RU2064677C1 - Method of quality testing of concrete

Info

Publication number: RU2064677C1
Application number: RU94043414A
Authority: RU
Inventors: З.М. Хадонов; Ю.С. Петров; И.Г. Ашуха
Original assignee: Северо-Кавказский государственный технологический университет
Priority date: 1994-12-08
Filing date: 1994-12-08
Publication date: 1996-07-27
Also published as: RU94043414A

Abstract

FIELD: construction industry. SUBSTANCE: invention relates to examination of properties of concrete used in industrial and civil construction. Examined and standard samples of concrete are prepared. Layer of conductive material is applied on sections of their surfaces. Electrodes are connected to them. Resistance of examined and standard samples is measured. Results of measurements of resistance of samples are compared by which quality of concrete is estimated. EFFECT: enhanced reliability of method, reduced testing costs. 1 dwg

Description

Изобретение относится к исследованию свойств бетона и может быть использовано для контроля качества бетона в промышленном и гражданском строительстве. The invention relates to the study of concrete properties and can be used to control the quality of concrete in industrial and civil engineering.

Известен способ определения трещин в бетонных и железобетонных конструкциях, согласно которому на изделие наносят полоски покрытия в виде сплавов различных металлов, создающих ЭДС, и о наличии трещин судят по прекращению ЭДС на участках между отводами ( 1 ). There is a method for determining cracks in concrete and reinforced concrete structures, according to which strips of coating in the form of alloys of various metals creating EMF are applied to the product, and the presence of cracks is judged by the termination of the EMF in the areas between the branches (1).

Недостатком данного способа является невозможность определения марки бетона, определяется только наличие дефектов (трещин). The disadvantage of this method is the inability to determine the brand of concrete, only the presence of defects (cracks) is determined.

Наиболее близким к заявляемому способу является способ определения прочностных свойств бетона, включающий изготовление испытуемого бетонного образца, пропускание через него электрического тока и измерение его электрической характеристики ( 2 ). Closest to the claimed method is a method for determining the strength properties of concrete, including the manufacture of the test concrete sample, passing an electric current through it and measuring its electrical characteristic (2).

Недостатком данного способа является невозможность определения марки бетона непосредственно образца, что сужает его функциональные возможности (контроль разрушающий). The disadvantage of this method is the inability to determine the concrete brand directly of the sample, which narrows its functionality (destructive control).

Задачей изобретения является определение марки бетона, измерением электрического сопротивления, непосредственно образца без его разрушения, расширение функциональных возможностей способа. The objective of the invention is to determine the brand of concrete, by measuring the electrical resistance, directly of the sample without destroying it, expanding the functionality of the method.

Технический результат достигается тем, что в контроле качества бетона, включающем изготовление испытуемого бетонного образца, пропускание через него электрического тока и измерение его электрической характеристики, предварительно изготавливают эталонные образцы различных марок бетона, наносят на контролируемые участки их поверхностей слой проводящего материала и подключают к ним электроды, измеряют электрическое сопротивление эталонных образцов и испытуемого бетонного образца, сравнивают результаты измерения электрического сопротивления эталонного и испытуемого образцов, по которым судят о качестве бетона. The technical result is achieved by the fact that in the quality control of concrete, including the manufacture of the test concrete sample, passing an electric current through it and measuring its electrical characteristics, reference samples of various concrete grades are pre-fabricated, a layer of conductive material is applied to the controlled areas of their surfaces and electrodes are connected to them , measure the electrical resistance of the reference samples and the test concrete sample, compare the results of measuring the electrical otivleniya reference and test specimens, which are judged on the quality of concrete.

Данный способ позволяет по изменению электрического сопротивления определять различные дефекты, трещины в испытуемом образце бетона и одновременно определять марку бетона, что расширяет его функциональные возможности. This method allows to determine various defects, cracks in the tested concrete sample by changing the electrical resistance and at the same time determine the concrete grade, which expands its functionality.

Сущность способа поясняется чертежом, на котором изображена общая схема измерения электрического сопротивления бетона. The essence of the method is illustrated in the drawing, which shows a General scheme for measuring the electrical resistance of concrete.

Эта схема состоит из эталонного или испытуемого образца 1, на противоположные поверхности которого наносят проводящее покрытие 2, измерительных электродов 3, соединенных проводами 4 с измерительным прибором 5 и струбцины 6. This circuit consists of a reference or test sample 1, on the opposite surfaces of which a conductive coating 2 is applied, measuring electrodes 3 connected by wires 4 to the measuring device 5 and clamp 6.

Предварительно готовят эталонные образцы 1 различных марок бетона: 100, 150, 200, 250. Reference samples of 1 different concrete grades are pre-prepared: 100, 150, 200, 250.

Две противоположные поверхности каждого эталонного образца 1 покрывают проводящим материалом 2. Подготовленные таким образом эталонные образцы 1 включают в измерительную цепь с помощью электродов 3 и закрепляют их вместе с образцом 1 струбциной 6. Включают измерительный прибор 5 (кило или мегаомметр) посредством соединительных проводов 4 и измеряют электрическое сопротивление каждого эталонного образца 1. Полученные данные заносят в таблицу (прилагается). Two opposite surfaces of each reference sample 1 are coated with a conductive material 2. Reference samples 1 prepared in this way are connected to the measuring circuit using electrodes 3 and clamped together with sample 1 with a clamp 6. The measuring device 5 is switched on (kilo or megaohmmeter) by connecting wires 4 and measure the electrical resistance of each reference sample 1. The obtained data are entered in the table (attached).

Затем аналогично готовят и измеряют электрическое сопротивление испытуемых бетонных образцов 1 и, сравнивая полученные результаты с эталонными, сразу определяют марку испытуемого образца бетона. Данные испытаний заносят в таблицу, в которой представлены результаты испытаний эталонных образцов разных марок и соответствующее им электрическое сопротивление и данные испытуемого бетонного образца. Then similarly prepare and measure the electrical resistance of the tested concrete samples 1 and, comparing the results with the reference, immediately determine the brand of the tested concrete sample. The test data are entered in the table, which presents the test results of reference samples of different grades and their corresponding electrical resistance and data of the tested concrete sample.

В зависимости от электрического сопротивления испытуемого бетонного образца по таблице определяют марку бетона. Depending on the electrical resistance of the test concrete sample, the concrete grade is determined from the table.

Существенным преимуществом данного способа является то, что способ по сравнению с прототипом и известным уровнем техники позволяет производить контроль качества бетона без разрушения образца. Способ может быть использован как для определения марки бетона, так и для контроля качества готовых изделий на наличие в нем дефектов, трещин, инородных включений. Позволяет снизить трудоемкость измерения, т.к. очень прост и надежен. A significant advantage of this method is that the method in comparison with the prototype and the prior art allows the quality control of concrete without destroying the sample. The method can be used both to determine the brand of concrete, and to control the quality of finished products for the presence of defects, cracks, foreign inclusions. It allows to reduce the complexity of the measurement, because very simple and reliable.

Claims

A method for controlling the quality of concrete, including manufacturing a test concrete sample, passing an electric current through it and measuring its electrical characteristics, characterized in that reference samples of various grades of concrete are pre-fabricated, a layer of conductive material is applied to the controlled areas of their surfaces and electrodes are connected to them, measured electrical resistance of the reference samples and the test concrete sample, compare the results of measuring the electrical resistance of the standard of the test and the samples used to judge the quality of concrete.