Abstract

FIELD: chemistry.

SUBSTANCE: invention relates to a crude mixture for making artificial rock and can be used in the industry of construction materials. The crude mixture for making artificial rock contains the following, wt %: portland cement 22-24; iron sulphides 2-4; water 22-24; powdered water treatment sludge formed from removing hardness salts during water treatment at thermoelectric plants, with packed density of 850-900 kg/m³ 48-50.5; superplasticiser S-3 1-1.5.

EFFECT: improved workability of the crude mixture.

1 tbl

Description

Изобретение относится к промышленности строительных материалов.The invention relates to the construction materials industry.

Известна сырьевая смесь для получения искусственной породы, включающая, мас.%: цемент (портландцемент) 25-30; мука и песок на основе карбоната кальция до 55; оксиды металлов (железо, хром, свинец, ртуть) 2-10; гидроксиды металлов (железо, хром, свинец, ртуть) 2-12; силикаты кальция 2-3; силициды углерода (карбид кремния) 0,1-0,6; фторсиликаты 6; сульфиды железа и меди 0,4-0,8; щавелевая кислота 0,3-0,5; вода 10-23 [1].Known raw mix for producing artificial rock, including, wt.%: Cement (Portland cement) 25-30; flour and sand based on calcium carbonate up to 55; metal oxides (iron, chromium, lead, mercury) 2-10; metal hydroxides (iron, chromium, lead, mercury) 2-12; calcium silicates 2-3; carbon silicides (silicon carbide) 0.1-0.6; fluorosilicates 6; sulfides of iron and copper 0.4-0.8; oxalic acid 0.3-0.5; water 10-23 [1].

Задача изобретения состоит в повышении удобоукладываемости сырьевой смеси для получения искусственной породы.The objective of the invention is to improve the workability of the raw material mixture to obtain artificial rock.

Технический результат достигается тем, что сырьевая смесь для получения искусственной породы, включающая портландцемент, карбонатсодержащий песок, сульфиды железа, воду, в качестве карбонатсодержащего песка содержит порошок шлама водоочистки, образующийся в результате удаления солей жесткости при водоподготовке на тепловых электроцентралях, с насыпной плотностью 850-900 кг/м³ и суперпластификатор C-3 при следующем соотношении компонентов, мас.%: портландцемент 22-24; сульфиды железа 2-4; вода 22-24; указанный порошок шлама водоочистки 48-50,5; суперпластификатор C-3 1-1,5.The technical result is achieved in that the raw material mixture for producing artificial rock, including Portland cement, carbonate-containing sand, iron sulfides, water, contains carbonate-containing sand as a carbonate-containing sand, which is formed as a result of removal of hardness salts during water treatment at thermal power plants, with a bulk density of 850- 900 kg / m ³ and superplasticizer C-3 in the following ratio of components, wt.%: Portland cement 22-24; iron sulfides 2-4; water 22-24; the specified powder sludge water treatment 48-50,5; superplasticizer C-3 1-1.5.

Составы для получения искусственной породы приведены в таблице.Compositions for producing artificial rock are shown in the table.

ТаблицаTable КомпонентыComponents Состав, мас.%:Composition, wt.%: 1one 22 33 ПортландцементPortland cement 2222 2323 2424 Сульфиды железаIron sulfides 4four 3,53,5 33 ВодаWater 2222 2323 2424 Порошок шлама водоочисткиWater Treatment Sludge Powder 50,550,5 49,249.2 4848 Суперпластификатор C-3Superplasticizer C-3 1,51,5 1,31.3 1one

Подготавливают и дозируют сырьевые компоненты. Портландцемент смешивают с порошком шлама водоочистки, сульфидами железа, добавляют воду, суперпластификатор C-3 и готовят смесь. Приготовленной смесью заполняют металлические формы, выдерживают смесь в формах в течение 12 ч при температуре 20-25°C, а затем изделия извлекают из форм. Сырьевая смесь хорошо заполняет формы (подвижность не менее 4 см).Raw materials are prepared and dosed. Portland cement is mixed with water purification slurry powder, iron sulfides, water, C-3 superplasticizer are added and the mixture is prepared. The metal mixture is filled with the prepared mixture, the mixture is kept in the molds for 12 hours at a temperature of 20-25 ° C, and then the products are removed from the molds. The raw mix well fills the molds (mobility of at least 4 cm).

Источники информацииInformation sources

1. Патент №268011 ПНР, C04B, 1990.1. Patent No. 268011 Poland, C04B, 1990.

Claims

The raw material mixture for producing artificial rock, including Portland cement, carbonate-containing sand, iron sulfides, water, characterized in that the carbonate-containing sand contains water treatment sludge powder resulting from the removal of hardness salts during water treatment at thermal power plants with a bulk density of 850-900 kg / m ³ and superplasticizer C-3 in the following ratio of components, wt.%:
Portland cement 22-24 iron sulfides 2-4 water 22-24 specified sludge powder water treatment 48-50.5 superplasticizer C-3 1-1.5