NO20005931D0 - Zinc aluminate with high specific surface area, process for production and use for treatment of exhaust gases from motor vehicles - Google Patents

Zinc aluminate with high specific surface area, process for production and use for treatment of exhaust gases from motor vehicles

Info

Publication number
NO20005931D0
NO20005931D0 NO20005931A NO20005931A NO20005931D0 NO 20005931 D0 NO20005931 D0 NO 20005931D0 NO 20005931 A NO20005931 A NO 20005931A NO 20005931 A NO20005931 A NO 20005931A NO 20005931 D0 NO20005931 D0 NO 20005931D0
Authority
NO
Norway
Prior art keywords
aluminate
surface area
specific surface
exhaust gases
treatment
Prior art date
Application number
NO20005931A
Other languages
Norwegian (no)
Other versions
NO20005931L (en
Inventor
Catherine Hedouin
Thierry Seguelong
Original Assignee
Rhodia Chimie Sa
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Rhodia Chimie Sa filed Critical Rhodia Chimie Sa
Publication of NO20005931D0 publication Critical patent/NO20005931D0/en
Publication of NO20005931L publication Critical patent/NO20005931L/en

Abstract

The invention concerns a zinc aluminate characterised in that it has, after calcination at 800 DEG C for 8 hours, a specific surface area of at least 85m<2>/g. The invention also concerns a precursor composition of said aluminate. The method for preparing the aluminate and the composition comprises the following steps: contacting in a solvent medium a salt, a zinc sol or alkoxide and an aluminium alkoxide; hydrolyzing the resulting mixture by adding an amount of water in excess relative to the aluminium alkoxide; recuperating the formed precipitate and optionally drying it, thereby obtaining the precursor composition; if required, calcining said precipitate, thereby obtaining the aluminate. Finally, the invention concerns the use of aluminate for treating motor vehicle exhaust gases.
NO20005931A 1998-05-26 2000-11-23 Zinc aluminate with high specific surface area, process for production and use for treatment of exhaust gases from motor vehicles NO20005931L (en)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
FR9806610A FR2779071B1 (en) 1998-05-26 1998-05-26 ZINC ALUMINATE WITH HIGH SPECIFIC SURFACE, PREPARATION METHOD THEREOF AND USE THEREOF IN THE TREATMENT OF AUTOMOTIVE EXHAUST GASES
PCT/FR1999/001210 WO1999061150A1 (en) 1998-05-26 1999-05-21 Zinc aluminate with high specific surface area, preparation method and use for treating motor vehicle exhaust gases

Publications (2)

Publication Number Publication Date
NO20005931D0 true NO20005931D0 (en) 2000-11-23
NO20005931L NO20005931L (en) 2001-01-18

Family

ID=9526717

Family Applications (1)

Application Number Title Priority Date Filing Date
NO20005931A NO20005931L (en) 1998-05-26 2000-11-23 Zinc aluminate with high specific surface area, process for production and use for treatment of exhaust gases from motor vehicles

Country Status (10)

Country Link
EP (1) EP1098701A1 (en)
JP (1) JP2002516245A (en)
KR (1) KR100392168B1 (en)
CN (1) CN1145524C (en)
BR (1) BR9910711A (en)
CA (1) CA2333426A1 (en)
FR (1) FR2779071B1 (en)
NO (1) NO20005931L (en)
WO (1) WO1999061150A1 (en)
ZA (1) ZA200005822B (en)

Families Citing this family (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE19960867A1 (en) * 1999-12-17 2001-06-28 Studiengesellschaft Kohle Mbh Synthesis of transition-metal aluminates with high specific surface areas by crystallization from transition metal-containing aluminosilicates
DE102004041295A1 (en) * 2004-08-25 2006-03-09 Beiersdorf Ag Preparation for fixing keratin fibers with a combination of fixing polymers and cellulose derivatives
KR101236612B1 (en) * 2005-01-06 2013-02-22 리써치 트라이앵글 인스티튜트 Zinc oxide-based sorbents and processes for preparing and using same
CN101555029B (en) * 2008-04-09 2011-05-04 清华大学 Method for preparing zinc aluminate nano-material
PL2141118T3 (en) * 2008-07-03 2014-01-31 Haldor Topsoe As Chromium-free water gas shift catalyst
CN102583467B (en) * 2012-02-24 2014-01-22 山东大学 Method for using hydrotalcite-like substance with low zinc-aluminum molar ratio as precursor to manufacture zinc-aluminum spinel

Family Cites Families (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3904553A (en) * 1973-08-20 1975-09-09 Corning Glass Works Thermally stable composite base metal oxide catalysts
JPH07149519A (en) * 1991-12-24 1995-06-13 Kawaken Fine Chem Co Ltd Production of spinel-type double oxide
JP2851773B2 (en) * 1993-09-09 1999-01-27 京セラ株式会社 Oxide catalyst material for removing nitrogen oxides and method for removing nitrogen oxides
FR2718371B1 (en) * 1994-04-08 1996-05-03 Rhone Poulenc Chimie Reduction catalysts for nitrogen oxides based on spinels.
DE4419486C2 (en) * 1994-06-03 1996-09-05 Daimler Benz Ag Catalyst, process for its preparation and use of the catalyst
DE4420932A1 (en) * 1994-06-16 1996-01-11 Basf Ag Spinel catalyst to reduce nitrogen oxide content of exhaust gas
JPH0824648A (en) * 1994-07-22 1996-01-30 Nissan Motor Co Ltd Exhaust gas purifying catalyst and preparation of the sam

Also Published As

Publication number Publication date
NO20005931L (en) 2001-01-18
EP1098701A1 (en) 2001-05-16
JP2002516245A (en) 2002-06-04
ZA200005822B (en) 2002-05-16
FR2779071B1 (en) 2000-08-18
CN1145524C (en) 2004-04-14
BR9910711A (en) 2001-01-30
FR2779071A1 (en) 1999-12-03
WO1999061150A1 (en) 1999-12-02
KR100392168B1 (en) 2003-07-22
CA2333426A1 (en) 1999-12-02
KR20010052401A (en) 2001-06-25
CN1302226A (en) 2001-07-04

Similar Documents

Publication Publication Date Title
ATE157102T1 (en) CATALYST SUPPORT, METHOD FOR PRODUCING A CATALYST SUPPORT PRECURSOR GEL
BR9703163A (en) Catalyst and process for the production of unsaturated aldehyde and unsaturated acid
KR850006540A (en) Cerium oxide with new morphological properties and preparation method thereof
JP2011521871A5 (en)
ATE9876T1 (en) CATALYST AND PROCESS OF MAKING THE CATALYST.
RU2009118959A (en) COMPOSITION WITH A HIGH ACIDITY BASED ON ZIRCONIUM OXIDE, TITANIUM OXIDE AND TUNGSTEN OXIDE, METHOD FOR PRODUCING AND APPLICATION FOR PROCESSING EXHAUST GASES
NO20005931D0 (en) Zinc aluminate with high specific surface area, process for production and use for treatment of exhaust gases from motor vehicles
ATE404283T1 (en) METHOD FOR PRODUCING CATALYSTS WITH LOW VOLUME SHROUD
PL347935A1 (en) Hydrogels absorbing aqueous fluids
US20030229151A1 (en) Process for producing organically modified metal oxides and products thereof
US6576204B2 (en) Process for the production of alumina
RU93050861A (en) ALUMINUM, STABILIZED LANTAN, METHOD FOR PRODUCING IT, CATALYST MEDIA AND CATALYST BASED ON
KR930000156A (en) Catalysts and methods for treating sulfur compounds-containing gases
JPH05504932A (en) MTW type zeolite and its manufacturing method
US8568687B2 (en) Method of manufacturing solid acid catalyst
JP2001240415A5 (en)
ES537364A0 (en) PROCEDURE FOR PREPARING HIGHLY REACTIVE AND FINALLY DIVIDED MAGNESIUM FROM MAGNESIUM HYDRIDE
JP3743964B2 (en) Method for producing dispersible aluminosilicate
ATE161801T1 (en) METHOD FOR RECOVERING ALUMINUM AND FLUORINE FROM WASTE CONTAINING FLUORINE
RU2002116371A (en) COLLOIDAL DISPERSION OF CERIUM COMPOUND CONTAINING CERIUM III AND USE
TW427926B (en) Acid contacted enhanced adsorbent particle and method of making and using therefor
EP0424187A1 (en) Process for the preparation of pillared clays and the pillared clays obtained from the process
JPH06218282A (en) Heat resistant catalyst carrier and production thereof
JPH11169659A (en) Acidic gas adsorptive decomposing agent and its production and acidic gas adsorptive decomposing method
JP3010212B1 (en) Method for producing high heat resistant porous alumina-based catalyst support

Legal Events

Date Code Title Description
FC2A Withdrawal, rejection or dismissal of laid open patent application