MX2020006643A - Lamina de acero chapada a base de zinc que tiene excelente resistencia de envejecimiento a temperatura ambiente y endurecibilidad en horno, y metodo para producirla. - Google Patents

Lamina de acero chapada a base de zinc que tiene excelente resistencia de envejecimiento a temperatura ambiente y endurecibilidad en horno, y metodo para producirla.

Info

Publication number
MX2020006643A
MX2020006643A MX2020006643A MX2020006643A MX2020006643A MX 2020006643 A MX2020006643 A MX 2020006643A MX 2020006643 A MX2020006643 A MX 2020006643A MX 2020006643 A MX2020006643 A MX 2020006643A MX 2020006643 A MX2020006643 A MX 2020006643A
Authority
MX
Mexico
Prior art keywords
steel sheet
zinc
room temperature
aging resistance
temperature aging
Prior art date
Application number
MX2020006643A
Other languages
English (en)
Inventor
Je - Woong Lee
Sang - Ho Han
Original Assignee
Posco
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Posco filed Critical Posco
Publication of MX2020006643A publication Critical patent/MX2020006643A/es

Abstract

Una lámina de acero chapada a base de zinc que tiene excelente resistencia de envejecimiento a temperatura ambiente y endurecibilidad en horno de acuerdo con un aspecto de la presente invención incluye una lámina de acero base y una capa de chapado a base de zinc formada sobre la superficie de la lámina de acero base, en donde la lámina de acero base contiene, en % en peso, no más de 0.005% (excluyendo 0%) de C, 0.1 - 1.0% de Mn, no más de 0.3% (excluyendo 0%) de Si, 0.01 - 0.08% de P, no más de 0.01% de S, no más de 0.01% de N, 0.01 - 0.06% de Al sol., 0.002 - 0.02% de Nb, y 0.001- 0.004% (excluyendo 0-001%) de B, con el resto que comprende Fe e impurezas inevitables, y Cs en la fórmula 1 enseguida puede satisfacer el intervalo de 0.0002 - 0.002%. En la fórmula 1, [C] y (Nb) representan los contenidos (% en peso) de C y Nb, respectivamente en la lámina de acero base. (Fórmula1) CS = (C) - (12/93) * (Nb).
MX2020006643A 2017-12-24 2018-11-23 Lamina de acero chapada a base de zinc que tiene excelente resistencia de envejecimiento a temperatura ambiente y endurecibilidad en horno, y metodo para producirla. MX2020006643A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
KR1020170178923A KR102031449B1 (ko) 2017-12-24 2017-12-24 상온내시효성 및 소부경화성이 우수한 아연계 도금강판 및 그 제조방법
PCT/KR2018/014520 WO2019124781A1 (ko) 2017-12-24 2018-11-23 상온내시효성 및 소부경화성이 우수한 아연계 도금강판 및 그 제조방법

Publications (1)

Publication Number Publication Date
MX2020006643A true MX2020006643A (es) 2020-09-14

Family

ID=66994981

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2020006643A MX2020006643A (es) 2017-12-24 2018-11-23 Lamina de acero chapada a base de zinc que tiene excelente resistencia de envejecimiento a temperatura ambiente y endurecibilidad en horno, y metodo para producirla.

Country Status (7)

Country Link
US (1) US20200332398A1 (es)
EP (1) EP3730645B1 (es)
JP (2) JP7214735B2 (es)
KR (1) KR102031449B1 (es)
CN (1) CN111492079B (es)
MX (1) MX2020006643A (es)
WO (1) WO2019124781A1 (es)

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR102312511B1 (ko) * 2019-12-18 2021-10-14 주식회사 포스코 소부경화성 및 상온 내시효성이 우수한 냉연강판 및 그 제조방법
KR102468037B1 (ko) * 2020-11-05 2022-11-17 주식회사 포스코 소부 경화성 및 내시효성이 우수한 냉연강판, 도금강판 및 이들의 제조방법
CN114411055A (zh) * 2021-12-31 2022-04-29 河钢股份有限公司 一种220MPa级烘烤硬化高强钢及其生产方法

Family Cites Families (19)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH06102810B2 (ja) * 1984-08-24 1994-12-14 日本鋼管株式会社 二次加工性に優れた深絞り用合金化溶融亜鉛メッキ鋼板の製造方法
JPH07116581B2 (ja) * 1990-05-22 1995-12-13 新日本製鐵株式会社 加工によるめっき剥離が少なく焼付硬化性に優れた高強度合金化溶融亜鉛めっき鋼板
US5690755A (en) * 1992-08-31 1997-11-25 Nippon Steel Corporation Cold-rolled steel sheet and hot-dip galvanized cold-rolled steel sheet having excellent bake hardenability, non-aging properties at room temperature and good formability and process for producing the same
JP3390084B2 (ja) * 1994-03-29 2003-03-24 川崎製鉄株式会社 成形性に優れた焼付硬化型薄鋼板およびその製造方法
JP3793351B2 (ja) * 1998-06-30 2006-07-05 新日本製鐵株式会社 焼付硬化性に優れた冷延鋼板
KR100363416B1 (ko) 1998-12-09 2003-02-19 주식회사 포스코 성형성이 우수한 고강도냉연강판의 제조방법
JP3596398B2 (ja) * 2000-01-18 2004-12-02 Ｊｆｅスチール株式会社 焼付硬化性と耐常温時効性に優れた冷延鋼板の製造方法
JP3855678B2 (ja) 2000-04-28 2006-12-13 住友金属工業株式会社 耐常温時効性、加工性、塗装焼付硬化性に優れた薄鋼板の製造方法
DE60121162T2 (de) * 2000-05-26 2006-11-09 Jfe Steel Corp. Kaltgewalztes stahlblech und galvanisiertes stahlblech mit guten reckalterungseigenschaften und herstellungsverfahren dafür
US6361624B1 (en) * 2000-09-11 2002-03-26 Usx Corporation Fully-stabilized steel for porcelain enameling
KR20020073564A (ko) 2000-11-28 2002-09-27 가와사끼 세이데쓰 가부시키가이샤 복합조직형 고장력 강판, 복합조직형 고장력 도금강판 및이들의 제조방법
JP4165272B2 (ja) 2003-03-27 2008-10-15 Ｊｆｅスチール株式会社 疲労特性および穴拡げ性に優れる高張力溶融亜鉛めっき鋼板およびその製造方法
JP2007270167A (ja) * 2006-03-30 2007-10-18 Jfe Steel Kk 焼付硬化性に優れた溶融亜鉛めっき鋼板の製造方法
JP4818880B2 (ja) 2006-10-31 2011-11-16 新日本製鐵株式会社 延性及び耐常温時効性に優れた焼付硬化性冷延鋼鈑の製造方法
JP4434198B2 (ja) * 2006-11-17 2010-03-17 Ｊｆｅスチール株式会社 低温焼付硬化性および耐時効性に優れる加工用薄鋼板の製造方法
KR101081057B1 (ko) * 2009-10-15 2011-11-07 현대하이스코 주식회사 고성형, 고품질 자동차 외판용 냉연강판 및 용융아연도금강판의 제조방법
WO2012070271A1 (ja) * 2010-11-22 2012-05-31 新日本製鐵株式会社 塗装焼付け後の耐時効性に優れた歪時効硬化型鋼板及びその製造方法
JP5310919B2 (ja) * 2011-12-08 2013-10-09 Ｊｆｅスチール株式会社 耐時効性と焼付き硬化性に優れた高強度冷延鋼板の製造方法
CN107532264B (zh) * 2015-04-21 2019-03-15 杰富意钢铁株式会社 合金化热镀锌原板及其制造方法和合金化热镀锌钢板

Also Published As

Publication number Publication date
JP7214735B2 (ja) 2023-01-30
EP3730645A1 (en) 2020-10-28
KR20190077176A (ko) 2019-07-03
CN111492079B (zh) 2021-12-03
EP3730645B1 (en) 2023-08-02
CN111492079A (zh) 2020-08-04
JP2021508772A (ja) 2021-03-11
JP2023052465A (ja) 2023-04-11
US20200332398A1 (en) 2020-10-22
KR102031449B1 (ko) 2019-10-11
WO2019124781A1 (ko) 2019-06-27
WO2019124781A8 (ko) 2020-02-27
EP3730645A4 (en) 2020-10-28
EP3730645C0 (en) 2023-08-02

Similar Documents

Publication Publication Date Title
MX2020006643A (es) Lamina de acero chapada a base de zinc que tiene excelente resistencia de envejecimiento a temperatura ambiente y endurecibilidad en horno, y metodo para producirla.
MX2017003310A (es) Partes formadas en prensa caliente que tienen excelente resistencia a la pulverizacion durante la formacion en prensa caliente y metodo para fabricar las mismas.
MX2011007977A (es) Lamina de acero galvanizada por inmersion en caliente de alta resistencia y metodo de fabricacion de la misma.
MX2016003144A (es) Laminas de acero galvanizadas por inmersion en caliente y laminas de acero recocidas despues de galvanizadas que tienen buen aspecto y buena adherencia al recubrimiento y metodos para la produccion de las mismas.
MX2016003143A (es) Laminas de acero galvanizadas por inmersion en caliente y laminas de acero recocidas despues de galvanizadas que tienen buen aspecto y buena adherencia al recubrimiento y metodos para la produccion de las mismas.
WO2012091310A3 (en) Hot dip plated steel sheet having excellent plating adhesiveness and method of manufacturing the same
MX2016001013A (es) Hoja de acero que tiene propiedades mecanicas de resistencia y ductibilidad muy altas, metodo de fabricacion y uso de tales hojas.
MX346491B (es) Placa de acero laminada en caliente o en frio, su proceso de fabricacion y su uso en la industria automotriz.
MX2009009769A (es) Acero para formacion en caliente o enfriamiento en una herramienta, que tiene ductilidad mejorada.
MX2009002966A (es) Lamina de acero esmaltada, sorprendentemente excelente en resistencia a escama de pescado y metodo para producir la misma.
MX2018005059A (es) Alambron no templado y revenido que tiene excelente trabajabilidad en frio y metodo de manufactura para el mismo.
UA100056C2 (ru) Способ производства холоднокатаного и отожженного листа из двухфазной стали, полученный таким способом лист, способ производства холоднокатаного, отожженного и оцинкованного листа из двухфазной стали (варианты) и использование указанного стального листа
MX2017003551A (es) Articulo formado en prensa en caliente que tiene excelente resisitencia a la deslaminacion y metodo para fabricar el mismo.
WO2016104881A8 (ko) 굽힘 특성이 우수한 hpf 성형부재 및 그 제조방법
UA116111C2 (uk) Низьколегована високоміцна сталь та її застосування
IN2014DN09576A (es)
WO2011081349A3 (ko) 취성 균열 발생 저항성이 우수한 고강도 강판 및 그 제조방법
WO2017082684A8 (ko) 냉간단조성이 우수한 선재 및 그 제조방법
BR112014005641A2 (pt) tira de aço galvanizada por imersão a quente de alta resistência
MX2019013725A (es) Aleacion a base de fe-si y un metodo para fabricarla.
MX2018011778A (es) Chapa de acero, chapa de acero revestida, metodo para producir chapa de acero laminada en caliente, metodo para producir chapa de acero muy dura laminada en frio, metodo para producir chapa de acero y metodo para producir chapa de acero revestida.
MY177836A (en) Low yield ratio high-strength hot-dip galvanized steel sheet, low yield ratio high-strength hot-dip galvannealed steel sheet, method for manufacturing low yield ratio highstrength hot-dip galvanized steel sheet, and method for manufacturing low yield ratio high-strength hot-dip galvannealed steel sheet
MX2016010001A (es) Lamina de acero galvano-recocida y metodo para la produccion de la misma.
EP3431624A3 (en) Soft magnetic component steel material having excellent pickling properties, soft magnetic component having excellent corrosion resistance and magnetic properties, and production method therefor
MX2019008079A (es) Lamina de acero laminada en frio de alta resistencia y metodo para la produccion de la misma.