RU2019102025A - Фотокаталитические композиции и их применение для получения водных красок - Google Patents

Фотокаталитические композиции и их применение для получения водных красок Download PDF

Info

Publication number
RU2019102025A
RU2019102025A RU2019102025A RU2019102025A RU2019102025A RU 2019102025 A RU2019102025 A RU 2019102025A RU 2019102025 A RU2019102025 A RU 2019102025A RU 2019102025 A RU2019102025 A RU 2019102025A RU 2019102025 A RU2019102025 A RU 2019102025A
Authority
RU
Russia
Prior art keywords
composition according
photocatalytic composition
weight
paragraphs
range
Prior art date
Application number
RU2019102025A
Other languages
English (en)
Other versions
RU2019102025A3 (ru
RU2767466C2 (ru
Inventor
Массимо БЕРНАРДОНИ
Антонио ЧАНЧИ
Original Assignee
ЭйЭм ТЕКНОЛОДЖИ ЛИМИТЕД
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from GBGB1611117.1A external-priority patent/GB201611117D0/en
Priority claimed from GBGB1613189.8A external-priority patent/GB201613189D0/en
Application filed by ЭйЭм ТЕКНОЛОДЖИ ЛИМИТЕД filed Critical ЭйЭм ТЕКНОЛОДЖИ ЛИМИТЕД
Publication of RU2019102025A publication Critical patent/RU2019102025A/ru
Publication of RU2019102025A3 publication Critical patent/RU2019102025A3/ru
Application granted granted Critical
Publication of RU2767466C2 publication Critical patent/RU2767466C2/ru

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B22/00—Use of inorganic materials as active ingredients for mortars, concrete or artificial stone, e.g. accelerators, shrinkage compensating agents
    • C04B22/06—Oxides, Hydroxides
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B14/00—Use of inorganic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of inorganic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
    • C04B14/02—Granular materials, e.g. microballoons
    • C04B14/30—Oxides other than silica
    • C04B14/305—Titanium oxide, e.g. titanates
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J21/00—Catalysts comprising the elements, oxides, or hydroxides of magnesium, boron, aluminium, carbon, silicon, titanium, zirconium, or hafnium
    • B01J21/06—Silicon, titanium, zirconium or hafnium; Oxides or hydroxides thereof
    • B01J21/063—Titanium; Oxides or hydroxides thereof
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J35/00—Catalysts, in general, characterised by their form or physical properties
    • B01J35/20—Catalysts, in general, characterised by their form or physical properties characterised by their non-solid state
    • B01J35/23—Catalysts, in general, characterised by their form or physical properties characterised by their non-solid state in a colloidal state
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J35/00—Catalysts, in general, characterised by their form or physical properties
    • B01J35/30—Catalysts, in general, characterised by their form or physical properties characterised by their physical properties
    • B01J35/39—Photocatalytic properties
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B14/00—Use of inorganic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of inorganic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
    • C04B14/02—Granular materials, e.g. microballoons
    • C04B14/04—Silica-rich materials; Silicates
    • C04B14/08—Diatomaceous earth
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B14/00—Use of inorganic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of inorganic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
    • C04B14/02—Granular materials, e.g. microballoons
    • C04B14/04—Silica-rich materials; Silicates
    • C04B14/10—Clay
    • C04B14/106—Kaolin
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B14/00—Use of inorganic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of inorganic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
    • C04B14/02—Granular materials, e.g. microballoons
    • C04B14/04—Silica-rich materials; Silicates
    • C04B14/22—Glass ; Devitrified glass
    • C04B14/24—Glass ; Devitrified glass porous, e.g. foamed glass
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B20/00—Use of materials as fillers for mortars, concrete or artificial stone according to more than one of groups C04B14/00 - C04B18/00 and characterised by shape or grain distribution; Treatment of materials according to more than one of the groups C04B14/00 - C04B18/00 specially adapted to enhance their filling properties in mortars, concrete or artificial stone; Expanding or defibrillating materials
    • C04B20/0016—Granular materials, e.g. microballoons
    • C04B20/002—Hollow or porous granular materials
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B24/00—Use of organic materials as active ingredients for mortars, concrete or artificial stone, e.g. plasticisers
    • C04B24/04—Carboxylic acids; Salts, anhydrides or esters thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B24/00—Use of organic materials as active ingredients for mortars, concrete or artificial stone, e.g. plasticisers
    • C04B24/24—Macromolecular compounds
    • C04B24/26—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B24/00—Use of organic materials as active ingredients for mortars, concrete or artificial stone, e.g. plasticisers
    • C04B24/24—Macromolecular compounds
    • C04B24/26—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • C04B24/2611—Polyalkenes
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B24/00—Use of organic materials as active ingredients for mortars, concrete or artificial stone, e.g. plasticisers
    • C04B24/24—Macromolecular compounds
    • C04B24/26—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • C04B24/2623—Polyvinylalcohols; Polyvinylacetates
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B24/00—Use of organic materials as active ingredients for mortars, concrete or artificial stone, e.g. plasticisers
    • C04B24/24—Macromolecular compounds
    • C04B24/26—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • C04B24/2682—Halogen containing polymers, e.g. PVC
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B24/00—Use of organic materials as active ingredients for mortars, concrete or artificial stone, e.g. plasticisers
    • C04B24/24—Macromolecular compounds
    • C04B24/26—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • C04B24/2688—Copolymers containing at least three different monomers
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B24/00—Use of organic materials as active ingredients for mortars, concrete or artificial stone, e.g. plasticisers
    • C04B24/24—Macromolecular compounds
    • C04B24/38—Polysaccharides or derivatives thereof
    • C04B24/383—Cellulose or derivatives thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B28/00—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements
    • C04B28/02—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements containing hydraulic cements other than calcium sulfates
    • C04B28/04—Portland cements
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B28/00—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements
    • C04B28/18—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements containing mixtures of the silica-lime type
    • C04B28/184—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements containing mixtures of the silica-lime type based on an oxide other than lime
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B41/00—After-treatment of mortars, concrete, artificial stone or ceramics; Treatment of natural stone
    • C04B41/45—Coating or impregnating, e.g. injection in masonry, partial coating of green or fired ceramics, organic coating compositions for adhering together two concrete elements
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D1/00—Coating compositions, e.g. paints, varnishes or lacquers, based on inorganic substances
    • C09D1/06—Coating compositions, e.g. paints, varnishes or lacquers, based on inorganic substances cement
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D7/00—Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
    • C09D7/40—Additives
    • C09D7/66—Additives characterised by particle size
    • C09D7/69—Particle size larger than 1000 nm
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2103/00—Function or property of ingredients for mortars, concrete or artificial stone
    • C04B2103/30—Water reducers, plasticisers, air-entrainers, flow improvers
    • C04B2103/304—Air-entrainers
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2103/00—Function or property of ingredients for mortars, concrete or artificial stone
    • C04B2103/50—Defoamers, air detrainers
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2103/00—Function or property of ingredients for mortars, concrete or artificial stone
    • C04B2103/54—Pigments; Dyes
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
    • C04B2111/00474—Uses not provided for elsewhere in C04B2111/00
    • C04B2111/00482—Coating or impregnation materials
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
    • C04B2111/00474—Uses not provided for elsewhere in C04B2111/00
    • C04B2111/00482—Coating or impregnation materials
    • C04B2111/00508—Cement paints
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
    • C04B2111/00474—Uses not provided for elsewhere in C04B2111/00
    • C04B2111/0081—Uses not provided for elsewhere in C04B2111/00 as catalysts or catalyst carriers
    • C04B2111/00827—Photocatalysts
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
    • C04B2111/20—Resistance against chemical, physical or biological attack
    • C04B2111/2038—Resistance against physical degradation
    • C04B2111/2061—Materials containing photocatalysts, e.g. TiO2, for avoiding staining by air pollutants or the like
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2201/00—Mortars, concrete or artificial stone characterised by specific physical values
    • C04B2201/30—Mortars, concrete or artificial stone characterised by specific physical values for heat transfer properties such as thermal insulation values, e.g. R-values

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Ceramic Engineering (AREA)
  • Materials Engineering (AREA)
  • Organic Chemistry (AREA)
  • Structural Engineering (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Inorganic Chemistry (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Wood Science & Technology (AREA)
  • Civil Engineering (AREA)
  • Nanotechnology (AREA)
  • Dispersion Chemistry (AREA)
  • Catalysts (AREA)
  • Paints Or Removers (AREA)
  • Building Environments (AREA)
  • Curing Cements, Concrete, And Artificial Stone (AREA)
  • Inks, Pencil-Leads, Or Crayons (AREA)
  • Health & Medical Sciences (AREA)
  • Molecular Biology (AREA)

Claims (45)

1. Фотокаталитическая композиция, содержащая
(a) по меньшей мере один неорганический связующий материал;
(b) по меньшей мере один фотокатализатор;
(c) по меньшей мере одну целлюлозу с очень низкой вязкостью;
(d) по меньшей мере один разжижающий агент;
(e) по меньшей мере один первый известковый наполнитель в виде частиц, среди которых по меньшей мере 95% по массе имеют размер не более 40 мкм;
(f) по меньшей мере один второй известковый наполнитель в виде частиц, среди которых по меньшей мере 95% по массе имеют размер не более 20 мкм;
(g) по меньшей мере один теплоизоляционный материал, содержащий полые керамические сферы с диаметром в субмиллиметровом диапазоне, и
(h) полые микросферы из боросиликатного стекла.
2. Фотокаталитическая композиция по п. 1, отличающаяся тем, что
(a) содержание неорганического связующего материала, который представляет собой связующий материал на цементной основе, находится в диапазоне от 20% до 50% по массе;
(b) содержание фотокатализатора, который представляет собой частицы диоксида титана, обладающие фотокаталитической активностью в видимой области спектра, составляет от 0,5% до 5% по массе;
(c) содержание целлюлозы с очень низкой вязкостью находится в диапазоне от 0,8% до 2,2% по массе;
(d) содержание разжижающего агента находится в диапазоне от 0,1% до 1,2% по массе;
(e) содержание первого известкового наполнителя находится в диапазоне от 15% до 35% по массе;
(f) содержание второго известкового наполнителя находится в диапазоне от 15% до 35% по массе;
(g) содержание теплоизоляционного материала, содержащего полые керамические сферы с диаметром в субмиллиметровом диапазоне, находится в диапазоне от 0,1% до 4% по массе;
(h) содержание полых микросфер из боросиликатного стекла находится в диапазоне от 0,1% до 4% по массе.
3. Фотокаталитическая композиция по п. 2, отличающаяся тем, что указанный связующий материал на цементной основе (a) представляет собой портландцемент.
4. Фотокаталитическая композиция по п. 2 или 3, отличающаяся тем, что указанный фотокатализатор представляет собой частицы диоксида титана в кристаллической форме анатаза.
5. Фотокаталитическая композиция по п. 4, отличающаяся тем, что указанные частицы диоксида титана в кристаллической форме анатаза имеют гранулометрический состав, где по меньшей мере 95% по массе частиц имеют размер не более 50 нм, предпочтительно не более 20 нм.
6. Фотокаталитическая композиция по п. 4 или 5, отличающаяся тем, что указанный фотокаталитический диоксид титана присутствует в смеси с нефотокаталитическим диоксидом титана.
7. Фотокаталитическая композиция по п. 6, отличающаяся тем, что содержание указанного нефотокаталитического диоксида титана находится в диапазоне от 2% до 10% по массе.
8. Фотокаталитическая композиция по любому из пп. 1-7, отличающаяся тем, что указанная целлюлоза (c) имеет вязкость по Брукфилду RVT при 20°C от 100 до 70000 мПа·с, предпочтительно от 100 до 30000 мПа·с, более предпочтительно от 200 до 10000 мПа·с.
9. Фотокаталитическая композиция по любому из пп. 1-8, дополнительно содержащая: (i) по меньшей мере один гидрофобный виниловый полимер, предпочтительно терполимер винилхлорида, этилена и сложного винилового эфира CH2=CH-O-C(=O)-R, где R представляет собой линейный или разветвленный C4-C24 алкил.
10. Фотокаталитическая композиция по п. 9, отличающаяся тем, что содержание указанного по меньшей мере одного гидрофобного винилового полимера находится в диапазоне от 1% до 6% по массе.
11. Фотокаталитическая композиция по любому из пп. 1-10, отличающаяся тем, что указанный разжижающий агент представляет собой поликарбоновую кислоту.
12. Фотокаталитическая композиция по любому из пп. 1-11, включающая метакаолин в количестве в диапазоне от 1,5% до 10% по массе.
13. Фотокаталитическая композиция по любому из пп. 1-12, включающая противопенный агент в количестве в диапазоне от 0,1% до 2,8% по массе.
14. Фотокаталитическая композиция по любому из пп. 1-13, отличающаяся тем, что указанные полые керамические сферы с размером в субмиллиметровом диапазоне имеют теплопроводность менее 0,20 Вт/(м·К).
15. Фотокаталитическая композиция по любому из пп. 1-14, отличающаяся тем, что указанные полые керамические сферы с размером в субмиллиметровом диапазоне включают теплоотражающее покрытие.
16. Фотокаталитическая композиция по любому из пп. 1-15, отличающаяся тем, что указанные полые керамические сферы с размером в субмиллиметровом диапазоне имеют средний диаметр менее 200 мкм.
17. Фотокаталитическая композиция по п. 16, отличающаяся тем, что указанные полые керамические сферы с размером в субмиллиметровом диапазоне имеют средний диаметр менее 50 мкм.
18. Фотокаталитическая композиция по любому из пп. 1-17, включающая быстро диспергируемый пигмент.
19. Применение фотокаталитической композиции по любому из пп. 1-18, для нанесения покрытия на строительные конструкции для уменьшения количества загрязняющих агентов.
20. Применение по п. 19, отличающееся тем, что в указанную фотокаталитическую композицию добавляют воду в заданном количестве путем смешения до получения гомогенного и текучего продукта.
21. Применение по п. 20, отличающееся тем, что массовое отношение воды к связующему материалу на цементной основе (a) составляет от 0,2 до 0,8.
22. Применение по любому из пп. 19-21, отличающееся тем, что указанная фотокаталитическая композиция после нанесения и сушки образует слой покрытия, имеющий толщину от 0,05 мм до 1 мм, предпочтительно от 0,1 до 0,5 мм.
23. Фотокаталитическая композиция по любому из пп. 1-18, которая (i) не включает тяжелые металлы и органические растворители, или (ii) в которой содержание летучих органических соединений (ЛОС) составляет менее 0,35 г/литр, или (iii) включает воздухововлекающие агенты, или (iv) включает кизельгур.
24. Покрытие, полученное с применением фотокаталитической композиции по любому из пп. 1-18 или 23.
25. Строение или конструкция, на которое(-ую) нанесено покрытие, включающее фотокаталитическую композицию по любому из пп. 1-18 или 23.
26. Строение или конструкция по п. 25, на наружную поверхность которого нанесено покрытие.
27. Строение или конструкция по п. 25, на внутреннюю поверхность которого нанесено покрытие.
28. Способ получения фотокаталитической композиции, включающий смешение компонентов по любому из пп. 1-18 или 23.
29. Способ по п. 28, включающий смешение компонентов в течение периода времени, достаточного для обеспечения хорошей гомогенизации.
RU2019102025A 2016-06-27 2017-06-27 Фотокаталитические композиции и их применение для получения водных красок RU2767466C2 (ru)