the strength of the porous aggregate obtained from the mixture.

Технический результат достигается тем, что шихта для производства пористого заполнителя, содержащая глину монтмориллонитовую, уголь, дополнительно включает каолин и просеянные через сетку №5, пропитанные насыщенным водным раствором буры и высушенные до влажности не более 6% древесные опилки при следующем соотношении компонентов, мас.%: глина монтмориллонитовая 95,5-97,0; размолотый до прохождения через сетку №0,63 уголь 1,0-1,5; каолин 1,0-1,5; указанные древесные опилки 1,0-1,5.The technical result is achieved by the fact that the mixture for the production of porous aggregate containing montmorillonite clay, coal, additionally includes kaolin and sifted through mesh No. 5, impregnated with a saturated aqueous solution of borax and sawdust dried to a moisture content of not more than 6% in the following ratio of components, wt. %: montmorillonite clay 95.5-97.0; coal 1.0–1.5 milled before passing through mesh No. 0.63; kaolin 1.0-1.5; these wood chips are 1.0-1.5.

В таблице приведены составы шихты для производства пористого заполнителя.The table shows the composition of the mixture for the production of porous aggregate.

В составе шихты для производства пористого заполнителя используют: глины монтмориллонитовые, включающие Al-монтмориллонит и Fe-монтмориллонит (нонтронит), каолины любых месторождений.The composition of the mixture for the production of porous aggregate is used: montmorillonite clays, including Al-montmorillonite and Fe-montmorillonite (nontronite), kaolins of any deposits.

Подготовленные компоненты сырьевой смеси дозируют в требуемых количествах и смешивают. Полученную шихту увлажняют до 18-26% и формуют из нее гранулы размером 20-40 мм, которые сушат и обжигают при температуре 950-1100°С.The prepared components of the raw mix are metered in the required quantities and mixed. The resulting mixture is moistened to 18-26% and granules of 20-40 mm in size are formed from it, which are dried and fired at a temperature of 950-1100 ° C.

Источники информацииInformation sources

1. SU 1161500, С04В 31/00, 1985.1. SU 1161500, C04B 31/00, 1985.

Claims

A mixture for the production of porous aggregate containing montmorillonite clay, coal, characterized in that it further includes kaolin and sifted through mesh No. 5, impregnated with a saturated aqueous solution of borax and sawdust dried to a moisture content of not more than 6% in the following ratio of components, wt.%:
montmorillonite clay 95.5-97.0 coal milled before passing through mesh No. 0.63 1.0-1.5 kaolin 1.0-1.5 specified wood sawdust 1.0-1.5