PL415816A1 - Sposób wytwarzania płytek klinkierowych - Google Patents
Sposób wytwarzania płytek klinkierowychInfo
- Publication number
- PL415816A1 PL415816A1 PL415816A PL41581616A PL415816A1 PL 415816 A1 PL415816 A1 PL 415816A1 PL 415816 A PL415816 A PL 415816A PL 41581616 A PL41581616 A PL 41581616A PL 415816 A1 PL415816 A1 PL 415816A1
- Authority
- PL
- Poland
- Prior art keywords
- weight
- raw materials
- clay
- solid fuel
- fe2o3
- Prior art date
Abstract
Przedmiotem zgłoszenia jest sposób wytwarzania ceramicznych płytek klinkierowych, polegający na przygotowaniu zestawu surowcowego zawierającego 55 - 65% wagowych surowców ilastych, 25 - 35% wagowych surowców skaleniowych, do 10% wagowych piasku kwarcowego oraz dodatki reologiczne i przemysłowe materiały odpadowe jako uzupełnienie do 100% wagowych zestawu, a następnie rozdrobnieniu i wymieszaniu surowców oraz poddaniu ich kolejno procesom: granulowania, formowania, suszenia i obróbki termicznej w temperaturze 1000 - 1200°C. Sposób ten charakteryzuje się tym, że do zestawu surowcowego dodaje się jako materiał odpadowy lub w miejsce części surowców ilastych i/lub skaleniowych 1 - 20% wagowych pozostałości mineralnej z procesu elektrochemicznego utleniania paliwa stałego w generatorach energii elektrycznej zawierającej 12 - 40% wagowych Fe2O3, 20 - 24% wagowych CaO, 10 - 15% wagowych Al2O3, 7 - 13% wagowych SO3, 6 - 10% wagowych SiO2, 8 -13% wagowych MgO, do 5% wagowych Na2O, do 3% wagowych K2O, do 0,5% wagowego P2O5 oraz do 0,5% wagowego BaO, a wielkości cząstek pozostałości mineralnej wynosi od 100 do 1000 nm, przy czym paliwo stałe jest w postaci mieszaniny składającej się z 85 - 95% wagowych sproszkowanego węgla kamiennego i 5 - 15% wagowych katalizatora Fe2O3.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PL415816A PL232761B1 (pl) | 2016-01-15 | 2016-01-15 | Sposób wytwarzania płytek klinkierowych |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PL415816A PL232761B1 (pl) | 2016-01-15 | 2016-01-15 | Sposób wytwarzania płytek klinkierowych |
Publications (2)
Publication Number | Publication Date |
---|---|
PL415816A1 true PL415816A1 (pl) | 2017-07-17 |
PL232761B1 PL232761B1 (pl) | 2019-07-31 |
Family
ID=59298134
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PL415816A PL232761B1 (pl) | 2016-01-15 | 2016-01-15 | Sposób wytwarzania płytek klinkierowych |
Country Status (1)
Country | Link |
---|---|
PL (1) | PL232761B1 (pl) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN110981428A (zh) * | 2019-12-10 | 2020-04-10 | 谢贵全 | 一种scs亚纳米硅晶石及其制备方法 |
-
2016
- 2016-01-15 PL PL415816A patent/PL232761B1/pl unknown
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN110981428A (zh) * | 2019-12-10 | 2020-04-10 | 谢贵全 | 一种scs亚纳米硅晶石及其制备方法 |
Also Published As
Publication number | Publication date |
---|---|
PL232761B1 (pl) | 2019-07-31 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
Al Bakri Abdullah et al. | Optimization of alkaline activator/fly ash ratio on the compressive strength of manufacturing fly ash-based geopolymer | |
MA30306B1 (fr) | Compositions de glaçure | |
CN102942376A (zh) | 钙长石轻质耐火砖及其制备方法 | |
JPWO2014077251A1 (ja) | セメント組成物の製造方法 | |
SG11201901975UA (en) | Cement composition for high-temperature environment and concrete for high-temperature environment | |
JP6600140B2 (ja) | セメント混和材の製造方法及びセメント組成物の製造方法 | |
CN102850012A (zh) | 高钙固硫灰加气混凝土砌块的制作方法 | |
CN103771751A (zh) | 一种水泥增强剂的制备方法 | |
RU2013132415A (ru) | Наноцемент и способ его изготовления | |
JP2009114011A (ja) | セメント添加材及びセメント組成物 | |
PL415816A1 (pl) | Sposób wytwarzania płytek klinkierowych | |
KR101658887B1 (ko) | 금광미를 이용한 경량골재 제조 방법 | |
RU2508269C2 (ru) | Керамическая композиция для изготовления легковесного кирпича | |
RU2415101C1 (ru) | Керамическая масса для производства кирпича | |
RU2430059C1 (ru) | Керамическая масса | |
Galán-Arboledas et al. | Production of ceramic materials using only waste as raw materials | |
JP5702872B1 (ja) | セメント組成物 | |
JP2008222475A (ja) | 焼成物、セメント添加材及びセメント組成物 | |
JP2005104804A (ja) | 人工骨材 | |
RU2411210C1 (ru) | Керамическая масса для производства кирпича | |
JP5501705B2 (ja) | セメント添加材及びセメント組成物 | |
RU2351569C2 (ru) | Шихта для изготовления легковесного огнеупорного материала | |
JP2011084413A (ja) | セメント添加材及びセメント組成物 | |
PL415930A1 (pl) | Zestaw surowcowy przeznaczony do wytwarzania klinkieru portlandzkiego | |
RU2576537C1 (ru) | Композиция для изготовления жаростойких бетонов |