RU2140503C1 - Wooden-metal block for floor

Info

Publication number: RU2140503C1
Application number: RU98105197A
Authority: RU
Inventors: П.Е. Дрындин
Original assignee: Дрындин Павел Егорович
Priority date: 1998-03-11
Filing date: 1998-03-11
Publication date: 1999-10-27

Abstract

FIELD: construction, in particular, manufacture of floors of domestic buildings and industrial objects. SUBSTANCE: the block comprises interconnected continuous hexahedral tiles of natural wood with vertical arrangement of wood fibre relative to the face surface. The tiles are made of compressed wood, for example, birch, and furnished with steel yokes in the lower base. The tiles are interconnected in the plane of engagement of the steel yokes by means of welding, for example, are welding with formation of a wooden-metal block with an enhanced modulus of elasticity and density of wood pulp up to 1000 kg/cu.m. EFFECT: enhanced wear resistance, durability, ecologically pure item for floor. 3 dwg

Description

Изобретение относится к строительству пола, главным образом промышленного назначения. The invention relates to the construction of floors, mainly for industrial use.

Изобретение может быть использовано в машиностроительных и других объектах, а так же для железнодорожных вокзалов, торговых объединений, учебных и медицинских строений, где требуется по условиям эксплуатации высокая износостойкость полов и повышенные требования, связанные с влиянием материала пола на здоровье человека. The invention can be used in engineering and other facilities, as well as for railway stations, trade associations, educational and medical buildings, where, according to operating conditions, high wear resistance of floors and increased requirements associated with the effect of floor material on human health are required.

Недостатком аналога конструкции торцового паркета по патенту RU 2081978 от 27.01.96 г. является: сплошные шестигранные плитки, изготовленные из натуральной древесины, главным образом из сосны и ели, произвольно установленный между собой на песчаную основу, часто раскалываются, образуя на полу песчаные углубления (ямы). Песчаные фракции от движения воздуха проникают в узлы трения технологического оборудования, выводя его таким образом, преждевременно из строя. Кроме того, указанная конструкция требует постоянного ремонта пола. The disadvantage of the analogue construction of the end parquet according to patent RU 2081978 dated 01/27/96 is: solid hexagonal tiles made of natural wood, mainly pine and spruce, arbitrarily installed between themselves on a sand base, often crack, forming sand depressions on the floor ( pits). Sand fractions from the movement of air penetrate into the friction units of the technological equipment, thus bringing it out prematurely out of order. In addition, this design requires constant floor repair.

Цель изобретения - создание износостойкое, долговечное, экологически чистое изделие для пола. The purpose of the invention is the creation of a wear-resistant, durable, environmentally friendly product for the floor.

Поставленная цель достигается тем, что в блоке для пола, включающем соединенные между собой сплошные шестигранные плитки из натуральной древесины с вертикальным расположением волокон древесины к лицевой поверхности, плитки выполнены из прессованной древесины, например березы, и соединены между собой в плоскости контакта стальных обойм в нижнем основании, посредством сварки, например дуговой, образуя древесно-металлический блок с повышенным модулем упругости и плотностью древесной массы до 1000 кг/м³.This goal is achieved by the fact that in the block for the floor, including interconnected solid hexagonal tiles made of natural wood with a vertical arrangement of wood fibers to the front surface, the tiles are made of pressed wood, such as birch, and are interconnected in the plane of contact of steel clips in the lower base, by welding, for example arc, forming a wood-metal block with a high modulus of elasticity and a density of wood pulp up to 1000 kg / m ³ .

На фиг.1 изображен древесно-металлический блок, а на фиг.2 - древесно-металлическая плитка и ее разрез. In Fig.1 shows a wood-metal block, and in Fig.2 - wood-metal tile and its section.

Прессование производится при влажности древесины от 8-12%. Pressing is carried out with wood moisture from 8-12%.

После прессования древесно-металлические плитки укладываются в рамочное устройство, где из них формируют древесно-металлический блок с определенными параметрами по площади. After pressing, wood-metal tiles are placed in a frame device, where they form a wood-metal block with certain parameters by area.

В зависимости от назначения поставки блоков потребителю назначается соответствующая технология обработки лицевой поверхности блока. Depending on the delivery destination of the blocks, the consumer is assigned the appropriate technology for processing the front surface of the block.

Например, по желанию потребителя может производиться дополнительная разделка неравномерных зазоров между прилегающими кромками плиток 1 (фиг. 1), придавая прилегающим кромкам 2 параллельность и заданную величину зазора (паза) между плитками. После разделки паз должен соответствовать 3-4 мм, с равномерным зазором прилегающих кромок. For example, at the request of the consumer, additional cutting of uneven gaps between the adjacent edges of the tiles 1 can be made (Fig. 1), giving the adjacent edges 2 parallelism and a given amount of gap (groove) between the tiles. After cutting, the groove should correspond to 3-4 mm, with a uniform gap of adjacent edges.

Полученные пазы между плитками заполняются клеем типа БФ-3 или БФ-4 с соответствующим наполнителем типа мелких опилок древесных или другого наполнителя. The resulting grooves between the tiles are filled with glue type BF-3 or BF-4 with a suitable filler such as fine wood sawdust or other filler.

Установка блоков на пол производится на ровное бетонное перекрытие или другие черновые полы. Installation of blocks on the floor is made on a smooth concrete floor or other rough floors.

Изготовленные полы из указанных блоков при их соединении образуют зазоры в 3-4 мм, которые также заполняются клеем с соответствующим наполнителем. Manufactured floors from these blocks when they are connected form gaps of 3-4 mm, which are also filled with glue with the appropriate filler.

Полученные полы из названных блоков обеспечивают хорошую эстетику, прочность и долговечность. The resulting floors from these blocks provide good aesthetics, strength and durability.

Указанные полы могут выдерживать нагрузку до 2,0 т на 1 м² пола, обеспечивая необходимые демпфирующие свойства на процесс работы узлов трения любого технологического оборудования, снижая шум работающих станков.These floors can withstand loads of up to 2.0 tons per 1 m ^{2 of} floor, providing the necessary damping properties for the operation of friction units of any technological equipment, reducing the noise of working machines.

Claims

Block for the floor, including interconnected solid hexagonal tiles made of natural wood with a vertical arrangement of wood fibers to the front surface, characterized in that the tiles are made of pressed wood, such as birch, and are provided with steel holders in the lower base, and connecting them together made in the plane of contact of steel clips by welding, for example, arc, forming a wood-metal block with a high modulus of elasticity and a density of wood pulp up to 1000 kg / m ³ .