RU2411202C1 - Mixure for making porous aggregate - Google Patents

Mixure for making porous aggregate Download PDF

Info

Publication number
RU2411202C1
RU2411202C1 RU2009146310/03A RU2009146310A RU2411202C1 RU 2411202 C1 RU2411202 C1 RU 2411202C1 RU 2009146310/03 A RU2009146310/03 A RU 2009146310/03A RU 2009146310 A RU2009146310 A RU 2009146310A RU 2411202 C1 RU2411202 C1 RU 2411202C1
Authority
RU
Russia
Prior art keywords
porous aggregate
making porous
dolomite
mixure
mixture
Prior art date
Application number
RU2009146310/03A
Other languages
Russian (ru)
Inventor
Юлия Алексеевна Щепочкина (RU)
Юлия Алексеевна Щепочкина
Original Assignee
Юлия Алексеевна Щепочкина
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Юлия Алексеевна Щепочкина filed Critical Юлия Алексеевна Щепочкина
Priority to RU2009146310/03A priority Critical patent/RU2411202C1/en
Application granted granted Critical
Publication of RU2411202C1 publication Critical patent/RU2411202C1/en

Abstract

FIELD: chemistry.
SUBSTANCE: invention relates to making porous aggregate for concrete. The mixture for making porous aggregate contains the following, wt %: montmorillonite clay 16.0-20.0; dolomite 38.0-40.0; ground scrap glass 40.0-46.0.
EFFECT: recycling scrap glass during production of porous filler.
1 cl, 1 tbl

Description

Изобретение относится к производству пористых заполнителей для бетонов.The invention relates to the production of porous aggregates for concrete.

Известна шихта для производства пористого заполнителя, содержащая, мас.%: глина монтмориллонитовая 35,0-38,0; уголь 5,0-6,0; доломит 36,0-50,0 [1].A known mixture for the production of porous aggregate, containing, wt.%: Clay montmorillonite 35,0-38,0; coal 5.0-6.0; dolomite 36.0-50.0 [1].

Задачей изобретения является утилизация стеклобоя в производстве пористого заполнителя.The objective of the invention is the disposal of cullet in the production of porous aggregate.

Технический результат достигается тем, что шихта для производства пористого заполнителя, содержащая глину монтмориллонитовую и доломит, дополнительно содержит молотый стеклобой при следующем соотношении компонентов, мас.%: глина монтмориллонитовая 16,0-20,0; доломит 38,0-40,0; молотый стеклобой 40,0-46,0.The technical result is achieved in that the mixture for the production of porous aggregate containing montmorillonite clay and dolomite, additionally contains ground cullet in the following ratio of components, wt.%: Montmorillonite clay 16.0-20.0; dolomite 38.0-40.0; ground cullet 40.0-46.0.

В составе шихты для производства пористого заполнителя используют глины монтмориллонитовые, включающие Al-монтмориллонит и Fe-монтмориллонит (нонтронит). Может быть использован бой любого силикатного стекла (медицинского, тарного, листового и др.).Montmorillonite clays, including Al-montmorillonite and Fe-montmorillonite (nontronite) are used in the mixture for the production of a porous aggregate. The battle of any silicate glass (medical, container, sheet, etc.) can be used.

В таблице приведены составы шихты для производства пористого заполнителя.The table shows the composition of the mixture for the production of porous aggregate.

ТаблицаTable КомпонентыComponents Состав, мас.%Composition, wt.% 1one 22 33 Глина монтмориллонитоваяMontmorillonite clay 16,016,0 18,018.0 20,020,0 ДоломитDolomite 38,038,0 39,039.0 40,040,0 Молотый стеклобойGround cullet 46,046.0 43,043.0 40,040,0

Компоненты сырьевой смеси дозируют в требуемых количествах. Доломит и предварительно очищенный от загрязнений стеклобой размалывают до получения порошков с удельной поверхностью 2000-4500 см2/г, смешивают, добавляют глину монтмориллонитовую и вновь смешивают. Полученную шихту увлажняют до 18-23% и формуют из нее гранулы размером 20-40 мм, которые сушат и обжигают в интервале температур 750-1050°С. Температуру обжига заполнителя подбирают в зависимости от используемого в составе шихты стеклобоя.The components of the raw mix are metered in the required quantities. Dolomite and pre-cleaned from contaminants cullet grind to obtain powders with a specific surface of 2000-4500 cm 2 / g, mix, add montmorillonite clay and mix again. The resulting mixture is moistened to 18-23% and granules of 20-40 mm in size are formed from it, which are dried and fired in the temperature range 750-1050 ° C. The firing temperature of the aggregate is selected depending on the cullet used in the mixture.

Источники информацииInformation sources

1. SU 1161500, С04В 31/00, 1985.1. SU 1161500, C04B 31/00, 1985.

Claims (1)

Шихта для производства пористого заполнителя, содержащая глину монтмориллонитовую и доломит, отличающаяся тем, что дополнительно содержит молотый стеклобой при следующем соотношении компонентов, мас.%:
глина монтмориллонитовая 16,0-20,0 доломит 38,0-40,0 молотый стеклобой 40,0-46,0
A mixture for the production of porous aggregate containing montmorillonite clay and dolomite, characterized in that it further contains ground cullet in the following ratio of components, wt.%:
montmorillonite clay 16.0-20.0 dolomite 38.0-40.0 ground cullet 40.0-46.0
RU2009146310/03A 2009-12-14 2009-12-14 Mixure for making porous aggregate RU2411202C1 (en)