RU2310007C1

RU2310007C1 - Steel

Info

Publication number: RU2310007C1
Application number: RU2006117497/02A
Authority: RU
Inventors: Юли Алексеевна Щепочкина (RU); Юлия Алексеевна Щепочкина
Original assignee: Юлия Алексеевна Щепочкина
Priority date: 2006-05-22
Filing date: 2006-05-22
Publication date: 2007-11-10

Abstract

FIELD: ferrous metallurgy; railway construction and machine-building industry; production of the steel intended for usage in the railway construction and machine-building industry.

SUBSTANCE: the invention presents the steel intended for usage in the railway construction and machine-building industry The steel contains (in mass %): carbon - 1.0-1.5; silicon - 0.5-1.0; manganese - 13.0-15.0; the titanium - 0.1-0.2; cerium - 0.05-0.15; vanadium - 0.8-1.2; molybdenum - 3.0-4.0; cobalt - 1.0-1.5; the boron - 0.03-0.05; iron - the rest. Then invention ensures the increased strength of the products made out of the steel.

EFFECT: the invention ensures the increased strength of the products made out of the steel.

1 tbl

Description

Изобретение относится к области черной металлургии, в частности к составам марганцовистых сталей, используемых в строительно-дорожном машиностроении.The invention relates to the field of ferrous metallurgy, in particular to compositions of manganese steels used in road construction machinery.

Известна сталь, содержащая, мас.%: углерод 1,0-1,5; кремний 0,3-1,0; марганец 11,5-15,0; титан 0,05-0,1; церий 0,03-0,05; ванадий 0,05-0,25; железо - остальное [1].Known steel containing, wt.%: Carbon 1.0-1.5; silicon 0.3-1.0; manganese 11.5-15.0; titanium 0.05-0.1; cerium 0.03-0.05; vanadium 0.05-0.25; iron - the rest [1].

Известна также сталь, содержащая, мас.%: углерод 0,001-2,0; кремний ≤4,0; марганец 20,0-36,0; титан ≤5,0; церий ≤4,0; ванадий 0,001-5,0; молибден ≤ 5,0; кобальт ≤ 4,0; бор ≤1,0; железо - остальное [2].Steel is also known, containing, wt.%: Carbon 0,001-2,0; silicon ≤ 4.0; manganese 20.0-36.0; titanium ≤5.0; cerium ≤ 4.0; vanadium 0.001-5.0; molybdenum ≤ 5.0; cobalt ≤ 4.0; boron ≤1.0; iron - the rest [2].

Задача изобретения состоит в повышении прочности стали.The objective of the invention is to increase the strength of steel.

Технический результат достигается тем, что в стали, содержащей углерод, кремний, марганец, титан, церий, ванадий, молибден, кобальт, бор, железо, компоненты находятся при следующем соотношении, мас.%: углерод 1,0-1,5; кремний 0,5-1,0; марганец 13,0-15,0; титан 0,1-0,2; церий 0,05-0,15; ванадий 0,8-1,2; молибден 3,0-4,0; кобальт 1,0-1,5; бор 0,03-0,05; железо - остальное.The technical result is achieved by the fact that in steel containing carbon, silicon, manganese, titanium, cerium, vanadium, molybdenum, cobalt, boron, iron, the components are in the following ratio, wt.%: Carbon 1.0-1.5; silicon 0.5-1.0; manganese 13.0-15.0; titanium 0.1-0.2; cerium 0.05-0.15; vanadium 0.8-1.2; molybdenum 3.0-4.0; cobalt 1.0-1.5; boron 0.03-0.05; iron is the rest.

В таблице приведены составы стали.The table shows the compositions of steel.

ТаблицаTable КомпонетыComponents Состав, мас.%:Composition, wt.%: 1one 22 33 УглеродCarbon 1,01,0 1,31.3 1,51,5 КремнийSilicon 1,01,0 0,70.7 0,50.5 МарганецManganese 15,015.0 14,014.0 13,013.0 ТитанTitanium 0,20.2 0,150.15 0,10.1 ЦерийCerium 0,050.05 0,10.1 0,150.15 ВанадийVanadium 1,21,2 1.01.0 0,80.8 МолибденMolybdenum 3,03.0 3,53,5 4,04.0 КобальтCobalt 1,51,5 1,31.3 1,01,0 БорBoron 0,030,03 0,040.04 0,050.05 ЖелезоIron остальноеrest остальноеrest остальноеrest Предел прочности, МПаTensile strength, MPa 950-980950-980 980-1000980-1000 950-980950-980

Повышение прочности стали достигается за счет комплексного влияния компонентов, входящих в ее состав. Молибден и ванадий упрочняют твердый раствор. Кобальт улучшает металлическую структуру стали. Титан придает стали мелкозернистость. Введение в состав стали бора стабилизирует карбиды, уменьшает транскристаллизацию. Церий выполняет функцию раскислителя, нейтрализует влияние примесей серы.Increasing the strength of steel is achieved due to the complex effect of the components that make up its composition. Molybdenum and vanadium strengthen the solid solution. Cobalt improves the metal structure of steel. Titanium imparts fine grain to steel. The introduction of boron into the composition stabilizes carbides and reduces transcrystallization. Cerium acts as a deoxidizing agent and neutralizes the influence of sulfur impurities.

Сталь может быть выплавлена в электропечах. Отливки подвергают нагреву до температуры 1100-1150°C и закалке в воде.Steel can be smelted in electric furnaces. The castings are heated to a temperature of 1100-1150 ° C and quenched in water.

Источники информацииInformation sources

1. SU 399569, C22C 39/30, 1973.1. SU 399569, C22C 39/30, 1973.

2. JP 2005-023426 A, C22C 38/00, 2005.2. JP 2005-023426 A, C22C 38/00, 2005.

Claims

Steel containing carbon, silicon, manganese, titanium, cerium, vanadium, molybdenum, cobalt, boron, iron, characterized in that the components are in the following ratio, wt.%: Carbon 1.0-1.5; silicon 0.5-1.0; manganese 13.0-15.0; titanium 0.1-0.2; cerium 0.05-0.15; vanadium 0.8-1.2; molybdenum 3.0-4.0; cobalt 1.0-1.5; boron 0.03-0.05; iron is the rest.