RU2014151475A - Композиция настенного и потолочного покрытия, имеющего теплоизоляционные свойства - Google Patents
Композиция настенного и потолочного покрытия, имеющего теплоизоляционные свойства Download PDFInfo
- Publication number
- RU2014151475A RU2014151475A RU2014151475A RU2014151475A RU2014151475A RU 2014151475 A RU2014151475 A RU 2014151475A RU 2014151475 A RU2014151475 A RU 2014151475A RU 2014151475 A RU2014151475 A RU 2014151475A RU 2014151475 A RU2014151475 A RU 2014151475A
- Authority
- RU
- Russia
- Prior art keywords
- coating composition
- composition according
- microspheres
- layer
- paragraphs
- Prior art date
Abstract
1. Композиция покрытия, содержащаяот 4 до 17мас.% полых микросфер, имеющих теплопроводность (обозначенную лямбда) ниже 0,1 Вт·м·K,от 0,05 до 1 мас.%, по меньшей мере, одного линейного спирта, у которого углеводородная цепь содержит, по меньшей мере, 8 атомов углерода,от 5 до 25 мас.%, по меньшей мере, одного связующего агента, выбранного из диспергируемых в воде или водорастворимых полимеров, имеющих температуру стеклования (T), равную или меньшую чем 65°С,от 25 до 50 мас.% негидравлического связующего, выбранного из следующих минеральных и металлических наполнителей: из карбоната щелочно-земельного металла, оксида алюминия, диоксида кремния, силиката металла, выбранного из алюминия, щелочных металлов и щелочно-земельных металлов и их смеси, указанные наполнители имеют средний размер частиц в пределах от 5 до 100 мкм,от 0,1 до 1 мас.%, по меньшей мере, одного загустителя,воду,проценты массовые выражаются в мас.% сухого вещества по отношению к общей массе композиции покрытия.2. Композиция покрытия по п. 1, отличающаяся тем, что полые микросферы имеют реальную плотность в пределах от 0,05 до 0,5 г/см.3. Композиция покрытия по любому из пп. 1 и 2, отличающаяся тем, что полые микросферы представляют собой полые микросферы, имеющие средний размер частиц (D50) в пределах от 0,10 до 100 мкм.4. Композиция покрытия по п. 1, отличающаяся тем, что полые микросферы представляют собой полые стеклянные или полимерные микросферы, выбранные из микросфер из боросиликата натрия и кальция, микросфер из алюмосиликата и микросфер из винилиденхлорида/акрилонитрила.5. Композиция покрытия по п. 1, отличающаяся тем, что спирт представляет собой смесь линейных жирных спиртов формулы ROH, где R представляет собой линейную углеводородную цепь, насыщенн
Claims (14)
1. Композиция покрытия, содержащая
от 4 до 17мас.% полых микросфер, имеющих теплопроводность (обозначенную лямбда) ниже 0,1 Вт·м-1·K-1,
от 0,05 до 1 мас.%, по меньшей мере, одного линейного спирта, у которого углеводородная цепь содержит, по меньшей мере, 8 атомов углерода,
от 5 до 25 мас.%, по меньшей мере, одного связующего агента, выбранного из диспергируемых в воде или водорастворимых полимеров, имеющих температуру стеклования (Tg), равную или меньшую чем 65°С,
от 25 до 50 мас.% негидравлического связующего, выбранного из следующих минеральных и металлических наполнителей: из карбоната щелочно-земельного металла, оксида алюминия, диоксида кремния, силиката металла, выбранного из алюминия, щелочных металлов и щелочно-земельных металлов и их смеси, указанные наполнители имеют средний размер частиц в пределах от 5 до 100 мкм,
от 0,1 до 1 мас.%, по меньшей мере, одного загустителя,
воду,
проценты массовые выражаются в мас.% сухого вещества по отношению к общей массе композиции покрытия.
2. Композиция покрытия по п. 1, отличающаяся тем, что полые микросферы имеют реальную плотность в пределах от 0,05 до 0,5 г/см3.
3. Композиция покрытия по любому из пп. 1 и 2, отличающаяся тем, что полые микросферы представляют собой полые микросферы, имеющие средний размер частиц (D50) в пределах от 0,10 до 100 мкм.
4. Композиция покрытия по п. 1, отличающаяся тем, что полые микросферы представляют собой полые стеклянные или полимерные микросферы, выбранные из микросфер из боросиликата натрия и кальция, микросфер из алюмосиликата и микросфер из винилиденхлорида/акрилонитрила.
5. Композиция покрытия по п. 1, отличающаяся тем, что спирт представляет собой смесь линейных жирных спиртов формулы ROH, где R представляет собой линейную углеводородную цепь, насыщенную или ненасыщенную, имеющую от 8 до 30 атомов углерода, и винилполиола (полиолов), имеющих Tg в пределах от 75 до 95°С.
6. Композиция покрытия по п. 1, отличающаяся тем, что диспергируемый в воде или водорастворимый полимер выбирают из сополимеров стирола и (мет)акриловой кислоты, сополимеров стирола и сложного эфира (мет)акриловой кислоты, сополимеров стирола и (мет)акриламида, и указанные сополимеры могут быть силанизированными, гомополимеров и сополимеров бутадиена, таких как полибутадиен и полибутадиен-стирол, виниловых полимеров, таких как поливинилхлорид и поливинилацетат, полиуретанов и их смеси.
7. Композиция покрытия по п. 1, отличающаяся тем, что минеральный наполнитель выбирают из карбоната кальция и диоксида кремния.
8. Композиция покрытия по п. 1, отличающаяся тем, что загуститель выбирают из глины, загустителей на основе полисахарида и их смеси, необязательно, в присутствии соды.
9. Способ нанесения композиции по любому из пп. 1-8, включающий, по меньшей мере, следующие стадии:
(i) нанесение указанной композиции в виде одного или нескольких последовательных слоев на поверхность подложки с использованием валика и/или инструмента для выравнивания, затем
(ii) сушку указанного слоя, затем
(iii) необязательное нанесение на указанный отвержденный слой покрытия слоя неизоляционного материала.
10. Способ по п. 9, отличающийся тем, что он включает, по меньшей мере, следующие стадии:
(i′) нанесение первого слоя композиции по любому из пп. 1-8 на поверхность подложки с использованием валика, затем
(ii′) нанесение второго слоя композиции по любому из пп. 1-8 на указанный первый слой, нанесенный с использованием инструмента для выравнивания, время, которое проходит между первым и вторым нанесение композиции, составляет меньше чем 30 мин, или
(ii′′) выравнивание поверхности с использованием инструмента для выравнивания без добавления дополнительного материала, затем
(iii′) сушку композиции покрытия, затем
(iv′) необязательное нанесение на указанный отвержденный слой покрытия слоя неизоляционного материала.
11. Способ по п. 9, отличающийся тем, что он включает, по меньшей мере, следующие стадии:
(i′′′) нанесение слоя композиции по любому из пп. 1-8 на поверхность подложки с использованием инструмента для выравнивания, затем
(ii′′′) сушку композиции покрытия, затем
(iii′′′) необязательное нанесение на указанный отвержденный слой покрытия слоя неизоляционного материала.
12. Способ по п. 9 или 10, отличающийся тем, что валик, используемый на стадии (i) или (i′), выбирают из валиков из пены с ячеистой структурой.
13. Подложка, покрытая отвержденным слоем композиции покрытия с толщиной в пределах от 0,5 до 3 мм, полученным способом по любому из пп. 9-12.
14. Применение композиции по любому из пп. 1-8 в качестве отделочного и/или теплоизоляционного покрытия для стен и потолков.