NO304318B1 - Anvendelse av sveisetrÕd for sveising av et gulvbelegg - Google Patents
Anvendelse av sveisetrÕd for sveising av et gulvbelegg Download PDFInfo
- Publication number
- NO304318B1 NO304318B1 NO902699A NO902699A NO304318B1 NO 304318 B1 NO304318 B1 NO 304318B1 NO 902699 A NO902699 A NO 902699A NO 902699 A NO902699 A NO 902699A NO 304318 B1 NO304318 B1 NO 304318B1
- Authority
- NO
- Norway
- Prior art keywords
- welding
- temperature zone
- vinyl acetate
- weight
- welding wire
- Prior art date
Description
Oppfinnelsen vedrører anvendelse av en sveisetråd, til sveising av homogene kunststoffbaner eller -plater, dvs. golvbelegg.
Fra DE-OS 37 43 296 og DE-OS 37 43 297 (= EP-OS 0 321 760) er det kjent en homogen, flerfargestrukturert kunststoffbane eller -plate på basis av meget fylt, myknerfritt bindemiddel, særlig med etylen-vinylacetat som bindemiddel. Disse kunststoffbanene eller -platene lar seg ikke sveise til-strekkelig med vanlige sveisesnorer på basis av myknerholdig PCV.
Oppgaven til foreliggende oppfinnelse er dermed å stille til rådighet en sveisesnor som gjør det mulig med sveising av kunststoffbaner eller -plater på basis av meget fylt, myknerfritt bindemiddel og særlig for baner eller plater som tilsvarer EP-OS 0 321 760.
Sveisesnoren ifølge oppfinnelsen skal særlig gi en sveising og dermed en absolutt avtetningsfunksjon med utmerkende fasthet i sveisesømmen. Den skal være lett av- og pårullbar og også god bearbeidbar ved innlegging for hånd, samt ved en sveiseautomat. Den må være så fleksibel at en overskytende del av sveisesnoren etter innlegging og sveising legg kan bli skåret, henholdsvis kuttet, vekk ved en kniv.
Mer spesifikt er oppfinnelsen rettet mot anvendelse av en sveisetråd som inneholder et bindemiddel på basis av etylen-vinylacetat-kopolymerisat (EVA), hvorved vinylacetatdelen i den samlede blandingen av sveisetråden utgjør 10 til 20 vekt-% og andelen av hjelpe- og fyllstoffer utgjør 1 til 30 vekt-# av den samlede blandingen, for sveising av gulvbelegg, idet gulvbelegget på basis av EVA inneholder en vinylacetatandel i den samlede blandingen på 3 til 14 vekt-# og en andel av fyllstoffer inkludert hjelpestoffer på 35 til 80 vekt-# av den samlede blandingen.
Fortrinnsvis oppviser sveisetråden som blir anvendt ifølge oppfinnelsen en vesentlig mindre andel av fyllstoffer enn kunststoffbanene eller -platene som skal sveises. Ifølge oppfinnelsen utgjør fyllstoffandelen i sveisetråden fortrinnsvis mindre enn 25 vekt-#, særlig mer enn 15 til 20 vekt-<$ >. Det er imidlertid mulig å anvende fyllstof f-f rie eller nesten fyllstoff-frie sveisetråder.
Bindemidlet i sveisestråden består fortrinnsvis av mer enn 60 vekt-# av etylen-vinylacetatkopolymerisat, hvorved vinylacetatandelen av EVA utgjør fortrinnsvis 15 til 30 vekt-#. Vinylacetatandelen utgjør 10 til 20 vekt-#, relativt til den totale blandingen i sveisetråden.
Bindemidlet i sveisetråden ifølge oppfinnelsen oppviser fortrinnsvis ingen eller bare små andeler av myknere. Eventuelt kan inntil 5$, fortrinnsvis inntil 2%, av en ftalat-mykner bli tilsatt.
I motsetning til smelteklebemidler på EVA-basis som blir tyntflytende etter de når smeltetemperaturen, blir sveisetråden ifølge oppfinnelsen høyviskøs til pastaaktig ved bearbeidingstemperaturen. Blandingen som anvendes ifølge oppfinnelsen er voksfri og inneholder ingen tilsatser av lavmolekylære polyolefiner (molekylvekt under 20 000), abietinsyreestere, terpenharpikser og andre tilsatser som nedsetter smelteviskositeten som er vanlig i andre smelteklebemidler.
Som fyllstoffer blir det fortrinnsvis anvendt 1 til 20 vekt-# kritt eller kaolin. Som hjelpestoffer blir det særlig anvendt inntil 3 vekt-# av et antioksiderende middel så vel som et antistatikum.
I det følgende blir oppfinnelsen nærmere forklart ved hjelp av utførelseseksempler.
Eksempel 1
Blanding som består av:
62,4 vekt-# etylenvinylacetat-kopolymerisat med en vinylacetatandel på 20 vekt-56 (relativt til EVA
[Riblene DHV 1040 X, Fa. Enichem]),
14,4 vekt-# etylenpropylendien-terpolymerisat (EPDM, Buna AP
437, Fa. Huls AG),
19,2 vekt-# kritt (Calcilit, Fa. Alpha Calcilit),
0,96 vekt-# kalsiumstearat (Ceasit, Fa. Bårlocher),
0,48 vekt-# antioksideringsmiddel (Irganox 1010, Fa. Ciba-Geigy),
0,96 vekt-# antistatikum (Lankrostat LA 3, Fa. Harcros
Chemicals ),
1,6 vekt-# farge
blir blandet i en Henschel-blander i 5 min. under avkjøling. Deretter blir blandingen bearbeidet som følger i en Reifenhåuser-ekstruder FH 80, snekkediameter 40 mm. lengde 25 D:
Temperatursone 1: 115 "C
Temperatursone 2: 150°C
Temperatursone 3: 130°C
Temperatursone 4: 115°C
Temperatursone 5: 80°C
Temperatursone 6: 70°C
Snekkedreietall: 10 min-<1>.
Det plastifiserte materiale ble videre bearbeidet til en 5 mm tykk streng, avkjølt og snittet til granulat. Det således fremstilte granulatet ble bearbeidet som følger i den samme ekstruderen:
Temperatursone 1: 138°C
Temperatursone 2: 185°C
Temperatursone 3: 175°C
Temperatursone 4: 180°C
Temperatursone 5: 145'C
Temperatursone 6: 158"C
Den 4 mm tykke sveisetråden ble trukket av i et vannbad med en båndhastighet på 9 m/min, tørket og viklet på.
Sveisetråden lar seg godt bearbeide både med hånd og gjennom en automat.
Til utprøving av styrken i sveisesømmen blir det fra en sveiset golvbeleggsprøve snittet 50 mm bred strimmel på tvers av sømretningen og på tvers av sømretningen blir det belastet til sveisesømmen blir revet opp. Som golvbelegg ble det anvendt en banevare ifølge siste eksemplet i EP-OS 0 321 760. Den således målte strekkstyrke utgjorde 296 N.
Eksempel 2
En blanding av:
60.5 vekt-# etylenvinylacetat-kopolymerisat med 28$ VA-andel
(Riblene DJV 1055, Fa, Enichem),
14,0 vekt-# etylenpropylen-terpolymerisat (EPDM) [Buna AP
437, Fa. Htils AG] ,
3,0 vekt-# polyetylen (Lupolen 1800 SP, BASF),
18.6 vekt-# calcilitt,
0,93 vekt-5é ceasitt,
0,46 vekt-# Irganox 1010,
0,96 vekt-# Lankrostat LA 3,
1,55 vekt-# farge
ble blandet i en Eirich-blander i 5 min og bearbeidet videre tilsvarende eksempel 1 i en Reifenhåuser-ekstruder med første trinn til granulat og deretter til en 4 mm tykk sveisetråd.
Temperatursone 1: 143°C
Temperatursone 2: 167°C
Temperatursone 3: 173°C
Temperatursone 4: 179°C
Temperatursone 5: 163°C
Temperatursone 6: 186°C
Båndhastigheten utgjorde 12 m/min. Den således fremstilte sveisesnoren lar seg godt bearbeide. Strekkstyrken etter sveisingen utgjorde 300 N.
Eksempel 3
Blandingen,
77,0 vekt-# etylenvinylacetat-kopolymerisat med 20$ VA-andel
(Riblene DHV 1040 X; Fa. Enichem),
19,0 vekt-# etylenpropylendien-terpolymerisat (EPDM) [Buna
AP 437, Fa. Hiils AG] ,
0,95 vekt-# kalsiumstearat (Ceasit, Fa. Barlocher),
0,48 vekt-# Irganox 1010 (Fa. Ciba-Geigy),
0. 95 vekt-# Lankrostat LA 3 (Fa. Harcros Chemicals),
2,68 vekt-# farge
ble bearbeidet på tilsvarende måte som eksempel 2 til en 4 mm tykk sveisetråd.
Temperaturene var:
1. Granulatfremstilling
Sone 1: 140°C
Sone 2: 170°C
Sone 3: 175°C
Sone 4: 180°C
Sone 5: 162°C
Sone 6: 189°C
II. Ferdiglaging av sveisetråd
Sone 1: 135°C
Sone 2: 165°C
Sone 3: 175°C
Sone 4: 180°C
Sone 5: 165°C
Sone 6: 209°C
De anvendingstekniske egenskapene var gode. Strekkstyrken etter sveising utgjorde 339 N.
Eksempel 4
Den anvendte blandingen
61,2 vekt-# etylenvinylacetat-kopolymerisat med 20% VA-andel
(Riblene DHV 1040 X, Fa. Enichem]),
14,1 vekt-# etylenpropylendien-terpolymerisat (EPDM), [Buna
AP 437, Fa. Htils AG] ,
18,8 vekt-# kritt (Calcilit, Fa. Alpha Calcilit),
0,94 vekt-# kalsiumstearat (Ceasit, Fa. Barlocher),
0,47 vekt-% antioksidanter (Irganox 1010, Fa. Ciba-Geigy), 2,5 vekt-# farge
1,99 vekt-# mykner-diisodecylftalat (Genomoll 180, Fa.
Hoechst),
ble blandet i en Henschel-blander FM 250 C i 5 min, hvorved mykneren 180 ble tilsatt etter de øvrige komponentene.
Granuleringen foregikk i en Reifenhåuser-ekstruder 30 D med en snekkediameter på 49/58 mm. Blandingen ble tilført med en doseringssnekke.
Temperatursone 1: 140°C
Temperatursone 2: 180°C
Temperatursone 3: 170°C
Temperatursone 4: 160°C
Temperatursone 5: 160°C
Temperatursone 6: 160°C
Temperatursone 7: 160°C
Temperatursone 8: 150°C
Temperatursone 9: 150°C
Det ble ferdiglaget strenger over en hullplate med 11 boringer av 5 mm diameter, avkjølt i vannbad og deretter granulert. Det tørkede granulatet ble bearbeidet i den samme ekstruderen under tilsvarende betingelser til strenger. Båndhastigheten utgjorde 1,8 m/min og diameteren på sveisetråden var 4 mm. Den anvendingstekniske oppførselen var god. Strekkstyrken utgjorde 340 N.
Eksempel 5
Blandingen,
63,41 vekt-# etylenvinylacetat-kopolymerisat med 20% VA-andel
(Riblene DJV 1055, Fa. Enichem]),
14,71 vekt-# etylenpropylendien-terpolymerisat (EPDM), [Buna
AP 437, Fa. Huls AG],
1,15 vekt-# polypropylen (Novolen 1300 E, Fa. BASF),
0,43 vekt-# polyetylen (Escorene LD 253),
14,0 vekt-56 calcilitt,
5,70 vekt-# kaolin (Typ RC 32, Fa. Sachtleben)
0,30 vekt-# antistatikum (Lankrostat LA 3, Fa. Harcros
Chemicals),
0,30 vekt-% farge
ble blandet i en Eirich-blander i 5 min og deretter valset på en Berstorff-valse type W 00622 i 10 min ved 140°C og malt på en Alpine-Mtlhle type A 16/8 over en 4 mm sikt.
Ferdiglagingen av sveisetråden ble foretatt på en Reifen-hauser-ekstruder type EH 80 med en snekkediameter på 40 mm og en lengde på 25 D. Boringen til dysen hadde en diameter på 4 mm.
Temperatursone 1: 132°C
Temperatursone 2: 170°C
Temperatursone 3: 173°C
Temperatursone 4: 180°C
Temperatursone 5: 164°C
Temperatursone 6: 208°C
Båndhastigheten var 12 m/min. Sveisetråden lar seg godt bearbeide i hånden og i automat. Strekkstyrken etter sveising utgjorde 285 N.
Claims (1)
- Anvendelse av en sveisetråd som inneholder et bindemiddel på basis av etylenvinylacetat-kopolymerisat (EVA), hvorved vinylacetatdelen i den samlede blandingen av sveisetråden utgjør 10 til 20 vekt-# og andelen av hjelpe- og fyllstoffer utgjør 1 til 30 vekt-% av den samlede blandingen, for sveising av gulvbelegg, idet gulvbelegget på basis av EVA inneholder en vinylacetatandel i den samlede blandingen på 3 til 14 vekt-# og en andel av fyllstoffer inkludert hjelpestoffer på 35 til 80 vekt-# av den samlede blandingen.