RU2011136161A - Высокотемпературное теплозащитное покрытие - Google Patents

Высокотемпературное теплозащитное покрытие Download PDF

Info

Publication number
RU2011136161A
RU2011136161A RU2011136161/05A RU2011136161A RU2011136161A RU 2011136161 A RU2011136161 A RU 2011136161A RU 2011136161/05 A RU2011136161/05 A RU 2011136161/05A RU 2011136161 A RU2011136161 A RU 2011136161A RU 2011136161 A RU2011136161 A RU 2011136161A
Authority
RU
Russia
Prior art keywords
microspheres
diameter
wall thickness
coating according
hollow ceramic
Prior art date
Application number
RU2011136161/05A
Other languages
English (en)
Other versions
RU2482146C2 (ru
Inventor
Юрий Александрович Григорьев
Original Assignee
Общество С Ограниченной Ответственностью "Овк-Руссия"
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Общество С Ограниченной Ответственностью "Овк-Руссия" filed Critical Общество С Ограниченной Ответственностью "Овк-Руссия"
Priority to RU2011136161/05A priority Critical patent/RU2482146C2/ru
Priority to PCT/RU2012/000714 priority patent/WO2013032368A2/ru
Publication of RU2011136161A publication Critical patent/RU2011136161A/ru
Application granted granted Critical
Publication of RU2482146C2 publication Critical patent/RU2482146C2/ru

Abstract

1. Теплозащитное покрытие, содержащее полые керамические или корундовые микросферы, связующее и воду, отличающееся тем, что в качестве связующего содержит одно из группы, включающей алюмоборфосфат, алюмохромфосфат, полититанат калия или смесь алюмохромфосфата и полититаната калия, при следующем соотношении компонентов, мас.%:2. Теплозащитное покрытие по п.1, отличающееся тем, что в качестве полых керамических микросфер содержит алюмосиликатные микросферы золы уноса с диаметром 3-150 мкм и толщиной стенок 1-6 мкм.3. Теплозащитное покрытие по п.1, отличающееся тем, что в качестве полых керамических микросфер содержит стеклокерамические микросферы с диаметром 3-100 мкм и толщиной стенок 0,3-1,0 мкм.4. Теплозащитное покрытие по п.1, отличающееся тем, что в качестве полых корундовых микросфер содержит микросферы с диаметром 3-90 мкм и толщиной стенок 0,5-3,0 мкм.

Claims (4)

1. Теплозащитное покрытие, содержащее полые керамические или корундовые микросферы, связующее и воду, отличающееся тем, что в качестве связующего содержит одно из группы, включающей алюмоборфосфат, алюмохромфосфат, полититанат калия или смесь алюмохромфосфата и полититаната калия, при следующем соотношении компонентов, мас.%:
полые керамические или корундовые микросферы 67-85 алюмоборфосфат или алюмохромфосфат или полититанат   калия или смесь алюмохромфосфата и полититаната калия 10-30 вода остальное
2. Теплозащитное покрытие по п.1, отличающееся тем, что в качестве полых керамических микросфер содержит алюмосиликатные микросферы золы уноса с диаметром 3-150 мкм и толщиной стенок 1-6 мкм.
3. Теплозащитное покрытие по п.1, отличающееся тем, что в качестве полых керамических микросфер содержит стеклокерамические микросферы с диаметром 3-100 мкм и толщиной стенок 0,3-1,0 мкм.
4. Теплозащитное покрытие по п.1, отличающееся тем, что в качестве полых корундовых микросфер содержит микросферы с диаметром 3-90 мкм и толщиной стенок 0,5-3,0 мкм.
RU2011136161/05A 2011-08-31 2011-08-31 Высокотемпературное теплозащитное покрытие RU2482146C2 (ru)