NL169490B - METHOD FOR PREPARING A COATING MATERIAL AND PREPARATIONS PREPARED USING THIS MATERIAL - Google Patents

METHOD FOR PREPARING A COATING MATERIAL AND PREPARATIONS PREPARED USING THIS MATERIAL

Info

Publication number
NL169490B
NL169490B NL7003110A NL7003110A NL169490B NL 169490 B NL169490 B NL 169490B NL 7003110 A NL7003110 A NL 7003110A NL 7003110 A NL7003110 A NL 7003110A NL 169490 B NL169490 B NL 169490B
Authority
NL
Netherlands
Prior art keywords
glass
inorganic material
glasses
coating
completely
Prior art date
Application number
NL7003110A
Other languages
Dutch (nl)
Other versions
NL7003110A (en
NL169490C (en
Original Assignee
Owens Illinois Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Owens Illinois Inc filed Critical Owens Illinois Inc
Publication of NL7003110A publication Critical patent/NL7003110A/xx
Publication of NL169490B publication Critical patent/NL169490B/en
Application granted granted Critical
Publication of NL169490C publication Critical patent/NL169490C/en

Abstract

1311889 Coating OWENS-ILLINOIS INC 11 March 1970 [11 March 1969 16 May 1969] 11562/70 Heading B2E [Also in Divisions C1 and C3] Substrates such as plate glass, ceramics, glass-ceramics, metals, carbon, plastics and ceramic/metallic composites, are provided with a coating of a particulate inorganic material by; (1) applying to the substrate a coating composition comprising a particulate inorganic material dispersed in a low molecular weight low vapour pressure liquid polymer having a relatively constant viscosity and thixotropic character and which is capable of being decomposed or pyrolysed completely to gaseous products without leaving a carbonaceous residue, the inorganic material having a fusing temperature higher than that at which the polymer is completely hydrolysed; (2) heating the thus coated substrate to completely pyrolyse the polymer and then (a) heating further to fuse the inorganic material to the substrate. The inorganic materials specified are silica, alumina, boric oxide, decorative glazers which are glassy compositions containing low melting compositions of fluxes such as alkali metal oxides, boric oxide and lead oxide; electron emissive compounds such as BaCO 3 , SrCO 3 and CaCO 3 ; metals such as Cu, Au, Ag, Ni and Pt, and alloys; glasses, thermally crystallisable glasses, solder glasses and mixtures thereof. The material is preferably vitreous solder glass consisting essentially of 70-80wt% PbO, 16-8wt% ZnO, 10-7wt% B 2 O 3 , 1-4 wt% SiO 2 , 0-1wt% BaO and 0-1wt% SnO 2 . The coating composition may also contain a cyclic isoprenoid solvent such as turpentine, which should be volatile at the pyrolysis stage. In the examples glass is coated using poly- (alpha methyl styrene) in which is dispersed a PbO/B 2 O 3 /SiO 2 mixture or a mixture of vitreous particles and glass ceramic particles.
NLAANVRAGE7003110,A 1969-03-11 1970-03-04 METHOD FOR PREPARING A COATING MATERIAL AND PREPARATIONS PREPARED USING THIS MATERIAL NL169490C (en)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US80632069A 1969-03-11 1969-03-11
US82541069A 1969-05-16 1969-05-16

Publications (3)

Publication Number Publication Date
NL7003110A NL7003110A (en) 1970-09-15
NL169490B true NL169490B (en) 1982-02-16
NL169490C NL169490C (en) 1982-07-16

Family

ID=27122879

Family Applications (1)

Application Number Title Priority Date Filing Date
NLAANVRAGE7003110,A NL169490C (en) 1969-03-11 1970-03-04 METHOD FOR PREPARING A COATING MATERIAL AND PREPARATIONS PREPARED USING THIS MATERIAL

Country Status (6)

Country Link
JP (1) JPS5034049B1 (en)
BE (1) BE747112A (en)
DE (1) DE2010920C3 (en)
FR (1) FR2037967A5 (en)
GB (1) GB1311889A (en)
NL (1) NL169490C (en)

Families Citing this family (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1356919A (en) * 1970-04-17 1974-06-19 Ici Ltd Glass reinforced polymer composites
GB2134413B (en) * 1983-01-10 1986-08-13 Atomic Energy Authority Uk Coating process
EP1807370A1 (en) * 2004-09-24 2007-07-18 E.I. Dupont De Nemours And Company Sealing compositions
JP2007291314A (en) * 2006-03-30 2007-11-08 Fujifilm Corp Coating film having water slipping property and process for producing the same
AU2012244185B2 (en) * 2007-09-20 2014-03-20 Green Source Energy Llc Extraction of Hydrocarbons from Hydrocarbon-Containing Materials
US8272442B2 (en) 2007-09-20 2012-09-25 Green Source Energy Llc In situ extraction of hydrocarbons from hydrocarbon-containing materials
US8404108B2 (en) 2007-09-20 2013-03-26 Green Source Energy Llc Extraction of hydrocarbons from hydrocarbon-containing materials and/or processing of hydrocarbon-containing materials
US8101812B2 (en) 2007-09-20 2012-01-24 Green Source Energy Llc Extraction of hydrocarbons from hydrocarbon-containing materials
JP2010540694A (en) * 2007-09-20 2010-12-24 グリーン・ソース・エナジー・リミテッド・ライアビリティ・カンパニー Hydrocarbon extraction from hydrocarbon-containing materials
MA33192B1 (en) * 2009-03-13 2012-04-02 Green Source Energy Llc Extraction of hydrocarbons from substances containing hydrocarbons
US8207251B2 (en) * 2009-03-23 2012-06-26 Xerox Corporation Low polarity nanoparticle metal pastes for printing application
CN106836536A (en) * 2017-03-24 2017-06-13 南通市苏东钢结构有限公司 A kind of flame retardant polyurethane warming plate

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2311513A (en) * 1940-01-17 1943-02-16 Westinghouse Electric & Mfg Co Method of applying luminescent coating
US2312229A (en) * 1940-04-12 1943-02-23 Gen Electric Method of forming fluorescent screens
NL278801A (en) * 1961-05-26
FR1581531A (en) * 1968-05-14 1969-09-19

Also Published As

Publication number Publication date
GB1311889A (en) 1973-03-28
FR2037967A5 (en) 1970-12-31
JPS5034049B1 (en) 1975-11-05
NL7003110A (en) 1970-09-15
DE2010920A1 (en) 1970-09-24
BE747112A (en) 1970-08-17
NL169490C (en) 1982-07-16
DE2010920B2 (en) 1979-07-05
DE2010920C3 (en) 1980-03-06

Similar Documents

Publication Publication Date Title
NL169490C (en) METHOD FOR PREPARING A COATING MATERIAL AND PREPARATIONS PREPARED USING THIS MATERIAL
CA1069349A (en) Metallizing compositions
US4186023A (en) Sealing glass composition
US3281309A (en) Ceramic bonding
KR910006165A (en) Thermistor composition
KR880005051A (en) Enamel composition and substrate coated with the composition
CA2037343A1 (en) Glass composition
GB1025125A (en) Improvements in or relating to the production of coating compositions based on glass
US3877962A (en) Substrate coating composition and process
KR101220443B1 (en) Crystallizable glass for sealing, crystallizable glass composition for sealing comprising the same, crystallizable glass paste, and oled panel
JP3800256B2 (en) Insulating glass composition
US3782989A (en) Polymeric based composition
US3661615A (en) Substrate coating process
US3625733A (en) Substrate coating process
GB1062378A (en) Vitreous compositions
US3888686A (en) Sealing glass compositions containing calcined zirconia vanadia silica stain
US3922471A (en) Surface having sealing glass composition thereon
US3018191A (en) Process of gold coating ceramic surfaces and articles produced thereby
US3380846A (en) Matte surface vitreous enamels and articles made therefrom
GB1022229A (en) Vitreous enamel resistor composition and electrical resistor made therefrom
GB1026627A (en) Improvements in or relating to resistance materials,and electrical resistors made therefrom
JP3424700B2 (en) Glass composition for insulation
JPH07330372A (en) Glass having low melting point
JPH0118020B2 (en)
WO2020153061A1 (en) Glass powder and sealing material using same

Legal Events

Date Code Title Description
V1 Lapsed because of non-payment of the annual fee