RU2411211C1 - Mixure for making porous aggregate - Google Patents

Mixure for making porous aggregate Download PDF

Info

Publication number
RU2411211C1
RU2411211C1 RU2009147545/03A RU2009147545A RU2411211C1 RU 2411211 C1 RU2411211 C1 RU 2411211C1 RU 2009147545/03 A RU2009147545/03 A RU 2009147545/03A RU 2009147545 A RU2009147545 A RU 2009147545A RU 2411211 C1 RU2411211 C1 RU 2411211C1
Authority
RU
Russia
Prior art keywords
porous aggregate
mixture
making porous
dolomite
mixure
Prior art date
Application number
RU2009147545/03A
Other languages
Russian (ru)
Inventor
Юлия Алексеевна Щепочкина (RU)
Юлия Алексеевна Щепочкина
Original Assignee
Юлия Алексеевна Щепочкина
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Юлия Алексеевна Щепочкина filed Critical Юлия Алексеевна Щепочкина
Priority to RU2009147545/03A priority Critical patent/RU2411211C1/en
Application granted granted Critical
Publication of RU2411211C1 publication Critical patent/RU2411211C1/en

Abstract

FIELD: chemistry. ^ SUBSTANCE: invention relates to making porous aggregate for concrete. The mixture for making porous aggregate contains the following, wt %: montmorillonite clay 33.0-44.0; ground clay 5.0-6.0; ground dolomite 40.0-45.0; calcined soda 1.0-2.0; quartz sand 10.0-14.0. ^ EFFECT: increased strength of the of the porous aggregate made from the mixture. ^ 1 tbl

Description

Изобретение относится к производству пористых заполнителей для бетонов.The invention relates to the production of porous aggregates for concrete.

Известна шихта для производства пористого заполнителя, содержащая, мас.%: глина монтмориллонитовая 35,0-38,0; уголь 5,0-6,0; доломит 36,0-50,0 [1].A known mixture for the production of porous aggregate, containing, wt.%: Clay montmorillonite 35,0-38,0; coal 5.0-6.0; dolomite 36.0-50.0 [1].

Задачей изобретения является повышение прочности пористого заполнителя, полученного из шихты.The objective of the invention is to increase the strength of the porous aggregate obtained from the mixture.

Технический результат достигается тем, что шихта для производства пористого заполнителя, содержащая глину монтмориллонитовую, уголь, доломит, дополнительно содержит соду кальцинированную и кварцевый песок при следующем соотношении компонентов, мас.%: глина монтмориллонитовая 33,0-44,0; уголь 5,0-6,0; доломит 40,0-45,0; сода кальцинированная 1,0-2,0; кварцевый песок 10,0-14,0.The technical result is achieved in that the mixture for the production of porous aggregate containing montmorillonite clay, coal, dolomite, additionally contains soda ash and quartz sand in the following ratio of components, wt.%: Montmorillonite clay 33.0-44.0; coal 5.0-6.0; dolomite 40.0-45.0; soda ash 1.0-2.0; silica sand 10.0-14.0.

В таблице приведены составы шихты.The table shows the composition of the charge.

КомпонентыComponents Состав, мас.%Composition, wt.% 1one 22 33 Глина монтмориллонитоваяMontmorillonite clay 44,044.0 38,538.5 33,033.0 УгольCoal 5,05,0 5,55.5 6,06.0 ДоломитDolomite 40,040,0 42,542.5 45,045.0 Сода кальцинированнаяSoda ash 1,01,0 1,51,5 2,02.0 Кварцевый песокQuartz sand 10,010.0 12,012.0 14,014.0 Прочность заполнителя на сжатие (фракция 20-40 мм), МПаThe strength of the filler in compression (fraction 20-40 mm), MPa ~6~ 6 ~6~ 6 ~6~ 6

В состав шихты для производства пористого заполнителя используют глины монтмориллонитовые, включающие Al-монтмориллонит и Fe-монтмориллонит (нонтронит) c удельной поверхностью 2500-3500 см2/г.Montmorillonite clays, including Al-montmorillonite and Fe-montmorillonite (nontronite) with a specific surface of 2500-3500 cm 2 / g, are used in the mixture for the production of porous aggregate.

Компоненты сырьевой смеси дозируют в требуемых количествах. Уголь, кварцевый песок и доломит размалывают до удельной поверхности 2500-3000 см2/г, добавляют глину монтмориллонитовую, соду кальцинированную и смешивают. Полученную шихту увлажняют до 20-25%, формуют из нее пластическим способом гранулы, которые сушат и обжигают при температуре 900-1000°C.The components of the raw mix are metered in the required quantities. Coal, quartz sand and dolomite are ground to a specific surface of 2500-3000 cm 2 / g, montmorillonite clay, soda ash are added and mixed. The resulting mixture is moistened to 20-25%, granules are formed from it in a plastic way, which are dried and fired at a temperature of 900-1000 ° C.

При приготовлении образцов шихты, имеющей составы, представленные в таблице, уголь, кварцевый песок и доломит размалывают до крупности 2700 см2/г, шихту увлажняют до 27%, а сушку и обжиг гранул ведут при температуре 950°С.When preparing samples of the mixture having the compositions shown in the table, coal, quartz sand and dolomite are crushed to a particle size of 2700 cm 2 / g, the mixture is moistened to 27%, and the granules are dried and fired at a temperature of 950 ° C.

Источники информацииInformation sources

1. SU 1161500, C04B 31/00, 1985.1. SU 1161500, C04B 31/00, 1985.

Claims (1)

Шихта для производства пористого заполнителя, содержащая глину монтмориллонитовую, молотые уголь и доломит, отличающаяся тем, что дополнительно содержит соду кальцинированную и молотый кварцевый песок при следующем соотношении компонентов, мас.%:
глина монтмориллонитовая 33,0-44,0 уголь 5,0-6,0 доломит 40,0-45,0 сода кальцинированная 1,0-2,0 кварцевый песок 10,0-14,0
A mixture for the production of porous aggregate containing montmorillonite clay, ground coal and dolomite, characterized in that it further comprises soda ash and ground quartz sand in the following ratio, wt.%:
montmorillonite clay 33.0-44.0 coal 5.0-6.0 dolomite 40.0-45.0 soda ash 1.0-2.0 quartz sand 10.0-14.0
RU2009147545/03A 2009-12-21 2009-12-21 Mixure for making porous aggregate RU2411211C1 (en)